IT202000015994A1 - COMPOSITE MATERIAL INCLUDING A CORK MATERIAL AND A POLYMER MATERIAL - Google Patents
COMPOSITE MATERIAL INCLUDING A CORK MATERIAL AND A POLYMER MATERIAL Download PDFInfo
- Publication number
- IT202000015994A1 IT202000015994A1 IT102020000015994A IT202000015994A IT202000015994A1 IT 202000015994 A1 IT202000015994 A1 IT 202000015994A1 IT 102020000015994 A IT102020000015994 A IT 102020000015994A IT 202000015994 A IT202000015994 A IT 202000015994A IT 202000015994 A1 IT202000015994 A1 IT 202000015994A1
- Authority
- IT
- Italy
- Prior art keywords
- cork
- composite material
- based material
- combination
- weight
- Prior art date
Description
DESCRIZIONE DESCRIPTION
Annessa a domanda di brevetto per INVENZIONE INDUSTRIALE avente per titolo Attached to a patent application for INDUSTRIAL INVENTION having the title
?Materiale composito comprendente un materiale a base di sughero e un materiale polimerico? ?Composite material comprising a cork-based material and a polymeric material?
CAMPIO TECNICO TECHNICAL FIELD
La presente invenzione ha per oggetto un materiale composito comprendente un materiale a base di sughero ed un materiale polimerico, un processo per ottenerlo e un multistrato comprendente detto materiale composito. La presente invenzione riguarda inoltre un manufatto interamente costituito da o comprendente detto materiale composito o detto multistrato ed il suo uso come elemento di arredo o rivestimento. The present invention relates to a composite material comprising a cork-based material and a polymeric material, a process for obtaining it and a multilayer comprising said composite material. The present invention also relates to a product entirely made up of or comprising said composite material or said multilayer and its use as a furnishing or covering element.
STATO DELL?ARTE STATE OF ART
I materiali a base di sughero attualmente disponibili sul mercato presentano numero svantaggi che ne limitano l?impiego soprattutto in quei settori in cui sono richiesti materiali aventi differenti caratteristiche, come ad esempio resistenza alla flessione coniugata a resistenza alla compressione, e che possano garantire allo stesso tempo le desiderate propriet? di resistenza all?usura, impermeabilit? all?acqua, all?olio, ai solventi organici e resistenza alla proliferazione parassitaria. Allo stato dell?arte attuale non ? infatti disponibile un materiale a base di sughero che possieda una tale vasta gamma di propriet? e che possa essere pertanto efficacemente impiegato in una variet? di usi differenti. The cork-based materials currently available on the market have a number of disadvantages which limit their use especially in those sectors where materials with different characteristics are required, such as for example flexural strength combined with compressive strength, and which can guarantee the same time do you want the property? of resistance to? wear, impermeabilit? to water, oil, organic solvents and resistance to parasitic proliferation. In the current state of the art, isn't it? In fact, is there a cork-based material that possesses such a wide range of properties? and that it can therefore be effectively used in a variety of? of different uses.
Permane pertanto nel settore la necessit? di mettere a disposizione un materiale a base di sughero che presenti differenti propriet?, in particolare un materiale caratterizzato da elevata flessibilit? e resistenza. Therefore remains in the sector the need? to make available a cork-based material that has different properties, in particular a material characterized by high flexibility? and resistance.
La presente invenzione risolve i problemi dell?arte nota sopra esposti mettendo a disposizione un materiale composito comprendente un materiale a base di sughero e un materiale polimerico che conferiscono al materiale le caratteristiche di resistenza alla flessione, resistenza alla compressione e/o resistenza alla proliferazione parassitaria desiderate e che pu? essere utilizzato in una variet? di impieghi differenti. The present invention solves the problems of the prior art set out above by making available a composite material comprising a cork-based material and a polymeric material which give the material the characteristics of resistance to bending, resistance to compression and/or resistance to parasitic proliferation do you want and what can? be used in a variety of different jobs.
Con la presente invenzione, la Richiedente mette inoltre a disposizione un multistrato comprendente detto materiale composito e un manufatto interamente costituito da o comprendente detto materiale composito o detto multistrato che pu? essere realizzato in varie forme e spessori rendendolo cos? versatile per una variet? di applicazioni differenti. With the present invention, the Applicant also makes available a multilayer comprising said composite material and a manufactured article entirely made up of or comprising said composite material or said multilayer which can be made in various shapes and thicknesses making it cos? versatile for a variety of different applications.
RIASSUNTO DELL?INVENZIONE SUMMARY OF THE INVENTION
La presente invenzione ha per oggetto un materiale composito comprendente un materiale a base di sughero ed un materiale polimerico, detto materiale polimerico essendo ottenuto dalla reazione di almeno una resina epossidica con almeno una resina poliammidica in un rapporto in peso resina epossidica:resina poliammidica compreso tra 10:90 e 70:30. The present invention relates to a composite material comprising a cork-based material and a polymeric material, said polymeric material being obtained from the reaction of at least one epoxy resin with at least one polyamide resin in an epoxy resin:polyamide resin weight ratio between 10:90 and 70:30.
Detto materiale composito possiede preferibilmente almeno una delle seguenti caratteristiche: Said composite material preferably possesses at least one of the following characteristics:
a) densit? compresa tra 0,4 e 2,5 g/cm<3>; a) density? between 0.4 and 2.5 g/cm<3>;
b) resistenza a flessione compresa tra 10 e 50 N/mm<2>; b) flexural strength between 10 and 50 N/mm<2>;
c) resistenza alla compressione compresa tra 25 e 400 Kg/cm<2>; c) compressive strength between 25 and 400 Kg/cm<2>;
d) resistenza alla proliferazione parassitaria, preferibilmente alla proliferazione di funghi e/o muffe. d) resistance to parasitic proliferation, preferably to the proliferation of fungi and/or moulds.
Secondo una forma di realizzazione preferita dell?invenzione, detto materiale a base di sughero e detto materiale polimerico sono intimamente miscelati e sono preferibilmente presenti all?interno del materiale composito in una quantit? compresa tra 5 e 2000 parti in peso di materiale polimerico per 100 parti in peso di materiale a base di sughero. According to a preferred embodiment of the invention, said cork-based material and said polymeric material are intimately mixed and are preferably present within the composite material in a quantity between 5 and 2000 parts by weight of polymeric material per 100 parts by weight of cork-based material.
Secondo un?altra forma di realizzazione della presente invenzione, detto materiale composito comprende almeno due strati discreti in cui un primo strato ? realizzato con detto materiale a base di sughero e in cui un secondo strato ? realizzato con detto materiale polimerico. According to another embodiment of the present invention, said composite material comprises at least two discrete layers wherein a first layer is made with said cork-based material and in which a second layer? made with said polymeric material.
La presente invenzione riguarda inoltre un processo per l?ottenimento di detto materiale composito comprendente i passaggi di: The present invention also relates to a process for obtaining said composite material comprising the steps of:
i) miscelare almeno una resina epossidica e almeno una resina poliammidica in un rapporto in peso resina epossidica:resina poliammidica compreso tra 10:90 e 70:30; i) mixing at least one epoxy resin and at least one polyamide resin in an epoxy resin:polyamide resin weight ratio comprised between 10:90 and 70:30;
ii) mescolare intimamente la miscela di resine ottenuta al passaggio i) con un materiale a base di sughero, preferibilmente in una quantit? compresa tra 5 e 2000 parti in peso di detta miscela di resine per 100 parti in peso di detto materiale a base di sughero; oppure ii) intimately mixing the mixture of resins obtained in step i) with a cork-based material, preferably in a quantity comprised between 5 and 2000 parts by weight of said mixture of resins per 100 parts by weight of said cork-based material; or
iia) colare la miscela di resine ottenuta al passaggio i) su uno strato realizzato con un materiale a base di sughero; iia) pouring the mixture of resins obtained in step i) onto a layer made of a cork-based material;
iii) attendere l?avanzamento della reazione di polimerizzazione tra l?almeno una resina epossidica e l?almeno una resina poliammidica, fino all?ottenimento di un materiale composito indurito comprendente il materiale a base di sughero e il materiale polimerico ottenuto dalla reazione dell?almeno una resina epossidica con l?almeno una resina poliammidica. iii) wait for the polymerization reaction to progress between the at least one epoxy resin and the at least one polyamide resin, until obtaining a hardened composite material comprising the cork-based material and the polymeric material obtained from the reaction of the at least an epoxy resin with the at least one polyamide resin.
