ES2167130A1 - Proceso de fabricacion de piezas metalicas a partir de polvos metalicos empleando resinas acrilicas termoestables como ligante. - Google Patents
Proceso de fabricacion de piezas metalicas a partir de polvos metalicos empleando resinas acrilicas termoestables como ligante.Info
- Publication number
- ES2167130A1 ES2167130A1 ES009802512A ES9802512A ES2167130A1 ES 2167130 A1 ES2167130 A1 ES 2167130A1 ES 009802512 A ES009802512 A ES 009802512A ES 9802512 A ES9802512 A ES 9802512A ES 2167130 A1 ES2167130 A1 ES 2167130A1
- Authority
- ES
- Spain
- Prior art keywords
- binder
- metallic
- manufacture
- acrylic resin
- thermostable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Proceso de fabricación de piezas metálicas a partir de polvos metálicos empleando resinas acrílicas termoestables como ligante. Se describe un proceso modificado de moldeo por inyección de metales (MIM), usando como ligante resinas acrílicas termoestables y como material cualquier metal o aleación susceptible de ser obtenido en forma de partículas o polvos. Este proceso consiste en varias etapas: (1) mezcla, (2) moldeo, (3) curado, (4) eliminación de ligante y (5) sinterización. El proceso de mezcla se realiza a temperatura ambiente y durante el moldeo se produce el curado de la resina a temperaturas moderadas. La eliminación del ligante se realiza en atmósfera de argón y aire, y la sinterización se lleva a cabo en atmósfera reductora ( vacío, hidrógeno o mezcla nitrógeno-hidrógeno). Las piezas obtenidas mediante este procedimiento presentan altas densidades y características equivalentes a las obtenidas por el proceso MIM convencional, lo que hace que este proceso de fabricación pueda competir en los sectores de la industria en los que se utiliza actualmente el proceso MIM convencional.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
ES9802512A ES2167130B1 (es) | 1998-11-30 | 1998-11-30 | Proceso de fabricacion de piezas metalicas a partir de polvos metalicos empleando resinas acrilicas termoestables como ligante. |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
ES9802512A ES2167130B1 (es) | 1998-11-30 | 1998-11-30 | Proceso de fabricacion de piezas metalicas a partir de polvos metalicos empleando resinas acrilicas termoestables como ligante. |
Publications (2)
Publication Number | Publication Date |
---|---|
ES2167130A1 true ES2167130A1 (es) | 2002-05-01 |
ES2167130B1 ES2167130B1 (es) | 2003-10-16 |
Family
ID=8305965
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
ES9802512A Expired - Fee Related ES2167130B1 (es) | 1998-11-30 | 1998-11-30 | Proceso de fabricacion de piezas metalicas a partir de polvos metalicos empleando resinas acrilicas termoestables como ligante. |
Country Status (1)
Country | Link |
---|---|
ES (1) | ES2167130B1 (es) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8940816B2 (en) | 2011-01-06 | 2015-01-27 | Commissariat A L'energie Atomique Et Aux Energies Alternatives | Master batch for ceramic- or metal-powder injection-molding, and method for preparing said master batch |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3989518A (en) * | 1975-05-08 | 1976-11-02 | United States Steel Corporation | Production of powder metallurgical parts by formation of sintered preforms in thermally degradable molds |
US4438004A (en) * | 1982-12-06 | 1984-03-20 | Raymark Industries, Inc. | Fused metallic friction materials |
US4795598A (en) * | 1986-12-05 | 1989-01-03 | Solid Micron Materials, Pte, Ltd. | Method of making articles from sinterable materials |
US4834800A (en) * | 1986-10-15 | 1989-05-30 | Hoeganaes Corporation | Iron-based powder mixtures |
