IN2014KN02799A - - Google Patents

Info

Publication number
IN2014KN02799A
IN2014KN02799A IN2799KON2014A IN2014KN02799A IN 2014KN02799 A IN2014KN02799 A IN 2014KN02799A IN 2799KON2014 A IN2799KON2014 A IN 2799KON2014A IN 2014KN02799 A IN2014KN02799 A IN 2014KN02799A
Authority
IN
India
Prior art keywords
less
temperature range
temperature
sec
steel pipe
Prior art date
Application number
Inventor
Shunsuke Toyoda
Sota Goto
Takatoshi Okabe
Tomohiro Inoue
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of IN2014KN02799A publication Critical patent/IN2014KN02799A/en

Abstract

A high strength electric resistance welded steel pipe having a yield strength of 450 MPa or more and excellent resistance to softening for a long period in an intermediate temperature range and a method for manufacturing the steel pipe are provided. Specifically, a steel pipe is made using a common method for manufacturing an electric resistance welded steel pipe and made from a hot rolled steel sheet manufactured by heating and soaking a steel material having a chemical composition containing, by mass%, C: 0.026% or more and 0.084% or less, Si: 0.10% or more and 0.30% or less, Mn: 0.70% or more and 1.90% or less, Al: 0.01% or more and 0.10% or less, Nb: 0.001% or more and 0.070% or less, V: 0.001% or more and 0.065% or less, Ti: 0.001% or more and 0.033% or less, Ca: 0.0001% or more and 0.0035% or less, in which the condition that Pcm is 0.20 or less is satisfied, at a temperature of higher than 1200°C and 1280°C or lower for 90 minutes or more, by performing hot rolling under conditions such that the hot rolling reduction in an un- recrystallization temperature range is 20% or more, by cooling the hot rolled steel sheet, in terms of the temperature of a central portion in the thickness direction, down at an average cooling rate of 7°C/sec. or more and 299°C/sec. or less in a temperature range of 780°C to 620°C, by subsequently performing a heat treatment under conditions in which a cumulative holding time in a temperature range of 480°C to 350°C is 2 hours or more and 20 hours or less. Subsequently, an online heat treatment is performed under conditions such that the whole of the wall thickness is heated up to a temperature of 800°C or higher and 1150°C or lower and then cooled, in terms of the temperature of a central portion in the wall thickness direction, at an average cooling rate of 7°C/sec. or more and 299°C/sec. or less in a temperature range of 780°C to 620°C, and further subjected to a treatment in which a cumulative holding time in a temperature range of 500°C to 360°C is 2 seconds or more and 200 seconds or less.
IN2799KON2014 2012-06-28 2013-06-17 IN2014KN02799A (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012145098A JP5516659B2 (en) 2012-06-28 2012-06-28 High-strength ERW pipe excellent in long-term softening resistance in the medium temperature range and its manufacturing method
PCT/JP2013/003764 WO2014002423A1 (en) 2012-06-28 2013-06-17 High-strength electric-resistance-welded steel pipe of excellent long-term softening resistance in intermediate temperature ranges, and method for producing same

Publications (1)

Publication Number Publication Date
IN2014KN02799A true IN2014KN02799A (en) 2015-05-08

Family

ID=49782622

Family Applications (1)

Application Number Title Priority Date Filing Date
IN2799KON2014 IN2014KN02799A (en) 2012-06-28 2013-06-17

Country Status (8)

Country Link
US (1) US9551047B2 (en)
EP (1) EP2868765B1 (en)
JP (1) JP5516659B2 (en)
KR (1) KR101663399B1 (en)
CA (1) CA2877610C (en)
IN (1) IN2014KN02799A (en)
RU (1) RU2618987C2 (en)
WO (1) WO2014002423A1 (en)

