IN2014CN03778A - - Google Patents
Info
- Publication number
- IN2014CN03778A IN2014CN03778A IN3778CHN2014A IN2014CN03778A IN 2014CN03778 A IN2014CN03778 A IN 2014CN03778A IN 3778CHN2014 A IN3778CHN2014 A IN 3778CHN2014A IN 2014CN03778 A IN2014CN03778 A IN 2014CN03778A
- Authority
- IN
- India
- Prior art keywords
- coating
- composition
- water
- compound
- pretreatment
- Prior art date
Abstract
The invention relates to a method for improving the throwing power of an electrodeposition coating by coating metallic surfaces with a pretreatment composition comprising silane/silanol/siloxane/polysiloxane said composition comprising as well as water a) at least one compound a) selected from silanes silanols siloxanes and polysiloxanes of which at least one of these compounds is still able to condense and comprising b) at least one titanium hafnium and/or zirconium containing compound b) and also comprising c) at least one kind of cations c) selected from cations of metals from transition groups 1 to 3 and 5 to 8 including lanthanides and also from main group 2 of the Periodic Table of the Elements and/or at least one corresponding compound c) and/or comprising d) at least one organic compound d) selected from monomers oligomers polymers and copolymers including block copolymers; the coating freshly applied with this composition is rinsed at least once with water wherein a) at least one water rinse comprises surfactant and/or wherein b) the substrates prior to the silane based pretreatment are treated at least once with an iron containing aqueous composition and after the water rinse an electrodeposition coating is applied the coating freshly applied with this composition not being through dried before said rinsing so that the at least one condensable compound a) does not condense to a great extent before the rinsing of the pretreatment coating with water and/or before being coated with an electrocoat material.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102011085091 | 2011-10-24 | ||
PCT/EP2012/070929 WO2013060662A2 (en) | 2011-10-24 | 2012-10-23 | Method for coating metallic surfaces with a multi-component aqueous composition |
Publications (1)
Publication Number | Publication Date |
---|---|
IN2014CN03778A true IN2014CN03778A (en) | 2015-09-04 |
Family
ID=47049176
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
IN3778CHN2014 IN2014CN03778A (en) | 2011-10-24 | 2012-10-23 |
Country Status (12)
Country | Link |
---|---|
US (1) | US10378120B2 (en) |
EP (1) | EP2771499B1 (en) |
JP (1) | JP6305340B2 (en) |
CN (1) | CN104271799B (en) |
BR (1) | BR112014009860B1 (en) |
DE (1) | DE102012219296A1 (en) |
ES (1) | ES2556967T3 (en) |
IN (1) | IN2014CN03778A (en) |
MX (1) | MX353928B (en) |
RU (1) | RU2661643C2 (en) |
WO (1) | WO2013060662A2 (en) |
ZA (1) | ZA201403569B (en) |
Families Citing this family (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR102278974B1 (en) | 2013-06-20 | 2021-07-16 | 헨켈 아게 운트 코. 카게아아 | Multi-step method for electrodeposition |
RU2691149C2 (en) * | 2014-01-23 | 2019-06-11 | Шеметалл Гмбх | Method of coating metal surfaces, bases coated with such method, and their use |
US20150315718A1 (en) * | 2014-05-05 | 2015-11-05 | Ppg Industries Ohio, Inc. | Metal pretreatment modification for improved throwpower |
DE102015225185A1 (en) * | 2014-12-15 | 2016-06-16 | Chemetall Gmbh | Composition for the adhesive coating of metallic surfaces, in particular of aluminum materials |
CN104988563A (en) * | 2015-07-30 | 2015-10-21 | 南京科润工业介质股份有限公司 | Silane-nanoceramic composite surface conditioning agent |
EP3133101B1 (en) * | 2015-08-21 | 2018-03-21 | Sika Technology AG | Aqueous adhesive composition on the basus of an epoxy resin with improved adhesion and storage stability |
US10435806B2 (en) | 2015-10-12 | 2019-10-08 | Prc-Desoto International, Inc. | Methods for electrolytically depositing pretreatment compositions |
EP3682042B1 (en) * | 2017-09-14 | 2021-11-10 | Chemetall GmbH | Method for pretreating aluminum materials, particularly aluminum wheels |
JP7410388B2 (en) * | 2019-10-17 | 2024-01-10 | 日本製鉄株式会社 | Painted plated steel plate |
