GB1142683A - Production of alloys - Google Patents

Production of alloys

Info

Publication number
GB1142683A
GB1142683A GB818466A GB818466A GB1142683A GB 1142683 A GB1142683 A GB 1142683A GB 818466 A GB818466 A GB 818466A GB 818466 A GB818466 A GB 818466A GB 1142683 A GB1142683 A GB 1142683A
Authority
GB
United Kingdom
Prior art keywords
powder
alloy
hot
alloys
feb
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB818466A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
IIT Research Institute
Original Assignee
IIT Research Institute
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by IIT Research Institute filed Critical IIT Research Institute
Publication of GB1142683A publication Critical patent/GB1142683A/en
Expired legal-status Critical Current

Abstract

1,142,683. Alloys; powder metallurgy. IIT RESEARCH INSTITUTE. Feb.24, 1966 [Feb. 26, 1965; Jan. 3, 1966 (6)], No. 8184/66. Headings C7A and C7D. A solid alloy having an ultrafine micro-structure is produced by (a) preparing an alloy powder consisting by weight of 0À6 - 4%C, at least 15% of one or more of Cr, W, Mo, Ti, Ta, Nb, Zr, Hf, V and Al, the balance being at least 30% of one or more of Co, Fe and Ni, by mechanically crushing the alloy or atomizing the molten alloy, (b) sealing the powder within a metal jacket and heating to a hot-working temperature, and (c) compressing and mechanically hot-working the jacketed powder to produce a body of consolidated powder having a uniformly dispersed hard phase with a grain size of 0À5 - 3 microns. In a modification particularly for use as a cutting tool, a blend of two powders is used, one powder to form a matrix and the other to form a relatively harder and wear-resistant dispersal constituent. Specifically, powder may be pressed at 5 - 30 t. s. i. in Mo-lined cans, heated to forging temperature (1850‹ - 2150‹F.), forged, hot-rolled, annealed (1500‹-1600‹F.), machined to shape, austenitized (2100‹-2200‹F. oil or air cooled, and tempered one or more times at 950‹- 1100‹F. Many compositional examples are given of alloys.
GB818466A 1965-02-26 1966-02-24 Production of alloys Expired GB1142683A (en)

Applications Claiming Priority (7)

Application Number Priority Date Filing Date Title
US43573365A 1965-02-26 1965-02-26
US51816266A 1966-01-03 1966-01-03
US51809866A 1966-01-03 1966-01-03
US51818166A 1966-01-03 1966-01-03
US51844266A 1966-01-03 1966-01-03
US51814566A 1966-01-03 1966-01-03
US51805866A 1966-01-03 1966-01-03

Publications (1)

Publication Number Publication Date
GB1142683A true GB1142683A (en) 1969-02-12

Family

ID=27569770

Family Applications (1)

Application Number Title Priority Date Filing Date
GB818466A Expired GB1142683A (en) 1965-02-26 1966-02-24 Production of alloys

Country Status (1)

Country Link
GB (1) GB1142683A (en)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2210895A (en) * 1987-10-10 1989-06-21 Brico Eng Sintered material
GB2210894A (en) * 1987-10-10 1989-06-21 Brico Eng Sintered materials
CN112658252A (en) * 2020-11-17 2021-04-16 南昌大学 Preparation method of AlFeCrNiMoNb hot-pressed plate applied to high-temperature chlorine corrosion environment
CN114686662A (en) * 2022-03-28 2022-07-01 江西宝顺昌特种合金制造有限公司 GH2132 high-temperature alloy and heat treatment method for improving hardness of GH2132 high-temperature alloy
CN117684033A (en) * 2024-02-04 2024-03-12 有研工程技术研究院有限公司 High-performance TZM alloy foil and preparation method thereof

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2210895A (en) * 1987-10-10 1989-06-21 Brico Eng Sintered material
GB2210894A (en) * 1987-10-10 1989-06-21 Brico Eng Sintered materials
US4970049A (en) * 1987-10-10 1990-11-13 Brico Engineering Limited Sintered materials
GB2210894B (en) * 1987-10-10 1991-09-18 Brico Eng Sintered materials
GB2210895B (en) * 1987-10-10 1991-10-02 Brico Eng Sintered materials
CN112658252A (en) * 2020-11-17 2021-04-16 南昌大学 Preparation method of AlFeCrNiMoNb hot-pressed plate applied to high-temperature chlorine corrosion environment
CN112658252B (en) * 2020-11-17 2022-02-11 南昌大学 AlFeNiMoNbCr alloy applied to high-temperature chlorine corrosion environment and preparation method thereof
CN114686662A (en) * 2022-03-28 2022-07-01 江西宝顺昌特种合金制造有限公司 GH2132 high-temperature alloy and heat treatment method for improving hardness of GH2132 high-temperature alloy
CN114686662B (en) * 2022-03-28 2023-09-19 江西宝顺昌特种合金制造有限公司 GH2132 high-temperature alloy and heat treatment method for improving hardness of GH2132 high-temperature alloy
CN117684033A (en) * 2024-02-04 2024-03-12 有研工程技术研究院有限公司 High-performance TZM alloy foil and preparation method thereof
CN117684033B (en) * 2024-02-04 2024-05-31 有研工程技术研究院有限公司 High-performance TZM alloy foil and preparation method thereof

Similar Documents

Publication Publication Date Title
CA1088784A (en) Elimination of carbide segregation to prior particle boundaries
US3785801A (en) Consolidated composite materials by powder metallurgy
US3837930A (en) Method of producing iron-chromium-aluminum alloys with improved high temperature properties
US3655458A (en) Process for making nickel-based superalloys
US3369891A (en) Heat-treatable nickel-containing refractory carbide tool steel
GB1433852A (en) Powder metallurgy process
GB1523922A (en) Method for processing and densifying metal powder
US3556780A (en) Process for producing carbide-containing alloy
GB1166686A (en) Nickel Base Alloys and Process for their Manufacture
GB1443900A (en) Powder metallurgy tool steel article
US3698962A (en) Method for producing superalloy articles by hot isostatic pressing
US3183127A (en) Heat treatable tool steel of high carbide content
US3787205A (en) Forging metal powders
US3000734A (en) Solid state fabrication of hard, high melting point, heat resistant materials
GB1142683A (en) Production of alloys
CA1036913A (en) Thermomechanical processing of mechanically alloyed materials
GB1457448A (en) Powder metallurgy process
US2588007A (en) Titanium-molybdenum-chromium alloys
US4534808A (en) Method for refining microstructures of prealloyed powder metallurgy titanium articles
GB928407A (en) Improvements in the production of titanium base alloys
US4708742A (en) Production of nitride dispersion strengthened alloys
GB1142523A (en) Working cycle for dispersion strengthened materials
Moll Utilization of gas-atomized titanium and titanium-aluminide powder
GB1013170A (en) Improvements in or relating to the hot consolidation of metal powders
GB1163967A (en) Stainless Steels and Process for their Manufacture