JP2001106207A - Heat-shrinkable outer packaging material - Google Patents
Heat-shrinkable outer packaging materialInfo
- Publication number
- JP2001106207A JP2001106207A JP28670099A JP28670099A JP2001106207A JP 2001106207 A JP2001106207 A JP 2001106207A JP 28670099 A JP28670099 A JP 28670099A JP 28670099 A JP28670099 A JP 28670099A JP 2001106207 A JP2001106207 A JP 2001106207A
- Authority
- JP
- Japan
- Prior art keywords
- heat
- shrinkable
- sheet
- shrinkage
- exterior material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、例えば紙コップ、
ペットボトルなどの外装に好適な熱収縮性外装材に関す
るものである。TECHNICAL FIELD The present invention relates to a paper cup,
The present invention relates to a heat-shrinkable exterior material suitable for exteriors such as PET bottles.
【０００２】[0002]
【従来の技術】お湯を注ぐだけで飲食が可能になる即席
麺や即席スープなどの容器は、一般的には、発泡ポリス
チレンから形成されているが、かかる容器は、今日、環
境性等の観点で発泡ポリスチレンタイプから紙タイプへ
の移行が進められている。2. Description of the Related Art Containers such as instant noodles and instant soups, which can be eaten and drink simply by pouring hot water, are generally formed from expanded polystyrene. The shift from expanded polystyrene type to paper type is under way.
【０００３】また、自動販売機、売店等で販売されるコ
ーヒー等の飲料やアイスクリームなどの容器には紙製の
カップ型容器が用いられている。[0003] A paper cup-shaped container is used as a container for drinks such as coffee and ice creams sold at vending machines and shops.
【０００４】[0004]
【発明が解決しようとする課題】上記紙製の容器は断熱
性が低く、内容物の温度によって冷たかったり、熱かっ
たりして、長時間手で持っていることが困難である。一
方、上記紙製の容器に収容された内容物についても、熱
がすぐに放散してしまい、ホットコーヒー等がすぐに冷
めてしまったり、冷たいジュース等がすぐに温くなって
しまうという不都合がある。The paper container described above has low heat insulating properties, and is difficult to hold for a long time because it is cold or hot depending on the temperature of the contents. On the other hand, the contents contained in the paper container also have the disadvantage that heat is quickly dissipated and hot coffee or the like is quickly cooled or cold juice or the like is immediately heated. .
【０００５】特に、上述の即席麺の紙容器は、一定の断
熱性が要求されるため、２層、３層等の複雑な構造にし
なければならず、製造性が悪化し、コスト的にも高くな
っている。[0005] In particular, the instant noodle paper container described above is required to have a certain heat insulating property, so that it must have a complicated structure such as two layers or three layers, which deteriorates manufacturability and costs. Is getting higher.
【０００６】本発明はこれらの不都合に鑑みてなされた
ものであり、例えば紙製等の容器へのシュリンク包装と
同時に、当該容器の断熱性を大きくできる熱収縮性外装
材の提供を目的とするものである。[0006] The present invention has been made in view of these disadvantages, and it is an object of the present invention to provide a heat-shrinkable exterior material capable of increasing the heat insulating property of a container at the same time as shrink packaging in a container made of paper or the like. Things.
【０００７】[0007]
【課題を解決するための手段】上記課題を解決するため
になされた発明は、熱収縮率が異なる高収縮性シートと
低収縮性シートとが部分的に塗布された接着剤で重着さ
れている熱収縮性外装材である。Means for Solving the Problems According to the invention made to solve the above problems, a high shrinkage sheet and a low shrinkage sheet having different heat shrinkage rates are overlaid with an adhesive partially applied thereto. Heat shrinkable exterior material.
