DE9321219U1 - Semi-finished products, namely building boards - Google Patents

Semi-finished products, namely building boards

Info

Publication number
DE9321219U1
DE9321219U1 DE9321219U DE9321219U DE9321219U1 DE 9321219 U1 DE9321219 U1 DE 9321219U1 DE 9321219 U DE9321219 U DE 9321219U DE 9321219 U DE9321219 U DE 9321219U DE 9321219 U1 DE9321219 U1 DE 9321219U1
Authority
DE
Germany
Prior art keywords
mortar
semi
core
finished product
product according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE9321219U
Other languages
German (de)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from DE19924234269 external-priority patent/DE4234269C1/en
Priority claimed from DE9313351U external-priority patent/DE9313351U1/en
Application filed by Individual filed Critical Individual
Priority to DE9321219U priority Critical patent/DE9321219U1/en
Priority claimed from EP93924031A external-priority patent/EP0625088B1/en
Publication of DE9321219U1 publication Critical patent/DE9321219U1/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

• ··

(WEG3IATl)(WEG3IATl)

Halbzeug, nämlich BauplatteSemi-finished product, namely building board

Die Erfindung betrifft ein Halbzeug, nämlich eine Bauplatte. The invention relates to a semi-finished product, namely a building board.

Aus der DE 34 23 00 6 C2 ist eine Bauplatte bekannt, bei der zunächst auf ein Schaumstoffteil ein Gewebe oder Geflecht stramm aufgespannt wird und anschließend wasserbeständiger Dünnbettmörtel aufgegeben und glattgestrichen wird, so daß das Gewebe oder Geflecht fest verklebt wird.From DE 34 23 00 6 C2 a building board is known in which a fabric or mesh is first stretched tightly over a foam part and then water-resistant thin-bed mortar is applied and smoothed out so that the fabric or mesh is firmly bonded.

Nachteilig ist, daß das Gewebe oder Geflecht beim Aufbringen aufzuspannen ist. Hierdurch können zwischen dem Schaumstoffteil und dem Gewebe oder Geflecht Kräfte auftreten, die zu einer Verformung des Schaumstoffteils bzw. zu einer Ablösung des Gewebes oder Geflechtes von diesem führen. Nachteilig ist darüber hinaus, daß durch das Einzelbespannen und Einzelbestreichen mit Mörtel jedes Teil sehr aufwendig in der Herstellung und eine kontinuierliche Fertigung von Platten nicht möglich ist.The disadvantage is that the fabric or mesh has to be stretched when it is applied. This can cause forces to arise between the foam part and the fabric or mesh, which can lead to the foam part deforming or the fabric or mesh coming off. Another disadvantage is that the individual covering and individual coating of mortar on each part makes it very complex to manufacture and continuous production of panels is not possible.

Aus der AT-PS 242 581 ist eine Bauplatte bekannt, bei der horizontal aufgelegte und geförderte Schaumstoffkerne zunächst mit einer ersten teigigen Mörtelschicht versehen werden, die mit einer schwingenden Walze verdichtet wird. Hinter der Verdichtungswalze wird von einerA building board is known from AT-PS 242 581, in which horizontally placed and conveyed foam cores are first provided with a doughy layer of mortar, which is compacted with a vibrating roller. Behind the compaction roller, a

Vorratsrolle eine Glasfasergewebebahn abgezogen, auf die Mörtelschichtoberseite aufgedrückt und von der laufenden Bahn mitgenommen. An einer weiteren, nachgeschaltetenA glass fibre fabric strip is pulled off a supply roll, pressed onto the top of the mortar layer and carried along by the moving strip. At another, downstream

Station wird auf die erste Deckschicht und die Glasfaser-5 Station is placed on the first cover layer and the fiberglass-5

gewebebahn eine weitere Mörtelschicht locker aufgebracht und mit einer zweiten schwingenden Walze verdichtet.Another layer of mortar is loosely applied to the fabric and compacted with a second vibrating roller.

Bauplatten, die nach dem Verfahren gemäß AT-PS 242 581 hergestellt werden, weisen auf dem Schaumstoffkern Deckschichten auf, deren Dicke zusammengenommen die Dicke der Armierung weit überschreitet. Die so hergestellten Bauplatten sind daher schwer im Gewicht und für Innenausbauten, insbesondere zur Herstellung von mit Fliesen zu belegenden Trennwänden, schlecht geeignet. Soweit be-Building boards manufactured using the process according to AT-PS 242 581 have covering layers on the foam core, the combined thickness of which far exceeds the thickness of the reinforcement. The building boards manufactured in this way are therefore heavy and poorly suited for interior fittings, in particular for the manufacture of partition walls to be covered with tiles.

kannt, werden die nach AT-PS 242 581 hergestellten Platten daher in erster Linie als Flachdach- und Fassadenpalatten verwendet. Mit anderen Worten: Für das Einbetten und Verkleben der Glasfasergewebebahn wird wesentlich zu viel Mörtel verwendet, gemessen am Bedarf für Innenaus-known, the panels manufactured according to AT-PS 242 581 are therefore primarily used as flat roof and facade panels. In other words: For embedding and bonding the glass fiber fabric, far too much mortar is used compared to the amount required for interior work.

bauplatten.building boards.

