FR2717416A1 - Wet concrete spraying process. - Google Patents
Wet concrete spraying process. Download PDFInfo
- Publication number
- FR2717416A1 FR2717416A1 FR9403260A FR9403260A FR2717416A1 FR 2717416 A1 FR2717416 A1 FR 2717416A1 FR 9403260 A FR9403260 A FR 9403260A FR 9403260 A FR9403260 A FR 9403260A FR 2717416 A1 FR2717416 A1 FR 2717416A1
- Authority
- FR
- France
- Prior art keywords
- mixture
- concrete
- precipitated silica
- silica
- tempered
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
PROCEDE DE PROJECTION DE BETON PAR VOIE HUMIDE
La présente invention concerne un procédé de projection de béton par voie humide mettant en oeuvre une silice précipitée.WET CONCRETE SPRAYING PROCESS
The present invention relates to a wet spraying method of concrete using precipitated silica.
L'utilisation de procédés de projection de béton pour appliquer une couche de béton projeté sur une surface à bétonner est bien connue. The use of concrete spraying methods to apply a layer of sprayed concrete on a surface to be concreted is well known.
II existe ainsi aujourd'hui essentiellement deux types de procédés de projection de béton : les procédés de projection de béton par voie sèche et les procédés de projection de béton par voie humide. Today, there are essentially two types of concrete spraying methods: concrete spraying methods by the dry method and concrete spraying methods by the wet method.
Dans les procédés de projection de béton par voie sèche, on forme d'abord un mélange sec comprenant tous les composants anhydres traditionnels d'un béton, c'està-dire un mélange comprenant du ciment, des granulats, généralement une charge telle que du sable et éventuellement des additifs sous forme solide ; ce mélange, qui doit être aussi sec que possible, est ensuite véhiculé généralement sous air comprimé, par voie pneumatique, dans une gaine de projection, vers une buse de projection ; ledit mélange est alors mélangé à de l'eau juste en aval de la buse de projection, le cisaillement subi par le mélange eau + solides (qui constituent le mélange anhydre initial) dans la gaine de projection devant théoriquement assurer l'homogénéité du béton final ; le mélange obtenu est alors projeté, à partir de la buse de projection, à l'aide d'air comprimé (air de projection ou air propulseur), sur la surface à bétonner. In dry concrete spraying processes, a dry mixture is first formed comprising all the traditional anhydrous components of a concrete, that is to say a mixture comprising cement, aggregates, generally a filler such as sand and optionally additives in solid form; this mixture, which must be as dry as possible, is then generally conveyed under compressed air, pneumatically, in a projection sheath, to a projection nozzle; said mixture is then mixed with water just downstream of the spray nozzle, the shear undergone by the water + solids mixture (which constitute the initial anhydrous mixture) in the spray sheath theoretically ensuring the homogeneity of the final concrete ; the mixture obtained is then sprayed, from the spray nozzle, using compressed air (spray air or propellant air), onto the surface to be concreted.
L'inconvénient majeur de ce type de procédé de projection de béton est la perte importante par rebond du béton à partir de la surface à bétonner lors de la phase de projection. De plus, la formation de poussière est élevée, ce qui constitue un risque pour l'environnement, mais également, tout comme le rebond important du béton, pour le technicien qui met en oeuvre le procédé. Enfin, I'homogénéité du mélange de béton final n'est pas toujours satisfaisante, du fait notamment d'un temps de mélange eau + solides relativement court. The major drawback of this type of concrete spraying process is the significant loss by rebound of the concrete from the surface to be concreted during the spraying phase. In addition, dust formation is high, which constitutes a risk for the environment, but also, like the significant rebound of concrete, for the technician who implements the process. Finally, the homogeneity of the final concrete mixture is not always satisfactory, due in particular to a relatively short water + solid mixing time.
Il a été alors proposé d'employer de la fumée de silice pour diminuer la perte par rebond. It was then proposed to use silica smoke to reduce the rebound loss.
Néanmoins, l'ajout de fumée de silice sous forme de poudre au mélange sec initial entraîne la formation de poussière et l'homogénéité du mélange de béton final n'est pas améliorée. However, the addition of silica smoke in powder form to the initial dry mix results in the formation of dust and the homogeneity of the final concrete mix is not improved.
Si l'utilisation de fumée de silice en suspension aqueuse, introduite juste en aval de la buse de projection, éventuellement en mélange avec l'eau, peut permettre d'abaisser un peu plus la perte par rebond, elle s'accompagne d'un poussièrage toujours aussi important ; aucune amélioration n'est par ailleurs constatée au niveau de l'homogénéité du mélange de béton final. If the use of silica smoke in aqueous suspension, introduced just downstream of the spray nozzle, possibly mixed with water, can make it possible to lower the rebound loss a little more, it is accompanied by a dust still as important; no improvement is moreover observed in terms of the homogeneity of the final concrete mixture.