【０００８】この熱収縮性外装材を用い、包装対象たる
物品に巻き付け、加熱トンネルやガスバーナーで熱を加
えることで、熱収縮率が大きい高収縮性シートが収縮し
て物品に密着し、シュリンク包装が完成する。このと
き、重着されている他方の低収縮性シートは、上記高収
縮性シートよりも熱収縮率が低いので、高収縮性シート
と部分的に接着している接着剤塗布部を起点に湾曲す
る。そのため、当該熱収縮性外装材の高収縮性シートと
低収縮性シートとの間に空間が形成され、この空間が断
熱層となる。従って、当該熱収縮性外装材を用いたシュ
リンク包装は、当該シュリンク包装と同時に包装物品に
断熱効果を付与することができる。Using this heat-shrinkable exterior material, the heat-shrinkable sheet is wound around an article to be packaged, and heat is applied thereto by a heating tunnel or a gas burner. The packaging is completed. At this time, the other low-shrinkable sheet that has been adhered has a lower heat shrinkage than the above-described high-shrinkage sheet, and thus curves from the adhesive-applied portion that is partially adhered to the high-shrinkage sheet. I do. Therefore, a space is formed between the high-shrinkable sheet and the low-shrinkable sheet of the heat-shrinkable exterior material, and this space becomes a heat insulating layer. Therefore, the shrink wrapping using the heat-shrinkable exterior material can provide the packaged article with a heat insulating effect simultaneously with the shrink wrapping.
【０００９】なお、当該熱収縮性外装材は、高収縮性シ
ートを包装物品側にしてシュリンク包装してもよく、逆
に、低収縮性シートを包装物品側にしてシュリンク包装
してもよい。高収縮性シートを物品側にしてシュリンク
包装すると、物品にぴったり密着したシュリンク包装が
可能になり、また、低収縮性シートの湾曲に対する抵抗
がなく、上記断熱空間の形成が容易になる。一方、低収
縮性シートを物品側にしてシュリンク包装すると、物品
の外周と低収縮性シートとの間にも空間が形成されるた
め、より断熱効果が促進される。The heat-shrinkable exterior material may be shrink-wrapped with the high-shrinkage sheet facing the packaged article, or may be shrink-wrapped with the low-shrinkage sheet facing the packaged article. When the high-shrinkable sheet is shrink-wrapped on the side of the article, shrink-wrapping that is tightly adhered to the article is possible, and the heat-insulating space is easily formed without resistance to bending of the low-shrinkage sheet. On the other hand, when the low-shrinkable sheet is shrink-wrapped with the article side, a space is formed between the outer periphery of the article and the low-shrinkage sheet, so that the heat insulating effect is further promoted.
【００１０】上記接着剤の塗布形態をストライプ状にす
るとよい。この手段によれば、当該熱収縮性外装材の高
収縮性シートと低収縮性シートとの間にトンネル状の断
熱空間が形成される。そのため、当該熱収縮性外装材
は、このストライプ状の接着剤塗布部と垂直方向に収縮
させた場合に上記トンネル状の断熱空間が形成されやす
い。従って、当該手段の熱収縮性外装材は、収縮方向が
一方向に大きいシュリンク包装の包装材料に好適であ
る。Preferably, the adhesive is applied in a stripe form. According to this means, a tunnel-like heat insulating space is formed between the high-shrinkable sheet and the low-shrinkable sheet of the heat-shrinkable exterior material. Therefore, when the heat-shrinkable exterior material is shrunk in a direction perpendicular to the stripe-shaped adhesive applied portion, the tunnel-shaped heat insulating space is easily formed. Therefore, the heat-shrinkable exterior material of the means is suitable for a shrink wrapping material in which the shrinkage direction is large in one direction.
【００１１】また、上記接着剤の塗布形態を格子状にし
てもよい。この手段によれば、当該熱収縮性外装材の高
収縮性シートと低収縮性シートとの間に略四角錐状の断
熱空間が形成される。そのため、例えばカップ型容器の
外周に当該熱収縮性外装材によるシュリンク包装を施し
た場合、当該カップ型容器又は把持する手に点状に接す
るため、断熱効果を向上させることができる。The adhesive may be applied in a grid form. According to this means, a substantially quadrangular pyramid-shaped heat insulating space is formed between the high-shrinkable sheet and the low-shrinkable sheet of the heat-shrinkable exterior material. Therefore, for example, when shrink wrapping with the heat-shrinkable exterior material is performed on the outer periphery of the cup-shaped container, the heat-shrinkable packaging material comes into contact with the cup-shaped container or the hand to be gripped in a dotted manner, so that the heat insulating effect can be improved.