La presente invenzione ha per oggetto anche un multistrato comprendente: The present invention also relates to a multilayer comprising:
A) un primo strato realizzato con detto materiale composito; A) a first layer made with said composite material;
B) almeno un ulteriore strato realizzato con un materiale scelto nel gruppo costituito da: quarzo intimamente miscelato con un materiale polimerico, fibra di vetro, fibra di carbonio, marmo, acciaio, legno, sughero in forma di una lastra preformata; e B) at least one further layer made with a material selected from the group consisting of: quartz intimately mixed with a polymeric material, glass fibre, carbon fibre, marble, steel, wood, cork in the form of a preformed plate; And
C) opzionalmente, almeno un ulteriore strato realizzato con detto materiale composito oppure uno strato di sughero in forma di una lastra preformata. C) optionally, at least one further layer made with said composite material or a layer of cork in the form of a preformed plate.
La presente invenzione riguarda anche un manufatto interamente costituito da o comprendente detto materiale composito o detto multistrato e il suo uso come elemento di arredo, di design, di costruzione, di rivestimento di una superficie o una loro combinazione. The present invention also relates to a product entirely made up of or comprising said composite material or said multilayer and its use as a furnishing, design, construction, surface covering element or a combination thereof.
DESCRIZIONE DETTAGLIATA DELL?INVENZIONE DETAILED DESCRIPTION OF THE INVENTION
Per ?temperatura ambiente?, ai fini della presente invenzione, si intende un intervallo di temperatura compreso tra i 5 e i 30 ?C, preferibilmente tra i 15 e i 30 ?C, preferibilmente tra i 18 e i 25 ?C. By "ambient temperature", for the purposes of the present invention, we mean a temperature range between 5 and 30 ?C, preferably between 15 and 30 ?C, preferably between 18 and 25 ?C.
Per ?pressione ambiente?, ai fini della presente invenzione, si intende un intervallo di pressione atmosferica compreso tra 880 e 1000 hPa e preferibilmente tra 950 e 990 hPa. By ?ambient pressure?, for the purposes of the present invention, we mean an atmospheric pressure range comprised between 880 and 1000 hPa and preferably between 950 and 990 hPa.
La presente invenzione ha per oggetto un materiale composito comprendente un materiale a base di sughero ed un materiale polimerico, detto materiale polimerico essendo ottenuto dalla reazione di almeno una resina epossidica con almeno una resina poliammidica in un rapporto in peso resina epossidica:resina poliammidica compreso tra 10:90 e 70:30. Preferibilmente, detto rapporto in peso resina epossidica:resina poliammidica ? compreso tra 80:20 e 30:70. The present invention relates to a composite material comprising a cork-based material and a polymeric material, said polymeric material being obtained from the reaction of at least one epoxy resin with at least one polyamide resin in an epoxy resin:polyamide resin weight ratio between 10:90 and 70:30. Preferably, said epoxy resin:polyamide resin weight ratio ? between 80:20 and 30:70.
Secondo una forma di realizzazione dell?invenzione, detto materiale composito possiede almeno una delle seguenti caratteristiche: According to an embodiment of the invention, said composite material has at least one of the following characteristics:
a) densit? compresa tra 0,4 e 2,5 g/cm<3>, preferibilmente tra 0,8 e 2,3 g/cm<3>, pi? preferibilmente tra 1 e 2 g/cm<3>; a) density? between 0.4 and 2.5 g/cm<3>, preferably between 0.8 and 2.3 g/cm<3>, more? preferably between 1 and 2 g/cm<3>;
b) resistenza a flessione compresa tra 10 e 50 N/mm<2>, preferibilmente tra 15 e 45 N/mm<2>, pi? preferibilmente tra 25 e 40 N/mm<2>; b) flexural strength between 10 and 50 N/mm<2>, preferably between 15 and 45 N/mm<2>, more? preferably between 25 and 40 N/mm<2>;
c) resistenza alla compressione compresa tra 25 e 400 Kg/cm<2>, preferibilmente tra 30 e 300 Kg/cm<2>, pi? preferibilmente tra 100 e 250 Kg/cm<2>; c) compressive strength between 25 and 400 Kg/cm<2>, preferably between 30 and 300 Kg/cm<2>, more? preferably between 100 and 250 Kg/cm<2>;
d) resistenza alla proliferazione parassitaria, preferibilmente alla proliferazione di funghi e/o muffe. Secondo una forma di realizzazione preferita dell?invenzione, detto materiale composito possiede almeno due delle suddette caratteristiche, preferibilmente almeno a) e b), pi? preferibilmente almeno a) e c), pi? preferibilmente almeno a) e d), pi? preferibilmente b) e d), ancora pi? preferibilmente c) e d). Secondo una forma di realizzazione preferita dell?invenzione, detto materiale composito possiede almeno tre delle suddette caratteristiche, preferibilmente almeno a), b) e c), pi? preferibilmente almeno a), b) e d), pi? preferibilmente almeno b), c) e d), ancora pi? preferibilmente a), c) e d). d) resistance to parasitic proliferation, preferably to the proliferation of fungi and/or moulds. According to a preferred embodiment of the invention, said composite material has at least two of the above characteristics, preferably at least a) and b), plus? preferably at least a) and c), pi? preferably at least a) and d), pi? preferably b) and d), even more? preferably c) and d). According to a preferred embodiment of the invention, said composite material has at least three of the above characteristics, preferably at least a), b) and c), plus? preferably at least a), b) and d), pi? preferably at least b), c) and d), even more? preferably a), c) and d).
Secondo una forma di realizzazione particolarmente preferita dell?invenzione, detto materiale composito possiede tutte e quattro le suddette caratteristiche, ovvero a), b), c) e d) simultaneamente. According to a particularly preferred embodiment of the invention, said composite material possesses all four of the above characteristics, ie a), b), c) and d) simultaneously.
Preferibilmente, in aggiunta o in alternativa alle caratteristiche sopracitate, secondo una forma di realizzazione dell?invenzione, il materiale composito possiede la caratteristica e) di essere resistente (ovvero rimanere integro e/o non deformato) se sottoposto ad un trattamento di compressione/spremitura sotto acqua calda, preferibilmente acqua ad una temperatura tra 80 e 100 ?C, ad un pH compreso tra 3 e 5, preferibilmente ad un pH di circa 4. Preferably, in addition or as an alternative to the aforementioned characteristics, according to an embodiment of the invention, the composite material has the characteristic e) of being resistant (that is, remaining intact and/or not deformed) if subjected to a compression/squeezing treatment under warm water, preferably water at a temperature between 80 and 100°C, at a pH between 3 and 5, preferably at a pH of about 4.
Preferibilmente, detta almeno una resina epossidica ? ottenuta dalla reazione di condensazione di almeno un fenolo poliidrico con almeno un?aloidrina polifunzionale e un agente vulcanizzante. Preferably, said at least one epoxy resin ? obtained from the condensation reaction of at least one polyhydric phenol with at least one polyfunctional halohydrin and a vulcanizing agent.
Preferibilmente detto almeno un fenolo poliidrico ? scelto tra Bisfenolo A, Bisfenolo AF, o una loro combinazione. Preferably said at least one polyhydric phenol ? selected from Bisphenol A, Bisphenol AF, or a combination thereof.
Preferibilmente detta almeno un?aloidrina polifunzionale ? scelta nel gruppo costituito da: epicloroidrina, glicerolo dicloidrina o una loro combinazione. Preferably called at least one polyfunctional halohydrin? chosen from the group consisting of: epichlorohydrin, glycerol dichlorohydrin or a combination thereof.
Preferibilmente detto agente vulcanizzate ? scelto tra: Preferably said vulcanizing agent ? chosen between:
- almeno una poliammina alifatica preferibilmente scelta nel gruppo costituito da: dietilammina, dietilenetriammina, metaxililendiammina, 2-piperazin-1-iletilammina o una loro combinazione - at least one aliphatic polyamine preferably selected from the group consisting of: diethylamine, diethylenetriamine, metaxylylenediamine, 2-piperazine-1-ylethylamine or a combination thereof
oppure or
- una miscela di detta almeno una poliammina alifatica con almeno un acido organico, preferibilmente scelto nel gruppo costituito da: acido salicilico, acido benzoico, acido lattico, o una loro combinazione. - a mixture of said at least one aliphatic polyamine with at least one organic acid, preferably selected from the group consisting of: salicylic acid, benzoic acid, lactic acid, or a combination thereof.
