JP2000189345A - Toilet seat having good antifoulancy - Google Patents
Toilet seat having good antifoulancyInfo
- Publication number
- JP2000189345A JP2000189345A JP10371563A JP37156398A JP2000189345A JP 2000189345 A JP2000189345 A JP 2000189345A JP 10371563 A JP10371563 A JP 10371563A JP 37156398 A JP37156398 A JP 37156398A JP 2000189345 A JP2000189345 A JP 2000189345A
- Authority
- JP
- Japan
- Prior art keywords
- toilet seat
- lubricant
- dirt
- toilet
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【発明の属する技術分野】本発明は防汚性に優れた便座
或いは局部洗浄便座に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a toilet seat or a local cleaning toilet seat having excellent antifouling properties.
【0002】[0002]
【従来の技術】従来、便座シート、便蓋、本体ケース等
の便座或いは局部洗浄便座の露出構成部品は、一般に、
アクリロニトリル−ブタジエン−スチレン樹脂(以下、
ABSと略する)もしくはポリプロピレン(以下、PP
と略する)の成形品で主に構成されている。2. Description of the Related Art Conventionally, exposed components of a toilet seat such as a toilet seat sheet, a toilet lid, and a main body case or a local cleaning toilet seat are generally formed as follows.
Acrylonitrile-butadiene-styrene resin (hereinafter, referred to as
ABS) or polypropylene (PP)
).
【0003】[0003]
【発明が解決しようとする課題】従来の便座或い局部洗
浄便座の場合、男性が小便をする場合は主として便座シ
ートを上げた状態で使用するため、便座シートの裏面や
本体ケースの前面部に小便がかかることがある。大便を
する場合は、便器内に落下した大便が便器内の水を跳ね
返し、便座シートの裏面に汚物や水が付着する場合があ
る。また、使用時に皮膚の触れる便座シートの表面や便
蓋についても、皮脂等の皮膚の汚れ等が付着する。In the case of a conventional toilet seat or a local flush toilet seat, when a man urinates, the toilet seat is mainly used while the toilet seat is raised. Pissing may occur. In the case of stool, stool that has fallen into the toilet bowl rebounds water in the toilet bowl, and dirt and water may adhere to the back surface of the toilet seat sheet. Further, skin dirt such as sebum adheres to the surface of the toilet seat sheet and the toilet lid that come into contact with the skin during use.
【0004】このように便座部材は、日常使用するにあ
たって、汚れ易いという状況がある。しかし汚れ成分の
組成、樹脂成形体が汚れるメカニズムは複雑であり、十
分な解明はなされていない。 一般的には、人体に由来
する油類および油性成分や蛋白質、ほこり類、水および
水溶性成分、洗剤などの界面活性剤などが挙げられ、こ
れらの成分が単一にまたは複合した状態で、汚れとして
認識される。その状態は以下のように区分できる。 樹脂成形体の表面の凹凸の中に埋まった状態。 樹脂成形体の表面分子と汚れの分子の分子間引力によ
る状態 樹脂成形体の表面分子と汚れの分子が化学結合した状
態 樹脂成形体の内部に汚れが浸透または拡散した状態 樹脂成形体の帯電によって静電気的に付着した状態 汚れ成分の粘着成分によって付着した状態 一方、生活環境中では、汚れが全く付かないという状態
を作り出す事は難しく、汚れが付き難く、汚れが付いた
場合は付いた汚れが取れ易い、掃除がしやすい、と言っ
た事が重要である。[0004] As described above, there is a situation in which the toilet seat member is easily soiled in daily use. However, the composition of the stain component and the mechanism by which the resin molded article is stained are complicated and have not been sufficiently elucidated. In general, oils and oily components and proteins derived from the human body, dust, water and water-soluble components, detergents such as detergents, and the like, in the state of these components alone or in combination, Recognized as dirt. The state can be classified as follows. A state of being buried in the irregularities on the surface of the resin molding. The state due to the intermolecular attraction between the surface molecules of the resin molded article and the dirt molecules The state in which the surface molecules of the resin molded article and the dirt molecules are chemically bonded The state in which dirt has penetrated or diffused inside the resin molded article On the other hand, in the living environment, it is difficult to create a state in which no dirt is attached, it is difficult to get dirt, and if dirt is attached, the dirt attached It is important to say that it is easy to remove and easy to clean.