Weiterhin ist eine Bauplatte aus der GB-PS 1 459 575 bekannt. Nach dieser Schrift wird auf ein sich gleichmäßig vorwärts bewegendes Förderband ein Material für eine erste Anlage aus einem Mischer geschüttet und danach mit einer Schaufel auf eine bestimmte Stärke verteilt. In gleicher Art und Weise werden eine Dichtungslage und eine weitere Außenlage darüber angeordnet. Nachteilig ist, daß die Stärke jeder einzelnen Lage von der Bandge- ° schwindigkeit und der genauen Arbeit des Personals bestimmt wird.A building board is also known from GB-PS 1 459 575. According to this document, a material for a first system is poured from a mixer onto a conveyor belt that moves forward at a constant speed and is then spread out to a certain thickness using a shovel. A sealing layer and another outer layer are placed on top in the same way. The disadvantage is that the thickness of each individual layer is determined by the speed of the belt and the precise work of the staff.

Ein Verfahren zur Herstellung eines plattenförmigen Bauteils mit Kern wird weiterhin in der DE 31 36 935 Cl ° beschrieben. Der Kern besteht aus im wesentlichen parallel nebeneinander liegenden und zu Schichten angeordneten Mineralfasern, die in einem Winkel zwischen 10 bisA method for producing a plate-shaped component with a core is also described in DE 31 36 935 Cl °. The core consists of mineral fibers lying essentially parallel to one another and arranged in layers, which are arranged at an angle of between 10 and

60° zur Bahn- oder Plattenebene verlaufen. Auf einer Seite der geschichteten Mineralfasern wird eine Aluminium- oder Kunststoffolie angeordnet, auf der ein Putz aus einem nicht brennbaren mineralischen Material aufgebracht wird.60° to the plane of the sheet or panel. An aluminum or plastic foil is placed on one side of the layered mineral fibers, onto which a plaster made of a non-combustible mineral material is applied.

Nachteilig ist, daß die Platte instabil ist und sich lediglich zum Umwickeln von Rohrleitungen oder Abdeckungen von ebenen geraden Flächen eignet.
10
The disadvantage is that the plate is unstable and is only suitable for wrapping around pipes or covering flat, straight surfaces.
10

Eine Bauplatte ist auch aus der DE 34 44 881 C2 bekannt. Der Kern dieser Bauplatte besteht aus einer Mineralfaserplatte, welche beispielsweise aus Stapelfasern von Glaswolle bzw. Glasseide hergestellt sein kann. Diese Mineralfaserplatte wird vor der Herstellung des Bauteils mehr oder minder stark verdichtet und daher auf einen Bruchteil der Plattendicke verringert. An beiden Plattenseiten wird eine Schicht aufgetragen, die aus Mörtelmix besteht. In diesen Mörtelmix sind Glasfasern eingebettet. Aufgrund der relativ geringen Festigkeit eignet sich darüber hinaus diese Bauplatte lediglich für ein Verkleiden stabiler Wände aus Beton.A building board is also known from DE 34 44 881 C2. The core of this building board consists of a mineral fiber board, which can be made from staple fibers of glass wool or glass silk, for example. This mineral fiber board is more or less compressed before the component is manufactured and is therefore reduced to a fraction of the board thickness. A layer consisting of a mortar mix is applied to both sides of the board. Glass fibers are embedded in this mortar mix. Due to its relatively low strength, this building board is only suitable for cladding stable concrete walls.

Der Erfindung liegt die Aufgabe zugrunde, ein Halbzeug, nämlich eine Bauplatte mit guten schalldämmenden, wärmedämmenden und/oder mechanischen Eigenschaften bei relativ geringem Gewicht zu schaffen, bei dem ein geringer Materialverbrauch zu einer ebenmäßigen Platte führt.The invention is based on the object of creating a semi-finished product, namely a building board with good sound-insulating, heat-insulating and/or mechanical properties at a relatively low weight, in which a low material consumption leads to a uniform board.

