FR3141171A1 - Process for manufacturing a part made of ceramic matrix composite material - Google Patents
Process for manufacturing a part made of ceramic matrix composite material Download PDFInfo
- Publication number
- FR3141171A1 FR3141171A1 FR2210902A FR2210902A FR3141171A1 FR 3141171 A1 FR3141171 A1 FR 3141171A1 FR 2210902 A FR2210902 A FR 2210902A FR 2210902 A FR2210902 A FR 2210902A FR 3141171 A1 FR3141171 A1 FR 3141171A1
- Authority
- FR
- France
- Prior art keywords
- layer
- fibrous structure
- matrix
- densified
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Procédé de fabrication d’une pièce en matériau composite à matrice céramique La présente invention concerne un procédé de fabrication d’une pièce en matériau composite à matrice céramique, comprenant : - l’infiltration (S60) d’une structure fibreuse pré-densifiée par une composition d’infiltration à l’état fondu comprenant du silicium afin de former une matrice céramique dans une porosité résiduelle de ladite structure fibreuse pré-densifiée, ladite structure fibreuse pré-densifiée comprenant une matrice de pré-densification comprenant une première couche de carbure de silicium et une deuxième couche protectrice recouvrant la première couche et apte à protéger celle-ci d’une attaque par le silicium de la composition d’infiltration, la deuxième couche protectrice étant formée par un système binaire B-C ou par un système ternaire Si-B-C. Figure pour l’abrégé : Fig. 1.Method of manufacturing a part made of ceramic matrix composite material The present invention relates to a method of manufacturing a part of ceramic matrix composite material, comprising: - the infiltration (S60) of a pre-densified fibrous structure by a melt infiltration composition comprising silicon to form a ceramic matrix in a residual porosity of said pre-densified fibrous structure, said pre-densified fibrous structure comprising a pre-densification matrix comprising a first carbide layer of silicon and a second protective layer covering the first layer and capable of protecting the latter from attack by the silicon of the infiltration composition, the second protective layer being formed by a binary system B-C or by a ternary system Si- B-C. Figure for abstract: Fig. 1.
Description
L’invention concerne la fabrication d’une pièce en matériau composite à matrice en céramique (« Ceramic Matrix Composite » ; « CMC ») durant laquelle la matrice céramique est formée par infiltration d’une composition à base de silicium fondu (« Melt-Infiltration » ; « MI »). L’invention propose la présence d’une couche protectrice permettant de protéger le carbure de silicium de pré-densification sous-jacent de l’attaque par le silicium fondu. La pièce en matériau composite ainsi obtenue peut trouver une application en tant que pièce de partie chaude de turbomachine, notamment de turbomachine aéronautique, telle qu’une pièce de turbine.The invention relates to the manufacture of a part made of ceramic matrix composite material (“Ceramic Matrix Composite”; “CMC”) during which the ceramic matrix is formed by infiltration of a composition based on molten silicon (“Melt- Infiltration”; “MI”). The invention proposes the presence of a protective layer making it possible to protect the underlying pre-densification silicon carbide from attack by molten silicon. The composite material part thus obtained can find application as a hot part of a turbomachine, in particular an aeronautical turbomachine, such as a turbine part.
Les matériaux composites à matrice céramique supportent des températures allant de 600°C à 1400°C. De par leur meilleure résistance aux hautes températures, les CMC nécessitent moins de refroidissement. Ce refroidissement étant traditionnellement issu d’un prélèvement dans le compresseur qui impacte le rendement de la turbomachine, les matériaux CMC permettent donc d’améliorer le rendement moteur ce qui réduit la consommation de carburant. Par ailleurs, leur utilisation contribue à optimiser les performances des turbomachines notamment par la baisse de la masse globale de la turbomachine qui contribue encore à une diminution de la consommation de carburant et donc à la réduction significative des émissions polluantes.Ceramic matrix composite materials withstand temperatures ranging from 600°C to 1400°C. Due to their better resistance to high temperatures, CMCs require less cooling. This cooling traditionally comes from a sample in the compressor which impacts the efficiency of the turbomachine, CMC materials therefore make it possible to improve engine efficiency which reduces fuel consumption. Furthermore, their use contributes to optimizing the performance of turbomachines, in particular by reducing the overall mass of the turbomachine, which further contributes to a reduction in fuel consumption and therefore to a significant reduction in polluting emissions.
