JP2001161315A - Calcium preparation - Google Patents

Calcium preparation

Info

Publication number
JP2001161315A
JP2001161315A JP34418099A JP34418099A JP2001161315A JP 2001161315 A JP2001161315 A JP 2001161315A JP 34418099 A JP34418099 A JP 34418099A JP 34418099 A JP34418099 A JP 34418099A JP 2001161315 A JP2001161315 A JP 2001161315A
Authority
JP
Japan
Prior art keywords
calcium
raw material
containing raw
active ingredient
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP34418099A
Other languages
Japanese (ja)
Inventor
Takatsugu Kakeida
孝嗣 筧田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to JP34418099A priority Critical patent/JP2001161315A/en
Publication of JP2001161315A publication Critical patent/JP2001161315A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain a calcium preparation having high rate of absorption to animals or plants. SOLUTION: This calcium preparation is such as to have a baked calcium- containing raw material as active ingredient; wherein the calcium-contg. raw material is at least one kind selected from fossil seashells, cattle bones, fish bones, crab shells, oyster shells, egg shells, corals and specially selected white lime, and the baking temperature for the raw material is 400 deg.C to a temperature immediately below the melting point.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【発明の属する技術分野】本願は、カルシウム含有原料
を利用し吸収率の高い状態にしたカルシウム剤であっ
て、すべての生物のカルシウムの補給に適したカルシウ
ム剤に関する。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a calcium preparation made of a calcium-containing raw material and having a high absorption rate, which is suitable for replenishing calcium in all living organisms.

【0002】[0002]

【従来の技術】カルシウムは人体にとって重要な成分で
あり、生命健康を維持するためには不可欠なものであ
る。ところが、近年、食生活の変化によって、食物から
必要量のカルシウムを摂取することがなかなか困難とな
り、特に、骨を形成する妊婦や小児、さらには更年期の
女性は、カルシウム不足が深刻な問題となっている。
2. Description of the Related Art Calcium is an important component for the human body and is indispensable for maintaining life health. However, in recent years, changes in dietary habits have made it difficult to obtain the required amount of calcium from food.In particular, pregnant women and children who form bones, and even menopausal women, have a serious problem of calcium deficiency. ing.

【0003】一方、農作物の生育にとってもカルシウム
は重要である。特に、わが国は諸外国に比して降雨量が
多く、化学肥料の施用量が多いため塩基の流亡が激し
く、酸性土壌が広く分布しており、とりわけ、酸性に起
因する作物の生育不良を回避するだけでなく、植物栄養
としてもカルシウムの存在が不可欠である。
On the other hand, calcium is also important for growing crops. In particular, compared to other countries, Japan has higher rainfall and more fertilizer application rates, so that bases run wild and acid soils are widely distributed, and in particular, avoid poor growth of crops caused by acidity. In addition to calcium, the presence of calcium is essential for plant nutrition.

【0004】[0004]

【発明が解決しようとする課題】そこで本発明は前記事
情に基づきなされたものであり、動物や植物への吸収率
の高いカルシウム剤を提供することを目的とする。
Accordingly, the present invention has been made in view of the above circumstances, and has as its object to provide a calcium agent having a high absorption rate to animals and plants.

【0005】[0005]

【課題を解決するための手段】上記目的を達成するため
に、本発明のうち請求項1記載の発明によるカルシウム
剤は、カルシウム含有原料を焼成したものを有効成分と
していることを特徴とする。
Means for Solving the Problems To achieve the above object, the calcium agent according to the first aspect of the present invention is characterized in that a calcium-containing raw material is calcined as an active ingredient.

【0006】ここで、カルシウム含有原料を焼成したの
は、原料に含まれる不純物を可能な限り除去すると共
に、有効成分であるカルシウムをイオン化させ、生物へ
の吸収に適した性状に変化させるためである。
Here, the reason why the calcium-containing raw material is calcined is to remove impurities contained in the raw material as much as possible and to ionize calcium as an active ingredient to change it into a property suitable for absorption into living organisms. is there.

