JP2001270234A - Recording sheet having matt metal gloss surface and label - Google Patents
Recording sheet having matt metal gloss surface and labelInfo
- Publication number
- JP2001270234A JP2001270234A JP2000089514A JP2000089514A JP2001270234A JP 2001270234 A JP2001270234 A JP 2001270234A JP 2000089514 A JP2000089514 A JP 2000089514A JP 2000089514 A JP2000089514 A JP 2000089514A JP 2001270234 A JP2001270234 A JP 2001270234A
- Authority
- JP
- Japan
- Prior art keywords
- recording
- support
- recording layer
- label
- recording sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、記録用シート及び
ラベルに関し、その中でも艶消しの金属箔に直接記録し
た印象を与える金属光沢感を持った記録用シート及びラ
ベルに関するものであって、インクジェット記録方式や
熱転写記録方式に適したものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a recording sheet and a label, and more particularly to a recording sheet and a label having a metallic luster that gives an impression of direct recording on a matte metal foil. It is suitable for a recording method and a thermal transfer recording method.
【０００２】[0002]
【従来の技術】インクジェット記録方式は、種々の作動
原理によりインクの微小液滴を飛翔させて紙などの記録
シートに付着させ、画像文字などの記録を行うものであ
るが、高速、低騒音、多色化が容易、記録パターンの融
通性が大きい、現像定着が不要等の特徴があり、漢字を
含め各種図形およびカラー画像などの記録装置として急
速に普及している。更に、多色インクジェット方式によ
り形成される画像は、製版方式による多色印刷に比較し
て遜色のない記録を得ることが可能である。また、作成
部数が少なくてすむ用途においては、安価であることか
らフルカラー画像記録分野にまで広く応用されるように
なった。2. Description of the Related Art An ink jet recording system records minute characters such as ink by flying minute droplets of ink on a recording sheet such as paper according to various operating principles. It has features such as easy multi-coloring, great flexibility in recording patterns, and no need for development and fixing, and is rapidly spreading as a recording device for various figures including Chinese characters and color images. Further, it is possible to obtain an image formed by the multi-color ink jet system which is comparable to multi-color printing by the plate making system. In applications where the number of copies required is small, it has been widely applied to the field of full-color image recording because of its low cost.
【０００３】また、ハードコピーの一手段として、溶融
型や昇華型の熱転写方式を利用する装置も普及してい
る。溶融型の熱転写記録方式は、熱溶融性のインク層を
形成した熱転写記録媒体をサーマルヘッド等で加熱する
ことにより記録シートにインクを転写し、記録を行うも
のである。また、昇華型熱転写記録方式とは昇華型色素
を含有するインク層を形成した熱転写記録媒体を加熱す
ることにより、昇華型色素が記録シートに転写し、記録
を行うものである。溶融型や昇華型の熱転写方式を利用
する装置は軽量、安価かつコンパクトで騒音が無く、操
作性保守性にも優れているなどの利点からコンピュー
タ、ワードプロセッサーなどの記録方式として広く利用
されている。[0003] Further, as a means of hard copy, an apparatus using a fusion type or sublimation type thermal transfer system has been widely used. In the fusion type thermal transfer recording method, recording is performed by transferring ink to a recording sheet by heating a thermal transfer recording medium having a heat-meltable ink layer formed thereon with a thermal head or the like. In the sublimation type thermal transfer recording system, a sublimation type dye is transferred to a recording sheet by heating a thermal transfer recording medium on which an ink layer containing the sublimation type dye is formed, and recording is performed. 2. Description of the Related Art An apparatus using a fusion type or sublimation type thermal transfer system is widely used as a recording system such as a computer and a word processor because of its advantages such as light weight, low cost, compactness, no noise, and excellent operability and maintainability.
【０００４】インクジェット記録方式、溶融型及び昇華
型熱転写記録方式は年々応用範囲を広げ、従来製版方式
で作成されていたポスターやラベル印刷の分野にまで使
用されるようになってきた。[0004] The ink-jet recording system, the fusion type and the sublimation type thermal transfer recording system have been expanding their application range year by year, and have been used even in the field of poster and label printing which has been conventionally produced by the plate making system.
【０００５】ところで、ポスターやラベル等はいかに人
目を引くかという効果に重点が置かれる。人目を引く手
段としては、印刷面に光沢感をもたせた用紙を用いる手
段があり、高光沢な用紙が種々開発されている。特に、
アルミニウム箔に代表される金属箔のように金属光沢を
持つ用紙、特に艶消しの金属光沢を持ち、高光沢な面は
その特異的光沢感から人目を引くという効果の点で際だ
つものである。[0005] By the way, emphasis is placed on how posters, labels and the like are noticeable. As a means of attracting attention, there is a means using paper having a glossy print surface, and various high gloss papers have been developed. In particular,
Paper having a metallic luster such as a metallic foil represented by an aluminum foil, particularly a matte metallic gloss, and a high gloss surface is outstanding in terms of its effect of being noticeable due to its unique glossiness.
【０００６】しかし、金属箔自体にインクジェットや、
熱転写プリンターで記録することは不可能であった。金
属箔を被記録面とした場合、インクジェット記録方式で
は、インクの溶媒を吸収する事が出来ず、また、溶融型
や昇華型の熱転写記録方式ではインク又は染料の定着性
が不十分であり、画像を形成することができない。However, the metal foil itself has an ink jet or
It was not possible to record with a thermal transfer printer. When a metal foil is used as the surface to be recorded, the ink jet recording method cannot absorb the solvent of the ink, and the fixability of the ink or the dye is insufficient in the fusion type or sublimation type thermal transfer recording method, Images cannot be formed.