Gemäß der Erfindung wird ein Halbzeug, nämlich eine Bauplatte vorgeschlagen, wie es aus Anspruch 1 hervorgeht.According to the invention, a semi-finished product, namely a building board, is proposed as it appears from claim 1.

Die mit der Erfindung erzielten Vorteile bestehen insbesondere darin, daß die Kernbahn aus einem Gummi-Kreppkern ist. Dadurch, daß in den noch feuchten, vorzugsweise durch Aufgießen auf den Gummi-Kreppkern aufgebrachten Mörtel das Glasfasergewebe mit der gleichen Geschwindig-The advantages achieved with the invention are in particular that the core sheet is made of a rubber crepe core. As a result of the fact that the glass fiber fabric is pressed into the still moist mortar, preferably by pouring it onto the rubber crepe core, at the same speed

keit wie die Transportbewegung der endlosen Kernbahn aufgebracht wird, kommt es zu keinerlei inneren Spannungen und dadurch zu keinem Verziehen der Platten. Nach dem Aushärten steht somit eine Bauplatte zur Verfügung, die sich durch eine hohe Festigkeit und gute wärme- und schallisolierende Eigenschaften auszeichnet, die nicht nur zum Aufbringen von Verkleidungen, sondern auch als Wandteil verwendbar ist und so verputzt, tapeziert oder gefliest werden kann.ity such as the transport movement of the endless core track, there are no internal tensions and therefore no warping of the panels. After curing, a building board is available that is characterized by high strength and good heat and sound insulating properties, which can be used not only for applying cladding, but also as a wall part and can therefore be plastered, wallpapered or tiled.

Von besonderem Vorteil ist hierbei, daß auf die glatte Fläche der Kernbahn eine armierte Mörtelschicht aufgebracht ist, so daß plattenförmige Bauteile entstehen, die sich besonders gut im Baugewerbe eignen. Die aus den Bauplatten hergestellten Trennwände haben eine solche Stabilität, daß Fliesen, Beschläge und Armaturen anbringbar sind.A particular advantage here is that a reinforced mortar layer is applied to the smooth surface of the core sheet, so that panel-shaped components are created that are particularly suitable for the construction industry. The partition walls made from the building panels are so stable that tiles, fittings and fixtures can be attached.

Wesentlich ist, daß auf der einen Seite die Mörtel-It is essential that on the one hand the mortar

schicht aufgrund der Konsistenz des flüssig aufgebrachten, ausgehärteten Mörtels ausgesprochen stabil ist, zum anderen aber diese Schicht auch sehr dünn sein kann. Es hat sich dabei als vorteilhaft erwiesen, wenn die Konsistenz des flüssig aufgebrachten Mörtels nach DIN 1060layer is extremely stable due to the consistency of the liquid, hardened mortar, but on the other hand this layer can also be very thin. It has proven to be advantageous if the consistency of the liquid mortar complies with DIN 1060

{Messung der Ausbreitung mit Wickertbecher) eine Ausbreitung von 22 - 28 cm ergibt.{Measurement of the spread with Wickert cup) results in a spread of 22 - 28 cm.

Dabei ist vorteilhaft, daß der flüssig aufzubringende Mörtel über zwei eng benachbart stehende, drehende WaI-It is advantageous that the liquid mortar is applied over two closely spaced, rotating rollers.

zen, die sich vorzugsweise gleichsinnig drehen, auf die Kernbahn läuft. Durch die Walzen läßt sich einmal die Homogenität des Mörtels immer wieder aufrechterhalten, so daß es nicht zu Aushärtungen vor dem Aufbringen kommt. Zum anderen ist durch die Drehgeschwindigkeit oder die Abstandsstellung der Walzen eine Feindosierung des Mörtelzulaufs unter Regelung möglich.zen, which preferably rotate in the same direction, run onto the core track. The rollers allow the homogeneity of the mortar to be maintained over and over again, so that it does not harden before it is applied. On the other hand, the rotation speed or the spacing of the rollers allows for fine dosing of the mortar flow under control.

Vorteilhaft ist weiterhin, die Gummi-Kreppbahn aus Fasern, Schnitzeln, Streifen oder Teilstücken aus Altgummi oder Kautschuk zu verdichten. Hierdurch ist es möglich, eine Kernbahn zu schaffen, die bereits im wesentlichen über die äußeren Abmessungen der späteren Bauplatte verfügt und darüberhinaus eine solche Festigkeit hat, daß sie statischen und/oder dynamischen Belastungen ausgesetzt werden kann, wie sie für den vorgenannten Verwendungszweck zu erwarten sind.It is also advantageous to compact the rubber crepe sheet from fibers, chips, strips or pieces of old rubber or caoutchouc. This makes it possible to create a core sheet that already has essentially the external dimensions of the later building board and, in addition, has such strength that it can be exposed to static and/or dynamic loads as can be expected for the aforementioned intended use.

