JP2002338908A - Thermal adhesion tape, fiber product and method for manufacturing the same - Google Patents
Thermal adhesion tape, fiber product and method for manufacturing the sameInfo
- Publication number
- JP2002338908A JP2002338908A JP2001144629A JP2001144629A JP2002338908A JP 2002338908 A JP2002338908 A JP 2002338908A JP 2001144629 A JP2001144629 A JP 2001144629A JP 2001144629 A JP2001144629 A JP 2001144629A JP 2002338908 A JP2002338908 A JP 2002338908A
- Authority
- JP
- Japan
- Prior art keywords
- heat
- adhesive tape
- thermal adhesive
- thermal
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は繊維製品を構成する
生地、フィルムなどを接合する際に熱融着により接合さ
せるための熱接着テープおよび熱接着テープを用い接合
した繊維製品に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a heat-bonding tape for bonding fabrics, films and the like constituting a fiber product by heat-sealing, and a fiber product bonded using a heat-bonding tape.
【0002】[0002]
【従来の技術】従来の熱接着テープは裾上げテープ等に
代表されるように熱融着層のみで構成され、特開昭61
−252372号公報に開示されるように生地と生地と
の間に挿入され、挿入後、加熱・圧着させることにより
生地と生地とを接合させるものである。2. Description of the Related Art A conventional heat-adhesive tape comprises only a heat-sealing layer as represented by a hemming tape.
As disclosed in Japanese Patent No. 252372, it is inserted between the doughs, and after the insertion, the doughs are joined by heating and pressing.
【0003】しかし、生地と生地の間に挿入させるとき
に熱接着テープのズレや生地のズレが生じやすく、ズレ
が生じたまま加熱・圧着させたものは接合箇所に歪みや
シワが発生し、製品としての価値が著しく低下する、も
しくは製品の価値がなくなるなどの問題を有している。
また、一度、加熱・圧着させたものを剥離させようとし
た場合、生地が損傷を受ける等の理由により修復出来な
い等の欠点を有していた。[0003] However, when inserted between cloths, the thermal adhesive tape and the cloth are apt to be displaced, and when heated and press-bonded with the dislocation, distortion and wrinkles are generated at the joints. There is a problem that the value as a product is significantly reduced or the value of the product is lost.
Further, when the heated and press-bonded material is to be peeled off once, it has a drawback that the fabric cannot be repaired because the fabric is damaged or the like.
【0004】したがって、熱接着テープを用いた商品を
製造する際には、熱接着テープや生地のズレが生じない
よう注意が必要であり、注意するあまり生地や熱接着テ
ープを挿入するのに手間がかかり作業性に問題が残り、
改善を求められるものであった。Therefore, when manufacturing a product using a thermal adhesive tape, it is necessary to pay attention so that the thermal adhesive tape and the cloth do not shift, and it takes much time to insert the cloth and the thermal adhesive tape. And workability remains,
Improvement was required.
【0005】[0005]
【発明が解決しようとする課題】本発明に係る熱接着テ
ープは、熱接着テープ挿入時の熱接着テープおよび生地
のズレを防止し、従来と同様の熱接着効果を維持したま
ま縫製工程内での熱接着作業時の作業性を向上させた熱
接着テープを提供することにある。The thermal adhesive tape according to the present invention prevents the thermal adhesive tape and the cloth from being displaced when the thermal adhesive tape is inserted, and can be used in a sewing process while maintaining the same thermal adhesive effect as before. It is an object of the present invention to provide a thermal adhesive tape having improved workability during thermal adhesive work.
【0006】[0006]
【課題を解決するための手段】本発明者らは、上記課題
を解決するため鋭意検討を重ねた結果、従来からの熱接
着テープと同等の接着性を維持しながら、作業性を向上
させた熱接着テープに達したものである。Means for Solving the Problems The inventors of the present invention have made intensive studies to solve the above-mentioned problems, and as a result, have improved the workability while maintaining the same adhesiveness as that of a conventional thermal adhesive tape. It has reached thermal adhesive tape.
