FR2650697A1 - Electrically insulating micaceous tape - Google Patents

Electrically insulating micaceous tape Download PDF

Info

Publication number
FR2650697A1
FR2650697A1 FR8910532A FR8910532A FR2650697A1 FR 2650697 A1 FR2650697 A1 FR 2650697A1 FR 8910532 A FR8910532 A FR 8910532A FR 8910532 A FR8910532 A FR 8910532A FR 2650697 A1 FR2650697 A1 FR 2650697A1
Authority
FR
France
Prior art keywords
sep
micaceous
thermoplastic polymer
micaceous tape
mica paper
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
FR8910532A
Other languages
French (fr)
Other versions
FR2650697B1 (en
Inventor
Alain Anton
Alain Dubuisson
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Alstom Holdings SA
Original Assignee
GEC Alsthom SA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GEC Alsthom SA filed Critical GEC Alsthom SA
Priority to FR8910532A priority Critical patent/FR2650697B1/en
Publication of FR2650697A1 publication Critical patent/FR2650697A1/en
Application granted granted Critical
Publication of FR2650697B1 publication Critical patent/FR2650697B1/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

Electrically insulating micaceous tape, comprising a mica paper adhesively bonded to at least one thermoplastic polymer film, using an adhesive based on epoxide resin, to which a hardening catalyst has been added. The adhesive based on epoxide resin additionally contains from 1 to 20 % by weight of polyvinylformaldehyde (polyacrolein). Application to medium or high voltage conductors of electrical equipment or of cables.

Description

Ruban micacé isolant électrique
La présente invention concerne un ruban micacé pour isolation de conducteurs électriques à moyenne ou haute tension de machines tournantes, de câbles, etc..., comprenant un papier de mica collé sur un film en polymère thermoplastique à l'aide d'un adhésif à base de résine époxyde additionnée d'un catalyseur de durcissement.Electrically insulating micaceous tape
The present invention relates to a micaceous tape for insulating medium or high voltage electrical conductors of rotating machines, cables, etc., comprising a mica paper bonded to a thermoplastic polymer film using a plastic adhesive. epoxy resin base supplemented with a hardening catalyst.

Le brevet EP-B-081154 de la demanderesse porte notamment sur un ruban de ce genre, comportant un papier de mica poreux reposant sur une deuxième couche constituant un support thermofusible destiné à être au contact d'un conducteur, et formé par exemple par un film à base de polyester ou de polymère fluoré, le papier de mica étant revêtu sur son autre face par une troisième couche de protection mécanique, par exemple un tissu de verre. La solidarisation du papier de mica avec les autres couches est assurée par une résine époxyde. Patent EP-B-081154 of the Applicant relates in particular to a ribbon of this kind, comprising a porous mica paper resting on a second layer constituting a hot melt holder intended to be in contact with a conductor, and formed for example by a a film based on polyester or fluoropolymer, the mica paper being coated on its other side with a third mechanical protection layer, for example a glass fabric. The bonding of the mica paper with the other layers is provided by an epoxy resin.

On a constaté cependant que l'adhérence du papier mica sur les autres -couches n'était pas excellente, et qu'il était possible de décoller le film de polymère thermoplastique, notamment un film de polytéréphtalate d'éthylène glycol, du papier de mica, avec un effort relativement faible. However, it was found that the adhesion of the mica paper to the other layers was not excellent, and that it was possible to peel off the thermoplastic polymer film, especially a film of polyethylene terephthalate glycol, mica paper with a relatively low effort.

La présente invention a pour but de procurer un ruban micacé isolant électrique présentant une très bonne adhérence entre le papier de mica et le film en polymère thermoplastique, et éventuellement une autre couche disposée sur l'autre face du papier de mica. The present invention aims to provide an electrical insulating micaceous tape having a very good adhesion between the mica paper and the thermoplastic polymer film, and optionally another layer disposed on the other side of the mica paper.

Le ruban micacé selon l'invention est caractérisé en ce que l'adhésif à base de résine époxyde contient en outre de 1 % à 20 % en poids de polyvinylformal. The micaceous tape according to the invention is characterized in that the epoxy resin adhesive further contains from 1% to 20% by weight of polyvinylformal.

Il répond en outre de préférence à au moins l'une des caractéristiques suivantes
- la résine époxyde comprend un mélange de résine novolaque et de résine au bisphénol A.It further preferably responds to at least one of the following features
the epoxy resin comprises a mixture of novolak resin and bisphenol A resin.

- l'adhésif contient environ 3 % en poids de polyvinylformal. the adhesive contains about 3% by weight of polyvinylformal.