【0007】このように構成されるカルシウム剤は、有
効成分のカルシウムがイオン化し、これを服用すれば体
内において血液中にカルシウムイオンとして溶出してカ
ルシウム栄養素として摂取されるものである。また、こ
のように構成されるカルシウム剤を土壌に施用すれば、
土壌溶液中のカルシウムイオンの濃度が大幅に上がって
植物の栄養素としてのカルシウムを吸収することができ
る。
[0007] The calcium agent thus constituted is one in which calcium as an active ingredient is ionized and, when taken, elutes in the body as calcium ions in the blood and is taken in as calcium nutrients. Also, if the calcium agent composed in this way is applied to the soil,
The concentration of calcium ions in the soil solution can be greatly increased to absorb calcium as a plant nutrient.

【0008】本発明のうち請求項2記載の発明は、カル
シウム含有原料として、例えば、貝化石、牛骨、魚骨、
かに甲羅、かき(牡蠣)殻、卵殻、サンゴ、特選白石灰
のうち一種類又は複数種類を選択して使用することがで
きる。ここで特選白石灰とは、石灰石の一種であって陶
芸原料として用いられている。
The invention according to claim 2 of the present invention is characterized in that as the calcium-containing raw material, for example, shell fossils, bovine bone, fish bone,
One or more of crab shell, oyster shell, eggshell, coral, and special white lime can be selected and used. Here, the special white lime is a kind of limestone and is used as a raw material for pottery.

【0009】さらに、請求項3記載の発明のように、焼
成温度を400℃から各カルシウム含有原料の融点の直
前温度の範囲内で焼成した前記各カルシウム含有原料
は、下記の表1に示すように、原料中のカルシウムがイ
オン化して飛躍的に生物体内へのカルシウムの吸収率が
向上するので、動物用及び植物用の栄養素を補給するた
めのカルシウム剤として使用することができる。特に、
各カルシウム含有原料の融点の直前温度の高温で焼成す
れば、各カルシウム含有原料中の不純物が燃えて除去さ
れ、カルシウムの含有率が高くなり、しかもカルシウム
のイオン濃度も大幅に上がって、生物体内へのカルシウ
ム吸収率が著しく向上し、最適なカルシウム剤を提供で
きる。融点の直前温度は各カルシウム含有原料によって
異なり、例えば、特選白石灰は1030℃であり、魚
骨、かに甲羅及び貝化石は1250℃であり、卵殻は1
260℃、牛骨は1270℃、かき殻及びサンゴは12
80℃である。
Further, the respective calcium-containing raw materials fired at a firing temperature of 400 ° C. to a temperature immediately before the melting point of each calcium-containing raw material according to the invention of claim 3 are as shown in Table 1 below. In addition, since calcium in the raw material is ionized and the absorption rate of calcium into living organisms is dramatically improved, it can be used as a calcium agent for supplementing nutrients for animals and plants. In particular,
If calcination is performed at a high temperature just before the melting point of each calcium-containing raw material, impurities in each calcium-containing raw material are burnt and removed, and the calcium content is increased, and the calcium ion concentration is significantly increased. Calcium absorption rate is remarkably improved, and an optimal calcium agent can be provided. The temperature immediately before the melting point depends on each calcium-containing raw material. For example, the special white lime is 1030 ° C, the fish bone, crab shell and shell fossil are 1250 ° C, and the eggshell is 1250 ° C.
260 ° C, beef bone 1270 ° C, husk and coral 12
80 ° C.

【0010】[0010]

【表1】 [Table 1]

【0011】ここで、焼成温度を上記の範囲に設定した
のは、焼成温度が400℃よりも低い温度である場合に
は、各カルシウム含有原料のイオン化の程度が少なくカ
ルシウム吸収率がカルシウム剤として使用するのには十
分な効果が期待できないからである。一方、焼成温度が
融点よりも高い温度では、各カルシウム含有原料の溶融
が始まり、ガラス状に固化してしまって特性が変化する
ので、カルシウム剤としての使用ができなくなるからで
ある。
Here, the reason why the calcination temperature is set in the above range is that when the calcination temperature is lower than 400 ° C., the degree of ionization of each calcium-containing raw material is small and the calcium absorptivity is a calcium agent. This is because a sufficient effect cannot be expected to be used. On the other hand, when the calcination temperature is higher than the melting point, each calcium-containing raw material starts to melt, solidifies into a glass state, and changes its properties, so that it cannot be used as a calcium agent.