【0007】すなわち本発明は、熱融着層を有する熱接
着テープであって、熱融着層の少なくとも片面上に粘着
性の素材を部分的に配した熱接着テープである。That is, the present invention is a thermal adhesive tape having a thermal adhesive layer, wherein the adhesive material is partially disposed on at least one surface of the thermal adhesive layer.
【0008】また本発明は、繊維製品を構成する接合部
分の少なくとも一部が、生地と生地の間に該熱接着テー
プを挿入され、上記の熱接着テープにより融着接合して
いる繊維製品である。[0008] The present invention also provides a textile product in which at least a part of a joining portion constituting the textile product has the thermal adhesive tape inserted between the fabrics and is fusion-bonded with the thermal adhesive tape. is there.
【0009】また本発明は、上記の熱接着テープを、生
地と生地の間に配し、当該熱接着テープの粘着性の素材
により固定した後、熱により融着させる繊維製品の製造
方法である。Further, the present invention is a method for producing a fiber product in which the above-mentioned heat adhesive tape is disposed between cloths, fixed with an adhesive material of the heat adhesive tape, and then fused by heat. .
【0010】[0010]
【発明の実施の形態】本発明の熱接着テープは、後述す
るように繊維製品に好適に用いることができるが、繊維
製品を構成する材料としては、ポリエステル、ポリアミ
ド等の合成繊維や綿や羊毛などの天然繊維などを単独ま
たは2種以上用いた織編物や不織布、織編物にウレタン
樹脂や防水フィルムなどがコーティングやボンディング
などの方法により付与された防水布、さらにはポリエス
テル、ポリアミド樹脂からなるフィルム類やファスナー
等の付属類などが考えられる。BEST MODE FOR CARRYING OUT THE INVENTION The heat-adhesive tape of the present invention can be suitably used for textiles as described later, and synthetic fibers such as polyester and polyamide, cotton and wool are used for the textiles. Woven or knitted or non-woven fabrics using natural fibers alone or two or more of them, waterproof fabrics obtained by coating or bonding a urethane resin or a waterproof film on a woven or knitted fabric, and further films made of polyester or polyamide resin And attachments such as fasteners.
【0011】よって本発明の熱接着テープの熱融着層の
素材としては、繊維製品を構成する上記のような被接着
材料との接着性を重視し選定すればよいが、柔軟性、接
着性、加工性、コスト面などから、ウレタン系、ポリエ
ステル系、ポリアミド系の樹脂の使用が好ましい。その
態様として、これらのような樹脂をフィルム状にしたも
のも好ましい。Therefore, the material for the heat-sealing layer of the heat-adhesive tape of the present invention may be selected with emphasis on the adhesiveness to the above-mentioned material constituting the textile product. From the viewpoints of workability, cost, and the like, it is preferable to use urethane-based, polyester-based, or polyamide-based resins. As such an embodiment, a resin made of such a resin is also preferable.
【0012】また本発明の熱接着テープは、熱融着層の
少なくとも片面上に粘着性の素材を配することが重要で
ある。室温で粘着性を有する素材を熱融着層上に配する
ことにより、接着させる生地と生地との間に熱接着テー
プを挿入する際にも、熱融着までの仮固定が確実にで
き、テープの滑りが防止され、熱接着作業時の作業性を
向上させることが可能である。It is important for the heat-adhesive tape of the present invention that an adhesive material is disposed on at least one surface of the heat-sealing layer. By arranging the material having tackiness at room temperature on the heat-sealing layer, even when inserting the heat-adhesive tape between the cloth to be bonded and the cloth, the temporary fixing until the heat fusion can be surely performed, It is possible to prevent the tape from slipping and to improve the workability during the thermal bonding operation.
