GB2036053A - Silicone Resin Coating Composition - Google Patents
Silicone Resin Coating Composition Download PDFInfo
- Publication number
- GB2036053A GB2036053A GB7939488A GB7939488A GB2036053A GB 2036053 A GB2036053 A GB 2036053A GB 7939488 A GB7939488 A GB 7939488A GB 7939488 A GB7939488 A GB 7939488A GB 2036053 A GB2036053 A GB 2036053A
- Authority
- GB
- United Kingdom
- Prior art keywords
- composition
- article
- weight percent
- colloidal silica
- coating composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Aqueous coating compositions comprise dispersions of colloidal silica in alcohol/water solutions containing partially condensed silanols of formula RSi(OH)3, where R is C1-C3 alkyl, at least 70% of R being CH3, and have pH values between 7.1 and 7.8. The compositions provide abrasion- resistant coatings on substrates. They are prepared by hydrolyzing an alkyltrialkoxysilane or an aryltrialkoxysilane in an aqueous colloidal silica dispersion with suitable adjustment of the pH if necessary.
Description
SPECIFICATION
Silicone Resin Coating Composition
This invention relates to a protective coating composition. More particularly, it relates to a silicone resin coating composition which, when applied to a substrate, forms a protective, abrasion-resistant coating thereof.
Recently, the substitution of glass glazing with transparent materials which do not shatter or are more resistant to shattering than glass, has become widespread. For example, transparent glazing made from synthetic organic polymers is now utilized in public transportation vehicles, such as trains, buses, taxis and airplanes. Lenses, such as for eye glasses and other optical instruments, as well as glazing for large buildings, also employ shatter-resistant transparent plastics.
The lighter weight of these plastics in comparison to glass is a further advantage, especially in the transportation industry where the weight of the vehicle is a major factor in its fuel economy.
While transparent plastics provide the major advantage of being more resistant to shattering and lighter than glass, a serious drawback lies in the ease with which these plastics mar and scratch, due to everyday contact with abrasives, such as dust, cleaning equipment and/or ordinary weathering. Continuous scratching and marring results in impaired visibility and poor aesthetics, and oftentimes requires replacement of the glazing or lens or the like.
One of the most promising and widely used transparent plastics for glazing is polycarbonate, such as that known as Lexan, sold by General
Electric Company. It is a tough material, having high impact strength, high heat deflection temperature, good dimensional stability, as well as being self-extinguishing, and is easily fabricated.
Attempts have been made to improve the abrasion resistance of transparent plastics. For example, scratch-resistant coatings formed from mixtures of silica, such as colloidal silica or silica gel, and hydrolyzable silanes in a hydrolysis medium, such as alcohol and water, are known.
U.S. Patents 3,708,225, 3,986,997 and 3,976,497, for example, describe such compositions.
While the afore-mentioned coating formulations have been found acceptable, there still remains room for improvement. For example, the coating compositions of this invention provide coatings having improved resistance to moisture and humidity and ultraviolet light, in comparison with those coatings provided in accordance with
U.S. 3,986,997. Moreover, it has been found herein that in direct contrast to the teachings of
U.S. 3,986,997, the basic coating compositions of this invention having a pH in the range of from 7.1-7.8, do not immediately gel and provide excellent coatings having good properties on solid substrates.
Protective coatings for metals, bright or dull, are also needed. For example, bright metallized plastics, wherein small amounts of metal are vacuum sputtered or vacuum metallized over the plastic, now popular with the auto industry because of their light weight, need protective layers to prevent scratching and marring of the brilliant surface. Metal wheel covers (hub caps) also require protective coatings for their preservation and lasting beauty.
The invention is accomplished herein by a coating composition comprising a dispersion of colloidal silica in an aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH)3, wherein R is selected from the group consisting of alkyl having from 1 to 3 carbon atoms and aryl, at least 70 weight percent of the silanol being CH3-Si(OH)3, said composition containing 10 to 50 weight percent solids, said solids consisting essentially of 10 to 70 weight percent colloidal silica and 30 to 90 weight percent of the partial condensate, said composition having a pH from 7.1 to about 7.8.