ES2070336T3 (es) * | 1989-06-02 | 1995-06-01 | Gregory M Brasel | Metodo de moldeo de componentes a partir de mezclas de ligantes termoestables y polvos que tienen una composicion quimica deseada. |
US5840785A (en) * | 1996-04-05 | 1998-11-24 | Megamet Industries | Molding process feedstock using a copper triflate catalyst |
-
1998
- 1998-11-30 ES ES9802512A patent/ES2167130B1/es not_active Expired - Fee Related
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3989518A (en) * | 1975-05-08 | 1976-11-02 | United States Steel Corporation | Production of powder metallurgical parts by formation of sintered preforms in thermally degradable molds |
US4438004A (en) * | 1982-12-06 | 1984-03-20 | Raymark Industries, Inc. | Fused metallic friction materials |
US4834800A (en) * | 1986-10-15 | 1989-05-30 | Hoeganaes Corporation | Iron-based powder mixtures |
US4795598A (en) * | 1986-12-05 | 1989-01-03 | Solid Micron Materials, Pte, Ltd. | Method of making articles from sinterable materials |
ES2070336T3 (es) * | 1989-06-02 | 1995-06-01 | Gregory M Brasel | Metodo de moldeo de componentes a partir de mezclas de ligantes termoestables y polvos que tienen una composicion quimica deseada. |
US5840785A (en) * | 1996-04-05 | 1998-11-24 | Megamet Industries | Molding process feedstock using a copper triflate catalyst |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US8940816B2 (en) | 2011-01-06 | 2015-01-27 | Commissariat A L'energie Atomique Et Aux Energies Alternatives | Master batch for ceramic- or metal-powder injection-molding, and method for preparing said master batch |
Also Published As
Publication number | Publication date |
---|---|
ES2167130B1 (es) | 2003-10-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP1113893A1 (en) | Process for debinding and sintering metal injection molded parts made with an aqueous binder | |
DE50111650D1 (de) | Verfahren zur herstellung von verbundbauteilen durch pulver-spritzgiessen | |
KR100857944B1 (ko) | 고밀도 성형 부품의 제조를 위한 분말 야금 방법 | |
ATE217351T1 (de) | Verfahren und vorrichtung zur herstellung von metallischem eisen | |
EP1097770A4 (en) | METAL POWDER MOLDING MATERIAL AND RECOMPRESSED MOLDED BODY, SINTERED BODY OBTAINED FROM SAID RECOMPRESSED MOLDED BODY, AND PROCESSES FOR PRODUCING THE SAME | |
US4209478A (en) | Method of sintering ceramics | |
US4781874A (en) | Process for making silicon nitride articles | |
ES2167130A1 (es) | Proceso de fabricacion de piezas metalicas a partir de polvos metalicos empleando resinas acrilicas termoestables como ligante. | |
EP0523658A2 (en) | Method for making injection molded soft magnetic material | |
JPS5751231A (en) | Manufacture of ferromagnetic aluminum-base parts | |
JP2743090B2 (ja) | 金属射出品の炭素量コントロール方法 | |
EP0523651A2 (en) | Method for making high strength injection molded ferrous material | |
GR3019999T3 (en) | Powder metallurgy tool steel | |
AU2783195A (en) | Hi-density sintered alloy and spheroidization method for pre-alloyed powders | |
JPH0472004A (ja) | 多孔質金型の製造方法 | |
JPS5895658A (ja) | 窒化ケイ素焼結体の製造方法 | |
JP2001507667A (ja) | 成形用組成物および金属様外観を示すセラミック成形体の製法 | |
JPS6389462A (ja) | 窒化珪素質焼結体の製造方法 | |
Takekawa | Injection molding of stainless steel powders | |
JPS6462402A (en) | Production of spiral precision sintered part by injection molding method | |
KR960021299A (ko) | 탄소함량을 제어할 수 있는 금속사출성형법에 의한 소결체의 제조방법 | |
JP2840304B2 (ja) | 鍛造方法 | |
JPH0339402A (ja) | 金属粉末焼結体の製造方法 | |
JPH089721B2 (ja) | 粉末焼結品の製造方法 | |
Kimura et al. | Method of Producing Sintered Ceramic Body |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
FG2A | Definitive protection |
Ref document number: 2167130B1 Country of ref document: ES |
|
FD2A | Announcement of lapse in spain |
Effective date: 20190326 |