【0013】本発明における粘着性の素材は、常温での
粘着性があれば良く、アクリル系やウレタン系の樹脂、
シリコン系やウレタン系の合成ゴム等特に限定されるも
のではないが、粘着性、加工性の面からアクリル共重合
系樹脂を用いることが好ましい。The adhesive material in the present invention only needs to have an adhesive property at room temperature, and may be an acrylic or urethane resin.
Although not particularly limited, such as a silicone-based or urethane-based synthetic rubber, it is preferable to use an acrylic copolymer-based resin from the viewpoint of adhesiveness and workability.
【0014】本発明の熱接着テープにおける粘着性の素
材は、熱融着層の持つ接着性能を十分に引き出し、接合
部分の接着強力を確保するため、熱融着層上に部分的に
塗布し配するものである。熱融着層上に部分的に配する
ことにより、例えば生地と生地との間に挿入し、融着の
ため加熱を行ない熱融着層を溶かし生地面との接合を図
るとき、熱融着層と生地面とが直接接触する部分がある
ため十分な接着強力を得ることが可能である。熱融着層
の全面に塗布し配した場合、粘着性の素材が障害となり
熱融着層を生地面まで十分に浸透させられず十分な接着
強力が得られず、製品使用時に剥がれや接合部分のパン
クが発生するため好ましくない。The adhesive material in the heat-adhesive tape of the present invention is partially applied onto the heat-sealing layer in order to sufficiently bring out the adhesion performance of the heat-sealing layer and secure the bonding strength at the joint. It is to arrange. By partially arranging on the heat-sealing layer, for example, when inserting between doughs and performing heating for fusion and fusing the heat-sealing layer to join the fabric surface, heat-sealing Since there is a portion where the layer and the fabric surface are in direct contact, it is possible to obtain a sufficient adhesive strength. When applied and arranged on the entire surface of the heat-sealing layer, the adhesive material becomes an obstacle and the heat-sealing layer cannot penetrate sufficiently to the fabric surface, resulting in insufficient adhesion strength. This is not preferable because puncturing occurs.
【0015】粘着性の素材を熱融着層上に部分的に配す
る態様としては例えば、図4に示すようなドット状、図
5に示すようなストライプ状、図6に示すような格子状
などをあげることができるが、熱融着層が直接接着する
生地面に接触することが重要であり特にこれらに限定さ
れるものではない。As the mode of partially disposing the adhesive material on the heat-sealing layer, for example, a dot shape as shown in FIG. 4, a stripe shape as shown in FIG. 5, a lattice shape as shown in FIG. However, it is important that the heat-sealing layer is in direct contact with the fabric surface to which the heat-sealing layer is directly adhered, and the present invention is not particularly limited thereto.
【0016】粘着性の素材を熱融着層上に配する量とし
ては、例えば生地と生地の間に挿入し熱接着を行うと
き、熱接着テープを所定の位置に置き、生地を重ねる、
折り返す等の作業時に熱接着テープが所定の位置からず
れないような仮接着性を確保出来れば良く、その使用
量、配置面積は仮接着性を確保できれば出来るだけ少な
くすることがより好ましい。The amount of the adhesive material to be disposed on the heat-sealing layer is, for example, when a heat-bonding tape is placed at a predetermined position when the heat-bonding is performed by inserting the material between the cloths.
It is only necessary to ensure temporary adhesiveness so that the thermal adhesive tape does not deviate from a predetermined position at the time of work such as folding back, and it is more preferable to reduce the amount of use and arrangement area as much as possible if temporary adhesiveness can be ensured.
【0017】本発明における粘着性の素材を熱接着層に
配置させる方法としては、離型紙上にコーティングされ
た熱融着層上に直接にコーティングする方法がある。コ
ーティング方法としては、グラビアコーティングが均一
性の面から優れているが、ドット状やストライプ状、格
子状にコーティングできればよく、特に限定されるもの
ではない。As a method of disposing the tacky material in the heat bonding layer according to the present invention, there is a method of directly coating the heat bonding layer coated on the release paper. As a coating method, gravure coating is excellent in terms of uniformity, but is not particularly limited as long as it can be coated in a dot shape, a stripe shape, or a grid shape.
