JP2001315259A - Decorative board - Google Patents
Decorative boardInfo
- Publication number
- JP2001315259A JP2001315259A JP2000138522A JP2000138522A JP2001315259A JP 2001315259 A JP2001315259 A JP 2001315259A JP 2000138522 A JP2000138522 A JP 2000138522A JP 2000138522 A JP2000138522 A JP 2000138522A JP 2001315259 A JP2001315259 A JP 2001315259A
- Authority
- JP
- Japan
- Prior art keywords
- synthetic resin
- decorative
- paper
- decorative board
- lubricant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、建具や家具、什
器、床材等の建装材用途の化粧板に関するものであり、
特に耐摩耗性や耐スクラッチ性が要求される用途に好適
な化粧板に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative board for use in building materials such as fittings, furniture, furniture, flooring, and the like.
In particular, the present invention relates to a decorative board suitable for applications requiring wear resistance and scratch resistance.
【０００２】[0002]
【従来の技術】従来のこの種の化粧板としては、合板等
の木質基材の表面に、天然木を薄くスライスした突板を
貼合せ、その上に表面保護のための合成樹脂による塗装
を施した化粧板などが代表的なものである。2. Description of the Related Art As a conventional decorative board of this kind, a veneer obtained by thinly slicing natural wood is attached to the surface of a wood base material such as plywood, and a synthetic resin coating for surface protection is applied thereon. Decorative boards and the like are typical.
【０００３】この化粧板は、天然木に由来する突板を使
用しているために天然の木目による意匠性に優れるこ
と、表面に傷がついてしまった場合にもへこみはするも
のの大きな問題にはなりにくいことなどの長所がある。This decorative veneer is excellent in design by natural wood grain due to the use of a veneer derived from natural wood. Even if the surface is scratched, it becomes a major problem, though it is dented. There are advantages such as being difficult.
【０００４】しかしその反面、短所としては、天然木の
原木の個体差や節、割れ等による品質のバラツキが大き
いことや、耐候性などの物性、近年の原料供給不安など
を挙げることができる。[0004] On the other hand, however, the disadvantages include large variations in quality due to individual differences, knots, cracks, and the like in the raw wood, physical properties such as weather resistance, and uncertainty in the supply of raw materials in recent years.
【０００５】上記した化粧板における天然木の突板に代
えて、原紙に木目模様等の印刷を施した化粧紙を使用し
た化粧板も、既に広く用いられている。[0005] In place of the veneer of natural wood in the decorative board described above, a decorative board using decorative paper in which a base paper is printed with a grain pattern or the like has already been widely used.
【０００６】係る化粧板にあっては、予め表面に合成樹
脂による塗装を施した化粧紙を木質基材に貼着する場合
もあるが、特に耐摩耗性や耐スクラッチ性が要求される
用途には、塗装の厚塗りが可能で表面物性に優れた化粧
板が容易に得られる、木質基材への化粧紙の貼着後に塗
装を施す場合が多い。In such decorative boards, decorative paper whose surface is coated with a synthetic resin in advance may be adhered to a wooden substrate, but it is particularly suitable for applications requiring wear resistance and scratch resistance. Is often applied after sticking decorative paper to a wooden substrate, which makes it possible to easily apply a thick decorative coating and obtain a decorative board having excellent surface properties.
【０００７】この化粧板は、意匠性を決定する化粧紙が
工業製品であることから品質が安定していること、天然
木等による天然の意匠の欠陥の人工的な修正や、天然に
は存在しない人工的な意匠（例えば抽象柄など）の付与
なども可能であり、色柄のバリエーションが自在である
こと、天然資源量や地理的条件などに左右されることが
なく、安定的な供給が可能であることなどの長所があ
る。[0007] This decorative board has a stable quality because decorative paper that determines the design is an industrial product, artificially corrects natural design defects caused by natural wood and the like, and does not exist in nature. It is also possible to provide artificial designs (for example, abstract patterns, etc.) that do not need to be used. The variety of colors and patterns is free, and stable supply is not affected by the amount of natural resources and geographical conditions. There are advantages such as being possible.
【０００８】また、係る化粧板の表面に、木目柄、抽象
柄などのエンボス加工を施すことで、立体感を付与し、
更なる意匠性の向上を図ることも行われている（特開平
８−３１８５０６号公報）。In addition, the surface of the decorative board is embossed with a wood grain pattern, an abstract pattern or the like to give a three-dimensional effect.
Further improvement of the design is also performed (Japanese Patent Application Laid-Open No. 8-318506).
【０００９】しかしその反面、短所としては、化粧紙が
本質的に天然木質繊維の絡み合い集合体である紙からな
ることから、紙間強度が弱く紙間剥離を発生する場合が
あること、摩耗や特にスクラッチに弱く傷が付き易いこ
と、水に濡れると強度が著しく低下することなどを挙げ
ることができる。[0009] On the other hand, however, the disadvantages are that the decorative paper is essentially made of paper which is an entangled aggregate of natural wood fibers, so that the strength between the papers is weak and the paper may be peeled off. In particular, it can be mentioned that the scratch is weak and easily damaged, and that the strength is significantly reduced when wet with water.
