DE9007268U1 - Building material, in particular concrete, concrete-like materials, mortar and the like. - Google Patents
Building material, in particular concrete, concrete-like materials, mortar and the like.Info
- Publication number
- DE9007268U1 DE9007268U1 DE9007268U DE9007268U DE9007268U1 DE 9007268 U1 DE9007268 U1 DE 9007268U1 DE 9007268 U DE9007268 U DE 9007268U DE 9007268 U DE9007268 U DE 9007268U DE 9007268 U1 DE9007268 U1 DE 9007268U1
- Authority
- DE
- Germany
- Prior art keywords
- building material
- concrete
- plastic
- granulate
- material according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
Angelder:Angelder:
NOE-Scr ltechnikNOE-Scr ltechnik
Georg hc/er-Keller Gs^n + Co.Georg hc/er-Keller Gs^n + Co.
Kuntzestr. 72Kuntzestr. 72
7334 Süssen7334 Suessen
3003 137 H-S/mr 01.8.90 (90/36)3003 137 H-S/mr 01.8.90 (90/36)
Titel; Baustoff, Insbesondere Beton, betonähnliche Stoffe, Mörtel und dgl. Title; Building material, in particular concrete, concrete-like materials, mortar and the like.
Gegenstand der Erfindung ist ein Baustoff, insbesondere Beton, betonähnliche stoffe, Mörtel und dgl. nach dem Oberbegriff des Patentanspruchs 1, sowie hiermit hergestellte bewehrte und unbewehrte Bauteile.The subject matter of the invention is a building material, in particular concrete, concrete-like materials, mortar and the like according to the generic term of patent claim 1, as well as reinforced and unreinforced components produced therewith.
Baustoffe der genannten Gattung sind bekannt. Im Bauwesen werden den vergießbaren Baustoffen, wie Beton, Mörtel und dgl. die verschiedenartigsten Zuschlagstoffe wieBuilding materials of the above-mentioned type are well known. In construction, the castable building materials such as concrete, mortar and the like are mixed with a wide variety of additives such as
Amierungseisen, Kies, Asbestfasern und dgl. mehr zur Erhöhung der Festigkeit oder als reine Füllstoffe beigegeben. Speziell ist aus der EP 0 242 334 Al ein Verfahren zur Herstellung von Beton und betonähnlichen Stoffen bekannt, bei d«£& 3:1s Zuschlagstoff ein Thermoplast-Kunststoffgranulat mit bis zu 60% Tsiocksnsubstanzanteil d*sr Betonbestandtaile -isia Betongfcisisch beigemengt wird. Dieses granulat kann kann in Fora von Primäricunsii -'~vffgranulat oder auch Recycling-Granulat aus thermoplastis len Kunststoffgemischen zugemischt werden, eins &Bgr;&bgr;&egr; c "äerheit hierbei ist, daß di- Granulatpartikel während des Abbindprozeßes durch die natürliche Erwärmung des Betons oder Bindemittelleims sowohl mit den übrigen Zuschlagstoffen als auch mit dem Mörtel verkleben.Reinforcing iron, gravel, asbestos fibres and the like are added to increase the strength or as pure fillers. In particular, a process for producing concrete and concrete-like materials is known from EP 0 242 334 A1, in which a thermoplastic synthetic granulate with up to 60% of the concrete components is mixed into the aggregate in a ratio of 3:1. This granulate can be mixed in as a mixture of primary granulate or recycled granulate from thermoplastic synthetic mixtures. One thing that is special about this is that the granulate particles stick to the other aggregates and to the mortar during the setting process due to the natural heating of the concrete or binding agent.
