GB2158462A - Abrasive resistant white cast iron - Google Patents
Abrasive resistant white cast ironInfo
- Publication number
- GB2158462A GB2158462A GB08515282A GB8515282A GB2158462A GB 2158462 A GB2158462 A GB 2158462A GB 08515282 A GB08515282 A GB 08515282A GB 8515282 A GB8515282 A GB 8515282A GB 2158462 A GB2158462 A GB 2158462A
- Authority
- GB
- United Kingdom
- Prior art keywords
- cast iron
- white cast
- melt
- globules
- abrasive resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A white cast iron having toughness, high tensile strength and abrasion resistance containing 0.01% to 4.0% boron in an iron-carbon alloy with the carbides in the form of globules and of an average size less than 4 microns. This white cast iron is produced by incorporating the boron in the composition to form a melt, super cooling the melt while liquid to at least 5<o>F below the equilibrium solidification temperature between 2200<o>F to 2400<o>F and then solidifying the melt to produce the globules of carbides uniformly dispersed and having a size much smaller than the size of the carbide particles of conventional cast iron.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/US1983/001656 WO1985001962A1 (en) | 1983-10-24 | 1983-10-24 | Abrasive resistant white cast iron |
Publications (3)
Publication Number | Publication Date |
---|---|
GB8515282D0 GB8515282D0 (en) | 1985-07-17 |
GB2158462A true GB2158462A (en) | 1985-11-13 |
GB2158462B GB2158462B (en) | 1988-02-24 |
Family
ID=22175514
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB08515282A Expired GB2158462B (en) | 1983-10-24 | 1983-10-24 | Abrasive resistant white cast iron |
Country Status (7)
Country | Link |
---|---|
EP (1) | EP0159981A4 (en) |
JP (1) | JPS60501958A (en) |
CH (1) | CH666908A5 (en) |
DE (1) | DE3390548T1 (en) |
GB (1) | GB2158462B (en) |
NL (1) | NL8320359A (en) |
WO (1) | WO1985001962A1 (en) |
Families Citing this family (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1994013847A1 (en) * | 1992-12-15 | 1994-06-23 | Kabushiki Kaisha Toshiba | Method of manufacturing cast iron of high strength and low expansion |
DE4409278A1 (en) * | 1994-03-18 | 1995-09-21 | Klein Schanzlin & Becker Ag | Corrosion and wear resistant chilled cast iron |
ES2111405T3 (en) * | 1994-05-17 | 1998-03-01 | Ksb Ag | HARD CAST IRON WITH HIGH CORROSION AND WEAR RESISTANCE. |
DE19721477A1 (en) | 1997-05-23 | 1998-11-26 | Abb Patent Gmbh | Microbial membrane reactor for use in flow systems |
DE19901170B4 (en) * | 1998-10-21 | 2006-11-23 | Reiloy Metall Gmbh | Use of an iron base age alloy |
CN106222531B (en) * | 2016-07-24 | 2017-11-21 | 莎车县军辉机械有限公司 | A kind of boron manganese chromium wear resistance castings and its manufacturing process |
CN114318116A (en) * | 2021-12-08 | 2022-04-12 | 河北澳金机械设备有限公司 | Composition improvement of KmTBCr26 high-chromium cast iron |
Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2978320A (en) * | 1958-12-29 | 1961-04-04 | Gen Motors Corp | Method for producing a high strength ferrous metal |
US3334996A (en) * | 1966-12-13 | 1967-08-08 | Xaloy Inc | Hard, wear-resistant ferrous alloy |
NL6917161A (en) * | 1969-09-15 | 1971-03-17 | ||
US3909252A (en) * | 1973-11-01 | 1975-09-30 | Suzuki Motor Co | Wear-resistant cast iron for sliding surfaces |
JPS53140218A (en) * | 1977-05-13 | 1978-12-07 | Mitsubishi Heavy Ind Ltd | Wear resistant white pig iron |
US4221612A (en) * | 1977-10-14 | 1980-09-09 | Acieries Thome Cromback | Grinding members |
JPS5693859A (en) * | 1979-12-28 | 1981-07-29 | Komatsu Ltd | Ball alloy for grinding |
SU850719A1 (en) * | 1978-09-29 | 1981-07-30 | Всесоюзный Научно-Исследователь-Ский И Проектно-Технологическийинститут Угольного Машиностроения | Cast iron |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
SU168322A1 (en) * | 1963-06-11 | 1965-02-18 | Ростовский Дону научно исследовательский институт технологии | FLOATS FOR TUNING? SOI) ZILYAN KATtJi'iHO-.} -. if ^ '"TEKHK ^ TLi'A' ^ '-ag?' 'I'; ': T;: L I. YANMA .. * lv" "zhl ^ chg * in:" MA: M. ^ ^^ - ^ f ^^^ The proposed alloy makes it possible to adjust the mechanical properties of the deposited layer by additionally doping with tungsten during the deposition process. It has a high elasticity that allows for significant deformation of the deposited parts during manufacture and operation. 10. Invention 1. A welding alloy containing chromium and manganese. and silicon, characterized in that, 15 in order to increase the hardness and wear resistance of the weldments, its composition includes (in o / o): carbon 3 , 0-3.7; manganese, 5.5-6.5; silicon; 1.8-2.2; chromium 22-26; boron 0.4–0.6; titanium 0.25–0.35; tungsten 2-10; 20 sulfur to 0.08; phosphorus to 0.08; iron - the rest of the alloy. The alloy according to claim 1, characterized in that, in order to improve the mechanical properties, tungsten is introduced directly in the process 25 of surfacing. |