Preferibilmente detta almeno una resina epossidica ? scelta nel gruppo costituito da: 2,2-bis-(4-idrossifenil) propano, diepossibutadiene, bis (2,3-epossi-2-metilpropile), o una loro combinazione. Preferably said at least one epoxy resin ? selected from the group consisting of: 2,2-bis-(4-hydroxyphenyl) propane, diepoxybutadiene, bis (2,3-epoxy-2-methylpropyl), or a combination thereof.
Secondo una forma di realizzazione dell?invenzione, detta almeno una resina epossidica ? preferibilmente caratterizzata dall?avere un numero di gruppi epossidici terminali in eccesso rispetto al numero di gruppi idrossilici primari terminali. According to an embodiment of the invention, called at least one epoxy resin ? preferably characterized by having a number of terminal epoxy groups in excess of the number of terminal primary hydroxyl groups.
Preferibilmente, detta almeno una resina poliammidica ? scelta nel gruppo costituito da: prodotti di addizione di poliammine alifatiche con silani, prodotti di reazione di acidi grassi polimerici con etilendiammina e/o dietilentriammina, N-etilendiammina, dietilenetriamina, trietilentetrammina, N- (idrossietil) dietilenetriammina, 1,4-fenilendiammina, o una loro combinazione. Preferably, said at least one polyamide resin ? selected from the group consisting of: addition products of aliphatic polyamines with silanes, reaction products of polymeric fatty acids with ethylenediamine and/or diethylenetriamine, N-ethylenediamine, diethylenetriamine, triethylenetetramine, N- (hydroxyethyl) diethylenetriamine, 1,4-phenylenediamine, or a combination thereof.
Secondo una forma di realizzazione dell?invenzione, detta almeno una resina poliammidica ? preferibilmente caratterizzata dall?avere una quantit? di gruppi amminici liberi in eccesso rispetto ai gruppi carbossilici. Vantaggiosamente, secondo tale forma di realizzazione, ? possibile ottenere un avanzamento della reazione di polimerizzazione tra l?almeno una resina epossidica e l?almeno una resina poliammidica con relativa formazione ed indurimento del materiale polimerico e formazione del materiale composito, indurito, in tempi relativamente rapidi, ovvero in tempi compresi tra 35 ed 50 minuti a temperature di esercizio comprese tra 20 e 35?C, e in tempi compresi tra 50 e 90 minuti per temperature di esercizio comprese tra 5 e 20?C. According to an embodiment of the invention, said at least one polyamide resin ? preferably characterized by? having a quantity? of free amino groups in excess of the carboxyl groups. Advantageously, according to this embodiment, ? it is possible to obtain an advancement of the polymerization reaction between the at least one epoxy resin and the at least one polyamide resin with relative formation and hardening of the polymeric material and formation of the composite material, hardened, in relatively rapid times, i.e. in times between 35 and 50 minutes at operating temperatures between 20 and 35?C, and in times between 50 and 90 minutes for operating temperatures between 5 and 20?C.
Secondo una forma di realizzazione alternativa dell?invenzione, detta almeno una resina poliammidica ? preferibilmente caratterizzata dall?avere una quantit? di gruppi carbossilici liberi in eccesso rispetto ai gruppi amminici. According to an alternative embodiment of the invention, called at least one polyamide resin ? preferably characterized by? having a quantity? of free carboxyl groups in excess of the amino groups.
Vantaggiosamente, secondo tale forma di realizzazione, ? possibile ottenere un avanzamento della reazione di polimerizzazione tra l?almeno una resina epossidica e l?almeno una resina poliammidica con relativa formazione ed indurimento del materiale polimerico e formazione del materiale composito, indurito, in tempi relativamente lenti, ovvero in tempi compresi tra 60 e 90 minuti a temperature di esercizio comprese tra 20 e 35 ?C, e in tempi compresi tra 90 e 240 minuti a temperature di esercizio comprese tra 5 e 20 ?C . Advantageously, according to this embodiment, ? it is possible to obtain an advancement of the polymerization reaction between the at least one epoxy resin and the at least one polyamide resin with relative formation and hardening of the polymeric material and formation of the composite material, hardened, in relatively slow times, i.e. in times between 60 and 90 minutes at operating temperatures between 20 and 35 ?C, and for times between 90 and 240 minutes at operating temperatures between 5 and 20 ?C .
Secondo una forma di realizzazione dell?invenzione, il materiale a base di sughero ? scelto nel gruppo costituito da: sughero naturale, sughero di riciclo, preferibilmente derivato da sughero di scarto e/o sughero rigenerato, sughero agglomerato con un materiale polimerico, ad esempio agglomerato con una resina poliuretanica, e una loro combinazione. According to one embodiment of the invention, the cork-based material is selected from the group consisting of: natural cork, recycled cork, preferably derived from waste cork and/or regenerated cork, cork agglomerated with a polymeric material, for example agglomerated with a polyurethane resin, and a combination thereof.
Secondo una forma di realizzazione particolarmente preferita dell?invenzione, il materiale a base di sughero ? in forma di materiale sminuzzato scelto tra granuli, scaglie, polvere, preferibilmente polvere particellare, e una loro combinazione. According to a particularly preferred embodiment of the invention, the cork-based material is in the form of comminuted material selected from granules, flakes, powder, preferably particulate powder, and a combination thereof.
Preferibilmente, detto materiale a base di sughero in forma di materiale sminuzzato ha una dimensione caratteristica compresa tra 1 e 10 mm, preferibilmente tra 1 e 7 mm, pi? preferibilmente tra 1 e 3, ancora pi? preferibilmente tra 5 e 7 mm. Preferably, said cork-based material in the form of shredded material has a characteristic size of between 1 and 10 mm, preferably between 1 and 7 mm, more preferably between 1 and 3, even more? preferably between 5 and 7 mm.
Nella forma di realizzazione in cui detto materiale a base di sughero ? in forma di granuli o polvere, per dimensione caratteristica si intende il diametro medio. In the embodiment wherein said cork-based material is in the form of granules or powder, the characteristic dimension refers to the average diameter.
Nella forma di realizzazione in cui detto materiale a base di sughero ? in forma di scaglie, per dimensione caratteristica si intende il lato pi? lungo (o base maggiore). In the embodiment wherein said cork-based material is in the form of flakes, the characteristic dimension means the side pi? long (or major base).
Secondo una forma di realizzazione dell?invenzione, detto materiale composito pu? ulteriormente comprendere almeno un additivo scelto nel gruppo costituito da: un pigmento, un diluente, un estensore, un plastificante, o una loro combinazione. According to an embodiment of the invention, said composite material can further comprising at least one additive selected from the group consisting of: a pigment, a diluent, an extender, a plasticizer, or a combination thereof.
Preferibilmente, detto pigmento ? scelto tra un pigmento in polvere e/o un pigmento liquido. Preferably, said pigment ? chosen between a powder pigment and/or a liquid pigment.
Pi? preferibilmente, detto pigmento in polvere ? scelto nel gruppo costituito da: ossido di ferro, biossido di titanio, carbon black, ossido di manganese, ossido di cromo, o una loro combinazione. Pi? preferably, said pigment powder ? selected from the group consisting of: iron oxide, titanium dioxide, carbon black, manganese oxide, chromium oxide, or a combination thereof.
Pi? preferibilmente, detto pigmento liquido ? scelto nel gruppo costituito da: una pasta colorante a base epossidica, una pasta colorante a base poliestere esente stirene, o una loro combinazione. Pi? preferably, said liquid pigment ? selected from the group consisting of: an epoxy-based coloring paste, a styrene-free polyester-based coloring paste, or a combination thereof.
Preferibilmente, detto diluente ? scelto nel gruppo costituito da: alcool etilico denaturato, etanolo, propilene glicole monometil etere acetato o una loro combinazione. Preferably, said thinner ? selected from the group consisting of: denatured ethyl alcohol, ethanol, propylene glycol monomethyl ether acetate, or a combination thereof.