【００１２】さらに、上記接着剤の塗布形態を散点状に
してもよい。この手段によれば、当該熱収縮性外装材の
高収縮性シートと低収縮性シートとの間に略層状の断熱
空間が形成される。また、当該熱収縮性外装材は、接着
剤塗布部である高収縮性シートと低収縮性シートとの連
結個所が少なく、断熱効果を向上させる作用がある。ま
た、当該熱収縮性外装材は、いかなる方向へ収縮させる
場合でも、上述の断熱空間を形成することができる。Further, the application form of the adhesive may be a dotted form. According to this means, a substantially layered heat-insulating space is formed between the high-shrinkable sheet and the low-shrinkable sheet of the heat-shrinkable exterior material. In addition, the heat-shrinkable exterior material has few connecting points between the high-shrinkage sheet and the low-shrinkage sheet, which are the adhesive application portions, and has an effect of improving the heat insulating effect. In addition, the heat-shrinkable exterior material can form the above-described heat-insulating space even when shrunk in any direction.
【００１３】上記高収縮性シートの熱収縮率としては、
３０％以上８０％以下が好ましい。これは、高収縮性シ
ートの熱収縮率が８０％を超えると、低収縮性シートの
非接着部分に形成される山が高くなりすぎて、断熱空間
の十分な強度が得られなくなってしまい、逆に、３０％
未満になると、低収縮性シートの湾曲ひいては断熱空間
が小さく、十分な断熱性を得ることができなくなること
からである。The heat shrinkage of the highly shrinkable sheet is as follows:
It is preferably from 30% to 80%. This is because, when the heat shrinkage of the high shrinkage sheet exceeds 80%, the peaks formed on the non-adhesive portion of the low shrinkage sheet become too high, so that sufficient strength of the heat insulating space cannot be obtained, Conversely, 30%
When the value is less than the above, the curvature of the low-shrinkage sheet and, consequently, the heat insulating space are small, and it becomes impossible to obtain sufficient heat insulating properties.
【００１４】一方、上記低収縮性シートの熱収縮率とし
ては、３０％未満が好ましい。これは、低収縮性シート
の熱収縮率が３０％以上になると、収縮時に低収縮性シ
ートと高収縮性シートとの間にあまりひずみが発生せ
ず、十分な断熱空間が形成されなくなることからであ
る。On the other hand, the heat shrinkage rate of the low shrinkage sheet is preferably less than 30%. This is because, when the heat shrinkage of the low-shrinkable sheet is 30% or more, little strain is generated between the low-shrinkage sheet and the high-shrinkage sheet during shrinkage, and a sufficient heat insulating space is not formed. It is.
【００１５】[0015]
【発明の実施の形態】以下、適宜図面を参照しつつ本発
明の実施の形態を詳説する。図１は本発明の一実施形態
に係る熱収縮性外装材を示す模式的断面図である。図１
の熱収縮性外装材１は、低収縮性シート２と高収縮性シ
ート３とが重ね合わされており、両シート２、３は部分
的に塗布された接着剤４で部分的に接着されている。Embodiments of the present invention will be described below in detail with reference to the drawings as appropriate. FIG. 1 is a schematic sectional view showing a heat-shrinkable exterior material according to one embodiment of the present invention. FIG.
The heat-shrinkable exterior material 1 has a low-shrinkage sheet 2 and a high-shrinkage sheet 3 overlapped with each other, and the two sheets 2 and 3 are partially adhered by an adhesive 4 partially applied. .
【００１６】上記高収縮性シート３は、上述のように熱
収縮率が３０％以上８０％以下のものが好ましく、かか
る範囲の熱収縮率が確保できれば種々の材質が適用可能
である。中でも、ポリ塩化ビニル、ポリプロピレン、ポ
リエステル、ポリスチレン及びポリエチレンが好まし
く、これらの群より選択される１種または２種以上のも
のを用いることができる。かかる材料は、熱収縮性が高
く、しかも防塵性、防水性に優れている。As described above, the high shrinkable sheet 3 preferably has a heat shrinkage of 30% or more and 80% or less, and various materials can be applied as long as the heat shrinkage in such a range can be secured. Among them, polyvinyl chloride, polypropylene, polyester, polystyrene and polyethylene are preferable, and one or more kinds selected from these groups can be used. Such a material has high heat shrinkage and is excellent in dustproofness and waterproofness.
