FR2554626A1 - Method of obtaining a matrix for copying a magnetic recording, matrix obtained by the said method, method of copying a magnetic recording by means of this matrix, and magnetic recording medium carrying the recording obtained by the said copying method - Google Patents
Method of obtaining a matrix for copying a magnetic recording, matrix obtained by the said method, method of copying a magnetic recording by means of this matrix, and magnetic recording medium carrying the recording obtained by the said copying method Download PDFInfo
- Publication number
- FR2554626A1 FR2554626A1 FR8317752A FR8317752A FR2554626A1 FR 2554626 A1 FR2554626 A1 FR 2554626A1 FR 8317752 A FR8317752 A FR 8317752A FR 8317752 A FR8317752 A FR 8317752A FR 2554626 A1 FR2554626 A1 FR 2554626A1
- Authority
- FR
- France
- Prior art keywords
- magnetic
- layer
- recording
- relief
- matrix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
La présente invention se rapporte au domaine de l'enregistrement magnétique et de la reproduction d'informations et a notamment pour objet un procédé de préparation d'une matrice pour le tirage d'un enregistrement magnétique, la matrice obtenue par ce procédé, un procédé de tirage d'un enregistrement magnétique au moyen de ladite matrice, et un porteur d'enregistrement magnétique comportant ledit enregistrement. L'invention peut être utilise notamment dans la technique d'enregistrement magnétique utilisant divers porteurs d'informations magnêtiques1dans la technique de l'enregistrement hologra phique et de la reproduction de cet enregistrement, pour le traitement optique d'informations, dans la technique de calcul, etc. The present invention relates to the field of magnetic recording and the reproduction of information and in particular relates to a method of preparing a matrix for drawing a magnetic recording, the matrix obtained by this method, a method for drawing a magnetic recording by means of said matrix, and a magnetic recording carrier comprising said recording. The invention can be used in particular in the magnetic recording technique using various carriers of magnetic information1 in the technique of holographic recording and of the reproduction of this recording, for the optical processing of information, in the calculation technique , etc.
On connaît une série de procédés pour la préparation d'une matrice pour le tirage d'un enregistrement magnétique, mais le plus proche de la présente invention est un procédé de préparation d'une matrice, réalisé de la façon suivante: on enregistre l'information sur la couche magnétique d'un porteur d'enregistrement à haute force coercitive (environ 1400 oersteds), par exemple sur un ruban magnétique, à partir d'un autre porteur d'enregistrement magnétique (original) en image miroir par rapport à l'enregistrement de l'original (voir par exemple, Funkshau 1969, Heft 11S346 "Schnelles kopieren von Video Bandera). A series of methods are known for the preparation of a matrix for drawing a magnetic recording, but the closest to the present invention is a method for preparing a matrix, carried out in the following way: the information on the magnetic layer of a recording medium with high coercive force (approximately 1400 oersteds), for example on a magnetic tape, from another magnetic recording medium (original) in mirror image compared to the recording of the original (see for example, Funkshau 1969, Heft 11S346 "Schnelles kopieren von Video Bandera).
Cependant, ce procédé de préparation d'une matrice pour le tirage d'un enregistrement magnétique comporte des inconvénients considérables, en particulier:
- il exige une appareillage spécial pour l'enregistrement miroir et la reproduction miroir;
- on doit disposer d'un porteur d'enregistrement à haute force coercitive (1400 oersteds), constituant plus tard la matrice, des têtes d t enregistrement et de reproduction spéciales, etc
- l'enregistrement des hautes fréquences est limité du fait que la matrice doit posséder une haute force coercitive (limitation en densité d'enregistrement). However, this method of preparing a matrix for drawing a magnetic recording has considerable drawbacks, in particular:
- it requires special equipment for mirror recording and mirror reproduction;
- one must have a recording medium with high coercive force (1400 oersteds), later constituting the matrix, special recording and reproduction heads, etc.
- the recording of high frequencies is limited because the matrix must have a high coercive force (limitation in recording density).
Il existe aujourd'hui trois procédés principaux de tirage d'enregistrements magnétiques largement connus thermomagnétique, thermique et magnétique. Today there are three main processes for drawing widely known magnetic, thermomagnetic, thermal and magnetic records.
Le procédé de tirage thermomagnétique d'un enregistrement (voir par exemple le brevet japonais NO 53-11846 cl. 102E82 "Dispositif thermomagnatique pour rubans magnétiques") assure le transfert de l'information à partir du porteur-original d'enregistrement magnétique-matrice sur un porteur d'enregistrement de la façon suivante. On chauffe la couche magnétique du porteur d'enregistrement, puis on le pose côté couche magnétique sur la couche magnétique du ruban copie. On fait refroidir à l'état serré, et lorsque le refroidissement est achevé il a sur le ruban-copie un enregistrement du à l'effet de copiage amplifié. Cependant, ce procédé est caractérisé par une faible efficacité de transfert de l'information.Sa réalisation est compliquée, car elle exige une haute précision de maintien du régime de tirage thermomagnétique pour des porteurs d'information mobiles et elle exige d'autre part la présence de dispositifs de chauffage et de refroidissement. Au cours du tirage, la matrice et le porteur d'enregistrement subissent une déformation thermique, ce qui réduit notablement la durée de service de la matrice et provoque une distorsion du transfert de l'information sur le porteur d'information. The process of thermomagnetic drawing of a recording (see for example Japanese patent NO 53-11846 cl. 102E82 "Thermomagnetic device for magnetic tapes") ensures the transfer of information from the original holder of magnetic recording-matrix on a record carrier as follows. The magnetic layer of the recording medium is heated, then it is placed on the magnetic layer side on the magnetic layer of the copy ribbon. It is cooled in the tight state, and when the cooling is complete it has on the tape-copy a recording of the effect of amplified copying. However, this method is characterized by a low efficiency of information transfer. Its realization is complicated, because it requires a high precision of maintenance of the thermomagnetic drawing regime for mobile information carriers and it requires on the other hand the presence of heating and cooling devices. During the drawing, the matrix and the recording carrier undergo thermal deformation, which notably reduces the service life of the matrix and causes a distortion of the transfer of information to the information carrier.
Ce procédé est inapplicable au tirage de masse, en premier lieu du fait de la longévité insuffisante de la matrice. This process is inapplicable to mass pulling, firstly because of the insufficient longevity of the matrix.
Un autre procédé de tirage thermique d'un enregistrement (voir, par exemple, le brevet Grande-Bretagne NO 1489197 cl. Another thermal drawing process for a recording (see, for example, Great Britain patent NO 1,489,197 cl.
G5R "Procédé de copie thermique de l'information à partir d'un ruban magnétique") prévoit le transfert de l'information sur un porteur d'enregistrement dont la couche magnétique est constituée de bioxyde de chrome (Cr02) et possède un point de Curie assez bas (125 C). On réchauffe la couche magnétique (cor02) du porteur d'enregistrement à une température dépassant le point de Curie. Puis on met en contact la couche magnétique réchauffée du porteur d'enregistrement avec la couche magnétique de la matrice, sur laquelle l'information est enregistrée sous forme de zones d'aimantation. Ce contact produit un fort refroidissement du porteur d'enregistrement et l'information est réenregistrée à partir de la matrice sur la couche magnétique du porteur d'enregistrement.Après le réenregistrement thermique, le porteur d'information est soumis à un chauffage supplémentaire jusqu'à une température inférieure au point de Curie (700C), mais non inférieure à 400C, pour réduire les déformations.G5R "Process for thermal copying of information from a magnetic tape") provides for the transfer of information to a record carrier whose magnetic layer consists of chromium dioxide (Cr02) and has a point of Fairly low curia (125 C). The magnetic layer (cor02) of the recording medium is heated to a temperature above the Curie point. Then the heated magnetic layer of the recording medium is brought into contact with the magnetic layer of the matrix, on which the information is recorded in the form of magnetization zones. This contact produces a strong cooling of the recording carrier and the information is re-recorded from the matrix on the magnetic layer of the recording carrier. After the thermal re-recording, the information carrier is subjected to additional heating until at a temperature below the Curie point (700C), but not less than 400C, to reduce deformations.
Cependant, ce procédé, malgré sa haute efficacité, est limité pour le tirage de masse à cause de la précision insuffisante du transfert de l'information, du fait de la déformation thermique du porteur d'enregistrement à substrat en polymère. D'autre part, pour le tirage thermique, on peut utiliser un porteur d'enregistrement avec une couche magnét#ique exclusivement en Cr02. However, this method, despite its high efficiency, is limited for mass pulling due to the insufficient precision of the information transfer, due to the thermal deformation of the recording carrier to polymer substrate. On the other hand, for thermal printing, it is possible to use a recording carrier with a magnetic layer exclusively of Cr02.