Dans les procédés de projection de béton par voie humide, on forme d'abord un mélange comprenant du ciment, des granulats, de l'eau (dite eau de gâchage), et éventuellement des additifs (ce mélange forme du béton dit gâché) ; ce mélange est ensuite généralement véhiculé au moyen d'une pompe dans une gaine de projection, vers une buse de projection ; ledit mélange est alors projeté, à partir de la buse de projection, à l'aide d'air comprimé (air de projection ou air propulseur), sur la surface à bétonner. In wet concrete spraying processes, a mixture is first formed comprising cement, aggregates, water (so-called mixing water), and possibly additives (this mixture forms so-called mixed concrete); this mixture is then generally conveyed by means of a pump in a projection sheath, to a projection nozzle; said mixture is then sprayed, from the spray nozzle, using compressed air (spray air or propellant air), onto the surface to be concreted.
Ces procédés possèdent, de manière générale, par rapport aux procédés de projection de béton par voie sèche un certain nombre d'avantages : le rapport eau/ciment, qui est un paramètre de qualité essentiel du béton, peut être réglé à volonté et, notamment, maintenu à une valeur constante ; le ciment est habituellement bien mouillé et le béton final est plus homogène ; enfin, la formation de poussière diminue. These processes generally have a number of advantages over spraying concrete by dry methods: the water / cement ratio, which is an essential quality parameter of concrete, can be adjusted at will and, in particular , maintained at a constant value; the cement is usually well wetted and the final concrete is more homogeneous; finally, dust formation decreases.
Cependant, ces procédés présentent quelques inconvénients ; ainsi, la densité du béton est réduite du fait de la présence, dans le mélange initial de béton, d'eau excédentaire non consommée lors de l'hydratation, d'où un amoindrissement de l'épaisseur de couche de béton projeté en une passe ; si l'addition de verre soluble dans le mélange initial de béton peut diminuer ce temps de prise, elle nuit en revanche à la résistance mécanique dans le temps du béton une fois projeté. However, these methods have some drawbacks; thus, the density of the concrete is reduced due to the presence, in the initial concrete mixture, of excess water not consumed during hydration, hence a reduction in the thickness of the layer of concrete sprayed in one pass ; If the addition of water glass in the initial concrete mixture can reduce this setting time, it however affects the mechanical resistance over time of the concrete once sprayed.
Il a été proposé d'introduire dans le mélange de béton un accélérateur de prise
I'inconvénient réside notamment dans le fait que les propriétés mécaniques du béton projeté final s'en trouvent le plus souvent dégradées.It has been proposed to introduce a setting accelerator into the concrete mixture.
The disadvantage lies in particular in the fact that the mechanical properties of the final shotcrete are most often degraded.
La présente invention a notamment pour but de proposer un nouveau procédé de projection de béton, qui non seulement est une alternative aux procédés décrits précédemment, mais qui, en plus de ne pas présenter les inconvénients susmentionnés, possèdent au moins les avantages essentiels des procédés "voie humide". The object of the present invention is in particular to propose a new method of spraying concrete, which not only is an alternative to the methods described above, but which, in addition to not having the abovementioned drawbacks, have at least the essential advantages of the methods " wet ".
Ainsi, le but de l'invention est en particulier de fournir un procédé de projection de béton par voie humide mettant en ouvre une silice précipitée, procédé dans lequel la silice se disperse bien dans le mélange de béton gâché et donc le mélange de béton final est homogène, la formation de poussière est faible, I'appareillage utilisé est simple, un compromis très satisfaisant propriétés mécaniques (notamment résistance mécanique) - faible perte par rebond peut être obtenu et l'épaisseur de couche de béton projeté est de préférence assez élevée. Thus, the object of the invention is in particular to provide a wet concrete spraying process using precipitated silica, a process in which the silica disperses well in the mixture of mixed concrete and therefore the mixture of final concrete is homogeneous, the formation of dust is low, the apparatus used is simple, a very satisfactory compromise mechanical properties (in particular mechanical resistance) - low loss by rebound can be obtained and the thickness of layer of shotcrete is preferably quite high .
Ce but et d'autres sont atteints par l'invention, qui présente deux variantes de réalisation. This object and others are achieved by the invention, which presents two alternative embodiments.
Selon la première variante, I'invention concerne un procédé de projection de béton par voie humide pour appliquer sur une surface une couche de béton, dans lequel on forme un mélange de béton gâché, on déplace ledit mélange gâché pour l'introduire dans un moyen de projection et on projette ledit mélange gâché à partir dudit moyen de projection sur la surface, caractérisé en ce que ledit mélange de béton gâché est formé à partir de ciment, de granulats, d'eau et d'au moins une silice précipitée. According to the first variant, the invention relates to a wet concrete spraying method for applying a layer of concrete to a surface, in which a mixture of tempered concrete is formed, said tempered mixture is moved to introduce it into a means spraying and said mixed mixture is projected from said projection means on the surface, characterized in that said mixed concrete mixture is formed from cement, aggregates, water and at least one precipitated silica.
