IN2014CN03373A - - Google Patents
Download PDFInfo
- Publication number
- IN2014CN03373A IN2014CN03373A IN3373CHN2014A IN2014CN03373A IN 2014CN03373 A IN2014CN03373 A IN 2014CN03373A IN 3373CHN2014 A IN3373CHN2014 A IN 3373CHN2014A IN 2014CN03373 A IN2014CN03373 A IN 2014CN03373A
- Authority
- IN
- India
- Prior art keywords
- ceramic layer
- weight percent
- coating systems
- outer ceramic
- consists essentially
- Prior art date
Abstract
Coating systems and processes by which the coating systems can be deposited to be resistant to contaminants and particularly resistant to infiltration and damage caused by CMAS. The coating systems include inner and outer ceramic layers. The inner ceramic layer consists essentially of zirconia stabilized by about 6 to about 9 weight percent yttria and optionally contains greater than 0.5 to 10 weight percent hafnium oxide. The outer ceramic layer overlies and contacts the inner ceramic layer to define the outermost surface of the coating system. The outer ceramic layer consists essentially of zirconia stabilized by about 25 to about 75 weight percent yttria has a thickness that is less than the thickness of the inner ceramic layer and further contains greater than 0.5 to 10 weight percent hafnium oxide and optionally 1 to 10 weight percent tantalum oxide. The outer ceramic layer has a porosity level that is lower than that of the inner ceramic layer.
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201161546793P | 2011-10-13 | 2011-10-13 | |
US13/341,247 US9023486B2 (en) | 2011-10-13 | 2011-12-30 | Thermal barrier coating systems and processes therefor |
US13/542,057 US9034479B2 (en) | 2011-10-13 | 2012-07-05 | Thermal barrier coating systems and processes therefor |
PCT/US2012/059841 WO2013103425A2 (en) | 2011-10-13 | 2012-10-12 | Thermal barrier coating systems and processes therefor |
Publications (1)
Publication Number | Publication Date |
---|---|
IN2014CN03373A true IN2014CN03373A (en) | 2015-10-09 |
Family
ID=48745525
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
IN3373CHN2014 IN2014CN03373A (en) | 2011-10-13 | 2012-10-12 |
Country Status (8)
Country | Link |
---|---|
US (1) | US9034479B2 (en) |
EP (1) | EP2766504B1 (en) |
JP (1) | JP5802838B2 (en) |
CN (1) | CN103874580B (en) |
BR (1) | BR112014008860A2 (en) |
CA (1) | CA2851281C (en) |
IN (1) | IN2014CN03373A (en) |
WO (1) | WO2013103425A2 (en) |
Families Citing this family (51)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11047033B2 (en) | 2012-09-05 | 2021-06-29 | Raytheon Technologies Corporation | Thermal barrier coating for gas turbine engine components |
US9649690B2 (en) * | 2014-02-25 | 2017-05-16 | General Electric Company | System having layered structure and method of making the same |
US20150275682A1 (en) * | 2014-04-01 | 2015-10-01 | Siemens Energy, Inc. | Sprayed haynes 230 layer to increase spallation life of thermal barrier coating on a gas turbine engine component |
US20160186580A1 (en) * | 2014-05-20 | 2016-06-30 | United Technologies Corporation | Calcium Magnesium Aluminosilicate (CMAS) Resistant Thermal Barrier Coating and Coating Process Therefor |
US20160362775A1 (en) * | 2014-09-30 | 2016-12-15 | United Technologies Corporation | Multi-Phase Pre-Reacted Thermal Barrier Coatings and Process Therefor |
DE102014222684A1 (en) * | 2014-11-06 | 2016-05-12 | Siemens Aktiengesellschaft | Segmented thermal barrier coating made of fully stabilized zirconium oxide |
US9869188B2 (en) | 2014-12-12 | 2018-01-16 | General Electric Company | Articles for high temperature service and method for making |
CN104891990B (en) * | 2015-05-08 | 2017-03-08 | 清华大学 | Eutectic structure heat barrier coat material and its powder manufacture method that can be used for thermal spraying |
US10745793B2 (en) | 2015-06-04 | 2020-08-18 | Raytheon Technologies Corporation | Ceramic coating deposition |
CN104988455B (en) * | 2015-07-09 | 2018-07-17 | 北京航空航天大学 | A kind of air plasma spraying preparation method of the heat-barrier coating ceramic layer of anti-CMAS corrosion |