【0018】本発明における粘着性の素材を熱融着層に
配置させる他の方法としては、離型紙上にコーティング
などで形成した粘着層を熱融着層に接合させた後、離型
紙を剥離する方法などもある。これらの場合には、熱融
着層や粘着性の素材上に離型紙を更に設けた熱接着テー
プを得ることができ、熱接着テープ同士の接着など余計
な所での接着を防いで作業性を向上させることができる
ため、好ましい。As another method of disposing the adhesive material in the heat-sealing layer according to the present invention, an adhesive layer formed by coating or the like on a release paper is bonded to the heat-sealing layer, and then the release paper is peeled off. There are also ways to do that. In these cases, it is possible to obtain a thermal adhesive tape in which release paper is further provided on the thermal adhesive layer or an adhesive material, and workability by preventing adhesion in unnecessary places such as adhesion between thermal adhesive tapes. This is preferable because it is possible to improve
【0019】本発明における粘着性の素材は、図1に示
すように熱融着層の片面上に部分的に塗布し配されたも
のや、図2に示すように熱融着層の両面上に部分的に塗
布し配されるものである。The adhesive material according to the present invention may be a material which is partially applied and arranged on one side of the heat-sealing layer as shown in FIG. 1 or a material which is coated on both sides of the heat-sealing layer as shown in FIG. Is partially applied and disposed on
【0020】また、図3に示すように離型紙を貼ったも
のも熱接着テープ同士の接着を防ぐ点で好ましい。Further, as shown in FIG. 3, a material to which a release paper is attached is also preferable in that the adhesion of the thermal adhesive tapes is prevented.
【0021】本発明における熱接着テープは、ファッシ
ョン用、ユニフォーム用、スポーツ用、和装などの衣類
や、カーテン、フトンカバー、ピロケースなどの建寝装
用品や、ショール、鞄、靴などの日用品などに用いるこ
とが可能である。 特に好ましくは、縫糸を用いたミシ
ン縫目では接合部分に隙間や穴があくため水の漏水が問
題となっているが、接着テープでの接合では隙間や針穴
がなく接合部分からの水の漏水が防止されるため、防水
性能が要求される雨衣や防寒衣、鞄、靴などの接合に用
いることが特に効果的である。The thermal adhesive tape of the present invention can be used for clothing for fashion, uniforms, sports, Japanese clothes, etc., built-up bedclothes such as curtains, futon covers, pillow cases, and daily necessities such as shawls, bags and shoes. It can be used. Particularly preferably, in the case of a sewing machine using a sewing thread, there is a problem of water leakage due to a gap or a hole in a joint portion, but there is no gap or a needle hole in joining with an adhesive tape, and water from the joint portion has no problem. Since water leakage is prevented, it is particularly effective to use it for joining rain clothes, cold clothes, bags, shoes, and the like that require waterproof performance.
【0022】[0022]
【実施例】以下、本発明の熱接着テープを実施例および
比較例を上げて説明するが本発明はこれらに限定される
ものではない。EXAMPLES Hereinafter, the thermal adhesive tape of the present invention will be described with reference to examples and comparative examples, but the present invention is not limited to these examples.
