GB207677A - Method of making refractory articles - Google Patents

Method of making refractory articles

Info

Publication number
GB207677A
GB207677A GB2894822A GB2894822A GB207677A GB 207677 A GB207677 A GB 207677A GB 2894822 A GB2894822 A GB 2894822A GB 2894822 A GB2894822 A GB 2894822A GB 207677 A GB207677 A GB 207677A
Authority
GB
United Kingdom
Prior art keywords
refractory
per cent
graphite
binder
heated
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB2894822A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BUFFALO REFRACTORY CORP
Original Assignee
BUFFALO REFRACTORY CORP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to NL13751D priority Critical patent/NL13751C/xx
Application filed by BUFFALO REFRACTORY CORP filed Critical BUFFALO REFRACTORY CORP
Priority to GB2894822A priority patent/GB207677A/en
Priority to DEB106928D priority patent/DE405236C/en
Publication of GB207677A publication Critical patent/GB207677A/en
Expired legal-status Critical Current

Abstract

207,677. Marks, E. C. R., (Buffalo Refractory Corporation). Oct. 24, 1922. Refractory substances containing graphite.-A mixture of graphite, a refractory electric furnace product, and a carbonizing binder, with or without a solid flux, is moulded and heated to carbonize the binder; the article is then dipped into a liquid flux, such as sodium borate or sodium silicate, and heated to a temperature of 1200‹ F. The refractory electric furnace product may be silicon carbide, fused magnesite, fused alumina, or fused silica. Feldspar may be used as the solid flux. The carbonizing binder may be molasses, pitch, or tar. The proportion of the ingredients may be 10-55 per cent of graphite, 20-80 per cent of refractory product, and up to 25 per cent of fluxing agent.
GB2894822A 1922-10-24 1922-10-24 Method of making refractory articles Expired GB207677A (en)

Priority Applications (3)

Application Number Priority Date Filing Date Title
NL13751D NL13751C (en) 1922-10-24
GB2894822A GB207677A (en) 1922-10-24 1922-10-24 Method of making refractory articles
DEB106928D DE405236C (en) 1922-10-24 1922-10-28 Method of manufacturing refractory bodies

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
GB2894822A GB207677A (en) 1922-10-24 1922-10-24 Method of making refractory articles

Publications (1)

Publication Number Publication Date
GB207677A true GB207677A (en) 1923-12-06

Family

ID=10283760

Family Applications (1)

Application Number Title Priority Date Filing Date
GB2894822A Expired GB207677A (en) 1922-10-24 1922-10-24 Method of making refractory articles

Country Status (2)

Country Link
GB (1) GB207677A (en)
NL (1) NL13751C (en)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2164301A1 (en) * 1970-12-25 1972-08-17 Nippon Crucible Co Refractory material based on graphite-aluminum oxide-silicon carbide

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE2164301A1 (en) * 1970-12-25 1972-08-17 Nippon Crucible Co Refractory material based on graphite-aluminum oxide-silicon carbide

Also Published As

Publication number Publication date
NL13751C (en)

Similar Documents

Publication Publication Date Title
US2118143A (en) Refractory material
GB207677A (en) Method of making refractory articles
Brown et al. Constitution of Copper‐Red Glazes
US3079266A (en) Process for the manufacture of refractory materials and resultant product
ES287794A1 (en) A procedure for the production of a refractory material (Machine-translation by Google Translate, not legally binding)
GB176437A (en) Improvements in non-recrystallized refractory composition
US2237485A (en) Process for the deoxidation and degasification of steel
GB393283A (en) Improvements in or relating to non-metallic resistors and methods of making them
Shute et al. Effect of iron oxide on melting of glass
US1491567A (en) Refractory product
GB492215A (en) Improvements in or relating to refractory articles
GB462966A (en) Improvements in and relating to abrasive articles and the manufacture thereof
GB519885A (en) Improvements in the manufacture of ceramic articles
GB253184A (en) Improvements in the manufacture of pottery or the like
GB348149A (en) Improved manufacture of graphitic refractories
GB137419A (en) A glazing cement for use in fireclay retorts and furnaces
GB573410A (en) An improved manufacture of refractories
SU104247A1 (en) Glaze to prevent burnout of graphite from graphite crucibles, molds, etc. products
US1609416A (en) Method of making brick and other burned-clay products
GB190408859A (en) Improved Process of Making a Grinding, Polishing or Smoothing Substance or a Substance Refractory to Heat.
GB316129A (en) Improvements in or relating to the manufacture of refractory articles
GB191201961A (en) Improvements in Refractory Blocks and Bricks.
GB176436A (en) Improvements in refractory composition
DE656961C (en) Lining of rotary tube furnaces for burning cement or lime
GB462866A (en) Improvements relating to refractory products