Mit Vorteil kann die armierte Mörtelschicht sehr dünn gewählt werden, beispielsweise bis auf 0,2 mm heruntergefahren werden. Nach oben sind im wesentlichen keine Grenzen gesetzt.The reinforced mortar layer can advantageously be made very thin, for example down to 0.2 mm. There are essentially no upper limits.

Um ein lockeres, aber gleichmäßiges Einlegen der Bahn aus Glasfasergewebe zu ermöglichen, ist diese über einen Bahnspeicher geführt.In order to enable the web of glass fibre fabric to be laid loosely but evenly, it is guided through a web storage system.

Es sei hier angemerkt, daß der Begriff "Glasfasergewebe"It should be noted here that the term "glass fibre fabric"

lediglich zur Vereinfachung der Beschreibung gewählt worden ist. Es können beispielsweise auch Glasfaservliese oder andere Glasfaser-Non-Woven-Materialien verwendet werden. Es sei aber auch nicht ausgeschlossen, daß beispielsweise Aramidgewebe, Polyester-Vliese oder dergleichen eingesetzt werden, wenn sie die erforderlichen Bewehrungseigenschaften erbringen. Möglich ist auch, dünne Schichten als Metallgeweben, z.B. aus Kupfer, oder oberflächenveredelten Eisengeweben einzusetzen. 30has only been chosen to simplify the description. For example, glass fiber fleece or other glass fiber non-woven materials can also be used. However, it is also not excluded that, for example, aramid fabric, polyester fleece or the like can be used if they provide the required reinforcement properties. It is also possible to use thin layers of metal fabric, e.g. made of copper, or surface-treated iron fabric. 30

In der Zeichnung ist ein Ausführungsbeispiel dargestellt. Es zeigen in schematischer DarstellungThe drawing shows an embodiment. It shows a schematic representation

Fig. 1 eine Bauplatte mit einem Gummi-Kreppkern in einer ° Schnittdarstellung undFig. 1 a building board with a rubber crepe core in a ° sectional view and

Fig. 2 eine Vorrichtung zur Herstellung einer Bauplatte aus einem Gummi-Kreppkern.Fig. 2 shows a device for producing a building board from a rubber crepe core.

Eine in Fig. 1 gezeigte Bauplatte besteht aus einem Kern 5A building board shown in Fig. 1 consists of a core 5

2 aus Altgummifasern 22 und Kautschukfasern 22'. Eine Möglichkeit zur Herstellung eines Gummi-Kreppkerns, im folgenden als Kernbahn 2 bezeichnet, besteht darin, daß die Altgummi- 22 oder Kautschukfasern 22' bahnförmig geformt werden, wobei eine Verdichtung der Fasern 22 bzw. 22' unter Formung einer Schicht vorgenommen werden kann, die entweder wasserdurch- oder wasserundurchlässig ist. Die Fasern 22 bzw. 22' werden aus zerkleinertem Kautschuk oder Altgummi hergestellt. Das Formen geschieht in der Art, daß die gehäckselten Fasern 22 bzw. 22' mit2 from waste rubber fibers 22 and rubber fibers 22'. One possibility for producing a rubber crepe core, hereinafter referred to as core web 2, is that the waste rubber 22 or rubber fibers 22' are formed into a web, whereby the fibers 22 or 22' can be compressed to form a layer that is either water-permeable or water-impermeable. The fibers 22 or 22' are made from chopped rubber or waste rubber. The forming takes place in such a way that the chopped fibers 22 or 22' are

einer sie verbindenden Masse, z. B. flüssigem Kautschuk oder durch Druck- oder Temperatureinwirkungen zu einer Kernbahn 2 geformt werden. Diese weist Fasern 22 bzw. 22' unterschiedlicher Länge und Breite auf, die unter Einschluß von Luft in die gewünschte Form gebracht wer-a mass that connects them, e.g. liquid rubber, or by pressure or temperature effects to form a core web 2. This has fibers 22 or 22' of different lengths and widths, which are brought into the desired shape by including air.

den. Die Fasern 22 bzw. 22' umschließen bei ihrem Zusammenfügen zu einer Kernbahn Luft in einem prozentualen Anteil zwischen 10 bis 60 % ein. Durch den Abstand der einzelnen Fasern 22 bzw. 22' und die eingeschlossene Luft wird das Dämmverhalten der Kernbahn 2 bestimmt. Auch wenn die Kernbahn 2 über im wesentlichen glatte Außenflächen verfügt, weisen diese jedoch Krepp-Vertiefungen zwischen den einzelnen Fasern auf.When the fibers 22 and 22' are joined together to form a core sheet, they enclose air in a percentage of between 10 and 60%. The insulation behavior of the core sheet 2 is determined by the distance between the individual fibers 22 and 22' and the enclosed air. Even if the core sheet 2 has essentially smooth outer surfaces, these have crepe depressions between the individual fibers.