Selon la seconde variante, I'invention concerne un procédé de projection de béton par voie humide pour appliquer sur une surface une couche de béton, dans lequel on forme un mélange de béton gâché, on déplace ledit mélange gâché pour l'introduire dans un moyen de projection et on projette ledit mélange gâché à partir dudit moyen de projection sur la surface, caractérisé en ce que ledit mélange de béton gâché est formé à partir de ciment, de granulats, d'eau, d'au moins un retardateur de prise et d'au moins une silice précipitée et en ce qu'on incorpore au moins un accélérateur de prise audit mélange gâché juste avant ou pendant l'introduction dudit mélange dans le moyen de projection. According to the second variant, the invention relates to a wet concrete spraying method for applying a layer of concrete to a surface, in which a mixed concrete mixture is formed, said mixed mixture is moved to introduce it into a means. spraying and said tempered mixture is projected from said projection means onto the surface, characterized in that said tempered concrete mixture is formed from cement, aggregates, water, at least one setting retarder and at least one precipitated silica and in that at least one setting accelerator is incorporated into said mixed mixture just before or during the introduction of said mixture into the spraying means.
Les Demanderesses ont notamment constaté que, de manière surprenante,
I'invention ne présentait pas les inconvénients d'un procédé de projection de béton dans lequel l'ajout d'une silice précipitée, au mélange de béton gâché, s'effectuerait juste avant la buse de projection et en mélange avec l'air propulseur, en particulier : une homogénéité du béton final peu satisfaisante, un poussiérage certain, un appareillage de mise en oeuvre quelque peu complexe.The Applicants have observed in particular that, surprisingly,
The invention did not have the drawbacks of a concrete spraying process in which the addition of precipitated silica to the mixture of tempered concrete would take place just before the spray nozzle and in admixture with the propellant air , in particular: unsatisfactory homogeneity of the final concrete, certain dust, somewhat complex processing equipment.
D'autres caractéristiques, détails et avantages de l'invention apparaîtront plus clairement à la lecture de la description qui va suivre. Other characteristics, details and advantages of the invention will appear more clearly on reading the description which follows.
Dans les deux variantes de réalisation de l'invention, les moyens utilisés pour former le mélange de béton gâché, qui doit être pompable et projetable, pour déplacer puis introduire ce mélange dans le moyen de projection et pour projeter le mélange sur la surface à bétonner à partir dudit moyen correspondent à ceux généralement employés dans le domaine de la projection de béton par voie humide et sont donc bien connus de l'homme du métier. In the two alternative embodiments of the invention, the means used to form the mixture of tempered concrete, which must be pumpable and sprayable, to move and then introduce this mixture into the spraying means and to spray the mixture onto the surface to be concreted from said means correspond to those generally used in the field of wet concrete spraying and are therefore well known to those skilled in the art.
Ainsi, le mélange de béton gâché est en général formé par malaxage des produits entrant dans sa composition , I'ordre d'introduction desdits produits dans le malaxeur peut être quelconque ; en général, les granulats, le ciment et la silice sont d'abord malaxés entre eux, I'eau étant ensuite introduite, le mélange humide ainsi formé étant enfin malaxé (les éventuels additifs peuvent être incorporés à tout moment adéquat lors de la formation du mélange gâché). Thus, the mixture of tempered concrete is generally formed by mixing the products entering into its composition, the order of introduction of said products into the mixer can be arbitrary; in general, the aggregates, the cement and the silica are first kneaded together, the water then being introduced, the wet mixture thus formed being finally kneaded (any additives can be incorporated at any suitable time during the formation of the spoiled mixture).
De plus, le mélange de béton gâché est introduit dans le moyen de projection généralement après avoir été véhiculé au moyen d'une pompe adéquate, par exemple une pompe à piston, dans une gaine de projection. In addition, the mixture of tempered concrete is introduced into the spraying means generally after having been conveyed by means of a suitable pump, for example a piston pump, in a spraying sheath.
Le moyen de projection est habituellement constitué par une buse de projection le mélange gâché est alors projeté, à partir de cette buse de projection, généralement à l'aide d'air propulseur qui alimente ladite buse, I'air propulseur étant habituellement de l'air comprimé. The projection means usually consists of a projection nozzle, the tempered mixture is then projected from this projection nozzle, generally using propellant air which supplies said nozzle, the propellant air usually being pressurized air.
L'utilisation d'au moins une silice précipitée et la formation du mélange gâché à partir notamment de ladite silice sont des caractéristiques essentielles de l'invention. The use of at least one precipitated silica and the formation of the mixed mixture from in particular said silica are essential characteristics of the invention.
Par silice précipitée, on entend ici une silice obtenue par précipitation à partir de la réaction d'un silicate alcalin avec un acide en général inorganique à un pH adéquat du milieu de précipitation, en particulier un pH basique, neutre ou peu acide ; le mode de préparation de la silice peut ici être quelconque (addition d'acide sur un pied de cuve de silicate, addition simultanée totale ou partielle d'acide et de silicate sur un pied de cuve d'eau ou de solution de silicate, etc...) et est choisi en fonction du type de silice que l'on souhaite obtenir. The term “precipitated silica” is understood here to mean a silica obtained by precipitation from the reaction of an alkaline silicate with a generally inorganic acid at an adequate pH of the precipitation medium, in particular a basic pH, neutral or slightly acid; the mode of preparation of the silica can be arbitrary here (addition of acid on a silicate base stock, total or partial simultaneous addition of acid and silicate on a base stock of water or silicate solution, etc. ...) and is chosen according to the type of silica that one wishes to obtain.
