GB1461849A - Impregnated fibrous substrates - Google Patents

Impregnated fibrous substrates

Info

Publication number
GB1461849A
GB1461849A GB1285474A GB1285474A GB1461849A GB 1461849 A GB1461849 A GB 1461849A GB 1285474 A GB1285474 A GB 1285474A GB 1285474 A GB1285474 A GB 1285474A GB 1461849 A GB1461849 A GB 1461849A
Authority
GB
United Kingdom
Prior art keywords
vinyl
impregnated
laminates
resin
substrate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB1285474A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dow Chemical Co
Original Assignee
Dow Chemical Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dow Chemical Co filed Critical Dow Chemical Co
Priority to GB1285474A priority Critical patent/GB1461849A/en
Publication of GB1461849A publication Critical patent/GB1461849A/en
Expired legal-status Critical Current

Abstract

1461849 Laminates DOW CHEMICAL CO 22 March 1974 12854/74 Heading B5N [Also in Division C3] An impregnated fibrous substrate suitable for use in the production of laminates is produced (a) by impregnating a fibrous substrate comprising glass, nylon, polyester or acrylic fibres with a mixture of 40-100% by weight of a polymerizable resin produced by reacting a polyepoxide with a substantially equivalent amount of acrylic and/or methacrylic acid, the polyepoxide being the polyglycidyl ether of a polyhydric phenol or polyhydric alcohol, and 0-60% by weight of a nonvolatile copolymerizable vinyl monomer having no aromatic groups directly attached to the vinyl group, (b) applying pressure to the impregnated substrate with a roller to express entrapped air bubbles therefrom and (c) exposing the impregnated substrate in an inert atmosphere to ionizing radiation, e.g. accelerated electrons or protons, gamma rays or X-rays, to polymerize the resin or resin/monomer mixture. The vinyl monomer may be an alkyl or hydroxy-alkyl acrylate or methacrylate in which the alkyl or hydroxyalkyl group contains at least 2 carbon atoms or a vinyl alkyl ether, vinyl ester, vinyl nitrile or vinyl amide. Prior to or durin gstep (b) a plurality of the impregnated fibrous substrates may be brought into contact with each other to form a laminate or a sheet of metal foil, e.g. of copper, aluminium or silver, or a plastics film, e.g. of polyester or polyolefin, may be brought into contact with at least one side of the impregnated fibrous substrate to form a laminate. In the drawing fibrous substrate 10 after passing through resin bath 13 is passed under tension over laminating roller 15, which may be cooled where it is contacted with copper foil 17 and polyester cover sheet 20 and where entrapped air is expressed, ionizing radiation being applied from source 23 and the laminates being wound up before or after removal of the polyester cover sheet. The resin bath and impregnated substrate are protected against radiation by lead shield 16. A mould release agent may be added to the resin bath. The top cover sheet may be eliminated if curing is effected in a chamber containing nitrogen or helium. In an alternative arrangement the terminating roll may be replaced by a pair of squeeze rollers. The laminates may be used in the production of printed circuits.
GB1285474A 1974-03-22 1974-03-22 Impregnated fibrous substrates Expired GB1461849A (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
GB1285474A GB1461849A (en) 1974-03-22 1974-03-22 Impregnated fibrous substrates

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
GB1285474A GB1461849A (en) 1974-03-22 1974-03-22 Impregnated fibrous substrates

Publications (1)

Publication Number Publication Date
GB1461849A true GB1461849A (en) 1977-01-19

Family

ID=10012368

Family Applications (1)

Application Number Title Priority Date Filing Date
GB1285474A Expired GB1461849A (en) 1974-03-22 1974-03-22 Impregnated fibrous substrates

Country Status (1)

Country Link
GB (1) GB1461849A (en)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2566014A1 (en) * 1984-06-15 1985-12-20 Dias Alain Manual appliance for the pressing of impregnated fabrics
EP0183803A1 (en) * 1984-06-04 1986-06-11 The Dow Chemical Company A laminate sheet and a process for making the sheet
GB2333737A (en) * 1998-02-03 1999-08-04 Kobe Steel Europ Ltd Fibre reinforced compositions and method for their production

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0183803A1 (en) * 1984-06-04 1986-06-11 The Dow Chemical Company A laminate sheet and a process for making the sheet
EP0183803A4 (en) * 1984-06-04 1988-01-21 Dow Chemical Co A laminate sheet and a process for making the sheet.
FR2566014A1 (en) * 1984-06-15 1985-12-20 Dias Alain Manual appliance for the pressing of impregnated fabrics
GB2333737A (en) * 1998-02-03 1999-08-04 Kobe Steel Europ Ltd Fibre reinforced compositions and method for their production

Similar Documents

Publication Publication Date Title
US3810816A (en) Process for making reinforced resin laminates of uniform thickness
GB1168641A (en) Formation of Polymer Coatings on Substrates.
GB1461849A (en) Impregnated fibrous substrates
US5085907A (en) Abrasion-resistant protective laminates
GB1356163A (en) Process for the production of pressure-sensitive adhesive materials
DE4219446C3 (en) Process for applying a decorative layer to a substrate
US4544573A (en) Process for curing radiation curable coating media
GB1208403A (en) Method of preparing modified polypropylene
US3823046A (en) Method of forming decorative sheet
JPS647001A (en) Production of fresnel lens
SE8405987L (en) LITIUMSTRALMAL
JPS6225429B2 (en)
JPS53136082A (en) Production of phenolic resin laminate
JPS5773028A (en) Production of graft polymer
JPS57195208A (en) Pressure-sensitive adhesive type polarizing plate
GB1275471A (en) Improvements relating to photo-resists
GB1128850A (en) Improvements relating to the preparation and use of photo-resists
JPS5757625A (en) Manufacture of laminated plate
JPS6256143A (en) Manufacture of resin composite body
JPS5736174A (en) Electric ray-curing type adhesive for laminating
JPS57123637A (en) Production of explosion-proof cathode ray tube
JPS57143380A (en) Double-coated pressure-sensitive adhesive tape
JP2906859B2 (en) Metal foil coating method
JPS6431886A (en) Method for treating side of laminated body of tacky tape or sheet
JPS5277186A (en) Films coated with resins

Legal Events

Date Code Title Description
PS Patent sealed
PCNP Patent ceased through non-payment of renewal fee