- le polymère thermoplastique est du polytéréphtalate d'éthylène-glycol, du polyimide, du polycarbonate ou du polyéthersulfone. the thermoplastic polymer is polyethylene terephthalate, polyimide, polycarbonate or polyethersulfone.

- il contient en outre un tissu de fils de verre collé sur le côté du papier de mica opposé au film de polymère thermoplastique. - It further contains a glass yarn fabric stuck on the side of the mica paper opposite to the thermoplastic polymer film.

I1 est decrit ci-après à titre d'exemple un ruban micacé isolant selon l'invention. I1 is hereinafter described by way of example an insulating micaceous tape according to the invention.

Ce ruban comprend un film polyester d'épaisseur 23 microns collé à un papier de mica muscovite de 160 g/m grâce à une résine époxyde modifiée de la composition pondérale suivante
a) résine époxyde novolaque de la désignation DEN438 de Dow Chemical 70 %
b) résine époxyde au bisphénol A de la marque Epikote ?4 de Shell 27 %
c) polyvinylformal de la marque Formvar 5/95 de
Monsanto
plus 3 parties pour 100 parties pondérales d'un complexe de bore et d'une amine comme catalyseur de durcissement.This ribbon comprises a 23 micron thick polyester film bonded to a 160 g / m muscovite mica paper using a modified epoxy resin of the following weight composition
a) Dow Chemical Designation DEN438 N-Epoxy Resin 70%
b) Shell Epikote ™ 4 Bisphenol A epoxy resin 27%
c) polyvinylformal of the trademark Formvar 5/95 of
Monsanto
plus 3 parts per 100 parts by weight of a boron complex and an amine as a curing catalyst.

On a préparé dans un premier temps le même ruban comportant la même résine de collage, mais sans polyvinylformal. Firstly, the same ribbon comprising the same bonding resin but without polyvinylformal was prepared.

A l'essai de décollement selon la norme française NF
C26-142, la force de décollement nécessaire a été de 5 Newtons.At the detachment test according to the French NF standard
C26-142, the necessary peeling force was 5 Newtons.

Avec le même ruban dont la colle époxyde a été additionée de polyvinylformal, conformément à la formulation ci-dessus, la force de décollement nécessaire s'est élevée à 15
Newtons.With the same tape whose epoxy adhesive was added with polyvinylformal, according to the above formulation, the required peel force was 15.
Newtons.

On donne ci-après les caractéristiques diélectriques d'une maquette réalisée à partir d'un fil de cuivre isolé par 6 couches à demi-recouvrement (épaisseur d'isolant 1,4 mm). The dielectric characteristics of a model made from a copper wire insulated by 6 semi-overlapping layers (insulation thickness 1.4 mm) are given below.

Le durcissement a eu lieu en presse pendant 1H à 1600 C, plus une post-cuisson de 15H à 1550C en étuve.Curing took place in press for 1 hour at 1600 C, plus a post-cure of 15H at 1550C in an oven.

Tansium nominale v N = 6 K
MESURES ELECTRIQUES

Figure img00030001
Rated tansium v N = 6 K
ELECTRICAL MEASUREMENTS
Figure img00030001