Nachteilig bei dem so beschriebenen Baustoff ist, daß nur speziell angepaßte Kunststoffgranulate mit sehr niedriger Schmelztemperatur zumischbar sind, um bei der geringen Abbindwärme eine ausreichende Anschmelzung des Kunststoffs sicher zu stellen; andernfalls muß zusätzlich Wärme zugeführt werden, was bei der schlechten Wärmeleitfähigkeit des Beton-Kunststoff-Gemischs einen erheblichen Zeit- und Energieaufwand zu dessen Herstellung mit sich bringt. Die Eingrenzung der Auswahl der einsetzbaren thermoplastischen Kunststoffe auf solche mit niedriger Schmelztemerpatur bringt es mit sich, daß die Verwendung beliebiger Duroplaste oder Thermoplaste mit hoher Schmelztemperatur nur in geringen Mengen und als sonstiger Zuschlagstoff erfolgen kann, da sonstThe disadvantage of the building material described is that only specially adapted plastic granules with a very low melting temperature can be mixed in to ensure sufficient melting of the plastic at the low setting heat; otherwise additional heat must be added, which, given the poor thermal conductivity of the concrete-plastic mixture, requires a considerable amount of time and energy to produce. Limiting the selection of thermoplastics that can be used to those with a low melting temperature means that any thermosetting plastics or thermoplastics with a high melting temperature can only be used in small quantities and as other additives, as otherwise
eine ungenügende Verklebung oder keinerlei Anbindung an die restlichen Zuschlagstoffe mit Hilfe der schmelzbaren Thermoplasten stattfindet, wodurch der abgebundene Beton an Festigkeit einbüßt.insufficient bonding or no bonding at all to the remaining aggregates using the meltable thermoplastics takes place, which causes the set concrete to lose strength.
Der Erfindung liegt die Aufgabe zugrunde, einen betonähnlicüien Baustoff anzugeben, bei dem ohne wesentliche Mindernvig dar einsatzspezifischen Festigkeit die Zusammensetzung des als Zuschlagstoff verwendeten Kunststoffs beliebig wählbar ist und als vollwertiger Ersatz für mineralische Zugschlagstoffe dient, aber der Zuschlag in unterschiedlichen Mengenbeigaben in Abhängigkeit des späteren Verwendungszwecks erfolgt.The invention is based on the object of specifying a concrete-like building material in which the composition of the plastic used as an aggregate can be freely selected without significantly reducing the application-specific strength and serves as a full replacement for mineral tensile aggregates, but the aggregate is added in different quantities depending on the later intended use.
Die Aufgabe wird dadurch gelöst, daß das Kunststoffgranulat aus zerkleinerten/gemahlenen thermoplastischen und/oder duroplastischen Althartkunststoff^n besteht, und daß dessen Raumanteil bezogen auf den Raumanteil des Sandes und/oder der anderen Zuschlagstoffe in Abhängigkeit des Baustoffeinsät&zgr;Zweckes bis zu 50 % beträgt und durch das Bindemittel innerhalb des Baustoffes gebunden ist. Es hat sich überraschenderweise und entgegen bestehender Bedenken gezeigt, daß durch Zuschlag eines Kunstoffgranulate bestehend aus beliebigen thermoplastischen und/oder duroplastisehen Kunststoffmischungen in bestimmten Volumeranteilen bezogen auf die restlichen Zuschlagstoffe die einsatzspezifische Festigkeit zwar gemindert, aber weitgehend erhalten bleibt. Die Abbindzeit wird durch die Beimischung desThe task is solved by the fact that the plastic granulate consists of crushed/ground thermoplastic and/or thermosetting old hard plastics, and that its volume share in relation to the volume share of the sand and/or the other additives is up to 50% depending on the building material's purpose and is bound by the binding agent within the building material. Surprisingly and contrary to existing concerns, it has been shown that by adding plastic granulate consisting of any thermoplastic and/or thermosetting plastic mixtures in certain volume shares in relation to the remaining additives, the application-specific strength is reduced but largely retained. The setting time is reduced by adding the
• · ♦ t ·• · ♦ t ·
Kunststoffgranulats nur äußerst gering beeinflußt und hat keinerlei Einfluß auf den Transport und die Bearbeitbarkeit des Betons. Besonders vorteilhaft ist hierbei, daß beliebige Recycling-Hartkunststoffe verwendet werden können, wodurch die oftmals schwierige Entsorgung bestimmter Kunststoffsorten durch Beimischung in don Baustoff entfallen kann. Ein Zerkleinern der Hartaltkunststoffteile wie bspw. Fernsehgehäuse, KunststoffVerschalungen und dgl. mehr kann dabei in herkömmlichen Mahlmühlen geschehen, ohne eine vorherige Aussortierung nach Kunststoffsorten durchführen zu müssen, da die Zusammensetzung des Kunststoffgranulate auf die Endfestigkeit, insbesondere die Druckfestigkeit des Danstoffs nur in vernachlässigbarem Maße von der Kunststoffzusammensetzung abhängig ist.Plastic granulate is only affected to a very small extent and has no influence on the transport and workability of the concrete. A particularly advantageous feature here is that any recycled hard plastic can be used, which means that the often difficult disposal of certain types of plastic by mixing them into the building material can be avoided. The hard plastic waste parts such as television casings, plastic cladding and the like can be crushed in conventional grinding mills without having to sort them out according to the type of plastic beforehand, since the composition of the plastic granulate only has a negligible effect on the final strength, in particular the compressive strength of the concrete, on the plastic composition.
