GB1001360A - Boron carbide spherules - Google Patents

Boron carbide spherules

Info

Publication number
GB1001360A
GB1001360A GB15298/65A GB1529865A GB1001360A GB 1001360 A GB1001360 A GB 1001360A GB 15298/65 A GB15298/65 A GB 15298/65A GB 1529865 A GB1529865 A GB 1529865A GB 1001360 A GB1001360 A GB 1001360A
Authority
GB
United Kingdom
Prior art keywords
carbide
spherules
carbon
isolating
medium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB15298/65A
Inventor
Harold G Sowman
James R Johnson
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
3M Co
Original Assignee
Minnesota Mining and Manufacturing Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Minnesota Mining and Manufacturing Co filed Critical Minnesota Mining and Manufacturing Co
Publication of GB1001360A publication Critical patent/GB1001360A/en
Expired legal-status Critical Current

Abstract

Crystalline carbide spherules of boron carbide of diameter 10m to 125 mils. are prepared by heating discrete irregular particles of this carbide uniformly dispersed throughout a finely divided inert solid isolating medium in a non-reactive atmosphere to above the melting point of the carbide but below that of the isolating medium to form spheres by the effect of the surface tension of the molten carbide. In a modification of the process, the carbide particles are replaced with irregular particles of boron or the oxide thereof, and the isolating medium is carbon or contains sufficient carbon to produce the carbide on heating. The preferred isolating media are boron nitride and carbon, e.g. graphite, carbon black, lampblack, amorphous carbon, or petroleum coke, and the particle size of the medium is at least one order of magnitude smaller than the material to be converted into spherules. The proportion of isolating material to carbide or carbide precursor can be varied over a wide range, and the non-reactive atmosphere may be helium or argon and the temperature 2300 DEG to 2700 DEG C. The spherules are cooled rapidly, e.g. by removal from the furnace, whilst maintaining the non-reactive atmosphere. The process may be carried out in a furnace or on a refractory pallet or on a bigger scale using a rotary kiln. Carbon may be removed from the surface of the spheres produced by treatment with a detergent or alternatively by oxidation under controlled conditions, e.g. by refluxing with chromic acid solution, or by heating in air to 1000 DEG C. Ultrasonic vibrations may also be utilized for cleaning the spherules. The spherules are used in atomic reactors as control elements, being dispersed in a metallic matrix.
GB15298/65A 1961-07-21 1961-07-21 Boron carbide spherules Expired GB1001360A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
GB26565/61A GB1001359A (en) 1961-07-21 1961-07-21 Refractory carbides

Publications (1)

Publication Number Publication Date
GB1001360A true GB1001360A (en) 1965-08-18

Family

ID=10245645

Family Applications (2)

Application Number Title Priority Date Filing Date
GB26565/61A Expired GB1001359A (en) 1961-07-21 1961-07-21 Refractory carbides
GB15298/65A Expired GB1001360A (en) 1961-07-21 1961-07-21 Boron carbide spherules

Family Applications Before (1)

Application Number Title Priority Date Filing Date
GB26565/61A Expired GB1001359A (en) 1961-07-21 1961-07-21 Refractory carbides

Country Status (1)

Country Link
GB (2) GB1001359A (en)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2515735A (en) * 2013-07-01 2015-01-07 Metal Nanopowders Ltd Hard Materials

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110577216B (en) * 2019-10-10 2022-07-29 燕山大学 Method for preparing carbon material with nano diamond structure through normal pressure catalysis
CN114605170A (en) * 2022-04-13 2022-06-10 北航（四川）西部国际创新港科技有限公司 Infiltration agent with multilayer coating structure and preparation method thereof
CN115976495B (en) * 2022-12-19 2024-04-12 杭州邦齐州科技有限公司 ALD (atomic layer deposition) coating fixture for micro-nano grating cathode assembly

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2515735A (en) * 2013-07-01 2015-01-07 Metal Nanopowders Ltd Hard Materials

Also Published As

Publication number Publication date
GB1001359A (en) 1965-08-18

Similar Documents

Publication Publication Date Title
US3175918A (en) Porous refractory bodies and the manufacture thereof
US4637837A (en) Process for boriding metals and metal alloys by means of solid boriding agents
US3385723A (en) Carbon article coated with beta silicon carbide
US3129188A (en) Crystalline spherules
GB1001360A (en) Boron carbide spherules
US3369871A (en) Preparation of metallurgical carbon
GB1311715A (en) Process for the production of fuel and or breeder elements for nuclear reactors
US2689167A (en) Production of gamma ferric oxide
JPS616247A (en) Manufacture of iron boron alloy or iron boron silicon alloy
US2689168A (en) Production of gamma ferric oxide
GB1088934A (en) Process for preparing finely divided amorphous silica
GB985943A (en) Process and apparatus for the manufacture of particulate refractories
US2800393A (en) Direct production of tungsten carbide from tungstic oxide
US2990261A (en) Processing of boron compact
US3094387A (en) Process for preparing boron phosphide
GB970858A (en) Method of and apparatus for carrying out metallurgical processes
GB1164810A (en) Improvements in or relating to Production of Particulate Refractory Material
EP0005359A1 (en) Method for making beta silicon carbide
GB940023A (en) Hard, refractory crystalline materials
US6652801B2 (en) Method for producing agglomerated boron carbide
GB970717A (en) Preparation of metal or silicon oxides
CN111977657A (en) Method for preparing silicon carbide nanowires by treating fly ash of coal-fired boiler by microwaves
USRE26941E (en) Hexagonal silicon carbide crystals produced from an elemental silicon vapor deposited onto a carbon plate
US3114629A (en) Production of columbium and tantalum
EP0044867B2 (en) Methods for the continuous production of silicon carbide