JP2000063719A - Ink composition for ink jet recording and recording - Google Patents

Ink composition for ink jet recording and recording

Info

Publication number
JP2000063719A
JP2000063719A JP22844098A JP22844098A JP2000063719A JP 2000063719 A JP2000063719 A JP 2000063719A JP 22844098 A JP22844098 A JP 22844098A JP 22844098 A JP22844098 A JP 22844098A JP 2000063719 A JP2000063719 A JP 2000063719A
Authority
JP
Japan
Prior art keywords
ink composition
polymer particles
polyvalent metal
metal salt
wt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
JP22844098A
Other languages
Japanese (ja)
Inventor
Kazuhide Kubota
Toshiyuki Miyabayashi
利行 宮林
和英 窪田
Original Assignee
Seiko Epson Corp
セイコーエプソン株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Seiko Epson Corp, セイコーエプソン株式会社 filed Critical Seiko Epson Corp
Priority to JP22844098A priority Critical patent/JP2000063719A/en
Publication of JP2000063719A publication Critical patent/JP2000063719A/en
Application status is Withdrawn legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide an ink composition for ink jet recording, capable of realizing brilliant printing even on plain paper and capable of ensuring quick dryability, in an ink jet recording method for printing a recording medium with a reactive solution and the ink composition, and to provide a method for recording. SOLUTION: An ink composition for ink jet recording comprises at least a pigment, polymer particles, an aqueous organic solvent, and water, and adopts a polyvalent metal salt as a reactant of a reaction solution. Therein, when the 0.1 wt.% aqueous dispersion of the polymer particles is mixed with an aqueous solution containing the polyvalent metal salt, aggregates comprising the added polyvalent metal salt and the polymer particles in a (polyvalent metal salt/polymer particle) weight ratio of <=50 are formed.

Description

【発明の詳細な説明】 【0001】 【発明の背景】本発明は、インクジェット記録用インク組成物および記録方法に関し、詳しくは少なくとも顔料、ポリマー微粒子、水溶性有機溶媒、水を含有するインク組成物および反応液と上記インク組成物とを付着させて印字を行うインクジェット記録方法に関する。 BACKGROUND OF THE INVENTION [0001] BACKGROUND OF THE INVENTION The present invention is an inkjet recording ink composition and a recording method, and more particularly at least a pigment, polymer particles, the ink composition containing a water-soluble organic solvent, water and an ink jet recording method for printing by reaction liquid and deposited and the ink composition. 【0002】<背景技術>インクジェット記録方法は、 [0002] <BACKGROUND> ink-jet recording method,
インク組成物の小滴を飛翔させ、紙等の記録媒体に付着させて印刷を行う印刷方法である。 By ejecting droplets of an ink composition is a printing method for printing by adhering to a recording medium such as paper. この方法は、比較的安価な装置で高解像度、高品位な画像を、高速で印刷可能であるという特徴を有する。 This method is characterized in that high resolution in a relatively inexpensive apparatus, a high-quality image can be printed at high speed. 通常インクジェット記録に使用されるインク組成物は、水を主成分とし、これに着色成分および目詰まり防止等の目的でグリセリン等の湿潤剤を含有したものが一般的である。 The ink composition used in the normal ink jet recording comprises water as a main, is generally one containing a wetting agent such as glycerin for the this coloring component and prevention of clogging and other purposes. 【0003】一方、インクジェット記録方法として、最近新たに、多価金属塩溶液を記録媒体に適用した後、少なくとも一つのカルボキシル基を有する染料を含むインク組成物を適用する方法が提案されている(例えば、特開平5−202328号公報)。 On the other hand, as an inkjet recording method, a new recently after applying a polyvalent metal salt solution onto a recording medium, a method of applying an ink composition containing a dye having at least one carboxyl group has been proposed ( For example, Japanese Unexamined Patent Publication No. 5-202328). この方法においては、 In this method,
多価金属イオンと染料から不溶性複合体が形成され、この複合体の存在により、耐水性がありかつカラーブリードがない高品位の画像を得ることができるとされている。 Insoluble complex is formed from a polyvalent metal ion and the dye, this due to the presence of the complex, there is a water resistant and it is possible to obtain an image of high quality free from color bleeding. 【0004】また、少なくとも浸透性を付与する界面活性剤または浸透性溶剤および塩を含有するカラーインクと、この塩との作用により増粘または凝集するブラックインクとを組合せて使用することにより、画像濃度が高くかつカラーブリードがない高品位のカラー画像が得られるという提案もなされている(特開平6−10673 Further, a color ink containing a surfactant or penetrable solvent and a salt for imparting at least permeability, by using a combination of a black ink to thicken or aggregate by the action of this salt, image concentration and has been made suggestion color image high quality free from color bleeding can be obtained high (JP-a-6-10673
5号公報)。 5 JP). すなわち塩を含んだ第一の液と、インク組成物との二液を印字することで、良好な画像が得られるとするインクジェット記録方法が提案されている。 Namely a first liquid containing a salt, by printing two liquids of the ink composition, inkjet recording method provide a good image has been proposed. 【0005】また、その他にも二液を印字するインクジェット記録方法が提案されている(例えば、特開平3− [0005] The ink jet recording method for printing Besides two liquids have been proposed (e.g., JP-3-
240557号公報、特開平3−240558号公報)。 240557 and JP-Hei 3-240558). 【0006】また、特開平3−157464では顔料、 [0006] In addition, the pigment in JP-A-3-157464,
ポリマー分散剤、水性媒体およびアセチレングリコール系浸透剤からなり、水性媒体が不揮発性有機溶剤と低級アルコールからなりインク中の添加量が0.5重量%〜 Polymeric dispersing agents, made from an aqueous medium and acetylene glycol penetrating agent, the aqueous medium is 0.5% by weight loading in the ink a non-volatile organic solvent and a lower alcohol ~
1重量%の範囲であるインク組成物が提案されている。 1 ink composition is in the range of weight percent have been proposed.