Preferibilmente, detto estensore ? scelto nel gruppo costituito da: acetato di 1-metil-2-metossietile, dimetilftalato, difenilftalato, o una loro combinazione. Preferably, said extender ? selected from the group consisting of: 1-methyl-2-methoxyethyl acetate, dimethyl phthalate, diphenyl phthalate, or a combination thereof.
Preferibilmente, detto plastificante ? scelto nel gruppo costituito da: una resina elastomerica, una silice reattiva, preferibilmente una silice colloidale micronizzata, o una loro combinazione. Preferably, said plasticizer ? selected from the group consisting of: an elastomeric resin, a reactive silica, preferably a micronized colloidal silica, or a combination thereof.
Secondo una forma di realizzazione particolarmente preferita dell?invenzione, detto materiale a base di sughero e detto materiale polimerico sono intimamente miscelati. Ai fini della presente invenzione, l?espressione ?intimamente miscelato? ? da intendersi riferita ad una forma di realizzazione in cui il materiale a base di sughero ? disperso ed incorporato all?interno del materiale polimerico a formare un materiale composito in cui non ? possibile discernere fasi e/o strati discreti e/o separati. Preferibilmente, secondo detta forma di realizzazione, detto materiale a base di sughero e detto materiale polimerico, intimamente miscelati, sono presenti all?interno del materiale composito in una quantit? compresa tra 5 e 2000 parti in peso di materiale polimerico per 100 parti in peso di materiale a base di sughero, preferibilmente compresa tra 50 e 2000 parti in peso di materiale polimerico per 100 parti in peso di materiale a base di sughero, pi? preferibilmente tra 100 e 1000 parti in peso di materiale polimerico per 100 parti in peso di materiale a base di sughero, ancora pi? preferibilmente tra 50 e 700 parti in peso di materiale polimerico per 100 parti in peso di materiale a base di sughero. According to a particularly preferred embodiment of the invention, said cork-based material and said polymeric material are intimately mixed. For the purposes of the present invention, the expression ?intimately blended? ? to be understood as referring to an embodiment in which the cork-based material? dispersed and incorporated within the polymeric material to form a composite material in which it is not possible to discern discrete and/or separate phases and/or layers. Preferably, according to said embodiment, said cork-based material and said polymeric material, intimately mixed, are present within the composite material in a quantity between 5 and 2000 parts by weight of polymeric material per 100 parts by weight of cork-based material, preferably between 50 and 2000 parts by weight of polymeric material per 100 parts by weight of cork-based material, plus? preferably between 100 and 1000 parts by weight of polymeric material per 100 parts by weight of cork-based material, even more? preferably between 50 and 700 parts by weight of polymeric material per 100 parts by weight of cork-based material.
Secondo un?altra forma di realizzazione, il materiale composito dell?invenzione comprende almeno due strati discreti in cui un primo strato ? realizzato con detto materiale a base di sughero e in cui un secondo strato ? realizzato con detto materiale polimerico. According to another embodiment, the composite material of the invention comprises at least two discrete layers in which a first layer is made with said cork-based material and in which a second layer? made with said polymeric material.
Ai fini della presente invenzione, l?espressione ?strati discreti? ? da intendersi riferita ad una forma di realizzazione in cui il materiale a base di sughero e il materiale polimerico formano un materiale composito in cui ? possibile discernere fasi e/o strati discreti separati ma adesi. For the purposes of the present invention, the expression ?discrete layers? ? to be understood as referring to an embodiment in which the cork-based material and the polymeric material form a composite material in which ? It is possible to discern separate but adherent discrete phases and/or layers.
Ai fini della presente invenzione, detto materiale composito secondo una tale forma di realizzazione pu? essere definito anche come ?bistrato?. For the purposes of the present invention, said composite material according to such an embodiment can also be defined as a ?bilayer?.
Preferibilmente, detto primo strato ? realizzato con detto materiale a base di sughero in forma di materiale sminuzzato, preferibilmente scelto tra granuli, scaglie polvere, preferibilmente polvere particellare, e una loro combinazione. Ancora pi? preferibilmente, detto primo stratto ? realizzato con detto materiale a base di sughero in forma di materiale sminuzzato pressato. Preferably, said first layer ? made with said cork-based material in the form of shredded material, preferably selected from granules, flakes, powder, preferably particulate powder, and a combination thereof. even more preferably, said first layer ? made with said cork-based material in the form of a pressed shredded material.
Vantaggiosamente, detta forma di realizzazione permette di ottenere, in un modo particolarmente efficace, due strati discreti, ovvero un primo strato compatto sopra il quale posizionare un secondo strato realizzato con detto materiale polimerico. Advantageously, said embodiment allows to obtain, in a particularly effective way, two discrete layers, ie a first compact layer over which to position a second layer made with said polymeric material.
Inoltre, senza volersi legare ad una specifica teoria, la Richiedente ha tuttavia trovato come, data la natura porosa di detto materiale a base di sughero, preferibilmente in forma di materiale sminuzzato, ancora pi? preferibilmente in forma di materiale sminuzzato pressato, e la natura di detto materiale polimerico, sia possibile avere un?adesione tra detti due strati discreti senza necessit? di utilizzare un legante, evitando cos? ad esempio la presenza di uno strato intermedio adesivo. Furthermore, without wanting to be bound by a specific theory, the Applicant has however found that, given the porous nature of said cork-based material, preferably in the form of chopped material, even more? preferably in the form of pressed comminuted material, and the nature of said polymeric material, it is possible to have an adhesion between said two discrete layers without the need for? to use a binder, thus avoiding? for example the presence of an intermediate adhesive layer.
Preferibilmente secondo tale forma di realizzazione, il materiale composito ?bistrato?, ha uno spessore compreso tra 0,1 e 500 mm, preferibilmente tra 1 e 100 mm. Preferably according to this embodiment, the "two-layer" composite material has a thickness of between 0.1 and 500 mm, preferably between 1 and 100 mm.
Forma ulteriore oggetto della presente invenzione anche un processo per l?ottenimento del materiale composito come precedentemente descritto. Secondo una forma di realizzazione particolarmente preferita, il processo secondo la presente invenzione ? un processo per l?ottenimento del materiale composito in cui detto materiale a base di sughero e detto materiale polimerico sono intimamente miscelati. Detto processo comprende i passaggi di: A further object of the present invention is also a process for obtaining the composite material as previously described. According to a particularly preferred embodiment, the process according to the present invention ? a process for obtaining the composite material in which said cork-based material and said polymeric material are intimately mixed. This process includes the steps of:
i) miscelare almeno una resina epossidica e almeno una resina poliammidica in un rapporto in peso resina epossidica:resina poliammidica compreso tra 10:90 e 70:30, preferibilmente compreso tra 80:20 e 30:70; ii) mescolare intimamente la miscela di resine ottenuta al passaggio i) con un materiale a base di sughero, preferibilmente in una quantit? compresa tra 5 e 2000 parti in peso di detta miscela di resine per 100 parti in peso di detto materiale a base di sughero; i) mixing at least one epoxy resin and at least one polyamide resin in an epoxy resin:polyamide resin weight ratio comprised between 10:90 and 70:30, preferably comprised between 80:20 and 30:70; ii) intimately mixing the mixture of resins obtained in step i) with a cork-based material, preferably in a quantity comprised between 5 and 2000 parts by weight of said mixture of resins per 100 parts by weight of said cork-based material;
iii) attendere l?avanzamento della reazione di polimerizzazione tra l?almeno una resina epossidica e l?almeno una resina poliammidica, preferibilmente mantenendo condizioni di temperatura e pressione costanti, fino all?ottenimento di un materiale composito indurito comprendente il materiale a base di sughero e il materiale polimerico ottenuto dalla reazione dell?almeno una resina epossidica con l?almeno una resina poliammidica. iii) waiting for the polymerization reaction to progress between the at least one epoxy resin and the at least one polyamide resin, preferably maintaining constant temperature and pressure conditions, until a hardened composite material is obtained comprising the cork-based material and the polymeric material obtained from the reaction of the at least one epoxy resin with the at least one polyamide resin.
Preferibilmente, detta almeno una resina epossidica e detta almeno una resina poliammidica sono come precedentemente descritte. Preferably, said at least one epoxy resin and said at least one polyamide resin are as previously described.