【0005】しかし、これらの汚れを除去する従来の清
掃方法では、樹脂成形体がABS樹脂の場合、耐洗剤性
に劣るため洗剤に繰り返し晒されるとソルベントクラッ
クが発生したり、樹脂成形体がPP樹脂の場合、耐擦傷
性に劣るため拭き取り時に表面に傷が付く等の問題があ
った。However, in the conventional cleaning method for removing these stains, when the resin molded article is made of ABS resin, the resin molded article is inferior in detergent resistance, so that solvent cracks occur when the resin molded article is repeatedly exposed to the detergent, or the resin molded article becomes PP. In the case of resin, there is a problem that the surface is scratched at the time of wiping because of poor scratch resistance.
【0006】本発明者らは、上記課題を解決すべく鋭意
研究を続けてきた。その結果、樹脂の中に滑剤を混入す
ることで従来と同様な樹脂成形条件で成形可能であり、
汚れが付いた場合は付いた汚れが拭き取れ易く、樹脂成
形体表面に傷がつかないことを見いだした。したがっ
て、本発明は防汚性に優れた便座或いは局部洗浄便座を
提供することを目的とする。[0006] The present inventors have intensively studied to solve the above problems. As a result, it is possible to mold under the same resin molding conditions as before by mixing a lubricant into the resin,
When stains were found, it was found that the stains were easily wiped off and the resin molded body surface was not damaged. Therefore, an object of the present invention is to provide a toilet seat or a local cleaning toilet seat having excellent antifouling properties.
【0007】[0007]
【課題を解決するための手段】上記目的を達成するため
になされた請求項1記載の発明は、便座シート、便蓋、
本体ケース等の便座の露出構成部品の構成材料の少なく
とも一部材が、樹脂の中に滑剤を混入した樹脂成形体で
構成された便座であることを特徴とする。According to the first aspect of the present invention, there is provided a toilet seat, a toilet lid,
At least one member of a constituent material of an exposed component of a toilet seat such as a main body case is a toilet seat formed of a resin molded body in which a lubricant is mixed in a resin.
【0008】上記目的を達成するためになされた請求項
2記載の発明は、便座シート、便蓋、本体ケース、洗浄
ノズル等の便座の露出構成部品の構成材料の少なくとも
一部材が、樹脂の中に滑剤を混入した樹脂成形体で構成
された局部洗浄便座であることを特徴とする。According to a second aspect of the present invention, there is provided a toilet seat including a toilet seat, a toilet lid, a main body case, and a cleaning nozzle. It is a local cleaning toilet seat made of a resin molded body mixed with a lubricant.
【0009】請求項3記載の発明は、滑剤をもとの母材
樹脂100重量部に対して0.03〜5重量部混入した
ことを特徴とする。The invention according to claim 3 is characterized in that 0.03 to 5 parts by weight of a lubricant is mixed with respect to 100 parts by weight of the base resin.
【0010】本発明は上記した構成により、便座シー
ト、便蓋、本体ケースなど露出構成部品についた汚れが
取れやすく掃除しやすくなり、また、防汚性に優れた便
座を提供できる。また従来と同様な樹脂成形条件で成形
可能であり、塗装、乾燥、硬化といった成形とは別の工
程が不必要である。また、表面硬度低下もほとんどない
ため従来と同様の構造でも高い防汚性および傷付き性を
持つ便座を提供できる。According to the present invention, with the above-described structure, it is easy to remove dirt on exposed components such as a toilet seat sheet, a toilet lid, and a main body case, and it is easy to clean the toilet seat. Further, it can be molded under the same resin molding conditions as in the past, and does not require another process such as painting, drying, and curing. Further, since there is almost no decrease in surface hardness, a toilet seat having high antifouling property and scratch resistance can be provided even with the same structure as the conventional one.
【0011】簡単に汚れの除去掃除ができるため汚れが
栄養源となる雑菌等の増殖も減少する。[0011] Since dirt can be easily removed and cleaned, the growth of germs and the like, from which dirt becomes a nutrient source, also decreases.
【0012】簡単に汚れの除去掃除ができるため掃除に
強い洗剤を用いる必要がなく、耐洗剤性に劣る樹脂を母
材として使用した場合でも洗剤によるソルベントクラッ
ク発生等がなくなる。Since dirt can be easily removed and cleaned, there is no need to use a detergent that is strong in cleaning. Even when a resin having poor detergent resistance is used as a base material, generation of solvent cracks or the like due to the detergent is eliminated.
【0013】簡単に汚れの除去掃除ができるため掃除の
際、強い力で何度も擦る作業が必要なく、耐擦傷性に劣
る樹脂を母材として使用した場合でも成形体表面への傷
付き等がなくなる。Since it is easy to remove and clean dirt, there is no need to repeatedly rub with strong force during cleaning, and even if a resin having poor scratch resistance is used as a base material, scratches on the surface of the molded body may occur. Disappears.