US10201831B2 (en) | 2015-12-09 | 2019-02-12 | General Electric Company | Coating inspection method |
FR3044946B1 (en) | 2015-12-14 | 2018-01-12 | Safran Aircraft Engines | ABRADABLE COATING WITH VARIABLE DENSITY |
FR3044945B1 (en) | 2015-12-14 | 2018-01-12 | Centre National De La Recherche Scientifique | ABRADABLE COATING WITH VARIABLE DENSITY |
US9997406B2 (en) | 2016-02-04 | 2018-06-12 | International Business Machines Corporation | Columnar interconnects and method of making them |
DE102016201947A1 (en) * | 2016-02-10 | 2017-08-10 | MTU Aero Engines AG | Thermal barrier coating with high corrosion resistance |
US10822966B2 (en) * | 2016-05-09 | 2020-11-03 | General Electric Company | Thermal barrier system with bond coat barrier |
US10202855B2 (en) | 2016-06-02 | 2019-02-12 | General Electric Company | Airfoil with improved coating system |
JP6908973B2 (en) * | 2016-06-08 | 2021-07-28 | 三菱重工業株式会社 | Manufacturing methods for thermal barrier coatings, turbine components, gas turbines, and thermal barrier coatings |
US9748173B1 (en) | 2016-07-06 | 2017-08-29 | International Business Machines Corporation | Hybrid interconnects and method of forming the same |
US9875966B1 (en) | 2016-08-01 | 2018-01-23 | International Business Machines Corporation | Method and structure of forming low resistance interconnects |
US9793156B1 (en) | 2016-09-12 | 2017-10-17 | International Business Machines Corporation | Self-aligned low resistance metallic interconnect structures |
CN106148874A (en) * | 2016-09-13 | 2016-11-23 | 中国农业机械化科学研究院 | Thermal barrier coating that a kind of anti-CMAS smelt deposits corrodes and preparation method thereof |
US10513463B2 (en) * | 2016-09-27 | 2019-12-24 | Skyworks Solutions, Inc. | Enhanced fracture toughness thermal barrier coating material |
JP7154752B2 (en) * | 2016-12-11 | 2022-10-18 | ゼネラル・エレクトリック・カンパニイ | Thermal barrier coating with low thermal conductivity |
US10822696B2 (en) | 2016-12-14 | 2020-11-03 | General Electric Company | Article with thermal barrier coating and method for making |
JP6877217B2 (en) * | 2017-03-31 | 2021-05-26 | 三菱重工業株式会社 | Manufacturing method of heat shield coating, turbine blade and heat shield coating |
FR3067391B1 (en) | 2017-06-12 | 2020-12-04 | Safran | REINFORCED ANTI-CMAS COATING |
FR3067392B1 (en) * | 2017-06-12 | 2020-12-04 | Safran | DOUBLE REACTIVITY ANTI-CMAS COATING |
EP3428136B1 (en) * | 2017-07-14 | 2020-04-01 | Ansaldo Energia IP UK Limited | High temperature thermal insulation material, particularly for gas turbine, and manufacturing method thereof |
US10947625B2 (en) * | 2017-09-08 | 2021-03-16 | Raytheon Technologies Corporation | CMAS-resistant thermal barrier coating and method of making a coating thereof |
US10224242B1 (en) | 2017-11-14 | 2019-03-05 | International Business Machines Corporation | Low-resistivity metallic interconnect structures |
WO2019108995A1 (en) * | 2017-12-01 | 2019-06-06 | Corning Incorporated | Apparatus and method for producing glass |
US20210047968A1 (en) * | 2018-03-02 | 2021-02-18 | Japan Fine Ceramics Center | Thermal barrier coating |
JP7169077B2 (en) * | 2018-03-26 | 2022-11-10 | 三菱重工業株式会社 | Thermal barrier coating, turbine component, gas turbine, and method for producing thermal barrier coating |
CN108442980B (en) * | 2018-04-03 | 2024-04-05 | 东莞传动电喷科技有限公司 | Ceramic thermal barrier coating applied to engine and engine thereof |
US20210140339A1 (en) * | 2018-04-09 | 2021-05-13 | Oerlikon Metco (Us) Inc. | Cmas resistant, high strain tolerant and low thermal conductivity thermal barrier coatings and thermal spray coating method |
US20190316246A1 (en) * | 2018-04-17 | 2019-10-17 | General Electric Company | Reactive phase spray formulation coatings |
US10600686B2 (en) | 2018-06-08 | 2020-03-24 | International Business Machines Corporation | Controlling grain boundaries in high aspect-ratio conductive regions |