Preferibilmente, detto materiale a base di sughero ? come precedentemente descritto ovvero scelto nel gruppo costituito da: sughero naturale, sughero di riciclo, preferibilmente derivato da sughero di scarto e/o sughero rigenerato, sughero agglomerato con polimeri, ad esempio agglomerato con una resina poliuretanica, e una loro combinazione. Preferably, said cork-based material ? as previously described or selected from the group consisting of: natural cork, recycled cork, preferably derived from waste cork and/or regenerated cork, cork agglomerated with polymers, for example agglomerated with a polyurethane resin, and a combination thereof.
Preferibilmente, detto materiale a base di sughero ? in forma di materiale sminuzzato, preferibilmente scelto tra granuli, scaglie, polvere e una loro combinazione. Pi? preferibilmente detto materiale a base di sughero ha una dimensione caratteristica compresa tra 1 e 10 mm, preferibilmente tra 1 e 7 mm, pi? preferibilmente tra 1 e 3 mm, ancora pi? preferibilmente tra 5 e 7 mm. Preferably, said cork-based material ? in the form of comminuted material, preferably selected from granules, flakes, powder and a combination thereof. Pi? preferably said cork-based material has a characteristic dimension between 1 and 10 mm, preferably between 1 and 7 mm, more? preferably between 1 and 3 mm, even more? preferably between 5 and 7 mm.
Nella forma di realizzazione in cui detto materiale a base di sughero ? in forma di granuli o polvere, per dimensione caratteristica si intende il diametro medio. In the embodiment wherein said cork-based material is in the form of granules or powder, the characteristic dimension refers to the average diameter.
Nella forma di realizzazione in cui detto materiale a base di sughero ? in forma di scaglie, per dimensione caratteristica si intende il lato pi? lungo (o base maggiore). In the embodiment wherein said cork-based material is in the form of flakes, the characteristic dimension means the side pi? long (or major base).
Preferibilmente la miscela di resine ottenuta al passaggio i) ? una miscela in cui dette resine sono liquide a temperatura e pressione ambiente in modo da risultare in una pi? efficace e vantaggiosa miscelazione intima nel passaggio ii) tra detta miscela di resine e il materiale a base di sughero. Preferably the mixture of resins obtained in step i)? a mixture in which said resins are liquid at room temperature and pressure so as to result in a more? effective and advantageous intimate mixing in step ii) between said mixture of resins and the cork-based material.
Ancora pi? preferibilmente la miscela di resine ottenuta al passaggio i) ha una viscosit?, misurata a temperatura e pressione ambiente, inferiore a 7000 Cps, pi? preferibilmente compresa tra 100 e 2000 Cps ed ancora pi? preferibilmente tra 100 e 400 Cps. even more preferably the mixture of resins obtained in step i) has a viscosity, measured at ambient temperature and pressure, lower than 7000 Cps, more? preferably between 100 and 2000 Cps and even more? preferably between 100 and 400 Cps.
Preferibilmente, al passaggio ii), la miscela di resine ottenuta al passaggio i) e il materiale a base di sughero sono intimamente miscelati in una quantit? compresa tra 50 e 2000 parti in peso di detta miscela di resine per 100 parti in peso di detto materiale a base di sughero, pi? preferibilmente tra 100 e 1000 parti in peso di detta miscela di resine per 100 parti in peso di detto materiale a base di sughero, ancora pi? preferibilmente tra 50 e 700 parti in peso di detta miscela di resine per 100 parti in peso di detto materiale a base di sughero. Preferably, in step ii), the mixture of resins obtained in step i) and the cork-based material are intimately mixed in a quantity between 50 and 2000 parts by weight of said mixture of resins per 100 parts by weight of said cork-based material, plus? preferably between 100 and 1000 parts by weight of said mixture of resins per 100 parts by weight of said cork-based material, even more? preferably between 50 and 700 parts by weight of said resin mixture per 100 parts by weight of said cork-based material.
Secondo una forma di realizzazione della presente invenzione, nel passaggio ii) di mescolare intimamente la miscela di resine ottenuta al passaggio i) con un materiale a base di sughero, ? possibile aggiungere almeno un additivo scelto nel gruppo costituito da: un pigmento, un diluente, un estensore, un plastificante, o una loro combinazione. According to an embodiment of the present invention, in step ii) of intimately mixing the mixture of resins obtained in step i) with a cork-based material,? It is possible to add at least one additive selected from the group consisting of: a pigment, a diluent, an extender, a plasticizer, or a combination thereof.
Preferibilmente detto almeno un additivo ? aggiunto direttamente a detta miscela di resine ottenuta al passaggio i) prima della miscelazione intima con il materiale a base di sughero. Preferably said at least one additive ? added directly to said mixture of resins obtained in step i) before intimate mixing with the cork-based material.
Preferibilmente, detto pigmento, diluente, estensore e plastificante sono come precedentemente descritti. Preferably, said pigment, diluent, extender and plasticizer are as previously described.
Secondo una forma di realizzazione preferita dell?invenzione, il processo per l?ottenimento del materiale composito in cui detto materiale a base di sughero e detto materiale polimerico sono intimamente miscelati comprende, prima del passaggio iii), un passaggio di disporre la miscela ottenuta al passaggio ii) in uno stampo, preferibilmente uno stampo sovradimensionato aperto o chiuso. According to a preferred embodiment of the invention, the process for obtaining the composite material in which said cork-based material and said polymeric material are intimately mixed comprises, before step iii), a step of arranging the mixture obtained in the step ii) in a mold, preferably an open or closed oversized mold.
Secondo una forma di realizzazione alternativa dell?invenzione, la miscela ottenuta al passaggio ii) pu? essere lavorata e formata con un qualsiasi mezzo adatto, ad esempio mediante lavorazione a mano. According to an alternative embodiment of the invention, the mixture obtained in step ii) can be worked and formed by any suitable means, for example by handwork.
Preferibilmente, il materiale composito ottenuto/ottenibile mediante il processo secondo la presente descrizione, comprendente i passaggi i)-iii) come precedentemente descritti, presenta un grado di espansione compreso tra il 50 e il 400%, preferibilmente tra il 50 e il 100%. Preferably, the composite material obtained/obtainable by the process according to the present description, comprising steps i)-iii) as previously described, has an expansion degree between 50 and 400%, preferably between 50 and 100%. .
Secondo una forma di realizzazione preferita dell?invenzione, il passaggio iii) di attendere l?avanzamento della reazione di polimerizzazione tra l?almeno una resina epossidica e l?almeno una resina poliammidica ? effettuato a temperatura ambiente, preferibilmente mantenendo tale temperatura costante, pi? preferibilmente per un periodo di tempo compreso tra 2 e 10 ore, pi? preferibilmente tra 3 e 5 ore (preferibilmente nel caso di temperatura compresa tra 5 e 18 ?C), ancora pi? preferibilmente per un periodo di tempo compreso tra 2 e 3 ore (preferibilmente nel caso di temperatura superiore a 18 ?C). According to a preferred embodiment of the invention, step iii) of waiting for the polymerization reaction to progress between the at least one epoxy resin and the at least one polyamide resin ? performed at room temperature, preferably maintaining this constant temperature, pi? preferably for a period of time between 2 and 10 hours, plus? preferably between 3 and 5 hours (preferably in the case of a temperature between 5 and 18?C), even more? preferably for a period of time comprised between 2 and 3 hours (preferably in the case of a temperature higher than 18°C).
In una forma di realizzazione dell?invenzione, il passaggio iii) viene effettuato ad una temperatura superiore alla temperatura ambiente, preferibilmente applicando una temperatura compresa tra 30 e 50 ?C, pi? preferibilmente tra 40 e 50 ?C. Preferibilmente, secondo una tale forma di realizzazione, una tale temperatura superiore alla temperatura ambiente, preferibilmente compresa tra 30 e 50 ?C, pi? preferibilmente tra 40 e 50 ?C, viene applicata in modo costante e/o uniforme su tutta la massa del materiale composito. In one embodiment of the invention, step iii) is carried out at a temperature higher than room temperature, preferably by applying a temperature between 30 and 50 ?C, plus? preferably between 40 and 50 ?C. Preferably, according to such an embodiment, such a temperature higher than the ambient temperature, preferably between 30 and 50°C, more? preferably between 40 and 50°C, it is applied in a constant and/or uniform manner over the whole mass of the composite material.
