GB2196988A - Electrolytic bath for forming a glossy black chromium coating layer - Google Patents
Electrolytic bath for forming a glossy black chromium coating layerInfo
- Publication number
- GB2196988A GB2196988A GB08724086A GB8724086A GB2196988A GB 2196988 A GB2196988 A GB 2196988A GB 08724086 A GB08724086 A GB 08724086A GB 8724086 A GB8724086 A GB 8724086A GB 2196988 A GB2196988 A GB 2196988A
- Authority
- GB
- United Kingdom
- Prior art keywords
- concentration
- coating layer
- electrolytic bath
- chromium coating
- forming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An electrolytic bath for the formation of a glossy black chromium coating layer on a substrate of iron, steel, nonferrous heavy metal or alloys thereof comprises a concentration between 300 and 440 g/l of chromic anhydride, 10 and 30 g/l of phosphate ions and nitrate ions of which the concentration corresponds to the presence of ammonium nitrate in a concentration comprised between 1 and 2 g/l, and optionally a concentration of baryum carbonate comprised between 5 and 8 g/l and a concentration of fluoride ions comprised between 5 and 20 mg/l.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
HU70286A HU198970B (en) | 1986-02-19 | 1986-02-19 | Electrolysis bath for making bright, black chromium plating |
Publications (3)
Publication Number | Publication Date |
---|---|
GB8724086D0 GB8724086D0 (en) | 1987-11-18 |
GB2196988A true GB2196988A (en) | 1988-05-11 |
GB2196988B GB2196988B (en) | 1990-05-02 |
Family
ID=10950923
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB8724086A Expired - Fee Related GB2196988B (en) | 1986-02-19 | 1987-02-19 | Electrolytic bath for forming a glossy black chromium coating |
Country Status (5)
Country | Link |
---|---|
AU (1) | AU7036087A (en) |
DE (1) | DE3790088D2 (en) |
GB (1) | GB2196988B (en) |
HU (1) | HU198970B (en) |
WO (1) | WO1987005056A1 (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2230275A (en) * | 1989-02-27 | 1990-10-17 | Omi Int Corp | Conversion composition and process |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
AU611957B2 (en) * | 1988-10-13 | 1991-06-27 | Council Of Scientific And Industrial Research | Improved black chromium plating bath useful for solar selective coatings |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB1449446A (en) * | 1974-04-05 | 1976-09-15 | Kampschulte & Cie Dr W | Electrolysis baths |
DE1621060C3 (en) * | 1966-04-08 | 1978-01-19 | Du Pont | AQUATIC BATH FOR GALVANIC DEPOSITION OF BLACK CHROME COATINGS |
GB2024863A (en) * | 1978-06-02 | 1980-01-16 | Bnf Metals Tech Centre | Black chromium deposits |
SU827606A1 (en) * | 1978-06-19 | 1981-05-07 | Предприятие П/Я Р-6762 | Electrolyte for precipitating black chrome coatings |
-
1986
- 1986-02-19 HU HU70286A patent/HU198970B/en not_active IP Right Cessation
-
1987
- 1987-02-19 WO PCT/HU1987/000006 patent/WO1987005056A1/en active Application Filing
- 1987-02-19 DE DE87HU8700006T patent/DE3790088D2/en not_active Expired
- 1987-02-19 GB GB8724086A patent/GB2196988B/en not_active Expired - Fee Related
- 1987-02-19 AU AU70360/87A patent/AU7036087A/en not_active Abandoned
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE1621060C3 (en) * | 1966-04-08 | 1978-01-19 | Du Pont | AQUATIC BATH FOR GALVANIC DEPOSITION OF BLACK CHROME COATINGS |
GB1449446A (en) * | 1974-04-05 | 1976-09-15 | Kampschulte & Cie Dr W | Electrolysis baths |
GB2024863A (en) * | 1978-06-02 | 1980-01-16 | Bnf Metals Tech Centre | Black chromium deposits |
SU827606A1 (en) * | 1978-06-19 | 1981-05-07 | Предприятие П/Я Р-6762 | Electrolyte for precipitating black chrome coatings |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
GB2230275A (en) * | 1989-02-27 | 1990-10-17 | Omi Int Corp | Conversion composition and process |
Also Published As
Publication number | Publication date |
---|---|
DE3790088D2 (en) | 1988-08-25 |
AU7036087A (en) | 1987-09-09 |
GB2196988B (en) | 1990-05-02 |
GB8724086D0 (en) | 1987-11-18 |
WO1987005056A1 (en) | 1987-08-27 |
HU198970B (en) | 1989-12-28 |
HUT43121A (en) | 1987-09-28 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CA2360633A1 (en) | Method of treating metals using amino silanes and multi-silyl-functional silanes in admixture | |
TW374096B (en) | Process for hot dip-coating a steel material with a molten aluminum alloy according to an one-stage metal alloy coating method using a flux | |
TW276273B (en) | ||
HK1007576A1 (en) | Zinc phosphate conversion coating composition and process | |
ES8302794A1 (en) | Method of phosphating metals, as well as its use in the electrodip painting pretreatment. | |
AU2309300A (en) | Method of treating metals using ureido silanes and multi-silyl-functional silanes in admixture | |
DE3173781D1 (en) | Method of phosphating metals | |
NO173454C (en) | Ferrous, ferritic dip-metal strip and method of continuous dip-metallization of a ferritic, chromium-alloy steel strip with aluminum or aluminum alloy | |
BR9004439A (en) | PROCESSING FOR PROTECTIVE COATING OF A STEEL SURFACE COATED WITH ZINC OR COATED WITH A ZINC ALLOY AND PROCESS FOR FORMING A CONVERSION COATING CONTAINING ZINC PHOSPHATES, MANGANES AND NICKELS | |
ES8505733A1 (en) | Process for activating the formation of a phosphate layer on metals, and means for carrying out the process. | |
ES8305052A1 (en) | Method of phosphating metallic surfaces. | |
SE8503251D0 (en) | HOT-GALVANIZED STEEL PRODUCT, NOTABLY INTENDED TO BE PHOSPHATED, AND METHOD FOR PREPARING SUCH A PRODUCT | |
ZA867903B (en) | A process for phosphating electrolytically zinc-coated metal goods | |
GB2196988A (en) | Electrolytic bath for forming a glossy black chromium coating layer | |
Magyar et al. | Electrolytic Bath for Forming a Glossy Black Chromium Coating Layer | |
BR8602096A (en) | WATER COMPOSITION USED IN THE CONDITIONING OF A METALLIC SURFACE AND PROCESS FOR PHOSPHATIZATION OF A METALLIC SURFACE | |
GB1396898A (en) | Method for making ferrous metal having highly improved resistances to corrosion at elevated temperatures and to oxidization | |
Poll | Mixed Metal Pretreatment | |
GB8828559D0 (en) | Composition & method for coating metal surfaces | |
Catuneanu et al. | Necessity of Reducing Refined Ferrochromium Consumption in Steel Production.(Retroactive Coverage) | |
Krepski | The influence of chemical pretreatment on zinc consumption during hot dip galvanizing | |
Hayashi et al. | Development of Corrosion Resistant Tinplate DI Cans With an Improved Conversion Coating Film | |
JPS5623293A (en) | Electroplating solution for forming zn-ti alloy plating film on iron and steel surface | |
Hahn et al. | Effect of surface texture and strain on painted appearance of zinc-coated steel | |
JPS56116883A (en) | Enhancement of phosphate treatment property of cold rolled steel plate |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PCNP | Patent ceased through non-payment of renewal fee |