CN113818015A (en) * | 2021-09-22 | 2021-12-21 | 浙江大学 | Safe and environment-friendly silane treatment fluid and application thereof |
CN116004118B (en) * | 2021-10-22 | 2023-09-29 | 中国石油化工股份有限公司 | Coating treatment fluid and preparation method and application thereof |
CN114074063A (en) * | 2021-11-22 | 2022-02-22 | 深圳市深赛尔股份有限公司 | Method for coating metal surface with multi-component aqueous composition |
WO2024081323A1 (en) * | 2022-10-13 | 2024-04-18 | Modine Manufacturing Company | Waterborne top coatings for aluminum heat exchangers |
Family Cites Families (25)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3620949A (en) | 1969-04-11 | 1971-11-16 | Balm Paints Ltd | Metal pretreatment and coating process |
JPS61291997A (en) | 1985-06-18 | 1986-12-22 | Nissan Motor Co Ltd | Coating method for steel sheet |
US5294266A (en) * | 1989-07-28 | 1994-03-15 | Metallgesellschaft Aktiengesellschaft | Process for a passivating postrinsing of conversion layers |
JPH04218681A (en) * | 1990-12-19 | 1992-08-10 | Nippon Parkerizing Co Ltd | Treatment of surface on formed material combining aluminum and steel material and treating solution |
JP3301817B2 (en) * | 1993-05-25 | 2002-07-15 | 北海製罐株式会社 | Aluminum container and manufacturing method thereof |
JP3343843B2 (en) | 1996-07-26 | 2002-11-11 | 日本ペイント株式会社 | Pre-electrodeposition treatment method for car bodies |
DE19733972A1 (en) | 1997-08-06 | 1999-02-11 | Henkel Kgaa | Alkaline band passivation |
US20050109627A1 (en) * | 2003-10-10 | 2005-05-26 | Applied Materials, Inc. | Methods and chemistry for providing initial conformal electrochemical deposition of copper in sub-micron features |
JP4707258B2 (en) * | 2001-05-07 | 2011-06-22 | 日本ペイント株式会社 | Acid cleaning agent for chemical film and treatment method |
JP4544450B2 (en) * | 2002-12-24 | 2010-09-15 | 日本ペイント株式会社 | Chemical conversion treatment agent and surface treatment metal |
DE60324379D1 (en) | 2002-12-24 | 2008-12-11 | Chemetall Gmbh | Chemical conversion coating agent and coated metal surfaces |
JP2008184690A (en) * | 2002-12-24 | 2008-08-14 | Nippon Paint Co Ltd | Pretreatment method for coating |
ATE553163T1 (en) * | 2003-02-25 | 2012-04-15 | Chemetall Gmbh | METHOD FOR COATING METAL SURFACES WITH A MIXTURE CONTAINING AT LEAST TWO SILANES |
DE102005015576C5 (en) | 2005-04-04 | 2018-09-13 | Chemetall Gmbh | A method of coating metallic surfaces with an aqueous composition and using the substrates coated by the methods |
US20060099332A1 (en) * | 2004-11-10 | 2006-05-11 | Mats Eriksson | Process for producing a repair coating on a coated metallic surface |
BRPI0517706B1 (en) | 2004-11-10 | 2017-12-26 | Chemetall Gmbh | METHOD AND METAL SURFACE REPAIR COATING PRODUCTION PROCESS AND ADEQUATE TOOL FOR APPLICATION IN SUCH PROCESS |
JP2007262577A (en) * | 2006-03-01 | 2007-10-11 | Nippon Paint Co Ltd | Composition for metal surface treatment, metal surface treatment method, and metallic material |
JP2008184620A (en) * | 2007-01-26 | 2008-08-14 | Nippon Paint Co Ltd | Method for forming bilayer paint film |
EP2094880B1 (en) * | 2007-02-12 | 2012-09-05 | Henkel AG & Co. KGaA | Process for treating metal surfaces |
CN101809200A (en) * | 2007-09-27 | 2010-08-18 | 日本油漆株式会社 | Method for producing surface-treated metal material and method for producing metal coated article |
JP5436782B2 (en) * | 2008-01-16 | 2014-03-05 | 日本ペイント株式会社 | Aluminum wheel manufacturing method and aluminum wheel |
JP2010013677A (en) * | 2008-07-01 | 2010-01-21 | Nippon Parkerizing Co Ltd | Chemical conversion liquid for metal structure and surface treatment method |
HUE034508T2 (en) * | 2008-07-11 | 2018-02-28 | Henkel Ag & Co Kgaa | Chemical treatment liquid for steel material coating primer and method of treatment |
DE102008038653A1 (en) * | 2008-08-12 | 2010-03-25 | Henkel Ag & Co. Kgaa | Successive anti-corrosive pretreatment of metal surfaces in a multi-stage process |
DE102010001686A1 (en) | 2010-02-09 | 2011-08-11 | Henkel AG & Co. KGaA, 40589 | Composition for the alkaline passivation of zinc surfaces |
-
2012
- 2012-10-23 MX MX2014004933A patent/MX353928B/en active IP Right Grant