Preferibilmente detto passaggio iii), altres? detto ?indurimento?, viene effettuato inserendo la miscela ottenuta al passaggio ii) in un forno, preferibilmente statico, ad una temperatura costante nell?intervallo 30-50 ?C, preferibilmente 40-50 ?C. Preferably said step iii), also? said ?hardening?, is carried out by inserting the mixture obtained in step ii) into an oven, preferably static, at a constant temperature in the range of 30-50 ?C, preferably 40-50 ?C.
Preferibilmente, detto passaggio iii) ? effettuato in condizioni di pressione costante, preferibilmente in condizioni di pressione ambiente, pi? preferibilmente applicando una pressione compresa tra 20 e 100 Kg/m<2>, preferibilmente tra 20 e 60 Kg/m<2>, ancora pi? preferibilmente tra 40 e 60 Kg/m<2>, detta pressione essendo preferibilmente applicata in modo costante e/o uniforme su tutta la massa del materiale composito. Preferably, said step iii) ? carried out in conditions of constant pressure, preferably in conditions of ambient pressure, more? preferably applying a pressure between 20 and 100 Kg/m<2>, preferably between 20 and 60 Kg/m<2>, even more? preferably between 40 and 60 Kg/m<2>, said pressure being preferably applied in a constant and/or uniform manner over the whole mass of the composite material.
Secondo una forma di realizzazione alternativa, il processo secondo la presente invenzione ? un processo per l?ottenimento del materiale composito comprendente almeno due strati discreti in cui un primo strato ? realizzato con un materiale a base di sughero e in cui un secondo strato ? realizzato con un materiale polimerico. According to an alternative embodiment, the process according to the present invention ? a process for obtaining the composite material comprising at least two discrete layers in which a first layer ? made with a cork-based material and in which a second layer is made with a polymeric material.
Detto processo comprende i passaggi di: This process includes the steps of:
i) miscelare almeno una resina epossidica e almeno una resina poliammidica in un rapporto in peso resina epossidica:resina poliammidica compreso tra 10:90 e 70:30, preferibilmente compreso tra 80:20 e 30:70; i) mixing at least one epoxy resin and at least one polyamide resin in an epoxy resin:polyamide resin weight ratio comprised between 10:90 and 70:30, preferably comprised between 80:20 and 30:70;
iia) colare la miscela di resine ottenuta al passaggio i) su uno strato realizzato con un materiale a base di sughero, preferibilmente detto materiale a base di sughero essendo disposto in uno stampo, preferibilmente uno stampo sovradimensionato aperto o chiuso, pi? preferibilmente detto materiale a base di sughero essendo pressato in detto stampo; iia) pouring the mixture of resins obtained in step i) onto a layer made of a cork-based material, preferably said cork-based material being arranged in a mould, preferably an open or closed oversized mould, more preferably said cork-based material being pressed into said mold;
iii) attendere l?avanzamento della reazione di polimerizzazione tra l?almeno una resina epossidica e l?almeno una resina poliammidica, preferibilmente mantenendo condizioni di temperatura e pressione costanti, fino all?ottenimento di un materiale composito indurito comprendente il materiale a base di sughero e il materiale polimerico ottenuto dalla reazione dell?almeno una resina epossidica con l?almeno una resina poliammidica. iii) waiting for the polymerization reaction to progress between the at least one epoxy resin and the at least one polyamide resin, preferably maintaining constant temperature and pressure conditions, until a hardened composite material is obtained comprising the cork-based material and the polymeric material obtained from the reaction of the at least one epoxy resin with the at least one polyamide resin.
Preferibilmente, detta almeno una resina epossidica e detta almeno una resina poliammidica sono come precedentemente descritte. Preferably, said at least one epoxy resin and said at least one polyamide resin are as previously described.
Preferibilmente, il passaggio i) ? come precedentemente descritto. Preferably, step i) ? as previously described.
Preferibilmente la miscela di resine ottenuta al passaggio i) ? una miscela in cui dette resine sono liquide a temperatura e pressione ambiente in modo da risultare in una pi? efficace e vantaggiosa colatura nel passaggio ii) di detta miscela di resine sullo strato realizzato con un materiale a base di sughero. Preferably the mixture of resins obtained in step i)? a mixture in which said resins are liquid at room temperature and pressure so as to result in a more? effective and advantageous pouring in step ii) of said mixture of resins on the layer made with a cork-based material.
Preferibilmente, nel passaggio iia) di colare la miscela di resine ottenuta al passaggio i) su uno strato realizzato con un materiale a base di sughero, ? possibile aggiungere almeno un additivo scelto nel gruppo costituito da: un pigmento, un diluente, un estensore, un plastificante, o una loro combinazione. Preferably, in step iia) to pour the mixture of resins obtained in step i) on a layer made with a cork-based material,? It is possible to add at least one additive selected from the group consisting of: a pigment, a diluent, an extender, a plasticizer, or a combination thereof.
Preferibilmente detto almeno un additivo ? aggiunto direttamente a detta miscela di resine ottenuta al passaggio i) prima della colatura su detto strato realizzato con un materiale a base di sughero. Preferably said at least one additive ? added directly to said mixture of resins obtained in step i) before pouring onto said layer made with a cork-based material.
Preferibilmente, detto pigmento, diluente, estensore e plastificante sono come precedentemente descritti. Preferably, said pigment, diluent, extender and plasticizer are as previously described.
Preferibilmente, al passaggio iia) detto strato ? realizzato con detto materiale a base di sughero in forma di materiale sminuzzato, preferibilmente scelto tra granuli, scaglie polvere, preferibilmente polvere particellare, e una loro combinazione. Ancora pi? preferibilmente, detto strato ? realizzato con detto materiale a base di sughero in forma di materiale sminuzzato pressato. Preferably, in step iia) said layer ? made with said cork-based material in the form of shredded material, preferably selected from granules, flakes, powder, preferably particulate powder, and a combination thereof. even more preferably, said layer ? made with said cork-based material in the form of a pressed shredded material.
Preferibilmente, detto materiale a base di sughero ? come precedentemente descritto ovvero scelto nel gruppo costituito da: sughero naturale, sughero di riciclo, preferibilmente derivato da sughero di scarto e/o sughero rigenerato, sughero agglomerato con polimeri, ad esempio agglomerato con una resina poliuretanica, e una loro combinazione. Preferably, said cork-based material ? as previously described or selected from the group consisting of: natural cork, recycled cork, preferably derived from waste cork and/or regenerated cork, cork agglomerated with polymers, for example agglomerated with a polyurethane resin, and a combination thereof.
Preferibilmente, detto materiale a base di sughero ? in forma di materiale sminuzzato, preferibilmente scelto tra granuli, scaglie, polvere e una loro combinazione. Pi? preferibilmente detto materiale a base di sughero ha una dimensione caratteristica compresa tra 1 e 10 mm, preferibilmente tra 1 e 7 mm, pi? preferibilmente tra 1 e 3 mm, ancora pi? preferibilmente tra 5 e 7 mm. Preferably, said cork-based material ? in the form of comminuted material, preferably selected from granules, flakes, powder and a combination thereof. Pi? preferably said cork-based material has a characteristic dimension between 1 and 10 mm, preferably between 1 and 7 mm, more? preferably between 1 and 3 mm, even more? preferably between 5 and 7 mm.
Nella forma di realizzazione in cui detto materiale a base di sughero ? in forma di granuli o polvere, per dimensione caratteristica si intende il diametro medio. In the embodiment wherein said cork-based material is in the form of granules or powder, the characteristic dimension refers to the average diameter.
Nella forma di realizzazione in cui detto materiale a base di sughero ? in forma di scaglie, per dimensione caratteristica si intende il lato pi? lungo (o base maggiore). In the embodiment wherein said cork-based material is in the form of flakes, the characteristic dimension means the side pi? long (or major base).
