FI114701B - Förfarande och komposition för framställning av betongelement med en betydande tryckhållfasthet och brottstyrka och så erhållna element - Google Patents

Förfarande och komposition för framställning av betongelement med en betydande tryckhållfasthet och brottstyrka och så erhållna element Download PDF

Info

Publication number
FI114701B
FI114701B FI950914A FI950914A FI114701B FI 114701 B FI114701 B FI 114701B FI 950914 A FI950914 A FI 950914A FI 950914 A FI950914 A FI 950914A FI 114701 B FI114701 B FI 114701B
Authority
FI
Finland
Prior art keywords
concrete
microns
water
mpa
composition
Prior art date
Application number
FI950914A
Other languages
English (en)
Finnish (fi)
Other versions
FI950914A (sv
FI950914A0 (sv
Inventor
Pierre Emile Felix Richard
Marcel Hubert Cheyrezy
Jerome Antoine Dugat
Original Assignee
Lafarge Sa
Bouygues Travaux Publics Sa
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from FR9308062A external-priority patent/FR2707627B1/fr
Application filed by Lafarge Sa, Bouygues Travaux Publics Sa filed Critical Lafarge Sa
Publication of FI950914A publication Critical patent/FI950914A/sv
Publication of FI950914A0 publication Critical patent/FI950914A0/sv
Application granted granted Critical
Publication of FI114701B publication Critical patent/FI114701B/sv

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
    • C04B28/18—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing mixtures of the silica-lime type
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B40/00—Processes, in general, for influencing or modifying the properties of mortars, concrete or artificial stone compositions, e.g. their setting or hardening ability
    • C04B40/02—Selection of the hardening environment
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2201/00—Mortars, concrete or artificial stone characterised by specific physical values

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Ceramic Engineering (AREA)
  • Structural Engineering (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Health & Medical Sciences (AREA)
  • Toxicology (AREA)
  • Inorganic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Curing Cements, Concrete, And Artificial Stone (AREA)
  • Chemical Or Physical Treatment Of Fibers (AREA)
  • Powder Metallurgy (AREA)
  • Producing Shaped Articles From Materials (AREA)

Claims (13)

1. Förfarande för att producera betong, vars kom-pressionshällfasthet är minst 400 Mpa och brottenergi 5 minst 1000 J/m2, kännetecknat av att det omfattar sotn steg blandning av en komposition, som innehäller följande komponenter i följande förhällanden uttryckt i viktdelar (p) : (a) 100 p portlandcement; 10 (b) 30 - 100 p eller företrädesvis 40 - 70 p fin- fördelat stenmaterial, vars partikelstorlek är ätminstone 150 mikrometer; (c) 10 - 40 p eller företrädesvis 20 - 30 p amorf kiseldioxid, vars partikelstorlek är under 0,5 mikrometer; 15 (d) 20 - 60 p eller f öreträdesvis 30 - 50 p maid kvarts, vars partikelstorlek är under 10 mikrometer; (e) 25 - 100 p eller företrädesvis 45 - 80 p stäl- ull; (f) fluidiserande medel; 20 (g) eventuellt övriga tillsatsmedel; (h) 13 - 26 p eller f öreträdesvis 15 - 22 p vat- 1'·; ten; och efter att blandningen har bundits härdning av be- tongen vid en temperatur pa minst 250 °C under en till-räckligt läng tid för att omvandla cementens hydratation- ; .·. 25 sprodukter till kristallina hydrater av xonotlittyp för > * I I att eliminera nästan allt fritt vatten och ätminstone största delen av det absorberade och kemiskt bundna vatt-. net. • « t
2. Förfarande enligt patentkrav 1, känneteck- » · ;· 30 nat av att det finfördelade stenmaterialets partikel- ’· storlek är högst 800 mikrometer.
: 3. Förfarande enligt patentkrav 2, känneteck- > » » ·' nat av att det finfördelade stenmaterialets partikel- . storlek är mellan 150 och 400 mikrometer. ‘ * 35
4. Förfarande enligt ett av patentkraven 1 - 3, kännetecknat av att stälullen är stälspän, vilka 114701 14 malts till storleken 1-5 mm (storleken pä malapparatens skärnät).
5. Förfarande enligt ett av patentkraven 1 och 4, kännetecknat av att man använder rostfritt stälull. 5
6. Förfarande enligt patentkrav 5, känneteck nat av att nämnda komposition innehäller minst 0,6 p, företrädesvis minst 1,4 p av ett likvifaktionsmedel av dess vikt.
7. Förfarande enligt ett av patentkraven 1 - 6, 10 kännetecknat av att stenmaterialkompositionen dess- utom innehäller cylindriska och släta metalliibrer, vilkas längd är mellan 4 och 20 mm, företrädesvis mellan 10 och 14, och diameter är under cirka 500 mikrometer, företrädesvis mellan 100 och 200 mikrometer, varvid nämnda fib-15 rers volym är 1 - 4 %, företrädesvis 2 - 3 % av betongens volym efter härdning.
8. Förfarande enligt ett av patentkraven 1-7, kännetecknat av att nämnda komposition innehäller per väsentligen 100 viktdelar portlandcement: 50 p sand, 20 23 p kiseldioxid, 39 p kvarts, 2 p likvifaktionsmedel, 63 p stalull och 18 p vatten.
,!" 9. Förfarande enligt ett av patentkraven 1 - 8, kännetecknat av att betongen härdas vid en tempera-.* : tur pä minst 250 °C eller företrädesvis minst 400 °C vid ; 25 normaltryck och i normalfuktighet.
10. Förfarande enligt ett av patentkraven 1-9, f i 1 f kännetecknat av att färsk betong utsätts under bind-ningen för ett tryck pä minst 5 MPa eller företrädesvis minst 50 MPa. *;;; 30
11. Kompositioner för f ramställning av betong, • · kännetecknat av att de är säsom definierats i pa- i » » : tentkraven 1-8.
12. Betongelement, kännetecknat av att de är framställda med ett förfarande enligt ett av patentkraven " 35 1 - 10. » » » * * » » »
FI950914A 1993-07-01 1995-02-28 Förfarande och komposition för framställning av betongelement med en betydande tryckhållfasthet och brottstyrka och så erhållna element FI114701B (sv)