【００１０】[0010]
【発明が解決しようとする課題】本発明は、従来の技術
における上記の問題点を解決する目的でなされたもので
あり、化粧紙による品質の安定した意匠が付与された化
粧板でありながら、層間強度が強く、耐摩耗性や耐スク
ラッチ性にも優れ、耐水性も向上した化粧板を提供しよ
うとするものである。DISCLOSURE OF THE INVENTION The present invention has been made for the purpose of solving the above-mentioned problems in the prior art, and is a decorative board provided with a design of stable quality using decorative paper. An object of the present invention is to provide a decorative board having high interlayer strength, excellent wear resistance and scratch resistance, and improved water resistance.
【００１１】[0011]
【課題を解決するための手段】上記の目的を達成するた
めに、本発明の請求項１によれば、木質基材の表面に化
粧紙を貼着し、該化粧紙上に合成樹脂による保護層を設
けてなる化粧板において、前記化粧紙は合成樹脂による
シーラー処理を施した原紙を使用した化粧紙であり、且
つ、前記合成樹脂による保護層には無機材料からなる減
摩剤が添加されていることを特徴とする化粧板である。In order to achieve the above object, according to the first aspect of the present invention, a decorative paper is attached to the surface of a wooden base material, and a protective layer made of a synthetic resin is formed on the decorative paper. Wherein the decorative paper is a decorative paper using base paper subjected to a sealer treatment with a synthetic resin, and a lubricant made of an inorganic material is added to the protective layer of the synthetic resin. It is a decorative plate characterized by having.
【００１２】また、本発明の請求項２によれば、前記合
成樹脂による保護層は複数層からなり、そのうち最外層
を除く層の少なくとも１層に、減摩剤が添加されている
ことを特徴とする。According to a second aspect of the present invention, the protective layer made of the synthetic resin comprises a plurality of layers, and at least one of the layers excluding the outermost layer contains a lubricant. And
【００１３】また、本発明の請求項３によれば、前記合
成樹脂による保護層に代えて、無機材料からなる減摩剤
が添加された合成樹脂による塗装を後に施すための再塗
装性の合成樹脂層が設けられていることを特徴とする。According to a third aspect of the present invention, in place of the protective layer made of the synthetic resin, a repaintable synthetic resin for applying a synthetic resin to which a lubricant made of an inorganic material is added later. It is characterized in that a resin layer is provided.
【００１４】また、本発明の請求項４によれば、前記再
塗装性の合成樹脂層は、表面に研磨処理が施されている
ことを特徴とする。According to a fourth aspect of the present invention, the repaintable synthetic resin layer has a surface subjected to a polishing treatment.
【００１５】また、本発明の請求項５によれば、前記再
塗装性の合成樹脂層の上に、無機材料からなる減摩剤が
添加された合成樹脂による塗装が施されていることを特
徴とする。According to a fifth aspect of the present invention, the repaintable synthetic resin layer is coated with a synthetic resin to which a lubricant made of an inorganic material is added. And
【００１６】また、本発明の請求項６によれば、前記無
機材料からなる減摩剤が添加された合成樹脂による塗装
の上に、更に無機材料からなる減摩剤が添加されていな
い合成樹脂による塗装が施されていることを特徴とす
る。According to a sixth aspect of the present invention, there is provided a synthetic resin to which a lubricant made of an inorganic material is not further added, on a coating of the synthetic resin to which a lubricant made of an inorganic material is added. It is characterized by being painted by.
【００１７】また、本発明の請求項７によれば、前記減
摩剤の平均粒径が１０〜１００μｍであることを特徴と
する。According to a seventh aspect of the present invention, the lubricant has an average particle size of 10 to 100 μm.
【００１８】また、本発明の請求項８によれば、表面に
エンボス加工が施されていることを特徴とする。Further, according to claim 8 of the present invention, the surface is embossed.
【００１９】[0019]
【発明の実施の形態】図面に基づき本発明を詳細に説明
すれば、図１に示すように、木質基材１の表面に、合成
樹脂によるシーラー処理３を施した原紙２に、木目等の
適宜の柄の絵柄インキ層４を施した化粧紙５を貼着し、
該化粧紙５の表面に、無機材料からなる減摩剤が添加さ
れた合成樹脂による保護層６が設けられている化粧板で
ある。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described in detail with reference to the drawings. As shown in FIG. 1, a base paper 2 obtained by subjecting a surface of a wooden base material 1 to a sealer treatment 3 with a synthetic resin, Affix a decorative paper 5 provided with a pattern ink layer 4 of an appropriate pattern,
The decorative sheet has a protective layer 6 made of a synthetic resin to which a lubricant made of an inorganic material is added on the surface of the decorative paper 5.
【００２０】無機材料からなる減摩剤が添加された合成
樹脂による保護層６の表面には、無機材料からなる減摩
剤が添加されていない合成樹脂による保護層７が設けら
れていてもよい。また、この化粧板の表面には、エンボ
ス加工８が施されていてもよいし、エンボス加工８は施
されていなくてもよい（図２）。A protective layer 7 made of a synthetic resin to which a lubricant made of an inorganic material is not added may be provided on the surface of the protective layer 6 made of a synthetic resin to which a lubricant made of an inorganic material is added. . Further, the surface of the decorative plate may be embossed 8 or may not be embossed 8 (FIG. 2).
【００２１】木質基材１としては、例えば天然木の単板
や合板、集成材、中密度繊維板（ＭＤＦ）、高密度繊維
板（ＨＤＦ）、パーティクルボード等を使用することが
できる。As the wood substrate 1, for example, a veneer, a plywood, a laminated wood, a medium-density fiberboard (MDF), a high-density fiberboard (HDF), a particle board and the like can be used.