Le procédé de tirage d'un enregistrement magnétique le plus proche du procédé de la présente invention est le procédé selon le brevet japonais NO 52-27526, cl. 102E82, 1977, qui est réalisé de la façon suivante. Sur une matrice constituant le porteur de l'original de l'enregistrement magnétique, par exemple un ruban magnétique à force coercitive de 2,5 fois supérieure à celle du porteur d'enregistrement, on enregistre au préalable une information sous forme de zones d'aimantation disposées en image miroir de l'infòrma- tion du porteur d'enregistrement. Puis la couche magnétique de la matrice est mise en contact avec la couche magnétique du porteur d'enregistrement et, dans cette position, les deux porteurs sont enroulés ensemble sur la même bobine en formant un rouleau.Au cours de l'enroulement, l'air se trouvant entre les porteurs d'enregistrement est chassé par des galets de serrage, qui assurent ainsi un contact étroit entre les porteurs. Puis la bobine est soumise à l'action d'un champ magnétique de valeur déterminée, de sorte que l'information est enregistrée à partir de la matrice sur le porteur d'enregistrement magnétique. The method for drawing a magnetic recording closest to the method of the present invention is the method according to Japanese patent NO 52-27526, cl. 102E82, 1977, which is carried out as follows. On a matrix constituting the carrier of the original magnetic recording, for example a magnetic tape with coercive force of 2.5 times that of the recording carrier, information is recorded beforehand in the form of zones of magnetization arranged in mirror image of the information of the recording carrier. Then the magnetic layer of the matrix is brought into contact with the magnetic layer of the recording carrier and, in this position, the two carriers are wound together on the same reel forming a roll. During the winding, the air between the recording carriers is expelled by clamping rollers, which thus ensure close contact between the carriers. Then the coil is subjected to the action of a magnetic field of determined value, so that the information is recorded from the matrix on the magnetic recording carrier.
Cependant, malgré la rapidité et la fiabilité de ce procédé celui-ci présente des inconvénients, à savoir:
- l'utilisation d'un appareillage spécial d'enregistrement et de reproduction, car on met en contact les couches magnétiques de la matrice et du porteur d'enregistrement et il faut avoir sur la matrice l'enregistrement de l'image miroir de l'original de l'information;
- on doit disposer d'un porteur d'enregistrement (d'une matrice) à haute force coercitive (1400 oersteds), ainsi que de têtes d'enregistrement et de reproduction spéciales;
- l'enregistrement des hautes fréquences est limité, car la matrice doit posséder une haute force coercitive et, par conséquent, le porteur d'enregistrement magnétique est limité en densité d'enregistrement de l'information.However, despite the speed and reliability of this process, it has drawbacks, namely:
- the use of a special recording and reproducing apparatus, because the magnetic layers of the matrix and the recording carrier are brought into contact and the mirror image of the image must be recorded on the matrix 'original information;
- a recording medium (a matrix) with high coercive force (1400 oersteds), as well as special recording and reproduction heads must be available;
- the recording of high frequencies is limited, because the matrix must have a high coercive force and, consequently, the carrier of magnetic recording is limited in density of recording of information.
La présente invention a pour but la création d'un procédé de préparation d'une matrice pour le tirage d'enregistrements magnétiques qui, grâce à la transformation de l'information magnétique enregistrée en relief sur la surface du porteur, permettrait de réaliser une matrice assurant une haute densité d'information, une bonne précision et en même temps une durée accrue d'utilisation pour le tirage des informations, et qui permettrait également de procéder au tirage sur divers porteurs d'enregistrement. The object of the present invention is to create a method for preparing a matrix for printing magnetic records which, by means of the transformation of the magnetic information recorded into relief on the surface of the carrier, would make it possible to produce a matrix. ensuring a high density of information, good accuracy and at the same time an increased duration of use for the printing of information, and which would also make it possible to carry out the printing on various record carriers.
Un autre but de la présente invention est la création d'un procédé de tirage d'un enregistrement magnétique, qui, grâce à l'utilisation de la matrice obtenue selon le procédé faisant l'objet de la présente invention, permettrait d'obtenir un niveau élevé du signal à partir de la copie, tout en conservant unehaute capacité de tirage et d'assurer la lecture de l'information à partir des copies de diverses manières,
Ce problème est résolu du fait, que dans un procédé de préparation d'une matrice pour le tirage d'un enregistrement magnétique par transfert sur une matrice des informations portées par un porteur d'enregistrement magnétique, matrice, selon l'invention on applique sur le porteur d'enregistrement un liquide ferromagnétique qui, en séchant dans le champ magnétique de cet enregistrement, transforme l'enregistrement en relief, puis on applique sur ce relief une première couche de matériau, puis on sépare cette couche de matériau et on obtient ainsi une matrice pour le tirage de l'enregistrement magnétique.Another object of the present invention is the creation of a method for drawing a magnetic recording, which, thanks to the use of the matrix obtained according to the method which is the subject of the present invention, would make it possible to obtain a high signal level from the copy, while retaining a high print capacity and ensuring the reading of information from the copies in various ways,
This problem is solved by the fact that in a method of preparing a matrix for drawing a magnetic recording by transfer to a matrix of information carried by a magnetic recording carrier, matrix, according to the invention is applied to the recording carrier a ferromagnetic liquid which, by drying in the magnetic field of this recording, transforms the recording into relief, then a first layer of material is applied to this relief, then this layer of material is separated and thus obtained a matrix for drawing the magnetic recording.
Ce procédé permet d'obtenir une matrice métallique résistant au tirage avec une longueur d'onde d'enregistrement minimale et une profondeur maximale du relief. This process makes it possible to obtain a metallic matrix resistant to printing with a minimum recording wavelength and a maximum depth of the relief.
Il est avantageux d'appliquer le liquide ferromagnétique de la façon suivante: on crée un champ magnétique externe dont la valeur d'induction est choisie entre zéro et l'induction de saturation du porteur d'enregistrement magnétique, puis on applique sur ce porteur le liquide ferromagnétique, qui sèche dans les deux champs magnétiques en interaction, c'est-à-dire le champ magnétique externe et le champ magnétique de l'enregistrement. It is advantageous to apply the ferromagnetic liquid as follows: an external magnetic field is created, the induction value of which is chosen between zero and the saturation induction of the magnetic recording carrier, then the carrier is applied to this carrier. ferromagnetic liquid, which dries in the two interacting magnetic fields, i.e. the external magnetic field and the magnetic field of the recording.
Ceci permet d'obtenir une fréquence des creux du relief égale à la fréquence d'enregistrement sur la couche magnétique du porteur d'enregistrement, d'augmenter la profondeur du relief, d'améliorer la "netteté" du relief. This makes it possible to obtain a frequency of the valleys of the relief equal to the frequency of recording on the magnetic layer of the recording carrier, to increase the depth of the relief, to improve the "sharpness" of the relief.
La composition du liquide ferromagnétique peut être la suivante : magnétite-10%, oléate de sodium82 eau 82%. The composition of the ferromagnetic liquid can be as follows: magnetite-10%, sodium oleate 82 water 82%.
Ces proportions des composants permettent de trans ferrer d'une façon précise la répartition de l'aimantation de la couche magnétique du porteur d'enregistrement et, ce qui est très important, d'accrottre la profondeur du relief. These proportions of the components make it possible to transfer in a precise manner the distribution of the magnetization of the magnetic layer of the record carrier and, which is very important, to increase the depth of the relief.
Il est avantageux que la transformation en relief de l'information magnétique enregistrée -soit réalisée selon la relation:
ho (k1U0+k2f) (1)
où ho (x,y,z) est le profil du relief formé par la couche
de liquide ferromagnétique séchée;
OC est un coefficient tenant compte des propriétés du
liquide ferromagnétique;
est un coefficient tenant compte de l'interaction du
champ magnétique externe et du champ magnétique de
l'enregistrement.It is advantageous that the transformation into relief of the recorded magnetic information - be carried out according to the relation:
ho (k1U0 + k2f) (1)
where ho (x, y, z) is the profile of the relief formed by the layer
dried ferromagnetic liquid;
OC is a coefficient taking into account the properties of
ferromagnetic liquid;
is a coefficient taking into account the interaction of
external magnetic field and the magnetic field of
the record.
k1,k2 sont des coefficients généralisés des pertes d'enre
gistrement dans le système d'enregistrement magnétique
de l'information;
U0 est l'amplitude du signal enregistré sur le porteur
d'enregistrement magnétique;
f est la fréquence du signal enregistré.k1, k2 are generalized coefficients of loss of ink
registration in the magnetic recording system
some information;
U0 is the amplitude of the signal recorded on the carrier
magnetic recording;
f is the frequency of the recorded signal.