【0023】(測定・評価) (1)熱接着テープの剥離強力 布帛間に熱接着テープをはさみ、平板プレス機を用い温
度160℃、圧力200g/cm2、時間20秒の条件
で熱圧着により接着後、幅2.5cm×約15cmにサ
ンプルカットし、つかみ間隔を5cm、引張速度10c
m/分に設定された定速伸長型引張試験機を用い、剥離
強力を測定した。 (2)作業性 パンツ裾部分の裾上げ接着における作業性を3段階で評
価した。 ○:接着テープのズレもなく作業性良好 △:若干接着テープがずれる ×:接着テープがズレ作業性悪い。(Measurement / Evaluation) (1) Peel Strength of Thermal Adhesive Tape A thermal adhesive tape is sandwiched between cloths, and subjected to thermocompression bonding using a flat plate press at a temperature of 160 ° C., a pressure of 200 g / cm 2 , and a time of 20 seconds. After bonding, sample cut to 2.5cm width × about 15cm, gripping interval 5cm, pulling speed 10c
Peel strength was measured using a constant-speed elongation type tensile tester set at m / min. (2) Workability The workability in bonding the hem of the pants to the hem was evaluated on a three-point scale. :: good workability without displacement of adhesive tape Δ: slight displacement of adhesive tape ×: poor workability of displacement of adhesive tape
【0024】(実施例1)熱融着樹脂(ポリエステル系
ポリウレタン、流動開始点100℃)を予め流動開始点
以上に加温し、流動化させたポリウレタン熱融着溶液を
ナイフオーバーロールコーターにて離型紙EV130T
PD(リンテック(株)製)に塗工し、厚み110μm
の熱融着層の膜を得た。Example 1 A heat-sealing resin (polyester polyurethane, flow starting point 100 ° C.) was heated to a temperature equal to or higher than the flow starting point in advance, and a fluidized polyurethane heat-sealing solution was applied using a knife over roll coater. Release paper EV130T
Coated on PD (manufactured by Lintec Co., Ltd.), thickness 110 μm
Was obtained.
【0025】次に、粘着性の樹脂としてアクリル共重合
体プラスターEH(新中村化学工業(株)製)をグラビ
アコーターにて熱融着層の膜上に図4のようにドット状
に塗工し、次いで80℃にて熱風乾燥し粘着性の素材を
部分的に配した本発明の熱接着テープを得た。Next, an acrylic copolymer plaster EH (manufactured by Shin-Nakamura Chemical Co., Ltd.) is applied as a sticky resin on the film of the heat-sealing layer in a dot form as shown in FIG. 4 by a gravure coater. Then, the resultant was dried at 80 ° C. with hot air to obtain a heat adhesive tape of the present invention in which an adhesive material was partially disposed.
【0026】次に78デシテックス、52フィラメント
のナイロン6フィラメント糸からなるタテ糸146本/
インチ、ヨコ糸94本/インチの織物にウレタンコーテ
ィングをし、コーティング面に22デシテックス、7フ
ィラメントのナイロン66フィラメント糸からなるトリ
コット編地を接着した3層構造の防水布を用い防水パン
ツを縫製した。Next, 146 warp yarns composed of a nylon 6 filament yarn of 52 filaments and 78 decitex are used.
Waterproof pants were sewn using a three-layer waterproof fabric in which a woven fabric of 94 inches / inch yarn / inch was coated with urethane, and a tricot knitted fabric consisting of 22 filaments of 22 filaments and 7 filaments of nylon 66 filaments was adhered to the coated surface. .
【0027】次にこの熱接着テープを用いパンツの裾上
げを行ない作業性を評価するとともにその部分の接着強
力を評価した。本実施例の熱接着テープを生地の間に挟
んだ際の熱接着テープのずれが防止され、作業しやすい
ものであった。評価結果を表1に示す。Next, using this thermal adhesive tape, the hem of the pants was raised to evaluate the workability and the adhesive strength of the portion. The displacement of the thermal adhesive tape when the thermal adhesive tape of the present example was sandwiched between the fabrics was prevented, and the work was easy. Table 1 shows the evaluation results.
【0028】(実施例2)粘着性の樹脂を図6のように
格子状に塗工した以外は実施例1と同様に本発明の熱接
着テープおよびパンツを縫製し、作業性および接着強力
を評価した。本実施例の熱接着テープを生地の間に挟ん
だ際の熱接着テープのずれが防止され、作業しやすいも
のであった。評価結果を表1に示す。(Example 2) The thermal adhesive tape and the pants of the present invention were sewn in the same manner as in Example 1 except that the adhesive resin was applied in a grid pattern as shown in FIG. evaluated. The displacement of the thermal adhesive tape when the thermal adhesive tape of this example was sandwiched between the fabrics was prevented, and the work was easy. Table 1 shows the evaluation results.