The coating compositions of this invention are prepared by hydrolyzing a trialkoxysilane or a mixture of trialkoxysilanes of the formula
RSi(OR)3, wherein R is alkyl of from 1 to 3 carbons or aryl, such as phenyl, in an aqueous dispersion of colloidal silica.
In the practice of the present invention, suitable aqueous colloidal silica dispersions generally have a particle size of from 5 to 150 millimicrons in diameter. These silica dispersions are well known in the art and commercially available ones include, for example, those sold under the trademarks of Ludox (duPont) and
Nalcoag (Nalco Chemical Co.). Such colloidal silicas are available as both acidic and basic hydrosols. For the purpose of this invention, wherein the pH of the coating compositions is on the basic side, basic colloidal silica sols are preferred. However, acidic colloidal silicas, wherein the pH is adjusted to a basic level, are also contemplated. In addition, it has been found that colloidal silicas having a low alkali content (e.g., Na2O) yield a more stable coating composition.Thus, colloidal silicas having an alkali content of less than 0.35% (calculated as Na2O) have been found to be preferable.
Moreover, colloidal silicas having average particle size of from 10 to 30 millimicrons are also preferred. A particularly preferred aqueous colloidal silica dispersion for the purposes herein is known as Ludox LS, sold by duPont Company.
In accordance with this invention, the aqueous colloidal silica dispersion is added to a solution of a small amount of alkyltriacetoxysilane in alkyltrialkoxysilane or aryltrialkoxysilane. For the
purposes herein, from about 0.07 parts by weight to about 0.1 parts by weight, based on 100 parts by weight of the total composition, of the alkyltriacetoxysilane is used. The temperature of the reaction mixture is maintained at about 200C to about 400C, preferably 200C to about 300C, and most preferably below 250C. It has been found that in about six to eight hours sufficient trialkoxysilane has hydrolyzed so as to reduce the
initial two phase liquid mixture to one liquid phase
in which the now treated silica (i.e., treated by its
admixture with the alkyltrialkoxysilane or
aryltrialkoxysilane) is dispersed.In general, the
hydrolysis reaction is allowed to continue for a total of about 24 to 48 hours, depending upon the desired viscosity of the final product. The more time the hydrolysis reaction is permitted to continue, the higher will be the viscosity of the product. After the hydrolysis has been completed to the desired extent, the solids content is adjusted by the addition of alcohol, preferably isobutanol, to the reaction mixture. Other suitable alcohols for the purposes herein include lower aliphatic alcohols such as methanol, ethanol, propanol, isopropanol, n-butyl alcohol and t-butyl alcohol. Mixtures of such alcohols can be used, too. The solvent system should contain from about 20 to 75 weight percent alcohol to ensure solubility of the partial condensate (siloxanol).
Optionally, additional water-miscible polar solvents, such as acetone, butyl cellosoive and the like in minor amounts, like no more than 20 weight percent of the co-solvent system can also be used. The solids content of the coating compositions of this invention is generally preferred to be in the range of from about 1 8 to 25%, most preferably, about 20% by weight of the total composition. The pH of the resultant coating composition is in the range of from about 7.1 to about 7.8, preferably higher than 7.2. If necessary, dilute base, such as ammonium hydroxide or weak acid, such as acetic acid, can be added to the composition to adjust the final pH to this desired range. At these basic pH's, the compositions are translucent liquids which are stable at room temperature for at least several weeks.When stored at temperatures below about 50C (400 F) the period of stability is increased further.
Additives and other modifying agents, such as thickeners, pigments, dyes, and the like, may be added to the composition at this time. A particularly desirable additive to the coating compositions of this invention has been found to be a small amount of a polysiloxane polyether copolymer. It has been found, and is the subject of another invention disclosed in a copending U.S.
application entitled "Improved Silicone Resin
Coating Composition" (Atty. Docket GE 951(60S1-230) by Robert Bruce Frye, that these polysiloxane polyether copolymers prevent the occurrence of undesirable flowmarks and dirtmarks which sometimes occur with the application of the coating composition onto the substrate. A particularly useful polysiloxane polyether copolymer for the purposes herein is known as SF-1066 and is available from the
General Electric Company. The preparation, further description and structural formulae for these polysiloxane polyether copolymers are found in U.S. Patent No. 3,629,165, incorporated by reference herein.