Les pièces en CMC peuvent être densifiées par infiltration à l’état fondu. Dans cette technique, une composition de silicium fondu peut être introduite dans la porosité d’une structure fibreuse pré-densifiée par un dépôt de carbure de silicium et chargée par des particules de carbure de silicium. Cette méthode permet d’obtenir une matrice Si-SiC totalement dense de haut module et un composite à haute limite de linéarité. Les composites obtenus présentent de bonnes propriétés mécaniques mais les inventeurs ont observé une certaine variabilité dans l’allongement à rupture qui diminue la tolérance aux dommages du matériau. Il est souhaitable de proposer une solution pour répondre à cet inconvénient.CMC parts can be densified by melt infiltration. In this technique, a molten silicon composition can be introduced into the porosity of a fibrous structure pre-densified by a silicon carbide deposit and loaded with silicon carbide particles. This method makes it possible to obtain a completely dense high modulus Si-SiC matrix and a composite with a high linearity limit. The composites obtained have good mechanical properties but the inventors observed a certain variability in the elongation at break which reduces the damage tolerance of the material. It is desirable to propose a solution to address this drawback.
L’invention concerne un procédé de fabrication d’une pièce en matériau composite à matrice céramique, comprenant :
- l’infiltration d’une structure fibreuse pré-densifiée par une composition d’infiltration à l’état fondu comprenant du silicium afin de former une matrice céramique dans une porosité résiduelle de ladite structure fibreuse pré-densifiée, ladite structure fibreuse pré-densifiée comprenant une matrice de pré-densification comprenant une première couche de carbure de silicium et une deuxième couche protectrice recouvrant la première couche et apte à protéger celle-ci d’une attaque par le silicium de la composition d’infiltration, la deuxième couche protectrice étant formée par un système binaire B-C ou par un système ternaire Si-B-C.The invention relates to a method of manufacturing a part made of ceramic matrix composite material, comprising:
- the infiltration of a pre-densified fibrous structure with a melt infiltration composition comprising silicon in order to form a ceramic matrix in a residual porosity of said pre-densified fibrous structure, said pre-densified fibrous structure comprising a pre-densification matrix comprising a first layer of silicon carbide and a second protective layer covering the first layer and capable of protecting the latter from attack by the silicon of the infiltration composition, the second protective layer being formed by a binary system BC or by a ternary system Si-BC.
Les inventeurs ont constaté que la variabilité du comportement à rupture était liée à une attaque non maîtrisée du carbure de silicium de la matrice de pré-densification par le silicium fondu dans la solution de l’art antérieur. Ce phénomène peut aller jusqu’à la dégradation du renfort fibreux et de l’interphase résultant en une diminution du caractère structural du composite. L’invention propose une fonctionnalisation de la matrice de pré-densification de sorte à y intégrer une couche protectrice telle que décrite plus haut qui permet de réduire l’attaque du carbure de silicium de la matrice de pré-densification. La couche protectrice, faisant partie intégrante de la matrice de pré-densification, est répartie de manière homogène dans la structure fibreuse pré-densifiée pour apporter une protection dans tout son volume et tout au long de l’infiltration. On obtient ainsi des matériaux composites avec un comportement à rupture bien plus performant.The inventors noted that the variability of the fracture behavior was linked to an uncontrolled attack on the silicon carbide of the pre-densification matrix by the molten silicon in the solution of the prior art. This phenomenon can go as far as the degradation of the fibrous reinforcement and the interphase resulting in a reduction in the structural character of the composite. The invention proposes a functionalization of the pre-densification matrix so as to integrate a protective layer as described above which makes it possible to reduce the attack of the silicon carbide of the pre-densification matrix. The protective layer, forming an integral part of the pre-densification matrix, is distributed homogeneously in the pre-densified fibrous structure to provide protection throughout its volume and throughout infiltration. We thus obtain composite materials with much more efficient breaking behavior.
Dans un exemple de réalisation, la matrice de pré-densification comprend en outre une couche protectrice additionnelle de pyrocarbone recouvrant la deuxième couche.In an exemplary embodiment, the pre-densification matrix further comprises an additional protective layer of pyrocarbon covering the second layer.
