GB2356738A - Ionic salt dyes as amorphous, thermally stable emitting and charge transport layers in organic light emitting diodes - Google Patents
Ionic salt dyes as amorphous, thermally stable emitting and charge transport layers in organic light emitting diodes Download PDFInfo
- Publication number
- GB2356738A GB2356738A GB0018081A GB0018081A GB2356738A GB 2356738 A GB2356738 A GB 2356738A GB 0018081 A GB0018081 A GB 0018081A GB 0018081 A GB0018081 A GB 0018081A GB 2356738 A GB2356738 A GB 2356738A
- Authority
- GB
- United Kingdom
- Prior art keywords
- organic dye
- counterion
- ionizable substituent
- charge transport
- amorphous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
2356738 Ionic Salt Dyes as Amorphous, Thermally Stable Emitting and Charge
Transport Layers in Organic Light Emitting Diodes
FIELD OF THE INVENTION
This invention relates to organic light emitting diodes and, more particularly, to thermally stable, nominally amorphous films for use as emitting layers or charge transport layers in organic light emitting diodes (OLEDs). Such films are prepared from dyes that are modified to result in ionic salt analogues.
BACKGROUND OF THE INVENTION is organic light emitting diodes (OLED's) have attracted broad attention due to their potential for use in display technologies. A few prototype displays have been demonstrated but their widespread use has not occurred because of problems associated with their operational stability and durability.
The degradation of OLED devices has been attributed to chemical changes of the organic layers, such as oxidation, and also to physical changes such as crystallization. Many potentially useful emitting or charge -transporting materials form polycrystalline films when deposited by physical vapor deposition. Such films contain grain boundaries that can act as luminescence quenching sites. To avoid such a problem, deposition of amorphous (glassy state) thin films seems to be a good alternative approach for device fabrication. However, most nonpolymeric organic dye glasses are thermally unstable and crystallize when subjected to driving voltages in a device, causing device failure.
In traditional OLED devices, the emitting organic dye molecules (D) are generally neutral molecules which interact through weak van der Waals interactions. Because of the weak nature of these interactions, heating of the initially amorphous films (for example joule heating when the device is driven, or even heating during deposition) easily causes rearrangement of the molecules, leading to crystallization and grain growth.
The film crystallization problem has been identified by many researchers in the OLED device field. Efforts to synthesize amorphous dyes have been mainly focused on dissolving them in thermally stable amorphous 2 polymers. A second approach is aimed at synthesizing large, symmetric, rigid and dense molecules that will be more heat-resistive (see Naito et al., J. Physical Chemistry, Vol 101, p. 2350 (1997)). An alternative approach is based on the introduction of spiro centers into defined low molecular weight structures (see Salbeck et al., Synthetic Metals, Vol. 91, p. 209 (1997)).
SUMMARY OF THE INVENTION
The invention modifies dyes so as to form ionic salt derivatives.
Such derivatives are used as emitting or charge transport layers in organic light emitting diodes (OLED Is). The modification involves attachment of ionizable substituents during initial synthesis, followed by formation of an ionic salt. An improvement of the OLED's durability and performance is results from use of such ionic dye salts, since the evaporated films are nominally amorphous, thermally stable and resist further crystallization.
Preliminary devices built using a test compound exhibit superior efficiency.
BRIEF DESCRIPTION OF THE DRAWINGS
Fig. la illustrates a single neutral AEQT molecule.
Fig. ib illustrates the AEQT-2HC1 chloride salt of an ionized AEQT molecule.
Fig. 2. is a powder X-ray diffraction pattern of an A-EQT-2HC1 film 1 and of an AEQT film 2.
Fig. 3a is a scanning electron microscope (SEM) picture of an AEQT-2HC1 film.
Fig. 3b is a scanning electron microscope (SEM) picture of an A.EQT film.
Fig. 4a is a schematic cross-section of an OLED device incorporating an AEQT-2HC1 dye salt as the emitting layer.
Fig. 4b is a schematic bottom view of a substrate showing four device areas.
3 Fig. 5a is a plot of e lectro luminescence versus drive voltage for the OLED device shown in Fig. 4.
Fig. 5b is a plot of current versus drive voltage for the OLED device shown in Fig. 4.
Fig. Sc is a plot of the electroluminescence spectrum for the OLED device shown in Fig. 4.
Fig. 6. is a perylene derivative modified to contain four substituents.