- 2012-10-23 CN CN201280063864.7A patent/CN104271799B/en active Active
- 2012-10-23 IN IN3778CHN2014 patent/IN2014CN03778A/en unknown
- 2012-10-23 JP JP2014537573A patent/JP6305340B2/en active Active
- 2012-10-23 RU RU2014120920A patent/RU2661643C2/en active
- 2012-10-23 WO PCT/EP2012/070929 patent/WO2013060662A2/en active Application Filing
- 2012-10-23 US US14/353,164 patent/US10378120B2/en active Active
- 2012-10-23 ES ES12775501.5T patent/ES2556967T3/en active Active
- 2012-10-23 DE DE201210219296 patent/DE102012219296A1/en not_active Withdrawn
- 2012-10-23 BR BR112014009860-3A patent/BR112014009860B1/en active IP Right Grant
- 2012-10-23 EP EP12775501.5A patent/EP2771499B1/en active Active
-
2014
- 2014-05-16 ZA ZA2014/03569A patent/ZA201403569B/en unknown
Also Published As
Publication number | Publication date |
---|---|
BR112014009860B1 (en) | 2021-01-19 |
MX2014004933A (en) | 2014-10-17 |
EP2771499B1 (en) | 2015-10-14 |
MX353928B (en) | 2018-02-06 |
BR112014009860A2 (en) | 2017-04-18 |
ES2556967T3 (en) | 2016-01-21 |
JP2015503021A (en) | 2015-01-29 |
RU2661643C2 (en) | 2018-07-18 |
US20140255706A1 (en) | 2014-09-11 |
WO2013060662A2 (en) | 2013-05-02 |
US10378120B2 (en) | 2019-08-13 |
CN104271799B (en) | 2017-03-08 |
RU2014120920A (en) | 2015-12-10 |
JP6305340B2 (en) | 2018-04-04 |
ZA201403569B (en) | 2015-07-29 |
DE102012219296A1 (en) | 2013-04-25 |
EP2771499A2 (en) | 2014-09-03 |
CN104271799A (en) | 2015-01-07 |
WO2013060662A3 (en) | 2013-11-14 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
IN2014CN03778A (en) | ||
TW200643217A (en) | Process for coating metallic surfaces with an aqueous composition, and this composition | |
MX2007005610A (en) | Method for the coating of metallic surfaces with an aqueous composition comprising silanes silanols siloxanes and polysiloxanes and said composition. | |
ATE509059T1 (en) | POLYHYDROXYFUNCTIONAL POLYSILOXANES, METHOD FOR THEIR PRODUCTION AND THEIR USE | |
JP2012524162A (en) | Aqueous silane systems based on tris (alkoxysilylalkyl) amines and uses thereof | |
RU2014145213A (en) | WATER-RESISTANT SILICON ORGANIC MATERIALS | |
RU2009141836A (en) | BIOCID / HYDROPHOBIC INTERNAL COVERING CONDENSER PIPES (INDUSTRIAL TURBINES AND SIDE COOLING CIRCUITS) | |
MX2016006981A (en) | Coating method for surfaces in chemical installations. | |
MX2011009234A (en) | Method for coating metal surfaces in a multi-step method. | |
WO2012047945A3 (en) | Wear resistant coating, article, and method | |
ATE412073T1 (en) | METHOD FOR PRE-TREATMENT BEFORE COATING | |
MX2015008173A (en) | Coatings for enhancing glass strength. | |
RU2015143198A (en) | EPOXYSILOXANE COMPOSITIONS FOR COATINGS | |
NZ732731A (en) | Soil-resistant, stain-resistant coatings and methods of applying on textile or other flexible materials | |
BR112014012199B1 (en) | composition of olefinomically olefinically functionalized siloxanes based on alkoxysilanes, their preparation and use process | |
RU2012112941A (en) | METHOD FOR PRODUCING SILICON FILM AND THE LIQUID USED IN IT FOR PROCESSING POLYSILAZANE COATING | |
WO2009103024A3 (en) | Methods and compositions for improving the surface properties of fabrics, garments, textiles and other substrates | |
WO2010144352A3 (en) | Method for treating hydrocarbon-bearing formations with fluoroalkyl silanes | |
MX2015012238A (en) | Inorganic composite coatings comprising novel functionalized acrylics. | |
WO2014090911A3 (en) | Method for treating the surface of a metallic substrate | |
ATE529485T1 (en) | LAYER OR COATING TO COUNTERACT CRYSTALLINE DEPOSITS | |
WO2019123263A3 (en) | Inorganic dental fillers including a silane treated surface | |
BR112012025125A2 (en) | heat-resistant compositions for color-resistant abrasion-resistant transparent hard coatings | |
ATE530593T1 (en) | USE OF A SILICON COMPOUND AS A PROCESSING AID AND AS A SURFACE SMOOTHING ADDITIVE IN A POLYOLEFIN COMPOSITION CONTAINING CROSS-LINKABLE POLYOLEFIN WITH SILANE GROUPS AND A SILANOL CONDENSATION CATALYST | |
MX351403B (en) | Resin based post rinse for improved throwpower of electrodepositable coating compositions on pretreated metal substrates. |