GB1323742A - Applying electroconductive heating circuits to glass - Google Patents
Applying electroconductive heating circuits to glassInfo
- Publication number
- GB1323742A GB1323742A GB1323742DA GB1323742A GB 1323742 A GB1323742 A GB 1323742A GB 1323742D A GB1323742D A GB 1323742DA GB 1323742 A GB1323742 A GB 1323742A
- Authority
- GB
- United Kingdom
- Prior art keywords
- glass
- frit
- activated
- metal
- catalytic metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1323742 Coating glass PPG INDUSTRIES Inc 22 Aug 1970 40525/70 Heading C1M [Also in Division C7] A metal pattern is electrically deposited on a glass substrate as a circuit to produce electrically heated windows for vehicles and buildings. A glass or ceramic frit is first applied in the required pattern to the glass e.g. by silk screening through a stencil or by filling preformed grooves in the glass. The frit is then fused, sensitized and activated with a catalytic metal prior to electroless deposition of metals such as Cu, Ni, Co, Cr, Fe, Pd on the activated frit. Alternatively the frit may contain a catalytic metal e.g. Au, Ag, Pt, Pd, Rh, Cu, W, Fe or Al preferably as a metal compound e.g. a resinate in which case sensitizing and activating after fusion is not required. The frit is preferably applied as a mixture with abrasive particles via medium such as turpentine or zinc oil and fuses to give a rough, porous, surface. Ni or Cu may be electroplated on to the electroless deposit and an insulating layer may be applied by electropainting. The coated substrate may be hot shaped to the required form and may be laminated with another glass sheet with an inter layer of polyvinyl butyral or polyurethane.
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB4052570 | 1970-08-22 |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1323742A true GB1323742A (en) | 1973-07-18 |
Family
ID=10415330
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB1323742D Expired GB1323742A (en) | 1970-08-22 | 1970-08-22 | Applying electroconductive heating circuits to glass |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB1323742A (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2015044091A1 (en) * | 2013-09-26 | 2015-04-02 | Atotech Deutschland Gmbh | Novel adhesion promoting process for metallisation of substrate surfaces |
-
1970
- 1970-08-22 GB GB1323742D patent/GB1323742A/en not_active Expired
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2015044091A1 (en) * | 2013-09-26 | 2015-04-02 | Atotech Deutschland Gmbh | Novel adhesion promoting process for metallisation of substrate surfaces |
US10487404B2 (en) | 2013-09-26 | 2019-11-26 | Atotech Deutschland Gmbh | Adhesion promoting process for metallisation of substrate surfaces |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US3772075A (en) | Applying electroconductive heating circuits to glass | |
US3721594A (en) | Applying electroconductive heating circuits to glass | |
US3703445A (en) | Applying electroconductive heating circuits to glass by electroplating | |
GB1496994A (en) | Pastes for forming electrically conductive films on non-conductive substrates | |
ES465472A1 (en) | Electroless deposition of nickel on a masked aluminum surface | |
KR940006425A (en) | Transparent plane heater and its manufacturing method | |
DE2159612A1 (en) | Method for electroless metal plating of non-conductive bodies | |
GB1430968A (en) | Electrically heatable glazing panel | |
GB1289262A (en) | ||
US3668003A (en) | Printed circuits | |
GB1282603A (en) | Bonding an insulator to an insulator | |
US3721595A (en) | Applying electroconductive heating circuits to glass | |
GB1404697A (en) | Production of fine conductor path structures on ceramic substrates | |
US2882377A (en) | Electrical resistor metal coatings on refractory materials | |
US3859128A (en) | Composition for resistive material and method of making | |
US3135046A (en) | Method of forming metallic films on glass | |
US2338091A (en) | Screen stencil and method of making same | |
US4510179A (en) | Electrode on heat-resisting and isolating substrate and the manufacturing process for it | |
GB1323742A (en) | Applying electroconductive heating circuits to glass | |
GB1354646A (en) | Method of making a gas discharge display device | |
ES254803A1 (en) | Method of making printed circuits | |
US3649567A (en) | Metallizing compositions which yield coatings having unobjectionable backside color | |
KR980007876A (en) | Copper foil for printed circuit boards, manufacturing method thereof, laminate and printed circuit board using the copper foil | |
US3721870A (en) | Capacitor | |
US4559279A (en) | Electrode on heat-resisting and isolating substrate |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
PS | Patent sealed | ||
PLNP | Patent lapsed through nonpayment of renewal fees |