GB1262070A - Process for the impregnation of glass fibre materials - Google Patents
Process for the impregnation of glass fibre materialsInfo
- Publication number
- GB1262070A GB1262070A GB51259/70A GB5125970A GB1262070A GB 1262070 A GB1262070 A GB 1262070A GB 51259/70 A GB51259/70 A GB 51259/70A GB 5125970 A GB5125970 A GB 5125970A GB 1262070 A GB1262070 A GB 1262070A
- Authority
- GB
- United Kingdom
- Prior art keywords
- phenyl
- silicone resins
- fibre materials
- methyl
- silicone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1,262,070. Treating glass fibres. KOMBINAT TECHNISCHES GLAS ILMENAU VEB. 28 Oct., 1970, No. 51259/70. Heading D1P. A process for the impregnation of inorganic fibre materials, such as glass fibre materials, comprises impregnating such materials with a composition containing silicone resins and fluoropolymers and optionally of graphite and/or molybdenum disulphide or with a composition containing silicone resins with graphite and/or molybdenum disulphide, which compositions are fixed at an elevated temperature, wherein,'as silicone resins, there are used mixtures of cross-linked silicon compounds with linear, non-cross linked silicone compounds in dissolved or dispersed form. The mixing ratio of silicone resins to silicone oils or silanes can be varied, depending upon the desired degree of flexibility. Preferably, there are used mixtures of methyl, phenyl or methyl-phenyl silicone resins with methyl, phenyl or methyl-phenyl silicone oils or phenyl silanes. The silicone resins and silicone oils or silanes are preferably used in dissolved or dispersed form. The process may also be applied to other inorganic fibre materials, e.g. mineral, asbestos and ceramic fibre materials.
Priority Applications (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB51259/70A GB1262070A (en) | 1970-04-07 | 1970-10-28 | Process for the impregnation of glass fibre materials |
FR717101828A FR2085885B3 (en) | 1970-04-07 | 1971-01-20 | |
DE19712103141 DE2103141A1 (en) | 1970-04-07 | 1971-01-23 | Process for impregnating fiberglass fabrics |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DD14666970 | 1970-04-07 | ||
GB51259/70A GB1262070A (en) | 1970-04-07 | 1970-10-28 | Process for the impregnation of glass fibre materials |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1262070A true GB1262070A (en) | 1972-02-02 |
Family
ID=25747312
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB51259/70A Expired GB1262070A (en) | 1970-04-07 | 1970-10-28 | Process for the impregnation of glass fibre materials |
Country Status (3)
Country | Link |
---|---|
DE (1) | DE2103141A1 (en) |
FR (1) | FR2085885B3 (en) |
GB (1) | GB1262070A (en) |
Cited By (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2866329A1 (en) * | 2004-02-12 | 2005-08-19 | Saint Gobain Vetrotex | Glass fibre or structure of glass fibres has coating of electrically conducting compound containing 20 - 75 per cent conducting particles |
WO2008030769A1 (en) * | 2006-09-05 | 2008-03-13 | Dow Corning Corporation | Silicone hot melt additive for fluoroplastics |
CN108929526A (en) * | 2017-05-25 | 2018-12-04 | 合肥杰事杰新材料股份有限公司 | A kind of low smell, PET composition of high abrasion and preparation method thereof |
-
1970
- 1970-10-28 GB GB51259/70A patent/GB1262070A/en not_active Expired
-
1971
- 1971-01-20 FR FR717101828A patent/FR2085885B3/fr not_active Expired
- 1971-01-23 DE DE19712103141 patent/DE2103141A1/en active Pending
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2866329A1 (en) * | 2004-02-12 | 2005-08-19 | Saint Gobain Vetrotex | Glass fibre or structure of glass fibres has coating of electrically conducting compound containing 20 - 75 per cent conducting particles |
WO2005077854A1 (en) * | 2004-02-12 | 2005-08-25 | Saint-Gobain Vetrotex France S.A. | Electrically conductive glass yarn and constructions including same |
US10173924B2 (en) | 2004-02-12 | 2019-01-08 | Saint-Gobain Technical Fabrics Europe | Electrically conducting glass strands and structures comprising such strands |
WO2008030769A1 (en) * | 2006-09-05 | 2008-03-13 | Dow Corning Corporation | Silicone hot melt additive for fluoroplastics |
CN108929526A (en) * | 2017-05-25 | 2018-12-04 | 合肥杰事杰新材料股份有限公司 | A kind of low smell, PET composition of high abrasion and preparation method thereof |
Also Published As
Publication number | Publication date |
---|---|
DE2103141A1 (en) | 1971-12-23 |
FR2085885B3 (en) | 1973-05-11 |
FR2085885A7 (en) | 1971-12-31 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB583927A (en) | Improvements in manufacture of glass yarn | |
IT1104693B (en) | PRELIMINARY ACRYLIC PRODUCT TO PREPARE BONE CONCRETE | |
CA2028164A1 (en) | Heat-curable silicone compositions having improved bath life | |
BR8601334A (en) | POLYSILAZAN COMPOSITION AND THE PROCESS OF LINING A COMPOSITION AND TO COVER OR IMPREGNATE A SUPPORT WITH A CERAMIC MATERIAL | |
ATE227T1 (en) | AROMATIC COPOLYESTERS, WHICH CAN FORM AN ANISOTROPIC MELT, AND MOLDINGS MADE THEREOF. | |
ES8105360A1 (en) | Silicone compositions for the treatment of glass fibers and methods of treatment | |
ES432270A1 (en) | Waterproofing of textiles | |
ES8106574A1 (en) | Organopolysiloxane-silica mixture for treatment of gypsum paper. | |
BR8004487A (en) | POLYSILOXAN MOLDING MASSES AND PROCESS FOR ITS PREPARATION | |
ES298444A1 (en) | Procedure for the manufacture of thermoplastic material. (Machine-translation by Google Translate, not legally binding) | |
GB1262070A (en) | Process for the impregnation of glass fibre materials | |
DE3279767D1 (en) | Asbestos free jointing | |
JPS5263961A (en) | Organo polysiloxane composition | |
ES2027397T3 (en) | NEW COMPOSITIONS INCLUDING CERAMIC MATERIALS. | |
GB882069A (en) | Organopolysiloxanes and process for producing same | |
GB1330526A (en) | Process for the manufacture of fibrous silicon carbide | |
BE763710A (en) | MIXTURE OF ELASTOMERIC SUBSTANCES FOR THE IMPREGNATION OF FIBROUS, FLEXIBLE AND FLAT ARTICLES, AS WELL AS FOR THE COATING OF THESE ARTICLES | |
GB1194216A (en) | Organopolysiloxane Compositions | |
KR840003229A (en) | Mineral nutrient composition for soil improvement | |
JPS57172302A (en) | Coating material for optical communication fiber | |
BE789495A (en) | MASTIC COMPOSED OF A MIXTURE OF ELECTRO-CORUNDUM, SILICON CARBIDE AND GLASS QUARTZ, AS WELL AS A BINDER | |
GB999122A (en) | Impregnating agents containing organic titanium and silicon reaction products | |
BE784198A (en) | SIZING COMPOSITION AND PRODUCTS REINFORCED WITH GLASS FIBERS SIZED BY SUCH COMPOSITION | |
JPS5742762A (en) | Cold-setting polyorganosiloxane composition | |
GB936408A (en) | Improvements in or relating to siloxane elastomers |