【０００７】そこで、特開平８−５８８２２７号公報に
は、インク遮断層である樹脂フィルムの片面に金属箔
を、フィルムの反対面にインク受容層を設けたものが提
案され、特開平１１−３２７４４２号公報には、上質紙
の表面に接着剤、金属箔、記録層を順次積層した記録用
紙が提案されている。これらはいずれも金属の光沢面
を、人目を引く点として利用したものである。このよう
な金属の高光沢面は鏡の作用を有するため、光の当たる
角度によっては非画像部のまぶしさのために、画像部が
見えにくくなったり、極端な場合は光の全反射により何
も見えなくなってしまうという欠点を有する。従って、
これらの高光沢紙は室内での小さなものでしか使いにく
いという問題がある。Japanese Patent Application Laid-Open No. Hei 8-588227 proposes a resin film as an ink blocking layer in which a metal foil is provided on one side and an ink receiving layer is provided on the opposite side of the film. Japanese Patent Application Laid-Open Publication No. H11-216, proposes a recording paper in which an adhesive, a metal foil, and a recording layer are sequentially laminated on the surface of a high-quality paper. Each of these uses the glossy surface of the metal as an eye-catching point. Since the high gloss surface of such a metal has a mirror effect, the image area may be difficult to see due to the glare of the non-image area depending on the angle of the light, or in extreme cases, the reflection may be caused by total reflection of light. Also has the drawback that it becomes invisible. Therefore,
There is a problem that these high gloss papers are difficult to use only in small rooms.
【０００８】[0008]
【発明が解決しようとする課題】従って、本発明が解決
しようとする課題は、人目を引くと同時に記録した文字
が判別しやすく、かつ、インクジェット記録方式や、溶
融型又は昇華型熱転写記録方式のプリンターを用いて印
刷が可能な記録用シート及びラベルを提供することにあ
る。SUMMARY OF THE INVENTION Therefore, the problem to be solved by the present invention is that it is easy to discriminate the recorded characters at the same time as being caught by the eye, and to use the ink jet recording system, the fusion type or sublimation type thermal transfer recording system. An object of the present invention is to provide a recording sheet and a label that can be printed by using a printer.
【０００９】[0009]
【課題を解決するための手段】本発明者らは、上記課題
を解決するために鋭意検討した結果、以下の発明に至っ
た。すなわち、第一の発明は少なくとも一方の面が金属
光沢を有する支持体の、金属光沢を有する面側に、パー
ル顔料を含有する記録層を設けた記録シートの発明であ
る。Means for Solving the Problems The present inventors have made intensive studies to solve the above problems, and as a result, have reached the following invention. That is, the first invention is an invention of a recording sheet in which a recording layer containing a pearl pigment is provided on a side having a metallic luster of a support having at least one surface having a metallic luster.
【００１０】すなわち、第二の発明は艶消しの金属面を
有する支持体が、基材上に接着剤を介して金属薄膜を設
けたものであり、支持体の艶消しの金属光沢を有する面
側に、パール顔料を含有する記録層を設けた記録シート
の発明である。[0010] That is, a second aspect of the present invention is a support having a matte metal surface on which a metal thin film is provided on a substrate via an adhesive, wherein the support has a matte metal gloss. This is an invention of a recording sheet provided with a recording layer containing a pearl pigment on the side.
【００１１】すなわち、第三の発明は少なくとも一方の
面が金属光沢を有する支持体の、金属光沢を有する面側
にパール顔料を含む記録層を設け、記録層側とは反対の
面側に接着層、剥離紙を順次設けたラベルの発明であ
り、また、金属面を有する支持体が、基材上に接着剤を
介して金属薄膜を設けたものであり、支持体の金属光沢
を有する面側に、パール顔料を含有する記録層を設け、
記録層側とは反対の面側に接着層、剥離紙を順次設けた
ラベルの発明である。That is, according to a third aspect of the present invention, a recording layer containing a pearl pigment is provided on a side having a metallic luster of a support having at least one side having a metallic luster, and is bonded to a side opposite to the recording layer. The present invention is a label invention in which a layer and a release paper are sequentially provided, and a support having a metal surface has a metal thin film provided on a base material via an adhesive, and a surface having a metallic luster of the support. On the side, a recording layer containing a pearl pigment is provided,
This is an invention of a label in which an adhesive layer and a release paper are sequentially provided on the side opposite to the recording layer side.
【００１２】[0012]
【発明の実施の形態】本発明に用いられる支持体は少な
くとも一方の面に金属光沢感を持つシートであり、特に
艶消しの金属面を持つシートであることが好ましい。艶
消しの光沢感を有する支持体を用いた場合は記録層中の
パール顔料の配合率を少なくすることができる。このよ
うなシートは金属シートそのものでも良いが、取り扱い
の安全性や記録後のシートを被着体に貼着したりあるい
はとじ合わせたりすることを考慮すると金属より柔らか
い基材上に金属箔や金属蒸着膜等の金属薄膜を設けたも
のが好ましい。このような金属箔や金属薄膜に用いる金
属としてはアルミニウム、金、銀、銅、クロム、インジ
ウム、錫等、加工適性があるものが好ましく用いられる
が、特に制限はない。BEST MODE FOR CARRYING OUT THE INVENTION The support used in the present invention is a sheet having a metallic luster on at least one surface, and is particularly preferably a sheet having a matte metal surface. When a support having a matte glossiness is used, the blending ratio of the pearl pigment in the recording layer can be reduced. Such a sheet may be a metal sheet itself, but considering the safety of handling and sticking or binding the sheet after recording to an adherend, a metal foil or a metal sheet may be formed on a substrate softer than the metal sheet. Those provided with a metal thin film such as a vapor deposition film are preferable. As a metal used for such a metal foil or a metal thin film, a material having processability such as aluminum, gold, silver, copper, chromium, indium, and tin is preferably used, but is not particularly limited.
【００１３】上記の支持体の基材としては、プリンター
で搬送可能なシート状のものであれば色、厚さ等特に限
定されず用いることができる。例えば、非塗工紙、塗工
紙、微塗工紙など通常の天然パルプ紙や、合繊繊維ある
いは合成樹脂フィルムを擬紙化したいわゆる合成紙、不
織布、布、合成樹脂フィルム等をあげることができる
が、耐水性、加工性に優れる合成紙を好ましく使用する
ことができる。The substrate of the above-mentioned support is not particularly limited in color, thickness, etc., so long as it can be transported by a printer. For example, ordinary natural pulp paper such as uncoated paper, coated paper, finely coated paper, so-called synthetic paper, nonwoven fabric, cloth, synthetic resin film, etc. in which synthetic fiber or synthetic resin film is simulated paper may be used. However, synthetic paper having excellent water resistance and processability can be preferably used.
