DE932828C - Welding and brazing agents - Google Patents

Welding and brazing agents

Info

Publication number
DE932828C
DE932828C DEG8497A DEG0008497A DE932828C DE 932828 C DE932828 C DE 932828C DE G8497 A DEG8497 A DE G8497A DE G0008497 A DEG0008497 A DE G0008497A DE 932828 C DE932828 C DE 932828C
Authority
DE
Germany
Prior art keywords
welding
brazing
brazing agents
percent
agents
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DEG8497A
Other languages
German (de)
Inventor
Georg Geuter
Fanny Kramer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Geuter & Kramer
Original Assignee
Geuter & Kramer
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Geuter & Kramer filed Critical Geuter & Kramer
Priority to DEG8497A priority Critical patent/DE932828C/en
Application granted granted Critical
Publication of DE932828C publication Critical patent/DE932828C/en
Expired legal-status Critical Current

Description

Schweiß- und Hartlötmittel Die Erfindung betrifft ein Schweiß- und Hartlötmittel. Das Mittel zeichnet sich vor allem dadurch aus, daß man mit ein und demselben Mittel sämtliche Guß-, Metall- und Stahlarten (auch besonders harte Stähle) schweißen und hartlöten kann. Hierfür benötigte man bisher verschiedene Flußmittel.Welding and brazing agents The invention relates to welding and Brazing agent. The main feature of the remedy is that you can use a and all types of cast iron, metal and steel (including particularly hard steels) can weld and braze. Various fluxes have been required for this up to now.

Das Schweiß- und Hartlötmittel besteht aus folgenden Bestandteilen: 8,2 Gewichtsprozent Alaun, 6,2 Gewichtsprozent Ammon. Chlorid, o,6 Gewichtsprozent Kupfersulfat, 0,3 Gewichtsprozent Borsäure, 84,7 Gewichtsprozent Borax.The welding and brazing agent consists of the following components: 8.2 percent by weight alum, 6.2 percent by weight ammonium. Chloride, 0.6 percent by weight copper sulfate, 0.3 percent by weight boric acid, 84.7 percent by weight borax.

Die Vorteile gegenüber anderen Mitteln sind höhere Festigkeitswerte, glattere Schweißnähte. Die Arbeiten werden bohr- und feilweich, porenfrei und haben ein feineres Gefüge.The advantages over other means are higher strength values, smoother welds. The work will be boring and filing soft, pore-free and have a finer structure.

Beim Arbeiten mit diesem Mittel entstehen keine gesundheitsschädlichen Dämpfe. Es bewirkt einen schnelleren Fluß, wodurch eine Einsparung von etwa 30°/o am üblichen Gas- und Sauerstoffverbrauch erzielt wird.When working with this product, there are no harmful substances Fumes. It causes a faster flow, which results in a saving of about 30 per cent is achieved on the usual gas and oxygen consumption.

Claims (1)

PATENTANSPRUCH: Schweiß- und Hartlötmittel, dadurch gekennzeichnet, daß es aus 8,2 % Alaun, 6,2 % Ammon. Chlorid, o,6 % Kupfersulfat; 0,3 % Borsäure und 84,7 % Borax besteht.PATENT CLAIM: Welding and brazing agents, characterized in that that it consists of 8.2% alum, 6.2% ammon. Chloride, 0.6% copper sulfate; 0.3% boric acid and 84.7% is borax.
DEG8497A 1952-06-22 1952-06-22 Welding and brazing agents Expired DE932828C (en)