【0014】[0014]
【実施例】以下本発明を実施例により詳細に説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in detail with reference to embodiments.
【0015】図1は本発明の実施形態の一例としての局
部洗浄便座((a);便座を上から見た図、(b);便座を横か
ら見た図)を示す。1は便座シート、2は便蓋、3は本
体ケース、4は局部を洗浄する洗浄ノズルである。FIG. 1 shows a local flush toilet seat ((a); a view of the toilet seat from above, and (b); a view of the toilet seat from the side) as an example of an embodiment of the present invention. 1 is a toilet seat sheet, 2 is a toilet lid, 3 is a main body case, 4 is a washing nozzle for washing a local part.
【0016】本発明における滑剤としては、パラフィン
ワックス、ポリエチレンワックス等の炭化水素系滑剤、
ステアリルアルコール、ステアリン酸、12-ヒドロキ
システアリン酸等の脂肪族アルコール系,脂肪酸系滑
剤、ステアリン酸アミド、オレイン酸アミド、エルカ酸
アミド等の脂肪族アミド系滑剤、ステアリン酸Ca、ステ
アリン酸Zn等の金属石鹸系滑剤、ステアリン酸ブチル、
ステアリルステアート等のエステル系滑剤、ステアリン
酸モノグリセリド等の脂肪酸と多価アルコールの部分エ
ステル系滑剤などが挙げられるがこれに限定するもので
はない。As the lubricant in the present invention, hydrocarbon lubricants such as paraffin wax and polyethylene wax,
Fatty alcohols such as stearyl alcohol, stearic acid and 12-hydroxystearic acid, fatty acid lubricants, stearic acid amides, oleic acid amides, aliphatic amide lubricants such as erucic acid amides, stearic acid Ca, stearic acid Zn and the like Metal soap lubricant, butyl stearate,
Examples thereof include, but are not limited to, ester lubricants such as stearyl steate, and partial ester lubricants of fatty acids such as stearic acid monoglyceride and polyhydric alcohols.
【0017】滑剤の配合割合は、母材樹脂100重量部
あたり0.03〜5重量部、望ましくは0.1〜3重量
部であることが良い。滑剤を配合することにより、樹脂
成形体表面のすべりが良くなり表面の傷付きを防止し、
さらに樹脂成形体に付着した汚れ成分が取れやすくなる
ため防汚性能は高くなるが、その配合割合が低いと、滑
剤の効果が減少すること、また、配合割合が高くなりす
ぎると、樹脂成形体表面の白化等が発生し、便座に必要
な外観等の特性が満足できなくなる等の問題がある。The mixing ratio of the lubricant is preferably 0.03 to 5 parts by weight, more preferably 0.1 to 3 parts by weight, per 100 parts by weight of the base resin. By compounding a lubricant, the slip of the resin molded body surface is improved, preventing scratches on the surface,
In addition, the stain resistance attached to the resin molded body is easily removed, so that the antifouling performance is increased. However, if the blending ratio is low, the effect of the lubricant is reduced, and if the blending ratio is too high, the resin molded body is reduced. There is a problem that the surface such as whitening occurs, and the characteristics such as the appearance required for the toilet seat cannot be satisfied.
【0018】以下の実施例については、母材樹脂として
はPP、滑剤としてエルカ酸アミド(以下滑剤と略称す
る)を例として以下説明するが、本発明はこれらの実施
例に限定されるものではない。In the following examples, PP is used as a base resin and erucamide (hereinafter abbreviated as a lubricant) is used as an example of a lubricant. However, the present invention is not limited to these examples. Absent.
【0019】図2は本発明の実施例1〜3、比較例1〜
3の対比表(組成、防汚性、硬度、傷付き性)である。FIG. 2 shows Examples 1 to 3 and Comparative Examples 1 to 3 of the present invention.
3 is a comparison table (composition, antifouling property, hardness, and scratch resistance).