【００１４】特に、結晶性ポリプロピレン系樹脂と高軟
化点石油樹脂とからなる組成物を延伸成形した層と結晶
性ポリプロピレン系樹脂に無機充填剤を配合した層を積
層することにより得られる合成紙は表面平滑性、白色度
が高く、均一な金属光沢面を得ることができるため、基
材として好ましい。このような合成紙としては、例えば
市販品として製品名 カルレ（チッソ株式会社製）を用
いることができる。In particular, synthetic paper obtained by laminating a layer formed by stretching a composition comprising a crystalline polypropylene resin and a high softening point petroleum resin and a layer obtained by mixing an inorganic filler with the crystalline polypropylene resin is It is preferable as a substrate because it has high surface smoothness and whiteness and can provide a uniform metallic glossy surface. As such a synthetic paper, for example, a commercial product having the product name Carre (manufactured by Chisso Corporation) can be used.
【００１５】また、本発明の基材には接着剤の目止めや
平滑性をあげるために各種アンカー処理を行ってもかま
わない。The base material of the present invention may be subjected to various kinds of anchor treatments in order to improve the filling and smoothness of the adhesive.
【００１６】本発明において、基材上に金属薄膜を設け
る方法は、基材状に接着剤を介して金属箔を貼着する方
法、基材上に直接金属を蒸着させる方法、あらかじめ合
成樹脂フィルム上に設けた金属薄膜を基材上に転写して
貼着する方法等がある。In the present invention, the method of providing a metal thin film on a substrate includes a method of attaching a metal foil to a substrate via an adhesive, a method of depositing a metal directly on the substrate, and a method of previously forming a synthetic resin film. There is a method of transferring the metal thin film provided thereon onto a base material and attaching the same.
【００１７】基材上に金属箔を貼着したり、直接蒸着す
る方法においては、金属薄膜貼着後の基材を、粗面を有
するロールに通して金属薄膜面を粗面化して艶消し処理
を行う方法が一般的である。この場合、支持体が粗面を
有するロールを通過するときの圧力で支持体の厚みが変
化したり接着剤がはみ出したり、支持体が破壊されたり
するなど問題点が多い。In the method of attaching a metal foil on a substrate or directly depositing a metal film, the substrate after the attachment of the metal thin film is passed through a roll having a rough surface to roughen the surface of the metal thin film to deluster the mat. A method of performing processing is general. In this case, there are many problems such as a change in the thickness of the support due to the pressure when the support passes through a roll having a rough surface, an overflow of the adhesive, and a break in the support.
【００１８】そこで、本発明では合成樹脂フィルム上に
金属薄膜を設け、接着剤を介して金属薄膜を基材上に貼
り付けた後、合成樹脂フィルムを剥離する、いわゆる転
写法により金属光沢をもつ支持体を得る。また、合成フ
ィルム上に金属薄膜を設けた時点で薄膜の均一性を検査
できるので結果として均一な艶消しの金属光沢を持つ支
持体を得ることができる。Therefore, in the present invention, a metal thin film is provided on a synthetic resin film, and after attaching the metal thin film to a base material via an adhesive, the synthetic resin film is peeled off. Obtain a support. In addition, since the uniformity of the thin film can be inspected at the time when the metal thin film is provided on the synthetic film, a support having a uniform matte metallic luster can be obtained as a result.
【００１９】また、あらかじめ合成樹脂フィルム表面を
所望の艶消し面を得られる粗面とし、この粗面上に金属
薄膜を設け、接着剤を介して金属薄膜を基材上に貼り付
けた後、合成樹脂フィルムを剥離することで艶消しの金
属光沢をもつ支持体を得る事ができる。この方法では、
合成樹脂フィルムの表面を所望の粗面とすることが容易
であることから、最終的に表面に現れる金属薄膜表面
（艶消し面）の設計が容易となる利点がある。Further, the surface of the synthetic resin film is previously made to be a rough surface capable of obtaining a desired matte surface, a metal thin film is provided on the rough surface, and the metal thin film is attached to a base material via an adhesive. By peeling the synthetic resin film, a support having a matte metallic luster can be obtained. in this way,
Since it is easy to make the surface of the synthetic resin film a desired rough surface, there is an advantage that the design of the metal thin film surface (matte surface) finally appearing on the surface becomes easy.
【００２０】上記合成樹脂フィルムは、最終的に金属薄
膜から剥離されるため、形成される金属薄膜に強い密着
性を持たないものを用いることが好ましい。このような
合成フィルムとしては２軸延伸ポリプロピレンフィルム
が好適である。Since the synthetic resin film is finally peeled off from the metal thin film, it is preferable to use a film having no strong adhesion to the formed metal thin film. As such a synthetic film, a biaxially stretched polypropylene film is preferable.
【００２１】上記の合成樹脂フィルム上に金属薄膜を形
成する手段としては、特に限定されるものではないが、
特に真空蒸着法やスパッタ法のような物理的成膜法であ
ることが好ましい。金属薄膜の厚みは格別限定されるも
のではないが、厚くしすぎると不経済であり、薄くしす
ぎると金属光沢が発現しない。具体的には２０〜１００
０Åが好ましい。The means for forming a metal thin film on the above synthetic resin film is not particularly limited,
In particular, a physical film formation method such as a vacuum evaporation method or a sputtering method is preferable. The thickness of the metal thin film is not particularly limited, but if it is too thick, it is uneconomical, and if it is too thin, metallic luster does not appear. Specifically, 20-100
0 ° is preferred.
【００２２】金属薄膜と基材を接着する接着剤としては
基材と金属薄膜を強く接着するものであれば材質、厚み
等特に限定されない。The material and thickness of the adhesive for bonding the metal thin film and the substrate are not particularly limited as long as the adhesive strongly bonds the substrate and the metal thin film.