【００１７】低収縮性シート２は、上述のように熱収縮
率が３０％未満のものが好ましく、材料としては紙素
材、合成樹脂フィルム等を用いることができる。当該低
収縮性シート２に使用可能な紙素材としては、例えば未
晒クラフト紙、晒クラフト紙、上質紙、中質紙、片艶未
晒クラフト紙、純白ロール、グラシン紙、感熱紙、感圧
紙、合成紙、和紙、トレーシングペーパー、各種コート
紙、板紙、ライナー紙、クレープ加工紙等が挙げられ
る。但し、後述するように当該低収縮性シート２が湾曲
して断熱空間を形成するため、所定の強度及び腰が必要
であり、かかる点を考慮すると、紙素材としては上質紙
が好適であり、その秤量も、３０ｇ／ｍ2以上３００ｇ
／ｍ2以下の範囲が好ましい。As described above, the low shrinkage sheet 2 preferably has a heat shrinkage of less than 30%, and may be a paper material, a synthetic resin film, or the like. Examples of paper materials that can be used for the low-shrinkage sheet 2 include unbleached kraft paper, bleached kraft paper, high-quality paper, medium-grade paper, single gloss unbleached kraft paper, pure white roll, glassine paper, heat-sensitive paper, and pressure-sensitive paper. , Synthetic paper, Japanese paper, tracing paper, various coated papers, paperboard, liner paper, creped paper and the like. However, since the low-shrinkable sheet 2 is curved to form a heat insulating space as described later, a predetermined strength and waist are necessary. In view of this point, high quality paper is preferable as the paper material. weighed also, 30g / m 2 or more 300g
/ M 2 or less.
【００１８】また低収縮性シート２に使用可能な合成樹
脂としては、例えばポリエチレン、ポリプロピレン、ポ
リメチルペンテン、エチレン酢酸ビニル樹脂、ポリアミ
ド樹脂、エチレンエチルアクリレート樹脂、エチレンア
クリル酸樹脂、エチレンメタクリル酸樹脂、エチレンア
クリル酸メチル樹脂、アイオノマー樹脂、ポリビニルア
ルコール、ポリエステル等が挙げられる。またいわゆる
メタロセン触媒を用いて重合されたポリエチレン、ポリ
プロピレン等も、好適に用いることができる。低収縮性
シート２に合成樹脂フィルムを用いる場合、この合成樹
脂フィルムの厚みは特には限定されないが、上述のよう
に湾曲して断熱空間が形成できる強度、弾力が必要であ
り、一般的には８μｍ以上２００μｍ以下程度とされ
る。Examples of the synthetic resin usable for the low-shrinkage sheet 2 include polyethylene, polypropylene, polymethylpentene, ethylene vinyl acetate resin, polyamide resin, ethylene ethyl acrylate resin, ethylene acrylic resin, ethylene methacrylic resin, and the like. Examples include ethylene methyl acrylate resin, ionomer resin, polyvinyl alcohol, polyester and the like. Further, polyethylene, polypropylene and the like polymerized using a so-called metallocene catalyst can also be suitably used. When a synthetic resin film is used for the low-shrinkable sheet 2, the thickness of the synthetic resin film is not particularly limited, but the synthetic resin film needs to have strength and elasticity capable of forming a heat insulating space by being curved as described above. It is about 8 μm or more and about 200 μm or less.
【００１９】接着剤４は、特に限定されるものではな
く、例えば、デンプン、にかわ、カゼイン、天然ゴム、
セラック、タールなどの天然物、及び熱可塑性や熱硬化
性の合成樹脂、合成ゴムなどの合成物を用いることがで
きる。また接着剤４は、（ａ）水や溶剤の蒸発によって
固化する一般的なものの他、（ｂ）エポキシやポリウレ
タン系のような２液反応型接着剤、（ｃ）空気中の水分
により高速でアニオン重合して固化するα−シアノアク
リラート型などの瞬間接着剤、（ｄ）エチレン−酢酸ビ
ニル共重合体、ポリアミド、ポリエステルなどのホット
メルト接着剤なども可能である。The adhesive 4 is not particularly limited. For example, starch, glue, casein, natural rubber,
Natural products such as shellac and tar, and synthetic products such as thermoplastic and thermosetting synthetic resins and synthetic rubbers can be used. The adhesive 4 is (a) a general one that solidifies by evaporating water or a solvent, (b) a two-part reactive adhesive such as an epoxy or polyurethane-based adhesive, and (c) a high-speed adhesive due to moisture in the air. Instantaneous adhesives such as α-cyanoacrylate which solidify by anionic polymerization, and hot melt adhesives such as (d) ethylene-vinyl acetate copolymer, polyamide and polyester are also possible.
