JP2002038616A - External heat insulating architectural structure - Google Patents
External heat insulating architectural structureInfo
- Publication number
- JP2002038616A JP2002038616A JP2001149350A JP2001149350A JP2002038616A JP 2002038616 A JP2002038616 A JP 2002038616A JP 2001149350 A JP2001149350 A JP 2001149350A JP 2001149350 A JP2001149350 A JP 2001149350A JP 2002038616 A JP2002038616 A JP 2002038616A
- Authority
- JP
- Japan
- Prior art keywords
- heat insulating
- siding
- external heat
- insulating material
- siding material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は、住宅などの壁構造
などとして用いられる外断熱建築構造体に係り、さらに
詳しくは、壁の総厚が薄く、防水性及び耐久性に優れ、
且つ建築が容易で、新築およびリフォームの両方に適し
た外断熱建築構造体に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an exterior heat-insulating building structure used as a wall structure of a house or the like, and more particularly, to a wall having a small thickness and excellent waterproofness and durability.
The present invention relates to an external heat-insulating building structure which is easy to build and is suitable for both new construction and renovation.
【0002】[0002]
【従来の技術】従来の外断熱建築構造体では、外装材と
して、窯業系サイディング材や金属系サイディング材が
多く用いられている。しかし、窯業系サイディング材は
防火上の優れた性能は有しているものの、重量が重いの
で、外断熱建築構造体において窯業系サイディング材を
用いる場合には、柱(間柱含む)の数に対応して、外断
熱材の外側に胴縁を取り付け、これらの胴縁に対して、
サイディング材を係止させる必要があった。また、窯業
系サイディング材は、一般に吸水し易く、そのために、
サイディング材の背後に通気空間を設ける必要があり、
そのためにも胴縁は必要であった。また、胴縁を柱に固
定させるために、連結スペーサをも取り付ける必要もあ
り、施工性が非常に悪いという問題があった。さらに、
窯業系サイディング材は、先にも記したとおり吸水し易
い性質があるため、寒冷地においては、昼間に雪氷など
が融解して生じた水分を窯業系サイディング材が吸収
し、夜間の気温低下に伴い、この水分が凍結・膨張し、
サイディングの破壊を生じるという欠点もあった。ま
た、建築物の既存壁の上から窯業系サイディングを使用
して、外断熱防火構造にリフォームする場合は、窯業系
サイディングの重量が重いため、地震や雨風からこれを
保持するための適切な補強が必要となり、施工にあたっ
ては、再設計が必要となる場合もあり、非常に煩雑な問
題を抱えていた。2. Description of the Related Art In conventional external heat-insulating building structures, ceramic siding materials and metal siding materials are often used as exterior materials. However, although ceramic siding has excellent fire protection performance, it is heavy, so if ceramic siding is used in external heat-insulating building structures, the number of pillars (including studs) must be met. Then, attach the rim to the outside of the outer insulation, and for these rims,
It was necessary to lock the siding material. In addition, ceramic siding materials are generally easy to absorb water,
It is necessary to provide a ventilation space behind the siding material,
The waistline was necessary for that. In addition, in order to fix the body edge to the pillar, it is necessary to attach a connecting spacer, and there is a problem that workability is extremely poor. further,
As described above, ceramic siding materials have a property of easily absorbing water, so in cold regions, ceramic siding materials absorb the water generated by melting snow and ice in the daytime, resulting in lower temperature at night. As a result, this water freezes and expands,
There was also a disadvantage that siding was destroyed. In addition, when using ceramic siding over existing walls of a building to renovate it to an external insulation and fire protection structure, the weight of the ceramic siding is heavy, so appropriate reinforcement to hold it from earthquakes, rain and wind, etc. Was required, and re-designing was sometimes required in the construction, which had a very complicated problem.
【0003】このように、従来の外断熱建築構造体で
は、建築に手間がかかり、費用も嵩むと言う課題を有し
ていた。また、壁の総厚が大きく、壁が嵩張り、室内空
間または外構空間(建物と塀などとの間の空間)を狭め
ていた。さらにまた、既存壁をリフォームすることによ
り、従来の外断熱防火構造を施す場合には、窯業系サイ
ディング材の重量が大きいことから、地震に対する強度
を満足させるためには、壁の補強などが必要となり、リ
フォームが困難であった。[0003] As described above, the conventional externally insulated building structure has a problem that the construction is troublesome and costly. Further, the total thickness of the walls is large, the walls are bulky, and the indoor space or the external space (the space between the building and the fence) is narrowed. Furthermore, when the existing external insulation and fire protection structure is applied by renovating the existing wall, the weight of the ceramic siding material is large, so it is necessary to reinforce the wall to satisfy the strength against earthquakes It was difficult to remodel.
【0004】また、金属系サイディング材は比較的軽量
で、新築・リフォームともに施工は容易であるが、塗装
が施してあっても経年的に腐食し易く、酸性雨による腐
食ばかりでなく、海岸地方における塩害による腐食、火
山、温泉地近傍での酸、アルカリによる腐食などの耐久
性の問題が多く指摘されてきた。[0004] The metal siding material is relatively lightweight, and is easy to construct for both new construction and renovation. However, even if it is painted, it is easily corroded over time. Many durability problems have been pointed out, such as corrosion due to salt damage, and volcanic and acid and alkali corrosion near hot springs.