【００２３】本発明の記録層はパール顔料を含有する層
である。記録層中にパール顔料を含有することで、支持
体のもつ艶消しの金属光沢を損なうことなくインク受容
層を形成することができる。記録層中にパール顔料を含
有しない場合、支持体の持つ光沢感は失われ、記録シー
トは灰色のシートになる。パール顔料を含有する記録層
の場合に、支持体の持つ艶消しの金属光沢感が保持され
る理由は定かではないが、記録層中のパール顔料からの
反射光の分布が艶消しの金属光沢を有する表面の反射光
の分布と似ているためと推測される。本発明の記録層は
パール顔料と樹脂を主成分とすることが好ましい。The recording layer of the present invention is a layer containing a pearl pigment. By containing a pearl pigment in the recording layer, an ink receiving layer can be formed without impairing the matte metallic luster of the support. When no pearl pigment is contained in the recording layer, the glossiness of the support is lost and the recording sheet becomes a gray sheet. The reason why the matte metallic glossiness of the support is maintained in the case of the recording layer containing the pearl pigment is not clear, but the distribution of the reflected light from the pearl pigment in the recording layer is matte metallic gloss. This is presumed to be similar to the distribution of reflected light on the surface having The recording layer of the present invention preferably contains a pearl pigment and a resin as main components.
【００２４】本発明でいうパール顔料とは真珠光沢を有
する顔料のことをいう。パール顔料は一般に薄板状であ
り、顔料表面で規則的多重反射が生じることにより真珠
のような光沢感を発現する。パール顔料としては例えば
雲母粒子に酸化チタン等の金属酸化物を被覆したものを
あげることができる。雲母粒子は天然雲母を粉砕、分級
して調製しても良いし、人工的に合成しても良いが、発
現する真珠光沢にくすみが無く、品質の安定した合成雲
母が好ましく用いられる。The pearl pigment in the present invention refers to a pigment having a pearl luster. The pearl pigment is generally in the form of a thin plate, and exhibits a pearl-like luster due to the occurrence of regular multiple reflections on the pigment surface. Examples of the pearl pigment include those obtained by coating mica particles with a metal oxide such as titanium oxide. The mica particles may be prepared by pulverizing and classifying natural mica, or may be artificially synthesized. However, synthetic mica which has no dullness in pearl luster and has stable quality is preferably used.
【００２５】本発明の記録層中において、パール顔料の
配合量を増やすと記録適性が落ちる傾向がある。インク
ジェット記録方式の場合は、インク吸収性が落ちる傾向
となり、溶融型熱転写記録方式の場合はインク定着性が
悪くなる傾向に、昇華型熱転写方式の場合は染料の染着
性が落ちる傾向がある。また、配合量を減らすと艶消し
の金属光沢感が弱くなる傾向がある。このため、パール
顔料は記録層中に５〜３０重量％の比率で配合すること
が好ましく、特に７〜１５重量％の比率で配合すると好
ましい。In the recording layer of the present invention, if the amount of the pearl pigment is increased, the recording suitability tends to decrease. In the case of the ink jet recording system, the ink absorbency tends to decrease, in the case of the fusion type thermal transfer recording system, the ink fixing property tends to deteriorate, and in the case of the sublimation type thermal transfer system, the dyeing property of the dye tends to decrease. In addition, when the amount is reduced, the matte metallic gloss tends to be weakened. For this reason, the pearl pigment is preferably blended in the recording layer at a ratio of 5 to 30% by weight, particularly preferably at a ratio of 7 to 15% by weight.
【００２６】また、本発明のパール顔料の粒度分布は必
要とされる艶消しの金属光沢面の面感に応じて、適宜選
択することができる。パール顔料の粒度分布を大きく
し、粒子径の大きいパール顔料の含有量が多くなると、
記録層はキラキラ感を持つ粗い面感となる。また、粒度
分布を小さくし、粒子径の小さなパール顔料の含有量が
多くなるとシルキーな、なめらかな面感になる。記録画
像の見やすさの点から、本発明のパール顔料の粒度分布
は５〜１５０μｍであることが好ましく、より好ましく
は１５〜１００μｍ、更に好ましくは１０〜６０μｍで
ある。パール顔料の厚みは０．１μｍ〜１μｍであれば
問題なく使用できる。The particle size distribution of the pearl pigment of the present invention can be appropriately selected according to the required matte metallic glossy surface. When the particle size distribution of the pearl pigment is increased and the content of the pearl pigment having a large particle diameter increases,
The recording layer has a rough surface with glitter. Further, when the particle size distribution is reduced and the content of the pearl pigment having a small particle diameter is increased, a silky and smooth surface is obtained. From the viewpoint of the readability of the recorded image, the particle size distribution of the pearl pigment of the present invention is preferably from 5 to 150 μm, more preferably from 15 to 100 μm, and still more preferably from 10 to 60 μm. If the pearl pigment has a thickness of 0.1 μm to 1 μm, it can be used without any problem.
【００２７】本発明における記録層の樹脂は、記録特性
があれば特に限定されるものではないが、各記録方式に
より記録特性が優れたものを選択することが好ましい。
記録方式がインクジェット記録方式の場合、記録層の樹
脂としては酸化澱粉、エーテル化澱粉、ポリビニルアル
コール、カルボキシルメチルセルロース・ヒドロキシエ
チルセルロース等のセルロース誘導体、カゼイン、ゼラ
チン、大豆タンパク等の水溶性樹脂が好ましく用いられ
る。これらの樹脂は単独で使用しても混合で使用しても
良く、また、記録層中に印字品質を損なわない程度に記
録層を耐水化させる耐水化剤等を添加しても良い。The resin of the recording layer in the present invention is not particularly limited as long as it has recording characteristics, but it is preferable to select a resin having excellent recording characteristics according to each recording method.
When the recording method is an ink jet recording method, as the resin of the recording layer, water-soluble resins such as oxidized starch, etherified starch, polyvinyl alcohol, cellulose derivatives such as carboxymethylcellulose and hydroxyethylcellulose, casein, gelatin, and soybean protein are preferably used. . These resins may be used alone or as a mixture, and a water-proofing agent or the like for making the recording layer water-resistant may be added to the recording layer to such an extent that the print quality is not impaired.