Dss Kunststoffgranulat kann hierbei Korngrößen zwischen Feinsandkorngröße bis Sandkorngröße aufweisen und in etwa nur einer Korngröße oder in gemischten Korngrößen dem Baustoff beigemischt werden. Vorteilhaft ist es jedoch, daß die Granulatzusammensetzung hinsichtlich der Korngröße so gewählt sein kann, daß ein entsprechender Volumenanteil von Granulatkörnern ähnlicher Korngröße wie die der zu ersetzenden mineralen Zuschlagstoffe vorgesehen wird» Hierdurch, ist es möglich, die Gesamtdichte des Baustoffs aufgrund des gringeren spezifischen Gewichts des Kunststoffgranulats verglichen mit den anderen mineralen Zuschlagstoffen herabzusetzen ohne daß eine wesentliche Beeinträchtigung der einsatzspezifischenThe plastic granulate can have grain sizes between fine sand grain size and sand grain size and can be mixed into the building material in approximately only one grain size or in mixed grain sizes. However, it is advantageous that the granulate composition can be selected in terms of grain size so that a corresponding volume proportion of granulate grains of a similar grain size to that of the mineral aggregates to be replaced is provided. This makes it possible to reduce the overall density of the building material due to the lower specific weight of the plastic granulate compared to the other mineral aggregates without significantly impairing the application-specific properties.
Festigkeitseigenschaften des Baustoffs auftritt.strength properties of the building material.
Zur Verbesserung der Bindungskräfte zwischen mineralischem Bindemittel und Kunststoffteilen ist es besonders vorteilhaft, wenn die Oberflö 'he der Kunststoffgranulatkörner rauhflächig und/oder unregelmäßig ausgestaltet ist, wodurch die Anbindoberfläche vergrößert ist. Eine andere Möglichkeit, die Adhäsionskräfte Bindemittel-Kunststoffgranulatteilchen zu erhöhen ist dadurch gegeben, daß zur Benetzung der Oberfläche des Kunststoffgranulats ein Entspannungsmittel eingesetzt werden kann; ferner ist es auch möglich, die Anbindkräfte dadurch zu erhöhen, daß die Oberfläche des Kunststoffgranulate mit einer Schicht aus Wasserglas überzogen sein kann. Letztgenannte Maßnahmen können für sich allein oder in Kombination zur Verbesserung der Adhäsion zwischen mineralischem Bindemittel und Kunststoffgranulat eingesetzt werden.To improve the bonding forces between mineral binder and plastic parts, it is particularly advantageous if the surface of the plastic granulate is rough and/or irregular, which increases the bonding surface. Another way to increase the bonding forces between the binder and plastic granulate particles is to use a relaxant to wet the surface of the plastic granulate; it is also possible to increase the bonding forces by coating the surface of the plastic granulate with a layer of water glass. The latter measures can be used alone or in combination to improve the adhesion between mineral binder and plastic granulate.