DETAILED DESCRIPTION OF THE INVENTION is The invention converts a dye into an ionic salt and uses the salt as an emitting or charge transport layer in an OLED DEVICE. An oligothiophene dye, based on a quaterthiophene oligomer was modified to include two ethylamino terminal groups (ionizable substituents). A schematic representation of the [5,51 1 1 -bis(aminoethyl) -2,21:5',2'':5' t 21 1 1 - quaterthiophene (AEQT) I molecule can be seen in Fig. Ia. By reacting AEQT with hydrochloric acid (HC1), the neutral amino groups (-NH2) become positively charged (-NH3'). To balance the charge, two chloride anions (Cl-) form ionic bonds with the corresponding ammonium cations (-NH3+). The resulting chloride salt C2oH22S4N2Cl2 or AEQT-2HC1 (Fig. 1b) is the compound used as an emitting layer in an OLED DEVICE.
Deposition of the material as a thin film is accomplished by various inexpensive, low temperature methods such as spin-coating, or thermal evaporation. In this case a single-source, thermal ablation technique was employed for the deposition of nominally amorphous thin films. The powder X-ray diffraction pattern (as shown at 1 in Fig 2) of an as-deposited films wis almost featureless, indicating an amorphous or very fine grained film.
The same pattern was obtained after thermal annealing at 901C and 135'C.
Presumably, this is because the molecules in the salt interact via strong ionic interactions, as well as through van der Waals forces.
The stronger bonding is expected to impede rearrangement of the dye molecules during and after thin film deposition. For comparison, the AEQT dye was evaporated without converting it to a salt. As shown at 2 in Fig.
2, the film is crystalline and well ordered, even without annealing. In fact, attempts to make OLEDs using such films failed. This was due to the 4 granular nature of these crystalline f ilms which could not be properly covered with a top metal electrode, thereby producing inhomogeneous, f ields and electrically shorted devices.
To further establish the ability of the method of the invention to provide amorphous films, scanning electron microscopy (SEM) was used to study the morphological properties of the films. As shown, in Fig. 3a, AEQT-2HC1 films have a very homogeneous and fine grained k -50 nm) structure that is ideal for devices. on the other hand, AEQT films have very irregular surfaces with big grain sizes (-500 nm), making them inappropriate for device fabrication (Fig. 3b).
The structure of a typical OLED DEVICE using a dye salt, as prepared in accord with the invention, is shown in Fig. 4. As a substrate, an optically smooth quartz substrate I was used. A transparent anode comprised a 1500 Angstroms thick layer 2 of indium tin oxide (ITO), that was evapgrated on top of the substrate. A 1200 Angstroms thick silicon dioxide layer 3 was then evaporated through a contact mask in order to define four device areas 4 on top of the ITO layer 2 (shown in Fig. 4b). The emitting layer 5, consisting of the C20H22S4NCl, salt, was deposited next using the single source thermal ablation technique (2400 Angstroms). This was followed by thermal annealing of the samples at 900C for 15 minutes and at 1350C for 2 minutes.
Next a thin layer of the electron transporting agent OXD7 6 was thermally deposited (300 Angstroms) and finally, the device was completed by thermally depositing the cathode. The latter consisted of a magnesiumsilver alloy (25:1) 7, which provides for a low work-function cathode, capped by 1200 Angstroms of pure silver 8 to inhibit air oxidation. The deposition of the OXD7 and of the cathode were performed in a vacuum system by thermal evaporation.
When a voltage 9 is applied across the device, green electroluminescence is readily observed under normal lighting conditions and at room temperature. Device characterization data of this device is shown in Fig. 5. Although unoptimized, the device exhibits low turn-on voltages (less than 9 V) and a high efficiency of 0.25 lm/W.
Previous work by Noda et al. on thin semiconducting f ilms of oligothiophenes yielded devices with inferior efficiencies (10' to 10' lm/W) due to the fact that such films were well ordered and crystalline. By using triphenyl-amino substituted quaterthiophenes to reduce crystallinity, higher efficiencies of 0.03 lm/W were obtained (see Noda et al., Adv.
Materials, Vol. 9, p 720 (1997)). Those reported efficiencies are lower, however, than the efficiencies exhibited by devices made in accord with the invention hereof.
The foregoing device description is only illustrative of the invention. The technique can be extended to hole and electron transport layers of an OLED DEVICE which includes similar organic molecules to those found in the emitting layer and which are also prone to crystallization. In typical OLED devices, either a single charge transport layer is used (electron or hole transporting) or both may be used to enhance charge injection into the organic emission layer.