【0012】[0012]

【発明の実施の形態】本発明によるカルシウム剤の一例
は次の製造工程を経て得ることができる。 (1)まず、さや鉢にカルシウム含有原料を入れ、これ
を窯の中に収容する。 (2)窯に火を入れ、徐々に温度を上げていきながら該
窯内の温度が1250℃になるまで24時間〜30時間
をかけてカルシウム含有原料を焼成する。 (3)そして、窯内の温度が1250℃に達した段階で
火を止めて焼成を停止する。 (4)焼成を停止した後、窯内でそのまま48時間放置
する。 (5)窯の中からカルシウム剤となる有効成分を取り出
し、該有効成分に精製水を加えたものをポットミル機内
に収容する。 (6)ポットミル機により精製水と共に有効成分を約4
8時間擦り合わせる。 (7)擦り合わせて微粉末化した有効成分を3日〜4日
間容器の中に保管する。 (8)このようにして保管した容器中には、泥状の沈殿
物と上澄液との二層に分かれ、上澄液を取り除いて有効
成分としての沈殿物を残す。 (9)容器から有効成分の沈殿物を取り出し、該沈殿物
は完全に自然乾燥することによって固まる。 (10)固まった有効成分を細かく砕くことによって、
所望する粉粒状の形態を有するカルシウム剤を得ること
ができる。
BEST MODE FOR CARRYING OUT THE INVENTION An example of a calcium agent according to the present invention can be obtained through the following production steps. (1) First, a calcium-containing raw material is put into a pod, and this is stored in a kiln. (2) Put the fire in the kiln and calcine the calcium-containing raw material over 24 to 30 hours until the temperature in the kiln becomes 1250 ° C. while gradually increasing the temperature. (3) Then, when the temperature in the kiln reaches 1250 ° C., the fire is stopped to stop firing. (4) After the firing is stopped, it is left in the kiln for 48 hours. (5) Take out an active ingredient to be a calcium agent from the kiln, and store a mixture of the active ingredient and purified water in a pot mill. (6) Using a pot mill machine, add about 4 active ingredients together with purified water.
Rub for 8 hours. (7) The active ingredient finely ground by rubbing is stored in a container for 3 to 4 days. (8) The container thus stored is separated into two layers, a mud-like precipitate and a supernatant, and the supernatant is removed to leave a precipitate as an active ingredient. (9) The precipitate of the active ingredient is taken out of the container, and the precipitate solidifies by completely air-drying. (10) By crushing the hardened active ingredient finely,
A calcium agent having a desired powdery morphology can be obtained.

【0013】[0013]

【実施例】次に、本発明の一実施例について説明する。
本実施例では、カルシウム含有原料として、富山県高岡
市五十辺地区で採掘した貝化石(白色、細砂状であり、
炭酸カルシウム80〜85%程度含む)を使用し、前述
の製造工程(1)〜(10)経てカルシウム剤を得た。
Next, an embodiment of the present invention will be described.
In this example, as a calcium-containing raw material, shell fossils (white, fine sand-like,
Using about 80 to 85% of calcium carbonate), a calcium agent was obtained through the above-described production steps (1) to (10).

【0014】このようにして得たカルシウム剤を男女3
3名の大人に、1日1回朝食後、0.3g(0.3g収
容のカプセルを使用)ずつ継続的に服用した。そして、
服用前の骨密度を測り、服用1ヶ月後、服用2ヶ月後、
服用3ヶ月後と順次測定したデータを下記の表2に示
す。このデータは、各服用者の年齢平均骨密度を「10
0」としたときの比較骨密度の割合(%)を示したもの
である。
The calcium preparation thus obtained was applied to male and female 3
After taking breakfast once a day, three adults continuously took 0.3 g (using a capsule containing 0.3 g) each. And
Measure the bone density before taking, 1 month after taking, 2 months after taking,
Table 2 below shows data measured sequentially three months after the administration. This data shows the age-average bone mineral density of each user as "10
It shows the ratio (%) of the comparative bone density when "0" is set.

【0015】[0015]

【表2】 [Table 2]

【0016】表2に示すように、前記の本カルシウム剤
を服用したすべての人に対して、老若男女を問わず、服
用後の骨密度割合が服用期間が長くなるに従って確実に
増え、顕著な改善がみられた。
As shown in Table 2, the percentage of bone mineral density after taking the drug increases steadily as the period of use increases, regardless of age or gender, for all the people who have taken the above calcium agent. Improvements have been seen.