しかし、このインク組成物は速乾性には優れるものの、 However, although the ink composition excellent in quick-drying,
普通紙に対する印字ではにじみが発生してしまう。 Bleeding in the printing on plain paper occurs. 【0007】本発明では、ニ液を用いるインクジェット記録方法において、普通紙においても印字にじみのないシャープな印字が実現できかつ速乾性にも優れたインクジェット記録用インク組成物および記録方法の提供を目的とする。 [0007] In the present invention, objects in an ink jet recording method using the two-component, to provide an ordinary inkjet recording ink composition the printing bleeding without sharp printing has excellent and quick drying can be achieved even in the paper and recording method to. 【0008】 【発明の概要】本発明者等は、多価金属塩を含有する第一液と少なくとも顔料、ポリマー微粒子、水溶性有機溶媒、水を含有するインク組成物を適応する記録方法において、多価金属塩とポリマー微粒子との凝集反応性が高い場合には普通紙上で高印字品質と印字速乾性を両立できるという知見を得た。 [0008] The present inventors have SUMMARY OF THE INVENTION least a pigment and a first liquid containing a polyvalent metal salt, polymer particles, water-soluble organic solvent, in the recording method for adapting an ink composition containing water, was obtained a finding that in the case of high aggregation reactivity with a polyvalent metal salt and the polymer particles compatible printing fast drying and high print quality on plain paper. 本発明はかかる知見に基づくものである。 The present invention is based on this finding. 【0009】多価金属塩を含んでなる反応液と着色剤、 [0009] comprising a polyvalent metal salt reaction solution and a coloring agent,
ポリマー微粒子、水溶性有機溶媒、水を少なくとも含有するインク組成物とを記録媒体に付着させて画像を形成するインクジェット記録方法においては、着色剤が顔料である場合、前記の反応液とインク組成物とが上質紙のみならず、あらゆる普通紙ならびに再生紙等の記録媒体表面で接触すると、前記インク組成物中のポリマー微粒子と顔料が反応液中の多価金属イオンと接触し、インク組成物中の分散状態が破壊され、顔料および前記ポリマー微粒子が急速に凝集するため、顔料は紙等の記録媒体への浸透を抑制され、記録媒体の表面近傍に残る。 In the inkjet recording method in which the polymer particles, a water-soluble organic solvent, by adhering an ink composition containing at least water to the recording medium to form an image, if the colorant is a pigment, the reaction liquid and the ink composition of the DOO not only high-quality paper, any plain paper and in contact with the recording medium surface of the recycled paper or the like, the polymer particles and the pigment in the ink composition is in contact with the polyvalent metal ion in the reaction liquid, the ink composition the state of dispersion destruction, since the pigment and the polymer particles rapidly agglomerate, the pigment is suppressed penetration into a recording medium such as paper, remains near the surface of the recording medium. この際、反応液中およびインク組成物中の水および水溶性有機溶媒は紙等の記録媒体内部へ浸透し、減少した後、室温においてポリマー微粒子同士が合一し融着して顔料を包含し皮膜を形成すると考えられる。 At this time, water and a water-soluble organic solvent in the reaction solution and the ink composition permeates into the internal recording medium such as paper, after reduction, include pigment fused coalesced polymer fine particles at room temperature It is believed to form a film. 【0010】この際に、ポリマー微粒子の多価金属イオンによる凝集反応の反応速度が速いほど、反応液およびインク組成物中の水および水性有機溶媒と顔料およびポリマー微粒子との分離が促進され速乾性が向上すると考えられる。 [0010] At this time, the faster the reaction rate of the agglutination reaction with polyvalent metal ions of the polymer particles, the reaction solution and water and aqueous organic solvents and pigments and the separated promote the polymer microparticles Quick-drying ink composition There is considered to be improved. 【0011】したがって、上記、反応液およびインク組成物を用いて得られる画像はにじみのない、色濃度が高く、印刷ムラの少ない高品位画像であって、かつ、速乾性、耐擦性、耐水性に優れ、紙等の記録媒体との定着性に優れたものとなる。 Accordingly, the image obtained by using the reaction liquid and the ink composition is no bleeding, high color density, a small high-quality image with uneven printing, and quick-drying, abrasion resistance, water excellent sex, and excellent fixability to a recording medium such as paper. また、カラー画像においては、異なる色の境界領域での不均一な色混じり、すなわちカラーブリードを有効に防止できる利点も有する。 Further, in a color image, uneven color mixing in different colors in the boundary region, i.e., an advantage that can be effectively prevented color bleeding has. 【0012】ただし、この機構の説明は、前記ポリマー微粒子を用いた場合の効果を説明するために述べたものであって、本発明はこの機構に限定して解釈されるものではない。 [0012] However, the description of this mechanism, there is set forth to illustrate the effect of using the polymer fine particles, the present invention is not to be construed as being limited to this mechanism. 【0013】 【発明の具体的説明】<インク組成物>本発明のインク組成物は少なくとも顔料、ポリマー微粒子、水性有機溶媒、水を含有し、インク中に分散して存在する該ポリマー微粒子が多価金属塩に対して高い凝集性を有するものである。 [0013] DETAILED DESCRIPTION OF THE INVENTION <Ink composition> The ink composition of the present invention is at least a pigment, polymer particles, aqueous organic solvents, contain water, the polymer particles multi present dispersed in the ink and it has a high cohesion with respect to the valence metal salt. すなわち、本発明のインク組成物に含有できるポリマー微粒子は、該ポリマー微粒子の0.1重量%水性分散液と多価金属塩水溶液とを混合した際に、添加した多価金属塩とポリマー微粒子の重量比(多価金属塩/ That is, the polymer particles can be contained in the ink composition of the present invention, when mixed with a 0.1 wt% aqueous dispersion and the polyvalent metal salt aqueous solution of the polymer particles, the polyvalent metal salt and the polymer particles The weight ratio (polyvalent metal salt /
ポリマー微粒子)が50以下で凝集物を形成可能であるという特徴を有する。 It has a characteristic that the polymer particles) is capable of forming aggregates at 50 or less. また本発明に用いる事のできるポリマー微粒子は該ポリマー微粒子の0.1重量%水性分散液と多価金属塩含有透明水溶液とを重量比で多価金属塩/ポリマー微粒子=50で混合した混合溶液の700 Mixed solution The polymer particles which can be used in the present invention is mixed with a multivalent metal salt / polymer particles = 50 and 0.1 wt% aqueous dispersion and the polyvalent metal salt-containing transparent aqueous solution of the polymer particles in a weight ratio of of 700
nmでの吸光度が同波長でのポリマー微粒子0.1重量%水性分散液の吸光度の1/2となるまでの時間が60 Time absorbance at nm is until the half of the absorbance of the polymer fine particles 0.1% by weight aqueous dispersion of the same wavelength 60