Families Citing this family (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104220622B (en) * 2012-04-13 2016-11-02 杰富意钢铁株式会社 There is high-strength thick electric-resistance-welded steel pipe and the manufacture method thereof of excellent low-temperature flexibility
JP5516680B2 (en) * 2012-09-24 2014-06-11 Ｊｆｅスチール株式会社 ERW steel pipe excellent in HIC resistance and low temperature toughness of ERW welded part and method for producing the same
KR20170043662A (en) * 2014-09-25 2017-04-21 제이에프이 스틸 가부시키가이샤 Steel strip for electric-resistance-welded steel pipe or tube, electric-resistance-welded steel pipe or tube, and process for producing steel strip for electric-resistance-welded steel pipe or tube
JP6160587B2 (en) * 2014-10-07 2017-07-12 Ｊｆｅスチール株式会社 Manufacturing method of high-strength ERW steel pipe with excellent creep characteristics in the middle temperature range of ERW welds
JP6394261B2 (en) * 2014-10-14 2018-09-26 新日鐵住金株式会社 ERW steel pipe for oil well and manufacturing method thereof
US10584405B2 (en) 2014-11-27 2020-03-10 Jfe Steel Corporation Electric resistance welded steel pipe and manufacturing method therefor
JP6241569B2 (en) 2015-03-27 2017-12-06 Ｊｆｅスチール株式会社 High strength steel and method for manufacturing the same, steel pipe and method for manufacturing the same
CN105127237A (en) * 2015-09-19 2015-12-09 云南昆钢新型复合材料开发有限公司 Production method of double-metal abrasion-resistant composite pipe
JP6645107B2 (en) * 2015-10-07 2020-02-12 日本製鉄株式会社 H-section steel and manufacturing method thereof
CN109072379B (en) * 2016-07-06 2020-11-06 日本制铁株式会社 Electric resistance welded steel pipe for main line pipe
MX2019002653A (en) 2016-10-03 2019-07-15 Nippon Steel Corp Electric resistance-welded steel pipe for torsion beam.
JP6635232B2 (en) * 2018-01-30 2020-01-22 Ｊｆｅスチール株式会社 Steel material for line pipe, method for manufacturing the same, and method for manufacturing line pipe
KR102164112B1 (en) * 2018-11-29 2020-10-12 주식회사 포스코 High-strength steel sheet having excellent ductility and low-temperature toughness and method for manufacturing thereof
ES2895456T3 (en) * 2018-12-11 2022-02-21 Ssab Technology Ab High-strength steel product and manufacturing method thereof
KR102236850B1 (en) * 2019-11-04 2021-04-06 주식회사 포스코 Hot rolled steel plate having exellent hydrogen induced crack resistance and tensile property at high temperature and method of manufacturing the same
JP7440741B2 (en) 2019-12-18 2024-02-29 日本製鉄株式会社 ERW steel pipe for line pipe and method for manufacturing ERW steel pipe for line pipe
WO2021161366A1 (en) * 2020-02-10 2021-08-19 日本製鉄株式会社 Line pipe-use electric resistance welded steel pipe
RU2747083C1 (en) * 2020-11-02 2021-04-26 Акционерное Общество "Выксунский металлургический завод" (АО ВМЗ") Method for production of electro-welded pipe made of low-carbon steel, resistant to hydrogen cracking (options)

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4268462B2 (en) * 2002-06-26 2009-05-27 新日本製鐵株式会社 Manufacturing method of non-tempered low yield ratio high strength steel sheet with excellent high temperature strength
JP3823906B2 (en) 2002-09-26 2006-09-20 Ｊｆｅスチール株式会社 Manufacturing method of ERW steel pipe for high-strength line pipe with excellent hydrogen cracking resistance and toughness
KR20080082015A (en) * 2003-12-19 2008-09-10 신닛뽄세이테쯔 카부시키카이샤 Steel plates for ultra-high-strength linepipes and ultra-high-strength linepipes having excellent low-temperature toughness and manufacturing methods thereof
JP4788146B2 (en) 2004-03-09 2011-10-05 Ｊｆｅスチール株式会社 Hot rolled steel sheet for low YR type ERW welded steel pipe excellent in aging resistance and method for producing the same
JP5055736B2 (en) 2004-12-02 2012-10-24 Ｊｆｅスチール株式会社 Manufacturing method of high-strength steam piping steel plate with excellent weld heat-affected zone toughness
JP4655670B2 (en) * 2005-02-24 2011-03-23 Ｊｆｅスチール株式会社 Manufacturing method of high strength welded steel pipe with low yield ratio and excellent weld toughness
JP2007244797A (en) 2006-03-20 2007-09-27 Onkyo Corp Game machine
JP2007254797A (en) * 2006-03-22 2007-10-04 Jfe Steel Kk Thick electric resistance welded pipe having excellent toughness in base metal part and electric resistance weld zone and its production method
EP2045348B1 (en) * 2006-07-13 2013-03-13 Nippon Steel & Sumitomo Metal Corporation Bend pipe and process for producing the same
JP4741528B2 (en) 2007-02-09 2011-08-03 新日本製鐵株式会社 Steel plates and steel pipes for steam transport piping having excellent high temperature characteristics and methods for producing them
JP5223375B2 (en) 2007-03-01 2013-06-26 新日鐵住金株式会社 High-strength hot-rolled steel sheet for line pipe excellent in low-temperature toughness and method for producing the same
KR101228610B1 (en) * 2008-05-26 2013-02-01 신닛테츠스미킨 카부시키카이샤 High-strength hot-rolled steel sheet for line pipe excellent in low-temperature toughness and ductile-fracture-stopping performance and process for producing the same
RU2375469C1 (en) * 2008-07-11 2009-12-10 Открытое акционерное общество "Северсталь" (ОАО "Северсталь") Production method of candies from low-alloyed steel
JP4853575B2 (en) 2009-02-06 2012-01-11 Ｊｆｅスチール株式会社 High strength steel pipe for low temperature excellent in buckling resistance and weld heat affected zone toughness and method for producing the same
KR101450976B1 (en) 2009-09-30 2014-10-15 제이에프이 스틸 가부시키가이샤 Steel plate with low yield ratio, high strength, and high toughness and process for producing same
CN104220622B (en) 2012-04-13 2016-11-02 杰富意钢铁株式会社 There is high-strength thick electric-resistance-welded steel pipe and the manufacture method thereof of excellent low-temperature flexibility