【００２２】化粧板の表面にエンボス加工８を施す場合
には、安定したエンボス品質が得られるように、各種の
欠陥や品質のバラツキのない、均質性の高い材料を使用
するのが良く、中密度繊維板（ＭＤＦ）に代表される木
質繊維板を使用することが最も好適である。When the embossing 8 is performed on the surface of the decorative board, it is preferable to use a material having high homogeneity without various defects and quality variations so as to obtain stable embossing quality. It is most preferable to use a wood fiber board represented by a density fiber board (MDF).
【００２３】化粧紙５の原紙２は一般的な化粧紙用の原
紙であれば良く、坪量１３〜１００ｇ／ｍ2の範囲の原
紙で、建材用紙間強化紙が最も好ましいが、建材用プリ
ント用紙その他の用途の原紙であっても良く、また樹脂
含浸紙であっても良い。The base paper 2 of the decorative paper 5 may be a base paper for general decorative paper, and is a base paper having a basis weight of 13 to 100 g / m 2. It may be base paper for paper or other uses, or may be resin-impregnated paper.
【００２４】上記建材用紙間強化紙としては、原料とな
る木材パルプの叩解割合を強くしてフィブリル化を進め
たパルプ繊維を用い、アクリルアマイド等の紙間強化剤
や湿潤強度剤の添加量を増やして抄紙することで、紙間
強度を高めた紙などを使用することができる。As the above-mentioned reinforcing paper between papers for building materials, pulp fibers obtained by increasing the beating rate of wood pulp as a raw material and fibrillating the fiber are used, and the amount of a paper reinforcing agent such as acrylamide or a wet strength agent is added. By increasing the number of papers, it is possible to use paper with increased inter-sheet strength.
【００２５】上記原紙２の表面には、合成樹脂によるシ
ーラー処理３が施される。シーラー処理３に使用する合
成樹脂は、一般的にはウレタン系、アクリル系などの２
液硬化型樹脂が好ましいが、その他の樹脂系であっても
良く、油性であっても水性であっても良い。The surface of the base paper 2 is subjected to a sealer treatment 3 using a synthetic resin. The synthetic resin used for the sealer treatment 3 is generally a urethane-based or acrylic-based synthetic resin.
Liquid-curable resins are preferred, but other resin-based resins may be used, such as oily or aqueous.
【００２６】シーラー処理３に使用する合成樹脂は１液
配合であっても良く、イソシアネート等の硬化剤として
用いられている材料を１液塗工しても良い。The synthetic resin used in the sealer treatment 3 may be a one-component compound, or a one-component material used as a curing agent such as isocyanate may be applied.
【００２７】さらに、原紙中の樹脂比率を高め、ウェッ
ト、ドライを問わず、紙間強度の向上を図るために、塗
工時の樹脂固形分は高くても低粘度で浸透性の良い樹脂
を使用することが好ましい。Further, in order to increase the resin ratio in the base paper and to improve the paper-to-paper strength regardless of whether the resin is wet or dry, a resin having low viscosity and good permeability even when the resin solid content is high at the time of coating is used. It is preferred to use.
【００２８】樹脂固形分は、粘度や浸透性等の問題か
ら、塗工時で１０〜５０％の範囲内が好ましい。無溶剤
タイプの樹脂など固形分１００％の樹脂は一般に粘度が
高いので、使用する場合には塗工時に加熱保温するなど
して低粘度に保つ注意が必要である。The resin solid content is preferably in the range of 10 to 50% at the time of coating, due to problems such as viscosity and permeability. Since a resin having a solid content of 100% such as a non-solvent type resin generally has a high viscosity, when using it, it is necessary to pay attention to maintain a low viscosity by, for example, heating and maintaining the temperature during coating.
【００２９】硬化方式は、熱硬化を初めとし、紫外線硬
化又は電子線硬化等、種々の方式を問わないが、その上
から印刷インキにて絵柄インキ層４を印刷するために、
リコート性が必要とされるから注意を要する。The curing method may be any of various methods such as thermal curing, ultraviolet curing, or electron beam curing. In order to print the pattern ink layer 4 with printing ink,
Care must be taken because recoatability is required.
【００３０】絵柄インキ層４は、本発明において特に限
定されるものではなく、通常の化粧紙用の印刷インキを
使用して、例えばグラビア印刷法等の、通常の方法で印
刷すれば良い。絵柄の種類も、例えば木目柄、抽象柄
等、所望により任意であり、特に限定されない。The pattern ink layer 4 is not particularly limited in the present invention, and may be printed by a usual method such as a gravure printing method using a usual printing ink for decorative paper. The type of the pattern is also arbitrary as desired, for example, a wood grain pattern, an abstract pattern, etc., and is not particularly limited.
【００３１】合成樹脂による保護層６は、化粧板の表面
を外的な物理的又は化学的作用から保護するために設け
るものであり、本発明の化粧板では特に、優れた耐摩耗
性や耐スクラッチ性を得るために、無機材料からなる減
摩剤を添加したものである。The protective layer 6 made of a synthetic resin is provided to protect the surface of the decorative board from external physical or chemical action, and in the decorative board of the present invention, particularly, it has excellent abrasion resistance and resistance to abrasion. In order to obtain scratch resistance, a lubricant made of an inorganic material is added.
