JP2000008004A - Tacky tape, its production, tape and production thereof - Google Patents
Tacky tape, its production, tape and production thereofInfo
- Publication number
- JP2000008004A JP2000008004A JP17313698A JP17313698A JP2000008004A JP 2000008004 A JP2000008004 A JP 2000008004A JP 17313698 A JP17313698 A JP 17313698A JP 17313698 A JP17313698 A JP 17313698A JP 2000008004 A JP2000008004 A JP 2000008004A
- Authority
- JP
- Japan
- Prior art keywords
- blade
- tape
- upper blade
- cutting
- film sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【0001】[0001]
【発明の属する技術分野】この発明は、荷造り等に使用
されるテープ及び粘着テープ、並びにそれらの製造方法
に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a tape and an adhesive tape used for packing and the like, and a method for producing the same.
【0002】[0002]
【従来の技術】現在使用されている手切れ性を有する粘
着テープは、PE横1軸延伸フィルムシート、横方向2
軸ポリプロピレンフィルムシート、ミシン目加工フィル
ムシート等に粘着剤を塗布してカッターで切断したもの
である。2. Description of the Related Art Currently used adhesive tapes having hand-cutting properties include a PE transversely uniaxially stretched film sheet, a transverse direction of 2 mm.
An adhesive is applied to a shaft polypropylene film sheet, a perforated film sheet, or the like, and cut with a cutter.
【0003】[0003]
【発明が解決しようとする課題】これらのフィルムは生
産時に高温にすると、フィルムの伸びとチリメン皺、フ
レアーが発生し、手切れが悪くなる欠点がある。また、
縦強度が極端に低いため、生産加工時にフィルム切断が
多発する欠点がある。When these films are heated to a high temperature during production, they have drawbacks in that film elongation, wrinkles and flare occur, and hand cutting is poor. Also,
Since the longitudinal strength is extremely low, there is a disadvantage that film cutting frequently occurs during production processing.
【0004】これらの欠点をなくすためには、一般的に
縦強度、大きい、すなわち引張り強度の大きい縦1軸延
伸または2軸延伸されたポリオレフィン,ポリエステ
ル,ポリエチレン系の粘着フィルムシートを切断し、得
られた粘着テープに、手切れのきっかけとなるV字ノッ
チを入れることが考えられる。このようにすると、粘着
テープの引張り強度は大きくなる。しかし、テープ巻戻
し時に、V字ノッチ部分からの裂けが伝播し、巻戻し切
れが発生する。また、使用時にV字ノッチ部分から裂け
て切れることがある。[0004] In order to eliminate these drawbacks, generally, an adhesive film sheet of a polyolefin, polyester, or polyethylene stretched uniaxially or biaxially stretched with a large longitudinal strength, that is, a large tensile strength, is obtained by cutting. It is conceivable to put a V-shaped notch in the obtained adhesive tape, which triggers a hand cut. In this case, the tensile strength of the adhesive tape increases. However, when the tape is rewound, the tear from the V-shaped notch propagates, and the rewound ends. In addition, it may tear off from the V-shaped notch during use.
【0005】このような切れが生じない手切りのきっか
けを作るためには、粘着フィルムシートをテープ状に切
断した時の切断面を連続した丸みのある微小凹凸面にす
る必要がある。[0005] In order to make a hand-cutting trigger that does not cause such a cut, it is necessary to make the cut surface when the adhesive film sheet is cut into a tape shape into a continuous rounded fine uneven surface.
【0006】この丸みのある微小凹凸面があれば、その
凹部をきっかけとして手で切ることができる。この時、
粘着テープが伸びれば、手切れ性は悪くなるが、粘着テ
ープの基材として上述した縦強度の大きいフィルムを使
用すれば、伸びは少なく、手切れ性は良くなる。[0006] If there is this rounded fine uneven surface, it can be cut by hand using the concave portion as a trigger. At this time,
If the pressure-sensitive adhesive tape is stretched, the hand-cutting property is deteriorated. However, if the above-described film having a large vertical strength is used as the base material of the pressure-sensitive adhesive tape, the hand-cutting property is improved with little elongation.
【0007】この発明は、このような技術的背景の下で
なされたもので、引張り強度が大きく、かつ手切れ性の
良い粘着テープ及びその製造方法、並びにテープ及びそ
の製造方法を提供することを目的とする。The present invention has been made under such a technical background, and it is an object of the present invention to provide an adhesive tape having high tensile strength and good hand-cutting properties, a method for manufacturing the same, and a tape and a method for manufacturing the same. Aim.