【0005】[0005]
【発明が解決しようとする課題】本発明は、このような
実状に鑑みてなされ、施工に際して、胴縁や連結スペー
サが不要であり、建築に手間がかからず、建築費が安価
であり、壁の総厚が薄く、外構空間を広くとれ、耐水性
にも優れた外断熱建築構造体を提供することを目的とす
る。SUMMARY OF THE INVENTION The present invention has been made in view of the above circumstances, and does not require a rim or a connecting spacer at the time of construction. It is an object of the present invention to provide an external heat-insulating building structure in which the total thickness of walls is thin, the external space can be widened, and the water resistance is excellent.
【0006】[0006]
【課題を解決するための手段】かくして本発明によれ
ば、上記目的を達成するために、以下の(1)〜(6)
が提供される。 (1)柱の屋外側に、外断熱材層を介して、合成樹脂製
サイディング材が、前記柱に対して固定してあることを
特徴とする外断熱建築構造体。 (2)外断熱材層が、難燃性断熱材から構成されている
前記(1)に記載された外断熱建築構造体。 (3)外断熱材層が、無機系断熱材から構成されている
前記(1)に記載された外断熱建築構造体。 (4)外断熱材層が、無機繊維材料から構成されている
前記(1)に記載された外断熱建築構造体。 (5)合成樹脂製サイディング材が、合成樹脂の複合体
である前記(1)記載された外断熱建築構造体。 (6)合成樹脂製サイディング材が、塩化ビニル樹脂か
ら構成されている前記(1)に記載された外断熱建築構
造体。本発明においては、柱と柱との間の空間にも、柱
間断熱材を具備させても良い。また、柱は間柱を含むも
のである。According to the present invention, in order to achieve the above object, the following (1) to (6)
Is provided. (1) An external heat-insulating building structure, wherein a synthetic resin siding material is fixed to the column outside the column via an external heat-insulating material layer. (2) The external heat-insulating building structure according to (1), wherein the external heat-insulating material layer is made of a flame-retardant heat-insulating material. (3) The external heat-insulating building structure according to (1), wherein the external heat-insulating material layer is made of an inorganic heat-insulating material. (4) The external heat-insulating building structure according to (1), wherein the external heat-insulating material layer is made of an inorganic fiber material. (5) The external heat-insulating building structure according to (1), wherein the siding material made of synthetic resin is a composite of synthetic resin. (6) The external heat-insulating building structure according to (1), wherein the siding material made of synthetic resin is made of vinyl chloride resin. In the present invention, the space between the columns may be provided with a heat insulating material between the columns. Further, the pillar includes a stud.
【0007】本発明における外断熱材層を構成する断熱
材料は、とくに限定されないが、無機系、有機系または
無機系/有機系複合体の断熱材料を挙げることができ
る。また、外断熱材層は難燃性断熱材から構成されてい
ることが好ましく、防火性能を有する外断熱材建築構造
体を得ることができる。無機系断熱材としては、たとえ
ば、グラスウール、ロックウール、炭酸カルシウム発泡
断熱材などが例示される。これらは、自己消化性能以上
の難燃性能を有する断熱材として知られ、なかでも、ロ
ックウール、グラスウール等の無機繊維系断熱材料が好
ましい。有機系断熱材としては、フェノール樹脂発泡
体、イソシアヌレート樹脂発泡体、シリコン系樹脂発泡
体等が挙げられる。また、無機系/有機系複合体の断熱
材料としては、例えば、無機フィラー高充填樹脂発泡体
等が挙げられる。これらの断熱材は、それぞれ単独で、
または組み合わせて使用することができる。The heat insulating material constituting the outer heat insulating material layer in the present invention is not particularly limited, and examples thereof include inorganic, organic, and inorganic / organic composite heat insulating materials. Further, the outer heat insulating material layer is preferably made of a flame-retardant heat insulating material, so that an outer heat insulating material building structure having fire prevention performance can be obtained. Examples of the inorganic heat insulating material include glass wool, rock wool, and calcium carbonate foam heat insulating material. These are known as heat insulating materials having flame retardancy higher than self-extinguishing performance. Among them, inorganic fiber heat insulating materials such as rock wool and glass wool are preferable. Examples of the organic heat insulating material include a phenol resin foam, an isocyanurate resin foam, and a silicone resin foam. As the heat insulating material of the inorganic / organic composite, for example, a resin foam highly filled with an inorganic filler and the like can be mentioned. Each of these insulations, alone,
Or they can be used in combination.
【0008】前記断熱材の密度は、特に限定されず、目
的とする断熱性能や防火性能から決定すればよいが、通
常、25〜300kg/m3、好ましくは50〜250
kg/m3である。この密度が低すぎると、サイディン
グ材の取り付けが不安定になる傾向にあり、密度が高す
ぎると、断熱性能が低下すると共に、高価格化する傾向
にある。本発明では、外断熱材層は、たとえば板状の断
熱材を張り巡らすことにより形成される。[0008] The density of the heat insulating material is not particularly limited and may be determined in accordance with the intended heat insulating performance and fire prevention performance, and is usually 25 to 300 kg / m 3 , preferably 50 to 250 kg / m 3 .
kg / m 3 . If the density is too low, the mounting of the siding material tends to be unstable, and if the density is too high, the heat insulating performance tends to decrease and the price tends to increase. In the present invention, the outer heat insulating material layer is formed, for example, by stretching a plate-shaped heat insulating material.