秒以下であるという特徴を有する事もできる。 Seconds can also have a feature that is less than or equal to. 上記のポリマー微粒子の特性については以下の試験方法において判定可能である。 The characteristics of the polymer particles can be determined in the following test methods. 【0014】多価金属イオンに対するポリマー微粒子の凝集性は、ポリマー微粒子の0.1重量%水性分散液とあらかじめ一定濃度に調製された多価金属含有水溶液を混合し、混合液中の多価金属塩/ポリマー微粒子の重量比50以下の条件で凝集物が生成するか否かで判定可能である。 [0014] aggregation of the polymer particles to the polyvalent metal ion, by mixing a polyvalent metal-containing aqueous solution which is prepared in advance a constant concentration of 0.1% by weight aqueous dispersion of polymer particles, the polyvalent metal in the mixture in a weight ratio of 50 under the following conditions salt / polymer particle can be determined by whether aggregates are produced. 【0015】凝集反応の反応速度については、ポリマー微粒子の0.1重量%水性分散液の吸光度の経時変化によって判定可能である。 [0015] For kinetics of agglutination it can be determined by time course of absorbance of 0.1% by weight aqueous dispersion of polymer particles. すなわち、ポリマー微粒子と多価金属含有水溶液とを混合した場合、多価金属イオンとポリマー微粒子との凝集反応が速いほど吸光度の変化も速くなる。 That is, when mixing the polymer particles and polyvalent metal-containing aqueous solution, even faster change in agglutination faster the absorbance with a polyvalent metal ion and the polymer particles. ポリマー微粒子の吸光度変化は低波長領域では明確に現れないため、高波長領域でのポリマー微粒子の吸光度の経時変化を調べることにより多価金属イオンとポリマー微粒子の凝集反応速度をがわかり、ポリマー微粒子の特徴を明確にできる。 Since the change in absorbance of the polymer particles do not appear clearly in the low wavelength region, understanding of the aggregation reaction rate of polyvalent metal ions and the polymer particles by examining the time course of absorbance of the polymer particles in the high wavelength region, of the polymer particles the feature can be clarified. 【0016】本発明の好ましい態様によればインク組成物に含有されるポリマー微粒子は0.1〜40重量%の範囲で含有される事が好ましく、1〜25重量%で含有されることがより好ましい。 Preferred polymer particles contained in the ink composition according to the aspect of the present invention is preferably not contained in the range of 0.1 to 40 wt%, more it is contained in 1 to 25 wt% preferable. 【0017】本発明に用いられるインク組成物に含まれるポリマー微粒子は下記に示すモノマーを単独もしくはニ種類以上のモノマーとを重合触媒と乳化剤の存在下で乳化重合することによって得ることができる。 The polymer particles contained in the ink composition used in the present invention can be obtained by emulsion polymerization in the presence of a polymerization catalyst and an emulsifier and a singly or two or more monomers monomers shown below. ポリマー微粒子を構成するモノマー成分としては、一般的に乳化重合で使用されるアクリル酸エステル類、メタクリル酸エステル類、芳香族ビニル単量体、ビニルエステル類、 As the monomer component constituting the polymer fine particles, acrylic acid esters that are commonly used in emulsion polymerization, methacrylic acid esters, aromatic vinyl monomers, vinyl esters,
ビニルシアン化合物類、ハロゲン化類、オレフィン類、 Vinyl cyanide compounds, halogenated ethers, olefins,
ジエン類、重合可能な二重結合を二つ以上有する架橋性単量体類、さらには安定性付与などを目的としたアクリルアミド類、水酸基含有化合物等を例示することができ、通常はこれらを単独あるいはニ種以上混合して使用する。 Dienes, crosslinking monomers having polymerizable double bond of two or more, more acrylamides for the purpose of such stability imparted can be exemplified a hydroxyl group-containing compounds such as, typically alone these or used in admixture two kinds or more. 【0018】また、特に、本発明に用いるポリマー微粒子は皮膜形成能を有することが望ましく、かかるポリマー微粒子を分散粒子とする樹脂エマルジョンは造膜性を有することが好ましい。 [0018] In particular, the polymer fine particles used in the present invention preferably have a film-forming ability, a resin emulsion such polymer fine particles dispersed particles preferably have a film-forming properties. 本発明のインク組成物に使用できるポリマー微粒子は、30℃以下の最低成膜温度を有するものであることが好ましい。 Polymer particles which can be used in the ink composition of the present invention is preferably one having a minimum film-forming temperature of 30 ° C. or less. 該微粒子のポリマー組成については、特に限定されないが、得られるポリマー微粒子は上記の点に留意して不飽和ビニル単量体を選択する必要がある。 The polymer composition of the fine particles is not particularly limited, the resulting polymer particles, it is necessary to select the note to unsaturated vinyl monomer of the above points. なお、上述の乳化重合の際に使用される開始剤、界面活性剤、分子量調整剤、さらには中和剤も特に限定されず常法に準じて使用される。 Incidentally, the initiator used in the emulsion polymerization described above, surfactants, molecular weight modifier, further may be used in accordance with conventional methods is not particularly limited neutralizing agent. 【0019】本発明に用いる顔料は、特別な制限なしに無機顔料、有機顔料を使用する事ができる。 Pigment used in [0019] The present invention can be used inorganic pigments, organic pigments without particular limitation. 無機顔料としては、酸化チタンおよび酸化鉄に加え、コンタクト法、ファーネス法、サーマル法などの公知の方法によって製造されたカーボンブラックを使用する事ができる。 As the inorganic pigments, in addition to titanium oxide and iron oxide, a contact method, a furnace method, it is possible to use carbon black produced by a known method such as a thermal method.
また有機顔料としては、アゾ染料(アゾレーキ、不溶性アゾ顔料、縮合アゾ顔料、キレートアゾ顔料などを含む)、多環式顔料(例えばフタロシアニン顔料、ペリレン顔料、ペリノン顔料、アントラキノン顔料、キナクリドン顔料、ジオキサジン顔料、チオインジゴ顔料、イソインドリノン顔料、キノフラロン顔料など)、染料キレート(例えば、塩基性染料型キレート、酸性染料型キレートなど)、ニトロ顔料、ニトロソ顔料、アニリンブラックなどを使用できる。 As also organic pigments (including azo lake, insoluble azo pigments, condensed azo pigments, and chelate azo pigments) azo dyes, polycyclic pigments (e.g. phthalocyanine pigments, perylene pigments, perinone pigments, anthraquinone pigments, quinacridone pigments, dioxazine pigments, thioindigo pigments, isoindolinone pigments, quinophthalone pigments), dye chelates (e.g., basic dye chelates and acid dye chelates), nitro pigments, nitroso pigments, and aniline black. 【0020】本発明の好ましい態様によれば、これらの顔料は、分散剤で水性媒体中に分散させて得られた顔料分散液としてインクに添加されるのが好ましい。 According to a preferred embodiment of the present invention, these pigments are preferably added to the ink as pigment dispersion liquid obtained by dispersing in an aqueous medium with a dispersant. 好ましい分散剤としては、顔料分散液を調製するのに慣用されている分散剤、例えば高分子分散剤、界面活性剤を使用する事ができる。 Preferred dispersants include dispersants which have been commonly used in the preparation of pigment dispersions, for example, polymeric dispersants may be used a surfactant. なお、この顔料分散液に含まれる分散剤および界面活性剤が後記するインク組成物の界面活性剤としても機能するであろうことは当業者に明らかであろう。 Incidentally, it would dispersant and the surfactant contained in the pigment dispersion function also as a surfactant described later to the ink composition will be apparent to those skilled in the art. 【0021】インクへの顔料の添加量は、0.5〜25 [0021] The amount of the pigment added to the ink is 0.5 to 25
重量%程度が好ましく、より好ましくは2〜15重量% Is preferably about wt%, more preferably 2 to 15 wt%