Um das Kernelement 2 ist zu beiden Seiten jeweils eineAround the core element 2 there is a

armierte Mörtelschicht 9' aufgebaut, bei der ein Glasfasergewebe oder -vlies 7 in der Mörtelschicht liegt. Das Beschichten der Kernbahn 2 wird mit einer Vorrichtung gemäß Fig. 2 vorgenommen. Hierbei wird die Kernbahn 2 auf eine angetriebene Rollenbahn 1 gelegt. Die endlose Bahn kann entweder platten- oder abschnittsweise herangeführt werden.reinforced mortar layer 9' is constructed, in which a glass fiber fabric or fleece 7 is placed in the mortar layer. The coating of the core web 2 is carried out using a device according to Fig. 2. The core web 2 is placed on a driven roller conveyor 1. The endless web can be fed in either in panels or in sections.

Eine Kernbahn 2 wird auf eine angegetriebene Rollenbahn gelegt. Hierbei kann die endlose Bahn entweder platten- oder abschnittsweise herangeführt werden. Ein Mörtelsilo 3 ist in einiger Entfernung von einem Mörtelsieb 4 angebracht. Zwischen dem Mörtelsieb 4 und Oberfläche der Kernbahn 2 ist eine Dosiervorrichtung 5 vorgesehen. Die Dosiervorrichtung 5 besteht aus zwei eng benachbarten, jedoch sich nicht kontaktierenden Walzen 105 und 106, die im gleichen Drehsinn rotieren. Die Walzen 105 und 106 sind mit flüssigkeitsabweisendem Gummi der Shore-Härte W 1357 beschichtet, haben einen Durchmesser von etwa 200 mm und sind synchron über einen drehzahlsteuerbaren Elektromotor angetrieben.A core web 2 is placed on a driven roller conveyor. The endless web can be fed in either in panels or in sections. A mortar silo 3 is installed at some distance from a mortar sieve 4. A metering device 5 is provided between the mortar sieve 4 and the surface of the core web 2. The metering device 5 consists of two closely spaced but non-contacting rollers 105 and 106, which rotate in the same direction. The rollers 105 and 106 are coated with liquid-repellent rubber with a Shore hardness of W 1357, have a diameter of approximately 200 mm and are driven synchronously by a speed-controlled electric motor.

Die Viskosität des aus dem Vorratsbehälter 3 durch ein Sieb der Walzenanordnung fließenden Mörtels ist sehr wichtig. Es handelt sich um einen Dünnbettmörtel auf Zementbasis mit Kunststoffanteilen, wobei letztere die Elastizität des ausgehärteten Mörtels verbessern. Der Mör-The viscosity of the mortar flowing from the storage container 3 through a sieve of the roller arrangement is very important. It is a thin-bed mortar based on cement with plastic components, the latter improving the elasticity of the hardened mortar. The mortar

tel ist außerdem mit Füllstoffen versehen, die seinetel is also provided with fillers that increase its

exakt einzuhaltenden Thixotropie-Eigenschaften verbessern. Hierzu eigenen sich beispielsweise Quarzmehl oder Kreide. Die einzelnen Rezepturen werden je nach Anforderungen von spezialisierten Firmen hergestellt. 25improve the thixotropic properties that must be precisely maintained. Quartz powder or chalk are suitable for this purpose. The individual recipes are manufactured by specialised companies depending on the requirements. 25

Das Ausbreitungsmaß des Mörtels wird in einem frustrokonischen Wickertring (oberer freier Durchmesser 79 mm, unterer 65 mm bei 40 mm Höhe) nach DIN 1060 (EN 196) auf einem Hegemann-Tisch gemessen. Dabei soll der Durchmes-The extent of mortar expansion is measured in a frustro-conical Wickert ring (upper free diameter 79 mm, lower 65 mm at 40 mm height) according to DIN 1060 (EN 196) on a Hegemann table. The diameter

ser des Ausbreitungskuchens zwischen 22 und 28 cm, vorzugsweise zwischen 23 und 27 cm betragen. Die sämige Konsistenz des Mörtels wird durch die Walzenbewegung der Walzen 105 und 106 homogenisiert bzw. erhalten. Durch den Spalt zwischen den Walzen läuft der Mörtel auf die Kernbahn 2 und wird durch einen Abstreifer 6, der dem Walzenpaar nachgeschaltet ist, auf der Oberfläche der Kernbahn verteilt.The thickness of the spreading cake should be between 22 and 28 cm, preferably between 23 and 27 cm. The creamy consistency of the mortar is homogenized or maintained by the rolling movement of the rollers 105 and 106. The mortar runs through the gap between the rollers onto the core web 2 and is distributed on the surface of the core web by a scraper 6, which is arranged downstream of the pair of rollers.