Il est avantageux d'appliquer sur la première couche
de matériau une couche de matériau servant de substrat.It is advantageous to apply on the first layer
of material a layer of material serving as a substrate.
Le substrat peut être réalisé en matériau polymère. The substrate can be made of polymer material.
Le substrat peut être également réalisé en métal ou
en alliage. Ceci permet d'obtenir une matrice à bas prix
de revient.The substrate can also be made of metal or
alloy. This makes it possible to obtain a matrix at low cost.
returns.
On peut rendre plus économique le processus de pré
paration des matrices en appliquant une seconde couche de
matériau entre le relief formé par le liquide ferromagné
tique séché et la première couche de matériau,et en réali
sant la séparation des couches entre les matériaux ferro
magnétiques, en obtenant ainsi deux matrices.Alors l'une
des matrices constitue un porteur d'enregistrement magnétique,
dont l'aimantation est transformée en relief par le liquide
ferromagnétique, et des couches de matériau selon la
relation:
* +k f)
ho
dans laquelle:
*
ho est le profil du relief de la matrice directe;
est un coefficient tenant compte des propriétés du
liquide ferromagnétique;
est un coefficient tenant compte de l'interaction
entre le champ magnétique externe et le champ magnétique
de l'enregistrement;
est un coefficient tenant compte de la distorsion du
relief due à la première couche de matériau appliquée; k1,k2 sont des coefficients généralisés des pertes d'enregis
trement dans le système d'enregistrement magnétique de
l'information;
UO est l'amplitude du signal enregistré sur le porteur
de l'enregistrement magnétique;
f est la fréquence du signal enregistré, tandis que
l'autre matrice constitue une couche de matériau avec
ou sans substrat, dont le profil du relief est relié à
*
ho (x,y,z) par la relation:
hm (x,y,z) = Y ho (x,y,z) (2)
hm (x,y,z) est le profil du relief de la matrice
inverse;
est un coefficient négatif tenant compte des pertes
de profil du relief ho (x,y,z) au cours du cycle
technologique de fabrication des matrices.We can make the pre process more economical
trim the matrices by applying a second coat of
material between the relief formed by the ferromagnetic liquid
dried tick and the first layer of material, and in real
the separation of the layers between the ferro materials
magnetic, thus obtaining two matrices.
matrices constitutes a magnetic recording carrier,
whose magnetization is transformed into relief by the liquid
ferromagnetic, and layers of material according to the
relationship:
* + kf)
ho
in which:
*
ho is the relief profile of the direct matrix;
is a coefficient taking into account the properties of the
ferromagnetic liquid;
is a coefficient taking into account the interaction
between the external magnetic field and the magnetic field
registration;
is a coefficient taking into account the distortion of the
relief due to the first layer of material applied; k1, k2 are generalized coefficients of recording losses
highly in the magnetic recording system of
information;
UO is the amplitude of the signal recorded on the carrier
magnetic recording;
f is the frequency of the recorded signal, while
the other matrix constitutes a layer of material with
or without substrate, whose relief profile is connected to
*
ho (x, y, z) by the relation:
hm (x, y, z) = Y ho (x, y, z) (2)
hm (x, y, z) is the profile of the relief of the matrix
reverse;
is a negative coefficient taking into account losses
in profile of the relief ho (x, y, z) during the cycle
technological manufacturing of dies.
On peut assurer le tirage de l'enregistrement magnétique sur lé porteur d'enregistrement magnétique en obtenant des matrices dont la première couche de matériau appliquée sur le relief du liquide ferromagnétique séché est réalisée en matériau ferromagnétique. It is possible to ensure the drawing of the magnetic recording on the magnetic recording carrier by obtaining matrices the first layer of material applied to the relief of the dried ferromagnetic liquid is made of ferromagnetic material.
On peut réaliser d'une manière plus économique le processus de fabrication des matrices pour le tirage d'enregistrements magnétiques sur le porteur d'enregistrement magnétique en appliquant une seconde couche de matériau ferroma magnétique entre le relief, formé par le liquide ferromagnétique séché, et la première couche de matériau ferromagnétique. The process of manufacturing the matrices for drawing magnetic recordings on the magnetic recording carrier can be carried out more economically by applying a second layer of magnetic ferroma material between the relief, formed by the dried ferromagnetic liquid, and the first layer of ferromagnetic material.
On peut disposer entre le relief formé par le liquide ferromagnétique séché et la couche de matériau ferromagnétique une couche de matériau conducteur de courant. It is possible to have between the relief formed by the dried ferromagnetic liquid and the layer of ferromagnetic material a layer of current conducting material.
Ceci permet d'améliorer la technologie du cycle de fabrication des matrices. This improves the technology of the die manufacturing cycle.
Une autre variante du procédé de fabrication de matrices à profils en relief correspondant à ho (x,y,z) et hm (x,y,z) , exécutés au cours d'un même cycle technologique et possédant des couches ferromagnétiques en matériau à hystérésis, consiste en ce qui suit. On crée un champ magnétique dans lequel on aimante les matrices obtenues pour le tirage de l'enregistrement magnétique1 la répartition des inductions rémanentes aux surfaces de ces matrices étant décrite par les relations
B1(x,y,z)=B0 & h*#(x,y,z);
B2(x,y,z)=B h (x,y,z) où Bo est l'induction du champ magnétique créé;
B1 (x,y,z) est la répartition de l'induction rémanente à la surface de la matrice à profil de
* relief ho (x,y,z); ;
B2(x,y,z) est la répartition de l'induction rémanente à la surface de la matrice à profil de relief hm (x,y,z);
61/ 62 sont des coefficients qui caractérisent les propriétés physico-mécaniques et magnétiques des couches de matériaux ferromagnétiques des matrices.Another variant of the process for manufacturing dies with raised profiles corresponding to ho (x, y, z) and hm (x, y, z), executed during the same technological cycle and having ferromagnetic layers of material with hysteresis, consists of the following. A magnetic field is created in which the matrices obtained for the magnetic recording are magnetized1 the distribution of the residual inductions on the surfaces of these matrices being described by the relations
B1 (x, y, z) = B0 & h * # (x, y, z);
B2 (x, y, z) = B h (x, y, z) where Bo is the induction of the magnetic field created;
B1 (x, y, z) is the distribution of the residual induction on the surface of the matrix with profile
* relief ho (x, y, z); ;
B2 (x, y, z) is the distribution of the residual induction at the surface of the matrix with relief profile hm (x, y, z);
61/62 are coefficients which characterize the physico-mechanical and magnetic properties of the layers of ferromagnetic materials of the matrices.
Le problème exposé plus haut est également résolu du fait, que dans un procédé de tirage d'un enregistrement magnétique par transfert des informations à partir d'une matrice, obtenue selon le procédé revendiqué, sur un porteur d'enregistrement magnétique serré contre ladite matrice, selon l'invention on crée un champ magnétique, puis on fait passer à travers ce champ la matrice avec le porteur d'informations ce qui assure la modulation du champ magnétique conformément au relief de la surface de la matrice, ce champ modulé étant enregistré sur le porteur d'informations lui même. The problem set out above is also solved by the fact that in a method of drawing a magnetic recording by transferring information from a matrix, obtained according to the claimed method, on a magnetic recording carrier pressed against said matrix , according to the invention a magnetic field is created, then the matrix is passed through this field with the information carrier which ensures the modulation of the magnetic field in accordance with the relief of the surface of the matrix, this modulated field being recorded on the information carrier himself.
Ledit probldme est également résolu du fait que dans le procédé de tirage d:un enregistrement magnétique par transfert d'informations à partir d'une matrice sur un porteur d'enregistrement serré contre elle, selon l'invention la couche de travail du porteur d'enregistrement est chauffée avant le tirage, puis est refroidie au cours du tirage, de sorte qu'on obtient sur le porteur d'enregistrement lui-même une empreinte du relief, conformément au relief de la surface de la matrice
Ceci permet de produire des copies de faible coût pour lecture optique.Said problem is also solved by the fact that in the process of drawing a magnetic recording by transfer of information from a matrix onto a recording carrier pressed against it, according to the invention the working layer of the carrier. the recording is heated before the printing, then is cooled during the printing, so that one obtains on the recording carrier itself an imprint of the relief, in accordance with the relief of the surface of the matrix
This makes it possible to produce low cost copies for optical reading.