程度である。 It is the degree. 【0022】本発明の好ましい態様によれば、インク組成物は糖を含有してなるのが好ましい。 According to a preferred embodiment of the invention, the ink composition preferably contains a sugar. 糖類の例としては、単糖類、ニ糖類、オリゴ糖(三糖類および四糖類を含む)および多糖類があげられ、好ましくはグルコース、マンノース、フルクトース、リボース、キシロース、アラビノール、ガラクトース、アルドン酸、グルシシール、マルトース、セロビオース、ラクトース、スクロース、トレハロース、マルトトリオースなどがあげられる。 Examples of saccharides include monosaccharides, disaccharides, (including trisaccharides and tetrasaccharides) oligosaccharides and polysaccharides, preferably glucose, mannose, fructose, ribose, xylose, Arabinoru, galactose, aldonic acid, Gurushishiru , maltose, cellobiose, lactose, sucrose, trehalose, and maltotriose. ここで、多糖類とは広義の糖を意味し、アルギン酸、α−シクロデキストリン、セルロースなど自然界に広く存在する物質を含む意味に用いることとする。 Here, polysaccharides means sugars in a broad, alginic acid, alpha-cyclodextrin, and used in the meaning as including substances which exist widely in nature, such as cellulose. 【0023】また、これらの糖類の誘導体としては、前記した糖類の還元糖(例えば、糖アルコール(一般式HO Further, derivatives of these saccharides include reducing sugars (for example, sugar alcohols (general formula HO
CH 2 (CHOH) n CH 2 OH(ここで、n=2〜5の整数で表す) CH 2 (CHOH) n CH 2 OH ( wherein, expressed in n = 2 to 5 integer)
で表わされる)、酸化糖(例えば、アルドン酸、ウロン酸など)、アミノ酸、チオ糖などがあげられる。 In represented), oxidized sugars (for example, aldonic acid and uronic acid), amino acids, and thiosugars and the like. 特に糖アルコールが好ましく、具体例としてはマルチトール、 Sugar alcohols are particularly preferred, maltitol specific examples,
ソルビットなどがあげられる。 Such as sorbitol, and the like. 【0024】これらの糖類の含有量はインクの0.1〜 The content of these saccharides is 0.1 inks
40重量%、好ましくは0.5〜30重量%の範囲が適当である。 40 wt%, and preferably from 0.5 to 30 wt%. 【0025】また、本発明の好ましい態様によれば、本発明に使用するインク組成物は低沸点有機溶剤を含んでなることが好ましい。 Further, according to a preferred embodiment of the present invention, the ink composition used in the present invention preferably contains a low-boiling organic solvent. 低沸点有機溶剤の例としては、メタノール、エタノール、n−プロピルアルコール、is Examples of low boiling organic solvents include methanol, ethanol, n- propyl alcohol, IS
o−プロピルアルコール、n−ブタノール、sec−ブタノール、ter−ブタノール、iso−ブタノール、 o- propyl alcohol, n- butanol, sec- butanol, ter-butanol, iso- butanol,
n−ペンタノールなどがあげられる。 Such as n- pentanol and the like. 特に一価アルコールが好ましい。 In particular, the monovalent alcohol is preferred. 【0026】本発明の好ましい態様によれば、本発明に使用するインクはさらに高沸点有機溶剤を含んでなることが好ましい。 According to a preferred embodiment of the present invention, the ink used in the present invention preferably further comprises a high-boiling organic solvent. 【0027】高沸点有機溶剤の好ましい例としては、エチレングリコール、ポリエチレングリコール、グリセリン、ポリプロピレングリコール、プロピレングリコール、ブチレングリコール、1,2,6−ヘキサントリオール、チオグリコール、ヘキシレングリコール、トリエチレングリコール、トリメチロールエタン、トリメチロールプロパンなどの多価アルコール類、エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノメチルエーテル、 [0027] Preferred examples of high-boiling organic solvents are ethylene glycol, polyethylene glycol, glycerin, polypropylene glycol, propylene glycol, butylene glycol, 1,2,6-hexanetriol, thioglycol, hexylene glycol, triethylene glycol, trimethylol ethane, polyhydric alcohols such as trimethylol propane, ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether,
ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、トリエチレングリコールモノエチルエーテル、トリエチレングリコールモノエチルエーテル、トリエチレングリコールモノメチルエーテル、トリエチレングリコールモノブチルエーテルなどの多価アルコールのアルキルエーテル類、尿素、2−ピロリドン、N−メチル−2−ピロリドン、1,3−ジメチル−2−イミダゾリジノン、トリエタノールアミンなどがあげられる。 Diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, triethylene glycol monoethyl ether, triethylene glycol monoethyl ether, triethylene glycol monomethyl ether, alkyl ethers of polyhydric alcohols such as triethylene glycol monobutyl ether, urea, 2-pyrrolidone, N- methyl-2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone, triethanolamine and the like. 【0028】これら高沸点有機溶媒の添加量は、インクの0.5〜40重量%が好ましく、より好ましくは2〜 The addition amount of these high-boiling organic solvent is preferably from 0.5 to 40% by weight of the ink, more preferably 2 to
20重量%の範囲である。 In the range of 20 wt%. また低沸点有機溶剤の添加量はインクの0.5〜10重量%が好ましく、より好ましくは1.5〜6重量%の範囲である。 The amount of low-boiling organic solvent is preferably 0.5 to 10% by weight of the ink, more preferably from 1.5 to 6 wt%. 【0029】その他、必要に応じて、pH調整剤、防腐剤、防カビ剤等を添加してもよい。 [0029] If necessary, pH adjusting agents, preservatives, may be added to the antifungal agent. 【0030】<インクジェット記録方法>本発明によるインクジェット記録方法は基本的に、記録媒体に反応液をインク組成物が付着される場所にのみ選択的に付着させた直後に、インク組成物を印字する工程を含んでなるものであるが、インク組成物をまず付着させ、直後にインク組成物が付着した場所にのみ選択的に反応液を印字する工程を含むことができる。 [0030] <Inkjet Recording Method> The inkjet recording method according to the invention is essentially a reaction mixture immediately after only selectively adhere to the location where the ink composition is deposited onto a recording medium, printing the ink composition although those comprising the step, firstly depositing the ink composition can include the step of printing only selectively reaction solution where the ink composition is deposited immediately. 【0031】そして、本発明にあっては、反応液の反応剤が多価金属塩でありかつインク組成物が前述したインク組成物であるインクジェット記録方法である。 [0031] Then, in the present invention, the reactant is a polyvalent metal salt and the ink composition of the reaction liquid is an inkjet recording method is an ink composition described above. 本発明によるインクジェット記録方法により、色濃度の高い、 The ink jet recording method according to the present invention, a high color density,
にじみ、ムラの少ない印字を実現し、さらに、カラー画像においては、異なる色の境界領域での不均一な色混じり、すなわちカラーブリードを有効に防止できるとの利点も有するとともに普通紙上での速乾性も確保できる。 Bleeding, to help minimize printing unevenness further, in a color image, quick-drying on plain paper which has the advantage of different colors uneven color mixing in boundaries, i.e. can be effectively prevented, color bleeding It can be ensured. 【0032】<反応液>本発明において用いられる反応液は、インク組成物と接触して凝集物を生成する反応剤を含んでなる。 The reaction solution used in the <Reaction Solution> The present invention comprises a reactant that produces an aggregate when contacting with the ink composition. 凝集物は反応剤とインク組成物中の顔料ならびにポリマー微粒子とが接触することによって形成されるものと考えれる。 Aggregates is believed that the pigment and polymer particles of the reactive agent and the ink composition is formed by contact. 本発明においてはこの様な反応剤として多価金属塩を使用することが最も好ましい。 It is most preferred to use a polyvalent metal salt such reactants in the present invention. 反応剤としての多価金属塩とは、二価以上の多価金属イオンとこれら多価金属イオンに結合する陰イオンとから構成され、水に可溶な塩が挙げられる。 The polyvalent metal salt as a reactant, is composed of an anion which binds to the divalent or higher polyvalent metal ion and the polyvalent metal ions, soluble salts in the water. 多価金属イオンの具体例としては、Ca 2+ 、Cu 2+ 、Ni 2+ 、Mg 2+ 、Zn 2+ 、Ba 2+ Specific examples of polyvalent metal ions, Ca 2+, Cu 2+, Ni 2+, Mg 2+, Zn 2+, Ba 2+