The alkyltriacetoxysilane is used to buffer the basicity of the initial two liquid phase reaction mixture and thereby also temper the hydrolysis rate. While the use of alkyltriacetoxysilane is preferred herein, glacial acetic acid may be
used in its place, as well as other acids such as organic acids like propionic, butyric, citric, benzoic, formic, oxalic and the like.
Alkyltriacetoxysilanes wherein the alkyl group contains from 1 to 6 carbon atoms can be used, alkyl groups having from 1 to 3 carbon atoms being preferred. Methyltriacetoxysilane is most preferred for the purposes herein.
The silanetriols, RSi(OH)3, hereinbefore mentioned, are formed in situ as a result of the admixture of the corresponding trialkoxysilanes with the aqueous medium, i.e., the aqueous dispersion of colloidal silica. Exemplary trialkoxysilanes are those containing methoxy, ethoxy, isopropoxy and n-butoxy substituents which, upon hydrolysis, generate the silanetriol and further liberate the corresponding alcohol. In this way, at least, a portion of the alcohol content present in the final coating Composition is provided. Of course, if a mixture of trialkoxysilanes is empioyed, as provided for hereinabove, a mixture of different silanetriols, as well as different alcohols, is generated. Upon the generation of the silanetriol or mixtures of silanetriols in the basic aqueous medium, condensation of the hydroxyl substituents to form
bonding occurs.This condensation takes place over a period of time and is not an exhaustive condensation but rather the siloxane retains an appreciable quantity of silicon-bonded hydroxyl groups which render the polymer soluble in the alcohol-water cosolvent. This soluble partial condensate can be characterized as a siloxanol polymer having at least one silicon-bonded hydroxyl group per every three
units.
The non-volatile solids portion of the coating composition herein is a mixture of colloidal silica and the partial condensate (or siloxanol) of a silanol. The major portion or all of the partial condensate or siloxanol is obtained from the condensation of CHSSi(OH)3 and, depending upon the input of ingredients to the hydrolysis reaction, minor portions of partial condensate can be obtained, for example, from the condensation of
CH3Si(OH)3 with C2HsSi(OH)3 or C3H7Si(OH)3;
CH3Si(OH)3 with C6HsSi(OH)3, or even mixtures of the foregoing. For optimum results in the cured coating it is preferred to use all methyltrimethoxysilane (thus generating all monomethylsilanetriol) in preparing the coating compositions herein.In the preferred coating compositions herein the partial condensate is present in an amount of from about 55 to 75 weight percent of the total solids in a cosolvent of alcohol and water, the alcohol comprising from
about 50% to 95% by weight of the cosolvent.
The coating composition of this invention will cure on a substrate at temperatures of, for example, 1 200C without the aid of an added curing catalyst. However, in order to employ more desirable milder curing conditions, buffered latent condensation catalysts can be added. Included in this class of catalysts are alkali metal salts of carboxylic acids, such as sodium acetate, potassium formate and the like. Amine carboxylates, such as dimethylamine acetate, ethanolamine acetate, dimethylaniline formate and the like, quaternary ammonium carboxylates such as tetramethylammonium acetate, benzyltrimethylammonium acetate, metal carboxylates, like tin octoate and amines such as triethylamine, triethanolamine, pyridine and the like are also contemplated curing catalysts herein.
Alkali hydroxides, like sodium hydroxide and ammonium hydroxide can also be used as curing catalysts herein. Moreover, typical commercially available colloidal silica, especially those having a basic pH, contain free alkali metal base and alkali metal carboxylate catalysts will be generated in situ during the hydrolysis reaction herein.
The amount of curing catalyst can be varied within a wide range, depending upon the desired curing conditions. However, in general, catalyst in the amounts of from about 0.05 to about 0.5 weight percent, preferably about 0.1 weight percent, of the composition can be used.
Compositions containing catalysts in these amounts can be cured on a solid substrate in a relatively short time at temperatures in the range of from about 750--1 500C to provide a transparent abrasion resistant surface coating.