Dadurch, daß das Kunststoffgranulat einen Volumenanteil bis 5% des Sandanteils ersetzen kann, der seinerseits 15 -60% des Baustoffvolumens ausmacht, ist es möglich, einen konstruktiven Beton herzustellen, der bei einer Rohdichte kleiner gleich 2,8 t/m3 und beliebiger Festigkeitsklasse zur Herstellung von tragenden und nicht tragenden Bauteilen bis zur Betongüte B 25 eingesetzt werden kann. Die Zusetzung des Kunststoffgranulate beeinträchtigt hierbei die Endfestigkeit des Betons nur unernebiich; die Beimischung hat auf die Äbbindzeit nur einenBecause the plastic granulate can replace a volume share of up to 5% of the sand, which in turn makes up 15-60% of the building material volume, it is possible to produce a structural concrete that can be used for the production of load-bearing and non-load-bearing components up to concrete quality B 25 with a density of less than or equal to 2.8 t/m 3 and any strength class. The addition of the plastic granulate only affects the final strength of the concrete insignificantly; the addition has only a minor effect on the setting time.
äußerst geringen Einfluß. Hierbei ist es zwar vorzuziehen, daß das Kunststoffgranulat einen Teil des Sandes des Mörtels ersetzt, welcher aus Wasser, Sand und Bindemittel (Zement, Kalk, Gips oder einem anderen mineralischen Bindemittel) besteht, er kann aber auch einen Volumenanteil von bis zu 5% der anderen Zuschlagstoffe, d.h. Kies, Split und dgl. bei gleicher Größe im Baustoff ersetzen, durch die Beigabe des Kunststoffgranulats wird der Konsistenzbereich des Baustoffs nur unwesentlich verändert; der Einfluß des Kunststoffgranulats auf die Endfestigkeit des ausgehärteten Materials, dessen Herstellungsparameter sowie dessen Abbindzeit liegen im Rahmen der üblichen Toleranz. Ein solcher Baustoff kann insbesondere zur Herstellung von bewehrten und unbewehrten Beton-Bauteilen dienen.extremely minor influence. It is preferable that the plastic granulate replaces part of the sand in the mortar, which consists of water, sand and binding agent (cement, lime, gypsum or another mineral binding agent), but it can also replace a volume share of up to 5% of the other aggregates, i.e. gravel, chippings and the like, of the same size in the building material. The addition of the plastic granulate only changes the consistency of the building material insignificantly; the influence of the plastic granulate on the final strength of the hardened material, its production parameters and its setting time are within the usual tolerance. Such a building material can be used in particular for the production of reinforced and unreinforced concrete components.
Ein besonders interessanter Baustoff ist dadurch gegeben, daß das Kunststoffgranulat einen Volumenanteil von bis zu 40% aller mineralen Zuschlagstoffe ersetzen kann, da hierdurch ein besonders leichter aber mit ausreichender Festigkeit versehener Leichtbeton oder betonähnlicher Leichtbaustoff hergestellt werden kann, der bei einer Rohdichte kleiner gleich 1,0 t/m3 zur Herstellung von Isolierplatten und dgl. verwendbar ist.A particularly interesting building material is that the plastic granulate can replace a volume share of up to 40% of all mineral aggregates, since this makes it possible to produce a particularly light but sufficiently strong lightweight concrete or concrete-like lightweight building material, which can be used for the production of insulating panels and the like with a gross density of less than or equal to 1.0 t/m 3 .
Dadurch, daß das Kunststoffgranulat in einen Füllbaustoff geringerer Festigkeit als Zuschlagstoff zugesetzt werden kann, ist es möglich, den hierdurch erhaltenen Füiibaustoff zurBecause the plastic granulate can be added to a filler material of lower strength as an aggregate, it is possible to use the filler material obtained in this way for
1 I · ·1 I · ·
Herstellung von Schichtbauteilen, Sandwichplatten und dgl. einzusetzen, bei welchen eine tragende Funktion bestimmter Bauteilbereiche gegeben sein muß, aber ein möglichst geringes spezifisches Gewicht des Gesamtbaukörpers angestrebt wird.To be used in the production of layered components, sandwich panels and the like, where a load-bearing function of certain component areas must be given, but the aim is to keep the specific weight of the entire structure as low as possible.
