DE904052C - Process for the dephosphorization of steel - Google Patents

Process for the dephosphorization of steel

Info

Publication number
DE904052C
DE904052C DER4089D DER0004089D DE904052C DE 904052 C DE904052 C DE 904052C DE R4089 D DER4089 D DE R4089D DE R0004089 D DER0004089 D DE R0004089D DE 904052 C DE904052 C DE 904052C
Authority
DE
Germany
Prior art keywords
steel
carbon
slag
dephosphorization
blown
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DER4089D
Other languages
German (de)
Inventor
Paul Girod
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BERG und HUETTENBETR E AG F
Original Assignee
BERG und HUETTENBETR E AG F
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BERG und HUETTENBETR E AG F filed Critical BERG und HUETTENBETR E AG F
Application granted granted Critical
Publication of DE904052C publication Critical patent/DE904052C/en
Expired legal-status Critical Current

Description

Verfahren zum Entphosphoren von Stählen Im der Patentschrift 898 4q:6 i,st ein Verfahren zum Entphosphoren von Stählen, insbesondere zur weitgehenden Entphosphor:ung von vorgeblasenem Thomasstahl, beschrieben, bei dem der Stahl auf eine in festem Zustande vorliegende biasische, oxydierende Schlackenmischung aufgegossen wird., die einen Zusatz von Kohlenstoff enthält. Die oxyd ischen Schlackenbestandteile reagieren dabei mit !dem Kohlenstoff unter Entwicklung von Kohlenoxyd und Kohlensäure, wobei eine kräftige Durchwirbelung von Schlacke und Stahl und dadurch eine schnelle und weitgehende Umsetzung der beiden Phasen erzielt wird.Process for the dephosphorization of steels in patent specification 898 4q: 6 i, st a process for the dephosphorization of steels, in particular for extensive Dephosphorization of pre-blown Thomasstahl, described in which the steel on a solid bias, oxidizing slag mixture is poured onto it which contains an addition of carbon. The oxide slag components react with the carbon to develop carbon dioxide and carbonic acid, with a strong turbulence of slag and steel and thus a rapid one and extensive implementation of the two phases is achieved.

Durch weitere Versuche wurde festgestellt, daß sich der Zusatz von Kohlenstoff zur Schlacke erübrigt, wenn das Stahlbad bereits einen gewissen Kohlenstoffgehalt besitzt. Eine Weiterverfolgung dieser Arbeitsweise führt zu dem Ergebnis, daß man in ider Schlacke auf :den Kohlenstoffzusatz verzichten kann, wenn man (den Stahl nach dem Herunterfrischen im Konverter in an sich bekannter Weise aufkohlt und darauf mit der .im Hauptpatent erwähnten Schlackenmnfschung ohne Kohlenstöffzu,satz behandelt. An diese Verfahrensstufe kann natürlich noch eine weitere Behandlung des entphosphorten Stahles in einem Herdofen angeschlossen werden.Through further experiments it was found that the addition of Carbon to the slag is unnecessary if the steel bath already has a certain carbon content owns. A continuation of this procedure leads to the result that one in the slag on: the addition of carbon can be dispensed with if one (the steel after freshening in the converter in a known manner carburized and on it with the .in the main patent mentioned slag reduction without carbon addition treated. A further treatment can of course be added to this procedural stage of the dephosphorized steel can be connected in a hearth furnace.

An Hand zweier Beispiele soll die Wirkungsweise des Verfahrens gemäß der Erfindung kurz geschnldert werden.Using two examples, the mode of operation of the method is intended according to of the invention can be briefly cut.

Beispiel i Die Thomascharge wird im Konverter auf folgende Zusammensetzung heruntergeblasen: C o;oi5%, Mn o,16'/o" P 0,0450/0, S o, o.36 0/0.Example i The Thomas batch is made up of the following composition in the converter blown down: C o; oi5%, Mn o, 16 '/ o "P 0.0450 / 0, S o, o.36 0/0.

Dieser vorgeblasene Stahl wird! mit Graphit auf o,o4o%, C aufgekohlt und darauf .in eine Pfanne gegossen, auf deren Boden ein gekörntes, vorgewärmtes Gemisch von Kalk, Erz und Flußspat von folgender Zusammensetzung eingebracht Ist: Kalk 50%, Häinatit 300/0, Fluß,spat io%, Kieselsäure io%. Wenige Minuten nach der Durch mischurig war der Phosphorge galt auf o,oi2% ge sanken.This pre-blown steel will! Carburized to 0.04%, C with graphite and then poured into a pan with a granular, preheated one on the bottom Mixture of lime, ore and fluorspar of the following composition is introduced: Lime 50%, heinatite 300/0, river, late 10%, silicic acid 10%. A few minutes after the The phosphorus was reduced to o, oi2% due to mixing.

Beispiel 2 Zusammensetzung (des vorgeblasenen Thomasstahles: C o,oi80/a, Mn o,2o%, P o,0720/0, S o,053 01o. Der Stahl wurde mit Graphit auf o,o56% Kohle aufgekohlt und in der gleichen Weise wie in. dem Beispiel i mixt einer Entphospho.rungsschlacke behandelt. Der Stahl zeigt kurz nach der Behandlung einen Phosphorgehalt von o,oi6°/o.Example 2 Composition (of the pre-blown Thomasstahl: C o, oi80 / a, Mn o, 2o%, P o, 0720/0, S o, 053 01o. The steel was made with graphite on 0.056% carbon carburized and in the same way as in. Example i mixes a dephosphorus slag treated. Shortly after the treatment, the steel shows a phosphorus content of 0.06%.

Claims (1)

PATENTANSPRUCH: Verfahren zum Entphos-phoren von Stählen mittels fester basifscher Schlacke nach Patent 898 446, dadurch gekennzeichnet, daß der Kahlenstoffzusatz zu der Schlacke ganz oder teilweise durch den Kohlenetoff des Stahles ersetzt ist.PATENT CLAIM: Process for the dephosphorus of steels by means of solid Basic slag according to Patent 898 446, characterized in that the carbon additive to the slag is wholly or partially replaced by the carbon of the steel.
DER4089D 1938-06-24 1939-06-22 Process for the dephosphorization of steel Expired DE904052C (en)