Nach dem Abstreifer 6 wird im weiteren Verlauf eine endlose Bahn aus Glasfasergewebe oder -vlies 7 in praktisch spannungslosem Zustand, d. h. im wesentlichen aufgrund des Eigengewichtes, und unter gleicher Geschwindigkeit wie die Transportgeschwindigkeit der Kernbahn 2, herangeführt. Auf einer Vorratsrolle 18 befindet sich ein Vorrat an Glasfasergewebe 7, der über einen Bahnspeicher geführt wird, wie er aus der Textiltechnik an sich bekannt ist. Die Bahn aus Glasfasergewebe oder -vlies 7 wird durch eine Andrückvorrichtung 8 auf eine geringe Höhe (ca. 2 mm) über der Bahn 2 geführt und dabei etwas in die Mörtelschicht 9 eingedrückt und eingebettet. Dabei dringt der Mörtel sowohl unter das Glasfasergewebe als auch in den Raum zwischen den einzelnen Maschen des Gewebes. Eine hohe Klebkraft wird damit gewährleistet, da der Abstand der Glasfasergewebeschicht so bestimmt ist, daß gerade noch eine Klebeschicht zwischen dem Glasfasergewebe und der Oberfläche der Kernbahn aufrechterhalten bleibt.After the stripper 6, an endless web of glass fiber fabric or fleece 7 is fed in a practically tension-free state, i.e. essentially due to its own weight, and at the same speed as the transport speed of the core web 2. A supply roll 18 contains a supply of glass fiber fabric 7, which is fed through a web storage device, as is known from textile technology. The web of glass fiber fabric or fleece 7 is fed to a low height (approx. 2 mm) above the web 2 by a pressing device 8 and is pressed slightly into the mortar layer 9 and embedded. The mortar penetrates both under the glass fiber fabric and into the space between the individual meshes of the fabric. A high adhesive strength is thus ensured, since the distance of the glass fiber fabric layer is determined in such a way that an adhesive layer is just maintained between the glass fiber fabric and the surface of the core web.

Durch einen weiteren Abstreifer 10 wird der überschüssige Mörtel oberhalb des Glasfasergewebes abgestreift und in einer solchen Schicht verteilt, daß diese die Bahn aus Glasfasergewebe oder -vlies 7 sowohl einbettet als auch leicht überragt, so daß die Bahn anschließend eine Armierung im noch feuchten Mörtel 9 bildet, die jedoch über eine nur dünne Mörtelschicht die Oberfläche der Bahn kontaktiert. Der sich vor dem Abstreifer 10 bilden- ou de Mörtelschwall 11 bildet als vordere Begrenzung eine Lippe 12, die mit Hilfe eines opto-elektronischen oder kapazitiven Fühlers 13 abgetastet wird.A further scraper 10 scrapes off the excess mortar above the glass fiber fabric and distributes it in such a layer that it both embeds the sheet of glass fiber fabric or fleece 7 and also slightly protrudes over it, so that the sheet then forms a reinforcement in the still wet mortar 9, which, however, only contacts the surface of the sheet via a thin layer of mortar. The mortar surge 11 that forms in front of the scraper 10 forms a lip 12 as a front boundary, which is sensed using an opto-electronic or capacitive sensor 13.

Erreicht die Lippe eine Stellung, die zu weit entfernt 3^ ist von dem Abstreifer 10, so wird das Fühlersignal vom Fühler 13 durch die Datenverarbeitungsanlage 14 so ausgelegt, daß die Dosiervorrichtung 5 weiter geschlossenIf the lip reaches a position that is too far away from the scraper 10, the sensor signal from the sensor 13 is interpreted by the data processing system 14 in such a way that the dosing device 5 is closed further .

♦ «♦ «

wird, indem die Walzengeschwindigkeit gedrosselt wird, so daß die zeitlich ausströmende Mörtelmenge abnimmt.by reducing the roller speed so that the amount of mortar flowing out over time decreases.

Weicht die Lippe 12 zurück in Richtung Abstreifer 10, so 5If the lip 12 moves back towards the scraper 10, 5

läßt die EDV-Signalverarbeitung die Drehgeschwindigkeit der beiden Walzen 105 und 106 erhöhen, so daß eine größere Mörtelmenge freigegeben wird.The computer signal processing increases the rotational speed of the two rollers 105 and 106 so that a larger quantity of mortar is released.