【0009】前記外断熱材層の厚みは、特に限定されな
い、目的とする断熱性能や防火性能から適宜決定すれば
よいが、好ましくは20〜200mm、さらに好ましく
は、25〜150mmである。その厚みが過度に薄いる
と、防火性および断熱性に乏しくなる傾向にあり、過度
に厚いと、サイディング材の取り付けが困難になる傾向
にある。The thickness of the outer heat-insulating material layer is not particularly limited and may be appropriately determined in accordance with the intended heat-insulating performance and fire-preventing performance, but is preferably 20 to 200 mm, more preferably 25 to 150 mm. If the thickness is excessively thin, fire protection and heat insulation tend to be poor. If the thickness is excessively large, mounting of the siding material tends to be difficult.
【0010】柱間断熱材としては、断熱性を有するもの
であれば、特に限定されず、外断熱材層と同じ材質に限
定されることなく、その他の断熱材を用いても良い。The inter-column heat insulating material is not particularly limited as long as it has heat insulating properties, and is not limited to the same material as the outer heat insulating material layer, and other heat insulating materials may be used.
【0011】本発明で使用する合成樹脂製サイディング
材を構成する合成樹脂としては、とくに限定されない
が、通常、熱可塑性樹脂が用いられる。熱可塑性樹脂と
しては、例えば、塩化ビニル樹脂、ポリエチレン、ポリ
プロピレン等のポリオレフィン、ポリメチルメタクリレ
ート、スチレン系共重合体、アクリレート−スチレン−
アクリロニトリル共重合体(AAS樹脂)、塩素化ポリ
エチレン、アクリロニトリル−スチレン共重合体(AC
S樹脂)、繊維強化プラスチック(FRP)などが挙げ
られる。なかでも、塩化ビニル樹脂製サイディング材
は、凍結破壊を生じることはなく、塩害・酸性・アルカ
リ性にも耐性が優れており、本発明の目的を達成するた
めに最適の合成樹脂である。塩化ビニル樹脂製サイディ
ング材は、長期間にわたって住宅等の建築物の秀麗さを
保持する加飾材として、サイディング材より屋内側に位
置する断熱材やその他の建築部材を保護するとともに、
防火性能を維持するものである。また、樹脂への着色の
自由度や成型時の形状設計の自由度が高く、長期にわた
り物性の低下が少なく、且つ難燃性を有する合成樹脂で
ある。The synthetic resin constituting the synthetic resin siding material used in the present invention is not particularly limited, but usually a thermoplastic resin is used. Examples of the thermoplastic resin include vinyl chloride resin, polyethylene, polyolefin such as polypropylene, polymethyl methacrylate, styrene-based copolymer, acrylate-styrene-
Acrylonitrile copolymer (AAS resin), chlorinated polyethylene, acrylonitrile-styrene copolymer (AC
S resin), fiber reinforced plastic (FRP) and the like. Above all, a siding material made of a vinyl chloride resin does not cause freezing breakage and has excellent resistance to salt damage, acidity, and alkalinity, and is an optimal synthetic resin for achieving the object of the present invention. The siding material made of vinyl chloride resin is a decorative material that keeps the excellence of buildings such as houses over a long period of time, while protecting insulation materials and other building members located indoors from the siding material,
It maintains fire protection performance. Further, it is a synthetic resin which has a high degree of freedom in coloring the resin and a degree of freedom in designing the shape at the time of molding, has little deterioration in physical properties over a long period of time, and has flame retardancy.
【0012】前記サイディング材の面密度は、通常、
0.5〜15Kg/m2以下、好ましくは0.5〜10
kg/m2である。面密度が過度に小さいと、外装材と
しての強度が弱く、また過度に面密度が大きいと、サイ
ディング材が重くなりすぎ、サイディング材の保持のた
めの補強構造が必要となる場合が生じるとともに、高所
での一人作業等の施工性が低下する。The surface density of the siding material is usually
0.5 to 15 kg / m 2 or less, preferably 0.5 to 10 kg / m 2
kg / m 2 . If the areal density is excessively small, the strength as the exterior material is weak, and if the areal density is excessively large, the siding material becomes too heavy, and a reinforcing structure for holding the siding material may be required, The workability of single-person work at high places is reduced.