【0029】(比較例1)熱融着樹脂(ポリエステル系
ポリウレタン、流動開始点100℃)を予め流動開始点
以上に加温し、流動化させたポリウレタン熱融着溶液を
ナイフオーバーロールコーターにて離型紙EV130T
PD(リンテック(株)製)に塗工し、厚み110μm
の熱融着層の膜を得て、これを熱接着テープとした。(Comparative Example 1) A heat-sealing resin (polyester-based polyurethane, flow starting point 100 ° C.) was heated to a temperature equal to or higher than the flow starting point in advance, and the fluidized polyurethane heat-sealing solution was applied using a knife over roll coater. Release paper EV130T
Coated on PD (manufactured by Lintec Co., Ltd.), thickness 110 μm
Was obtained as a heat-bonded tape.
【0030】この熱接着テープを用い実施例1と同様の
パンツを縫製し、作業性および接着強力を評価した。生
地の間に挟む際、熱接着テープがすべり、なかなか思っ
た位置にテープを挟むことが出来ず作業性の悪いもので
あった。評価結果を表1に示す。Pants similar to those in Example 1 were sewn using this heat-adhesive tape, and workability and adhesive strength were evaluated. When sandwiched between the fabrics, the thermal adhesive tape slipped, and the tape could not be easily sandwiched at a desired position, resulting in poor workability. Table 1 shows the evaluation results.
【0031】(比較例2)熱融着樹脂(ポリエステル系
ポリウレタン、流動開始点100℃)を予め流動開始点
以上に加温し、流動化させたポリウレタン熱融着溶液を
ナイフオーバーロールコーターにて離型紙EV130T
PD(リンテック(株)製)に塗工し、厚み110μm
の熱融着層の膜を得た。(Comparative Example 2) A heat-sealing resin (polyester-based polyurethane, flow starting point 100 ° C.) was heated to a temperature equal to or higher than the flow starting point in advance, and the fluidized polyurethane heat-sealing solution was applied using a knife over roll coater. Release paper EV130T
Coated on PD (manufactured by Lintec Co., Ltd.), thickness 110 μm
Was obtained.
【0032】次に、粘着性の樹脂としてアクリル共重合
体プラスターEH(新中村化学工業(株)製)をナイフ
オーバーロールコーターにて熱融着膜全体に塗工し、次
いで80℃にて熱風乾燥し粘着性の素材を全面に配した
熱接着テープを得た。Next, an acrylic copolymer plaster EH (manufactured by Shin-Nakamura Chemical Co., Ltd.) is applied to the entire heat-sealed film as a sticky resin with a knife over roll coater, and then heated at 80 ° C. with hot air. A dried and tacky material was provided on the entire surface to obtain a heat adhesive tape.
【0033】この接着テープを用い実施例1と同様のパ
ンツを縫製し、作業性および接着強力を評価した。生地
の間に挟む際の熱接着テープのズレが防止され、作業し
やすいものであったが、十分な接着強力が得られなかっ
た。評価結果を表1に示す。Using this adhesive tape, the same pants as in Example 1 were sewn to evaluate workability and adhesive strength. The heat adhesive tape was prevented from slipping when sandwiched between the fabrics, and was easy to work. However, sufficient adhesive strength was not obtained. Table 1 shows the evaluation results.