La silice précipitée peut être employée sous forme de poudre (sèche) ou en suspension aqueuse (slurry ou bouillie). The precipitated silica can be used in powder form (dry) or in aqueous suspension (slurry or boiled).
Même si la quantité en poids de silice précipitée utilisée n'est pas une caractéristique essentielle de l'invention, cette teneur peut être d'au plus 6 %, en particulier d'au plus 5 %, et, de préférence, comprise entre 2 et 4 %, par rapport au poids de ciment. En effet, même à ces teneurs relativement faibles en silice précipitée, les performances du procédé selon l'invention sont très satisfaisantes. Even if the quantity by weight of precipitated silica used is not an essential characteristic of the invention, this content can be at most 6%, in particular at most 5%, and preferably between 2 and 4%, based on the weight of cement. Indeed, even at these relatively low contents of precipitated silica, the performance of the process according to the invention is very satisfactory.
Les silices précipitées utilisées dans la présente invention possèdent préférentiellement une surface spécifique BET d'au moins 40 m2/g, notamment comprise entre 40 et 400 m2/g, par exemple entre 50 et 350 m2/g. The precipitated silicas used in the present invention preferably have a BET specific surface of at least 40 m2 / g, in particular between 40 and 400 m2 / g, for example between 50 and 350 m2 / g.
Selon un mode réalisation particulier, cette surface spécifique BET est comprise entre 210 et 300 m2/g. According to a particular embodiment, this specific BET surface is between 210 and 300 m2 / g.
La surface spécifique BET est déterminée selon la méthode de BRUNAUER
EMMET-TELLER décrite dans "The Journal of the American Chemical Society", vol. 60, page 309, février 1938 et correspondant à la norme ISO 5794/1 (annexe 1). The BET specific surface is determined according to the BRUNAUER method
EMMET-TELLER described in "The Journal of the American Chemical Society", vol. 60, page 309, February 1938 and corresponding to standard ISO 5794/1 (annex 1).
De même, les silices précipitées utilisées dans la présente invention possèdent préférentiellement une taille moyenne des particules d'au moins 0,5 um, notamment comprise entre 1 et 300 um, en particulier entre 1 et 40 um, voire entre 1 et 20 ijm ; elle peut être par exemple comprise entre 1,5 et 15 pu. Similarly, the precipitated silicas used in the present invention preferably have an average particle size of at least 0.5 μm, in particular between 1 and 300 μm, in particular between 1 and 40 μm, or even between 1 and 20 μm; it can for example be between 1.5 and 15 pu.
Selon des modes de réalisation particuliers, cette taille moyenne des particules est comprise entre 1,5 et 3,5 um ou entre 6 et 15 pu. According to particular embodiments, this average particle size is between 1.5 and 3.5 μm or between 6 and 15 μm.
La taille moyenne des particules est déterminée, pour les particules à taille élevée (au moins 100 um), de préférence selon la norme NFX-11507 (décembre 1970) par tamisage à sec et détermination de la taille correspondant à un refus cumulé de 50 %, et, pour les particules à taille faible (inférieure à 100 lit), de préférence par diffraction laser sur un granulomètre SYMPATEC. The average particle size is determined, for particles with a large size (at least 100 μm), preferably according to standard NFX-11507 (December 1970) by dry sieving and determination of the size corresponding to a cumulative refusal of 50%. , and, for particles of small size (less than 100 lit), preferably by laser diffraction on a SYMPATEC granulometer.
Dans la première variante de réalisation de l'invention, au moins un accélérateur de prise peut éventuellement être incorporé au mélange gâché juste avant (c'est-à-dire généralement après que celui-ci ait été véhiculé un certain temps au moyen d'une pompe) ou pendant (c'est-à-dire directement dans le moyen de projection) I'introduction dudit mélange dans le moyen de projection. In the first embodiment of the invention, at least one setting accelerator can optionally be incorporated into the tempered mixture just before (that is to say generally after it has been conveyed for a certain time by means of a pump) or during (that is to say directly into the spraying means) the introduction of said mixture into the spraying means.
Dans la seconde variante de réalisation de l'invention, le mélange de béton gâché est formé à partir de ciment, de granulats, d'eau, d'au moins un retardateur de prise et d'au moins une silice précipitée. Au moins un accélérateur de prise est alors incorporé au mélange gâché juste avant (c'est-à-dire généralement après que celui-ci ait été véhiculé un certain temps au moyen d'une pompe) ou pendant (c'est-à-dire directement dans le moyen de projection) I'introduction dudit mélange dans le moyen de projection. In the second variant embodiment of the invention, the mixture of tempered concrete is formed from cement, aggregates, water, at least one setting retarder and at least one precipitated silica. At least one setting accelerator is then incorporated into the tempered mixture just before (that is to say generally after it has been conveyed for a certain time by means of a pump) or during (i.e. say directly into the projection means) the introduction of said mixture into the projection means.
Cette seconde variante permet notamment, en plus, de contrôler la maniabilité du béton (maintien de la rhéologie du béton pendant le temps désiré par l'utilisateur) et d'améliorer ses propriétés mécaniques. This second variant makes it possible in particular, in addition, to control the workability of the concrete (maintenance of the rheology of the concrete for the time desired by the user) and to improve its mechanical properties.