【0008】[0008]
【課題を解決するための手段】(1)この発明に係る粘
着テープは、縦1軸延伸または縦2軸延伸されたポリオ
レフィン,ポリエステル,ポリウレタン系の粘着フィル
ムシートを縦方向にテープ状に切断して得られる粘着テ
ープであって、切断面が連続した丸みのある微小凹凸面
となっているものである。(1) An adhesive tape according to the present invention is obtained by cutting a polyolefin, polyester or polyurethane-based adhesive film sheet stretched uniaxially or biaxially in a longitudinal direction into a tape shape. The adhesive tape obtained in this manner has a cut surface having a continuous rounded fine uneven surface.
【0009】上記連続した丸みのある微小凹凸面は、上
刃に回転ミシン目刃、下刃に砂状表面の回転ロールを使
用して粘着フィルムシートを切断することによって得る
ことができる。The continuous rounded fine irregular surface can be obtained by cutting a pressure-sensitive adhesive film sheet using a rotary perforated blade as an upper blade and a rotating roll with a sandy surface as a lower blade.
【0010】上記上刃と下刃の回転速度比は、1:1.
1〜1:3.0の範囲にあるのが好ましい。The rotation speed ratio between the upper blade and the lower blade is 1: 1.
It is preferably in the range of 1-1: 3.0.
【0011】上記上刃のミシン目の大きさは、上刃の円
周の1/100〜1/600であり、下刃の砂状表面は
6号〜8号の珪砂を使用した砂状表面に相当するもので
あるのが好ましい。The size of the perforations of the upper blade is 1/100 to 1/600 of the circumference of the upper blade, and the sandy surface of the lower blade is a sandy surface using silica sand of No. 6 to No. 8. Is preferably equivalent to
【0012】(2)この発明に係る粘着テープの製造方
法は、縦1軸延伸または縦2軸延伸されたポリオレフィ
ン,ポリエステル,ポリウレタン系の粘着フィルムシー
トを、上刃に回転ミシン目刃、下刃に砂状表面の回転ロ
ールを使用して、縦方向にテープ状に切断することを特
徴とする方法である。(2) The method for producing a pressure-sensitive adhesive tape according to the present invention is characterized in that a vertically uniaxially stretched or biaxially stretched polyolefin, polyester, or polyurethane-based pressure-sensitive adhesive film sheet is used as an upper blade with a rotary perforated blade and a lower blade. Using a rotating roll having a sand-like surface, and cutting the tape in the vertical direction.
【0013】上記上刃と下刃の回転速度比は、1:1.
1〜1:3.0の範囲にあるのが好ましい。The rotational speed ratio between the upper blade and the lower blade is 1: 1.
It is preferably in the range of 1-1: 3.0.
【0014】上記上刃のミシン目の大きさは、上刃の円
周の1/100〜1/600であり、下刃の砂状表面は
4号〜8号の珪砂を使用した砂状表面に相当するもので
あるのが好ましい。The size of the perforations of the upper blade is 1/100 to 1/600 of the circumference of the upper blade, and the sandy surface of the lower blade is a sandy surface using silica sand of No. 4 to No. 8. Is preferably equivalent to
【0015】(3)この発明に係るテープは、縦1軸延
伸または縦2軸延伸されたポリオレフィン,ポリエステ
ル,ポリウレタン系のフィルムシートを縦方向にテープ
状に切断して得られるテープであって、切断面が連続し
た丸みのある微小凹凸面となっているものである。(3) The tape according to the present invention is a tape obtained by cutting a longitudinally uniaxially or biaxially oriented polyolefin, polyester, or polyurethane film sheet into a tape in the longitudinal direction. The cut surface is a continuous rounded fine uneven surface.
【0016】上記連続した丸みのある微小凹凸面は、上
刃に回転ミシン目刃、下刃に砂状表面の回転ロールを使
用してフィルムシートを切断することによって得ること
ができる。[0016] The continuous rounded fine uneven surface can be obtained by cutting a film sheet using a rotary perforated blade as an upper blade and a rotating roll having a sandy surface as a lower blade.
【0017】上記上刃と下刃の回転速度比は、1:1.
1〜1:3.0の範囲にあるのが好ましい。The rotational speed ratio between the upper blade and the lower blade is 1: 1.