【0013】本発明で使用する合成樹脂製サイディング
材の構造はとくに限定されないが、通常は、単層の合成
樹脂板で構成されたもの、複数の合成樹脂板を積層した
もの、単層または複数の合成樹脂板の裏側に適当な発泡
体を張り合わせた複合体等が挙げられる。複数の合成樹
脂板を積層する場合には、同一の樹脂素材であること
が、分別リサイクルの観点から好ましい。たとえば塩化
ビニル樹脂を用いて共押し出しの二層構造とし、基層部
は、リサイクル材を主成分とする低コスト樹脂コンパウ
ンド材を用いて構成し、表層部は、耐候性に優れたバー
ジン樹脂コンパウンド材を用いて構成することが経済的
である。特に、表面層に耐候性の良好な材料層を設け、
下層に低コストの材料を積層することにより、耐久性の
工場を図りつつ経済性を確保することができる。単層ま
たは複数の合成樹脂板に適当な発泡体を組み合わせた複
合体の場合は、薄層の合成樹脂サイディングの剛性不足
を補い、断熱性能を補強し、取り扱い性や施工性等を改
良することができる。発泡体としては、発泡ポリウレタ
ン、発砲ポリスチレン、イソシアヌレート発泡体等が挙
げられる。この場合、発泡体の厚さは、1〜30mm程
度のものが用いられる。Although the structure of the synthetic resin siding material used in the present invention is not particularly limited, it is usually composed of a single-layer synthetic resin plate, a laminate of a plurality of synthetic resin plates, a single-layer And a composite in which an appropriate foam is attached to the back side of the synthetic resin plate. When laminating a plurality of synthetic resin plates, it is preferable to use the same resin material from the viewpoint of separation and recycling. For example, a co-extruded two-layer structure using vinyl chloride resin, the base layer is made of a low-cost resin compound mainly composed of recycled materials, and the surface layer is a virgin resin compound with excellent weather resistance. Is economical. In particular, a material layer having good weather resistance is provided on the surface layer,
By laminating low-cost materials in the lower layer, it is possible to secure economical efficiency while achieving a durable factory. In the case of a single layer or a composite of multiple synthetic resin boards combined with a suitable foam, make up for the lack of rigidity of the thin synthetic resin siding, reinforce the heat insulation performance, and improve the handleability and workability. Can be. Examples of the foam include foamed polyurethane, foamed polystyrene, and isocyanurate foam. In this case, the thickness of the foam is about 1 to 30 mm.
【0014】サイディング材を構成する合成樹脂板の成
型方法は、塩化ビニル樹脂やポリプロピレン等の熱可塑
性樹脂の場合は、単層あるいは多層の異型押出し成型法
や、単層あるいは多層のTダイ押出し成型を経て熱間フ
ォーミングロールにより成型される方法が通常採られ
る。では、異形押出成形方法や、Tダイ押出を経てフォ
ーミングダイで成型する方法が好ましく用いられる。ポ
リオレフィンで構成する場合には、通常、異形押出成形
が用いられる。FRPのような熱硬化性樹脂で構成する
場合には、圧縮成型が好ましく用いられる。このよう
に、サイディング材を構成する合成樹脂板の種類に応じ
て、それぞれに適した成型方法を採用すればよい。In the case of a thermoplastic resin such as vinyl chloride resin or polypropylene, the molding method of the synthetic resin plate constituting the siding material is a single-layer or multilayer irregular extrusion molding method or a single-layer or multilayer T-die extrusion molding. Through a hot forming roll. In this case, a profile extrusion molding method or a method of molding with a forming die via T-die extrusion is preferably used. When composed of polyolefin, profile extrusion is usually used. When using a thermosetting resin such as FRP, compression molding is preferably used. As described above, a molding method suitable for each type of synthetic resin plate constituting the siding material may be employed.
【0015】サイディング材の大きさは、特に限定され
ないが、通常は、押出成形品の場合には、縦寸法が10
0〜400mm、横寸法が1000〜5000mm、射
出成形品の場合、縦寸法が500〜1000mm、横寸
法が500〜1500mm程度が好ましい。とくに、サ
イディング材の通常の施工は、建築物の下から上(ある
いはこの逆)、またはは横方向に向かって行われるた
め、縦横とも各々の寸法は、100〜5000mmの範
囲のものが施工上便利である。また、サイディング材の
厚みも特に限定されないが、0.5〜10mm程度が好
ましい。本発明では、サイディング材を構成する合成樹
脂板には、必要に応じて、顔料、加工助剤、熱安定剤、
紫外線吸収剤などの添加物が添加される。[0015] The size of the siding material is not particularly limited.
In the case of an injection-molded product having a width of 0 to 400 mm and a width of 1000 to 5000 mm, it is preferable that the length is about 500 to 1000 mm and the width is about 500 to 1500 mm. In particular, normal construction of siding materials is performed from the bottom of the building to the top (or vice versa), or in the horizontal direction. It is convenient. Also, the thickness of the siding material is not particularly limited, but is preferably about 0.5 to 10 mm. In the present invention, the synthetic resin plate constituting the siding material, if necessary, a pigment, a processing aid, a heat stabilizer,
Additives such as UV absorbers are added.