Secondo una forma di realizzazione preferita dell?invenzione, il passaggio iii) di attendere l?avanzamento della reazione di polimerizzazione tra l?almeno una resina epossidica e l?almeno una resina poliammidica ? come precedentemente descritto, ovvero viene effettuato a temperatura ambiente, preferibilmente mantenendo tale temperatura costante, pi? preferibilmente per un periodo di tempo compreso tra 2 e 10 ore, pi? preferibilmente tra 3 e 5 ore (preferibilmente nel caso di temperatura compresa tra 5 e 18 ?C), ancora pi? preferibilmente per un periodo di tempo compreso tra 2 e 3 ore (preferibilmente nel caso di temperatura superiore a 18 ?C). According to a preferred embodiment of the invention, step iii) of waiting for the polymerization reaction to progress between the at least one epoxy resin and the at least one polyamide resin ? as previously described, or is it carried out at room temperature, preferably keeping this temperature constant, more? preferably for a period of time between 2 and 10 hours, plus? preferably between 3 and 5 hours (preferably in the case of a temperature between 5 and 18?C), even more? preferably for a period of time comprised between 2 and 3 hours (preferably in the case of a temperature higher than 18°C).
In una forma di realizzazione dell?invenzione, al passaggio iii) viene effettuato ad una temperatura superiore alla temperatura ambiente preferibilmente applicando una temperatura compresa tra 30 e 50 ?C, pi? preferibilmente tra 40 e 50 ?C. Preferibilmente, secondo una tale forma di realizzazione, una tale temperatura superiore alla temperatura ambiente, preferibilmente compresa tra 30 e 50 ?C, pi? preferibilmente tra 40 e 50 ?C, viene applicata in modo costante e/o uniforme su tutta la massa del materiale composito. In one embodiment of the invention, step iii) is carried out at a temperature higher than room temperature, preferably by applying a temperature between 30 and 50 ?C, plus? preferably between 40 and 50 ?C. Preferably, according to such an embodiment, such a temperature higher than the ambient temperature, preferably between 30 and 50°C, more? preferably between 40 and 50°C, it is applied in a constant and/or uniform manner over the whole mass of the composite material.
Preferibilmente detto passaggio iii), altres? detto ?indurimento?, viene effettuato inserendo lo strato realizzato con il materiale a base di sughero su cui ? stata colata la miscela di resine come descritto al passaggio ii), in un forno, preferibilmente statico, ad una temperatura costante nell?intervallo 30-50 ?C, preferibilmente 40-50 ?C. Preferably said step iii), also? called ?hardening?, is carried out by inserting the layer made with the cork-based material on which ? the resin mixture was poured as described in step ii), in an oven, preferably static, at a constant temperature in the range of 30-50°C, preferably 40-50°C.
Preferibilmente, detto passaggio iii) ? effettuato in condizioni di pressione costante, preferibilmente in condizioni di pressione ambiente, pi? preferibilmente applicando una pressione compresa tra 20 e 100 Kg/m<2>, preferibilmente tra 20 e 60 Kg/m<2>, ancora pi? preferibilmente tra 40 e 60 Kg/m<2>, detta pressione essendo preferibilmente applicata in modo costante e/o uniforme su tutta la massa del materiale composito. Preferably, said step iii) ? carried out in conditions of constant pressure, preferably in conditions of ambient pressure, more? preferably applying a pressure between 20 and 100 Kg/m<2>, preferably between 20 and 60 Kg/m<2>, even more? preferably between 40 and 60 Kg/m<2>, said pressure being preferably applied in a constant and/or uniform manner over the whole mass of the composite material.
Secondo tale forma di realizzazione, il materiale composito indurito ottenuto al passaggio iii) comprende un primo strato realizzato con il materiale a base di sughero e un secondo strato realizzato con il materiale polimerico ottenuto dalla reazione dell?almeno una resina epossidica con l?almeno una resina poliammidica, precedentemente colate, sotto forma di miscela, su detto primo strato come descritto nel passaggio ii). According to this embodiment, the hardened composite material obtained in step iii) comprises a first layer made with the cork-based material and a second layer made with the polymeric material obtained from the reaction of the at least one epoxy resin with the at least one polyamide resin, previously cast, in the form of a mixture, on said first layer as described in step ii).
Ai fini della presente invenzione, detto materiale composito secondo una tale forma di realizzazione pu? essere definito anche come ?bistrato?. For the purposes of the present invention, said composite material according to such an embodiment can also be defined as a ?bilayer?.
Senza volersi legare ad una specifica teoria, la Richiedente ha tuttavia trovato che al fine di ottenere il materiale composito preferibilmente avente le caratteristiche desiderate e sopra descritte, che risulti essere efficacemente indurito una volta prodotto e che possa essere utilizzato per la realizzazione di una variet? di manufatti versatili per differenti usi e applicazioni, risulta essere particolarmente vantaggioso che il materiale polimerico ottenuto dalla reazione di almeno una resina epossidica con almeno una resina poliammidica sia caratterizzato dall?avere un rapporto in peso resina epossidica:resina poliammidica compreso tra 10:90 e 70:30, preferibilmente tra compreso tra 80:20 e 30:70. Without wishing to be bound by a specific theory, the Applicant has however found that in order to obtain the composite material preferably having the desired and above-described characteristics, which results to be effectively hardened once produced and which can be used for the realization of a variety of of versatile articles for different uses and applications, it is particularly advantageous that the polymeric material obtained from the reaction of at least one epoxy resin with at least one polyamide resin is characterized by having an epoxy resin:polyamide resin weight ratio between 10:90 and 70:30, preferably between 80:20 and 30:70.
Miscele di resine in cui l?almeno una resina poliammidica ? presente in una quantit? inferiore a 30 parti per 100 parti in peso di materiale polimerico totale non permettono un indurimento efficace del materiale composito secondo la presente invenzione. Analogamente, miscele di resine in cui l?almeno una resina epossidica ? presente in una quantit? inferiore a 10 parti in peso per 100 parti in peso di materiale polimerico totale lasciano una quantit? troppo grande di resina poliammidica non indurita. La Richiedente ha trovato che, a meno che il rapporto in peso delle due resine non sia di circa 50:50 in peso, ci sar? un eccesso dell'una o dell'altra delle due resine. Laddove la resina poliammidica ? in eccesso, l'eccesso funge da plastificante per il materiale a base di sughero e, pertanto, ? spesso desiderabile. Il rapporto preciso delle due resine entro i limiti sopra indicati pu? venire vantaggiosamente selezionato in base al grado di flessibilit? e comprimibilit? desiderato per il materiale composito finale. Entro i limiti indicati, le maggiori quantit? dell?almeno una resina poliammidica producono un materiale composito pi? flessibile e comprimibile. Mixtures of resins in which the at least one polyamide resin ? present in a quantity less than 30 parts per 100 parts by weight of total polymeric material do not allow effective curing of the composite material according to the present invention. Similarly, resin blends in which the at least one epoxy resin is present in a quantity less than 10 parts by weight per 100 parts by weight of total polymeric material leave a quantity? too large amount of uncured polyamide resin. The Applicant has found that, unless the weight ratio of the two resins is about 50:50 by weight, there will be an excess of one or the other of the two resins. Where is the polyamide resin? in excess, the excess acts as a plasticizer for the cork-based material and, therefore, ? often desirable. The precise ratio of the two resins within the above limits can? be advantageously selected on the basis of the degree of flexibility? and compressibility? desired for the final composite material. Within the limits indicated, the largest quantities? of at least one polyamide resin produce a composite material more? flexible and compressible.
La Richiedente ha inoltre trovato che lo specifico rapporto in peso resina epossidica:resina poliammidica compreso tra 10:90 e 70:30, preferibilmente compreso tra 80:20 e 30:70, come sopra descritto risulta essere particolarmente vantaggioso in quanto contribuisce a conferire al materiale composito dell?invenzione un?inaspettata ed efficace resistenza alla proliferazione parassitaria, preferibilmente alla proliferazione di funghi e/o muffe. The Applicant has also found that the specific epoxy resin:polyamide resin weight ratio comprised between 10:90 and 70:30, preferably comprised between 80:20 and 30:70, as described above is particularly advantageous in that it helps to give the composite material of the invention an unexpected and effective resistance to parasitic proliferation, preferably to the proliferation of fungi and/or moulds.
Secondo una forma di realizzazione della presente invenzione, dopo il passaggio iii), il materiale composito indurito ottenuto al passaggio iii) ? sottoposto ad una fase iv) di invecchiamento, ovvero un processo di cura e termoregolazione, a temperature preferibilmente comprese tra 40-300?C, pi? preferibilmente tra 60-80?C, preferibilmente per un periodo di tempo di almeno 24 ore, pi? preferibilmente per un periodo di tempo compreso tra 24 ore e 3 giorni. According to an embodiment of the present invention, after step iii), the cured composite material obtained in step iii) is subjected to a phase iv) of aging, i.e. a process of cure and thermoregulation, at temperatures preferably between 40-300?C, more? preferably between 60-80°C, preferably for a period of time of at least 24 hours, more? preferably for a period of time between 24 hours and 3 days.