L'invention sera mieux comprise et d'autres buts, détails et avantages de celle-ci apparaltront mieux à la lumière de la description explicative qui va suivre de différents modes de réalisation donnés uniquement à titre d'exemples non limitatifs avec références aux dessins non limitatifs annexés dans lesquels::
- la figure 1 est une vue d'ensemble schématique d'un porteur d'enregistrement magnétique, sur lequel les informations sont enregistrées sous forme d'une répartition de zones d'aimantation rémanente, et le relief séché de la couche de liquide ferromagnatique dans le champ du porteur d'enregistrement, selon l'invention;
- la figure 2 représente schématiquement le processus de formation d'un relief sur le porteur de l'original de l'enregistrement magnétique dans un champ magnétique, selon l'invention;
- la figure 3 représente shcématiquement une vue en coupe du porteur d'enregistrement sur lequel sont appliquées les couches de liquide ferromagnétique et de matériau, selon l'invention;;
- la figure 4 représente schématiquement une vue d'ensemble du porteur d'enregistrement magnétique sur lequel sont appliquées les couches de liquide ferromagnatique séché et de matériau, selon l'invention;
- la figure 5 représente shcématiquement une vue d'ensemble du porteur denregistrement, de la couche de liquide ferromagnétique séchée, de la couche de matériau et du substrat, obtenus lors de la préparation de la matrice;
- la figure 6 représente schématiquement une vue en coupe de l'original du porteur d'enregistrement en relief du liquide ferromagnétique séché de la couche de matériau et du substrat, selon l'invention;;
- la figure 7 représente schématiquement une vue d'ensemble du porteur d'enregistrement avec le relief obtenu à partir de la couche de liquide magnétique séché et portant les couches de matériaux ferromagnétiques, selon 1' invention;
- la figure 8 représente schématiquement une vue d'ensemble du porteur d'enregistrement, de la couche de liquide ferromagnétique séché sur laquelle est appliquée une couche de matériau ferromagnétique, et, séparée de cette dernière, une autre couche de matériau ferromagnétique dans un système de coordonnées linéaires x,y,z, selon l'invention;
- la figure 9 représente schématiquement une vue en coupe transversale du porteur d'enregistrement magnétique, de la couche de liquide ferromagnétique séché, de la couche conductrice de courant, et de la matrice ferromagnétique, selon l1invention;;
- la figure 10 illustre schématiquement le procédé de tirage des informations à partir d'une matrice sur un porteur d'enregistrement magnétique dans un champ magnétique, selon l'invention;
- la figure 11 illustre schématiquement le procédé de tirage des informations sur un porteur à partir d'une matrice thermoplastique.The invention will be better understood and other objects, details and advantages thereof will appear better in the light of the explanatory description which will follow of various embodiments given solely by way of nonlimiting examples with reference to the non-drawing drawings. annexed limitative in which:
- Figure 1 is a schematic overview of a magnetic recording carrier, on which the information is recorded in the form of a distribution of remanent magnetization zones, and the dried relief of the layer of ferromagnetic liquid in the field of the record holder, according to the invention;
- Figure 2 schematically shows the process of forming a relief on the carrier of the original magnetic recording in a magnetic field, according to the invention;
- Figure 3 schematically shows a sectional view of the recording carrier on which are applied the layers of ferromagnetic liquid and material, according to the invention;
- Figure 4 schematically shows an overview of the magnetic recording carrier on which are applied the layers of dried ferromagnetic liquid and material, according to the invention;
- Figure 5 schematically shows an overview of the recording carrier, the layer of dried ferromagnetic liquid, the layer of material and the substrate, obtained during the preparation of the matrix;
- Figure 6 shows schematically a sectional view of the original of the recording carrier in relief of the dried ferromagnetic liquid of the material layer and the substrate, according to the invention;
- Figure 7 schematically shows an overview of the recording carrier with the relief obtained from the layer of dried magnetic liquid and carrying the layers of ferromagnetic materials, 1 according to the invention;
- Figure 8 schematically shows an overview of the recording medium, the layer of dried ferromagnetic liquid on which is applied a layer of ferromagnetic material, and, separated from the latter, another layer of ferromagnetic material in a system linear coordinates x, y, z, according to the invention;
- Figure 9 schematically shows a cross-sectional view of the magnetic recording carrier, the layer of dried ferromagnetic liquid, the current conducting layer, and the ferromagnetic matrix, according to the invention;
- Figure 10 schematically illustrates the method of drawing information from a matrix on a magnetic recording carrier in a magnetic field, according to the invention;
- Figure 11 schematically illustrates the method of drawing information on a carrier from a thermoplastic matrix.
Le procédé revendiqué de préparation d'une matrice pour le tirage d'un enregistrement magnétique est mis en oeuvre de la façon suivante. The claimed method of preparing a matrix for drawing a magnetic recording is carried out as follows.
On enregistre sur la couche magnétique 1 d'un porteur d'enregistrement magnétique, qui, d'ordinaire est constitué par la couche magnétique de travail 1 (figure 1) et un substrat 2, des informations sous forme de zones d'aimantation longitudinale caractérisée par la fréquences f, dont la répartition dans le volume de la couche magnétique de travail 1 est représentée par les lignes magnétiques de force 3. Information is recorded on the magnetic layer 1 of a magnetic recording carrier, which usually consists of the magnetic working layer 1 (FIG. 1) and a substrate 2, in the form of zones of longitudinal magnetization characterized by the frequencies f, the distribution of which in the volume of the magnetic working layer 1 is represented by the magnetic lines of force 3.
Ensuite on applique une couche de liquide ferromag nétique 4, qui rend visible la répartition de l'aimantation du porteur d'enregistrement en créant un relief à sa surface. La fréquence du relief ainsi formé est deux fois supérieure à la fréquence des informations enregistrées, la hauteur des "bosses" du relief correspondant à la profondeur d'aimantation du porteur d'enregistrement magnétique. Then a layer of ferromagnetic liquid 4 is applied, which makes the distribution of the magnetization of the recording carrier visible by creating a relief on its surface. The frequency of the relief thus formed is twice as high as the frequency of the information recorded, the height of the "bumps" in the relief corresponding to the depth of magnetization of the magnetic recording carrier.
Après que la couche de liquide ferromagnétique 4 ait séché, on applique une première couche de matériau 5 (figures 3, 4) qui en entrant en contact avec le relief obtenu constitue son image miroir. Ladite couche de matériau peut être constituez d'un matériau polymère, ou d'un métal, ou encore d'un alliage. After the layer of ferromagnetic liquid 4 has dried, a first layer of material 5 is applied (FIGS. 3, 4) which, by coming into contact with the relief obtained, constitutes its mirror image. Said layer of material may consist of a polymer material, or of a metal, or even of an alloy.
On peut utiliser comme matériau polymère le produit connu sous la dénomination commerciale "Lavsan", par exemple.The product known under the trade name "Lavsan", for example, can be used as polymer material.
Les métaux, tels que par exemple le cuivre, le nickel, ou les alliages tels que par exemple l'alliage connu sous la dénomination commerciale "Permalloy "le laiton, peuvent être appliqués par exemple par vaporisation sous vide.The metals, such as for example copper, nickel, or the alloys such as for example the alloy known under the trade name "Permalloy" brass, can be applied for example by vaporization under vacuum.
Puis la couche de matériau 5 est séparée des autres couches, c'est-à-dire de la couche de liquide ferromagnétique 4 et et de la couche magnétique de travail 1 du porteur d'enregistrement, qui sont enlevées, par exemple, par une méthode chimico-mécanique, en obtenant ainsi une matrice pour le tirage de l'enregistrement magnétique.Then the material layer 5 is separated from the other layers, i.e. from the ferromagnetic liquid layer 4 and from the magnetic working layer 1 of the recording carrier, which are removed, for example, by a chemical-mechanical method, thus obtaining a matrix for drawing the magnetic recording.