Une telle caractéristique permet avantageusement de fournir une source de carbone supplémentaire permettant de réduire davantage encore le risque d’une attaque du carbure de silicium de la matrice de pré-densification.Such a characteristic advantageously makes it possible to provide an additional source of carbon making it possible to further reduce the risk of attack on the silicon carbide of the pre-densification matrix.
Dans un exemple de réalisation, la composition d’infiltration comprend du bore.In an exemplary embodiment, the infiltration composition comprises boron.
Une telle caractéristique permet avantageusement de protéger davantage encore le carbure de silicium sous-jacent.Such a characteristic advantageously makes it possible to further protect the underlying silicon carbide.
Dans un exemple de réalisation, la deuxième couche protectrice est en carbure de bore, avec éventuellement présence de carbone libre en excès, ou en carbone dopé au bore avec du bore en une proportion atomique comprise entre 5% et 20%.In an exemplary embodiment, the second protective layer is made of boron carbide, possibly with the presence of excess free carbon, or of carbon doped with boron with boron in an atomic proportion of between 5% and 20%.
Une telle couche protectrice présente l’avantage d’être relativement simple à former.Such a protective layer has the advantage of being relatively simple to form.
En variante, la deuxième couche protectrice est formée par un système ternaire Si-B-C ayant, en pourcentage atomique, une teneur en bore comprise entre 56% et 79%, une teneur en carbone comprise entre 17% et 39% et une teneur en silicium comprise entre 3% et 6%.Alternatively, the second protective layer is formed by a ternary Si-B-C system having, in atomic percentage, a boron content of between 56% and 79%, a carbon content of between 17% and 39% and a silicon content between 3% and 6%.
L’emploi d’un système ternaire Si-B-C est avantageux dans la mesure où il ne nécessite pas d’ajouter un précurseur carboné, rendant le système de traitement des effluents d’un four SiC-CVI compatible de la formation de ce système.The use of a ternary Si-B-C system is advantageous in that it does not require adding a carbon precursor, making the effluent treatment system from a SiC-CVI furnace compatible with the formation of this system.
Dans un exemple de réalisation, la structure fibreuse pré-densifiée comprend un renfort fibreux partiellement densifié par la matrice de pré-densification, et la deuxième couche protectrice, ou l’éventuelle couche protectrice additionnelle, forme la couche de la matrice de pré-densification la plus éloignée du renfort fibreux.In an exemplary embodiment, the pre-densified fibrous structure comprises a fibrous reinforcement partially densified by the pre-densification matrix, and the second protective layer, or the possible additional protective layer, forms the layer of the pre-densification matrix furthest from the fibrous reinforcement.
Dans un exemple de réalisation, une épaisseur de la deuxième couche est comprise entre 0,1 µm et 4 µm.In an exemplary embodiment, a thickness of the second layer is between 0.1 µm and 4 µm.
Une telle caractéristique permet d’obtenir un bon compromis entre une protection efficace du carbure de silicium de pré-densification durant l’infiltration, sans pénaliser le temps de fabrication de la pièce par maîtrise de l’épaisseur de la couche protectrice.Such a characteristic makes it possible to obtain a good compromise between effective protection of the pre-densification silicon carbide during infiltration, without penalizing the manufacturing time of the part by controlling the thickness of the protective layer.
Dans un exemple de réalisation, la structure fibreuse pré-densifiée comprend en outre une interphase de nitrure de bore entre un renfort fibreux et la matrice de pré-densification.In an exemplary embodiment, the pre-densified fibrous structure further comprises a boron nitride interphase between a fibrous reinforcement and the pre-densification matrix.
La présence d’une interphase de nitrure de bore permet avantageusement de dévier les fissures qui peuvent apparaître dans la matrice de la pièce composite en fonctionnement de sorte à préserver le renfort fibreux, et d’apporter une résistance à l’oxydation.The presence of a boron nitride interphase advantageously makes it possible to deflect cracks which may appear in the matrix of the composite part in operation so as to preserve the fibrous reinforcement, and to provide resistance to oxidation.
Dans un exemple de réalisation, la structure fibreuse pré-densifiée comprend un renfort fibreux formé par tissage tridimensionnel ou à partir d’une pluralité de strates fibreuses bidimensionnelles.In an exemplary embodiment, the pre-densified fibrous structure comprises a fibrous reinforcement formed by three-dimensional weaving or from a plurality of two-dimensional fibrous layers.