Les accélérateurs de prise utilisés dans la présente invention peuvent être de tout type connu ; on peut notamment citer, à titre d'exemples, I'aluminate de sodium, le silicate de sodium, l'aluminate de potassium, le carbonate de potassium. The setting accelerators used in the present invention can be of any known type; there may be mentioned, by way of example, sodium aluminate, sodium silicate, potassium aluminate, potassium carbonate.
Ces accélérateurs de prise sont ici de préférence sous forme liquide, c'est-à-dire mis en oeuvre en solution aqueuse. These setting accelerators are preferably here in liquid form, that is to say used in aqueous solution.
Un accélérateur de prise avantageux utilisé dans la présente invention est l'alumine, de préférence essentiellement amorphe. An advantageous setting accelerator used in the present invention is alumina, preferably essentially amorphous.
On peut employer en particulier l'alumine, de préférence sous forme de poudre, issue de la déshydratation rapide d'au moins un hydroxyde d'aluminium (par exemple la bayerite, i'hydrargillite ou gibbsite, la nordstrandite) et/ou d'au moins un oxyhydroxyde d'aluminium (par exemple la boehmite, le diaspore). Alumina can be used in particular, preferably in the form of a powder, resulting from the rapid dehydration of at least one aluminum hydroxide (for example bayerite, hydrargillite or gibbsite, nordstrandite) and / or at least one aluminum oxyhydroxide (for example boehmite, diaspore).
Cette déshydratation est généralement opérée, dans tout appareillage approprié, à l'aide d'un courant de gaz chauds permettant d'éliminer et entrainer très rapidement l'eau évaporée. La température desdits gaz dans l'appareillage varie en général de 400 à 1200 "C environ, par exemple de 800 à 1200 "C environ, avec un temps de contact entre l'hydroxyde (et/ou l'oxyhydroxyde) et lesdits gaz chauds habituellement de l'ordre d'une fraction de seconde à 4 ou 5 secondes. This dehydration is generally carried out, in any suitable apparatus, using a current of hot gases making it possible to eliminate and entrain very quickly the evaporated water. The temperature of said gases in the apparatus generally varies from 400 to 1200 "C approximately, for example from 800 to 1200" C, with a contact time between the hydroxide (and / or oxyhydroxide) and said hot gases usually in the range of a fraction of a second to 4 or 5 seconds.
L'alumine issue de cette déshydratation peut éventuellemnt subir un traitement en vue d'éliminer au moins une partie des alcalins présents. The alumina resulting from this dehydration can possibly undergo a treatment with a view to eliminating at least part of the alkalis present.
La surface spécifique BET de l'alumine issue de la déshydratation rapide d'hydroxyde(s) et/ou d'oxyhydroxyde(s) d'aluminium est en général supérieure à environ 50 m2/g (par exemple comprise entre environ 50 et 450 m2/g), notamment à environ 100 m2/g, le diamètre des particules variant habituellement entre 0,1 et 300 ijm, par exemple entre 1 et 120 um. The BET specific surface area of alumina resulting from rapid dehydration of aluminum hydroxide (s) and / or oxyhydroxide (s) is generally greater than approximately 50 m2 / g (for example between approximately 50 and 450 m2 / g), in particular at approximately 100 m2 / g, the diameter of the particles usually varying between 0.1 and 300 μm, for example between 1 and 120 μm.
Cette alumine peut provenir notamment de la déshydratation rapide de l'hydrate de Bayer (hydrargillite) qui est un hydroxyde d'aluminium industriel facilement accessible et très bon marché. Une telle alumine est bien connue de l'homme du métier et est en particulier décrite dans le brevet français 1108011. This alumina can come in particular from the rapid dehydration of Bayer hydrate (hydrargillite) which is an easily accessible and very inexpensive industrial aluminum hydroxide. Such an alumina is well known to those skilled in the art and is described in particular in French patent 1108011.
Dans le cas où l'on utilise de l'alumine, telle que décrite précédemment, on peut éventuellement l'introduire avec les produits utilisés pour former le mélange de béton gâché. Néanmoins, elle est de préférence incorporée, comme dans le cas des autres accélérateurs de prise, au mélange gâché juste avant ou pendant l'introduction dudit mélange dans le moyen de projection. In the case where alumina is used, as described above, it can optionally be introduced with the products used to form the mixture of tempered concrete. However, it is preferably incorporated, as in the case of other setting accelerators, in the tempered mixture just before or during the introduction of said mixture into the projection means.
On peut éventuellement employer, dans le cadre de l'invention, un mélange de plusieurs accélérateurs de prise. It is optionally possible to use, within the framework of the invention, a mixture of several setting accelerators.
L'accélérateur de prise, en particulier dans le cas de l'alumine précitée, est avantageusement introduite dans l'air propulseur qui alimente le moyen de projection (habituellement une buse de projection). The setting accelerator, in particular in the case of the aforementioned alumina, is advantageously introduced into the propellant air which supplies the projection means (usually a projection nozzle).