【００２８】溶融型熱転写記録方式の場合は熱転写記録
媒体の熱溶融性インクと密着性の良い樹脂が選択される
ことが好ましい。例えばポリエステル樹脂、酢酸ビニル
樹脂、スチレンブタジエン共重合樹脂、アクリル樹脂、
ポリウレタン等が選択される。これらの樹脂は単独で使
用しても混合で使用しても良い。In the case of the fusion type thermal transfer recording system, it is preferable to select a resin having good adhesion to the heat-meltable ink of the thermal transfer recording medium. For example, polyester resin, vinyl acetate resin, styrene butadiene copolymer resin, acrylic resin,
Polyurethane or the like is selected. These resins may be used alone or in combination.
【００２９】昇華型熱転写記録方式の場合は昇華性染料
に染着しやすい樹脂であればいずれも好適に使用でき
る。例えば、ポリエステル樹脂、ポリアクリル酸エステ
ル樹脂等のエステル結合を有する樹脂、ポリウレタン等
ウレタン結合を有する樹脂、ポリアミド等アミド結合を
有する樹脂、その他ポリスチレン樹脂、ポリ塩化ビニル
樹脂、ポリアクリロニトリル樹脂など極性が高い樹脂が
使用できる。さらに、上記樹脂の、構成単位の内の１種
以上を主成分とする共重合体、例えばスチレンブタジエ
ン共重合体などとしても使用することができ、更に上記
樹脂を単独、又は混合して使用することができる。In the case of the sublimation type thermal transfer recording system, any resin can be suitably used as long as it is a resin which easily dyes the sublimable dye. For example, polyester resins, resins having ester bonds such as polyacrylate resins, resins having urethane bonds such as polyurethane, resins having amide bonds such as polyamide, other polystyrene resins, polyvinyl chloride resins, and high polarity such as polyacrylonitrile resins. Resin can be used. Further, the above-mentioned resin, a copolymer containing at least one of the structural units as a main component, for example, a styrene-butadiene copolymer and the like can be used. Further, the above-mentioned resin is used alone or as a mixture. be able to.
【００３０】本発明の記録層は、支持体からの反射光が
透過できる程度透明であることが好ましく、記録層の透
過率は８５％以上であると好ましい。The recording layer of the present invention is preferably transparent to the extent that light reflected from the support can be transmitted, and the transmittance of the recording layer is preferably 85% or more.
【００３１】また、本発明の記録層中には、支持体の金
属光沢の色調に合わせて、記録層中に着色顔料を配合す
ることができる。着色顔料を配合することで、より金属
に近い光沢感を付与することができる。さらに、記録層
中には発明の効果を損なわない程度に防腐剤、消泡剤、
紫外線吸収剤、帯電防止剤、分散剤、各種顔料等各種助
剤を添加することができる。In the recording layer of the present invention, a coloring pigment can be blended in the recording layer in accordance with the color tone of the metallic luster of the support. By blending a color pigment, a glossiness closer to that of a metal can be imparted. Furthermore, in the recording layer, an antiseptic, an antifoaming agent,
Various assistants such as an ultraviolet absorber, an antistatic agent, a dispersant, and various pigments can be added.
【００３２】本発明の記録層及び粘着層は従来公知の塗
工方法で形成される。例えば、各種ブレードコーター、
ロールコーター、エアーナイフコーター、バーコータ
ー、ロッドブレードコーター等、各種装置をオンマシン
あるいは、オフマシンで用いることができる。又塗工後
には各種カレンダー装置等カレンダー処理を行っても良
い。The recording layer and the adhesive layer of the present invention are formed by a conventionally known coating method. For example, various blade coaters,
Various devices such as a roll coater, an air knife coater, a bar coater, and a rod blade coater can be used on-machine or off-machine. Further, after the coating, a calendering treatment such as various calendering devices may be performed.
【００３３】本発明の支持体においては記録層に対する
密着性の向上等のために発明の効果を損なわない程度に
表面処理を行ってもかまわない。例えば、支持体の記録
層を設ける側にコロナ表面処理やプラズマ表面処理を行
うことができる。また、支持体表面と記録層の両方に密
着性の良い樹脂層（易接着層）を設けることもできる。The support of the present invention may be subjected to a surface treatment so as not to impair the effects of the present invention in order to improve the adhesion to the recording layer. For example, corona surface treatment or plasma surface treatment can be performed on the side of the support on which the recording layer is provided. In addition, a resin layer having good adhesion (an easy-adhesion layer) can be provided on both the support surface and the recording layer.
【００３４】本発明のラベルの粘着層は一般公知の粘着
剤を支持体の記録層を形成した反対側の面に塗工あるい
は転写して形成される。粘着剤としては、一般公知のも
のを利用でき、例えば、アクリル樹脂、天然及び合成ゴ
ム、スチレン／ブタジエン共重合樹脂、ポリ酢酸ビニ
ル、酢酸ビニル／エチレン共重合樹脂、澱粉、シリコー
ン化合物、ニカワ、カゼイン、ポリビニルアルコール、
ポリウレタン等の樹脂を溶液、水溶液、エマルジョンの
形で単独あるいは混合して用いることができる。The pressure-sensitive adhesive layer of the label of the present invention is formed by applying or transferring a generally known pressure-sensitive adhesive to the surface of the support opposite to the side on which the recording layer is formed. As the pressure-sensitive adhesive, generally known ones can be used, for example, acrylic resin, natural and synthetic rubber, styrene / butadiene copolymer resin, polyvinyl acetate, vinyl acetate / ethylene copolymer resin, starch, silicone compound, glue, casein , Polyvinyl alcohol,
Resins such as polyurethane can be used alone or in the form of a solution, an aqueous solution or an emulsion.
【００３５】粘着層にはさらに、防腐剤、消泡剤、紫外
線吸収剤、帯電防止剤、分散剤、各種顔料等各種助剤を
添加することができる。また、前記粘着剤は再剥離性で
あっても良い。The adhesive layer may further contain various auxiliaries such as a preservative, an antifoaming agent, an ultraviolet absorber, an antistatic agent, a dispersant, and various pigments. Further, the pressure-sensitive adhesive may be removable.