Nach dem Abstreifer 10 befindet sich eine äußerst gleichmäßige Mörtelschicht 9 auf der Bahn 2.After the scraper 10, an extremely uniform layer of mortar 9 is present on the track 2.

Die Bahn 2 gelangt nun in eine Schneidstation 15, wo ein Messer 15' die noch feuchte Mörtelschicht 9 und die Armierung aus Glasfasergewebe oder -vlies 7 durchschnei-The web 2 now reaches a cutting station 15, where a knife 15' cuts through the still wet mortar layer 9 and the reinforcement made of glass fiber fabric or fleece 7.

det, gegebenenfalls auch die Kernbahn 2, und zwar im Bereich der Stöße, wenn einzelne Kernelemente aufgelegt worden sind, bzw. in gewählten Abständen bei kontinuierlicher Kernbahn. Anschließend wird die Kernbahn 2 mit der aufgebrachten armierten Mörtelschicht 9 in einemdet, if necessary also the core sheet 2, namely in the area of the joints, if individual core elements have been laid, or at selected intervals in the case of a continuous core sheet. The core sheet 2 is then covered with the applied reinforced mortar layer 9 in a

Wärmeofen 16 getrocknet und ausgehärtet. Damit ist die armierte Mörtelschicht 9' auf der Kernbahn 2 fest verankert . Der einseitig beschichtete Kern kann in dieser Form als Bau- bzw. Verbundplatte bereits verwendet werden. Üblicherweise wird jedoch eine beidseitig beschichtete Platte hergestellt. Dazu wird eine einseitig beschichtete Platte wieder an den Anfang der Rollenbahn 1 gebracht und so gewendet, daß nunmehr die unbeschichtete Bahnseite oben liegt und dieselbe Prozedur durchgeführtThe reinforced mortar layer 9' is then dried and hardened in the heating oven 16. The reinforced mortar layer 9' is thus firmly anchored on the core track 2. The core coated on one side can already be used in this form as a construction or composite board. Usually, however, a board coated on both sides is produced. To do this, a board coated on one side is brought back to the beginning of the roller track 1 and turned so that the uncoated side of the track is now on top and the same procedure is carried out.

werden kann, wie bereits beschrieben worden ist. 30can be, as already described. 30

Als Mörtelmaterialien eignen sich verschiedene, an sich bekannte Mixturen aus Zement, Wasser, Kunststoffanteilen, aus denen ein sogenannter Dünnbettmörtel hergestellt wird. Deren Rezepturen sind jedoch spezifizierbar und bilden nicht den Gegenstand der Erfindung. Diese "Dünnbettmörtel" werden so bezeichnet, da sie üblicher-Various known mixtures of cement, water and plastic components are suitable as mortar materials, from which a so-called thin-bed mortar is made. However, their recipes can be specified and are not the subject of the invention. These "thin-bed mortars" are called this because they are usually

weise wasserbeständigen Dünnbettmörteln für die Fliesenverlegung entsprechen.water-resistant thin-bed mortars for tile laying.

Die Dicke der Kernbahn ist relativ unkritisch. Sie kann 5The thickness of the core track is relatively uncritical. It can be 5

zwischen wenigen Millimetern und einigen Zentimetern liegen, z. B. zwischen 20 - 100 mm. Das hängt von dem jeweiligen Bedarf ab. Die Mörtelschicht 9 wird üblicherweise möglichst sparsam aufgelegt, d.h., im allgemeinen so,between a few millimetres and a few centimetres, e.g. between 20 - 100 mm. This depends on the respective requirements. The mortar layer 9 is usually applied as sparingly as possible, i.e., in general,

daß die Glasfasergewebebahn gerade umhüllt wird. 10that the glass fibre fabric is wrapped straight. 10

Von besonderem Vorteil ist bei der beschriebenen Bauplatte, daß die Abschlußebene der Mörtelschicht und des Glasfasergewebes oder -vlieses 7 in einer Ebene liegen. Hierdurch wird gewährleistet, daß das Glasfasergewebe oder -vlies 7 zum einen innig durch die armierte Mörtelschicht 9' mit dem Kern verbunden ist und zum anderen die äußere Mörtelschicht eine solche Konfiguration aufweist, daß sie sich für eine weitere Verarbeitung, z. B. zum Bekleben mit Tapete, zum Aufbringen von Fliesen undA particular advantage of the building board described is that the end plane of the mortar layer and the glass fiber fabric or fleece 7 lie in one plane. This ensures that the glass fiber fabric or fleece 7 is intimately connected to the core by the reinforced mortar layer 9' and that the outer mortar layer has a configuration such that it is suitable for further processing, e.g. for sticking wallpaper on, for applying tiles and

dergleichen eignet.the like.