Les retardateurs de prise utilisés dans la seconde variante de réalisation de l'invention peuvent être de tout type connu ; on peut notamment citer, à titre d'exemples, les acides hydrocarboxyliques contenant du bore, l'acide phosphorique, le phosphate d'aluminium, le sulfate ferreux, le sulfate de sodium, le chlorure de zinc, I'acétate de cuivre, le gluconate de sodium, le sulfate acétate de sodium cellulose, le produit de réaction formaldéhyde-aminolignosulfate, le dialdéhyde amidon, les silicofluomres, la
N,N-diméthyloldihydroxyéthylène urée, le tall oil, le sucrose ; on peut éventuellement employer un mélange de plusieurs retardateurs de prise.The setting retarders used in the second variant embodiment of the invention can be of any known type; there may be mentioned, by way of example, the hydrocarboxylic acids containing boron, phosphoric acid, aluminum phosphate, ferrous sulfate, sodium sulfate, zinc chloride, copper acetate, sodium gluconate, sodium acetate sulfate cellulose, formaldehyde-aminolignosulfate reaction product, dialdehyde starch, silicofluomers,
N, N-dimethyloldihydroxyethylene urea, tall oil, sucrose; a mixture of several setting retarders can optionally be used.
Les retardateurs de prise peuvent être sous forme liquide, c'est-à-dire mis en oeuvre en solution aqueuse. The setting retarders can be in liquid form, that is to say used in aqueous solution.
II peut être avantageux d'employer la silice précipitée et le retardateur de prise sous la forme d'un composé obtenu par absorption préalable du retardateur de prise sur la silice précipitée, cette absorption s'effectuant en particulier par co-atomisation de la silice précipitée et du retardateur de prise ou par mise sur support du retardateur de prise sur la silice précipitée. Les techniques proprement dites de co-atomisation et de mise sur support sont bien connues de l'homme du métier. On entend notamment par mise sur support l'absorption d'un composé sous forme liquide, ici le retardateur de prise, dans les pores de la silice précipitée. Dans ce cas, on emploie, de préférence, une silice précipitée présentant une prise d'huile DOP comprise entre 180 et 350 ml/1 00g (la prise d'huile DOP étant déterminée selon la norme ISO 787/5 en mettant en oeuvre le dioctylphtalate). It may be advantageous to use the precipitated silica and the setting retarder in the form of a compound obtained by prior absorption of the setting retarder on the precipitated silica, this absorption taking place in particular by co-atomization of the precipitated silica and the setting retarder or by placing on setting the setting retarder on the precipitated silica. The actual techniques of co-atomization and placing on a support are well known to those skilled in the art. The expression “placing on a support” in particular means the absorption of a compound in liquid form, here the setting retarder, in the pores of the precipitated silica. In this case, use is preferably made of a precipitated silica having a DOP oil intake of between 180 and 350 ml / 100 g (the DOP oil intake being determined according to ISO standard 787/5 by implementing the dioctylphthalate).
Cette mise en oeuvre particulière entraîne, en plus, une simplification du travail de l'opérateur au niveau du dosage lors de la formation du mélange de béton gâché (deux additifs sont remplacés par un seul additif) et une meilleure répartition du retardateur de prise dans le mélange de béton. This particular implementation leads, in addition, to a simplification of the work of the operator at the dosage level during the formation of the mix of tempered concrete (two additives are replaced by a single additive) and a better distribution of the setting retarder in the concrete mixture.
On ne sort toutefois pas du cadre de l'invention lorsque le composé précité ne contient qu'une partie de la silice utilisée dans le procédé. It is not, however, outside the scope of the invention when the above-mentioned compound contains only part of the silica used in the process.
Dans les deux variantes de réalisation de l'invention, on peut utiliser, lors de la formation du mélange de béton gâché, un certain nombre d'additifs supplémentaires, notamment choisis dans le groupe formé par les fluidifiants, les agents anti-mousse, les latex. In the two alternative embodiments of the invention, it is possible to use, during the formation of the mixture of tempered concrete, a certain number of additional additives, in particular chosen from the group formed by fluidizers, anti-foaming agents, latex.
II peut être avantageux d'employer la silice précipitée et au moins un desdits additifs sous la forme d'un seul composé obtenu par absorption préalable de l'additif (ou des additifs) sur la silice précipitée, cette absorption s'effectuant en particulier par coatomisation de la silice précipitée et de l'additif (ou des additifs) ou par mise sur support de l'additif (ou des additifs) sur la silice précipitée. It may be advantageous to use precipitated silica and at least one of said additives in the form of a single compound obtained by prior absorption of the additive (or additives) on the precipitated silica, this absorption being carried out in particular by coatomization of the precipitated silica and the additive (or additives) or by placing the additive (or additives) on a support on the precipitated silica.
Ainsi, on peut utiliser, lors de la formation du mélange de béton gâché, au moins un composé comprenant de la silice précipitée et au moins un additif choisi dans le groupe formé par les fluidifiants, les agents anti-mousse, les latex, ce(s) composé(s) étant préparé(s) par co-atomisation d'une silice précipitée et d'au moins un additif choisi dans le groupe précité ou par mise sur support d'au moins un additif choisi dans le groupe précité sur une silice précipitée. Thus, it is possible to use, during the formation of the mixture of tempered concrete, at least one compound comprising precipitated silica and at least one additive chosen from the group formed by fluidizers, anti-foaming agents, latexes, this ( s) compound (s) being prepared by co-atomization of a precipitated silica and of at least one additive chosen from the above group or by placing on support of at least one additive chosen from the above group on a precipitated silica.