It is preferably in the range of 1-1: 3.0.
【0018】上記上刃のミシン目の大きさは、上刃の円
周の1/100〜1/600であり、下刃の砂状表面は
4号〜8号の珪砂を使用した砂状表面に相当するもので
あることが好ましい。The size of the perforations of the upper blade is 1/100 to 1/600 of the circumference of the upper blade, and the sandy surface of the lower blade is a sandy surface using silica sand of No. 4 to No. 8. Preferably, it is equivalent to
【0019】(4)この発明に係るテープの製造方法
は、縦1軸延伸または縦2軸延伸されたポリオレフィ
ン,ポリエステル,ポリウレタン系のフィルムシート
を、上刃に回転ミシン目刃、下刃に砂状表面の回転ロー
ルを使用して、縦方向にテープ状に切断することを特徴
とする方法である。(4) The method for producing a tape according to the present invention is characterized in that a longitudinally uniaxially or biaxially stretched polyolefin, polyester, or polyurethane film sheet is provided with a rotary perforated blade as an upper blade and sand as a lower blade. The method is characterized in that it is cut into a tape shape in the vertical direction using a rotating roll having a shape surface.
【0020】上記上刃と下刃の回転速度比は、1:1.
1〜1:3.0の範囲にあるのが好ましい。The rotation speed ratio between the upper blade and the lower blade is 1: 1.
It is preferably in the range of 1-1: 3.0.
【0021】上記上刃のミシン目の大きさは、上刃の円
周の1/100〜1/600であり、下刃の砂状表面は
4号〜8号の珪砂を使用した砂状表面に相当するもので
あるのが好ましい。The size of the perforations of the upper blade is 1/100 to 1/600 of the circumference of the upper blade, and the sandy surface of the lower blade is a sandy surface using silica sand of No. 4 to No. 8. Is preferably equivalent to
【0022】[0022]
【作用】この発明による粘着テープ及びテープは、上述
のフィルムシートを基材としているから、引張り強度が
強い。また、それらの切断面は、丸みのある微小凹凸面
となっているから、その凹部は手切りのきっかけとなる
が、テープを引張った時の断裂のきっかけとはならな
い。The pressure-sensitive adhesive tape and tape according to the present invention have a high tensile strength because the above-mentioned film sheet is used as a base material. In addition, since the cut surfaces are rounded minute uneven surfaces, the concave portions serve as triggers for hand-cutting, but do not serve as triggers for tearing when the tape is pulled.
【0023】また、この発明における粘着テープ及びテ
ープは、上記回転ミシン目刃と砂状表面の回転ロールを
使用して切断するから、その切断面は丸みのある微小凹
凸面となる。特に、両者の回転速度比を1:1.1〜
1:3.0の範囲にした場合には、回転ミシン目刃がフ
ィルムシートを回転ロールに押しつけるようにして、同
シートの上を移動するので、その切断面は、手切りのき
っかけとなるが、断裂のきっかけとならない丸みのある
微小凹凸面となる。Further, since the adhesive tape and the tape in the present invention are cut using the above-mentioned rotary perforation blade and a rotary roll having a sand-like surface, the cut surface becomes a rounded fine uneven surface. In particular, the rotational speed ratio of both is 1: 1.1 to
In the case of the range of 1: 3.0, since the rotating perforation blade moves on the rotating sheet while pressing the film sheet against the rotating roll, the cut surface is a trigger for hand cutting. , Resulting in a rounded micro uneven surface that does not trigger a tear.
【0024】[0024]
【発明の実施の形態】以下、この発明の実施の形態を実
施例によって説明する。Embodiments of the present invention will be described below with reference to embodiments.
【0025】下記の縦強度の大きい粘着フィルムシート
(幅600mm、長さ30m)を、下記スリッターで切断
して幅15mmの粘着テープを得た。The following adhesive film sheet having a large longitudinal strength (width: 600 mm, length: 30 m) was cut by a slitter to obtain an adhesive tape having a width of 15 mm.
【0026】(1)粘着フィルムシートの種類(1) Types of adhesive film sheet
【0027】[0027]
【表1】 [Table 1]
【0028】(2)スリッターによる粘着フィルムシー
トの切断 図1に示すように、実施例1〜4の粘着フィルムシート
1の原反2から同シート1を引き出し、ガイドローラ3
で上刃4と下刃5の間に導き、ここでテープ状に切断し
て粘着テープ6とした。(2) Cutting of the adhesive film sheet by the slitter As shown in FIG. 1, the sheet 1 is pulled out from the raw material 2 of the adhesive film sheet 1 of Examples 1 to 4,
Then, it was guided between the upper blade 4 and the lower blade 5, and cut into a tape shape to form an adhesive tape 6.