La presente invenzione ha per oggetto anche un multistrato comprendente: The present invention also relates to a multilayer comprising:
A) un primo strato realizzato con il materiale composito secondo una qualsiasi delle rivendicazioni precedenti; e A) a first layer made with the composite material according to any one of the preceding claims; And
B) almeno un ulteriore strato realizzato con un materiale scelto nel gruppo costituito da: quarzo intimamente miscelato con un materiale polimerico, fibra di vetro, fibra di carbonio, marmo, acciaio, legno, sughero in forma di una lastra pre-formata. B) at least one further layer made with a material selected from the group consisting of: quartz intimately mixed with a polymeric material, glass fibre, carbon fibre, marble, steel, wood, cork in the form of a pre-formed plate.
Secondo una forma di realizzazione particolarmente preferita, detto primo strato A) ? realizzato con il materiale composito dell?invenzione comprendente il materiale a base di sughero e il materiale polimerico intimamente miscelati, come precedentemente descritto. According to a particularly preferred embodiment, said first layer A) ? made with the composite material of the invention comprising the cork-based material and the polymeric material intimately mixed, as previously described.
Secondo tale forma di realizzazione, il multistrato dell?invenzione comprendente A) e B) ? un multistrato formato da almeno due strati. According to this embodiment, the multilayer of the invention comprising A) and B) ? a multilayer formed by at least two layers.
Secondo una forma di realizzazione alternativa, detto primo strato A) ? realizzato con il materiale composito dell?invenzione ?bistrato? come precedentemente descritto, ovvero comprendente almeno due strati discreti in cui un primo strato ? realizzato con detto materiale a base di sughero e in cui un secondo strato ? realizzato con detto materiale polimerico. According to an alternative embodiment, said first layer A) ? made with the composite material of the invention ?bilayer? as previously described, i.e. comprising at least two discrete layers wherein a first layer ? made with said cork-based material and in which a second layer? made with said polymeric material.
Secondo tale forma di realizzazione, il multistrato dell?invenzione comprendente A) e B) ? un multistrato formato da almeno tre strati. According to this embodiment, the multilayer of the invention comprising A) and B) ? a multilayer formed by at least three layers.
Secondo una forma di realizzazione della presente invenzione, il multistrato comprendente A) e B) come sopra descritti pu? ulteriormente comprendere: According to an embodiment of the present invention, the multilayer comprising A) and B) as described above can further understand:
C) almeno un ulteriore strato realizzato con il materiale composito precedentemente descritto oppure uno strato di sughero in forma di una lastra preformata. C) at least one further layer made with the composite material described above or a layer of cork in the form of a preformed plate.
Secondo una forma di realizzazione particolarmente preferita, A) e C) sono realizzati con il materiale composito dell?invenzione comprendente il materiale a base di sughero e il materiale polimerico intimamente miscelati, come precedentemente descritto. According to a particularly preferred embodiment, A) and C) are made with the composite material of the invention comprising the cork-based material and the polymeric material intimately mixed, as previously described.
Secondo tale forma di realizzazione, il multistrato dell?invenzione comprendente A), B) e C) ? un multistrato formato da almeno tre strati. Secondo una forma di realizzazione alternativa, A) e C) sono realizzati con il materiale composito dell?invenzione ?bistrato? come precedentemente descritto, ovvero comprendente almeno due strati discreti in cui un primo strato ? realizzato con detto materiale a base di sughero e in cui un secondo strato ? realizzato con detto materiale polimerico. According to this embodiment, the multilayer of the invention comprising A), B) and C) ? a multilayer formed by at least three layers. According to an alternative embodiment, A) and C) are made with the composite material of the invention ?bilayer? as previously described, i.e. comprising at least two discrete layers wherein a first layer ? made with said cork-based material and in which a second layer? made with said polymeric material.
Secondo tale forma di realizzazione, il multistrato dell?invenzione comprendente A), B) e C) ? un multistrato formato da almeno cinque strati. Secondo una forma di realizzazione, A) ? realizzato con il materiale composito dell?invenzione comprendente il materiale a base di sughero e il materiale polimerico intimamente miscelati, come precedentemente descritto e C) ? realizzato con il materiale composito dell?invenzione ?bistrato? come precedentemente descritto, ovvero comprendente almeno due strati discreti in cui un primo strato ? realizzato con detto materiale a base di sughero e in cui un secondo strato ? realizzato con detto materiale polimerico. According to this embodiment, the multilayer of the invention comprising A), B) and C) ? a multilayer formed by at least five layers. According to one embodiment, A) ? made with the composite material of the invention comprising the cork-based material and the polymeric material intimately mixed, as previously described and C) ? made with the composite material of the invention ?bilayer? as previously described, i.e. comprising at least two discrete layers wherein a first layer ? made with said cork-based material and in which a second layer? made with said polymeric material.
Secondo tale forma di realizzazione, il multistrato dell?invenzione comprendente A), B) e C) ? un multistrato formato da almeno quattro strati. According to this embodiment, the multilayer of the invention comprising A), B) and C) ? a multilayer formed by at least four layers.
Secondo una forma di realizzazione, A) ? realizzato con il materiale composito dell?invenzione ?bistrato? come precedentemente descritto, ovvero comprendente almeno due strati discreti in cui un primo strato ? realizzato con detto materiale a base di sughero e in cui un secondo strato ? realizzato con detto materiale polimerico e C) ? realizzato con il materiale composito dell?invenzione comprendente il materiale a base di sughero e il materiale polimerico intimamente miscelati, come precedentemente descritto. According to one embodiment, A) ? made with the composite material of the invention ?bilayer? as previously described, i.e. comprising at least two discrete layers wherein a first layer ? made with said cork-based material and in which a second layer? made with said polymeric material and C) ? made with the composite material of the invention comprising the cork-based material and the polymeric material intimately mixed, as previously described.
Secondo tale forma di realizzazione, il multistrato dell?invenzione comprendente A), B) e C) ? un multistrato formato da almeno quattro strati. According to this embodiment, the multilayer of the invention comprising A), B) and C) ? a multilayer formed by at least four layers.
Preferibilmente, il multistrato secondo la presente invenzione ha uno spessore compreso tra 0,1 e 500 mm, preferibilmente tra 1 e 100 e mm. La presente invenzione ha per oggetto anche un manufatto interamente costituito da o comprendente il materiale composito o il multistrato come precedentemente descritti. Preferably, the multilayer according to the present invention has a thickness of between 0.1 and 500 mm, preferably between 1 and 100 mm. The present invention also relates to a product entirely made up of or comprising the composite material or the multilayer as previously described.
Preferibilmente, il manufatto secondo la presente invenzione ? scelto nel gruppo costituto da: un piano di un tavolo, un piano di rivestimento per cucina e/o bagno, un bancone, una scaffalatura, una libreria, una credenza, un?anta di una porta o di una finestra, una spalla portante e non, un fondello, una mensola, un divisorio, una lampada, un elemento di Boiserie, un armadio, una madia, una parete attrezzata, una composizione living, gambe di sedie e tavoli, un elemento di sostegno per il mobilio, una pavimentazione industriale, residenziale, commerciale, nautica o navale, un elemento da esterno, preferibilmente una panca, un vaso, o un gazebo. La presente invenzione riguarda inoltre anche un uso del manufatto come precedentemente descritto come elemento di arredo, di design, di costruzione, di rivestimento di una superficie o una loro combinazione. Preferably, the article according to the present invention ? chosen from the group consisting of: a table top, a kitchen and/or bathroom covering surface, a counter, a shelving unit, a bookcase, a sideboard, a door or window leaf, a load-bearing shoulder and non, a back, a shelf, a divider, a lamp, a Boiserie element, a wardrobe, a sideboard, an equipped wall, a living composition, chair and table legs, a support element for furniture, an industrial flooring , residential, commercial, nautical or naval, an outdoor element, preferably a bench, a vase, or a gazebo. The present invention also relates also to a use of the article as previously described as an element of furniture, design, construction, coating of a surface or a combination thereof.
Claims (15)