【００３２】無機材料からなる減摩剤は、例えばアルミ
ナや炭化珪素などからなるもので、平均粒径１０〜１０
０μｍのものが良い。添加量は、合成樹脂１００重量部
当たり２〜３０重量部程度とするのが良い。The lubricant made of an inorganic material is made of, for example, alumina or silicon carbide, and has an average particle diameter of 10 to 10.
The one having 0 μm is good. The addition amount is preferably about 2 to 30 parts by weight per 100 parts by weight of the synthetic resin.
【００３３】無機材料からなる減摩剤の形状は、不定
形、鱗片形、球形、多面体形などのいずれでも良いが、
不定形よりも鱗片形や球形、多面体形などの方が耐摩耗
効果が高いので好ましい。The shape of the lubricant made of an inorganic material may be any of an irregular shape, a scale shape, a spherical shape and a polyhedral shape.
A scaly shape, a spherical shape, a polyhedral shape, and the like are preferable to an amorphous shape because they have a higher abrasion resistance effect.
【００３４】無機材料からなる減摩剤は、合成樹脂によ
る保護層を複数層（６、７）設けた内の最外層（７）で
はない層に添加することが望ましい。最外層に添加しな
い理由は、無機材料からなる減摩剤の樹脂塗膜上での保
持力の強化と、樹脂塗膜の表面状態の改善、摩耗効果の
低減が挙げられる。The lubricant made of an inorganic material is desirably added to a layer other than the outermost layer (7) among a plurality of protective layers made of a synthetic resin (6, 7). The reason why it is not added to the outermost layer is to enhance the holding power of the lubricant made of an inorganic material on the resin coating, to improve the surface condition of the resin coating, and to reduce the abrasion effect.
【００３５】樹脂塗膜上での保持力の強化とは、無機材
料からなる減摩剤が合成樹脂による保護層６の樹脂塗膜
の平均表面から突出していると、外力により樹脂塗膜か
ら離脱し、これが化粧板の表面を擦られることで傷が付
くという問題があるためである。The strengthening of the holding force on the resin coating means that the lubricant made of an inorganic material protrudes from the average surface of the resin coating of the protective layer 6 made of synthetic resin, and is separated from the resin coating by external force. However, this is because there is a problem that the surface of the decorative board is rubbed, thereby causing damage.
【００３６】無機材料からなる減摩剤を添加した合成樹
脂による保護層６の上に、無機材料からなる減摩剤を添
加していない合成樹脂による保護層７を設けることで、
前者の樹脂塗膜の平均表面から突出した減摩剤粒子が後
者の樹脂塗膜によって被覆され、化粧板の表面から離脱
しにくくなり、従って離脱粒子による表面の傷付きも防
止することができる。By providing a protective layer 7 made of a synthetic resin to which a lubricant made of an inorganic material is not added, on a protective layer 6 made of a synthetic resin to which a lubricant made of an inorganic material is added,
Lubricant particles protruding from the average surface of the former resin coating film are covered with the latter resin coating film, making it difficult to separate from the surface of the decorative board, and thus preventing the surface from being damaged by the separated particles.
【００３７】樹脂塗膜の表面状態の改善とは、最外層の
合成樹脂による保護層７に無機材料からなる減摩剤を添
加すると、その粒径との関係から、樹脂塗膜の表面にピ
ンホールやスジ等が発生し易くなり、表面状態が悪化す
るという問題があるためである。The improvement of the surface condition of the resin coating means that when a lubricant made of an inorganic material is added to the outermost protective layer 7 made of synthetic resin, a pin is formed on the surface of the resin coating due to its particle size. This is because there is a problem that holes and streaks are easily generated and the surface state is deteriorated.
【００３８】無機材料からなる減摩剤を添加した合成樹
脂による保護層６の上に、無機材料からなる減摩剤を添
加していない合成樹脂による保護層７を設けることで、
前者の表面にピンホールやスジ等の欠陥が発生すること
があっても、それらの欠陥を後者によって埋めることが
でき、得られる化粧板の表面状態を改善することができ
る。By providing a protective layer 7 made of a synthetic resin to which a lubricant made of an inorganic material is not added, on a protective layer 6 made of a synthetic resin to which a lubricant made of an inorganic material is added,
Even if defects such as pinholes and streaks occur on the former surface, those defects can be filled by the latter, and the surface condition of the decorative board obtained can be improved.
【００３９】摩耗効果の低減とは、合成樹脂による保護
層６に無機材料からなる減摩剤を添加することで化粧板
自体の耐摩耗性は向上しているが、逆に化粧板がこれに
接するものを削ってしまうという問題があるためであ
る。The reduction of the abrasion effect means that the abrasion resistance of the decorative board itself is improved by adding a lubricant made of an inorganic material to the protective layer 6 made of a synthetic resin. This is because there is a problem in that the objects that come into contact are cut off.
【００４０】具体的には、仮にこの化粧板が机の天板や
書棚の棚板等に使用されると、その上に置かれた本の表
面を削ってしまい、表紙の文字が見えにくくなってしま
う。また、雑巾掛けをした際に、雑巾の繊維を削ってし
まい、雑巾掛けをする度に埃が発生してしまう。Specifically, if this decorative board is used for a desk top plate, a book shelf shelf, or the like, the surface of a book placed on the top plate will be scraped, and the characters on the cover will become invisible. Would. In addition, when the rag is ragged, the fibers of the rag are scraped, and dust is generated every time the rag is ragged.