The coating compositions of the present invention can be applied to a variety of solid substrates by conventional methods, such as flowing, spraying or dipping, to form a continuous surface film. Substrates which are especially contemplated herein are transparent, as well as non-transparent, plastics and metals. More particularly, these plastics are synthetic organic polymeric substrates such as acrylic polymers, like poly(methylmethacrylate), polyesters, such as poly(ethylene terephthalate), poly(butylene terephthalate), etc., polyamides, polyimides, acrylonitrile-styrene copolymers styrene-acrylonitrile-butadiene copolymers, polyvinyl chloride, butyrates, polyethylene and the like. As noted above, the coating compositions of this invention are especially useful as coatings for polycarbonates, such as those polycarbonates known as Lexan, sold by General Electric Company.
The metal substrates on which the present protective coatings are utilized include bright and dull metals like aluminum and bright metallized surfaces like sputtered chromium alloy. Other solid substrates contemplated herein include wood, painted surfaces, leather, glass, ceramics and textiles.
By choice of the proper formulation, application conditions and pretreatment, including the use of primers, of the substrate, the coatings can be adhered to substantially all solid substrates. A hard coating having all of the aforementioned characteristics and advantages is obtained by the removal of the soivent and volatile materials. The coating composition will air-dry to a tack-free condition, but heating in the range of 750C to 2000C is necessary to obtain condensation of residual silanols in the partial condensate. This final cure results in the formation of silsesquioxane (RSiO3/2). In the finished cured coating the ratio of Rio3/2 units to
SiO2 will range from about 0.43 to about 9.0, preferably 1 to 3.A cured coating having a ratio of RSiO3/2 to SiO2, where R is methyl, of 2 is most preferred. The coating thickness can be varied by means of the particular application technique, but coatings of about 0.5 to 20 microns, preferably 2-10 micron thickness are generally utilized.
In order that those skilled in the art may better understand how to practice the present invention, the following examples are given by way of illustration and not by way of limitation.
Example 1
22.1 parts by weight of Ludox LS, silica sol (aqueous dispersion of colloidal silica, average particle size of 12 millimicrons, pH of 8.2, sold by duPont) is added to a solution of 0.1 parts by weight of methytriacetoxysilane in 26.8 parts by weight of methyltrimethoxysilane. The temperature of the reaction mixture is maintained at 200C to 300C, preferably below 250C. The hydrolysis is allowed to continue for 24 hours.
The solids content of the resultant reaction mixture is 40.5% and is diluted to about 20% solids with the addition of isobutanol thereto. The pH of the product is about 7.2.
This composition is flow-coated onto a transparent Lexan (poly-(bisphenol-A carbonate)) panel primed with a thermosetting acrylic emulsion. After air drying for 30 minutes the panel is cured for one hour at 1 200C. After 500
Taber Abraser cycles (500 g. load, CS-1 OF wheels) (ANSI-Z26.1--1977 section 5.17) the change in percent haze (A%H) is 1.8. The sample passes the cross-hatched adhesion test (DIN 53-1 51) after 7 days in 650C water. It also passes the cross-hatched adhesion test (DIN 53-1 51) after 1000 hours under R-S Lamp exposure on a rotating platform 10" from the faces of an array of 6 lamps arranged at 1200 from one another. The platform rotates at about 3
RPM.
Example 2
300 grams of a 30% aqueous colloidal silica dispersion having an average particle size of 20 millimicrons and pH of 9.2 (prepared by dilution of
Nalcoag 1050, a product of Nalco Chemical
Company) is added to a solution of 0.9 grams glacial acetic acid and 366 grams of
methyltrimethoxysilane. The temperature of the reaction mixture is maintained below 300C. The hydrolysis is allowed to continue for 3 days. The solids content of the resultant reaction mixture is 40.5% and is diluted with 419 grams of isopropanol to a final dilution of 25% solids. The pH of the final composition is about 7.5.