などの二価金属イオンAl 3+ 、Fe 3+ 、Cr 3+などの三価金属イオンがあげられる。 Divalent metal ion Al 3+, such as, Fe 3+, trivalent metal ions such as Cr 3+ and the like. 陰イオンとしては、Cl 、N The anion, Cl -, N
O 3 、I 、Br 、ClO 3 およびCH 3 COO などがあげられる。 O 3 -, I -, Br -, ClO 3 - and CH 3 COO - and the like, such as. 【0033】とりわけ、 Ca 2+またはMg 2+より構成される金属塩は、反応液のpH、得られる印刷物の品質という二つの観点から、好適な結果を与える。 [0033] Especially, a metal salt constituted by Ca 2+ or Mg 2+ is, pH of the reaction solution, from two viewpoints of the quality of prints give favorable results. 【0034】これら多価金属塩のインク組成物中における濃度は印字品質、目詰まり防止の効果が得られる範囲で適宜決定されてよいが、好ましくは0.1〜40重量%程度であり、より好ましくは5〜25重量%程度である。 [0034] These polyhydric concentrations print quality in the ink composition of the metal salt, may be suitably determined within a range in which the effect of preventing clogging is obtained, and preferably about 0.1 to 40 wt%, more preferably about 5 to 25 wt%. 【0035】本発明の好ましい態様においては、多価金属塩は、二価以上の多価金属イオンと、これら多価金属イオンに結合する硝酸イオンまたはカルボン酸イオンとから構成され、水に可溶なものであるのが好ましい。 In a preferred embodiment of the present invention, the polyvalent metal salt is composed of a divalent or higher polyvalent metal ions, and nitrate ions or carboxylate ions bonded to the polyvalent metallic ions, soluble in water preferably one such. 【0036】ここで、カルボン酸イオンは、好ましくは炭素数1〜6の飽和脂肪酸モノカルボン酸または炭素数7〜11の炭素環式モノカルボン酸から誘導されるものである。 [0036] Here, carboxylate ions are preferably those derived from carbocyclic monocarboxylic acid saturated fatty monocarboxylic or 7 to 11 carbon atoms having 1 to 6 carbon atoms. 炭素数1〜6の飽和脂肪族モノカルボン酸の好ましい例としては、蟻酸、酢酸、プロピオン酸、酪酸、 Preferred examples of saturated aliphatic monocarboxylic acids having 1 to 6 carbon atoms, formic acid, acetic acid, propionic acid, butyric acid,
イソ酪酸、吉草酸、イソ吉草酸、ピバル酸、ヘキサン酸などが挙げられる。 Isobutyric acid, valeric acid, isovaleric acid, pivalic acid, and hexanoic acid. 特に蟻酸、酢酸が好ましい。 In particular, formic acid and acetic acid are preferred. 【0037】このモノカルボン酸の飽和脂肪族炭化水素基上の水素原子は水酸基で置換されていてもよく、そのようなカルボン酸の好ましい例としては、乳酸が挙げられる。 The hydrogen atoms on the saturated aliphatic hydrocarbon residue in the monocarboxylic acid may be substituted by a hydroxyl group, Preferred examples of such carboxylic acids include lactic acid. 【0038】さらに、炭素数6〜10の炭素環式モノカルボン酸の好ましい例としては、安息香酸、ナフト酸等が挙げられ、より好ましくは安息香酸である。 [0038] Further, preferred examples of the carbocyclic monocarboxylic acid having 6 to 10 carbon atoms, benzoic acid, etc. naphtho acid., And more preferably it is benzoic acid. 【0039】本発明の好ましい態様によれば、反応液は、多価金属塩に加えて、ポリオールを含んでなる。 According to a preferred embodiment of the [0039] present invention, the reaction liquid, in addition to the polyvalent metal salt, comprising a polyol. ポリオールの好ましい具体例としては、多価アルコール、 Specific examples of preferred polyols are polyhydric alcohols,
例えば、グリセリン、ジエチレングリコール、トリエチレングリコール、ポリエチレングリコール、ポリプロピレングリコール、プロピレングリコール、ブチレングリコール、1、2、6−ヘキサントリオール、チオグリコール、ヘキシレングリコール、トリメチロールエタン、 For example, glycerin, diethylene glycol, triethylene glycol, polyethylene glycol, polypropylene glycol, propylene glycol, butylene glycol, 1,2,6-hexanetriol, thioglycol, hexylene glycol, trimethylol ethane,
トリメチロールプロパン1,5−ペンタンジオール、1,4 Trimethylolpropane 1,5, 1,4
―ブタンジオールなどが挙げられる。 - such as butane diol, and the like. 本発明の好ましい態様によれば、このポリオールの反応液に対する添加量は10重量%以上であるのが好ましく、より好ましくは10〜30重量%程度である。 According to a preferred embodiment of the present invention, the addition amount relative to the reaction mixture of the polyol that is 10 wt% or more by weight, more preferably about 10 to 30 wt%. 【0040】本発明の好ましい態様によれば、本発明に使用する反応液は糖を含有してなるのが好ましい。 According to a preferred embodiment of the [0040] present invention, the reaction liquid used in the present invention is preferably comprising a sugar. 糖の具体例としては、例えば単糖類、二糖類、オリゴ糖類(三糖類および四糖類を含む)および多糖類があげられ、好ましくはグルコース、マンノース、フルクトース、リボース、キシロース、アラビノース、ガラクトース、アルドン酸、グルシシール、ソルビット、マルトース、セロビオース、ラクトース、スクロース、トレハロース、マルトトリオース、などがあげられる。 Specific examples of sugars, for example monosaccharides, disaccharides, oligosaccharides (including trisaccharides and tetrasaccharides) and other polysaccharides, preferably glucose, mannose, fructose, ribose, xylose, arabinose, galactose, aldonic acid , Gurushishiru, sorbitol, maltose, cellobiose, lactose, sucrose, trehalose, maltotriose, and the like. 【0041】これらポリオールならびに糖は単独で添加されても、二以上の混合物として添加されてもよい。 [0041] be added these polyols and sugars alone, it may be added as a mixture of two or more. 【0042】本発明の好ましい態様によれば、反応液は高沸点有機溶媒からなる湿潤剤を含んでなる。 According to a preferred embodiment of the [0042] present invention, the reaction solution comprises a wetting agent comprising a high-boiling organic solvent. 高沸点有機溶媒は、反応液の乾燥を防ぐことによりヘッドの目詰まりを防止する。 High-boiling organic solvent to prevent clogging of the head by preventing drying of the reaction solution. 【0043】高沸点有機溶媒の好ましい例としては、前記ポリオールとも一部重なるが、エチレングリコール、 [0043] Preferred examples of high-boiling organic solvent is partially overlapped with the polyol, ethylene glycol,
ジエチレングリコール、トリエチレングリコール、ポリエチレングリコール、ポリプロピレングリコール、プロピレングリコール、ブチレングリコール、1、2、6− Diethylene glycol, triethylene glycol, polyethylene glycol, polypropylene glycol, propylene glycol, butylene glycol, 1,2,6
ヘキサントリオール、チオグリコール、ヘキシレングリコール、グリセリン、トリメチロールエタン、トリメチロールプロパンなどの多価アルコール類;エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、トリエチレングリコールモノメチルエーテル、トリエチレングリコールモノエチルエーテル、トリエチレングリコールモノブチルエーテルなどの多価アルコールのアルキルエーテル類、 Hexanetriol, thioglycol, hexylene glycol, glycerin, trimethylol ethane, polyhydric alcohols such as trimethylol propane, ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, diethylene glycol monobutyl ether, triethylene glycol monomethyl ether, triethylene glycol monoethyl ether, alkyl ethers of polyhydric alcohols such as triethylene glycol monobutyl ether,
尿素、2−ピロリドン、N−メチル−2−ピロリドン、 Urea, 2-pyrrolidone, N- methyl-2-pyrrolidone,
1、3−ジメチル−2−イミダゾリジノン、トリエタノールアミンなどが挙げられる。 1,3-dimethyl-2-imidazolidinone, triethanolamine and the like. 【0044】高沸点有機溶媒の添加量は特に限定されないが、このましくは0.5〜40重量%程度であり、より好ましくは2〜20重量%程度である。 The addition amount of the high boiling organic solvent is not particularly limited, preferably about 0.5 to 40 wt%, more preferably about 2 to 20 wt%. 【0045】本発明の好ましい態様によれば、反応液はpH調整のためにトリエタノールアミンを含んでなる。 According to a preferred embodiment of the [0045] present invention, the reaction mixture comprises triethanolamine for pH adjustment.