Bei der Herstellung de ; betonähnlichen Baustoffes ist es besonders vorteilhaft, daß das Kunststoffgranulat mit den restlichen Zuschlagstoffen vor der Herstellung des betonähnlichen Baustoffes vermengt und ggi. als Zuschlagmischung zwischenlagerbar sein kann und erst am Einsatzort durch Zugabe eines mineralischen Bindemittels, insbesondere Zement oder Kalk zu dem betonähnlichen Baustoff verarbeitbar ist.When producing the concrete-like building material, it is particularly advantageous that the plastic granulate is mixed with the remaining aggregates before the concrete-like building material is produced and can be temporarily stored as an aggregate mixture and can only be processed into the concrete-like building material at the place of use by adding a mineral binding agent, in particular cement or lime.
Zur Herstellung eines vergießbaren Baustoffes, insbesondereFor the production of a castable building material, in particular
Hartkunststoffteilen ist es besonders vorteilhaft, daß als Abfall anfallende Hartkunststoffprodukte, wie Kunststoffensterrahmen, Verschalungen und dgl. zu einem Kunststoffgranulat auf maximal Kieselkorngrößfc zerkleinert als Zuschlagstoff oder als Teilersatz eines mineralischen Zuschlagstoffes des außerdem noch ein mineralisches Bindemittel, wie Zement, Kalk oder dgl. sowie Wasser aufweisenden Baustoffes beigemengt werden kann und in diesem nur mittels des Bindemittels eingebunden ist. Hierdurch ist eine besonders effektive Kunststoffabfallentsorgungsmaßnahme gegeben, wobei der Kunststoff einem weiteren VerwendungszweckIt is particularly advantageous for hard plastic parts that hard plastic products that accrue as waste, such as plastic window frames, formwork and the like, can be crushed into plastic granules to a maximum of pebble grain size as an aggregate or as a partial replacement for a mineral aggregate that also contains a mineral binding agent such as cement, lime or the like as well as water and is only bound in the building material by means of the binding agent. This provides a particularly effective plastic waste disposal measure, whereby the plastic can be used for another purpose.
zugeführt wird, ohne daß hierdurch die einsatzspezifische Verwendbarkeit des so hergestellten Baustoffs beeinträchtigt wird.without affecting the specific use of the building material produced in this way.
Anhand einiger Beispiele wird vorliegende Erfindung nachfolgend näher erläutert.The present invention is explained in more detail below using some examples.
Zur Herstellung eines konstruktiven Betons werden in der Regel 300kg Portlandzement auf 1 m3 losen Zuschlagstoff zugegeben und trocken durchmischt; der Zuschlagstoff besteht, je nach herzustellender Betongefügegüte aus einer Mischung von mindestens 15 Volumenprozent eines Betonsandes, der unterschiedliche Körnungen aufweisen kann (z.B. Mittelsand 0,2/1 : 15 Gew.%; Grobsand 1/3 : 35 Gew%; Kies 3/30 : 50 Gew%) und maximal 5 VoI% eines Hartkunststcffgranulats, dessen Körnung vorzugsweise der des Sandes entspricht. Je nach Bearbeitungserfordernissen wird nachfolgend die Trockenmischung mit Hasser derart durchfeuchtet, daß nach nochmaligem gründlichem Mischen eine gleichmäßige Masse entsteht, die je nach Verwendungszweck einen erdfeuchten, weichen oder flüssigen Beton ergibt. Bezogen auf die Trockensubstanzmenge kann der Waeserzusatz zwischen 14,5 -19,5 Volumenprozent betragen.To produce structural concrete, 300 kg of Portland cement is usually added to 1 m3 of loose aggregate and mixed dry; depending on the quality of the concrete structure to be produced, the aggregate consists of a mixture of at least 15% by volume of concrete sand, which can have different grain sizes (e.g. medium sand 0.2/1 : 15% by weight; coarse sand 1/3 : 35% by weight; gravel 3/30 : 50% by weight) and a maximum of 5% by volume of hard plastic granulate, the grain size of which preferably corresponds to that of the sand. Depending on the processing requirements, the dry mixture is then moistened with a slurry so that after further thorough mixing a uniform mass is produced, which, depending on the intended use, produces a moist, soft or liquid concrete. In relation to the amount of dry matter, the water addition can be between 14.5 and 19.5% by volume.