US11555241B2 (en) * | 2018-07-03 | 2023-01-17 | Raytheon Technologies Corporation | Coating system having synthetic oxide layers |
US11668198B2 (en) | 2018-08-03 | 2023-06-06 | Raytheon Technologies Corporation | Fiber-reinforced self-healing environmental barrier coating |
US10934220B2 (en) | 2018-08-16 | 2021-03-02 | Raytheon Technologies Corporation | Chemical and topological surface modification to enhance coating adhesion and compatibility |
US11535571B2 (en) | 2018-08-16 | 2022-12-27 | Raytheon Technologies Corporation | Environmental barrier coating for enhanced resistance to attack by molten silicate deposits |
US11505506B2 (en) | 2018-08-16 | 2022-11-22 | Raytheon Technologies Corporation | Self-healing environmental barrier coating |
EP3712379A1 (en) * | 2019-03-22 | 2020-09-23 | Siemens Aktiengesellschaft | Fully stabilized zirconia in a seal system |
CN110436947B (en) * | 2019-08-23 | 2022-02-18 | 益阳鸿源稀土有限责任公司 | Anti-leakage material for large rare earth electrolytic cell |
CN112144003A (en) * | 2020-10-20 | 2020-12-29 | 华瑞(江苏)燃机服务有限公司 | Spraying process of gas turbine blade |
CN113149641B (en) * | 2021-01-08 | 2022-11-25 | 北京金轮坤天特种机械有限公司 | Composite coating, preparation method thereof and engine |
CN113105237B (en) * | 2021-04-30 | 2023-02-17 | 昆明理工大学 | AB2O6 type tantalate ceramic and preparation method thereof |
CN113956037B (en) * | 2021-12-11 | 2022-10-04 | 广西大学 | Preparation method of CMAS corrosion-resistant two-phase structure scandium-yttrium rare earth doped zirconia powder |
CN116477943B (en) * | 2022-01-17 | 2024-04-12 | 中国人民解放军国防科技大学 | Tantalate complex-phase ceramic and preparation method thereof |
CN116477970A (en) * | 2023-03-05 | 2023-07-25 | 广西大学 | Preparation method of CMAS corrosion-resistant in-situ generated rare earth apatite phase compact reaction layer |
Family Cites Families (47)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5073433B1 (en) | 1989-10-20 | 1995-10-31 | Praxair Technology Inc | Thermal barrier coating for substrates and process for producing it |
US5238752A (en) | 1990-05-07 | 1993-08-24 | General Electric Company | Thermal barrier coating system with intermetallic overlay bond coat |
GB9204791D0 (en) | 1992-03-05 | 1992-04-22 | Rolls Royce Plc | A coated article |
CA2110007A1 (en) | 1992-12-29 | 1994-06-30 | Adrian M. Beltran | Thermal barrier coating process |
US5520516A (en) | 1994-09-16 | 1996-05-28 | Praxair S.T. Technology, Inc. | Zirconia-based tipped blades having macrocracked structure |
EP0705911B1 (en) | 1994-10-04 | 2001-12-05 | General Electric Company | Thermal barrier coating |
US5660885A (en) | 1995-04-03 | 1997-08-26 | General Electric Company | Protection of thermal barrier coating by a sacrificial surface coating |
US6102656A (en) | 1995-09-26 | 2000-08-15 | United Technologies Corporation | Segmented abradable ceramic coating |
US6071627A (en) | 1996-03-29 | 2000-06-06 | Kabushiki Kaisha Toshiba | Heat-resistant member and a method for evaluating quality of a heat-resistant member |
GB9617267D0 (en) | 1996-08-16 | 1996-09-25 | Rolls Royce Plc | A metallic article having a thermal barrier coating and a method of application thereof |
US6930066B2 (en) | 2001-12-06 | 2005-08-16 | Siemens Westinghouse Power Corporation | Highly defective oxides as sinter resistant thermal barrier coating |
US5897921A (en) | 1997-01-24 | 1999-04-27 | General Electric Company | Directionally solidified thermal barrier coating |
US6047359A (en) | 1997-11-04 | 2000-04-04 | The United States Of America As Represented By The Secretary Of The Navy | Predictive read cache memories for reducing primary cache miss latency in embedded microprocessor systems |
US6047539A (en) | 1998-04-30 | 2000-04-11 | General Electric Company | Method of protecting gas turbine combustor components against water erosion and hot corrosion |
US6482537B1 (en) | 2000-03-24 | 2002-11-19 | Honeywell International, Inc. | Lower conductivity barrier coating |