JPS5419371B2 (en) * | 1973-02-15 | 1979-07-14 | ||
DE2428822A1 (en) * | 1974-06-14 | 1976-01-02 | Goetzewerke | SPHERICAL CAST IRON ALLOY WITH INCREASED WEAR RESISTANCE |
JPS5751241A (en) * | 1980-09-12 | 1982-03-26 | Komatsu Ltd | Ball alloy for pulverization |
SU954481A1 (en) * | 1981-01-12 | 1982-08-30 | Гомельский Филиал Белорусского Ордена Трудового Красного Знамени Политехнического Института | Wear-resistant white iron |
GB2134542B (en) * | 1982-07-19 | 1987-06-03 | Giw Ind Inc | Abrasive resistant white cast iron |
ZA844074B (en) * | 1983-05-30 | 1986-04-30 | Vickers Australia Ltd | Abrasion resistant materials |
-
1983
- 1983-10-24 EP EP19830903718 patent/EP0159981A4/en not_active Withdrawn
- 1983-10-24 GB GB08515282A patent/GB2158462B/en not_active Expired
- 1983-10-24 CH CH2839/85A patent/CH666908A5/en not_active IP Right Cessation
- 1983-10-24 DE DE19833390548 patent/DE3390548T1/en active Granted
- 1983-10-24 JP JP58503752A patent/JPS60501958A/en active Pending
- 1983-10-24 NL NL8320359A patent/NL8320359A/en not_active Application Discontinuation
- 1983-10-24 WO PCT/US1983/001656 patent/WO1985001962A1/en not_active Application Discontinuation
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2978320A (en) * | 1958-12-29 | 1961-04-04 | Gen Motors Corp | Method for producing a high strength ferrous metal |
US3334996A (en) * | 1966-12-13 | 1967-08-08 | Xaloy Inc | Hard, wear-resistant ferrous alloy |
NL6917161A (en) * | 1969-09-15 | 1971-03-17 | ||
US3909252A (en) * | 1973-11-01 | 1975-09-30 | Suzuki Motor Co | Wear-resistant cast iron for sliding surfaces |
JPS53140218A (en) * | 1977-05-13 | 1978-12-07 | Mitsubishi Heavy Ind Ltd | Wear resistant white pig iron |
US4221612A (en) * | 1977-10-14 | 1980-09-09 | Acieries Thome Cromback | Grinding members |
SU850719A1 (en) * | 1978-09-29 | 1981-07-30 | Всесоюзный Научно-Исследователь-Ский И Проектно-Технологическийинститут Угольного Машиностроения | Cast iron |
JPS5693859A (en) * | 1979-12-28 | 1981-07-29 | Komatsu Ltd | Ball alloy for grinding |
Also Published As
Publication number | Publication date |
---|---|
JPS60501958A (en) | 1985-11-14 |
GB2158462B (en) | 1988-02-24 |
EP0159981A1 (en) | 1985-11-06 |
GB8515282D0 (en) | 1985-07-17 |
DE3390548T1 (en) | 1985-11-28 |
DE3390548C2 (en) | 1988-12-01 |
WO1985001962A1 (en) | 1985-05-09 |
NL8320359A (en) | 1985-09-02 |
EP0159981A4 (en) | 1987-04-29 |
CH666908A5 (en) | 1988-08-31 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB2134542A (en) | Abrasive resistant white cast iron | |
GB2158462A (en) | Abrasive resistant white cast iron | |
US3367395A (en) | Method and apparatus for treating molten metals | |
RU95113726A (en) | CASTING FORM, IN PARTICULAR CRYSTALIZER FOR INSTALLATION OF CONTINUOUS CASTING | |
Hrusovsky et al. | Effect of composition on solidification of compacted graphite iron | |
JPS55145158A (en) | Free cutting bearing steel and its manufacture | |
Thyberg | Hard Castings of Grey and Ductile Iron: Causes and Preventive Measures | |
Sykora | Pearlitic Grey Cast Iron with Foliated Graphite and Copper-Alloyed Nodular Cast Iron | |
Serafino | A New View on Inoculation | |
Zhurakovskii et al. | The Effect of Boron and Calcium on the Graphitization of Hypereutectoid Silicon Steel | |
Patterson et al. | Fifty years of progress in cast iron inoculation | |
SU1468953A1 (en) | Iron alloying composition | |
Bauer et al. | The Relationship Between Attainable Mechanical Properties and the Morphology of Cast Iron With Lamellar Graphite(Grey Cast Iron) | |
Fidos | Effect of Composition and Cooling Rate on Graphite Nodule Morphology in Spheroidal Graphite Iron | |
Moore | Engineering Cast Iron | |
JPS57123951A (en) | Aluminum alloy containing dispersed graphite and lead | |
Kozlov et al. | Deformation of Cast Iron With Spheroidal Graphite | |
Kaplunovskii | Process Improvements in Cupola Melting of Cast Iron | |
Gerchikov et al. | Effect of the Quality of Cast Iron on the Wear Resistance of the Basic Parts of Lathes | |
Berns | Ferrous Materials With Hard Phases and Increased Resistance to Wear | |
Singh | An investigation into the effect of residual lead in gray iron castings | |
Khusnutdinov et al. | Factors Determining the Shape of Graphite Inclusions in Refined Fe--C--Si Alloys | |
Pelikh et al. | A Melting Process and Certain Properties of High-Manganese Alloyed Bronze | |
Kimstach et al. | Microdistribution of Magnesium in the Structure of Nodular Iron | |
Rohrig | Cast Iron With Vermicular Graphite--Processing, Properties, Applications |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PCNP | Patent ceased through non-payment of renewal fee |
Effective date: 19941024 |