GB1528148A - Refractory dry tamping composition for lining of crucible induction furnaces - Google Patents

Refractory dry tamping composition for lining of crucible induction furnaces

Info

Publication number
GB1528148A
GB1528148A GB4862775A GB4862775A GB1528148A GB 1528148 A GB1528148 A GB 1528148A GB 4862775 A GB4862775 A GB 4862775A GB 4862775 A GB4862775 A GB 4862775A GB 1528148 A GB1528148 A GB 1528148A
Authority
GB
United Kingdom
Prior art keywords
per cent
composition
refractory
cao
content
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB4862775A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Veitscher Magnesitwerke AG
Original Assignee
Veitscher Magnesitwerke AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Veitscher Magnesitwerke AG filed Critical Veitscher Magnesitwerke AG
Publication of GB1528148A publication Critical patent/GB1528148A/en
Expired legal-status Critical Current

Abstract

1528148 Refractory composition VEITSCHER MAGNESITWERKE-ACTIEN-GES 26 Nov 1975 [29 Nov 1974] 48627/75 Heading C1J A refractory dry tamping composition for lining crucible induction furnaces contains not more than 1À5 wt. per cent Si0 2 and (a) a principal basic refractory material having a content of at least 96 wt. per cent MgO and/or CaO, an Fe 2 O 3 content below 2À5 wt. per cent, a CaO content of at least 2 wt. per cent and a molecular lime-silica ratio above 2; and (b) an additive which on heating reacts with the principal material with an increase in volume, the additive being a zirconium compound that forms the oxide on heating, having a granule size below 1 mm., and being present in an amount of 5-40 wt. per cent calculated as ZrO 2 based on the total composition, preferably sufficient to bind the free CaO with formation of calcium zirconate.
GB4862775A 1974-11-29 1975-11-26 Refractory dry tamping composition for lining of crucible induction furnaces Expired GB1528148A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
AT960374A AT345716B (en) 1974-11-29 1974-11-29 FIRE-RESISTANT DRY MASS FOR LINING INDUCTION FURNACES

Publications (1)

Publication Number Publication Date
GB1528148A true GB1528148A (en) 1978-10-11

Family

ID=3615623

Family Applications (1)

Application Number Title Priority Date Filing Date
GB4862775A Expired GB1528148A (en) 1974-11-29 1975-11-26 Refractory dry tamping composition for lining of crucible induction furnaces

Country Status (7)

Country Link
AT (1) AT345716B (en)
BE (1) BE835868A (en)
DE (1) DE2552150C3 (en)
FR (1) FR2292686A1 (en)
GB (1) GB1528148A (en)
IT (1) IT1049024B (en)
SE (1) SE407213B (en)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2010103463A1 (en) * 2009-03-10 2010-09-16 Saint-Gobain Centre De Recherches Et D'etudes Europeen Zircon powder
KR101382968B1 (en) 2012-05-08 2014-04-09 에이트 세라믹스 주식회사 apparatus for fabricating sapphire ingot and manufacturing method thereof
CN112094125A (en) * 2020-09-22 2020-12-18 武汉科技大学 Low-thermal-conductivity low-thermal-expansion magnesium-based raw material and preparation method thereof
CN114057504A (en) * 2021-11-26 2022-02-18 武汉科技大学 Low-thermal-conductivity calcium zirconate material and preparation method thereof
CN115448703A (en) * 2022-09-06 2022-12-09 宜兴市隆昌耐火材料有限公司 Preparation method of high-temperature wear-resistant castable containing zirconia corundum

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3037268C2 (en) * 1980-10-02 1984-10-25 Dynamit Nobel Ag, 5210 Troisdorf Highly refractory dry ramming mass based on zirconium dioxide for lining induction crucible furnaces and their use
FR2696445B1 (en) * 1992-10-01 1994-12-16 Rennes Inst Nal Sciences Appli Composition for obtaining products based on pure lime, application of this composition and process for its implementation.
DE102008019529B4 (en) * 2008-04-18 2010-05-12 Refractory Intellectual Property Gmbh & Co. Kg Refractory ceramic product and associated molding