トリエタノールアミンが添加される場合、その添加量は、0.1〜2.0重量程度が好ましい。 When triethanolamine is added, the addition amount thereof is preferably about 0.1 to 2.0 wt. 【0046】また、この反応液は、後記のインク組成物の項で記載したカラー着色剤を添加して着色され、インク組成物の機能を兼ね備えたものとされてもよい。 [0046] Further, the reaction solution is colored by adding a color colorant described in the section of below the ink composition, may be assumed that both the functions of the ink composition. 【0047】 【実施例】以下、本発明を以下の実施例によって詳細に説明するが、本発明はこれらに限定されるものではない。 [0047] EXAMPLES Hereinafter, the present invention will be described in detail by the following examples, the present invention is not limited thereto. 【0048】<樹脂エマルジョン1>撹袢機、還流冷却器、滴下装置および温度計と窒素導入管を備えた反応容器に蒸留水200ml、ドデシルベンゼンスルホン酸ナトリウム0.6gを仕込み、窒素雰囲気中で撹袢しながら70℃まで加温し、さらに過硫酸アンモニウム2gを添加する。 [0048] <Resin Emulsion 1> 撹袢 machine, a reflux condenser, 200ml of distilled water in a reaction vessel equipped with a dropping device and a thermometer and a nitrogen inlet tube was charged with sodium dodecyl benzene sulfonate 0.6 g, in a nitrogen atmosphere撹袢 while heated to 70 ° C., further adding ammonium persulfate 2g. 一方、ブチルアクリレート40g、スチレン54g、アクリルアミド5g、アクリル酸1g、t−ドデシルメルカプタン0.15gを混合溶解してこれを前記反応容器中に滴下する。 On the other hand, butyl acrylate 40 g, styrene 54 g, acrylamide 5g, added dropwise acrylic acid 1g, it was mixed and dissolved t- dodecyl mercaptan 0.15g in the reaction vessel. さらに、70℃で6時間反応させた後、常温まで冷却し、中和剤としてアンモニア水を添加してpH調整をし、10μmのフィルターで濾過して目的のポリマー微粒子が水に分散した樹脂エマルジョンを得る。 Further, after reacting for 6 hours at 70 ° C., cooled to room temperature, aqueous ammonia was added to pH adjustment as a neutralizing agent, resin emulsion was filtered through a 10μm filter is object of the polymer particles dispersed in water obtained. 【0049】得られた樹脂エマルジョンの最低成膜温度は以下の方法によって測定した。 The minimum film-forming temperature of the obtained resin emulsion was measured by the following methods. 最低成膜温度測定装置をセットし、アルミニウム製の試料板上の温度勾配が平衡に達したところで、試料の樹脂エマルジョンを薄く延ばして乾燥させた。 Set the minimum film-forming temperature measuring device, when the temperature gradient of the aluminum sample plate has reached equilibrium, and dried thinly spread the resin emulsion of the sample. 乾燥終了後に試料板上を観察すると、最低成膜温度以上の領域では透明な連続フィルムが形成されるが、最低成膜温度以下の領域では白色粉末状となる。 Observation on the sample plate after the completion of drying, which is transparent continuous film at the lowest film-forming temperature or more areas are formed, a white powder in the following areas minimum film-forming temperature. この境界の温度を最低成膜温度として測定した。 The temperature of the boundary was measured as the minimum film-forming temperature. この方法によって測定した結果、樹脂エマルジョン1は25〜30℃で成膜した。 Result of measurement by this method, resin emulsion 1 was deposited at 25 to 30 ° C.. (最低成膜温度) <樹脂エマルジョン2>撹袢機、還流冷却器、滴下装置および温度計と窒素導入管を備えた反応容器に蒸留水2 (Minimum film-forming temperature) <Resin Emulsion 2> 撹袢 machine, a reflux condenser, distilled water 2 A reaction vessel equipped with a dropping device and a thermometer and a nitrogen inlet tube
00ml、ドデシルベンゼンスルホン酸ナトリウム0. 100 ml, sodium dodecylbenzenesulfonate 0.