<tb> tension <SEP> Capacité <SEP> Capacité <SEP> Fréq:50 <SEP> Hz <SEP> Permittivi
<tb> nominale <SEP> TEMP. C <SEP> Tg <SEP> de <SEP> té
<tb> Un: <SEP> 6 <SEP> KV <SEP> Cn:112 <SEP> pF <SEP> CO:67,8 <SEP> pF <SEP> l'angle <SEP> de <SEP> Eps <SEP> (#)
<tb> I <SEP> Tension <SEP> perte <SEP> Tg <SEP> #
<tb> 1 <SEP> 20 <SEP> 0,2#N <SEP> <SEP> 0,0043 <SEP> 4,5
<tb> 2 <SEP> 20 <SEP> 0,6" <SEP> 0,0046 <SEP> 4,5
<tb> 3 <SEP> 20 <SEP> 1 <SEP> " <SEP> 0,005 <SEP> 4,5
<tb> 4 <SEP> 20 <SEP> 1,4 <SEP> 0,0062 <SEP> 4,51
<tb> 5 <SEP> 80 <SEP> 0,2 <SEP> " <SEP> 0,0087 <SEP> 4,62
<tb> 6 <SEP> 80 <SEP> 0,6 <SEP> " <SEP> 0,0090 <SEP> 4,62
<tb> 7 <SEP> 80 <SEP> 1 <SEP> " <SEP> 0,0096 <SEP> 4,62
<tb> 8 <SEP> 80 <SEP> 1,4 <SEP> " <SEP> 0,01 <SEP> 4,62
<tb> 9 <SEP> 100 <SEP> 0,2 <SEP> " <SEP> 0,152 <SEP> 4,73
<tb> || <SEP> 10 <SEP> H <SEP> <SEP> 100 <SEP> || <SEP> 0,6 <SEP> " <SEP> H <SEP> <SEP> H <SEP> <SEP> 0,156 <SEP> 11 <SEP> 4,73 <SEP> 11
<tb> 11 <SEP> 100 <SEP> 1 <SEP> " <SEP> 0,16 <SEP> 4,74
<tb> 12 <SEP> 100 <SEP> 1,4 <SEP> " <SEP> 0,168 <SEP> 4,74
<tb> 13 <SEP> 120 <SEP> 0,2 <SEP> " <SEP> 0,302 <SEP> 4,9
<tb> 14 <SEP> 120 <SEP> 0,6 <SEP> " <SEP> 0,0308 <SEP> 4,9
<tb> 15 <SEP> 120 <SEP> 1 <SEP> " <SEP> 0,032 <SEP> 4,9
<tb> H <SEP> 16 <SEP> H <SEP> 120 <SEP> H <SEP> 1,4 <SEP> " <SEP> || <SEP> || <SEP> 0,0338 <SEP> H <SEP> <SEP> 4,9 <SEP> H
<tb> 17 <SEP> 140 <SEP> 0,2 <SEP> " <SEP> 0,1128 <SEP> 5,12
<tb> 18 <SEP> 140 <SEP> 0,6 <SEP> " <SEP> 0,1185 <SEP> 5,13
<tb> 19 <SEP> 140 <SEP> 1 <SEP> " <SEP> 0,1281 <SEP> 5,14
<tb> 20 <SEP> 140 <SEP> 1,4 <SEP> " <SEP> 0,141 <SEP> 5,16
<tb> 21 <SEP> 155 <SEP> 0,2 <SEP> " <SEP> 0,347 <SEP> 6,03
<tb> H <SEP> 22 <SEP> H <SEP> <SEP> 155 <SEP> H <SEP> <SEP> 0,6 <SEP> " <SEP> H <SEP> <SEP> H <SEP> <SEP> 0,357 <SEP> H <SEP> <SEP> 6,06 <SEP> <SEP> H <SEP>
<tb> || <SEP> 23 <SEP> H <SEP> 155 <SEP> H <SEP> <SEP> 1 <SEP> " <SEP> H <SEP> <SEP> H <SEP> <SEP> 0,37 <SEP> H <SEP> <SEP> 6,14 <SEP> <SEP> H <SEP>
<tb> 24 <SEP> 155 <SEP> 1,4 <SEP> " <SEP> 0,382 <SEP> 6,23
<tb> <tb> voltage <SEP> Capacity <SEP> Capacity <SEP> Freq: 50 <SEP> Hz <SEP> Permittivi
<tb> nominal <SEP> TEMP. C <SEP> Tg <SEP> of <SEP> tee
<tb> A: <SEP> 6 <SEP> KV <SEP> Cn: 112 <SEP> pF <SEP> CO: 67.8 <SEP> pF <SEP> the <SEP> angle of <SEP> Eps <SEP>(#)
<tb> I <SEP> Tension <SEP> Loss <SEP> Tg <SEP>#
<tb> 1 <SEP> 20 <SEP> 0.2 # N <SEP><SEP> 0.0043 <SEP> 4.5
<tb> 2 <SEP> 20 <SEP> 0.6 "<SEP> 0.0046 <SEP> 4.5
<tb> 3 <SEP> 20 <SEP> 1 <SEP>"<SEP> 0.005 <SEP> 4.5
<tb> 4 <SEP> 20 <SEP> 1.4 <SEP> 0.0062 <SEP> 4.51
<tb> 5 <SEP> 80 <SEP> 0.2 <SEP>"<SEP> 0.0087 <SEP> 4.62
<tb> 6 <SEP> 80 <SEP> 0.6 <SEP>"<SEP> 0.0090 <SEP> 4.62
<tb> 7 <SEP> 80 <SEP> 1 <SEP>"<SEP> 0.0096 <SEP> 4.62
<tb> 8 <SEP> 80 <SEP> 1.4 <SEP>"<SEP> 0.01 <SEP> 4.62
<tb> 9 <SEP> 100 <SEP> 0.2 <SEP>"<SEP> 0.152 <SEP> 4.73
<tb> || <SEP> 10 <SEP> H <SEP><SEP> 100 <SEP> || <SEP> 0.6 <SEP>"<SEP> H <SEP><SEP> H <SEP><SEP> 0.156 <SEP> 11 <SEP> 4.73 <SEP> 11
<tb> 11 <SEP> 100 <SEP> 1 <SEP>"<SEP> 0.16 <SEP> 4.74
<tb> 12 <SEP> 100 <SEP> 1.4 <SEP>"<SEP> 0.168 <SEP> 4.74
<tb> 13 <SEP> 120 <SEP> 0.2 <SEP>"<SEP> 0.302 <SEP> 4.9
<tb> 14 <SEP> 120 <SEP> 0.6 <SEP>"<SEP> 0.0308 <SEP> 4.9
<tb> 15 <SEP> 120 <SEP> 1 <SEP>"<SEP> 0.032 <SEP> 4.9
<tb> H <SEP> 16 <SEP> H <SEP> 120 <SEP> H <SEP> 1,4 <SEP>"<SEP> || <SEP> || <SEP> 0,0338 <SEP> H <SEP><SEP> 4.9 <SEP> H
<tb> 17 <SEP> 140 <SEP> 0.2 <SEP>"<SEP> 0.1128 <SEP> 5.12
<tb> 18 <SEP> 140 <SEP> 0.6 <SEP>"<SEP> 0.1185 <SEP> 5.13
<tb> 19 <SEP> 140 <SEP> 1 <SEP>"<SEP> 0.1281 <SEP> 5.14
<tb> 20 <SEP> 140 <SEP> 1.4 <SEP>"<SEP> 0.141 <SEP> 5.16
<tb> 21 <SEP> 155 <SEP> 0.2 <SEP>"<SEP> 0.347 <SEP> 6.03
<tb> H <SEP> 22 <SEP> H <SEP><SEP> 155 <SEP> H <SEP><SEP> 0.6 <SEP>"<SEP> H <SEP><SEP> H <SEP><SEP> 0.357 <SEP> H <SEP><SEP> 6.06 <SEP><SEP> H <SEP>
<tb> || <SEP> 23 <SEP> H <SEP> 155 <SEP> H <SEP><SEP> 1 <SEP>"<SEP> H <SEP><SEP> H <SEP><SEP> 0.37 <SEP> H <SEP><SEP> 6.14 <SEP><SEP> H <SEP>
<tb> 24 <SEP> 155 <SEP> 1.4 <SEP>"<SEP> 0.382 <SEP> 6.23
<Tb>