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2010103463A1 (en) * 2009-03-10 2010-09-16 Saint-Gobain Centre De Recherches Et D'etudes Europeen Zircon powder
FR2943055A1 (en) * 2009-03-10 2010-09-17 Saint Gobain Ct Recherches ZIRCONIA POWDER
US8376318B2 (en) 2009-03-10 2013-02-19 Saint-Gobain Centre De Recherches Et D'etudes Europeen Zirconia powder
KR101382968B1 (en) 2012-05-08 2014-04-09 에이트 세라믹스 주식회사 apparatus for fabricating sapphire ingot and manufacturing method thereof
CN112094125A (en) * 2020-09-22 2020-12-18 武汉科技大学 Low-thermal-conductivity low-thermal-expansion magnesium-based raw material and preparation method thereof
CN114057504A (en) * 2021-11-26 2022-02-18 武汉科技大学 Low-thermal-conductivity calcium zirconate material and preparation method thereof
CN115448703A (en) * 2022-09-06 2022-12-09 宜兴市隆昌耐火材料有限公司 Preparation method of high-temperature wear-resistant castable containing zirconia corundum

Also Published As

Publication number Publication date
SE407213B (en) 1979-03-19
DE2552150C3 (en) 1979-03-15
SE7513443L (en) 1976-05-31
AT345716B (en) 1978-10-10
BE835868A (en) 1976-03-16
ATA960374A (en) 1978-01-15
IT1049024B (en) 1981-01-20
DE2552150A1 (en) 1976-08-12
FR2292686A1 (en) 1976-06-25
DE2552150B2 (en) 1977-01-20
FR2292686B1 (en) 1980-04-25

Similar Documents

Publication Publication Date Title
GB1512275A (en) Control of setting time in magnesia-phosphate cements
SE7709947L (en) KIT FOR DESULFURATION OF IRON MELTER
GB1528148A (en) Refractory dry tamping composition for lining of crucible induction furnaces
ES355066A1 (en) Phosphate-bonded basic refractory composition
ES408499A1 (en) Lime composition for basic oxygen steel-making process
ES435063A1 (en) Refractory compositions
GB1387468A (en) Basic refractory shapes
GB1262328A (en) Refractory brick composition
GB1381797A (en) Method of manufacturing high fireproof calcium aluminate cement
ES386444A1 (en) Sintered preformed slag for the steel industry
ES356637A1 (en) Highly refractory aluminous cement and process for its manufacture
SE8006112L (en) THE IRON ORE PELLET CONTAINING MAGNESIUM OXIDE
GB1413985A (en) Refractory magnesia
ES377265A1 (en) Process of manufacturing refractory magnesia-chrome and chrome-magnesia bricks
ES298884A1 (en) Improvements introduced in the manufacture of refractory bricks (Machine-translation by Google Translate, not legally binding)
ES395853A1 (en) Refractory substance
ES435606A1 (en) Development of hot strength in synthetic magnesia refractories having high b{11 o content
GB1418653A (en) Lining induction crucible furnaces
GB1270008A (en) A pelletising method
ES369232A2 (en) Improvements introduced in the manufacture of calcinated refractory bricks. (Machine-translation by Google Translate, not legally binding)
GB1411964A (en) Heat storage bricks and method of production thereof
ES271731A1 (en) Improvements relating to refractories and refractory bricks containing calcined magnesia
ES326685A1 (en) A procedure for the manufacture of refractory bricks. (Machine-translation by Google Translate, not legally binding)
SU1678809A1 (en) Charge mixture for manufacturing induction furnace crucible
GB668187A (en) Method of consolidating refractory materials

Legal Events

Date Code Title Description
PS Patent sealed
PCNP Patent ceased through non-payment of renewal fee