【0016】[0016]
【作用】本発明の構造体では、サイディング材は、釘、
ビスまたはボルトなどを用いて外断熱材層を貫通させて
柱に直接に取り付けられ、その結果、外断熱材層も、胴
縁や連結スペーサを用いることなく柱に固定される。ま
た、断熱材の固定が、これだけでは不足する場合には、
事前に柱にスピンドルピンを立てておき、断熱材の固定
を補強してもよい。本発明では、サイディング材は、合
成樹脂で構成してあるので、軽量であり、施工に際し
て、胴縁や連結スペーサが不要であり、建築に手間がか
からず、建築費が安価である。とくに、その材質が塩化
ビニルの場合は、その成型性を活かして複雑な形状に加
工することが可能となり、デザイン性の優れた外観が得
られるだけでなく、耐塩害性、耐酸性、耐アルカリ性、
耐凍結破壊性等に優れた、極めて耐久性の高い外壁構造
とすることが可能となる。また、胴縁や連結スペーサが
不要であることから、壁の総厚が薄く、外構空間を広く
とれる。また、サイディング材が合成樹脂製であるため
に、耐水性にも優れている。しかも、無機系の外断熱材
層を有しているので、防火性および断熱性に優れてい
る。→本発明により得られる外断熱防火構造体は、断熱
材に防火性能を有する材質のものを使用しているため、
防火性能、断熱性能も高い優れたものになる。とくに、
断熱材として、適切な厚みと密度のロックウールやガラ
スウール等の無機繊維系断熱材を使用した場合は、住宅
の防火性能上とくに重要な、建築基準法2条および23
条で規定される、防火構造および準防火構造の性能も付
与することが可能となる。In the structure of the present invention, the siding material is a nail,
The outer heat insulating material layer is directly attached to the pillar by using a screw or a bolt to penetrate the outer heat insulating material layer, and as a result, the outer heat insulating material layer is also fixed to the pillar without using a trunk edge or a connecting spacer. Also, if this is not enough to fix the insulation,
A spindle pin may be erected on the pillar in advance to reinforce the fixing of the heat insulating material. In the present invention, since the siding material is made of a synthetic resin, the siding material is lightweight, does not require a rim or a connecting spacer at the time of construction, does not require construction work, and has low construction costs. In particular, when the material is vinyl chloride, it can be processed into complex shapes by taking advantage of its moldability, and not only can an excellent design appearance be obtained, but also salt damage resistance, acid resistance, and alkali resistance ,
An extremely durable outer wall structure having excellent resistance to freezing and destruction can be obtained. Further, since the trunk edge and the connecting spacer are not required, the total thickness of the wall is thin, and the external space can be widened. Further, since the siding material is made of a synthetic resin, it has excellent water resistance. Moreover, since it has an inorganic outer heat insulating material layer, it is excellent in fire resistance and heat insulation. → Since the outer heat-insulating and fire-preventing structure obtained by the present invention uses a material having a fire-preventing property for the heat insulating material,
The fire prevention performance and the heat insulation performance are also excellent. In particular,
When an inorganic fiber-based heat insulating material such as rock wool or glass wool having an appropriate thickness and density is used as the heat insulating material, the building standard law, Articles 2 and 23, which are particularly important for the fire prevention performance of a house, are required.
It is also possible to provide the performance of the fire protection structure and the quasi-fire protection structure specified in the article.
【0017】さらに、本発明では、合成樹脂製のサイデ
ィング材が外断熱材層を介して柱に固定してあるため、
サイディング材を、釘、ビスまたはボルトなどで、打ち
加減または締め加減の調節を考慮せずに、比較的に強く
または固く柱に取り付けることができる。外断熱材層が
緩衝作用を発揮し、使用に際してのサイディング材の膨
張および収縮を吸収するからである。Further, in the present invention, since the siding material made of synthetic resin is fixed to the column via the outer heat insulating material layer,
The siding material can be attached to the column relatively strongly or firmly with nails, screws or bolts, etc., without taking into account the adjustment of setting or tightening. This is because the outer heat insulating material layer exerts a buffering action and absorbs expansion and contraction of the siding material during use.
【0018】ちなみに従来では、サイディング材を、釘
やボルトなどで胴縁などに固定するときには、胴縁との
間に0.5〜2mmの隙間ができるように止める必要が
あった。気温の季節変化などによりサイディング材が膨
張または収縮して膨らみや割れを生じさせないためであ
る。しかし、作業者にとっては、全ての釘やボルトなど
に対して、この打ち加減または締め加減の調節を行うこ
とは煩わしいものであった。また、打ち加減または締め
加減にばらつきがあった場合には、サイディング材の膨
張および収縮を吸収することができない箇所が生じてし
まうという課題があった。Conventionally, when the siding material is fixed to the body edge with nails or bolts, it is necessary to stop the siding material so that a gap of 0.5 to 2 mm is formed between the siding material and the body edge. This is because the siding material does not expand or shrink due to seasonal changes in the temperature, and does not cause swelling or cracking. However, it is troublesome for the operator to adjust the setting or tightening of all nails and bolts. In addition, there is a problem that if there is a variation in the setting and tightening of the siding material, there may be places where the expansion and contraction of the siding material cannot be absorbed.
【0019】[0019]
【発明の実施の形態】以下、本発明を、図面に示す実施
形態に基づき説明する。図1は本発明の1実施形態に係
る外断熱建築構造体の要部分解斜視図、図2は図1に示
す構造体の要部断面図である。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below based on embodiments shown in the drawings. FIG. 1 is an exploded perspective view of a main part of an external heat insulating building structure according to an embodiment of the present invention, and FIG. 2 is a cross-sectional view of a main part of the structural body shown in FIG.
【0020】図1に示すように、本実施形態に係る外断
熱建築構造体1は、柱3および間柱5を有し、これら柱
の間に、柱間断熱材7が介在してある。柱間断熱材7
は、たとえばグラスウールなどで構成してある。As shown in FIG. 1, the external heat-insulating building structure 1 according to the present embodiment has columns 3 and studs 5, and inter-column heat insulating materials 7 are interposed between these columns. Post insulation 7
Is made of, for example, glass wool.