【００４１】無機材料からなる減摩剤を添加した合成樹
脂による保護層６の上に、無機材料からなる減摩剤を添
加していない合成樹脂による保護層７を設けることで、
前者の樹脂塗膜の平均表面から突出した無機材料からな
る減摩剤は、後者の樹脂塗膜によって被覆されることか
ら、化粧板に接するものが無機材料からなる減摩剤に直
接接することはなくなり、その表面が削られるという問
題を改善することができる。By providing a protective layer 7 made of a synthetic resin to which a lubricant made of an inorganic material is not added, on a protective layer 6 made of a synthetic resin to which a lubricant made of an inorganic material is added,
Since the former lubricant made of an inorganic material protruding from the average surface of the resin coating is covered with the latter resin coating, it is impossible for the lubricant in contact with the decorative plate to directly contact the lubricant made of the inorganic material. And the problem that the surface is shaved can be improved.
【００４２】合成樹脂による保護層６、７に使用する合
成樹脂としては、強度や硬度、物性などの観点から、硬
化性樹脂を使用することが好ましい。具体的には、例え
ば２液硬化型ウレタン系樹脂、アミノアルキド系樹脂、
メラミン系樹脂、不飽和ポリエステル系樹脂等の熱硬化
性樹脂や、アクリレート系樹脂などの紫外線又は電子線
硬化性樹脂を使用することが好ましい。As the synthetic resin used for the protective layers 6 and 7 made of a synthetic resin, it is preferable to use a curable resin from the viewpoints of strength, hardness and physical properties. Specifically, for example, a two-component curable urethane-based resin, an aminoalkyd-based resin,
It is preferable to use a thermosetting resin such as a melamine resin or an unsaturated polyester resin, or an ultraviolet or electron beam curable resin such as an acrylate resin.
【００４３】これらの合成樹脂には、必要に応じて種々
の添加剤を添加することができる。例えば、無機材料か
らなる減摩剤を添加した合成樹脂による保護層６を形成
するための合成樹脂塗料に、シランカップリング剤を添
加することにより、減摩剤の保持力を向上したり、沈降
防止剤を添加することにより、塗装作業中の減摩剤の沈
降を防止し、塗装作業の安定性を向上したりすることが
できる。Various additives can be added to these synthetic resins as needed. For example, by adding a silane coupling agent to a synthetic resin paint for forming the protective layer 6 made of a synthetic resin to which a lubricant made of an inorganic material has been added, the holding power of the lubricant can be improved or the sedimentation can be improved. By adding the inhibitor, sedimentation of the lubricant during the coating operation can be prevented, and the stability of the coating operation can be improved.
【００４４】本発明の化粧板は、上記した合成樹脂によ
る保護層６、７に代えて、無機材料からなる減摩剤が添
加された合成樹脂による塗装を後に施すための、再塗装
性の合成樹脂層９を設けた構成とすることもできる。The decorative plate of the present invention has a recoating property for applying a synthetic resin to which a lubricating agent made of an inorganic material is added instead of the protective layers 6 and 7 made of the synthetic resin described above. A configuration in which the resin layer 9 is provided may be employed.
【００４５】再塗装性の合成樹脂層９としては、例えば
アクリル系樹脂、ウレタン系樹脂、ポリアミド系樹脂、
ポリエステル系樹脂、繊維素誘導体等からなる合成樹脂
塗料などを使用することができる。As the repaintable synthetic resin layer 9, for example, an acrylic resin, a urethane resin, a polyamide resin,
Synthetic resin paints composed of polyester resins, cellulose derivatives, and the like can be used.
【００４６】更に、再塗装性の合成樹脂層９の表面に、
研磨処理を施すことにより、表面を平滑化すると共に、
再塗装の密着性を向上することもできる。Further, on the surface of the repaintable synthetic resin layer 9,
By performing the polishing process, while smoothing the surface,
The adhesion of repainting can also be improved.
【００４７】この構成の化粧板は、例えば建築現場にお
ける施工後や、家具の製造における組立後などの適宜の
段階に、再塗装性の合成樹脂層９の上に、無機材料から
なる減摩剤が添加された合成樹脂による塗装６が施され
て、実用に供される。The decorative plate having this structure is formed on the repaintable synthetic resin layer 9 at an appropriate stage, for example, after construction at a building site or after assembly in the manufacture of furniture. Is applied with a synthetic resin to which is added, and is put to practical use.
【００４８】なお、前述した合成樹脂による保護層６、
７の場合と同様に、無機材料からなる減摩剤の樹脂塗膜
上での保持力の強化、樹脂塗膜の表面状態の改善、摩耗
効果の低減の観点から、上記無機材料からなる減摩剤が
添加された合成樹脂による塗装６の上に、更に無機材料
からなる減摩剤が添加されていない合成樹脂による塗装
７を施すことが望ましい。The protective layer 6 made of the synthetic resin described above,
As in the case of No. 7, from the viewpoint of enhancing the holding force of the lubricant made of an inorganic material on the resin coating, improving the surface condition of the resin coating, and reducing the abrasion effect, the lubrication made of the inorganic material is used. It is desirable to further apply a coating 7 of a synthetic resin to which a lubricant made of an inorganic material is not added, on the coating 6 of the synthetic resin to which the agent is added.
【００４９】[0049]
【実施例】以下に、本発明の化粧板の具体的な実施例を
挙げ、本発明をより詳細に説明する。EXAMPLES Hereinafter, the present invention will be described in more detail with reference to specific examples of the decorative board of the present invention.
