DE928320C - Process for melting colorless glass - Google Patents
Process for melting colorless glassInfo
- Publication number
- DE928320C DE928320C DES18706D DES0018706D DE928320C DE 928320 C DE928320 C DE 928320C DE S18706 D DES18706 D DE S18706D DE S0018706 D DES0018706 D DE S0018706D DE 928320 C DE928320 C DE 928320C
- Authority
- DE
- Germany
- Prior art keywords
- glass
- added
- constituents
- oxide
- melting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Das Erschmelzen von Glas oder glasähnlichen Massen mittels Durchleiten eines elektrischen Stromes durch ein als Widerstand wirkendes Glasbad ist unter anderem mit dem Übelstand behaftet, daß hierdurch das erschmolzene Glas eine leicht gelbe bzw. grünlichgelbe Färbung annimmt. Man hat durch verschiedene Mittel versucht, diesen Nachteil zu beheben bzw. zu verringern, ohne jedoch zu einem besonderen Erfolg zu kommen.The melting of glass or glass-like masses by passing an electric current through it by acting as a resistance glass bath is afflicted, among other things, with the drawback that this the melted glass takes on a light yellow or greenish-yellow color. One has through different Means tries to remedy this disadvantage or to reduce it, however, without any particular success get.
So hat man z. B. der Glasschmelze oxydierende Stoffe, wie z. B. Nitrate, beigemischt, die imstande sind, die in der Glasmasse aufgelösten färbenden Bestandteile zu verändern. Auch hat man versucht,So one has z. B. the molten glass oxidizing substances such. B. nitrates, added, which is capable are to change the coloring components dissolved in the glass mass. They also tried
durch Umrühren die Berührungsflächen der Glasschmelze mit einer oxydierenden Atmosphäre zu erneuern und zu vergrößern. Endlich hat man je nach der Beschaffenheit der Elektroden die in unmittelbarer Nähe der letzteren je Raumeinheit abgegebene Energiemenge derart eingestellt, daß die Glasanfärbung auf einen Mindestwert herabgesetzt wurde.by stirring the contact surfaces of the glass melt to renew and enlarge with an oxidizing atmosphere. Finally one has depending on the nature of the electrodes, the amount emitted per unit of space in the immediate vicinity of the latter Amount of energy adjusted in such a way that the color of the glass was reduced to a minimum value.
Erfahrungsgemäß haben sich diese verschiedenen Mittel als unzureichend erwiesen, um die färbende Wirkung gewisser, beim Durchleiten des elektrischen Stromes entstehender reduzierender Bestandteile der entstehenden Schmelze, wie z. B. losgerissener und in der Glasmasse verstreuter Elektrodenteilchen, oderExperience has shown that these various agents have proven to be inadequate for the staining Effect of certain reducing components of the resulting when the electrical current is passed through resulting melt, such. B. loose and scattered in the glass mass electrode particles, or
durch Einwirkung solcher Teilchen auf schwefelhaltige glaserzeugende Stoffe, wie z. B. auf Alkali- und Erdalkalisulfate, gebildeter Verbindungen zu beheben.by the action of such particles on sulfur-containing glass-generating substances, such as. B. on alkali and alkaline earth sulfates, to fix formed connections.
Mangels geeigneter Mittel zur Entfernung dieser färbenden Bestandteile hat man daran, gedacht, die Elektroden mit Hüllen zu umgeben, um das Glas abzutrennen, welches mit den Elektroden in Berührung steht. Man kann so vermeiden, daß das.durch Be-In the absence of suitable means for removing these coloring constituents, thought has been given to the To enclose electrodes with sheaths to separate the glass which is in contact with the electrodes stands. In this way you can avoid that.
■ rührung mit den Elektroden verunreinigte Glas sich■ Touching the electrodes contaminated the glass
ίο mit der Glasmasse mischt. Die Hüllen müssen von Zeit zu Zeit gereinigt werden, um das unreine Glas zu entfernen, das sich in jeder Hülle sammelt. Dieses Verfahren ist umständlich und auch nicht zuverlässig.ίο mixes with the glass mass. The cases must be from Periodically cleaned to remove the unclean glass that collects in each envelope. This Procedure is cumbersome and also not reliable.