【００２０】当該熱収縮性外装材１は、図２（ａ）に示
すように、カップ型容器のシュリンク包装用にしたもの
であり、外形が略円筒状のカップ型容器をシュリンク包
装するため、かかるカップ型容器より大きいサイズの円
筒状に形成されている。この熱収縮性外装材１は、高収
縮性シート３が内側に、低収縮性シート２が外側になる
よう配設され、接着剤４が円筒の軸方向に向けてストラ
イプ状に塗布されている。As shown in FIG. 2 (a), the heat-shrinkable exterior material 1 is used for shrink-wrapping a cup-shaped container. It is formed in a cylindrical shape having a size larger than the cup-shaped container. The heat-shrinkable exterior material 1 is disposed such that the high-shrinkage sheet 3 is on the inside and the low-shrinkage sheet 2 is on the outside, and the adhesive 4 is applied in a stripe shape in the axial direction of the cylinder. .
【００２１】次に、当該熱収縮性外装材１を用いたシュ
リンク包装について説明する。まず当該熱収縮性外装材
１を、図２（ａ）に示すようにカップ型容器５の外側に
中心軸が一致するように被せる。その後、加熱トンネル
やガスバーナーで熱を加えることによって、図２（ｂ）
に示すようにカップ型容器５のシュリンク包装が完成す
る。Next, shrink wrapping using the heat-shrinkable exterior material 1 will be described. First, the heat-shrinkable exterior material 1 is placed on the outside of the cup-shaped container 5 so that the central axes thereof are aligned as shown in FIG. Then, by applying heat with a heating tunnel or a gas burner, the heat is applied as shown in FIG.
As shown in (1), the shrink wrapping of the cup type container 5 is completed.
【００２２】上述のようにシュリンク包装されたカップ
型容器５の外周には、図３に示すように、当該熱収縮性
外装材１の高収縮性シート３が収縮して密着する。一
方、低収縮性シート２は、高収縮性シート３より熱収縮
率が低く、高収縮性シート３よりも熱収縮しないので、
高収縮性シート３と部分的に接着されている接着剤４塗
布部を起点として湾曲し、トンネル状の断熱空間６が形
成される。接着剤４の塗布形態がカップ型容器５の軸方
向と平行なストライプ状であるため、かかるトンネル状
の断熱空間６もカップ型容器５の軸方向と平行なストラ
イプ状に形成される。As shown in FIG. 3, the high-shrinkable sheet 3 of the heat-shrinkable exterior material 1 shrinks and adheres to the outer periphery of the cup-shaped container 5 shrink-wrapped as described above. On the other hand, the low-shrinkage sheet 2 has a lower heat shrinkage than the high-shrinkability sheet 3 and does not shrink more than the high-shrinkability sheet 3.
A curved heat-insulating space 6 is formed starting from the adhesive 4 applied portion partially adhered to the high-shrinkable sheet 3 to form a tunnel-shaped heat insulating space 6. Since the application form of the adhesive 4 is a stripe shape parallel to the axial direction of the cup-shaped container 5, the tunnel-shaped heat insulating space 6 is also formed in a stripe shape parallel to the axial direction of the cup-shaped container 5.
【００２３】このように、当該熱収縮性外装材１による
シュリンク包装を施せば、カップ型容器５の外周に断熱
空間６が形成され、単純な構造の紙製のカップ型容器５
の断熱性を向上させることができる。そのため、当該カ
ップ型容器５に入れたものの保温性が向上でき、かつ、
当該カップ型容器５を把持した手に内部の熱が伝達し難
いので、把持を容易にする。As described above, when the shrink wrapping is performed by the heat-shrinkable exterior material 1, the heat insulating space 6 is formed on the outer periphery of the cup-shaped container 5, and the paper-made cup-shaped container 5 having a simple structure is formed.
Can be improved in heat insulation. Therefore, the heat retention of the container placed in the cup type container 5 can be improved, and
Since the internal heat is hardly transmitted to the hand holding the cup-shaped container 5, the holding is facilitated.