Claims (8)

&agr;&idigr; ylv *5 ti &idigr; ' "Ji J {WEG3IAAl) Schutzansprüche:&agr;&idigr; ylv *5 ti &idigr; ' "Ji J {WEG3IAAl) Protection claims: 1. Halbzeug, nämlich Bauplatte &ggr;&eegr; &igr;-I- einem Gummi-Kreppkern (2), an dessen wenigstens einer Außenfläche zur Stabilisierung und Bewehrung und zur weiteren Verarbeitung, insbesondere Verkleidung mit beliebigen Werkstoffen eine Glasfasergewebebahn (7) in einer Mörtelschicht {9) aus einem aushärtbaren Mörtel eingebettet aufgebracht ist.1. Semi-finished product, namely a building board with a rubber crepe core (2), on at least one outer surface of which a glass fiber fabric web (7) is applied embedded in a mortar layer (9) made of a hardenable mortar for stabilization and reinforcement and for further processing, in particular cladding with any materials. 2. Halbzeug nach Anspruch 1, dadurch gekennzeichnet, daß die Konsistenz des flüssig aufgebrachten Mörtels nach DIN 1060 {Messung der Ausbreitung mit Wickertring) eine Ausbreitung von 22 bis 28 cm hat.2. Semi-finished product according to claim 1, characterized in that the consistency of the liquid mortar applied according to DIN 1060 (measurement of the spread with Wickert ring) has a spread of 22 to 28 cm. 3. Halbzeug nach Anspruch 1, dadurch gekennzeichnet, daß der flüssig aufgetragene Mörtel über zwei eng benachbart stehende, drehende Walzen (105, 106) auf den Gummikreppkern (2) läuft.3. Semi-finished product according to claim 1, characterized in that the liquid mortar is applied to the rubber crepe core (2) via two closely spaced, rotating rollers (105, 106). 4. Halbzeug nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß der Gummi-Kreppkern {2) mit der noch feuchten Mörtelschicht (9) und der Glasfaserarmierung im Bereich von Stoßen bzw. gewählten Abständen zerschnitten und dann trocknet und zur Aushärtung wärmebehandelt ist.4. Semi-finished product according to one of the preceding claims, characterized in that the rubber crepe core (2) with the still moist mortar layer (9) and the glass fiber reinforcement is cut in the area of joints or selected distances and then dried and heat-treated for hardening. 5. Halbzeug nach Anspruch 1, dadurch gekennzeichnet, daß der Gummi-Kreppkern (2) eine Schicht aus Altgummi- und/oder Kautschukfasern {22, 22') ist, die Teilstücke von zerkleinerten natürlichen oder synthetischen Kautschuken sind.5. Semi-finished product according to claim 1, characterized in that the rubber crepe core (2) is a layer of waste rubber and/or rubber fibers (22, 22'), which are parts of shredded natural or synthetic rubbers. &Agr;2α2 6. Halbzeug nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, daß nach dem Trocknen und Aushärtenlassen der armierten Mörtelschicht auf der einen Außenfläche des Gummi-Kreppkerns (2) die einseitig fertiggestellte Verbundplatte gewendet wird und auf die andere, bisher unbeschichtete Außenfläche eine weitere Glasfasergewebebahn (7) in einer weiteren Mörtelschicht (9) aus dem aushärtbaren Mörtel eingebettet aufgebracht ist.6. Semi-finished product according to one of claims 1 to 5, characterized in that after drying and allowing the reinforced mortar layer on one outer surface of the rubber crepe core (2) to harden, the composite panel finished on one side is turned over and a further glass fiber fabric web (7) embedded in a further mortar layer (9) made of the hardenable mortar is applied to the other, previously uncoated outer surface. 7. Halbzeug nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß die Dicke der ausgehärteten, armierten Mörtelschicht (9) wenigstens 0,2 mm beträgt.7. Semi-finished product according to one of claims 1 to 6, characterized in that the thickness of the hardened, reinforced mortar layer (9) is at least 0.2 mm. 8. Halbzeug nach einem der vorhergehenden Ansprüche, dadurch gekennzeichnet, daß das Glasfasergewebe über einen Bahnspeicher (19) geführt ist.8. Semi-finished product according to one of the preceding claims, characterized in that the glass fiber fabric is guided over a web storage device (19).
DE9321219U 1992-10-10 1993-10-09 Semi-finished products, namely building boards Expired - Lifetime DE9321219U1 (en)