【００５０】実施例１ 坪量３０ｇ／ｍ2の紙間強化紙を原紙としてその表面
に、まず下記組成のアクリルポリオール系イソシアネー
ト硬化反応型シーラーを、固形分が３０％になるように
溶剤希釈し、グラビア印刷法にて乾燥後の塗布量３ｇ／
ｍ2に塗工した。但し、ここでの硬化剤は耐光性を考慮
し、無黄変タイプのヘキサメチレンジイソシアネート
（ＨＭＤＩ）を用いた。Example 1 A paper-reinforced paper having a basis weight of 30 g / m 2 was used as a base paper, and an acrylic polyol-based isocyanate curing reaction type sealer having the following composition was diluted with a solvent so that the solid content was 30%. , Coating amount after drying by gravure printing method 3g /
It was applied to the m 2. However, a non-yellowing type hexamethylene diisocyanate (HMDI) was used as the curing agent in consideration of light resistance.
【００５１】シーラー組成 シーラー主剤 １００重量部 硬化剤（ＨＭＤＩ） ２０重量部 ウレタン溶剤 ３０重量部Sealer composition Sealer base 100 parts by weight Curing agent (HMDI) 20 parts by weight Urethane solvent 30 parts by weight
【００５２】次いで、建材用硝化綿系インキを使用し
て、ベタ印刷と木目柄（若しくは抽象柄）の絵柄印刷と
を施して、化粧紙を作製した。Next, using a nitrifying cotton-based ink for building materials, solid printing and pattern printing of a wood grain pattern (or an abstract pattern) were performed to prepare a decorative paper.
【００５３】この化粧紙を、尿素／酢酸ビニル系接着剤
にて、厚さ２．７ｍｍの中密度繊維板（ＭＤＦ）基材に
貼り合わせた。尿素系接着剤は原紙への浸透が良く、シ
ーラーの効果と併せ、原紙の樹脂比率を増し、紙間を強
化する役割を果たす。但し、ホルマリンの発生問題から
ノンホルマリンタイプを用いた。This decorative paper was bonded to a 2.7 mm thick medium density fiberboard (MDF) substrate with a urea / vinyl acetate adhesive. The urea-based adhesive has good penetration into the base paper, and plays a role of increasing the resin ratio of the base paper and strengthening the paper interval in addition to the effect of the sealer. However, a non-formalin type was used due to the problem of formalin generation.
【００５４】貼り合わせ条件 プリントロールラミネーター １５０℃ φ３００ｍｍ
ロール３本 板基材 約９００×１８００ｍｍ（３×６尺） ２．７
ｍｍ ＭＤＦ 接着剤 尿素・酢ビ混合接着剤 約５５ｇ／ｍ2（５ｇ
／尺2）ｗｅｔ ラインスピード ３０ｍ／ｍｉｎBonding conditions Print roll laminator 150 ° C. φ300 mm
Three rolls Substrate Approx. 900 x 1800 mm (3 x 6 feet) 2.7
mm MDF adhesive urea / vinyl acetate mixed adhesive About 55 g / m 2 (5 g
/ Shaku 2 ) wet line speed 30m / min
【００５５】これを１晩養生後、ロールエンボス機にて
木目柄（若しくは抽象柄）のエンボス模様を形成した。After curing this overnight, a wood-grained (or abstract) embossed pattern was formed using a roll embossing machine.
【００５６】ロールエンボス条件 エンボス圧力 線圧約１５０〜２５０ｋＮ／ｍ（１５０
〜２５０ｋｇｆ／ｃｍ） エンボススピード ３０ｍ／ｍｉｎRoll embossing conditions Embossing pressure Linear pressure About 150 to 250 kN / m (150
Embossing speed 30m / min
【００５７】エンボス模様の形成後、合成樹脂による保
護層の塗工形成を行った。After the formation of the embossed pattern, a protective layer was formed by coating with a synthetic resin.
【００５８】 保護層塗工条件 塗工装置 ３ヘッドロールコーター 塗布量 第１ヘッド 約２２ｇ／ｍ2（２ｇ／尺2）ｗｅｔ 第２・第３ヘッド 約１７ｇ／ｍ2（１．５ｇ／尺2）ｗｅｔProtective Layer Coating Conditions Coating Apparatus 3-Head Roll Coater Coating Amount First Head Approx. 22 g / m 2 (2 g / shaku 2 ) wet Second / Third Head Approx. 17 g / m 2 (1.5 g / shaku 2) ) Wet
【００５９】 第１ヘッド塗工剤組成 ウレタン系主剤（サンディングシーラータイプ） １００重量部 硬化剤（ＨＭＤＩ系） ２５重量部 減摩剤（鱗片形アルミナ、平均粒径２５μｍ） １０重量部 希釈溶剤 適量 粘度 イワタカップ２０〜３５秒First Head Coating Composition Urethane-based base (sanding sealer type) 100 parts by weight Hardener (HMDI-based) 25 parts by weight Lubricant (scale alumina, average particle size 25 μm) 10 parts by weight Diluent solvent Suitable amount Viscosity Iwata cup 20-35 seconds
【００６０】 第２ヘッド塗工剤組成 ウレタン系主剤（サンディングシーラータイプ） １００重量部 硬化剤（ＨＭＤＩ系） ２５重量部 希釈溶剤 適量 粘度 イワタカップ２０〜３５秒Composition of second head coating agent Urethane base agent (sanding sealer type) 100 parts by weight Curing agent (HMDI system) 25 parts by weight Diluent solvent proper amount Viscosity Iwata cup 20 to 35 seconds
【００６１】 第３ヘッド塗工剤組成 ウレタン系主剤（上塗りタイプ） １００重量部 硬化剤（ＨＭＤＩ系） ２５重量部 希釈溶剤 適量 粘度 イワタカップ２０〜３５秒Composition of third head coating agent Urethane-based base material (top coating type) 100 parts by weight Curing agent (HMDI-based) 25 parts by weight Diluent solvent appropriate amount Viscosity Iwata cup 20 to 35 seconds
【００６２】実施例２ 上記実施例１において、エンボス模様の形成後、合成樹
脂による保護層の塗工形成に加え、エンボス模様へのワ
イピング加工を行った。Example 2 In Example 1, after the embossed pattern was formed, wiping to the embossed pattern was performed in addition to coating the protective layer with a synthetic resin.
