GB715704A - Improvements in and relating to titanium carbide composite material - Google Patents
Improvements in and relating to titanium carbide composite materialInfo
- Publication number
- GB715704A GB715704A GB28980/51A GB2898051A GB715704A GB 715704 A GB715704 A GB 715704A GB 28980/51 A GB28980/51 A GB 28980/51A GB 2898051 A GB2898051 A GB 2898051A GB 715704 A GB715704 A GB 715704A
- Authority
- GB
- United Kingdom
- Prior art keywords
- powder
- mixture
- chromium
- per cent
- carbide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
In a method of making articles which are permanently resistant to mechanical and chemical stresses at high temperatures by infiltrating a porous body of refractory metal carbide with a metallic material, the porous body or skeleton is produced from a mixture of free-carbon containing titanium carbide powder and chromium powder in which mixture the major portions of the chromium and carbon are present as a solid solution of chromium carbide and titanium carbide and before compacting and sintering to form the skeleton, the particles of the mixture are coated with a metallic binder comprising cobalt nickel, iron or their alloys. In one example a powder mixture comprising carbide powder comprising 75.96 per cent. titan-carbide powder comprising 75.96 per cent. titanium 18.0 per cent. combined carbon and 2.53 per cent. free carbon, all of 325 mesh was placed in a graphite crucible and heated in dry hydrogen for 30 minutes at 2300 DEG C. and the agglomerated mass thus formed was crushed to pass a 140 mesh screen Ten per cent. by weight of carbonyl nickel powder was added as a binder and the mixture treated in a ball mill for 24 hours. The mixture was then hot-pressed to the required shape at 1650 DEG C. and sintered for one hour at 1500 DEG C. in dry hydrogen and finally infiltrated at 1530 DEG C. with a nickel chromium-iron alloy known under the Registered Trade Mark "Nichrome." In another example, the binder was cobalt powder and the infiltrant was a cobalt-chromium-molybdenum alloy. The amount of chromium powder added to the original mixture may be increased to 15 per cent.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US715704XA | 1950-12-16 | 1950-12-16 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB715704A true GB715704A (en) | 1954-09-22 |
Family
ID=22102173
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB28980/51A Expired GB715704A (en) | 1950-12-16 | 1951-12-11 | Improvements in and relating to titanium carbide composite material |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB715704A (en) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
PL422609A1 (en) * | 2017-08-22 | 2019-02-25 | Zakład Mechaniki Maszyn Bukpol Łagodziński Spółka Jawna | Burnishing element of the hydraulic burnishing tool |
US10336654B2 (en) | 2015-08-28 | 2019-07-02 | Kennametal Inc. | Cemented carbide with cobalt-molybdenum alloy binder |
US11821062B2 (en) | 2019-04-29 | 2023-11-21 | Kennametal Inc. | Cemented carbide compositions and applications thereof |
-
1951
- 1951-12-11 GB GB28980/51A patent/GB715704A/en not_active Expired
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US10336654B2 (en) | 2015-08-28 | 2019-07-02 | Kennametal Inc. | Cemented carbide with cobalt-molybdenum alloy binder |
PL422609A1 (en) * | 2017-08-22 | 2019-02-25 | Zakład Mechaniki Maszyn Bukpol Łagodziński Spółka Jawna | Burnishing element of the hydraulic burnishing tool |
US11821062B2 (en) | 2019-04-29 | 2023-11-21 | Kennametal Inc. | Cemented carbide compositions and applications thereof |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US2814566A (en) | Boron and carbon containing hard cemented materials and their production | |
US4012230A (en) | Tungsten-nickel-cobalt alloy and method of producing same | |
US2765227A (en) | Titanium carbide composite material | |
GB715704A (en) | Improvements in and relating to titanium carbide composite material | |
US2657129A (en) | Aluminum-alloyed corrosion-resistant metal powders and related products and processes | |
US2840891A (en) | High temperature structural material and method of producing same | |
US2657127A (en) | Production of chromium-alloyed corrosion-resistant metal powders and related products | |
GB781083A (en) | Improvements relating to high speed tool forms and their production | |
US3510276A (en) | Sintered titanium carbide bodies | |
US3384465A (en) | Iron bonded tungsten carbide | |
GB716034A (en) | Method for the manufacture of high-temperature resistant articles | |
GB716604A (en) | Hot-strength corrosion resistant compounds and bodies and their production | |
US1812811A (en) | Sintered hard metal alloy and articles made thereof | |
Moskowitz et al. | High-strength tungsten carbides | |
US2119488A (en) | Alloys and process of making same | |
Nelson et al. | Refractory bodies composed of boron and titanium carbides bonded with metals | |
GB818827A (en) | Improvements in or relating to methods for, and mould assemblies for, producing infiltrated articles | |
US2657128A (en) | Silicon-alloyed corrosion-resistant metal powders and related products and processes | |
US3900936A (en) | Cemented ferrochrome material | |
GB798190A (en) | Improvements in and relating to composite refractory bodies | |
GB1321947A (en) | Process for producing a cemented tungsten carbide composition | |
Takagi et al. | Effects of Mo/B atomic ratio on the properties and structure of iron-molybdenum complex boride base hard alloys | |
GB354562A (en) | Improvements in the manufacture and production of shaped articles from metal powders | |
US3445203A (en) | Cemented chromium carbide containing small additions of phosphorus | |
US3532492A (en) | Process of producing cemented chromium carbide using phosphorous |