【0020】以下図2に基づき説明する。 実施例1〜3;PP100重量部と図2に示す量の滑剤
を良く混合し、成形機で成形して便座シートを得た。 比較例1;PPを実施例と同様に成形機で成形して便座
シートを得た。比較例2〜3;PP100重量部と図2
に示す量の滑剤を良く混合し、成形機で成形して便座シ
ートを得た。 各実施例、比較例で得た便座から試験片を切り出し、
防汚性(疑似汚物試験)、硬度(鉛筆硬度)、傷付き
性、外観について試験を行った。The operation will be described below with reference to FIG. Examples 1 to 3; 100 parts by weight of PP and the amount of the lubricant shown in FIG. 2 were mixed well, and molded with a molding machine to obtain a toilet seat sheet. Comparative Example 1 PP was molded with a molding machine in the same manner as in the example to obtain a toilet seat sheet. Comparative Examples 2-3: 100 parts by weight of PP and FIG.
The amount of the lubricant shown in (1) was well mixed and molded by a molding machine to obtain a toilet seat sheet. Each example, a test piece was cut out from the toilet seat obtained in the comparative example,
Tests were conducted for antifouling properties (pseudofiltration test), hardness (pencil hardness), scratch resistance, and appearance.
【0021】次に試験について説明する。 防汚性 ・疑似汚物試験;口腔染色ジェルと墨汁を用いて、下記
試験を行う。 墨汁−塗布後24時間放置、乾燥後、乾布拭きによる除
去の具合を目視によって観察し、比較例1における汚れ
具合を(△)とし、それより良い場合を(○)、悪い場
合(×)として評価した。Next, the test will be described. Antifouling property ・ Pseudo-fouling test: The following test is performed using oral dye gel and ink. The ink was left standing for 24 hours after application, dried, and then visually observed for the degree of removal by wiping with a dry cloth. The degree of dirt in Comparative Example 1 was indicated by (△), and a better case was indicated by (○) and a worse case was indicated by (X). evaluated.
【0022】硬度;100gの重りを用い鉛筆硬度計
により測定。Hardness: Measured with a pencil hardness tester using a 100 g weight.
【0023】耐傷つき性;便座を掃除する際使用する
可能性の高い、綿布、トイレットペーパーを用いて、摺
動部1cm2当たり1kgの荷重で試験片表面を10往
復擦り、耐傷つき性を評価した。なお、耐傷つき性の比
較は目視にて観察し、傷つきなしを(○)、摺動部全面
に傷を(×)、その中間を(△)として評価した。Scratch resistance: The surface of the test piece was rubbed 10 times with a load of 1 kg per 1 cm 2 of the sliding portion using a cotton cloth or toilet paper, which is likely to be used when cleaning the toilet seat, and the scratch resistance was evaluated. did. The scratch resistance was evaluated by visual observation, where no damage was evaluated (○), the entire surface of the sliding portion was evaluated as (x), and the middle was evaluated as (△).
【0024】外観;成形体表面の外観を目視にて比較
し、表面に白化がない場合を(○)、白化がある場合を
(×)として評価した。Appearance: The appearance of the surface of the molded article was visually compared, and evaluation was made when the surface was not whitened (() and when it was white (X).
【0025】図2に示す結果より本発明の滑剤を混入し
た樹脂成形体を使用することにより、防汚性、傷付き性
に優れ、しかも表面硬度の低下がほとんどないため、便
座用の材料として非常に優れることがわかった。From the results shown in FIG. 2, the use of the resin molded article mixed with the lubricant of the present invention has excellent antifouling properties and scratch resistance, and hardly reduces the surface hardness. It turned out to be very good.
【0026】なお、上記実施例および比較例の成形品は
便座シートであったが、便蓋、本体ケースあるいは洗浄
ノズルであっても同様な結果が得られる。Although the molded products of the above Examples and Comparative Examples are toilet seat sheets, similar results can be obtained by using a toilet lid, a main body case or a washing nozzle.
【0027】また、本発明により汚れが付着しにくく、
さらに汚れが取れやすく掃除しやすくなり、防汚性に優
れた便座を提供できるため、雑菌等の繁殖は低減する
が、発明の効果を損なわない程度で、無機系抗菌剤、有
機系抗菌剤、抗カビ剤を配合することができる。Further, the present invention makes it difficult for dirt to adhere,
In addition, it is easy to remove dirt, it is easy to clean, and it is possible to provide a toilet seat with excellent antifouling properties, so that propagation of germs etc. is reduced, but to the extent that the effect of the invention is not impaired, inorganic antibacterial agents, organic antibacterial agents, Antifungal agents can be included.
【0028】また、発明の効果を損なわない程度で、適
宜各種の添加剤を配合することができる。例えば、可塑
剤、内部離型剤、加水分解防止剤、酸化防止剤、紫外線
吸収剤、帯電防止剤、難燃剤、発泡剤、無機顔料、有機
顔料等があげられる。Further, various additives can be appropriately blended to such an extent that the effects of the invention are not impaired. Examples include plasticizers, internal mold release agents, hydrolysis inhibitors, antioxidants, ultraviolet absorbers, antistatic agents, flame retardants, foaming agents, inorganic pigments, organic pigments, and the like.