6gを仕込み、窒素雰囲気中で撹袢しながら70℃まで加温し、さらに過硫酸アンモニウム2gを添加する。 Were charged 6 g, it warmed to 70 ° C. while 撹袢 in a nitrogen atmosphere, further addition of ammonium persulfate 2g. 一方、ブチルアクリレート40g、スチレン50g、アクリルアミド5g、アクリル酸5g、t−ドデシルメルカプタン0.15gを混合溶解してこれを前記反応容器中に滴下する。 On the other hand, butyl acrylate 40 g, styrene 50 g, acrylamide 5g, added dropwise acrylic acid 5g, it was mixed and dissolved t- dodecyl mercaptan 0.15g in the reaction vessel. さらに、70℃で6時間反応させた後、常温まで冷却し、中和剤としてアンモニア水を添加してp Further, after reacting for 6 hours at 70 ° C., cooled to room temperature, aqueous ammonia was added as a neutralizing agent p
H調整をし、10μmのフィルターで濾過して目的のポリマー微粒子が水に分散した樹脂エマルジョンを得る。 The H adjusted to obtain a resin emulsion object of the polymer particles by filtration is dispersed in water at a 10μm filter. 【0050】樹脂エマルジョン2の最低成膜温度を前記の方法で測定した結果、25〜30℃で成膜した。 The results of the minimum film formation temperature of the resin emulsion 2 were measured by the aforementioned method, it was deposited at 25 to 30 ° C.. (最低成膜温度) <反応液>以下に記載する成分を混合し、反応液とした。 (Minimum film-forming temperature) by mixing the ingredients described <Reaction Liquid> The following were the reaction liquid. 【0051】 <反応液1> 硝酸マグネシウム・六水和物 25.6wt% (硝酸マグネシウム重量 14.8wt%) トリエチレングリコールモノブチルエーテル 10wt% グリセリン 10wt% イオン交換水 残量<反応液2> 硝酸マグネシウム・六水和物 34.6wt% (硝酸マグネシウム重量 20wt%) トリエチレングリコールモノブチルエーテル 10wt% グリセリン 10wt% イオン交換水 残量<樹脂エマルジョンの凝集性の評価>樹脂エマルジョン1および樹脂エマルジョン2の0.1重量%水分散液(樹脂成分換算で0.1重量%)を調製し、この水分散液を4g採取し、その後この水分散液に前記反応液1を1 [0051] <Reaction Solution 1> Magnesium nitrate hexahydrate 25.6wt% (magnesium nitrate weight 14.8wt%) Triethylene glycol monobutyl ether 10 wt% Glycerin 10 wt% Ion-exchanged water Balance <reaction 2> magnesium nitrate hexahydrate 34.6wt% <evaluation of cohesion of the resin emulsion> (magnesium nitrate by weight 20 wt%) triethylene glycol monobutyl ether 10 wt% glycerin 10 wt% ion-exchanged water Balance 0 resin emulsions 1 and resin emulsion 2. to prepare a 1 wt% aqueous dispersion (0.1 wt% in the resin component basis), the aqueous dispersion was 4g collected, then the reaction solution 1 in the aqueous dispersion 1
g添加し凝集物の発生の有無を目視で確認する(多価金属塩/樹脂エマルジョン=37)。 g was added to confirm the presence or absence of occurrence of aggregates visually (polyvalent metal salt / resin emulsion = 37). 【0052】A:凝集物の発生あり。 [0052] A: Yes occurrence of aggregates. NG:凝集物の発生無し。 NG: No occurrence of aggregates. 【0053】<吸光度の経時変化>樹脂エマルジョン1 [0053] <time-dependent change in absorbance> resin emulsion 1
および樹脂エマルジョン2の0.1重量%水分散液の吸光度を分光光度計(日立製作所製 U-3300)で700n And 700n absorbance of 0.1 wt% aqueous dispersion of resin emulsion 2 a spectrophotometer (manufactured by Hitachi, Ltd. U-3300)
mでの吸光度を測定する。 Measuring the absorbance at m. 次に、樹脂エマルジョン1および樹脂エマルジョン2の0.1重量%水分散液4gをそれぞれ吸光度測定用石英セル中に採取した後、同石英セル中に反応液2を1g添加し、反応液を添加した時間をゼロとして700nmでの吸光度の経時変化を測定する(多価金属塩/樹脂エマルジョン=50)。 Then, after collecting resin emulsion 1 and 0.1 wt% aqueous dispersion 4g resin emulsion 2 each in absorbance measurement for quartz cell, the reaction solution 2 was added 1g into the quartz cell, adding a reaction solution measuring the change with time in absorbance at 700nm and the time as zero (polyvalent metal salt / resin emulsion = 50). 【0054】吸光度測定は混合溶液の700nmでの吸光度が樹脂エマルジョン1および樹脂エマルジョン2の0.1重量%水分散液の吸光度の1/2となるまでの時間を求め以下の基準で評価する。 [0054] Absorbance measurements absorbance at 700nm of the mixed solution is evaluated by the time determined following criteria until half of the absorbance of 0.1 wt% aqueous dispersion of resin emulsion 1 and resin emulsion 2. A:60秒以内で吸光度が1/2となる。 A: absorbance is half in less than 60 seconds. B:吸光度が1/2となる時間が60秒以上である。 B: time the absorbance is 1/2 is greater than or equal to 60 seconds. 【0055】樹脂エマルジョンの評価結果は以下の通りであった。 [0055] The evaluation results of the resin emulsion were as follows. 【0056】 【表1】 [0056] [Table 1] 【0057】以下のインク組成物および反応液を常法に従い調製した。 [0057] The following ink composition and the reaction solution was prepared according to a conventional method. すなわち、インク組成物は着色剤成分の顔料を分散剤成分とともに分散した後に、他の成分を加え混合し、10μmのフィルターで濾過してインク組成物とした。 That is, the ink composition after the pigment of the coloring agent component is dispersed with a dispersant component were added and mixed with other ingredients, and the ink composition was filtered through a 10μm filter. 【0058】 <インク組成物> <インク1> カーボンブラックMA7 5wt% 液媒体スチレン−アクリル共重合体・アンモニウム塩 1.5wt% (分子量7000、樹脂成分38wt%:分散剤) 樹脂エマルジョン1 5wt% (樹脂成分30%) グリセリン 10wt% イオン交換水 残量インク2 カーボンブラックRaven1080 5wt% 液媒体スチレン−アクリル共重合体・アンモニウム塩 1.5wt% (分子量7000、樹脂成分38wt%:分散剤) 樹脂エマルジョン2 3wt% (樹脂成分30%) マルチトール 7wt% グリセリン 10wt% インク交換水 残量<評価1> <印字にじみ>インクジェットプリンターMJ−700 [0058] <Ink composition> <Ink 1> Carbon black MA7 5 wt% solution medium styrene - acrylic copolymer ammonium salt 1.5 wt% (molecular weight 7000, resin component 38 wt%: dispersant) resin emulsion 1 5 wt% ( resin component 30%) glycerin 10 wt% ion-exchanged water Balance ink 2 carbon black Raven 1080 5 wt% solution medium styrene - acrylic copolymer ammonium salt 1.5 wt% (molecular weight 7000, resin component 38 wt%: dispersant) resin emulsion 2 3 wt% (30% resin component) maltitol 7 wt% glycerin 10 wt% ink-exchanged water Balance <evaluation 1> <bleeding printing> jet printer MJ-700
V2C(セイコーエプソン(株)製)を用いて、Xerox Using the V2C (manufactured by Seiko Epson (Ltd.)), Xerox
4024 3R 721(ゼロックス(株)製)、Xerox R(ゼロックス(株)製、再生紙)の2紙に印刷を行った。 4024 (manufactured by Xerox Corp.) 3R 721, Xerox R (Xerox Corp., recycled paper) was printed on a 2 paper. 印刷は反応液を100%dutyで印刷した後、ドットを印字した。 Printing The reaction solution was printed at 100% duty, and printed dots. 【0059】インク組成物によるドットの真円度を4π [0059] The roundness of the dot by the ink composition 4π