Das Hartkunststoffgranulat besteht insbesondere aus zerkleinerten, als Abfall anfallenden Hart-pvc-Teilen, dessenThe hard plastic granulate consists mainly of shredded hard PVC parts that are generated as waste, the
t ·t ·
Granulatpartikel eine unregelmäßige und rauhe Oberfläche aufweisen und nach dem Mahlprozeß gegebenenfalls mit einem Haftvermittler, wie z.B. handelsübliche Natriumsilikate (Wasserglas) oberflächenbentzt und anschließend getrocknet wurden. Der Haftvermittler ist swar nicht unbedingt erforderlich, fördert aber die Adhäsion zwischen Zementleim und Km» iätoffgranule.c,Granulate particles have an irregular and rough surface and, after the grinding process, are optionally surface-treated with an adhesion promoter, such as commercially available sodium silicates (water glass) and then dried. The adhesion promoter is not absolutely necessary, but promotes adhesion between the cement paste and the cement granules.c,
Ein so hero?~t:ellter Beton, dessen Rohdichte zwischen 2,0 t/m3 und 2,8 t/m3 je nach Zuschlagstoffbestandteile und Verdichtungsmaß beträgt, kann zur Herstellung von tragenden Bauteilen verwendet werden. Hierbei hat der Kunststoffgranulatzuschlag keinen oder einen nur unwesentlichen Einfluß auf die Festigkeitsklasse des Betons sowie auf dessen Herstellungsparameter.Concrete produced in this way, with a density of between 2.0 t/m 3 and 2.8 t/m 3 depending on the aggregate components and degree of compaction, can be used to manufacture load-bearing components. The plastic granulate additive has no or only an insignificant influence on the strength class of the concrete and on its manufacturing parameters.
Zur Herstellung des Kunststoffgranulate eignen sich insbesondere Hart-PVC-Kunststoffbauverschalungen, welche nach mehrmaliger Verwendung zum Herstellen von Schalbetonteilen als Abfall anfallen und hierdurch einem weiteren Verwendungszweck bei gleichzeitiger Entsorgung zugeführt werden.Rigid PVC plastic formwork is particularly suitable for the production of plastic granules, which, after being used several times to produce formwork concrete parts, becomes waste and is thus given another use while being disposed of at the same time.
Zweites Aueführungsbeispiel:Second example:
Zur Herstellung eines unbewehrten Leichtbetons werden mindestens 200 kg Portland-Zement auf 1 m3 losen Betonvolumen zugegeben und trocken durchgemischt; der Zuschlagstoff bestehtTo produce unreinforced lightweight concrete, at least 200 kg of Portland cement are added to 1 m 3 of loose concrete volume and mixed dry; the aggregate consists of
im vorliegenden Fall aus leichten mineralischen Zuschlagstoffen wie Bims, Hüttenbims, Blähton und Sand in unterschiedlichen Gewichtsverhältnissen zueinander. Diesen können Treibmittel bzw. Schaumbildner beigesetzt iäin, die nach Einbringung des Wassers mit diesem oder mit dem Bindemittel reagieren und durch Blasenbildung d « Rohdichte des fertigen Betons herabsetzen. Die Rohdichten eins solchen Leichtbetons betrage;? ?·:■??.sehen 500-800 kg/m3 für nicht trisgfähige als Is_liermateri-1 zu verwendende Baustoffe und zwischen ·*00-200&udigr; kg/m3 im Falle eine-, tragfähigen Leichtbetons.in the present case from light mineral aggregates such as pumice, granulated blast furnace pumice, expanded clay and sand in different weight ratios to one another. Blowing agents or foaming agents can be added to these which react with the water or with the binding agent after the water has been added and reduce the density of the finished concrete by forming bubbles. The density of such lightweight concrete is between 500 and 800 kg/m 3 for non-trisile building materials to be used as insulating material and between 100 and 200 kg/m 3 in the case of load-bearing lightweight concrete.
