DE977422C - Gears with high core strength and impact strength - Google Patents

Gears with high core strength and impact strength

Info

Publication number
DE977422C
DE977422C DEG3279A DEG0003279A DE977422C DE 977422 C DE977422 C DE 977422C DE G3279 A DEG3279 A DE G3279A DE G0003279 A DEG0003279 A DE G0003279A DE 977422 C DE977422 C DE 977422C
Authority
DE
Germany
Prior art keywords
gears
strength
steel
impact strength
sel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DEG3279A
Other languages
German (de)
Inventor
August Dipl-Ing Dammer
Erich Dr-Ing Theis
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Gussstahlwerk Witten AG
Original Assignee
Gussstahlwerk Witten AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Gussstahlwerk Witten AG filed Critical Gussstahlwerk Witten AG
Priority to DEG3279A priority Critical patent/DE977422C/en
Application granted granted Critical
Publication of DE977422C publication Critical patent/DE977422C/en
Expired legal-status Critical Current

Description

Erteilt auf Grund des Ersten Oberleitungsgesetzes vom 8. Juli 1949Issued on the basis of the First Overhead Line Act of July 8, 1949

(WiGBl, S. 175)(WiGBl, p. 175)

BUNDESREPUBLIK DEUTSCHLANDFEDERAL REPUBLIC OF GERMANY

AUSGEGEBEN AM 26. MAI 1966ISSUED MAY 26, 1966

DEUTSCHES PATENTAMTGERMAN PATENT OFFICE

PATENTSCHRIFTPATENT LETTERING

KLASSE 40 b GRUPPE 39 26 INTERNAT. KLASSE C 22c CLASS 40 b GROUP 39 26 INTERNAT. CLASS C 22 c

G 32/p VI al40 bG 32 / p VI al40 b

. August Dammer und S)r.=3ttg. Erich Theis, Witten/Ruhr. August Dammer and S) r. = 3ttg. Erich Theis, Witten / Ruhr

sind als Erfinder genannt wordenhave been named as inventors

Gußstahlwerk Witten Aktiengesellschaft, Witten/RuhrCast steel works Witten Aktiengesellschaft, Witten / Ruhr

Zahnräder mit hoher Kernfestigkeit und SchlagzähigkeitGears with high core strength and impact resistance

Zusatz zum Patent 977 287Addendum to patent 977 287

Patentiert im Gebiet der Bundesrepublik Deutschland vom 15. August 1950 anPatented in the territory of the Federal Republic of Germany on August 15, 1950

Das Hauptpatent hat angefangen am 8. Dezember 1949The main patent started on December 8, 1949

Patentanmeldung bekanntgemacht am 24. Januar 1952Patent application published January 24, 1952

Patenterteilung bekanntgemadit am 5. Mai 1966Patent granted May 5, 1966

In dem Patent 977 287 sind nichtzementierte und ohne Verwendung eines Zyanbades gefertigte Zahnräder, insbesondere Getriebe- und Schalträder, mit hoher Schlagzähigkeit bei einer Härte von mindestens 58 Rockwell C geschützt, die aus einem Stahl mit etwaIn the '977,287 patent are non-cemented and fabricated without the use of a cyan bath Gears, especially gear and ratchet wheels, with high impact strength and hardness Protected by at least 58 Rockwell C, which is made of a steel with about

0,55 bis 0,70% Kohlenstoff,
0,20 bis 0,50% Silizium,
0,60 bis 1,00% Mangan,
0,90 bis 1,10% Chrom,
0,05 bis 0,20% Vanadin,
Rest technisches Eisen0.55 to 0.70% carbon,
0.20 to 0.50% silicon,
0.60 to 1.00% manganese,
0.90 to 1.10% chromium,
0.05 to 0.20% vanadium,
Remainder technical iron

bestehen und nach direkter Härtung auf Temperaturen von 150 bis 2400 C, vorzugsweise 180 bis 200° C angelassen sind. Die genannten Stähle können zusätzlich noch bis etwa 0,2 % Molybdän enthalten, und schließlich ist es möglich, den Stählen noch zusätzlich 0,3 % Blei zuzugeben, um die Bearbeitbarkeit zu verbessern.exist and are tempered to temperatures of 150 to 240 0 C, preferably 180 to 200 ° C after direct curing. The steels mentioned can also contain up to about 0.2% molybdenum, and finally it is possible to add 0.3% lead to the steels in order to improve the machinability.