【0029】(3)使用した上刃4と下刃5の組み合わ
せと回転速度比(3) Combination of upper blade 4 and lower blade 5 used and rotational speed ratio
【0030】[0030]
【表2】 [Table 2]
【0031】得られた実施例1〜4と比較例1,2の粘
着テープの手切れ性を評価したところ、表3のとおりで
あった。The adhesive tapes of Examples 1 to 4 and Comparative Examples 1 and 2 were evaluated for hand-cutting properties.
【0032】手切れ性は、粘着テープをロールテープか
ら引き出し、ロールテープ上に指で押さえつけ、先端部
を横方向に引張って引き裂くことによって評価した。The hand-cutting property was evaluated by pulling out the adhesive tape from the roll tape, pressing the adhesive tape on the roll tape with a finger, and pulling the tip portion in the lateral direction to tear.
【0033】[0033]
【表3】 [Table 3]
【0034】また、実施例1〜4と比較例1,2の粘着
テープを引張って伸ばしたときの断裂性について調べた
ところ、表4のとおりであった。Table 4 shows the tearability of the pressure-sensitive adhesive tapes of Examples 1 to 4 and Comparative Examples 1 and 2 when pulled and stretched.
【0035】断裂性は、ロールテープを高速(300
r.p.m)で巻き戻したときの断裂の有無で評価し
た。The tear property is determined by using a high-speed roll tape (300
r. p. The evaluation was performed based on the presence or absence of a tear when the film was rewound in m).
【0036】[0036]
【表4】 [Table 4]
【0037】上記実施例は、粘着フィルムシートを切断
して得られる粘着テープについたものであるが、粘着剤
を塗布しないフィルムシートから得られるテープについ
ての実施例もほぼ同様の結果が得られた。Although the above-described example is for an adhesive tape obtained by cutting an adhesive film sheet, almost the same results were obtained in an example of a tape obtained from a film sheet to which no adhesive was applied. .
【0038】[0038]
【発明の効果】以上説明したように、この発明によれ
ば、上述のような構成としたので、引張り強度が大き
く、かつ手切れ性の良い粘着テープ及びテープを得るこ
とができる。As described above, according to the present invention, since the above-mentioned structure is adopted, it is possible to obtain an adhesive tape and a tape having high tensile strength and good hand-cutting properties.
【図面の簡単な説明】[Brief description of the drawings]
【図1】 実施例の粘着テープを製造するスリッターの
構成図FIG. 1 is a configuration diagram of a slitter for producing an adhesive tape of an embodiment.
1 粘着フィルムシート 2 原反 3 ガイドローラ 4 上刃 5 下刃 DESCRIPTION OF SYMBOLS 1 Adhesive film sheet 2 Raw material 3 Guide roller 4 Upper blade 5 Lower blade
Claims (14)
オレフィン,ポリエステル,ポリウレタン系の粘着フィ
ルムシートを縦方向にテープ状に切断して得られる粘着
テープであって、切断面が連続した丸みのある微小凹凸
面となっていることを特徴とする粘着テープ。A pressure-sensitive adhesive tape obtained by cutting a polyolefin, polyester, or polyurethane-based pressure-sensitive adhesive film sheet that has been stretched uniaxially or biaxially in a longitudinal direction into a tape, wherein the cut surface has a continuous roundness. Adhesive tape characterized by having a fine uneven surface with roughness.
に回転ミシン目刃、下刃に砂状表面の回転ロールを使用
して粘着フィルムシートを切断することによって得られ
るものである請求項1記載の粘着テープ。2. The continuous rounded micro-textured surface is obtained by cutting an adhesive film sheet using a rotary perforated blade as an upper blade and a rotating roll with a sandy surface as a lower blade. Item 6. The adhesive tape according to Item 1.
1:3.0である請求項2記載の粘着テープ。3. The rotation speed ratio between the upper blade and the lower blade is 1: 1.1 to
The pressure-sensitive adhesive tape according to claim 2, wherein the ratio is 1: 3.0.