Die Erfindung gestattet die Vermeidung allerThe invention allows the avoidance of all
vorerwähnten Schwierigkeiten und Ünzuträglichkeiten. Sie besteht darin, den Glasbildnem des Gemenges geeignete Stoffe beizumischen, um die reduzierenden Bestandteile aufzulösen und die durch sie entstehenden färbenden Verbindungen zu zersetzen.the aforementioned difficulties and inefficiencies. It consists in adding suitable substances to the glass formers of the mixture in order to reduce the Dissolve constituents and decompose the resulting coloring compounds.
Diese Stoffe, unter denen das Zinkoxyd und das Kadmiumoxyd besonders wirksam sind, werden vorzugsweise dem Gemenge hinzugefügt, dessen Zusammensetzung zweckmäßig durch Hinzufügen anderer, schon in den verschiedenen Gemengen angewendeter Stoffe, z. B. Nitrate, Arsenik (Arsenigsäureanhydrid As2O3) oder Antimonoxyd, bereits oxydierend gemacht worden sind.These substances, among which the zinc oxide and the cadmium oxide are particularly effective, are preferably added to the mixture, the composition of which is expedient by adding other substances already used in the various mixtures, e.g. B. nitrates, arsenic (arsenic anhydride As 2 O 3 ) or antimony oxide, have already been made oxidizing.
Der Anteil der zur Verwendung gelangenden Stoffe richtet sich selbstverständlich nach der Menge der in der Glasmasse entstehenden reduzierenden Bestandteile. So genügt insbesondere bei Natron-Kalk-Gläsern gebräuchlicher Zusammensetzung ein Zusatz an Zinkoxyd von weniger als 5 °/0. Im nachstehenden sollen als Beispiele einige Zusammen-Setzungen von Glasschmelzen entsprechend der Erfindung angegeben werden, bei denen die Färbung des Glases vermieden wird.The proportion of the substances used depends, of course, on the amount of reducing constituents formed in the glass mass. So common composition satisfies an addition of zinc oxide of less than 5 ° / 0 particularly in the case of soda lime glass. In the following, some compositions of glass melts according to the invention are to be given as examples, in which the color of the glass is avoided.
Sand 100,0Sand 100.0
Natriumkarbonat 29,4Sodium carbonate 29.4
Natriumsulfat 2,0Sodium sulfate 2.0
Natriumnitrat 3,0Sodium nitrate 3.0
Kalkstein 26,8Limestone 26.8
Zinkoxyd 2,7Zinc oxide 2.7
Arsenik 0,5Arsenic 0.5
Sand 100,0Sand 100.0
Feldspat 11,8Feldspar 11.8
Natriumkarbonat 33,3Sodium carbonate 33.3
Natriumsulfat 1,0Sodium sulfate 1.0
Natriumnitrat 4,0Sodium nitrate 4.0
Kalkstein 21,0Limestone 21.0
Dolomit 6,8Dolomite 6.8
Zinkoxyd , 4,5Zinc oxide, 4.5
Arsenik 0,5Arsenic 0.5
Sand 100,0Sand 100.0
Borax 3,8Borax 3.8
Tonerdehydrat ΐ,ΐAlumina hydrate ΐ, ΐ
Natriumkarbonat 36,7Sodium carbonate 36.7
Natriumnitrat ...'. 2,0Sodium nitrate ... '. 2.0
Kalkstein r 20,3Limestone r 20.3
Zinkoxyd 6,4Zinc oxide 6.4
Antimonoxyd 0,7Antimony oxide 0.7
Die aus diesen drei Gemischen erschmolzenen Gläser enthalten je 2, 3 und 4,5 °/0 Zinkoxyd.The molten mixtures of these three glasses each contain 2, 3 and 4,5 ° / 0 of zinc oxide.
Claims (3)