In summary, instead of using a neutral dye molecule (D), the invention modifies a dye during its synthesis to contain ionizable substituents (A) to give (D-A). An ionic salt (DA X- or DA- X) of the dye is then synthesized by application of an appropriate reactant which contains charge balancing ions (X). When deposited in the form of films, the ionic salts are typically amorphous as opposed to the crystalline f ilms of the neutral dye. In addition, the ionic salt f ilms remain amorphous even when heated to higher temperatures (indicating thermal stability). These ionic salts are used as the emitting layer in OLED devices, which are more efficient and robust than the corresponding neutral dye devices.
Various alternatives can be devised by modifying the components of the (DA X-) dye salt. The most important modification is the appropriate selection of different dyes (D) that define the emission properties of the device (color, intensity). Potential candidates, for example, include derivatives of the tolan, thioxanthone, coumarin, rhodamine and perylene families and the present invention is intended to embrace all such alternatives. This allows preparation of devices with different colors and enables realization of a full color display.
Other factors that can be modified include the use of different ionic substituents (A) and charge balancing ions (X). The charge balancing ion can be either an organic or an inorganic entity. The number of ionic substituents (A) attached to a molecule is also important in the glass forming properties of the resulting films. Since it is believed that the ionic forces present in the salt are responsible for the lack of crystallinity, then by using a larger number of ionic substituents (A), 6 more thermally stable films can be formed. An example is given Fig. 6, in which a perylene derivative has been modified to contain four substituents, to form a (D-A4) X-4 salt.
It should be understood that the foregoing description is only illustrative of the invention. Various alternatives and modifications can be devised by those skilled in the art without departing from the invention. Accordingly, the present invention is intended to embrace all such alternatives, modifications and variances which fall within the scope of the appended claims.
7
Claims (1)
1. An electrolumine scent device comprising: an anode, a cathode and an emitting layer disposed between said anode and said cathode, said emitting layer comprising an organic dye salt material that includes an organic dye containing an ionizable substituent and a counterion to balance a charge of the organic dye.
2. The device of claim 1 wherein said organic dye salt material fluoresces in the visible range.
3. The device of claim 1 wherein said organic dye is selected from the group consisting of: derivatives of tolan, thioxanthone, coumarin, perylene, pyrene, oxadiazole, polyenes, oligothiophenes, oligophenylenes, phenylene vinylenes, thiophene vinylenes and mixtures thereof.
4. The device of claim 1 wherein said organic dye is cluaterthiophene.
5. The device of claim 1 wherein said ionizable substituent is selected from functional groups consisting of: amino-, hydroxy-, oxo-, nitro-, sulfo-, carboxy-, phospho-. 6. The device of claim 1 wherein said ionizable substituent is an 25 alkylamine. 7. The device of claim 1 wherein said ionizable substituent is ethylamine. 8. The device of claim 1 wherein said counterion is selected from the group 30 consisting of: halides, alkali metal cations, alkaline earth cations. 9. The device of claim 1 wherein said counterion is an organic ion containing an ionized form of one or more following functional groups: amino-, hydroxy-, oxo-, nitro-, sulfo-, carboxy-, phospho-. 35 10. An electroluminescent device comprising: an anode, a cathode, an emitting layer, and at least one charge transport layer disposed adjacent to said emitting layer and between said anode and said cathode and comprising an organic dye salt material that includes an organic dye containing an ionizable substituent and a counterion to balance a charge of 40 the organic dye.
8 11. The device of claim 10 wherein said charge transport layer includes molecules selected from the group consisting of: derivatives of tolan, thioxanthone, coumarin, perylene, pyrene, oxadiazole, polyenes, oligothiophenes, oligophenylenes, phenylene vinylenes, thiophene vinylenes and mixtures thereof.
12. The device of claim 10 wherein said ionizable substituent is selected from functional groups consisting of: amino-, hydroxy-, oxo-, nitro-, sulfo-, carboxy-, phospho-.
13. The device of claim 10 wherein said ionizable substituent is an alkylamine.
14. The device of claim 10 wherein said ionizable substituent is is ethylamine.
15. The device of claim 10 wherein said counterion is selected from the group consisting of: halides, alkali metal cations, alkaline earth cations.
16. The device of claim 10 wherein said counterion is an organic ion containing the ionized form of one or more of the following functional groups: amino-, hydroxy-, oxo-, nitro-, sulfo-, carboxy-, phospho-.