Also Published As

Publication number Publication date
KR101663399B1 (en) 2016-10-06
EP2868765A4 (en) 2015-08-12
US9551047B2 (en) 2017-01-24
RU2618987C2 (en) 2017-05-11
EP2868765A1 (en) 2015-05-06
JP5516659B2 (en) 2014-06-11
CA2877610C (en) 2018-09-11
JP2014009366A (en) 2014-01-20
RU2015102582A (en) 2016-08-20
CN104411853A (en) 2015-03-11
KR20150013861A (en) 2015-02-05
EP2868765B1 (en) 2019-03-20
US20150203933A1 (en) 2015-07-23
WO2014002423A1 (en) 2014-01-03
CA2877610A1 (en) 2014-01-03

Similar Documents

Publication Publication Date Title
IN2014KN02799A (en)
IN2014MN01980A (en)
UA119459C2 (en) Method for manufacturing a high strength steel sheet and sheet obtained
MX2017001106A (en) Method for producing high-strength hot dipped galvanized steel sheet.
MX2017006303A (en) Method for manufacturing a high strength steel product and steel product thereby obtained.
MX2017001024A (en) Method for heating up steel sheets and device for carrying out the method.
MX348196B (en) Method for manufacturing hot stamped body having vertical wall, and hot stamped body having vertical wall.
IN2014KN01251A (en)
IN2014MN00193A (en)
AR075976A1 (en) METHOD FOR THE MANUFACTURE OF PIPE WITHOUT SEWING
RU2016151388A (en) METHOD FOR PRODUCING HIGH-STRENGTH STEEL COATED SHEET HAVING IMPROVED STRENGTH AND PLASTICITY AND THE PRODUCED SHEET
MX2016003258A (en) Method for manufacturing press-molded article, and press-molded article.
IN2015DN00425A (en)
MX350226B (en) High-strength cold-rolled steel sheet having excellent deep-drawability and bake hardenability, and method for manufacturing same.
RU2016151402A (en) A method of manufacturing a high strength steel sheet with or without coating and the resulting steel sheet
RU2016151385A (en) METHOD FOR PRODUCING HIGH-STRENGTH STEEL COATED SHEET WITH HIGH STRENGTH, PLASTICITY AND FORMABILITY
JP2011140686A5 (en)
JP2011256437A5 (en)
WO2011091983A3 (en) Process for the heat treatment of metal strip material, and strip material produced in that way
JP2013542315A (en) Method of hot forming coated metal parts and molded parts
WO2014186689A3 (en) High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath
MX354354B (en) Method for producing electromagnetic steel sheet.
RU2016151786A (en) METHOD FOR PRODUCING HIGH-STRENGTH STEEL SHEET WITH IMPROVED FORMABILITY AND PLASTICITY, AND THE RECEIVED SHEET
GB2548049A (en) Hot rolled light-gauge martensitic steel sheet and method for making the same
MX2021015145A (en) Method for producing a high strength coated steel sheet having improved strength, formability and obtained sheet.