Afin de conserver les informations introduites à la fréquence du signal enregistré, on applique le liquide ferromagnétique 4 (figure 2) dans un champ magnétique externe créé par exemple par l'aimant permanent 6. Ce champ peut être un champ continu, alternatif ou pulsatoire, son induction étant choisie (en fonction du type d'enregistrement magnétique, du type de porteur d'enregistrement magnétique, des paramètres magnétiques de la couche de travail 1 du porteur d'enregistrement magnétique, des paramètres du liquide ferromagnétique 4) dans une plage allant de zéro à une valeur proche de l'induction de saturation du porteur d'enregistrement magnétique.Pour former un relief plus "net" à partir du liquide ferromagnétique 4 sur la couche magnétique 1 du porteur d'enregistrement magnétique portant les informations, il est avantageux de réaliser le processus d'application et de séchage du liquide ferromagnétique 4 dans un champ magnétique pulsatoire, dont leamplitude des pulsations et la fréquence sont choisies en fonction des caractéristiques de l'enregistrement magnétique et des propriétés magnétiques du liquide ferromagnétique. Lorsque le champ magnétique dans lequel sont effectués l'application et le séchage du liquide ferromagnétique 4 sur la couche magnétique 1 du porteur d'enregistrement portant les informations possède une induction proche de zéro, on observe un doublement de la fréquence des saillies du relief, tandis que dans le cas d'un champ magnétique possédant une induction proche de l'induction de saturation du porteur d'enregistrement magnétique, on observe une diminution de la hauteur du relief, et d'autre part, la "netteté du relief devient moins bonne lorsque l'induction des champs magnétiques se
rapproche de zéro et de l'induction de saturation de la
couche magnétique de travail 1 du porteur d'enregistre
ment.In order to preserve the information introduced at the frequency of the recorded signal, the ferromagnetic liquid 4 (FIG. 2) is applied in an external magnetic field created for example by the permanent magnet 6. This field can be a continuous, alternating or pulsating field, its induction being chosen (as a function of the type of magnetic recording, of the type of magnetic recording carrier, of the magnetic parameters of the working layer 1 of the magnetic recording carrier, of the parameters of the ferromagnetic liquid 4) in a range from from zero to a value close to the saturation induction of the magnetic recording carrier. To form a "sharper" relief from the ferromagnetic liquid 4 on the magnetic layer 1 of the magnetic recording carrier carrying the information, it is advantageous to carry out the process of application and drying of the ferromagnetic liquid 4 in a pulsating magnetic field, including the amplitude of the pulsations and the frequency are chosen according to the characteristics of the magnetic recording and the magnetic properties of the ferromagnetic liquid. When the magnetic field in which the application and the drying of the ferromagnetic liquid 4 are carried out on the magnetic layer 1 of the record carrier carrying the information has an induction close to zero, a doubling of the frequency of the projections of the relief is observed, while in the case of a magnetic field having an induction close to the saturation induction of the magnetic recording carrier, a decrease in the height of the relief is observed, and on the other hand, the "sharpness of the relief becomes less good when induction of magnetic fields occurs
approximates zero and the saturation induction of the
working magnetic layer 1 of the record holder
is lying.
L'interaction du champ magnétique de l#électroaimant
6 (figure 2) et des zones d#aimantation de la couche
magnétique de travail 1 du porteur d'enregistrement provo
que une modification de la répartition du champ magnétique
à l'intérieur et au-dessus de la surface de sa couche de
travail 1.La forme et la direction du champ magnétique
externe sont choisies de façon à transformer les infor
mations enregistrées en un relief du liquide ferromagné
tique séché dans ce clamp dans un système de coordonnées
conforme à la relation:
(k1U0+k2f) (1)
od ho (x,y,z) est le profil du relief du liquide ferromag
tique à la surface du porteur d'enregistrement
dans un système de coordonnées rectangulaire;
g est un coefficient tenant compte des propriétés du
liquide ferromagnêtique;
est un coefficient tenant compte de l'interaction du
champ magnétique externe avec le champ magnétique de
l'enregistrement; k1,k2 sont des coefficients généralisés des pertes d9enre
gistrement dans le système d'enregistrement magnéti
que des informations;
UO est l'amplitude du signal enregistré sur le porteur
d'enregistrement magnétique;
f est la fréquence du signal enregistré sur le porteur
d'enregistrement magnétique;;
Le profil du relief ho (x,y,z) dans le système de coordonnées rectangulaires, formé par le liquide ferromagnétique 4 séché à la surface du porteur d'enregistrement magnétique sous l'action d'un champ magnétique externe choisi entre zéro et la valeur de l'induction de saturation du por teur d'enregistrement magnétique, et du champ magnétique du porteur d'enregistrement, est déterminé par les pro priétés physico-mécaniques et magnétiques du porteur d'enregistrement magnétique, par les caractéristiques du signal enregistré, par les caractéristiques des moyens d'enregistrement (des têtes), par les conditions du processus d'enregistrement, par les caractéristiques du liquide ferromagnétique, par la valeur et le caractère du champ magnétique externe dans lequel sèche le liquide ferromagnétique..Interaction of the magnetic field of the electromagnet
6 (Figure 2) and magnetization zones of the layer
working magnetic 1 of the provo record holder
that a change in the distribution of the magnetic field
inside and above the surface of its layer of
1.The shape and direction of the magnetic field
are chosen to transform the information
mations recorded in relief of ferromagnetic liquid
tick dried in this clamp in a coordinate system
consistent with the relationship:
(k1U0 + k2f) (1)
od ho (x, y, z) is the relief profile of the ferromag liquid
tick on the surface of the record holder
in a rectangular coordinate system;
g is a coefficient taking into account the properties of the
ferromagnetic liquid;
is a coefficient taking into account the interaction of
external magnetic field with the magnetic field of
the record; k1, k2 are generalized coefficients of losses from
recording in the magnetic recording system
that information;
UO is the amplitude of the signal recorded on the carrier
magnetic recording;
f is the frequency of the signal recorded on the carrier
magnetic recording;
The profile of the relief ho (x, y, z) in the rectangular coordinate system, formed by the ferromagnetic liquid 4 dried on the surface of the magnetic recording carrier under the action of an external magnetic field chosen between zero and the value of the saturation induction of the magnetic recording carrier, and of the magnetic field of the recording carrier, is determined by the physico-mechanical and magnetic properties of the magnetic recording carrier, by the characteristics of the recorded signal, by the characteristics of the recording means (heads), by the conditions of the recording process, by the characteristics of the ferromagnetic liquid, by the value and the character of the external magnetic field in which the ferromagnetic liquid dries.
Le profil ho (x,y,z) du relief dans le système de coordonnées rectangulaires est décrit par une fonction exponentielle dont l'exposant représente la somme de l'amplitude UO et de la fréquence f du signal à enregistrer avec des coefficients k1 et k2 appropriés tenant compte des propriétés du porteur de l'enregistrement magnétique : de l'aimantation rémanente, de la force coercitive, de la forme de la boucle d'hystérésis, ainsi que des pertes d'enregistrement dans le système d'enregistrement magnétique des informations, dues à l'absence de contact de la tête d'enregistrement avec le porteur d'enregistrement magnétique, à la variation de la vitesse de déplacement de l'enregistrement magnétique, à la caractéristique de la tête d'enregistrement, etc.Le coefficient tient compte des propriétés du liquide ferromagnétique: de l'aimantation. de saturation, des dimensions et du matériau des particules magnétiques, de la densité, de la tension superficielle, etc. Le coeffi externe et le compte magnetique de l'enregistrement, qui estmagnétique sur le liquide ferromagnétique séché
Le profil du relief ho (x,y,z) suivant la relation (1) correspond d'autant plus au signal à enregistrer, que les pertes d'enregistrement dans le système tête d'enregistrement-porteur d'enregistrement magnétique sont faibles, l'aimantation de saturation du liquide ferromagnétique plus élevée, la densité plus faible et plus petites sont les dimensions des particules magnétiques du liquide ferromagnétique.The profile ho (x, y, z) of the relief in the rectangular coordinate system is described by an exponential function whose exponent represents the sum of the amplitude UO and the frequency f of the signal to be recorded with coefficients k1 and k2 appropriate taking into account the properties of the magnetic recording carrier: the remanent magnetization, the coercive force, the shape of the hysteresis loop, as well as the recording losses in the magnetic recording system of the information, due to the absence of contact of the recording head with the magnetic recording carrier, to the variation of the speed of movement of the magnetic recording, to the characteristic of the recording head, etc. coefficient takes into account the properties of the ferromagnetic liquid: of the magnetization. saturation, dimensions and material of magnetic particles, density, surface tension, etc. The external coefficient and the magnetic count of the recording, which is magnetic on the dried ferromagnetic liquid
The profile of the relief ho (x, y, z) according to the relation (1) corresponds all the more to the signal to be recorded, the lower the recording losses in the recording head-carrier system for magnetic recording, the higher saturation magnetization of the ferromagnetic liquid, the lower density and smaller are the dimensions of the magnetic particles of the ferromagnetic liquid.