Dans un exemple de réalisation, la pièce est une pièce de turbomachine.In an exemplary embodiment, the part is a turbomachine part.
La pièce peut être une pièce de turbine, par exemple une pièce de turbine de moteur d’aéronef. La pièce peut par exemple être une aube de turbomachine, un secteur d’anneau de turbine ou un distributeur.The part may be a turbine part, for example an aircraft engine turbine part. The part can for example be a turbomachine blade, a turbine ring sector or a distributor.
Un exemple de procédé de fabrication d’une pièce en matériau CMC selon l’invention va maintenant être décrit en lien avec l’ordinogramme de la
Une première étape S10 du procédé peut consister à former la structure fibreuse par mise en œuvre d’une ou plusieurs opérations textiles comme un tissage tridimensionnel. La structure fibreuse peut être formée de fils céramiques, par exemple de fils en carbure de silicium. La structure fibreuse peut constituer le renfort fibreux 10 de la pièce en matériau composite à obtenir. Des exemples de fils en carbure de silicium utilisables peuvent être des fils commercialisés sous la référence « Nicalon », « Hi-Nicalon », « Hi-Nicalon-S » ou Tyranno SA3 de la société UBE Industries. Les fils céramiques de la structure fibreuse peuvent présenter une teneur en oxygène inférieure ou égale à 1% en pourcentage atomique. Les fils « Hi-Nicalon-S », par exemple, présentent une telle caractéristique. Par « tissage tridimensionnel » ou « tissage 3D », il faut comprendre un mode de tissage par lequel certains au moins des fils de chaine lient des fils de trame sur plusieurs couches de trame. Une inversion des rôles entre chaine et trame est possible dans le présent texte et doit être considérée comme couverte aussi par les revendications. La structure fibreuse peut par exemple présenter une armure interlock. Par « armure ou tissu interlock », il faut comprendre une armure de tissage 3D dont chaque couche de fils de chaîne lie plusieurs couches de fils de trame avec tous les fils de la même colonne de chaîne ayant le même mouvement dans le plan de l’armure. Il est aussi possible de partir de textures fibreuses telles que des tissus bidimensionnels ou des nappes unidirectionnelles, et d’obtenir la structure fibreuse par drapage de telles textures fibreuses sur une forme. Ces textures peuvent éventuellement être liées entre elles par exemple par couture ou implantation de fils pour former la structure fibreuse.A first step S10 of the process may consist of forming the fibrous structure by implementing one or more textile operations such as three-dimensional weaving. The fibrous structure can be formed from ceramic wires, for example silicon carbide wires. The fibrous structure can constitute the fibrous reinforcement 10 of the composite material part to be obtained. Examples of usable silicon carbide wires may be wires marketed under the reference “Nicalon”, “Hi-Nicalon”, “Hi-Nicalon-S” or Tyranno SA3 from the company UBE Industries. The ceramic yarns of the fibrous structure may have an oxygen content less than or equal to 1% in atomic percentage. “Hi-Nicalon-S” threads, for example, have such a characteristic. By “three-dimensional weaving” or “3D weaving”, we must understand a mode of weaving by which at least some of the warp threads bind weft threads on several weft layers. A reversal of roles between warp and weft is possible in the present text and must be considered as also covered by the claims. The fibrous structure can for example have an interlock weave. By “weave or interlock fabric”, we must understand a 3D weave weave in which each layer of warp threads links several layers of weft threads with all the threads of the same warp column having the same movement in the plane of the armor. It is also possible to start from fibrous textures such as two-dimensional fabrics or unidirectional webs, and to obtain the fibrous structure by draping such fibrous textures on a form. These textures can possibly be linked together, for example by sewing or implantation of threads to form the fibrous structure.