【００３６】本発明のラベルで用いられる剥離紙は、剥
離性を有するものであれば何ら制限されることなく、フ
ィルムベース剥離紙、上質紙ベース剥離紙、ラミネート
ベース剥離紙等いかなるもの用いても良い。また、その
厚み、色に関しても何ら制限されることはなく、その剥
離剤もその使用用途に合っているものであればどのよう
なものを用いてもかまわない。The release paper used in the label of the present invention is not limited as long as it has releasability, and any release paper such as a film-based release paper, a high-quality paper-based release paper, a laminate-based release paper, or the like can be used. good. The thickness and color are not limited at all, and any release agent may be used as long as it meets the intended use.
【００３７】一般にラベルにおいては型抜き加工（ダイ
カット）が施されるが、ラベルの支持体として合成樹脂
フィルムに形成した金属薄膜を基材上に接着剤を介して
転写したシートを用いることが好ましい。この場合、金
属箔（厚さ数μｍ〜数１０μｍ程度）を貼り合わせたシ
ートを支持体として用いる場合と比較して、型抜きに使
用する型にかかる負担が小さく、また、少ない押力で簡
単にカットができる傾向にある。In general, a label is subjected to die cutting (die cutting), and it is preferable to use a sheet obtained by transferring a metal thin film formed on a synthetic resin film onto a base material via an adhesive as a support for the label. . In this case, as compared with a case where a sheet to which a metal foil (thickness of about several μm to several tens of μm) is adhered is used as a support, the burden on the die used for the die cutting is small, and the pressing force is simple. Tend to be cut.
【００３８】[0038]
【実施例】以下に、本発明の実施例をあげて説明する
が、本発明はこれらに限定されるものではない。また、
実施例、及び比較例において「部」及び「％」は特に明
示しない限り「重量部」、「重量％」を示す。The present invention will be described below with reference to examples of the present invention, but the present invention is not limited to these examples. Also,
In Examples and Comparative Examples, “parts” and “%” indicate “parts by weight” and “% by weight” unless otherwise specified.
【００３９】支持体の作製 （支持体Ａ：艶消しの金属光沢面を持つ支持体の作製）
一方の表面が粗面である厚さ25μｍのポリプロピレンフ
ィルムフィルムの粗面上に真空蒸着法により厚さ６００
Åとなるようにアルミ蒸着層を形成する。さらに、アル
ミ蒸着層上に、ポリエステルウレタン系主剤とポリイソ
シアネート系硬化剤からなるドライラミネート接着剤
（ディックドライＬＸ９０１／ＫＷ７５；大日本インキ
化学工業（株）製）を乾燥時の固形分で３ｇ／ｍ2とな
るように塗布し、合成紙（カルレ ＳＮＦ１００チッソ
株式会社製）を互いに重ね合わせた状態で８０℃の加熱
金属ロールの間に挿入し、加熱および圧着する。その後
適当な接着力を得るために、50℃に加熱した状態で、48
時間貯蔵して接着剤層を硬化させた後、ポリプロピレン
フィルムを剥離して艶消しの金属光沢を持つ支持体Ａを
得た。Preparation of Support (Support A: Preparation of Support with Matte Metallic Glossy Surface)
On a rough surface of a 25 μm-thick polypropylene film having one rough surface, a thickness of 600
An aluminum vapor-deposited layer is formed so as to become Å. Further, a dry laminating adhesive (Dick Dry LX901 / KW75; manufactured by Dainippon Ink and Chemicals, Inc.) comprising a polyester urethane-based base material and a polyisocyanate-based curing agent was applied on the aluminum-deposited layer at a solid content of 3 g / dry. m 2, and inserted between heated metal rolls at 80 ° C. with synthetic paper (Carre SNF100 manufactured by Chisso Corporation) superposed on each other, and heated and pressed. Then, in order to obtain an appropriate adhesive strength, heat at 50 ° C,
After storage for a time to cure the adhesive layer, the polypropylene film was peeled off to obtain a support A having a matte metallic luster.
【００４０】（支持体Ｂ：鏡面の金属光沢を持つ支持体
の作製）表面が平滑な面である厚さ25μｍのポリプロピ
レンフィルムフィルムの平滑な面上に真空蒸着法により
厚さ６００Åとなるようにアルミ蒸着層を形成した以外
は支持体Ａと同様にして鏡面の金属光沢を持つ支持体Ｂ
を得た。(Support B: Preparation of a support having a mirror-like metallic luster) A 600 μm thick vacuum-deposited film was formed on a smooth surface of a 25 μm-thick polypropylene film having a smooth surface. Support B having a mirror-like metallic luster in the same manner as Support A except that an aluminum vapor-deposited layer was formed.
I got
【００４１】記録層塗工液の調製 （インクジェット記録層用塗工液）ポリビニルアルコー
ル（ＰＶＡ１１７、クラレ製）９０部、パール顔料（イ
リオジン１０３ メルクジャパン社製、粒度分布１０〜
６０μｍ）１０部、青色顔料１部、黒色顔料１部、水４
５０部、メタノール４５０部を用い、これをインクジェ
ット記録層用塗工液とした。 （溶融型熱転写記録層用塗工液）ポリエステルディスパ
ージョン（バイロナールＭＤ−１２００、東洋紡社製）
固形分で９０部、パール顔料（イリオジン１０３）１０
部、青色顔料１部、黒色顔料１部、水２００部、メタノ
ール２００部を用い、これを溶融型熱転写記録層用塗工
液とした。 （昇華型熱転写記録層用塗工液）ポリエステルディスパ
ージョン（バイロナールＭＤ−１２００、東洋紡社製）
固形分で９０部、パール顔料（イリオジン１０３）１０
部、青色顔料１部、黒色顔料１部、水２００部、メタノ
ール２００部を用い、これを昇華型熱転写記録記録層用
塗工液とした。 Preparation of Coating Solution for Recording Layer (Coating Solution for Inkjet Recording Layer) 90 parts of polyvinyl alcohol (PVA117, manufactured by Kuraray), pearl pigment (Iriodin 103, manufactured by Merck Japan Ltd., particle size distribution 10 to 10)
60 μm) 10 parts, blue pigment 1 part, black pigment 1 part, water 4
50 parts and 450 parts of methanol were used, and this was used as a coating liquid for an ink jet recording layer. (Coating liquid for melt-type thermal transfer recording layer) Polyester dispersion (Vylonal MD-1200, manufactured by Toyobo Co., Ltd.)