Le liquide ferromagnétique appliqué peut, par exemple, avoir la composition suivante: magnétite 10%, eau distillée 82%, oléate de sodium 8%, avec une viscosité de l'ordre de 16 à 18 cSt. The ferromagnetic liquid applied can, for example, have the following composition: magnetite 10%, distilled water 82%, sodium oleate 8%, with a viscosity of the order of 16 to 18 cSt.
Il convient de remarquer que le liquide ferromagnétique peut avoir une autre composition connue et caractéristique pour les liquides ferromagnétiques. En qualité de liquide ferromagnétique il est avantageux d'utiliser notamment un liquide ferromagnétique colloïdal, car il donne un relief plus contrasté à la surface du porteur et possède une plus grande longévité lors du stockage. It should be noted that the ferromagnetic liquid may have another known and characteristic composition for ferromagnetic liquids. As a ferromagnetic liquid it is advantageous to use in particular a colloidal ferromagnetic liquid, since it gives a more contrasted relief to the surface of the carrier and has a greater longevity during storage.
Après que la couche 4 de liquide ferromagnétique ait séché, on applique la couche de matériau 5 (figure 3, 4) qui, en entrant avec le relief obtenu, constitue son image miroir. La couche de matériau 5 peut être appliquée d'une façon connue quelconque, par exemple par voie chimique. Puis la couche de matériau 5 est séparée des autres couches. Cette séparation laisse sur la couche de matériau avec l'image miroir du relief des traces des couches précédentes: du liquide ferromagnétique 4, de la couche magnétique de travail 1 du porteur d'enregistrement, que l'on fait disparaître, par exemple, par des moyens chimiques ou mécaniques. La couche de matériau 5 formant le relief miroir correspondant au relief du liquide magnétique séché 4 et débarassé des autres couches constitue la matrice destinée au tirage de l'enregistrement magnétique. After the layer 4 of ferromagnetic liquid has dried, the layer of material 5 is applied (FIG. 3, 4) which, entering with the relief obtained, constitutes its mirror image. The layer of material 5 can be applied in any known manner, for example chemically. Then the layer of material 5 is separated from the other layers. This separation leaves on the layer of material with the mirror image of the relief traces of the previous layers: ferromagnetic liquid 4, the magnetic working layer 1 of the recording carrier, which is made to disappear, for example, by chemical or mechanical means. The layer of material 5 forming the mirror relief corresponding to the relief of the dried magnetic liquid 4 and removed from the other layers constitutes the matrix intended for printing the magnetic recording.
La matrice pour le tirage d'un enregistrement magnétique peut être obtenue de la façon suivante. Sur le relief de la couche 4 (figures5, 6) de liquide ferromagnétique séché on applique la couche de matériau 5 selon un procédé connu quelconque, par exemple par vaporisation de métal sous vide. The matrix for drawing a magnetic recording can be obtained as follows. On the relief of the layer 4 (FIGS. 5, 6) of dried ferromagnetic liquid, the layer of material 5 is applied according to any known method, for example by vaporization of metal under vacuum.
Puis on applique, par exemple au moyen de galets de contact, une couche 7 de matériau polymère constituant le substrat. Ce matériau polymère peut être, par exemple, du "Lavsan". Le substrat (7) portant la couche de matériau 5 séparée des autres couches (1 ,4) sert de matrice. Le substrat (7) peut être réalisé en métal, par exemple selon un procédé galvanoplastique de dépôt d'un métal ou d'un alliage soit ferromagnétique, tel que le nickel, le "Permalloy", soit magnétiques, tel que le cuivre, le laiton, sur la couche 5. Les matrices métalliques ont une meilleure endurance au tirage comparée à celle des matrices à substrat en matériau polymère.Then a layer 7 of polymeric material constituting the substrate is applied, for example by means of contact rollers. This polymer material can be, for example, "Lavsan". The substrate (7) carrying the layer of material 5 separated from the other layers (1, 4) serves as a matrix. The substrate (7) can be made of metal, for example according to an electroplating process of depositing a metal or an alloy either ferromagnetic, such as nickel, "Permalloy", or magnetic, such as copper, brass, on layer 5. The metal matrices have a better endurance when drawn compared to that of the matrices with a polymer material substrate.
On peut rendre plus économique la production de matrices pour le tirage d'un enregistrement magnétique sur un porteur d'enregistrement (1,2), à partir duquel la lecture est effectuée selon un procédé optique, en opérant par exemple de la façon suivante. Après que la couche 4 (figure 7) de liquide ferromagnétique ait séché, on applique successivement sur la surface de travail 1 du porteur d'enregistrement magnétique une première et une seconde couche d'un matériau (5,8) qui peut être un polymère, un métal ou un alliage, selon n'importe quelle méthode connue. Puis on sépare la première couche de matériau de la seconde, en obtenant ainsi deux matrices 10, 11 (figure 8) dont les profils respectifs sont des imagemiroirs, l'un par rapport à l'autre. The production of matrices for printing a magnetic recording on a recording carrier (1,2) can be made more economical, from which the reading is carried out according to an optical process, for example by operating as follows. After the layer 4 (FIG. 7) of ferromagnetic liquid has dried, a first and a second layer of a material (5,8) which may be a polymer, are successively applied to the working surface 1 of the magnetic recording carrier. , a metal or an alloy, by any known method. Then the first layer of material is separated from the second, thus obtaining two matrices 10, 11 (FIG. 8) whose respective profiles are mirror images, one with respect to the other.
Le profil du relief de la matrice 10, qui est constituee par le porteur d'enregistrement magnétique (1,2), la couche de liquide ferromagnétique 4 et la couche de matériau 8, en cas de transfert du relief à la couche 8, correspond à la relation:
ho (x ,y, z) e (k1U0+k2f),
o (x,y, o dans laquelle ho (x,y,z) est le profil du relief de la matrice directe ;
est un coefficient tenant compte des propriétés
du liquide ferromagnétique;
est un coefficient tenant compte de la déforma-
tion du relief, due à la couche de matériau ap
pliquée;;
est un coefficient tenant compte de l'interaction
du champ magnétique externe avec le champ magné
tique de l'enregistrement; k1, k2 sont des coefficients généralisés des pertes
d'enregistrement dans le système d'enregistre
ment magnétique des informations;
UO est l'amplitude du signal enregistré sur le
porteur d'enregistrement magnétique;
f est la fréquence du signal enregistré.The profile of the relief of the matrix 10, which is constituted by the magnetic recording carrier (1,2), the layer of ferromagnetic liquid 4 and the layer of material 8, in the event of transfer of the relief to the layer 8, corresponds to the relationship:
ho (x, y, z) e (k1U0 + k2f),
o (x, y, o in which ho (x, y, z) is the profile of the relief of the direct matrix;
is a coefficient taking into account the properties
ferromagnetic liquid;
is a coefficient taking into account the deformation
tion of the relief, due to the layer of material ap
plicated ;;
is a coefficient taking into account the interaction
of the external magnetic field with the magnetic field
registration tick; k1, k2 are generalized coefficients of losses
recording in the recording system
magnetic information;
UO is the amplitude of the signal recorded on the
magnetic recording carrier;
f is the frequency of the recorded signal.
Le profil du relief de la seconde matrice obtenue
11, constituée par la couche de matériau 6, est inverse -et
correspond à la relation:
h (x,y,z)= Y h (x,y,z) (2)
est un coefficient négatif tenant compte des pertes
*
du profil du relief ho (x,y,z) au cours du cycle
technologique.The relief profile of the second matrix obtained
11, constituted by the layer of material 6, is inverse -and
corresponds to the relation:
h (x, y, z) = Y h (x, y, z) (2)
is a negative coefficient taking into account losses
*
of the profile of the relief ho (x, y, z) during the cycle
technological.
hm (x,y,z) est le profil du relief de la matrice inverse. hm (x, y, z) is the relief profile of the inverse matrix.