Dans une étape S20, on peut former une interphase 20 de défragilisation par infiltration chimique en phase vapeur (« Chemical Vapor Infiltration ») sur les fils de la structure fibreuse. La structure fibreuse peut être positionnée dans un outillage de conformation permettant de la mettre à la forme de la pièce à obtenir durant le dépôt de l’interphase. L’épaisseur e20de l’interphase peut par exemple être comprise entre 10 nm et 1000 nm, et par exemple entre 200 nm et 500 nm. Après formation de l’interphase, la structure fibreuse reste poreuse, la porosité accessible initiale n’étant comblée que pour une partie minoritaire par l’interphase. L’interphase peut être monocouche ou multicouches. L’interphase peut comporter au moins une couche de carbone pyrolytique (PyC), de nitrure de bore (BN), de nitrure de bore dopé au silicium (BN(Si), avec du silicium en une proportion massique comprise entre 5% et 40%, le complément étant du nitrure de bore) ou de carbone dopé au bore (BC, avec du bore en une proportion atomique comprise entre 5% et 20%, le complément étant du carbone). L’interphase a ici une fonction de défragilisation du matériau composite qui favorise la déviation de fissures éventuelles parvenant à l’interphase après s’être propagées dans la matrice, empêchant ou retardant la rupture de fibres par de telles fissures. En variante, on notera qu’il est possible de former l’interphase sur les fils avant la formation de la structure fibreuse, c’est-à-dire avant mise en œuvre de l’étape S10.In a step S20, an interphase 20 of defragmentation can be formed by chemical vapor infiltration (“Chemical Vapor Infiltration”) on the threads of the fibrous structure. The fibrous structure can be positioned in conformation tooling allowing it to be shaped into the shape of the part to be obtained during the deposition of the interphase. The thickness e 20 of the interphase can for example be between 10 nm and 1000 nm, and for example between 200 nm and 500 nm. After formation of the interphase, the fibrous structure remains porous, the initial accessible porosity being filled for only a minority part by the interphase. The interphase can be single-layer or multi-layer. The interphase may comprise at least one layer of pyrolytic carbon (PyC), boron nitride (BN), boron nitride doped with silicon (BN(Si), with silicon in a mass proportion of between 5% and 40 %, the complement being boron nitride) or carbon doped with boron (BC, with boron in an atomic proportion of between 5% and 20%, the complement being carbon). The interphase here has a function of weakening the composite material which promotes the deflection of possible cracks reaching the interphase after having propagated in the matrix, preventing or delaying the rupture of fibers by such cracks. Alternatively, it will be noted that it is possible to form the interphase on the wires before the formation of the fibrous structure, that is to say before implementation of step S10.
Il est ensuite réalisé une étape S30 de formation d’un dépôt de carbure de silicium. Cette étape S30 peut être séparée en deux phases. Lors de la première phase, la structure fibreuse est toujours dans l’outillage de conformation et une couche 301 de consolidation de carbure de silicium est déposée sur l’interphase 20 et le renfort fibreux 10. La couche 301 de consolidation peut être déposée au contact de l’interphase 20. Cette couche a une épaisseur suffisante pour lier suffisamment les fibres de sorte que la structure conserve sa forme sans assistance de l’outillage de maintien. Cette couche apporte une protection à l’interphase vis-à-vis de l’oxydation et peut être formée par infiltration chimique en phase vapeur de manière connue en soi, par exemple à partir d’une phase gazeuse comprenant du méthyltrichlorosilane (MTS) et de l’hydrogène (H2). L’épaisseur e301de la couche 301 de consolidation peut être supérieure ou égale à 0,1 µm, par exemple comprise entre 0,1 µm et 5 µm. Lors de la deuxième phase, la structure fibreuse consolidée et mise à la forme de la pièce à obtenir peut être retirée de l’outillage et la formation de la matrice 35 de pré-densification peut être initiée en déposant une première couche 302 de celle-ci en carbure de silicium. La première couche 302 peut être déposée au contact de la couche 301 de consolidation. L’épaisseur e302de la première couche 302 peut être supérieure à l’épaisseur e301de la couche 301 de consolidation. Cette première couche de carbure de silicium apporte une large contribution de performance mécanique au matériau composite et apporte une protection vis-à-vis du silicium fondu mis en œuvre lors de l’infiltration ultérieure. L’épaisseur e302de la première couche 302 peut être supérieure ou égale à 1 µm, par exemple comprise entre 1 µm et 20 µm. Comme pour la couche de consolidation, la première couche de la matrice de pré-densification peut être formée par infiltration chimique en phase vapeur de manière connue en soi. D’une manière générale, la matrice de pré-densification peut être formée par infiltration chimique en phase vapeur. Selon une variante