GB714681A - Improvements in or relating to plain bearings - Google Patents
Improvements in or relating to plain bearingsInfo
- Publication number
- GB714681A GB714681A GB2796/51A GB279651A GB714681A GB 714681 A GB714681 A GB 714681A GB 2796/51 A GB2796/51 A GB 2796/51A GB 279651 A GB279651 A GB 279651A GB 714681 A GB714681 A GB 714681A
- Authority
- GB
- United Kingdom
- Prior art keywords
- copper
- lead
- strip
- tube
- heated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
714,681. Coating with metals. GLACIER METAL CO. Ltd. Jan. 18. 1952. [Feb 5, 1951; April 25, 1951], Nos. 2796/51 and 9639/51. Class 82 (2) [Also in Group XXII] in a method of making plain bearing surfaces comprising a copper-clad structure containing 5-50 per cent. of lead bonded to a steel &c. backing, a copper sponge structure is subjected to heat treatment at sintering temperature while immersed in molten lead. Copper powder is applied from a hopper 2 to form a layer 3 on a copper-plated steel strip 1 which is continuously fed through a sintering furnace 4 oontain:ng a reducing atmosphere of hydrogen or a mixture of hydrogen and nitrogen in which the powder becomes partially sintered and bonded to the steel backing The composite strip then passes through a bath 5 of molten lead protected from oxidation by a floating cover or a gas blanket and which is heated by burners 6 to have a temperature gradient so that the strip is near sintering temperature at entry and is cooled to a temperature just above the melting point of lead as it leaves. The strip then passes through a chamber 7 where it is wiped to remove excess lead and cooled in a neutral or reducing' atmosphere before passing into the open air for cooling The bi-metallic strip so formed may be used for making bearing liners, sleeves and external bearing surfaces, thrust washers &c. In a modified process the partially sintered strip is severed into lengths which are treated in batches in a chamber containing a reducing gas which is heated by a bell-type electric furnace. After the temperature has been raised sufficiently to reduce all. oxides on the copper sponge, molten lead is introduced into the chamber, and heated near sintering temperature after which it is allowed to cool and is run off just before it solidifies. In another example the copper lead layer is formed on the inner face of a tube by spinning the tube between end plates with copper powder inside while the tube is heated in a neutral atmosphere to bring about partial sintering, molten lead then being introduced into the tube. In all examples modifications in the spongy texture of the copper may be brought about by the introduction of small percentages of tin, silver nickel, arsenic or silicon powders. Specification 676,209 is referred to.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB2796/51A GB714681A (en) | 1951-02-05 | 1951-02-05 | Improvements in or relating to plain bearings |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB2796/51A GB714681A (en) | 1951-02-05 | 1951-02-05 | Improvements in or relating to plain bearings |
Publications (1)
Publication Number | Publication Date |
---|---|
GB714681A true GB714681A (en) | 1954-09-01 |
Family
ID=9746080
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB2796/51A Expired GB714681A (en) | 1951-02-05 | 1951-02-05 | Improvements in or relating to plain bearings |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB714681A (en) |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3154844A (en) * | 1960-12-09 | 1964-11-03 | Federai Mogul Bower Bearings I | Process for making composite bearings |
US6800377B2 (en) | 2001-09-19 | 2004-10-05 | Daido Metal Company Ltd. | Multilayer sliding material |
-
1951
- 1951-02-05 GB GB2796/51A patent/GB714681A/en not_active Expired
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3154844A (en) * | 1960-12-09 | 1964-11-03 | Federai Mogul Bower Bearings I | Process for making composite bearings |
US6800377B2 (en) | 2001-09-19 | 2004-10-05 | Daido Metal Company Ltd. | Multilayer sliding material |
GB2381007B (en) * | 2001-09-19 | 2004-11-03 | Daido Metal Co | Multi-layer sliding material |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US4812372A (en) | Refractory metal substrate and coatings therefor | |
JPS55122865A (en) | Molten zinc plating method for difficult plating steel sheet | |
JPS5913924B2 (en) | Core metal for piercing rolling mill | |
ES459891A1 (en) | Process for cube-on-edge oriented boron-bearing silicon steel including normalizing | |
GB932820A (en) | Method of making a composite material | |
JPS5739105A (en) | Production of multilayer sliding material | |
GB714681A (en) | Improvements in or relating to plain bearings | |
US3039902A (en) | Method of treating steel | |
US3615917A (en) | Process for diffusing silicon into sheet steel | |
ES478713A1 (en) | Processing for electromagnetic silicon steel | |
US4140552A (en) | Method of treating aluminum-killed and low alloy steel strip and sheet surfaces, in sulfur-bearing atmosphere, for metallic coating | |
GB544903A (en) | Improvements in methods of making composite metallic articles | |
US2228600A (en) | Powder metallurgy | |
GB480349A (en) | Improvements relating to the manufacture of bearings | |
GB676198A (en) | Process for coating metallic objects with other metals | |
US1752474A (en) | Method of treating metals | |
JP2949715B2 (en) | Casting method of metal for plastic working | |
US2950526A (en) | Elevated temperature working of metals and alloys | |
GB2117374A (en) | Process for annealing steel strip | |
GB740157A (en) | Improvements in or relating to plain bearings | |
KR102177524B1 (en) | Heater device for transferring molten magnesium and method for manufacturing the same | |
US2311881A (en) | Insulating means or cover for metal baths | |
JPS55161005A (en) | Production of bronze compound sintered bearing material | |
SU442896A1 (en) | The method of copper products from tungsten-copper and molybdenum-copper pseudo-alloys | |
KR0146787B1 (en) | Method for manufacturing electrical sheet |