GB1129951A - Improvements in or relating to the bonding of ceramic members to metal members and of ceramic members to each other - Google Patents

Improvements in or relating to the bonding of ceramic members to metal members and of ceramic members to each other

Info

Publication number
GB1129951A
GB1129951A GB392965A GB392965A GB1129951A GB 1129951 A GB1129951 A GB 1129951A GB 392965 A GB392965 A GB 392965A GB 392965 A GB392965 A GB 392965A GB 1129951 A GB1129951 A GB 1129951A
Authority
GB
United Kingdom
Prior art keywords
ceramic
metal
bonding
forsterite
alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB392965A
Inventor
Frederick Charles Carpenter
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Smiths Group PLC
Original Assignee
Smiths Group PLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Smiths Group PLC filed Critical Smiths Group PLC
Priority to GB392965A priority Critical patent/GB1129951A/en
Publication of GB1129951A publication Critical patent/GB1129951A/en
Expired legal-status Critical Current

Abstract

1,129,951. Ceramic seals ; welding by pressure; brazing. SMITHS INDUSTRIES Ltd. 29 April, 1966 [29 Jan., 1965], No. 3929/65. Headings B3R and B3V. A method of bonding a ceramic to a ceramic or to metal comprises pressing together the surfaces to be joined and causing relative movement between the surfaces transversely to the direction of the applied pressure to form a melt at the surfaces which solidifies, producing the bond. One of the parts may be stationary while the other is rotated or reciprocated, e.g. ultrasonically. In a ceramic-to-metal example, a recess is machined in the metal member and filled with Ti, Zr, Hf or Th braze material or an alloy of any of these when the metal to be bonded is Ni, Cr, Cu, Fe, Mo, Pt, Co or an alloy of any of these. Alternatively, the braze material may be from the Ni group and the metal to be bonded from the Ti group. The braze material may be a powder or, to obviate the need for a recess in one or both faces to be bonded, one or more discs. In a ceramic-to-ceramic example,. the braze material is an alloy or mixture of metals or alloys from both the above Ni and Ti groups. The ceramic material may be forsterite or have a high alumina content. As applied to bonding W or Mo to a ceramic, e.g. forsterite having a glassy phase, without an additional brazing material and in an oxidizing atmosphere, e.g. air, the frictional heating melts the glassy phase of the forsterite, and traces of W-oxide or Mo-oxide formed during heating mix with the glassy phase. Upon solidification, the mixture produces a bond.
GB392965A 1965-01-29 1965-01-29 Improvements in or relating to the bonding of ceramic members to metal members and of ceramic members to each other Expired GB1129951A (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
GB392965A GB1129951A (en) 1965-01-29 1965-01-29 Improvements in or relating to the bonding of ceramic members to metal members and of ceramic members to each other

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
GB392965A GB1129951A (en) 1965-01-29 1965-01-29 Improvements in or relating to the bonding of ceramic members to metal members and of ceramic members to each other

Publications (1)

Publication Number Publication Date
GB1129951A true GB1129951A (en) 1968-10-09

Family

ID=9767557

Family Applications (1)

Application Number Title Priority Date Filing Date
GB392965A Expired GB1129951A (en) 1965-01-29 1965-01-29 Improvements in or relating to the bonding of ceramic members to metal members and of ceramic members to each other

Country Status (1)

Country Link
GB (1) GB1129951A (en)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2555159A1 (en) * 1983-11-21 1985-05-24 Ceraver METHOD FOR WELDING TWO HALF-PIECES HOLLOWED IN CERAMIC, AND WELDING MACHINE FOR PERFORMING THE PROCESS
US5270135A (en) * 1989-07-04 1993-12-14 Chloride Silent Power, Ltd. Articles including a ceramic member and a metal member bonded together
EP1395387A1 (en) * 2001-05-23 2004-03-10 Rolls-Royce Corporation High temperature melting braze materials for bonding niobium based alloys
US8511535B1 (en) 2010-04-19 2013-08-20 Aegis Technology Inc. Innovative braze and brazing process for hermetic sealing between ceramic and metal components in a high-temperature oxidizing or reducing atmosphere
CN114749750A (en) * 2021-12-31 2022-07-15 上海工程技术大学 Forming control method for brazing joint of 3D printed product

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2555159A1 (en) * 1983-11-21 1985-05-24 Ceraver METHOD FOR WELDING TWO HALF-PIECES HOLLOWED IN CERAMIC, AND WELDING MACHINE FOR PERFORMING THE PROCESS
EP0142852A1 (en) * 1983-11-21 1985-05-29 Ceramiques Et Composites Method of bonding two ceramic hollow half-members together, and apparatus therefor
US5270135A (en) * 1989-07-04 1993-12-14 Chloride Silent Power, Ltd. Articles including a ceramic member and a metal member bonded together
EP1395387A1 (en) * 2001-05-23 2004-03-10 Rolls-Royce Corporation High temperature melting braze materials for bonding niobium based alloys
EP1395387A4 (en) * 2001-05-23 2004-09-15 Rolls Royce Corp High temperature melting braze materials for bonding niobium based alloys
EP2343150A3 (en) * 2001-05-23 2011-11-23 Rolls-Royce Corporation High temperature melting braze materials for bonding niobium based alloys
US8511535B1 (en) 2010-04-19 2013-08-20 Aegis Technology Inc. Innovative braze and brazing process for hermetic sealing between ceramic and metal components in a high-temperature oxidizing or reducing atmosphere
CN114749750A (en) * 2021-12-31 2022-07-15 上海工程技术大学 Forming control method for brazing joint of 3D printed product
CN114749750B (en) * 2021-12-31 2024-01-30 上海工程技术大学 Forming control method of braze welding joint for 3D printing product

Similar Documents

Publication Publication Date Title
US2570248A (en) Method of metalizing and bonding nonmetallic bodies
US3717442A (en) Brazing alloy composition
GB1008022A (en) Friction welding and brazing
CA2099278A1 (en) Method of brazing metal surfaces
GB1462510A (en) Method of making abrasive tools
GB1022432A (en) Improvements in or relating to the bonding of a ceramic to a metal
GB1129951A (en) Improvements in or relating to the bonding of ceramic members to metal members and of ceramic members to each other
AU5458294A (en) Method of bonding hard metal objects
KR870005940A (en) Copper-silver-titanium filler metal for direct brazing of structural ceramics
GB1209658A (en) Improvements in or relating to the production of soldered joints between bodies of refractory materials
US4508257A (en) Method of brazing with nickel based alloy
US3188732A (en) Diffusion-bonding of metal members
US3382052A (en) Ceramic brazing means
JPS5865588A (en) Production of joined sintered hard alloy
JPS6216896A (en) Brazing filler metal for ceramics
US4078713A (en) Brazing sintered ferrous powder metal articles
ES435597A1 (en) Method of bonding sintered iron articles
GB1408145A (en) Metal parts joined with sintered powdered metal
JPH0317791B2 (en)
JPS56116803A (en) Bonding method metal member
JPS59207885A (en) Method of bonding ceramic member to metal member
KR930007666B1 (en) Melting induced diffusion bonding
JPS609846A (en) Homogeneous low melting point copper base alloy
JPS55114482A (en) Bonding method of heat-resistant alloy
JPS6177680A (en) Method of bonding ceramic and metal