【００２４】なお、本発明の熱収縮性外装材は上記実施
形態に限定されるものではなく、例えば、接着剤４の塗
布形態は、上述のようにストライプ状に限定されず、高
収縮性シート３が熱収縮したときに、低収縮性シート２
の非接着部分が湾曲して断熱空間を形成しやすいように
塗布すればよく、例えば、格子状、散点状なども可能で
ある。The heat-shrinkable exterior material of the present invention is not limited to the above embodiment. For example, the application form of the adhesive 4 is not limited to the striped shape as described above, but may be a highly shrinkable sheet. When the heat-shrinkable sheet 3 shrinks, the low-shrinkable sheet 2
It may be applied so that the non-adhesive portion is curved to easily form a heat insulating space. For example, a lattice shape, a scattered point shape, or the like can be used.
【００２５】[0025]
【発明の効果】以上説明したように、本発明の熱収縮性
外装材によれば、包装と同時に断熱効果が付与でき、ま
た、断熱効果を得るための構造もシンプルであり、製造
コストの削減が可能になる。As described above, according to the heat-shrinkable exterior material of the present invention, a heat insulating effect can be imparted at the same time as packaging, and the structure for obtaining the heat insulating effect is simple, so that the manufacturing cost can be reduced. Becomes possible.
【図１】本発明の一実施形態に係る熱収縮性外装材を示
す模式的断面図である。FIG. 1 is a schematic sectional view showing a heat-shrinkable exterior material according to an embodiment of the present invention.
【図２】（ａ）は図１の熱収縮性外装材を用いてシュリ
ンク包装する過程を説明する斜視図で、（ｂ）は図１の
熱収縮性外装材によるシュリンク包装が完成した状態を
示す斜視図である。2 (a) is a perspective view illustrating a process of shrink wrapping using the heat-shrinkable exterior material of FIG. 1, and FIG. 2 (b) shows a state in which the shrink wrapping by the heat-shrinkable exterior material of FIG. 1 is completed. FIG.
【図３】図１の熱収縮性外装材によるシュリンク包装が
完成した状態を示す部分的横断面図である。FIG. 3 is a partial cross-sectional view showing a state in which shrink wrapping with the heat-shrinkable exterior material of FIG. 1 is completed.
１ 熱収縮性外装材 ２ 低収縮性シート ３ 高収縮性シート ４ 接着剤 ５ カップ型容器 ６ 断熱空間 DESCRIPTION OF SYMBOLS 1 Heat-shrinkable exterior material 2 Low-shrinkage sheet 3 High-shrinkage sheet 4 Adhesive 5 Cup-type container 6 Insulated space
フロントページの続き Ｆターム(参考） 4F100 AJ07G AJ08G AK04A AK04B AK07A AK07B AK12A AK15A AK25B AK41A AK46B AK51G AK68B AK68G AN01G AR00A AR00B BA02 BA10A BA10B BA26 BA32 DG10B GB16 JA03A JA03B JJ02 YY00A YY00B Continued on the front page F-term (reference) 4F100 AJ07G AJ08G AK04A AK04B AK07A AK07B AK12A AK15A AK25B AK41A AK46B AK51G AK68B AK68G AN01G AR00A AR00B BA02 BA10A BA10B BA26 BA32 DG10Y00 GBA
Claims (6)
縮性シートとが部分的に塗布された接着剤で重着されて
いる熱収縮性外装材。1. A heat-shrinkable exterior material in which a high-shrinkage sheet and a low-shrinkage sheet having different heat-shrinkage rates are overlaid with a partially applied adhesive.
ある請求項１に記載の熱収縮性外装材。2. The heat-shrinkable exterior material according to claim 1, wherein the adhesive is applied in a stripe form.
求項１に記載の熱収縮性外装材。3. The heat-shrinkable exterior material according to claim 1, wherein the adhesive is applied in a lattice form.
求項１に記載の熱収縮性外装材。4. The heat-shrinkable exterior material according to claim 1, wherein the adhesive is applied in a scattered dot form.
以上８０％以下である請求項１から請求項４のいずれか
１項に記載の熱収縮性外装材。5. The heat-shrinkable sheet having a heat shrinkage of 30%.
The heat-shrinkable exterior material according to any one of claims 1 to 4, which is not less than 80%.
未満である請求項１から請求項５のいずれか１項に記載
の熱収縮性外装材。6. The heat shrinkage rate of the low shrinkage sheet is 30%.
The heat-shrinkable exterior material according to any one of claims 1 to 5, wherein the heat-shrinkable exterior material is less than.