【００６３】 保護層塗工条件 塗工装置 ３ヘッドロールコーター 塗布量 第１ヘッド 約１７ｇ／ｍ2（１．５ｇ／尺2）ｗｅｔ 第２ヘッド 約２２ｇ／ｍ2（２ｇ／尺2）ｗｅｔ 第３ヘッド 約１７ｇ／ｍ2（１．５ｇ／尺2）ｗｅｔ 但し、第１ヘッド塗工後、第２ヘッド塗工前に、 ワイピング機にてウレタン系インキをワイピングProtective Layer Coating Conditions Coating Apparatus 3-Head Roll Coater Coating Amount 1st head Approx. 17 g / m 2 (1.5 g / shaku 2 ) wet Second head Approx. 22 g / m 2 (2 g / shaku 2 ) wet 3 heads Approx. 17 g / m 2 (1.5 g / size 2 ) wet However, after coating the first head and before coating the second head, wipe the urethane-based ink with a wiping machine.
【００６４】 第１ヘッド塗工剤組成 ウレタン系主剤（サンディングシーラータイプ） １００重量部 硬化剤（ＨＭＤＩ系） １０重量部 希釈溶剤 適量 粘度 イワタカップ２０〜３５秒Composition of First Head Coating Agent Urethane-based base material (sanding sealer type) 100 parts by weight Curing agent (HMDI-based) 10 parts by weight Diluent solvent appropriate amount Viscosity Iwata cup 20 to 35 seconds
【００６５】 第２ヘッド塗工剤組成 ウレタン系主剤（サンディングシーラータイプ） １００重量部 硬化剤（ＨＭＤＩ系） １０重量部 減摩剤（鱗片形アルミナ、平均粒径２５μｍ） ２０重量部 希釈溶剤 適量 粘度 イワタカップ２０〜３５秒Composition of second head coating agent Urethane-based base material (sanding sealer type) 100 parts by weight Hardener (HMDI-based) 10 parts by weight Lubricant (scale alumina, average particle size 25 μm) 20 parts by weight Diluent solvent Suitable amount Viscosity Iwata cup 20-35 seconds
【００６６】 第３ヘッド塗工剤組成 ウレタン系主剤（上塗りタイプ） １００重量部 硬化剤（ＨＭＤＩ系） １０重量部 希釈溶剤 適量 粘度 イワタカップ２０〜３５秒Third Head Coating Composition 100% by weight of urethane base (top coating type) 10 parts by weight of curing agent (HMDI) Diluent solvent Viscosity Iwata cup 20 to 35 seconds
【００６７】[0067]
【発明の効果】本発明の化粧板は、原紙へのシーラー処
理により紙間が強化され、紙間剥離が防止され、耐水性
も向上していることに加え、合成樹脂による保護層への
減摩剤の添加により、耐摩耗性や耐スクラッチ性等の表
面性能も向上しており、こすりキズにも強い化粧板であ
る。According to the decorative sheet of the present invention, in addition to the fact that the space between the sheets is strengthened by the sealer treatment of the base paper, separation between the sheets is prevented, the water resistance is improved, and the reduction of the protective layer by the synthetic resin is achieved. By the addition of a lubricant, the surface performance such as abrasion resistance and scratch resistance is also improved, and the decorative board is resistant to rubbing and scratching.
【００６８】更に、合成樹脂による保護層への減摩剤の
添加により、化粧板に接触する物が摩耗しすぎる問題が
あるところを、複数層からなる合成樹脂による保護層の
最外層以外の層に減摩剤を添加することで、化粧板の上
に置かれた物が減摩剤に直接触れることがなくなり、接
触物が摩耗しすぎることを防ぐことができる。Furthermore, the addition of a lubricating agent to the protective layer made of a synthetic resin causes a problem that an object in contact with a decorative plate is excessively worn. By adding a lubricant to the decorative board, the object placed on the decorative board is prevented from directly contacting the lubricant, so that the contact object can be prevented from being excessively worn.
【００６９】例えば、この化粧板を書棚の棚板に使用し
た際の本の摩耗や、フローリングに使用した際のストッ
キングの伝線、洋服箪笥の敷き板に使用した際の洋服の
毛羽立ちやホコリの発生などは、効果的に防止すること
ができる。For example, when this decorative board is used as a bookcase shelf, a book wears, when it is used for flooring, when it is used as a stocking line, and when it is used as a wardrobe for clothes, it has fluff and dust. Generation can be effectively prevented.