【0021】これら柱3,5および柱間断熱材7の屋外
側に、無機系の外断熱材層9が配置してある。外断熱材
層9は、たとえば炭酸カルシウムを主成分とする無機質
系の硬質軽量発泡板で構成してある。具体的には、不燃
材または準不燃材として認定されているフジ化成工業株
式会社製のロックセルボード(登録商標)などが用いら
れる。An inorganic outer heat insulating material layer 9 is arranged on the outdoor side of the pillars 3, 5 and the inter-pillar heat insulating material 7. The outer heat insulating material layer 9 is made of, for example, an inorganic hard lightweight foamed board mainly composed of calcium carbonate. Specifically, a lock cell board (registered trademark) manufactured by Fuji Kasei Kogyo Co., Ltd., which is certified as a noncombustible material or a quasi-noncombustible material, is used.
【0022】外断熱材層9の屋外側に、合成樹脂製のサ
イディング材2が張り巡らされ、これらサイディング材
2を、釘50などで、外断熱材層9を貫通して柱3,5
に打ち込むことで、サイディング材2の取り付けと、外
断熱材層9の取り付けとを同時に行っている。A siding material 2 made of synthetic resin is stretched on the outdoor side of the outer heat insulating material layer 9, and the siding material 2 is passed through the outer heat insulating material layer 9 with a nail 50 or the like, and the columns 3, 5 are formed.
The mounting of the siding material 2 and the mounting of the outer heat insulating material layer 9 are performed simultaneously.
【0023】図1に示すように、本実施形態に係るサイ
ディング材2は、略水平方向に伸びる凹凸模様部4を有
する。凹凸模様部4の数は、特に限定されず、1以上形
成される。As shown in FIG. 1, the siding material 2 according to the present embodiment has a concavo-convex pattern portion 4 extending substantially in the horizontal direction. The number of the concavo-convex pattern portions 4 is not particularly limited, and one or more are formed.
【0024】本実施形態に係るサイディング材2は、そ
の上端部に、取付板部(上端取付部)10が一体成形し
てあり、その取付板部10には、略水平方向に沿って細
長い吊り下げ孔12が所定間隔で形成してある。In the siding material 2 according to the present embodiment, a mounting plate portion (upper end mounting portion) 10 is integrally formed at an upper end portion thereof, and the mounting plate portion 10 has a slender suspension along a substantially horizontal direction. Downholes 12 are formed at predetermined intervals.
【0025】取付板部10の下側には、図2に示すよう
に、上側に配置される他のサイディング材2の下端部に
形成された下端フック部20が覆い被さるように係止す
る下向きの隠れ凹所18が形成された膨出部16が一体
に形成してある。サイディング材2の下端部には、図2
に示すように、下側に配置される他のサイディング材2
の膨出部16に形成された隠れ凹所18に係止する下端
フック部20が形成してある。As shown in FIG. 2, a lower hook portion 20 formed at a lower end portion of another siding material 2 disposed on the upper side is locked downward so as to cover the lower side of the mounting plate portion 10, as shown in FIG. The bulging portion 16 in which the hidden recess 18 is formed is integrally formed. At the lower end of the siding material 2, FIG.
The other siding material 2 arranged on the lower side as shown in FIG.
The lower end hook portion 20 is formed to be locked in the hidden recess 18 formed in the bulging portion 16 of FIG.
【0026】本実施形態では、サイディング材2は、塩
化ビニル樹脂を用いて共押し出しの二層構造とし、基層
部は、リサイクル材を主成分とする低コスト樹脂コンパ
ウンド材を用いて構成し、表層部は、耐候性に優れたバ
ージン樹脂コンパウンド材を用いて構成してある。本実
施形態の取付板部10、膨出部16、隠れ凹所18およ
び下端フック部20は、押出成形により、サイディング
材2を成形する際に一体に成形することができる。In the present embodiment, the siding material 2 has a two-layer structure of co-extrusion using a vinyl chloride resin, and the base layer portion is made of a low-cost resin compound material mainly composed of recycled material. The part is formed using a virgin resin compound material having excellent weather resistance. The mounting plate part 10, the bulging part 16, the hidden recess part 18, and the lower end hook part 20 of the present embodiment can be integrally formed when the siding material 2 is formed by extrusion.
【0027】本実施形態において、サイディング材2の
施工に際しては、まず、外断熱材層9を、新築すべき柱
3および5の屋外側、または補修すべき壁面に張り巡ら
す。In the present embodiment, when the siding material 2 is applied, first, the outer heat insulating material layer 9 is stretched on the outdoor side of the pillars 3 and 5 to be newly constructed or the wall surface to be repaired.