S/L と定義したとき(ここで、Sはドット面積であり、Lはドットの周長である)、真円度を次のように評価した。 When defined as S / L 2 (where, S is a dot area, L is the circumferential length of dots) to evaluate the roundness as follows. A:両紙において、真円度が1〜0.9の場合。 A: In both papers, if the roundness of 1 to 0.9. B:いずれかまたは両紙において、真円度が0.9〜 B: in either or both papers, roundness 0.9
0.8。 0.8. NG:いずれかまたは両紙において、真円度が0.8未満。 NG: In either or both papers, is less than 0.8 roundness. 【0060】<評価2> <速乾性評価>インクジェットプリンターMJ−700 [0060] <Evaluation 2> <fast-drying evaluation> ink-jet printer MJ-700
V2C(セイコーエプソン(株)製)を用いて、 Xerox Using the V2C (manufactured by Seiko Epson (Ltd.)), Xerox
4024 3R 721(ゼロックス(株)製)にベタパターンを印字し、速乾性評価を行なった。 To print a solid pattern in 4024 3R 721 (manufactured by Xerox Co., Ltd.), was carried out the quick-drying evaluation. 印刷は反応液を100 100 The reaction solution is printing
%dutyで印刷した後、インク1〜2によりベタパターンを印刷し、印刷部分に印刷に使用した紙と同じ紙を置き、その上から250g/cm の荷重をかけ紙への裏移りの有無を調べ、紙への裏移りが無くなるまでの時間を測定する。 % After printing with duty, a solid pattern was printed by the ink 1-2, place the same paper as the paper used for printing in the printing section, the presence or absence of the set-off from thereon to paper under a load of 250 g / cm 2 It was examined to measure the time until the back transfer to the paper is eliminated. A:裏移りの無くなる時間が60秒未満。 A: no time of the setoff is less than 60 seconds. B:裏移りの無くなるまでの時間が60以上〜90秒未満。 B: time until no longer of setoff is less than more than 60 to 90 seconds. NG:裏移りの無くなるまでの時間が90秒以上。 NG: time until no longer of setoff is more than 90 seconds. 【0061】なお反応液重量は20ng/dot、インク重量は40ng/dotとした。 [0061] Note that reaction weight 20 ng / dot, the ink weight was 40 ng / dot. 【0062】 【表2】 [0062] [Table 2]

───────────────────────────────────────────────────── フロントページの続き Fターム(参考) 2C056 FC01 4J039 AB01 AD02 AD05 AD06 AD10 AD11 AD12 BA17 BA30 BC09 BC13 BC19 BC31 BC35 BC37 BC50 BC51 BC54 BE12 BE22 BE33 CA06 EA01 EA46 GA24 ────────────────────────────────────────────────── ─── front page of continued F-term (reference) 2C056 FC01 4J039 AB01 AD02 AD05 AD06 AD10 AD11 AD12 BA17 BA30 BC09 BC13 BC19 BC31 BC35 BC37 BC50 BC51 BC54 BE12 BE22 BE33 CA06 EA01 EA46 GA24

Claims (1)

  1. 【特許請求の範囲】 【請求項1】 少なくとも顔料、ポリマー微粒子、水溶性有機溶媒、水を含有するインクジェット記録用インク組成物であって、ポリマー微粒子が該ポリマー微粒子の0.1重量%水性分散液と多価金属塩含有水溶液とを混合した際に、多価金属塩とポリマー微粒子の重量比(多価金属塩/ポリマー微粒子)が50以下で凝集物を形成する事を特徴とするインクジェット記録用インク組成物。 [Claims 1 wherein at least a pigment, polymer particles, water-soluble organic solvent, an ink jet recording ink composition containing water, the polymer particles 0.1 wt% aqueous dispersion of the polymer particles when mixed with a liquid and a polyvalent metal salt-containing aqueous solution, an ink jet recording that the weight ratio of polyvalent metal salt and the polymer microparticles (polyvalent metal salt / polymer particles) is characterized in that to form aggregates at 50 or less iNK composition. 【請求項2】 少なくとも顔料、ポリマー微粒子、水溶性有機溶媒、水を含有するインクジェット記録用インク組成物であって、ポリマー微粒子が該ポリマー微粒子の0.1重量%水性分散液と多価金属塩含有水溶液との混合において、重量比で多価金属塩/ポリマー微粒子=5 Wherein at least a pigment, polymer particles, water-soluble organic solvent, an ink jet recording ink composition containing water, 0.1 wt% aqueous dispersion and the polyvalent metal salt of the polymer particles the polymer particles in admixture with an aqueous solution containing polyvalent metal salt / polymer particles in a weight ratio = 5
    0で混合した混合溶液の700nmでの吸光度が同波長でのポリマー微粒子水性分散液0.1重量%の吸光度の1/2となるのに要する時間が60秒以下である事を特徴とするインクジェット記録用インク組成物。 Inkjet absorbance at 700nm of the mixed mixture solution at 0 time required for a half of the polymer fine particle aqueous dispersion 0.1 wt% of the absorbance at the same wavelength is equal to or less than 60 seconds recording ink composition. 【請求項3】 前記ポリマー微粒子が皮膜形成能を有するポリマーからなるものである請求項1または2に記載のインクジェット記録用インク組成物。 Wherein the inkjet recording ink composition according to claim 1 or 2 polymer fine particles is made of a polymer having film forming ability. 【請求項4】 前記ポリマー微粒子を分散粒子とする水性樹脂エマルジョンが30℃以下の最低成膜温度を有するものである請求項1〜3のいずれか一項記載のインクジェット記録用インク組成物。 4. The inkjet recording ink composition of any one of the preceding claims, wherein 1 to 3 aqueous resin emulsion is one having a minimum film-forming temperature of 30 ° C. below the polymer particles and dispersion particles. 【請求項5】 前記ポリマー微粒子が親水性基を有するものである請求項1〜4のいずれか一項記載のインクジェット記録用インク組成物。 5. The inkjet recording ink composition of any one of claims 1 to 4 wherein the polymer particles are those having a hydrophilic group. 【請求項6】 前記ポリマー微粒子がカルボキシル基を有するものである請求項6記載のインクジェット記録用インク組成物。 6. An ink jet recording ink composition according to claim 6, wherein said polymer particles has a carboxyl group. 【請求項7】 前記ポリマー微粒子が水を分散媒とする樹脂エマルジョンの形態で用いられる事を特徴とする請求項1〜6のいずれか一項記載のインクジェット記録用インク組成物。 7. The inkjet recording ink composition of any one of claims 1 to 6, characterized in that the polymer particles used in the form of a resin emulsion as a dispersion medium of water. 【請求項8】 記録媒体に、反応剤を含んだ反応液とインク組成物とを付着させて印字を行なうインクジェット記録方法であって、前記反応液の反応剤が多価金属塩であり、前記インク組成物が請求項1〜7のいずれか一項記載のインク組成物であることを特徴とするインクジェット記録方法。 8. A recording medium, containing a reactant is adhered a reaction solution and an ink composition comprising an ink jet recording method for printing a reactant polyvalent metal salt of the reaction solution, the ink jet recording method wherein the ink composition is an ink composition of any one of claims 1 to 7.
JP22844098A 1998-08-12 1998-08-12 Ink composition for ink jet recording and recording Withdrawn JP2000063719A (en)