On peut ainsi employer au moins un composé silice-fluidifiant, silice-latex, silice agent anti-mousse, silice-fluidifiant-latex, silice-fluidifiant-agent anti-mousse, silice-latexagent-anti-mousse et/ou silice-flu idifiant-latex-agent anti-mousse. It is thus possible to use at least one silica-thinning compound, silica-latex, silica anti-foaming agent, silica-thinning-latex, silica-thinning-anti-foaming agent, silica-latex-anti-foaming agent and / or silica-flu identifier-latex-anti-foaming agent.
II est à noter que, dans le cas où de tels composés sont utilisés, toute la silice précipitée mise en oeuvre dans le procédé selon l'invention n'est pas nécessairement sous la forme de tels composés ; une partie de la silice précipitée peut en effet être éventuellement employée telle quelle. It should be noted that, in the case where such compounds are used, all of the precipitated silica used in the process according to the invention is not necessarily in the form of such compounds; part of the precipitated silica can indeed be optionally used as it is.
Dans la seconde variante de réalisation de l'invention, le(s) composé(s) utilisé(s) peut (peuvent) éventuellement comprendre le retardateur de prise ; ce(s) composé(s) est (sont) alors préparé(s) par co-atomisation d'une silice précipitée, d'un retardateur de prise et d'au moins un additif choisi dans le groupe précité ou par mise sur support d'un retardateur de prise et d'au moins un additif choisi dans le groupe précité sur une silice précipitée. In the second embodiment of the invention, the compound (s) used can optionally comprise the setting retarder; this (these) compound (s) is (are) then prepared (s) by co-atomization of a precipitated silica, of a setting retarder and of at least one additive chosen from the aforementioned group or by placing on a support a setting retarder and at least one additive chosen from the above group on precipitated silica.
On peut ainsi éventuellement employer, dans le cadre de la seconde variante de réalisation de l'invention, au moins un composé silice-fluidifiant-retardateur de prise, silice-latex-retardateur de prise, silice-agent anti-mousse-retardateur de prise, silice fluidifiant-latex-retardateur de prise, silice-fluidifiant-agent anti-mousse-retardateur de prise, sil ice-latex-agent-anti-mousse- retardateur de prise et/ou silice-fluidifiant-latexagent anti-mousse-retardateur de prise. It is thus optionally possible to use, in the context of the second variant embodiment of the invention, at least one silica-fluidifying-setting retarder, silica-latex-setting retarding compound, silica-anti-foaming agent-setting retardant compound , silica-thinning-latex-setting retardant, silica-thinning-antifoaming agent-setting retardant, sil ice-latex-antifoaming agent-setting retarder and / or silica-thinning-latex-defoaming agent-retardant hold.
De même, il est à noter que, dans le cas où de tels composés sont utilisés, toute la silice précipitée mise en oeuvre dans le procédé selon l'invention n'est pas nécessairement sous la forme de tels composés ; une partie de la silice précipitée peut en effet être éventuellement employée telle quelle. Likewise, it should be noted that, in the case where such compounds are used, all of the precipitated silica used in the process according to the invention is not necessarily in the form of such compounds; part of the precipitated silica can indeed be optionally used as it is.
On peut citer, à titre d'exemples de fluidifiants, notamment la mélamine, le polynaphtalène sulfonate de sodium, le polyacrylate de sodium. There may be mentioned, by way of examples of fluidizers, in particular melamine, sodium polynaphthalene sulfonate, sodium polyacrylate.
De manière préférée, on utilise, lors de la formation du mélange de béton gâché, au moins un fluidifiant. Preferably, at least one plasticizer is used during the formation of the tempered concrete mixture.
Les Demanderesses ont constaté, d'une part, que les agents anti-mousses permettaient de réduire l'entraînement d'air, d'augmenter la densité du béton projeté et d'améliorer ses propriétés mécaniques à terme, et, d'autre part, que les latex permettaient d'améliorer l'adhésion du béton sur la surface à bétonner, et donc de réduire le rebond et la perméabilité du béton
On peut citer, à titre d'exemples d'agents anti-mousse, notamment les huiles silicones et, à titre d'exemples de latex, notamment les copolymères styrène-butadiène.The Applicants have found, on the one hand, that the anti-foaming agents make it possible to reduce the entrainment of air, to increase the density of the sprayed concrete and to improve its mechanical properties over time, and, on the other hand , that latexes made it possible to improve the adhesion of the concrete to the surface to be concreted, and therefore to reduce the rebound and the permeability of the concrete
Mention may be made, as examples of anti-foaming agents, in particular silicone oils and, as examples of latex, in particular styrene-butadiene copolymers.
L'invention n'est pas du tout limitée à un type de ciment particulier ; on peut ainsi utiliser tous les types de ciment employés traditionnellement dans les procédés de projection de béton, notamment les ciments de type Portland. The invention is not at all limited to a particular type of cement; it is thus possible to use all the types of cement traditionally used in concrete spraying processes, in particular Portland type cements.