【００７０】その他、突板化粧板と異なり、工業製品で
ある化粧紙を使用することにより、一定の品質の製品の
安定供給が可能であること、柄意匠の様々なバリエーシ
ョンが可能であること、エンボスやワイピング、カラー
コート等による意匠の向上も可能であること、エンボス
機によるＭＤＦ、ＨＤＦ、パーティクルボードなど様々
な木質基材へのムラなく安定したエンボスが可能である
こと等の効果をも併せ持つものである。In addition, unlike decorative veneer, the use of decorative paper, which is an industrial product, enables stable supply of products of a certain quality, enables various variations of pattern designs, and embossing. It also has the effect of improving the design by wiping, color coating, etc., and the ability to emboss evenly and stably on various wood base materials such as MDF, HDF, particle board using an embossing machine. It is.
【図１】本発明の化粧板の実施の形態の一例を示す模式
断面図である。FIG. 1 is a schematic sectional view showing an example of an embodiment of a decorative board of the present invention.
【図２】本発明の化粧板の実施の形態の一例を示す模式
断面図である。FIG. 2 is a schematic cross-sectional view showing an example of an embodiment of the decorative board of the present invention.
【図３】本発明の化粧板の実施の形態の一例を示す模式
断面図である。FIG. 3 is a schematic sectional view showing an example of an embodiment of the decorative board of the present invention.
１ 木質基材 ２ 原紙 ３ 合成樹脂によるシーラー処理 ４ 絵柄インキ層 ５ 化粧紙 ６ 減摩剤が添加された合成樹脂による保護層（塗
装） ７ 減摩剤が添加されていない合成樹脂による保護層
（塗装） ８ エンボス加工 ９ 再塗装性の合成樹脂層Reference Signs List 1 wood base material 2 base paper 3 sealer treatment with synthetic resin 4 picture ink layer 5 decorative paper 6 protective layer of synthetic resin to which lubricant was added (coating) 7 protective layer of synthetic resin to which no lubricant was added ( 8) Embossing 9 Repaintable synthetic resin layer
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2B002 AA03 AA04 DA01 DA04 4F100 AA01C AA01E AA01H AA19H AJ06 AK01C AK01D AK22G AK36G AK51 AP00A AP03 BA03 BA04 BA07 BA10A BA10C BA10D BA10E CA23C CA23E CB02 CC00E DG10B EJ34D EJ64B GB08 GB81 HB00B HB01 HB21D JB07 JK06 JK09C JK09E JK09H JL01D YY00C YY00E YY00H ──────────────────────────────────────────────────の Continued on the front page F-term (reference) 2B002 AA03 AA04 DA01 DA04 4F100 AA01C AA01E AA01H AA19H AJ06 AK01C AK01D AK22G AK36G AK51 AP00A AP03 BA03 BA04 BA07 BA10A BA10C BA10D BA10E CA23C CA23B CB01B02 CB02E JK06 JK09C JK09E JK09H JL01D YY00C YY00E YY00H
Claims (8)
紙上に合成樹脂による保護層を設けてなる化粧板におい
て、前記化粧紙は合成樹脂によるシーラー処理を施した
原紙を使用した化粧紙であり、且つ、前記合成樹脂によ
る保護層には無機材料からなる減摩剤が添加されている
ことを特徴とする化粧板。1. A decorative board comprising a decorative paper having a protective layer made of a synthetic resin provided on a surface of a wooden substrate and a decorative layer made of a synthetic resin provided on the decorative paper. A decorative paper, wherein the protective layer made of the synthetic resin is added with a lubricant made of an inorganic material.
り、そのうち最外層を除く層の少なくとも１層に、減摩
剤が添加されていることを特徴とする請求項１に記載の
化粧板。2. The decorative board according to claim 1, wherein the protective layer made of the synthetic resin comprises a plurality of layers, and at least one of the layers excluding the outermost layer contains a lubricant. .
材料からなる減摩剤が添加された合成樹脂による塗装を
後に施すための再塗装性の合成樹脂層が設けられている
ことを特徴とする請求項１に記載の化粧板。3. A repaintable synthetic resin layer for applying a coating of a synthetic resin to which a lubricating agent made of an inorganic material is added, instead of the protective layer of the synthetic resin. The decorative board according to claim 1, wherein:
処理が施されていることを特徴とする請求項３に記載の
化粧板。4. The decorative board according to claim 3, wherein the surface of the repaintable synthetic resin layer is polished.
料からなる減摩剤が添加された合成樹脂による塗装が施
されていることを特徴とする請求項３又は４に記載の化
粧板。5. The coating according to claim 3, wherein the repaintable synthetic resin layer is coated with a synthetic resin to which a lubricant made of an inorganic material is added. Decorative board.
合成樹脂による塗装の上に、更に無機材料からなる減摩
剤が添加されていない合成樹脂による塗装が施されてい
ることを特徴とする請求項５に記載の化粧板。6. A coating made of a synthetic resin to which a lubricant made of an inorganic material is not added, on top of a coating made of a synthetic resin to which a lubricant made of an inorganic material is added. The decorative board according to claim 5, wherein
であることを特徴とする請求項１〜６のいずれか１項記
載の化粧板。7. The lubricant has an average particle size of 10 to 100 μm.
The decorative board according to any one of claims 1 to 6, wherein
特徴とする請求項１〜７のいずれか１項記載の化粧板。8. The decorative board according to claim 1, wherein the surface is embossed.