90 parts by solid content, pearl pigment (Iriodin 103) 10
Parts, 1 part of a blue pigment, 1 part of a black pigment, 200 parts of water, and 200 parts of methanol, and this was used as a coating liquid for a melt-type thermal transfer recording layer. (Coating liquid for sublimation type thermal transfer recording layer) Polyester dispersion (Vylonal MD-1200, manufactured by Toyobo Co., Ltd.)
90 parts by solid content, pearl pigment (Iriodin 103) 10
Parts, 1 part of a blue pigment, 1 part of a black pigment, 200 parts of water, and 200 parts of methanol, and this was used as a coating liquid for a sublimation type thermal transfer recording layer.
【００４２】（実施例１）支持体として艶消しの金属光
沢を持つ支持体Ａを用い、前記インクジェット記録層用
塗工液をバーコーターにて塗布し、乾燥温度１００℃の
ドライヤー中で乾燥してインクジェット記録用シートを
作製した。乾燥後の記録層の塗工量は１５ｇ／ｍ2であ
った。Example 1 Using a support A having a matte metallic luster as a support, the above-mentioned coating solution for an ink jet recording layer was applied by a bar coater and dried in a dryer at a drying temperature of 100 ° C. Thus, an ink jet recording sheet was prepared. The coating amount of the recording layer after drying was 15 g / m 2 .
【００４３】（実施例２）支持体として艶消しの金属光
沢を持つ支持体Ａを用い、前記溶融型熱転写記録層用塗
工液をバーコーターにて塗布し、乾燥温度１００℃のド
ライヤー中で乾燥しして溶融型熱転写記録用シートを作
製した。乾燥後の記録層塗工量は５ｇ／ｍ2であった。Example 2 Using a support A having a matte metallic luster as a support, the above-mentioned coating solution for a heat transfer recording layer was applied by a bar coater and dried in a dryer at a drying temperature of 100 ° C. After drying, a sheet for fusion-type thermal transfer recording was prepared. The coating amount of the recording layer after drying was 5 g / m 2 .
【００４４】（実施例３）支持体として艶消しの金属光
沢を持つ支持体Ａを用い、前記昇華型熱転写記録層用塗
工液をバーコーターにて塗布し、乾燥温度１００℃のド
ライヤー中で乾燥しして昇華型熱転写記録用シートを作
製した。乾燥後の記録層の塗工量は５ｇ／ｍ 2であっ
た。Example 3 Matte Metal Light as Support
Using the support A having a swab, the sublimation type thermal transfer recording layer coating
Apply the working liquid with a bar coater and dry at a drying temperature of 100 ° C.
Dry in a lier to produce a sublimation type thermal transfer recording sheet.
Made. The coating amount of the recording layer after drying is 5 g / m TwoSo
Was.
【００４５】（実施例４）インクジェット記録層用塗工
液において、青色顔料、及び黒色顔料を配合しなかった
以外は実施例１と同様にしてインクジェット記録用シー
トを作製した。Example 4 An ink jet recording sheet was prepared in the same manner as in Example 1 except that the blue pigment and the black pigment were not added to the coating liquid for the ink jet recording layer.
【００４６】（比較例１）インクジェット記録層用塗工
液においてパール顔料を配合しない以外は実施例１と同
様にしてインクジェット記録用シートを作製した。Comparative Example 1 An ink jet recording sheet was prepared in the same manner as in Example 1, except that the pearl pigment was not added to the coating liquid for the ink jet recording layer.
【００４７】（比較例２）支持体として鏡面の金属光沢
を持つ支持体Ｂを用いた以外は比較例１と同様にしてイ
ンクジェット記録用シートを作製した。Comparative Example 2 An ink jet recording sheet was prepared in the same manner as in Comparative Example 1 except that the support B having a mirror-like metallic luster was used as the support.
【００４８】（比較例３）インクジェット記録用塗工液
において、パール顔料の代わりにシリカ顔料（ファイン
シールＸ３７Ｂ 徳山曹達社製）を１０部用いた以外は
実施例１と同様にしてインクジェット記録用シートを作
製した。Comparative Example 3 An ink jet recording sheet was prepared in the same manner as in Example 1 except that 10 parts of a silica pigment (Fine Seal X37B manufactured by Tokuyama Soda Co., Ltd.) was used in place of the pearl pigment in the coating liquid for ink jet recording. Was prepared.
【００４９】上記実施例１〜４、比較例１〜３で得られ
た記録シートを以下に示す各種方式のプリンターにて文
字と線画からなる画像を記録した。 （インクジェットプリンター）ＥＰＳＯＮ社製 ＰＭ−
７７０Ｃ （溶融型熱転写プリンター）アルプス電気社製 ＭＤ−
４０００Ｊ （昇華型熱転写プリンター）三菱電機社製 Ｓ３６００
−３０Images composed of characters and line drawings were recorded on the recording sheets obtained in Examples 1 to 4 and Comparative Examples 1 to 3 using printers of various types described below. (Inkjet printer) PM- manufactured by EPSON
770C (fusion type thermal transfer printer) MD- manufactured by Alps Electric Co., Ltd.
4000J (sublimation type thermal transfer printer) S3600 manufactured by Mitsubishi Electric Corporation
-30
【００５０】記録画像の評価を表１にまとめる。Table 1 summarizes the evaluations of the recorded images.