Zusätzlich zu den sIneralen Zuschlägen ist mit bis zu 40VoI.% der Gesamtzuschlagstoffmenge ein Hartkunststoffgranulat in der Zuschlagtrockenmasse enthalten, dessen Körnung je nacTi Einsatzzweck des Leichtbetons unterschiedlich sein kann. Ein solcher Leichtbeton eignet sich besonders gut zur Herstellung von Hohlblocksteinen, Voll-Leichtbausteinen, Isolier-Leichtbauplatten und dgl., bei welchen es nicht in erster Linie auf Festigkeitseigenschaften, sondern auf Isolierschutz ankommt.In addition to the mineral aggregates, up to 40% by volume of the total aggregate quantity is contained in the dry aggregate mass of hard plastic granulate, the grain size of which can vary depending on the intended use of the lightweight concrete. Such lightweight concrete is particularly suitable for the production of hollow blocks, solid lightweight building blocks, insulating lightweight building panels and the like, where the main focus is not on strength properties but on insulation protection.
Eine weitere Verwendung des Leichtbaustoffes sieht insbesondere vor, diesen als flüssig einzufüllenden und aushärtbaren Füllbaustoff geringerer Festigkeit in tragenden Betonteilen vorzusehen, bspw. zur Ausfüllung von Hohlisauern und ähnlichen Schichtbauteilen.Another use of the lightweight construction material is to provide this liquid, curable filling material of lower strength in load-bearing concrete parts, e.g. for filling hollow concrete walls and similar layered components.
&eegr; ff * · ·&eegr; ff * · ·
Selbstverständlich beschränkt sich das Vorsehen eines mineralischen Bindemittels nicht auf Zement, es können auch ande. 3 mineralische Bindemittel wie bspw. Gips, Kalk und dgl. verwendet wurden» Kit welchen ein ·Iz Bauzwecke geeigneter M-^tel oder betonähnlicher Baustoff hergestellt werden kann. Ferner ist es ohne Belang, welche Hartkunststoffe als Basismaterial des Kunststoff granulats Verwendung fir:, ten. Dieses kann auch aus anderweitig nicht wiederverwendbaren oder als Abfall anfallenden zerkleinerten Kunststoffprodukten, wie bspw. Epoxid- oder Phenol-Kunststoffbauteilen bestehen. Es ist denkbar, beliebige Alt-Hartkunststoffe einer sog. Recycling-Wiederverwendung zuzuführen, indem diese, abhängig des spezifischen Einsatzspektrums des Baustoffes in unterschiedlichen Raumanteilmengen in diesem vorgesehen werden, wodurch gleichzeitig eine Entsorgung des sonst als Abfall anfallenden Kunststoffes erfolgt.Of course, the use of a mineral binding agent is not limited to cement; other mineral binding agents such as gypsum, lime and the like can also be used, with which a cement or concrete-like building material suitable for construction purposes can be produced. Furthermore, it is irrelevant which hard plastics are used as the base material for the plastic granulate. This can also consist of shredded plastic products that cannot otherwise be reused or that accrue as waste, such as epoxy or phenol plastic components. It is conceivable to recycle any old hard plastics by including them in the building material in different volume proportions depending on the specific range of uses, which at the same time disposes of the plastic that would otherwise accrue as waste.
Claims (16)