non illustrée, la couche 301 pourrait être omise et l’on pourrait directement former la première couche 302 de la matrice de pré-densification sur l’interphase 20. La formation de la matrice de pré-densification peut être poursuivie par formation du dépôt protecteur sur la première couche (étape S40). Comme indiqué plus haut, ce dépôt permet de protéger le carbure de silicium sous-jacent de l’attaque par le silicium fondu. Différentes structures sont envisageables pour ce dépôt, comme illustré aux figures 2 et 3.A step S30 of forming a silicon carbide deposit is then carried out. This step S30 can be separated into two phases. During the first phase, the fibrous structure is still in the conformation tooling and a consolidation layer 301 of silicon carbide is deposited on the interphase 20 and the fibrous reinforcement 10. The consolidation layer 301 can be deposited in contact of the interphase 20. This layer has sufficient thickness to sufficiently bind the fibers so that the structure retains its shape without assistance from the holding tooling. This layer provides protection to the interphase against oxidation and can be formed by chemical vapor infiltration in a manner known per se, for example from a gas phase comprising methyltrichlorosilane (MTS) and hydrogen (H 2 ). The thickness e 301 of the consolidation layer 301 may be greater than or equal to 0.1 µm, for example between 0.1 µm and 5 µm. During the second phase, the fibrous structure consolidated and shaped into the part to be obtained can be removed from the tooling and the formation of the pre-densification matrix 35 can be initiated by depositing a first layer 302 of it. here in silicon carbide. The first layer 302 can be deposited in contact with the consolidation layer 301. The thickness e 302 of the first layer 302 may be greater than the thickness e 301 of the consolidation layer 301. This first layer of silicon carbide provides a large contribution of mechanical performance to the composite material and provides protection against the molten silicon used during subsequent infiltration. The thickness e 302 of the first layer 302 may be greater than or equal to 1 µm, for example between 1 µm and 20 µm. As for the consolidation layer, the first layer of the pre-densification matrix can be formed by chemical vapor infiltration in a manner known per se. Generally speaking, the pre-densification matrix can be formed by chemical vapor infiltration. According to a variant not illustrated, the layer 301 could be omitted and the first layer 302 of the pre-densification matrix could be directly formed on the interphase 20. The formation of the pre-densification matrix can be continued by formation of the protective deposit on the first layer (step S40). As indicated above, this deposit protects the underlying silicon carbide from attack by molten silicon. Different structures are possible for this deposit, as illustrated in Figures 2 and 3.
Dans l’exemple de la
Dans l’exemple de la
Le taux volumique de porosité résiduelle de la structure fibreuse pré-densifiée obtenue suite à l’étape S40 peut être supérieur ou égal à 20%, par exemple compris entre 20% et 40%, par exemple entre 30% et 35%.The residual porosity volume rate of the pre-densified fibrous structure obtained following step S40 may be greater than or equal to 20%, for example between 20% and 40%, for example between 30% and 35%.
Le procédé se poursuit par introduction d’une composition pulvérulente dans une porosité résiduelle de la structure pré-densifiée (étape S50). Cette composition pulvérulente peut être introduite dans la structure fibreuse par voie barbotine (« slurry-cast ») de manière connue en soi. La composition pulvérulente peut comprendre une poudre de carbure de silicium et/ou une poudre de carbone et/ou une poudre de carbure de bore. Le taux volumique de porosité résiduelle de la structure fibreuse pré-densifiée et chargée par la composition pulvérulente peut être inférieur ou égal à 25%, par exemple compris entre 15% et 25%. Si cela est souhaité, on peut procéder à une désoxydation de la poudre de carbure de silicium avant l’infiltration par application d’une température supérieure ou égale à 1250°C pendant une durée d’au moins 30 minutes sous vide ou une pression inférieure ou égale à 100 mbar d’un gaz neutre.The process continues by introducing a powder composition into a residual porosity of the pre-densified structure (step S50). This powdery composition can be introduced into the fibrous structure by slurry-cast method in a manner known per se. The powder composition may comprise a silicon carbide powder and/or a carbon powder and/or a boron carbide powder. The residual porosity volume rate of the pre-densified fibrous structure loaded with the powder composition may be less than or equal to 25%, for example between 15% and 25%. If desired, the silicon carbide powder can be deoxidized before infiltration by applying a temperature greater than or equal to 1250°C for a period of at least 30 minutes under vacuum or a lower pressure. or equal to 100 mbar of a neutral gas.