【0034】[0034]
【表1】 [Table 1]
【0035】[0035]
【発明の効果】本発明に係る熱接着テープは熱融着層の
上に粘着性の素材が部分的に配されているため、接着強
力を維持したまま熱接着作業時に生地の上に乗せたとき
のテープの滑りが防止され、熱接着作業時の作業性を向
上させることが可能である。According to the thermal adhesive tape of the present invention, since the adhesive material is partially disposed on the thermal adhesive layer, it is put on the fabric at the time of thermal adhesive work while maintaining the adhesive strength. This prevents the tape from slipping at the time, thereby improving the workability during the thermal bonding operation.
【0036】また、接着テープでの接合では、縫糸を用
いたミシン縫目とは異なり、隙間や針穴がないため接合
部分からの水の漏水が防止されるため、防水性能が要求
される雨衣や防寒衣、鞄、靴などの接合に用いることが
特に効果的である。In addition, unlike the sewing stitch using a sewing thread, the joining with the adhesive tape prevents water leakage from the joining portion because there is no gap or a needle hole, so that raincoats that require waterproof performance are required. It is particularly effective to use it for bonding of clothing, winter clothing, bags, shoes, and the like.
【図1】本発明の熱接着テープの一例を示す断面図であ
る。FIG. 1 is a cross-sectional view illustrating an example of a thermal adhesive tape of the present invention.
【図2】本発明の熱接着テープの他の例を示す断面図で
ある。FIG. 2 is a sectional view showing another example of the thermal adhesive tape of the present invention.
【図3】本発明の熱接着テープのさらに他の例を示す断
面図である。FIG. 3 is a sectional view showing still another example of the thermal adhesive tape of the present invention.
【図4】本発明の熱接着テープの一例を示す正面図であ
る。FIG. 4 is a front view showing an example of the thermal adhesive tape of the present invention.
【図5】本発明の熱接着テープの他の例を示す正面図で
ある。FIG. 5 is a front view showing another example of the thermal adhesive tape of the present invention.
【図6】本発明の熱接着テープのさらに他の例を示す正
面である。FIG. 6 is a front view showing still another example of the thermal adhesive tape of the present invention.
【図7】本発明の熱接着テープの一例を示す斜視図であ
る。FIG. 7 is a perspective view showing an example of the thermal adhesive tape of the present invention.
1:熱融着層 2:粘着性素材 3:離型紙 1: heat sealing layer 2: adhesive material 3: release paper
───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 3B035 AA24 AB06 AB16 AC11 AD11 4J004 AA10 AA11 AA14 AB01 AB03 CA06 CE03 EA05 FA08 4L032 AA06 AB03 AC03 AC04 BA06 BC01 BD01 CA04 DA01 ────────────────────────────────────────────────── ─── Continued on the front page F term (reference) 3B035 AA24 AB06 AB16 AC11 AD11 4J004 AA10 AA11 AA14 AB01 AB03 CA06 CE03 EA05 FA08 4L032 AA06 AB03 AC03 AC04 BA06 BC01 BD01 CA04 DA01
Claims (4)
熱融着層の少なくとも片面上に粘着性の素材を部分的に
配した熱接着テープ。1. A heat-adhesive tape having a heat-sealing layer,
A heat adhesive tape in which an adhesive material is partially disposed on at least one surface of the heat sealing layer.
熱接着テープに離型紙を更に設けた請求項1記載の熱接
着テープ。2. The heat-adhesive tape according to claim 1, wherein a release paper is further provided on the heat-adhesive tape in which an adhesive material is partially disposed on the heat-sealing layer.
一部が、生地と生地の間に該熱接着テープを挿入され、
請求項1記載の熱接着テープにより融着接合している繊
維製品。3. A thermal adhesive tape is inserted between cloths at least in a part of a joint part constituting a textile product,
A textile product fusion-bonded with the thermal adhesive tape according to claim 1.
地の間に配し、当該熱接着テープの粘着性の素材により
固定した後、熱により融着させる繊維製品の製造方法。4. A method for producing a fiber product, comprising disposing the heat adhesive tape according to claim 1 between cloths, fixing the heat adhesive tape with an adhesive material of the heat adhesive tape, and fusing by heat.