【表１】 [Table 1]
【００５１】表１から明らかなように実施例１〜４はの
ように本発明の記録シートは艶消しの金属光沢を有し、
記録画像の視認性も優れていることがわかる。一方、記
録層中にパール顔料が含まれていない比較例１は金属光
沢感が発現せず、また、鏡面の金属光沢感を持つ比較例
２は非画像部に背景や、光源が写り込み、記録した画
像、特に文字が判別しづらいことがわかる。As is clear from Table 1, as in Examples 1 to 4, the recording sheet of the present invention has a matte metallic luster,
It can be seen that the visibility of the recorded image is also excellent. On the other hand, in Comparative Example 1 in which the pearl pigment was not contained in the recording layer, no metallic luster was exhibited, and in Comparative Example 2 having a specular metallic luster, the background and light source were reflected in the non-image area, It can be seen that the recorded image, especially characters, is difficult to distinguish.
【００５２】ラベルの製造 （実施例５）実施例１〜３で作製した各記録シートの記
録層が形成された面と反対側の面にコンマコーターで粘
着剤（アロンタック ＨＶＣ−３３００ 東亞合成化学
工業社製）を、乾燥塗工量２５ｇ／ｍ2となるように塗
工し、シリコーン樹脂をを主成分とする剥離層を設けた
厚さ７５μｍのポリエチレンテレフタレートフィルムを
重ね合わせて本発明のラベルを作製した。 Manufacture of Label (Example 5) An adhesive (Arontack HVC-3300 Toagosei Chemical Co., Ltd.) was applied to the surface of each of the recording sheets prepared in Examples 1 to 3 on the side opposite to the side on which the recording layer was formed with a comma coater. Co., Ltd.) was applied so as to have a dry coating amount of 25 g / m 2, and a 75 μm-thick polyethylene terephthalate film provided with a release layer containing a silicone resin as a main component was overlaid to form a label of the present invention. Produced.
【００５３】（実施例６）支持体として坪量１４０ｇ／
ｍ2の上質紙に、溶融押出ダイにより接着剤樹脂として
低密度ポリエチレンを厚み１５μｍでラミネートを行う
と同時に、金属箔として厚み７μｍのアルミニウム箔を
艶消しの光沢を持つ面を外側にして圧着して接着し、金
属貼り合わせ紙を得た。この金属貼り合わせ紙を支持体
とした以外は実施例１と同様にしてインクジェット記録
用シートを作製し、実施例５と同様にしてラベルを作製
した。(Example 6) A basis weight of 140 g /
At the same time, low-density polyethylene as an adhesive resin is laminated to a thickness of 15 μm on a high-quality paper of m 2 by a melt extrusion die, and at the same time, a 7 μm-thick aluminum foil is pressed as a metal foil with its matte gloss side facing out. To obtain a metal-laminated paper. An ink jet recording sheet was produced in the same manner as in Example 1 except that this metal-bonded paper was used as a support, and a label was produced in the same manner as in Example 5.
【００５４】（ラベルの評価）Ａ４版の大きさの中に２
０ｍｍ×５０ｍｍの四角の刃が１０個付いたダイカット
用の抜き型を用意し、実施例５、６で作製した本発明の
ラベルをカットした。すべてのラベルにおいて、問題な
く型抜きすることができたが、実施例６に関しては完全
に型抜きできない部分が発生することがあった。(Evaluation of label) In the size of A4 size, 2
A die for die cutting having 10 square blades of 0 mm × 50 mm was prepared, and the labels of the present invention produced in Examples 5 and 6 were cut. In all the labels, the die could be cut without any problem, but in the case of Example 6, there was a case where a part could not be completely cut.
【００５５】[0055]
【発明の効果】本発明の記録シート及びラベルを用いる
ことにより、他の印刷物とは異なった、人目を引く印字
物を得ることができる。また、本発明の記録シート及び
ラベルは艶消しの光沢感を有するため、記録した画像が
判別し易く、印字文字等が読みやすい。また、金属蒸着
膜を合成紙に転写したシートを支持体として用いたラベ
ルはダイカット性が優れる。By using the recording sheet and the label of the present invention, a noticeable printed matter different from other printed matter can be obtained. Further, since the recording sheet and label of the present invention have a matte glossiness, the recorded image can be easily distinguished, and printed characters and the like can be easily read. Further, a label using a sheet obtained by transferring a metal vapor-deposited film onto synthetic paper as a support has excellent die-cut properties.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） // Ｃ０９Ｊ 7/02 Ｂ４１Ｍ 5/26 １０１Ｈ (72)発明者 渡邉 芳人 東京都千代田区有楽町１丁目12番１号 日 本製紙株式会社内 Ｆターム(参考） 2H086 BA01 BA15 BA18 BA19 BA24 BA33 BA41 2H111 AA01 AA26 AA27 CA03 CA05 CA25 CA26 CA33 CA41 4J004 AA04 AA05 AA07 AA08 AA09 AA10 AA11 AA14 AB01 CA02 CA04 CB01 CB02 CB03 CC03 CC05 CD01 DB02 FA01 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) // C09J 7/02 B41M 5/26 101H (72) Inventor Yoshito Watanabe 1-12 Yurakucho, Chiyoda-ku, Tokyo No. 1 Nippon Paper Industries Co., Ltd. F term (reference) 2H086 BA01 BA15 BA18 BA19 BA24 BA33 BA41 2H111 AA01 AA26 AA27 CA03 CA05 CA25 CA26 CA33 CA41 4J004 AA04 AA05 AA07 AA08 AA09 AA10 AA11 AA14 AB01 CA02 CA04 CB01 CC03 CC03 DB02 FA01
Claims (3)
持体の、金属光沢を有する面側に、パール顔料を含有す
る記録層を設けた艶消し金属光沢面を持つ記録用シー
ト。1. A recording sheet having a matte metallic glossy surface provided with a recording layer containing a pearl pigment on the metallic glossy side of a support having at least one surface having a metallic glossiness.
属薄膜を設けたものである請求項１に記載された艶消し
金属光沢面を持つ記録用シート。2. A recording sheet having a matte metallic glossy surface according to claim 1, wherein the support comprises a substrate and a metal thin film provided on the substrate via an adhesive.
沢面を持つ記録用シートの記録層と反対の面側に、粘着
層、剥離紙を順次設けたラベル。3. A label comprising a recording sheet having a matte metallic glossy surface according to claim 1 or 2 and a pressure-sensitive adhesive layer and a release paper sequentially provided on the side opposite to the recording layer.