Claims (5)

Revendications 1. Ruban micacé isolant électrique, comprenant un papier de mica collé sur au moins un film en polymère thermoplastique, à l'aide d'un adhésif à base de résine époxyde, additionné d'un catalyseur de durcissement.1. An electrical insulating micaceous tape, comprising a mica paper adhered to at least one thermoplastic polymer film, using an epoxy resin adhesive, supplemented with a hardening catalyst. caractérisé en ce que l'adhésif à base de résine époxyde contient en outre de 1 à 20 % en poids de polyvinylformal.characterized in that the epoxy resin adhesive further contains from 1 to 20% by weight of polyvinylformal. 2. Ruban micacé selon la revendication 1, caractérise en ce que la résine époxyde comprend un mélange de résine novolaque et de résine au bisphénol A.2. The micaceous tape according to claim 1, characterized in that the epoxy resin comprises a mixture of novolak resin and bisphenol A resin. 3.Ruban micacé selon les revendications 1 ou 2, caractérisé en ce que l'adhésif contient environ 3% en poids de polyvinylformal.3. micaceous tape according to claims 1 or 2, characterized in that the adhesive contains about 3% by weight of polyvinylformal. 4. Ruban micacé selon l'une des revendications 1 à 3, caractérisé en ce que le polymère thermoplastique est du polytéréphtalate d'éthylène- glycol, du polyamide, du polycarbonate ou du polyéthersulfone.4. Micaceous tape according to one of claims 1 to 3, characterized in that the thermoplastic polymer is polyethylene terephthalate, polyamide, polycarbonate or polyethersulfone. 5. Ruban micacé selon l'une des revendications 1 à 4, caractérisé en ce qu'il contient en outre un tissu de fils de verre collé sur le côté du papier de mica opposé au film de polymère thermoplastique. 5. Micaceous tape according to one of claims 1 to 4, characterized in that it further contains a glass yarn fabric bonded to the side of the mica paper opposite to the thermoplastic polymer film.
FR8910532A 1989-08-04 1989-08-04 ELECTRIC INSULATING MICACE TAPE Expired - Fee Related FR2650697B1 (en)