GB1236282A - Improvements in or relating to the pre-oxidation of thermally resistant aromatic polymers - Google Patents
Improvements in or relating to the pre-oxidation of thermally resistant aromatic polymersInfo
- Publication number
- GB1236282A GB1236282A GB3372668A GB3372668A GB1236282A GB 1236282 A GB1236282 A GB 1236282A GB 3372668 A GB3372668 A GB 3372668A GB 3372668 A GB3372668 A GB 3372668A GB 1236282 A GB1236282 A GB 1236282A
- Authority
- GB
- United Kingdom
- Prior art keywords
- temperature
- polyamide
- thermally resistant
- treated
- fibres
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1,236,282. Polyamide filaments. MONSANTO CO. 15 July, 1968, No. 33726/68. Heading B5B. [Also in Divisions B5 and C3] Thermally resistant wholly aromatic polyamides in the form of films, fibres, fabrics, webs, foams and other shaped articles having similarly high surface: volume ratio are pre-oxidized by heating in air from room temperature to a temperature between 350‹ and 500‹ C. but below that at which structural identity and strength are lost over a period between 45 and 60 minutes and maintaining the polyamide at that temperature for up to 12 hours. Various polyamide, some of which contain heterocyclic rings, are mentioned. The treated articles may be used for flameproof applications, e.g. heat shields, high temperature and electrical insulation, protective clothing and curtains, hot filtration media and supports for ablative materials; they may also be used as precursors for carbon and graphite fibres. In examples poly-mphenylenebis (m-benzamido) terephthalamide and polymers having the repeat unit are treated in the form of fabric or yarn.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB3372668A GB1236282A (en) | 1968-07-15 | 1968-07-15 | Improvements in or relating to the pre-oxidation of thermally resistant aromatic polymers |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
GB3372668A GB1236282A (en) | 1968-07-15 | 1968-07-15 | Improvements in or relating to the pre-oxidation of thermally resistant aromatic polymers |
Publications (1)
Publication Number | Publication Date |
---|---|
GB1236282A true GB1236282A (en) | 1971-06-23 |
Family
ID=10356668
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
GB3372668A Expired GB1236282A (en) | 1968-07-15 | 1968-07-15 | Improvements in or relating to the pre-oxidation of thermally resistant aromatic polymers |
Country Status (1)
Country | Link |
---|---|
GB (1) | GB1236282A (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2016029074A (en) * | 2009-10-13 | 2016-03-03 | リガンド・ファーマシューティカルズ・インコーポレイテッド | Hematopoietic growth factor mimetic small molecule compounds and their uses |
-
1968
- 1968-07-15 GB GB3372668A patent/GB1236282A/en not_active Expired
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2016029074A (en) * | 2009-10-13 | 2016-03-03 | リガンド・ファーマシューティカルズ・インコーポレイテッド | Hematopoietic growth factor mimetic small molecule compounds and their uses |
US9622991B2 (en) | 2009-10-13 | 2017-04-18 | Ligand Pharmaceuticals Inc. | Hematopoietic growth factor mimetic small molecule compounds and their uses |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
GB909379A (en) | Polymer coated fabric | |
KR910014563A (en) | Manufacturing method of industrial fabric with low air permeability which does not require coating treatment | |
GB1241937A (en) | Production of carbonised and graphitised fibres | |
US4401588A (en) | Manufacture of activated carbon fabric | |
DK0451263T3 (en) | Linear carbonaceous fiber with improved stretchability | |
US3764374A (en) | Process for placing modifiers within polyester fibers and films | |
BE852611A (en) | TEXTILE FIBERS HAVING DELAYED FLAMMABILITY PROPERTIES AND THEIR PREPARATION PROCESS | |
GB1236282A (en) | Improvements in or relating to the pre-oxidation of thermally resistant aromatic polymers | |
DK166092C (en) | PROCEDURE FOR PREPARING DEFORMABLE FLAT TEXTILE PRODUCT BY WOVEN OR KNITTED | |
GB1295289A (en) | ||
CN109825913A (en) | A kind of anti-corrosion fabric | |
CA1085087A (en) | Wholly aromatic polyamide fibers | |
NO953092D0 (en) | Reinforced thermal protection system | |
SU488421A3 (en) | Method for flame retardant finishing of fibrous material | |
FR2373616A1 (en) | POLYTETRAFLUOROETHYLENE YARNS OR FIBERS, THEIR MANUFACTURING PROCESS, AND THEIR USE AS SEALING ELEMENTS | |
GB986926A (en) | Improvements relating to polyester filamentary material | |
US3292991A (en) | Process of fire-proofing a blend of ceramic fibers and acrylic resin fibers by heating in an oxidizing atmosphere | |
US4008345A (en) | Process for fire-proofing treatment of shaped articles of aromatic polyamides | |
US3576769A (en) | Semicarbonization of thermally stable aromatic polymers | |
CN105603719A (en) | Preparation method of easy-to-dye polyimide fabric employing chemical reduction method | |
GB1242867A (en) | Improvements in and relating to the treatment of aromatic polyamide shaped articles | |
GB1411443A (en) | Naphthalate polyester fibres | |
LeMaistre et al. | The origin of structure in carbonized PAN fibers(Axial alignment of basal planes in polyacrylonitrile base carbon fibers, increasing axial and radial microstructural textures via heat treatment temperature) | |
ES427503A1 (en) | Process for flameproofing organic fibre material by the transfer process | |
GB1110596A (en) | Improvements in or relating to carbon and graphite fabrics |