の1/100〜1/600であり、下刃の砂状表面は4
号〜8号の珪砂を使用した砂状表面に相当するものであ
ることを特徴とする請求項2または3記載の粘着テー
プ。4. The size of the perforations of the upper blade is 1/100 to 1/600 of the circumference of the upper blade, and the sandy surface of the lower blade is 4/100.
The pressure-sensitive adhesive tape according to claim 2 or 3, which corresponds to a sand-like surface using silica sand of Nos. 1 to 8.
オレフィン,ポリエステル,ポリウレタン系の粘着フィ
ルムシートを、上刃に回転ミシン目刃、下刃に砂状表面
の回転ロールを使用して、縦方向にテープ状に切断する
ことを特徴とする粘着テープの製造方法。5. An adhesive film sheet of a polyolefin, polyester, or polyurethane stretched uniaxially or biaxially longitudinally, using a rotary perforated blade as an upper blade and a rotary roll having a sandy surface as a lower blade. A method for producing a pressure-sensitive adhesive tape, comprising cutting the tape in a longitudinal direction.
1:3.0である請求項5記載の粘着テープの製造方
法。6. The rotation speed ratio of the upper blade to the lower blade is 1: 1.1 to
The method for producing an adhesive tape according to claim 5, wherein the ratio is 1: 3.0.
の1/100〜1/600であり、下刃の砂状表面は4
号〜8号の珪砂を使用した砂状表面に相当するものであ
ることを特徴とする請求項5または6記載の粘着テープ
の製造方法。7. The size of the perforations of the upper blade is 1/100 to 1/600 of the circumference of the upper blade, and the sandy surface of the lower blade is 4/100.
The method for producing a pressure-sensitive adhesive tape according to claim 5 or 6, which corresponds to a sand-like surface using silica sand of Nos. 1 to 8.
オレフィン,ポリエステル,ポリウレタン系のフィルム
シートを縦方向にテープ状に切断して得られる粘着テー
プであって、切断面が連続した丸みのある微小凹凸面と
なっていることを特徴とするテープ。8. An adhesive tape obtained by cutting a longitudinally or biaxially stretched polyolefin, polyester, or polyurethane film sheet into a tape in the longitudinal direction, wherein the cut surface has a continuous round shape. A tape characterized by having a certain uneven surface.
に回転ミシン目刃、下刃に砂状表面の回転ロールを使用
してフィルムシートを切断することによって得られるも
のである請求項8記載のテープ。9. The continuous rounded fine uneven surface is obtained by cutting a film sheet using a rotary perforated blade as an upper blade and a rotating roll with a sand-like surface as a lower blade. 8. The tape according to 8.
〜1:3.0である請求項9記載のテープ。10. The rotation speed ratio between the upper blade and the lower blade is 1: 1.1.
10. The tape according to claim 9, wherein the ratio is 1 : 1: 3.0.
周の1/100〜1/600であり、下刃の砂状表面は
4号〜8号の珪砂を使用した砂状表面に相当するもので
あることを特徴とする請求項9または10記載のテー
プ。11. The size of the perforation of the upper blade is 1/100 to 1/600 of the circumference of the upper blade, and the sandy surface of the lower blade is sandy using silica sand of No. 4 to No. 8. 11. The tape according to claim 9, wherein the tape corresponds to a surface.
リオレフィン,ポリエステル,ポリウレタン系のフィル
ムシートを、上刃に回転ミシン目刃、下刃に砂状表面の
回転ロールを使用して、縦方向にテープ状に切断するこ
とを特徴とするテープの製造方法。12. A polyolefin, polyester, or polyurethane film sheet stretched uniaxially or biaxially in a longitudinal direction is rotated by using a rotary perforated blade as an upper blade and a rotating roll having a sandy surface as a lower blade. A method for producing a tape, comprising cutting the tape in a direction.
〜1:3.0である請求項12記載のテープの製造方
法。13. The rotation speed ratio between the upper blade and the lower blade is 1: 1.1.
The method for producing a tape according to claim 12, wherein the ratio is 1 : 1: 3.0.
周の1/100〜1/600であり、下刃の砂状表面は
4号〜8号の珪砂を使用した砂状表面に相当するもので
あることを特徴とする請求項12または13記載のテー
プの製造方法。14. The size of the perforations of the upper blade is 1/100 to 1/600 of the circumference of the upper blade, and the sandy surface of the lower blade is sandy using silica sand of No. 4 to No. 8. 14. The method for producing a tape according to claim 12, wherein the tape corresponds to a surface.