JP2002167636A (en) | 2000-10-30 | 2002-06-11 | United Technol Corp <Utc> | Low density oxidation resistant superalloy material capable of thermal barrier coating retention without bond coat |
US6890668B2 (en) | 2002-08-30 | 2005-05-10 | General Electric Company | Thermal barrier coating material |
US6764779B1 (en) | 2003-02-24 | 2004-07-20 | Chromalloy Gas Turbine Corporation | Thermal barrier coating having low thermal conductivity |
US6982126B2 (en) | 2003-11-26 | 2006-01-03 | General Electric Company | Thermal barrier coating |
US7291403B2 (en) | 2004-02-03 | 2007-11-06 | General Electric Company | Thermal barrier coating system |
US20050118334A1 (en) | 2004-09-03 | 2005-06-02 | General Electric Company | Process for inhibiting srz formation and coating system therefor |
US7264888B2 (en) | 2004-10-29 | 2007-09-04 | General Electric Company | Coating systems containing gamma-prime nickel aluminide coating |
US7115326B2 (en) | 2005-01-21 | 2006-10-03 | General Electric Company | Thermal/environmental barrier coating with transition layer for silicon-comprising materials |
US7597966B2 (en) | 2005-06-10 | 2009-10-06 | General Electric Company | Thermal barrier coating and process therefor |
US8603930B2 (en) * | 2005-10-07 | 2013-12-10 | Sulzer Metco (Us), Inc. | High-purity fused and crushed zirconia alloy powder and method of producing same |
US7723249B2 (en) * | 2005-10-07 | 2010-05-25 | Sulzer Metco (Us), Inc. | Ceramic material for high temperature service |
US20070160859A1 (en) | 2006-01-06 | 2007-07-12 | General Electric Company | Layered thermal barrier coatings containing lanthanide series oxides for improved resistance to CMAS degradation |
US7736759B2 (en) | 2006-01-20 | 2010-06-15 | United Technologies Corporation | Yttria-stabilized zirconia coating with a molten silicate resistant outer layer |
US7785722B2 (en) | 2006-01-20 | 2010-08-31 | United Technologies Corporation | CMAS resistant thermal barrier coating |
US20080160172A1 (en) | 2006-05-26 | 2008-07-03 | Thomas Alan Taylor | Thermal spray coating processes |
US7875370B2 (en) | 2006-08-18 | 2011-01-25 | United Technologies Corporation | Thermal barrier coating with a plasma spray top layer |
US7722959B2 (en) | 2006-09-06 | 2010-05-25 | United Technologies Corporation | Silicate resistant thermal barrier coating with alternating layers |
US7862901B2 (en) * | 2006-12-15 | 2011-01-04 | General Electric Company | Yttria containing thermal barrier coating topcoat layer and method for applying the coating layer |
US20090162690A1 (en) * | 2007-12-24 | 2009-06-25 | Bangalore Aswatha Nagaraj | Thermal barrier coating systems |
US20090162692A1 (en) | 2007-12-24 | 2009-06-25 | Bangalore Aswatha Nagaraj | Coated Superalloy Articles |
EP2128299B1 (en) | 2008-05-29 | 2016-12-28 | General Electric Technology GmbH | Multilayer thermal barrier coating |
EP2196559A1 (en) * | 2008-12-15 | 2010-06-16 | ALSTOM Technology Ltd | Thermal barrier coating system, components coated therewith and method for applying a thermal barrier coating system to components |
US20100154422A1 (en) * | 2008-12-19 | 2010-06-24 | Glen Harold Kirby | Cmas mitigation compositions, environmental barrier coatings comprising the same, and ceramic components comprising the same |
JP5610698B2 (en) | 2009-03-26 | 2014-10-22 | 三菱重工業株式会社 | Thermal barrier coating material, thermal barrier coating, turbine component and gas turbine |
JP5075880B2 (en) | 2009-06-30 | 2012-11-21 | 株式会社日立製作所 | Heat-resistant parts and high-temperature parts for gas turbines |
US20110033284A1 (en) | 2009-08-04 | 2011-02-10 | United Technologies Corporation | Structurally diverse thermal barrier coatings |
US20110171488A1 (en) | 2009-08-11 | 2011-07-14 | Thomas Alan Taylor | Thermal barrier coating systems |
JP2011167994A (en) | 2010-02-22 | 2011-09-01 | Hitachi Ltd | Heat-resistant member having thermal barrier coating and gas turbine component using the same |
FR2957358B1 (en) | 2010-03-12 | 2012-04-13 | Snecma | METHOD FOR MANUFACTURING THERMAL BARRIER PROTECTION AND MULTILAYER COATING FOR FORMING A THERMAL BARRIER |