【0028】次に、図2に示すように、外断熱材層9の
下側外面から順に、サイディング材2を外断熱材層9の
外面に取り付ける。その際に、図1に示すように、柱
3,5の位置に対応する吊り下げ孔12へ釘50を通
し、外断熱材層9を貫通させて、柱3,5へ釘50を打
ち付け、サイディング材2を吊り下げ保持する。なお、
釘50の代わりにビスなどを用いても良い。Next, as shown in FIG. 2, the siding material 2 is attached to the outer surface of the outer heat insulating material layer 9 in order from the lower outer surface of the outer heat insulating material layer 9. At that time, as shown in FIG. 1, the nail 50 is passed through the hanging holes 12 corresponding to the positions of the columns 3 and 5, the outer heat insulating material layer 9 is penetrated, and the nail 50 is driven into the columns 3 and 5. The siding material 2 is suspended and held. In addition,
A screw or the like may be used instead of the nail 50.
【0029】その後、サイディング材2の上端取付板部
10の下側に形成された膨出部16の隠れ凹所18に、
図2に示すように、上側に配置される他のサイディング
材2の下端部に形成された下端フック部20を係止させ
る。その状態で、当該他のサイディング材2の上端部に
形成された上端取付板部10を、前述した手法と同様な
手法により、釘50を用いて外断熱材層9の外面で、柱
3,5に対して吊り下げ保持する。このような動作を繰
り返すことにより、サイディング材2を壁に張り巡ら
し、外断熱建築構造体1を得ることができる。Thereafter, a hidden recess 18 of the bulging portion 16 formed below the upper end mounting plate portion 10 of the siding material 2
As shown in FIG. 2, the lower hook 20 formed at the lower end of the other siding material 2 disposed on the upper side is locked. In this state, the upper end mounting plate portion 10 formed on the upper end portion of the other siding material 2 is fixed on the outer surface of the outer heat insulating material layer 9 with the nail 50 by using a method similar to the method described above. 5 and hold it suspended. By repeating such an operation, the siding material 2 can be stretched around the wall, and the outer heat-insulating building structure 1 can be obtained.
【0030】本実施形態に係る外断熱建築構造体1で
は、サイディング材2は、釘50などを用いて外断熱材
層9を貫通させて柱3,5に直接に取り付けられ、その
結果、外断熱材層9も、胴縁や連結スペーサを用いるこ
となく柱3,5に固定される。サイディング材2は、合
成樹脂で構成してあるので、軽量であり、施工に際し
て、胴縁や連結スペーサが不要であり、建築に手間がか
からず、建築費が安価である。また、胴縁や連結スペー
サが不要であることから、壁の総厚が薄く、外構空間を
広くとれる。また、サイディング材2が合成樹脂製であ
るために、耐水性にも優れている。しかも、無機系の外
断熱材層9を有しているので、防火性および断熱性に優
れている。In the outer heat-insulating building structure 1 according to the present embodiment, the siding material 2 is directly attached to the columns 3 and 5 by penetrating the outer heat-insulating material layer 9 using a nail 50 or the like. The heat insulating material layer 9 is also fixed to the columns 3 and 5 without using a trunk or a connecting spacer. Since the siding material 2 is made of a synthetic resin, the siding material 2 is lightweight, does not require a rim or a connecting spacer at the time of construction, does not require much labor for construction, and has low construction costs. Further, since the trunk edge and the connecting spacer are not required, the total thickness of the wall is thin, and the external space can be widened. Further, since the siding material 2 is made of a synthetic resin, it has excellent water resistance. Moreover, since it has the inorganic outer heat insulating material layer 9, it is excellent in fire prevention and heat insulation.
【0031】さらに、合成樹脂製のサイディング材2が
外断熱材層9を介して柱3,5に固定してあるため、サ
イディング材2を、釘50などで、打ち加減の調節を考
慮せずに、比較的に強く柱3,5に取り付けることがで
きる。外断熱材層9が緩衝作用を発揮し、使用に際して
のサイディング材2の膨張および収縮を吸収するからで
ある。したがって、温度変化によるサイディング材2の
熱伸縮を有効に吸収することができ、サイディング材2
に割れやヒビなどが生じることを有効に防止することが
できる。Further, since the siding material 2 made of a synthetic resin is fixed to the columns 3 and 5 via the outer heat insulating material layer 9, the siding material 2 is not taken into consideration with the nail 50 or the like without taking into account the adjustment of the driving force. In addition, it can be attached to the columns 3 and 5 relatively strongly. This is because the outer heat insulating material layer 9 exerts a buffering function and absorbs expansion and contraction of the siding material 2 during use. Therefore, thermal expansion and contraction of the siding material 2 due to temperature change can be effectively absorbed, and the siding material 2
It is possible to effectively prevent cracks, cracks, and the like from being generated in the steel.
【0032】さらにまた、サイディング材2の下端に形
成してある下端フック部20は、それより下側に配置さ
れるサイディング材2の膨出部16に形成してある下向
きの隠れ凹所18に係止させることができる。したがっ
て、サイディング材2の上端取付部10は、それより上
側に配置されるサイディング材2の下端フック部20に
より外部が覆われ、サイディング材2の見栄えも向上す
る。Further, the lower end hook portion 20 formed at the lower end of the siding material 2 is provided with a downwardly facing concave recess 18 formed at the bulging portion 16 of the siding material 2 disposed below. Can be locked. Therefore, the outer end of the upper end mounting portion 10 of the siding material 2 is covered by the lower end hook portion 20 of the siding material 2 disposed thereabove, and the appearance of the siding material 2 is also improved.