【0017】前述と同様に貝化石の原料を焼成して製造
したカルシウム剤を土壌肥料として施用して収穫した農
作物の可食部と、生の貝化石、すなわち、貝化石をその
まま乾燥・粉砕したものを施用して収穫した農作物の可
食部分と、のカルシウムの含有している量の割合を比較
した結果を下記の表3に示してある。
In the same manner as described above, the edible portion of agricultural crops obtained by applying a calcium agent produced by calcining the raw material of shell fossils as a soil fertilizer and raw shell fossils, that is, shell fossils, were dried and ground as they were. Table 3 below shows the result of comparing the ratio of the amount of calcium contained in the edible portion of the crop harvested by applying the product.

【0018】[0018]

【表3】 [Table 3]

【0019】表3に示すように、各種作物について、貝
化石を400℃〜1250℃までの範囲で焼成したカル
シウム剤を肥料として施用したものは、生の貝化石を施
用したものに比し(前記カルシウム剤と同量を施用)、
作物の可食部分に含有しているカルシウム量が飛躍的な
割合で増大していることが分かる。特に、融点付近の1
250℃で焼成した場合には、一段とカルシウム含有量
の優れた作物を得ることができた。
As shown in Table 3, with respect to various crops, the application of a calcium agent obtained by calcining shell fossils at a temperature in the range of 400 ° C. to 1250 ° C. as a fertilizer is different from that obtained by applying raw shell fossils ( Apply the same amount as the calcium agent),
It can be seen that the amount of calcium contained in the edible portion of the crop is increasing at a dramatic rate. In particular, 1 near the melting point
When calcined at 250 ° C., it was possible to obtain a crop having an even higher calcium content.

【0020】[0020]

【発明の効果】本発明によるカルシウム剤によれば、カ
ルシウム含有原料を焼成することによって有効成分であ
るカルシウムをイオン化し、生物への吸収に適した性状
に変化させたので、人間や植物などの生物への栄養素と
してのカルシウム補給に優れた効果を有するものであ
る。
According to the calcium agent of the present invention, calcium, which is an active ingredient, is ionized by calcining a calcium-containing raw material and changed into a property suitable for absorption into living organisms. It has an excellent effect on calcium supplementation as a nutrient to living organisms.

───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 FI テーマコート゛(参考) C05D 3/02 C05D 3/02 Fターム(参考) 4B018 MD04 MD73 MD75 ME05 MF04 4C086 AA01 AA02 HA04 HA16 MA01 MA04 NA05 NA11 ZA96 4C087 AA01 AA02 BA02 BB04 BB16 BB18 BB29 BB33 BB46 BB61 CA01 MA01 NA05 NA11 ZA96 4H061 AA01 CC01 CC04 CC31 CC32 GG24 HH50 LL02 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) C05D 3/02 C05D 3/02 F term (Reference) 4B018 MD04 MD73 MD75 ME05 MF04 4C086 AA01 AA02 HA04 HA16 MA01 MA04 NA05 NA11 ZA96 4C087 AA01 AA02 BA02 BB04 BB16 BB18 BB29 BB33 BB46 BB61 CA01 MA01 NA05 NA11 ZA96 4H061 AA01 CC01 CC04 CC31 CC32 GG24 HH50 LL02

Claims (3)

【特許請求の範囲】[Claims] 【請求項1】 カルシウム含有原料を焼成したものを有
効成分とするカルシウム剤。
1. A calcium agent comprising a calcined calcium-containing raw material as an active ingredient.
【請求項2】 前記カルシウム含有原料は、貝化石、牛
骨、魚骨、かに甲羅、かき殻、卵殻、サンゴ、特選白石
灰のうち一種類又は複数種類である請求項1記載のカル
シウム剤。
2. The calcium agent according to claim 1, wherein the calcium-containing raw material is one or more of fossil shellfish, beef bone, fish bone, crab shell, oyster shell, eggshell, coral, and special white lime. .
【請求項3】 前記各カルシウム含有原料の焼成温度は
400℃から融点の直前温度の範囲である請求項1又は
2記載のカルシウム剤。
3. The calcium agent according to claim 1, wherein the calcination temperature of each calcium-containing raw material is in a range from 400 ° C. to a temperature immediately before a melting point.
JP34418099A 1999-12-03 1999-12-03 Calcium preparation Pending JP2001161315A (en)