Une fois la composition pulvérulente introduite, on réalise l’étape S60 durant laquelle on infiltre la porosité résiduelle avec une composition d’infiltration à l’état fondu comprenant au moins du silicium de manière à former une matrice céramique dans la porosité de la structure fibreuse. La formation de cette matrice céramique peut permettre de finaliser la densification de la pièce. Cette étape d’infiltration correspond à une étape d’infiltration à l’état fondu. La composition d’infiltration peut être constituée de silicium pur fondu ou en variante être sous la forme d’un alliage fondu de silicium et d’un ou plusieurs autres constituants. La composition d’infiltration peut comprendre majoritairement en masse du silicium, c’est-à-dire présenter une teneur massique en silicium supérieure ou égale à 50%. La composition d’infiltration peut par exemple présenter une teneur massique en silicium supérieure ou égale à 75%. Le(s) constituant(s) présent(s) au sein de l’alliage de silicium peuvent être choisi(s) parmi B, Al, Mo, Ti, Ge et leurs mélanges. Lorsque la composition pulvérulente comprend des particules de carbone, une réaction chimique peut se produire entre la composition d’infiltration et ces particules de carbone lors de l’infiltration aboutissant à la formation de carbure de silicium.Once the powder composition has been introduced, step S60 is carried out during which the residual porosity is infiltrated with a melt infiltration composition comprising at least silicon so as to form a ceramic matrix in the porosity of the fibrous structure. . The formation of this ceramic matrix can make it possible to finalize the densification of the part. This infiltration step corresponds to a melt infiltration step. The infiltration composition may consist of pure molten silicon or alternatively be in the form of a molten alloy of silicon and one or more other constituents. The infiltration composition may comprise a majority of silicon by mass, that is to say have a silicon mass content greater than or equal to 50%. The infiltration composition may for example have a silicon mass content greater than or equal to 75%. The constituent(s) present within the silicon alloy can be chosen from B, Al, Mo, Ti, Ge and their mixtures. When the powder composition comprises carbon particles, a chemical reaction can occur between the infiltration composition and these carbon particles during infiltration resulting in the formation of silicon carbide.
Après l’étape S60, on obtient une pièce en matériau CMC. Une telle pièce en matériau CMC peut être une pièce statique ou rotative de turbomachine. Des exemples de pièces de turbomachine ont été mentionnés plus haut. Une telle pièce peut en outre être revêtue d’un revêtement de barrière environnementale ou thermique avant son utilisation.After step S60, we obtain a part made of CMC material. Such a part made of CMC material can be a static or rotating part of a turbomachine. Examples of turbomachine parts have been mentioned above. Such a part may additionally be coated with an environmental or thermal barrier coating before use.
L’expression « compris(e) entre … et … » doit se comprendre comme incluant les bornes.The expression “between… and…” must be understood as including the limits.
Claims (10)
- l’infiltration (S60) d’une structure fibreuse pré-densifiée par une composition d’infiltration à l’état fondu comprenant du silicium afin de former une matrice céramique dans une porosité résiduelle de ladite structure fibreuse pré-densifiée, ladite structure fibreuse pré-densifiée comprenant une matrice (35 ; 35a) de pré-densification comprenant une première couche (302) de carbure de silicium et une deuxième couche (40) protectrice recouvrant la première couche et apte à protéger celle-ci d’une attaque par le silicium de la composition d’infiltration, la deuxième couche protectrice étant formée par un système binaire B-C ou par un système ternaire Si-B-C.Process for manufacturing a part made of ceramic matrix composite material, comprising:
- infiltration (S60) of a pre-densified fibrous structure with a melt infiltration composition comprising silicon in order to form a ceramic matrix in a residual porosity of said pre-densified fibrous structure, said fibrous structure pre-densified comprising a pre-densification matrix (35; 35a) comprising a first layer (302) of silicon carbide and a second protective layer (40) covering the first layer and capable of protecting the latter from attack by the silicon of the infiltration composition, the second protective layer being formed by a binary BC system or by a ternary Si-BC system.