This composition (containing 3% of a 3% solution of tetramethylammonium acetate) is flow-coated on a transparent Lexan panel primed with an ethanol-isobutanol solution containing
1.5 weight percent of gammaaminopropyltriethoxysilane and 1.5 wt. % of a preformed reaction product of gammaaminopropyltriethoxysilane and maleic anhydride as disclosed in copending U.S. application Serial No. 901,543, filed on May 1, 1978 by Holub and
Vaughn. After air drying for 30 minutes the panel is cured for 1 hour at 1 200C. After 500 Taber
Abraser cycles the change in percent haze (A%H) is 1.15.
Example3 17.9 grams of Ludox LS is added to a solution of 0.06 grams of glacial acetic acid in 27.2 grams of methyltrimethoxysilane. The temperature of the reaction mixture is maintained below 300C. The hydrolysis is allowed to continue for 6 hours. The solids content is 41.6% and is diluted with 30 grams of isobutanol to a final solids content of 25%. The pH is about 7.2.
The composition (containing 3% of a 3% solution of tetramethylammonium acetate) is flow-coated on a transparent Lexan panel primed as in Example 2. After curing, the (A%H) of the panel is 1.6.
Obviously, other modifications and variations of the present invention are possible in the light of the above teachings. It is therefore to be understood that changes may be made in the particular embodiments described above which are within the full intended scope of the invention as defined in the appended claims.
Claims (19)
1. An aqueous coating composition which comprises a dispersion of colloidal silica in an aliphatic alcohol-water solution of a partial condensate of a silanol of the formula RSi(OH)3, wherein R is alkyl having from 1 to 3 carbon atoms or aryl, at least 70 weight percent of the silanol being CH3Si(OH)3, said composition having a pH of 7.1 to 7.8 and a solids content of 10 to 50 weight percent, said solids comprising 10 to 70 weight percent of colloidal silica and 30 to 90 weight percent of the partial condensate.
2. A composition as claimed in Claim 1 wherein the aliphatic alcohol is a mixture of methanol and isobutanol.
3. A composition as claimed in Claim 1 or 2, wherein said partial condensate is entirely derived from CH3Si(OH)3.
4. A composition as claimed in any preceding
Claim which comprises from 0.05 to 0.5 weight percent of a buffered latent silanol-condensation catalyst.
5. A composition as claimed in Claim 4 wherein said catalyst is sodium acetate or tetramethylammonium acetate.
6. A composition as claimed in any preceding
Claim wherein the pH is 7.2 to 7.8.
7. A composition as claimed in any preceding
Claim wherein the solids content is from 18 to 25 weight percent and the solids comprise 25 to 45 weight percent of colloidal silica and 55 to 75 weight percent of the partial condensate.
8. A composition as claimed in any preceding
Claim prepared by mixing an aqueous colloidal silica dispersion with a solution of an alkyltriacetoxy silane in an alkyltrialkoxy-silane, maintaining the temperature of the resulting mixture at from 20 to 300C for a sufficient time to reduce the reaction mixture to one liquid phase, maintaining the pH of the composition in the range of from 7.1 to 7.8, and adjusting the solids content of the mixture by addition of the aliphatic alcohol.
9. A composition as claimed in Claim 8 wherein the alkyl-trialkoxysilane is methyltrimethoxysilane, the alkyl(triacetoxy) silane is methyl(triacetoxy)silane and the aliphatic alcohol is isobutanol.
10. A coating composition as claimed in Claim 1 and substantially as hereinbefore defined with reference to any of Examples 1 to 3.
11. An article which comprises a solid substrate having at least one surface coated with an aqueous coating composition as claimed in any of the preceding Claims.
12. An article as claimed in Claim 11 wherein the solid substrate comprises a synthetic organic polymer.
13. An article as claimed in Claim 11 wherein the solid substrate is a metal.
14. An article as claimed in Claim 11 wherein the solid substrate is a synthetic organic polymer having a metallized surface.
15. An article as claimed in Claim 12 wherein the polymer is transparent.
16. An article as claimed in Claim 12 or 1 5 wherein the polymer is a polycarbonate.
17. An article as claimed in Claim 16 wherein the polycarbonate is a poly(bisphenol-A carbonate).
18. An article as claimed in any of Claims 11 to 1 7 wherein the aqueous coating composition has been cured on the surface of the solid substrate.
19. An article as claimed in Claim 11 and substantially as hereinbefore defined with reference to any of Examples 1 to 3.