Le coefficient ~tient compte de la transformation
miroir du profil du relief ho (x,y,z) en un profil de relief h (x,y,z), des propriétés physico-mécaniques de la
m
couche appliquée,de l'homogénéité, etc.The coefficient ~ takes into account the transformation
mirror of the relief profile ho (x, y, z) into a relief profile h (x, y, z), of the physico-mechanical properties of the
m
applied layer, homogeneity, etc.
La relation 2 met en évidence le fait que le processus
technologique est d'autant plus efficace que la valeur du
coefficient 2 se rapproche de l'unité.Relation 2 highlights the fact that the process
the more effective the value of
coefficient 2 gets closer to unity.
La matrice pour le tirage de l'enregistrement magnétique
sur un porteur d'enregistrement magnétique peut être obtenue
de la façon suivante.The matrix for drawing the magnetic recording
on a magnetic recording carrier can be obtained
as follows.
On enregistre les informations sous la forme de zones
a aimantation longitudinale sur la couche magnétique de travail 1 (figures 5, 6) d'un porteur d'enregistrement magnétique. Puis on applique une couche de liquide ferromagnétique 4, qui; en séchant dans un champ magnétique externe et le champ magnétique de l'enregistrement, forme un relief.The information is recorded in the form of zones
has longitudinal magnetization on the magnetic working layer 1 (FIGS. 5, 6) of a magnetic recording carrier. Then a layer of ferromagnetic liquid 4 is applied, which; by drying in an external magnetic field and the magnetic field of the recording, forms a relief.
On applique la couche de matériau ferromagnétique 5 selon une méthode connue quelconque, par exemple par voie chimique.The layer of ferromagnetic material 5 is applied according to any known method, for example chemically.
On sépare la couche de matériau ferromagnétique 5 des autres couches, et on enlève les traces des couches précédentes: du liquide ferromagnétique 4 et de la couche magnétique de travail 1 du porteur d'enregistrement, par une méthode chimico-mécanique par exemple. La couche nettoyée 5 de matériau ferromagnétique constitue une matrice pour le tirage de 11 enregistrement magnétique sur un porteur d'enregistrement magnétique.The layer of ferromagnetic material 5 is separated from the other layers, and the traces of the previous layers are removed: ferromagnetic liquid 4 and the working magnetic layer 1 of the recording medium, by a chemical mechanical method for example. The cleaned layer 5 of ferromagnetic material constitutes a matrix for printing the magnetic recording on a magnetic recording carrier.
On peut rendre plus économique la production de matrices pour le tirage sur un porteur d'enregistrement magnétique de la façon suivante. Après que la couche de liquide ferromagnétique 4 Figure 7) ait séché, on applique successivement deux couches à la surface du porteur d'enregistrement: une couche 8 de matériau ferromagnétique et une couche 5 de matériau ferromagnétique. Puis on sépare les couches 5 et 8 de matériaux ferromagnétiques en obtenant alors deux matrices 10 et 11 (figures 8) dont les profils sont des images miroirs l'un par rapport à l'autre. The production of matrices for printing on a magnetic recording carrier can be made more economical in the following manner. After the layer of ferromagnetic liquid 4 (Figure 7) has dried, two layers are successively applied to the surface of the recording medium: a layer 8 of ferromagnetic material and a layer 5 of ferromagnetic material. Then the layers 5 and 8 of ferromagnetic materials are separated, thereby obtaining two matrices 10 and 11 (Figures 8) whose profiles are mirror images with respect to each other.
Aujourd'hui, l'un des procédés les plus avantageux, du point de vue technologique de préparation de la matrice pour le tirage sur un porteur d'enregistrement magnétique est le suivant. Today, one of the most advantageous processes, from the technological point of view of preparing the matrix for printing on a magnetic recording carrier is the following.
Sur le relief obtenu sur la surface de travail 1 (figure 9) du porteur d'enregistrement magnétique au moyen du liquide ferromagnétique 4, on applique une couche 9 de matériau conducteur, par exemple une couche de cuivre, par vaporisation sous vide. Ensuite on procède à un traitement galvanoplastique du relief métallisé dans un électrolyte d'amino-sulfate de nickel en déposant ainsi une couche ferro magnétique 5 de nickel sur la couche conductrice 9. On the relief obtained on the working surface 1 (FIG. 9) of the magnetic recording carrier by means of the ferromagnetic liquid 4, a layer 9 of conductive material is applied, for example a layer of copper, by vacuum vaporization. Next, a galvanic plastic treatment of the metallized relief is carried out in a nickel amino sulfate electrolyte, thereby depositing a ferro magnetic layer 5 of nickel on the conductive layer 9.
Puis on sépare la couche ferromagnétique de nickel 5 des autres couches : de la couche magnétique 1 du porteur d'enregistrement, de la couche de liquide ferromagnétique séché 4 et de la couche conductrice 9. Après la séparation, il subsiste sur l'image miroir du relief de la couche 5 de matériau ferromagnétique des restes desdites couches, que l'on fait disparaître par des moyens chimico-mécaniques, en obtenant ainsi une matrice en nickel pour le tirage de l'enregistrement magnétique sur des porteurs d'enregistrement magnétique
Le procédé proposé de préparation d'une matrice offre de larges possibilités pour le tirage de masse d'enregistrements dans la technique audio et vidéo.Ce procédé est hautement avantageux du point de vue technologique, car le relief est créé directement sur le porteur magnétique d'enregistrement et la matrice représente une image miroir.Then the ferromagnetic nickel layer 5 is separated from the other layers: from the magnetic layer 1 of the recording medium, from the dried ferromagnetic liquid layer 4 and from the conductive layer 9. After the separation, it remains on the mirror image. of the relief of the layer 5 of ferromagnetic material from the remains of said layers, which are made to disappear by chemical-mechanical means, thereby obtaining a nickel matrix for drawing the magnetic recording on magnetic recording carriers
The proposed method of preparing a matrix offers wide possibilities for the mass production of recordings in the audio and video technique. This method is highly advantageous from the technological point of view, since the relief is created directly on the magnetic carrier of the record and the matrix represent a mirror image.
Les matrices obtenues selon le procédé revendiqué ont un faible prix de revient, améliorent la gamme des fréquences d'enregistrement des informations, ce qui, à son tour, accroît la densité des informations pouvant être transférées. The matrices obtained according to the claimed method have a low cost price, improve the range of information recording frequencies, which, in turn, increases the density of the information that can be transferred.
D'autre part, si la matrice connue pour le tirage supporte jusqu'à 1000 contacts, les matrices métalliques réalisées selon le procédé revendiqué ont une durée de vie pratiquement illimitée.On the other hand, if the known matrix for the drawing supports up to 1000 contacts, the metal matrices produced according to the claimed process have a practically unlimited lifetime.
Les matrices destinées au tirage d'enregistrements magnétiques peuvent aussi être obtenues selon une autre variante de réalisation de la présente invention. The matrices intended for the printing of magnetic recordings can also be obtained according to another alternative embodiment of the present invention.
Pour la réalisation de ce procédé, les couches ferromagnétiques, qui comportent des reliefs volumiques, sont réalisées en matériau possédant une importante force coercitive, c'est-à-dire en un matériau à hystérésis. For carrying out this process, the ferromagnetic layers, which include volume reliefs, are made of material having a high coercive force, that is to say a material with hysteresis.
De telles matrices sont soumises à l'action d'un champ d'aimantation externe (6) dont les lignes de force sont perpendiculaires aux surfaces à reliefs. En conséquence, les couches ferromagnétiques des matrices s'aimantent et on dispose l'un des pôles sur les surfaces comportant un relief. D'autre part, l'une des matrices possède une répartition de l'induction rémanente au-dessus de la surface du relief correspondant à la relation:
B1 (x,y,z)=B06 IhO (x,y,z) (3) et à l'autre:
B2 (x,y,z)=Bo où Bo est l'induction du champ magnétique créé,
ff 1 t y2 sont des coefficients caractérisant les propriétés physico-mécaniques et magnétiques des couches de matériaux ferromagnétiques des matrices.Such matrices are subjected to the action of an external magnetization field (6) whose lines of force are perpendicular to the relief surfaces. Consequently, the ferromagnetic layers of the matrices magnetize and one of the poles is placed on the surfaces comprising a relief. On the other hand, one of the matrices has a distribution of the residual induction above the surface of the relief corresponding to the relation:
B1 (x, y, z) = B06 IhO (x, y, z) (3) and to the other:
B2 (x, y, z) = Bo where Bo is the induction of the magnetic field created,
ff 1 t y2 are coefficients characterizing the physico-mechanical and magnetic properties of the layers of ferromagnetic materials of the matrices.