JP5620577B2 (en) | 2010-07-23 | 2014-11-05 | ロールス−ロイス コーポレイション | Thermal barrier coating comprising a CMAS resistant thermal barrier coating layer |
US20120034471A1 (en) | 2010-08-09 | 2012-02-09 | Honeywell International Inc. | Thermal barrier systems including yttrium gradient layers and methods for the formation thereof |
US9023486B2 (en) * | 2011-10-13 | 2015-05-05 | General Electric Company | Thermal barrier coating systems and processes therefor |
-
2012
- 2012-07-05 US US13/542,057 patent/US9034479B2/en active Active
- 2012-10-12 EP EP12846792.5A patent/EP2766504B1/en active Active
- 2012-10-12 JP JP2014535892A patent/JP5802838B2/en not_active Expired - Fee Related
- 2012-10-12 WO PCT/US2012/059841 patent/WO2013103425A2/en active Application Filing
- 2012-10-12 IN IN3373CHN2014 patent/IN2014CN03373A/en unknown
- 2012-10-12 CN CN201280050181.8A patent/CN103874580B/en active Active
- 2012-10-12 CA CA2851281A patent/CA2851281C/en not_active Expired - Fee Related
- 2012-10-12 BR BR112014008860A patent/BR112014008860A2/en not_active Application Discontinuation
Also Published As
Publication number | Publication date |
---|---|
BR112014008860A2 (en) | 2017-04-18 |
CN103874580B (en) | 2017-01-18 |
JP5802838B2 (en) | 2015-11-04 |
EP2766504A2 (en) | 2014-08-20 |
US9034479B2 (en) | 2015-05-19 |
CA2851281C (en) | 2016-08-30 |
JP2015501375A (en) | 2015-01-15 |
CA2851281A1 (en) | 2013-07-11 |
WO2013103425A3 (en) | 2013-09-26 |
US20140220378A1 (en) | 2014-08-07 |
CN103874580A (en) | 2014-06-18 |
EP2766504B1 (en) | 2015-12-30 |
WO2013103425A2 (en) | 2013-07-11 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
IN2014CN03373A (en) | ||
IN2015DN03013A (en) | ||
WO2013177269A3 (en) | Zirconium-containing precursors for vapor deposition | |
FR2966455B1 (en) | METHOD FOR COATING A PART OF A COATING AGAINST OXIDATION | |
WO2014170005A3 (en) | Chromium-based oxidation protection layer | |
TW200728593A (en) | Yttria-stabilized zirconia coating with a molten silicate resistant outer layer | |
EP2806483A4 (en) | Secondary battery separation membrane including double porous coating layers of inorganic particles having different surface properties, secondary battery including same, and method for manufacturing separation membrane | |
MX343044B (en) | CUTTING TOOLS WITH Al-Cr-B-N / Ti-Al-N MULTILAYER COATINGS. | |
WO2012174101A3 (en) | Corrodible downhole article and method of removing the article from downhole environment | |
TW201614092A (en) | Selective deposition with alcohol selective reduction and protection | |
WO2011028549A3 (en) | Corrosion resistant glass coating applied to ceramic foam used to filter molten metal | |
UA96581C2 (en) | Antifouling material and production method thereof | |
RU2009119821A (en) | CERAMIC COATING SYSTEM CREATING A THERMAL BARRIER WITH TWO CERAMIC LAYERS | |
WO2012033326A3 (en) | Dense rare earth metal oxide coating film for sealing porous ceramic surface, and preparation method thereof | |
NZ707530A (en) | Micro-devices for disease detection | |
GB0907010D0 (en) | Improvements in or relating to composite structures | |
WO2014065928A3 (en) | Thermal barrier coating for gas turbine engine components | |
IN2015KN00588A (en) | ||
WO2012091456A3 (en) | Magnesium alloy with dense surface texture and surface treatment method thereof | |
WO2015082697A3 (en) | Bearing element and method for manufacturing a bearing element | |
EA201692390A1 (en) | SUBSTRATE CONTAINING A MULTILAYERED SYSTEM, INCLUDING AN UNFINISHED METAL LAYER, GLASS PACKAGE, APPLICATION AND METHOD | |
WO2012047249A3 (en) | Silicon titanium oxide coating, coated article including silicon titanium oxide coating, and method of making the same | |
WO2012030818A3 (en) | Chemochromic hydrogen sensors | |
EP2419697A4 (en) | System and method of measuring the thickness of a layer of coating | |
MY176682A (en) | Electrode for oxygen evolution in industrial electrochemical processes |