【0033】なお、本発明は、上述した実施形態に限定
されるものではなく、本発明の範囲内で種々に改変する
ことができる。たとえば、上述した実施形態では、柱
3,5間に断熱材7を配置したが、本発明では、断熱材
7は、かならずしも配置しなくても良い。The present invention is not limited to the above-described embodiment, but can be variously modified within the scope of the present invention. For example, in the above-described embodiment, the heat insulating material 7 is disposed between the columns 3 and 5, but in the present invention, the heat insulating material 7 does not necessarily have to be disposed.
【0034】[0034]
【発明の効果】以上説明してきたように、本発明によれ
ば、施工に際して、胴縁や連結スペーサが不要であり、
建築に手間がかからず、建築費が安価であり、壁の総厚
が薄く、外構空間を広くとれ、耐水性と耐久性に優れた
外断熱建築構造体を提供することができる。本発明の外
断熱建築構造体は、特に寒冷地の建築物に適用して好適
である。As described above, according to the present invention, a rim and a connecting spacer are not required at the time of construction.
It is possible to provide an external heat-insulating building structure that does not require much labor for construction, has low construction costs, has a small total wall thickness, can have a wide exterior space, and has excellent water resistance and durability. The outer heat-insulating building structure of the present invention is particularly suitable for application to buildings in cold regions.
【図1】 図1は本発明の1実施形態に係る外断熱建築
構造体の要部分解斜視図である。FIG. 1 is an exploded perspective view of a main part of an external heat-insulating building structure according to an embodiment of the present invention.
【図2】 図2は図1に示す構造体の要部断面図であ
る。FIG. 2 is a sectional view of a main part of the structure shown in FIG.
1… 外断熱建築構造体 2… サイディング材 3,5… 柱 7… 柱間断熱材 9… 外断熱材層 50… 釘 DESCRIPTION OF SYMBOLS 1 ... Outer insulation building structure 2 ... Siding material 3, 5 ... Pillar 7 ... Insulation material between pillars 9 ... Outer insulation material layer 50 ... Nail
───────────────────────────────────────────────────── フロントページの続き (72)発明者 矢田 誠規 東京都港区芝公園二丁目4番1号 ゼオン 化成株式会社内 (72)発明者 黒田 英志 東京都港区芝公園二丁目4番1号 ゼオン 化成株式会社内 (72)発明者 福島 明 北海道札幌市南区真駒内上町5丁目3−6 (72)発明者 廣田 誠一 北海道札幌市西区西野3条10丁目7−12− 601 Fターム(参考) 2E001 DD01 DE01 FA04 GA05 GA12 GA44 HA22 HA32 HA33 HD02 HD04 HD08 HD12 HD13 HF11 HF12 2E002 FB10 FB24 GA01 HA03 MA22 MA34 MA38 2E110 AA02 AB04 AB22 BA02 CA03 CA25 DB22 DC12 GA24Y GA33W GA33Y GA42Y GB12Y GB17Y GB19Y GB22Y GB42W GB43W GB44W GB46W GB49Y GB53Y ──────────────────────────────────────────────────続 き Continuing on the front page (72) Inventor Seiki Yada 2-4-1 Shiba Park, Minato-ku, Tokyo Inside Zeon Kasei Co., Ltd. (72) Eiji Kuroda 2-4-1 Shiba Park, Minato-ku, Tokyo No. Zeon Kasei Co., Ltd. (72) Inventor Akira Fukushima 5-3-6 Makomanai Kamimachi, Minami-ku, Sapporo, Hokkaido (72) Inventor Seiichi Hirota 3-7-110-601 Nishino, Nishi-ku, Sapporo, Hokkaido F-term (reference) ) 2E001 DD01 DE01 FA04 GA05 GA12 GA44 HA22 HA32 HA33 HD02 HD04 HD08 HD12 HD13 HF11 HF12 2E002 FB10 FB24 GA01 HA03 MA22 MA34 MA38 2E110 AA02 AB04 AB22 BA02 CA03 CA25 DB22 DC12 GA24Y GA33W GA33Y GA42Y GB12 GB43 GB19 GB GB GB GB GB GB GB GB GB GB GB
Claims (6)
成樹脂製サイディング材が、前記柱に対して固定してあ
ることを特徴とする外断熱建築構造体。1. An external heat insulating building structure, wherein a siding material made of synthetic resin is fixed to the column outside the column via an external heat insulating material layer.
れている請求項1に記載された外断熱建築構造体。2. The external heat-insulating building structure according to claim 1, wherein the external heat-insulating material layer is made of a flame-retardant heat-insulating material.
れている請求項1に記載された外断熱建築構造体。3. The external heat insulating building structure according to claim 1, wherein the external heat insulating material layer is made of an inorganic heat insulating material.
れている請求項1に記載された外断熱建築構造体。4. The external heat insulating building structure according to claim 1, wherein the external heat insulating material layer is made of an inorganic fiber material.
の複合体である請求項1に記載された外断熱建築構造
体。5. The external heat insulating building structure according to claim 1, wherein the siding material made of synthetic resin is a composite of synthetic resin.
ル樹脂から構成されている請求項1に記載された外断熱
建築構造体。6. The external heat-insulating building structure according to claim 1, wherein the siding material made of synthetic resin is made of vinyl chloride resin.