Ces relations mettent en évidence également le fait que la répartition de l'induction rémanente au-dessus des surfaces des reliefs dépend de la valeur de l'induction magnétique créée par le champ magnetique, des profils des reliefs sur la surface des couches ferromagnétiques des matrices et des propriétés physico-mécaniques et magnétiques des couches de matériaux ferromagnétiques des matrices, notamment de l'induction de saturation, de la force coercitive, de la perméabilité magnétique, du procédé de production de la couche ferromagnétique, qui comprend les dimensions et l'orientation de-ses particules, l'homogénéité de sa composition, la densité du matériau, ainsi que les déformations qui surviennent en cours de fabrication. These relations also highlight the fact that the distribution of the residual induction above the relief surfaces depends on the value of the magnetic induction created by the magnetic field, on the relief profiles on the surface of the ferromagnetic layers of the matrices. and physico-mechanical and magnetic properties of the layers of ferromagnetic materials in the matrices, in particular the induction of saturation, the coercive force, the magnetic permeability, the process for producing the ferromagnetic layer, which includes the dimensions and orientation of its particles, the homogeneity of its composition, the density of the material, as well as the deformations which occur during manufacture.
L'aimantation des matrices est réalisées dans des champs magnétiques soit continus, soit alternatifs, ou dans une combinaison de tels champs. The magnetization of the matrices is carried out in magnetic fields either continuous or alternating, or in a combination of such fields.
Le procédé revendiqué pour le tirage d'un enregistrement magnétique par transfert d'informations à partir d'une matrice sur un porteur d'enregistrement permet de transformer celle-ci, dans un cas, en aimantation rémanente d'un porteur d'enregistrement magnétique, et dans un autre, en relief, par exemple, sur un porteur thermoplastique d'enregistrement. Lors du tirage sur un porteur d'enregistrement magnétique, on utilise des matrices exécutées en matériaux ferromagnétiques, à hystérésis, magnétiquement doux ou des matrices dont la couche de travail 5 à relief est exécutée en matériau ferromagnatique.Au cours du tirage sur un porteur thermoplastique, lorsque le relief de la matrice est transformé en-un relief sur ledit porteur d'enregistrement, on peut utiliser une matrice quelconque parmi celles réalisées selon le procédé revendi qué. The method claimed for drawing a magnetic recording by transfer of information from a matrix onto a recording carrier makes it possible to transform the latter, in one case, into the remanent magnetization of a magnetic recording carrier. , and in another, in relief, for example, on a thermoplastic recording carrier. When printing on a magnetic recording carrier, matrices executed in ferromagnetic, hysteresis, magnetically soft materials or matrices whose relief working layer 5 is executed in ferromagnetic material are used. During printing on a thermoplastic carrier , when the relief of the matrix is transformed into a relief on said recording carrier, one can use any matrix among those produced according to the claimed method.
Les copies obtenues sur un porteur d'enregistrement magnétique sont lues sur des magnétophones au moyen de têtes magnétiques, tandis que les copies obtenues sur un porteut thermoplastique d'enregistrement et possédant un relief sont lues, par exemple, selon un procédé optique. The copies obtained on a magnetic recording carrier are read on tape recorders by means of magnetic heads, while the copies obtained on a thermoplastic recording carrier and having a relief are read, for example, by an optical process.
Le procédé revendiqué de tirage d'un enregistrement magnétique par transfert des informations à partir d'une matrice sur un porteur d'enregistrement magnétique est mis en oeuvre de la façon suivante. The claimed method of drawing a magnetic recording by transferring information from a matrix onto a magnetic recording carrier is implemented as follows.
La matrice 10 (11) (figure 10) destinée au tirage d'un enregistrement magnétique constitué,par exemple, par une couche uniforme de matériau ferromagnétique magnétiquement doux, sur l'une des surfaces de laquelle il y a un relief correspondant à l'enregistrement magnétique, est serrée contre la surface de travail 1 du porteur d'enregistrement magnétique. Au moyen de l'electro-aimant 6, on crée un champ magnétique externe, perpendiculaire aux surfaces de travail de la matrice 10 (11) et du porteur (1', 2') d'enregistrement, puis on fait passer à travers ce champ la matrice 10 (11) avec le porteur d'information (1', 2'). The matrix 10 (11) (FIG. 10) intended for drawing a magnetic recording constituted, for example, by a uniform layer of magnetically soft ferromagnetic material, on one of the surfaces of which there is a relief corresponding to the magnetic recording, is pressed against the work surface 1 of the magnetic recording carrier. By means of the electromagnet 6, an external magnetic field is created, perpendicular to the working surfaces of the matrix 10 (11) and of the recording carrier (1 ′, 2 ′), then it is passed through this field the matrix 10 (11) with the information carrier (1 ', 2').
Le relief de la matrice 10 (11), sous l'action du champ magnétique externe, module le champ magnétique qui aimante la couche de travail 1 du porteur d'enregistrement. The relief of the matrix 10 (11), under the action of the external magnetic field, modulates the magnetic field which magnetizes the working layer 1 of the recording carrier.
Le champ magnétique externe peut être soit continu, soit alternatif, ou bien peut présenter une combinaison de tels champs. The external magnetic field can be either continuous or alternating, or can have a combination of such fields.
Le procédé revendiqué de tirage d'un enregistrement magnétique par transfert d'informations à partir d'une matrice sur un porteur d'enregistrement thermoplastique est mis en oeuvre de la façon suivante. The claimed method of drawing a magnetic recording by transferring information from a matrix onto a thermoplastic recording carrier is implemented as follows.
Le porteur d'enregistrement 1' (figure 11), par exemple un porteur d'enregistrement thermoplastique, est chauffé du côté de sa couche de travail denregistrement et est serré contre la matrice 10 (11) constituée, par exemple, par une couche de métal sur l'une des surfaces de laquelle il y a un relief correspondant à l'enregistrement magnétique, la matrice 10 (11) et le porteur (1', 2') d'enregistrement étant mis en contact par leurs surfaces de travail respectives, c'est-à-dire le relief et la couche d'enregistrement. Au cours de l'impression à l'état comprimé, on refroidit la matrice et le porteur (1', 2') d'enregistrement, l'impression de la couche de travail du porteur (1', 2') d'enregistrement étant réalisée par la surface possédant le relief. il reste sur la copie un relief correspondant. The recording carrier 1 ′ (FIG. 11), for example a thermoplastic recording carrier, is heated on the side of its recording working layer and is pressed against the matrix 10 (11) constituted, for example, by a layer of metal on one of the surfaces of which there is a relief corresponding to the magnetic recording, the matrix 10 (11) and the carrier (1 ′, 2 ′) of recording being brought into contact by their respective working surfaces , i.e. the relief and the recording layer. During printing in the compressed state, the matrix and the recording carrier (1 ', 2') are cooled, the printing of the working layer of the recording carrier (1 ', 2') being produced by the surface having the relief. there remains on the copy a corresponding relief.
Le procédé de tirage revendiqué transforme un type de présentation des informations: le relief de la matrice, en d'autres formes de presentation des informations, soit une aimantation d'un porteur d'enregistrement magnétique: une copie, soit un relief d'un porteur thermoplastique. The claimed printing process transforms a type of presentation of information: the relief of the matrix, into other forms of presentation of information, either a magnetization of a magnetic recording carrier: a copy, or a relief of a thermoplastic carrier.
Le procédé revendiqué de tran#sfert d'informations offre de larges possibilités pour le tirage de masse dans la technique des enregistrements vidéo et sonores, ce qui est particulièrement important pour la multiplication rapide et pour obtenir des copies à bas prix. Le procédé de tirage proposé présente des avantages particuliers dans la technique de calcul. The claimed method of transferring information offers wide possibilities for mass printing in the technique of video and sound recordings, which is particularly important for rapid multiplication and for obtaining copies at low cost. The proposed drawing process has particular advantages in the calculation technique.
Ainsi il devient possible de transformer l'aimantation d'un porteur magnétique portant des informations en un relief approprié d'une matrice et la transformation inverse des informations correspondant à un relief sur un porteur d'informations soit en un relief sur un porteur d'informations, soit en aimantation d'un porteur d'enregistrement magnétique. Thus it becomes possible to transform the magnetization of a magnetic carrier carrying information into an appropriate relief of a matrix and the reverse transformation of the information corresponding to a relief on an information carrier or into a relief on a carrier information, either by magnetization of a magnetic recording carrier.
Claims (16)