Gegenstand der vorliegenden Erfindung sind nichtzementierte und ohne Verwendung eines Zyanbades gefertigte Zahnräder, insbesondere Getriebe- und Schalträder, mit hoher Schlagzähigkeit bei einer Härte von mindestens 58 Rockwell C, die aus einem im Hauptpatent genannten Stahl bestehen, der jedoch zusätzlich einen die Bearbeitbarkeit erleichternden Gehalt an Schwefel aufweist. Die Zahnräder werden in der gleichen Weise warm behandelt, wie es im Hauptpatent vorgesehen ist.The present invention relates to non-cemented and without the use of a cyan bath Manufactured gears, especially gear and ratchet wheels, with high impact strength a hardness of at least 58 Rockwell C, which consists of a steel named in the main patent, which, however, also has a sulfur content which makes it easier to process. The gears are heat treated in the same way as provided in the main patent.

Außer dem erhöhten Schwefelgehalt kann zusätzlich ein im Hauptpatent vorgesehener Gehalt an Blei vorhanden sein.In addition to the increased sulfur content, a content of Lead to be present.

Die Erleichterung der Bearbeitbarkeit ist bei den zu verwendenden Stählen von besonderer Bedeutung, weil es auf Grund der Zusammensetzung nicht möglich ist, diesen Stählen durch Glühung eine Weichheit zu verleihen, wie sie Einsatzstähle nach entsprechender Behandlung besitzen. Außer der leichteren Bearbeitbarkeit, insbesondere bei der Verzahnung der Zahnräder, werden bei den erfindungsgemäß zu verwendenden Stählen glatte Zahnflanken erzielt, so daß sich ein Nachschleifen vor dem Einbau erübrigt.The ease of machinability is of particular importance with the steels to be used, because due to their composition it is not possible to anneal these steels to give a softness, as they have case-hardened steels after appropriate treatment. Except the easier machinability, in particular with the toothing of the gears, are in accordance with the invention To be used steels achieved smooth tooth flanks, so that regrinding not necessary before installation.

Der Zusatz von Schwefel zu Stählen mit dem Zweck, die Bearbeitbarkeit zu verbessern, ist an sich bekannt. Die Erfindung betrifft daher nur die Anwendung dieser Maßnahme in Verbindung mit dem Gegenstand des Hauptpatentes.The addition of sulfur to steels with the purpose of improving machinability is on known. The invention therefore only relates to the use of this measure in connection with the subject of the main patent.

Claims (1)

PATENTANSPRUCH:PATENT CLAIM: Nichtzementierte und ohne Verwendung eines Zyanbades gefertigte Zahnräder, insbesondere Getriebe- und Schalträder, mit hoher Schlagzähigkeit bei einer Härte von mindestens 58 Rockwell C, dadurch gekennzeichnet, daß sie aus einem Stahl mit etwaUncemented gears made without the use of a cyan bath, in particular Gear and ratchet wheels, with high impact strength and a hardness of at least 58 Rockwell C, characterized in that they from a steel with about 0,55 bis 0,70% Kohlenstoff,
0,20 bis 0,50% Silizium,
0,60 bis 1,00% Mangan,
0,90 bis 1,10% Chrom,
0,05 bis 0,20% Vanadin,0.55 to 0.70% carbon,
0.20 to 0.50% silicon,
0.60 to 1.00% manganese,
0.90 to 1.10% chromium,
0.05 to 0.20% vanadium, ο bis etwa 0,2 % Molybdän,ο up to about 0.2% molybdenum, ο bis etwa 0,3 % Bleiο up to about 0.3% lead und einem die Bearbeitbarkeit erleichternden Gehalt an Schwefel, Rest technisches Eisen, bestehen und nach direkter Härtung auf Temperaturen von 150 bis 2400 C, vorzugsweise 180 bis 2oo° C, angelassen sind (Zusatz zum Patent 977 287). . and a workability facilitating content of sulfur, the remainder being iron technical exist and to direct curing at temperatures of 150 to 240 0 C, preferably 180 to 2oo ° C, annealed (additional patent 977,287). . In Betracht gezogene Druckschriften:
Französische Patentschrift Nr. 839 239;
Stahleisenliste (SEL III, 23 und 1. Nachtrag,Considered publications:
French Patent No. 839,239;
Steel list (SEL III, 23 and 1st addendum, Februar 1949, SEL III, 16);February 1949, SEL III, 16); Werkstoffhandbuch Stahl und Eisen, 2. Auflage,Material handbook steel and iron, 2nd edition, S. G 10-6.S. G 10-6. © 609 582/13 5.66 © 609 582/13 5.66
DEG3279A 1950-08-15 1950-08-15 Gears with high core strength and impact strength Expired DE977422C (en)