【0029】[0029]
【発明の効果】以上説明したように本発明の請求項1、
2の便座または局部洗浄便座によれば次の効果が得られ
る。便座シート、便蓋、本体ケース等の構成材料の少な
くとも一部材が、樹脂の中に滑剤が混入されている樹脂
成形体で構成することによって、樹脂成形体表面のすべ
りを良くし、便座の汚れの大部分である、便、尿などの
水に分散あるいは溶解した汚れが付着しても、容易に除
去でき掃除が簡単にできるため、汚れが栄養源となる雑
菌の増殖を減少させ、かつ、清掃時の拭き取りによる樹
脂成形体表面への傷付きを防止するという防汚性、傷付
き性に優れた便座を提供することが出来る。As described above, according to the first aspect of the present invention,
According to the second toilet seat or the local flush toilet seat, the following effects can be obtained. At least one member of the constituent materials such as the toilet seat sheet, the toilet lid, and the main body case is made of a resin molded body in which a lubricant is mixed in the resin, thereby improving the slip on the surface of the resin molded body and contaminating the toilet seat. Even if dirt dispersed or dissolved in water, such as stool or urine, which is the majority of the dirt, it can be easily removed and cleaned easily, so that the dirt reduces the growth of germs as a nutrient source, and It is possible to provide a toilet seat that is excellent in antifouling property and scratching property by preventing the surface of the resin molded article from being scratched by wiping during cleaning.
【0030】さらに本発明の請求項3によれば樹脂の硬
度等の物理的特性を損なうことなく優れた防汚性、傷付
き性を確保、継続することができる。Further, according to the third aspect of the present invention, excellent antifouling property and scratch resistance can be secured and continued without impairing physical properties such as hardness of the resin.
【図1】図1は本発明の実施形態の一例を示す局部洗浄
便座の外観図((a);便座を上から見た図、(b);便座を横
から見た図) )である。FIG. 1 is an external view ((a); a view of a toilet seat from above; (b); a view of a toilet seat from the side) showing an example of an embodiment of the present invention; .
【図2】図2は本発明の実施例1〜3、比較例1〜3の
対比表(組成、防汚性、硬度、傷付き性)である。FIG. 2 is a comparison table (composition, antifouling property, hardness, and scratch resistance) of Examples 1 to 3 and Comparative Examples 1 to 3 of the present invention.
1… 便座シート、2…便蓋、3…本体ケース、4…洗
浄ノズル、5…操作部DESCRIPTION OF SYMBOLS 1 ... Toilet seat sheet, 2 ... Toilet lid, 3 ... Body case, 4 ... Cleaning nozzle, 5 ... Operation part
───────────────────────────────────────────────────── フロントページの続き (72)発明者 藤村 弘樹 福岡県北九州市小倉北区中島2丁目1番1 号 東陶機器株式会社内 Fターム(参考) 2D037 AA13 AE17 ────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Hiroki Fujimura 2-1-1 Nakajima, Kokurakita-ku, Kitakyushu-shi, Fukuoka F-term (reference) 2D037 AA13 AE17
Claims (3)
露出構成部品の構成材料の少なくとも一部材が、母材樹
脂の中に滑剤を混入した樹脂成形体で構成された防汚性
に優れた便座。1. An antifouling property in which at least one member of a constituent material of an exposed component of a toilet seat such as a toilet seat sheet, a toilet lid, and a main body case is formed of a resin molded body in which a lubricant is mixed in a base resin. Excellent toilet seat.
ル等の便座の露出構成部品の構成材料の少なくとも一部
材が、母材樹脂の中に滑剤を混入した樹脂成形体で構成
された局部洗浄用の防汚性に優れた便座。2. A local part in which at least one member of a constituent material of an exposed component of a toilet seat such as a toilet seat sheet, a toilet lid, a main body case, and a washing nozzle is formed of a resin molded body in which a lubricant is mixed into a base resin. Toilet seat with excellent antifouling properties for cleaning.
て0.03〜5重量部ともに混入されていることを特徴
とする請求項1又は2記載の防汚性に優れた便座。3. The toilet seat with excellent antifouling properties according to claim 1, wherein 0.03 to 5 parts by weight of a lubricant is mixed with 100 parts by weight of the original base resin. .