Les granulats (ou agrégats) employés dans le cadre de l'invention sont connus ; il peut s'agir de sable, de gravillons et/ou de cailloux. The aggregates (or aggregates) used in the context of the invention are known; it can be sand, gravel and / or pebbles.
Le procédé selon l'invention s'applique sur tout type de surface. The method according to the invention applies to any type of surface.
L'exemple suivant illustre l'invention sans toutefois en limiter la portée. The following example illustrates the invention without however limiting its scope.
EXEMPLE
On prépare un mélange de béton gâché en mélangeant les constituants ci-après selon le processus suivant
- introduction dans un malaxeur de 640 kg de sable roulé 0/2 mm, 180 kg de sable fin 0/0,3 mm et 1000 kg de gravier roulé 2/6 mm
- ajout de 430 kg de ciment Portland et 13 kg de silice précipitée (présentant une surface spécifique de 250 m2/g et une taille moyenne des particules de 3,5 pm)
- homogénéisation (par malaxage) du mélange sec obtenu pendant 15 secondes;
- ajout de 180 litres d'eau et 4,3 kg de fluidifiant (commercialisé par la société
Chryso sous le nom Durciplast);
- homogénéisation (par malaxage) du mélange humide obtenu pendant 30 secondes.EXAMPLE
A mixture of tempered concrete is prepared by mixing the following constituents according to the following process
- introduction into a mixer of 640 kg of 0/2 mm rolled sand, 180 kg of 0 / 0.3 mm fine sand and 1000 kg of 2/6 mm rolled gravel
- addition of 430 kg of Portland cement and 13 kg of precipitated silica (with a specific surface of 250 m2 / g and an average particle size of 3.5 pm)
- homogenization (by kneading) of the dry mixture obtained for 15 seconds;
- addition of 180 liters of water and 4.3 kg of plasticizer (marketed by the company
Chryso under the name Durciplast);
- homogenization (by kneading) of the wet mixture obtained for 30 seconds.
On constate que le mélange gâché ainsi réalisé est cohérent au repos et fluide lorsqu'on le met en mouvement. It is found that the spoiled mixture thus produced is coherent at rest and fluid when it is put into motion.
On introduit ce mélange dans une pompe à piston qui véhicule ensuite ledit mélange dans une gaine de projection vers un moyen de projection. This mixture is introduced into a piston pump which then conveys said mixture in a projection sheath towards a projection means.
Ce moyen de projection est constitué d'une buse de projection, qui se trouve en bout de gaine et qui est alimentée en air comprimé (air propulseur). This projection means consists of a projection nozzle, which is located at the end of the sheath and which is supplied with compressed air (propellant air).
Le mélange gâché est alors projeté à partir de cette buse sur une surface verticale rugueuse ; on obtient une couche de béton, cohérent, d'épaisseur supérieure à 20 cm en une seule passe, sans glissement, avec un taux de perte minimum, qui est égal à la moitié seulement de celui obtenu lorsque l'on n'utilise pas de silice précipitée. The tempered mixture is then sprayed from this nozzle onto a rough vertical surface; a coherent layer of concrete greater than 20 cm thick is obtained in a single pass, without slipping, with a minimum loss rate, which is only half that obtained when not using precipitated silica.
La surface couverte est ici augmentée de plus de 10 % par rapport à celle obtenue lorsque l'on n'utilise pas de silice précipitée (pour la même quantité de béton). The covered surface is here increased by more than 10% compared to that obtained when precipitated silica is not used (for the same quantity of concrete).
La perte par rebond est de plus notablement réduite. The loss by rebound is moreover significantly reduced.
On n'observe pas de dégagement sensible de poussière. No appreciable generation of dust is observed.
On constate que le béton ainsi projeté présente une résistance à l'écrasement élevée: 49 MPa minimum, contre 41 MPa maximum sans utilisation de silice précipitée, soit un gain d'au moins environ 20 % (mesure de résistance à l'écrasement à 28 jours faite sur des carottes de béton). It is found that the concrete thus sprayed exhibits a high crushing resistance: 49 MPa minimum, against 41 MPa maximum without the use of precipitated silica, or a gain of at least about 20% (measurement of crushing resistance at 28 days made on concrete cores).
Enfin, la durabilité du béton ainsi projeté est considérablement améliorée par rapport à celle d'un béton projeté sans utilisation de silice précipitée. En effet, on sait que la durabilité d'un béton est directement liée à sa perméabilité (perméabilité à l'eau, à l'air, à la carbonatation, aux ions chlorure) ; or, la perméabilité du béton projeté selon l'invention est diminuée d'un facteur d'au moins 100 par rapport à celle d'un béton projeté sans utilisation de silice précipitée. Finally, the durability of the sprayed concrete is considerably improved compared to that of a sprayed concrete without the use of precipitated silica. Indeed, we know that the durability of a concrete is directly linked to its permeability (permeability to water, air, carbonation, chloride ions); however, the permeability of the sprayed concrete according to the invention is reduced by a factor of at least 100 compared to that of a sprayed concrete without the use of precipitated silica.
Claims (15)