DE742374C - Process for making structures made of superpolyamides more difficult - Google Patents
Process for making structures made of superpolyamides more difficultInfo
- Publication number
- DE742374C DE742374C DES149815D DES0149815D DE742374C DE 742374 C DE742374 C DE 742374C DE S149815 D DES149815 D DE S149815D DE S0149815 D DES0149815 D DE S0149815D DE 742374 C DE742374 C DE 742374C
- Authority
- DE
- Germany
- Prior art keywords
- superpolyamides
- treated
- structures made
- treatment
- disodium phosphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Verfahren zum Erschweren von Gebilden aus Superpolyamiden Das technische Verfahren zum Erschweren von Seide besteht darin; daß diese zunächst in einer wässerigen Lösung von Zinnchlorid (Sn Cl,) behandelt, sodann mit Wasser gewaschen und hiernach mit wässeriger Dinatriumphosphatlösung behandelt wird, worauf gegebenenfalls eine abschließende Behandlung mit wässeriger Natriumsilicatlösung folgt. Eine derartige Behandlung erteilt der Seide eine Erschwerung aus Zinnsilicophosphat von 1s bis 30 Gewichtsprozent. Die Faser bleibt weich und glänzend, und die erzielte Gewichtserhöhung ermöglicht die Gewinnung von Geweben, die besonders guten Griff und Fall besitzen. Außerdem ermöglicht die Reißfestigkeit der .Seide, auf die Fäden und Gewebe erhebliche Erschwerungen aufzubringen und trotzdem eine -genügende Festigkeit der Seide zu bewahren.Method for making structures made of superpolyamides more difficult The technical method for making silk more difficult consists in this; that this is first treated in an aqueous solution of tin chloride (Sn Cl,), then washed with water and then treated with aqueous disodium phosphate solution, which is optionally followed by a final treatment with aqueous sodium silicate solution. Such a treatment gives the silk a stannous silicophosphate weight of 1s to 30 percent by weight. The fiber remains soft and shiny, and the increase in weight achieved enables fabrics to be obtained that have particularly good grip and drape. In addition, the tensile strength of the silk makes it possible to impose considerable difficulties on the threads and fabric and still maintain sufficient strength of the silk.
Aus den gleichen Gründen wie für Seide würde es -sehr wertvoll sein, Erschwerungen aus Zinnsilicophosphat auf Fase-#n,-Fäden.und Geweben aus Superpolyamiden aufzubringen. Diese Fasern sind ebenso widerstandsfähig, wenn nicht überhaupt noch widerstandsfähiger als Seide, was ohne eine Beeinträchtigung -der Eigenschaften der Fasern und Gewebe die Anwendung von sehr hohen Erschwerungsmengen gestatten würde.For the same reasons as for silk it would be very valuable Compromises made of tin silicophosphate on fibers, threads and fabrics made of super polyamides to raise. These fibers are just as tough, if not at all still more resistant than silk, without any impairment of the properties the fibers and fabrics allow the application of very high levels of aggravation would.
Wenn man indessen auf Fäden oder Gewebe aus Superpolyamiden das übliche Seidenerschwerungsverfahren anwendet, ist die Erschwerung unbedeutend und übersteigt nicht i bis 2 °,`o vom Warengewicht.If, on the other hand, you work on threads or fabrics made of superpolyamides, the usual Applies silk weighting method, the weighting is insignificant and exceeds not i up to 2 °, `o of the weight of the goods.
Es wurde nun gefunden, daß man erheblich beträchtlichere Erschwerungen, und zwar von der Größenordnung der Erschwerungen, wie man sie auf Seide erzielt, erhalten kann, wenn man Fäden, Fasern, Borsten, Bändchen oder Gewebe aus Superpolyamiden vor oder während oder vor und während des Erschwerungsverfahrens einer Behandlung mit Quellungsmitteln unterwirft.It has now been found that considerably more difficult on the order of magnitude of the difficulties that one achieves on silk, can be obtained by using threads, fibers, bristles, ribbons or fabrics made of superpolyamides before or during or before and during the aggravation procedure of a treatment Subjected with swelling agents.
Es ist bekannt, dar Gebilde aus Superpolyainiden, wenn diese mit einer wässerigen Lösung oder einer wässerigen Emulsion einer oder mehrerer Verbindungen behandelt werden, die in reinem Zustande Lösungsmittel oder Ouelluiigsmittel oder Lösuti(ys=:tindOuellungsmittel für Superpolyamide sind, größere Mengen Wasser aus der Lösung oder Suspension der Lösungs- oder Ouellungsmittel aufnehmen. Wenn man diese Behandlung ausfülirt, bevor die Gebilde aus Superpolyamiden in das Zinnchloridbad eingeführt werden, nehmen die Gebilde eine viel größere .Menge dieses Bades und infolgedessen auch ,des Zinnsalzes auf. Man hydrolysiert_ dieses Zinnsalz durch Waschen mit Wasser und fixiert durch Hindurchführung durch ein Dinatriumphosphatbad. Man kann diese Fixierung erleichtern, indem man die Gebilde vorher nochmals in dem Quellungsbade behandelt, «-odurch eine gute Durchdringung der Faser durch die Dinatriumphosphatlösung ermöglicht wird. Erforderlichenfalls kann inan, wie bei Seide, diese Behandlungen durch ein Hindurchführen der Gebilde durch ein Natriumsilicatbad abschließen. Man erreicht so, daß auf den Fasern oder Geweben aus Superpolvaniiden Erschwerungen aus Zinnsilicophosphat niedergeschlagen werden, die bis zu i o Gewichtsprozent der behandelten Ware betragen.It is known that the structure of superpolyainides, if these with an aqueous solution or an aqueous emulsion of one or more Compounds are treated which, in their pure state, are solvents or oils or solvent (ys =: they are swelling agents for super polyamides, larger amounts of water take up from the solution or suspension of the solvent or source agent. if this treatment is carried out before the superpolyamide structures are placed in the tin chloride bath are introduced, the structures take up a much larger amount of this bath and as a result, too, the tin salt on. This tin salt is hydrolyzed through Wash with water and fixed by passing through a disodium phosphate bath. This fixation can be facilitated by first repeating the structure in the Swelling bath treated, "by a good penetration of the fibers by the disodium phosphate solution is made possible. If necessary, as with silk, these treatments can be used complete by passing the structures through a sodium silicate bath. Man achieved so that aggravations on the fibers or fabrics made of Superpolvaniiden from tin silicophosphate are precipitated, which is up to i o weight percent of the treated goods.
Eine Ausführungsform, durch «-elche die Erzielung von noch größeren Erschwerungsausbeuten ermöglicht wird, besteht darin, die Quellungsbehandlung gleichzeitig mit' den eigentlichen Erschwerungsbehandlungen durchzuführen. Man gibt dem Zinnchloridbade das Quellungsmittel zu, welches so eine sehr gatte Durchdringung des Superpolyamids Jürch die Salzlösung ermöglicht. Die nachfolgende Behandlung mit dem Phosphatbade kann ohne Otiellung oder, wie bereits erwälnit, mit vorangehender Ouellung oder auch mit Zugabe des Ouellungsmittels zu dem Bade erfolgen. 11an erreicht durch dieses Verfahren, daß das Superpolyamid mit Erschwerungsmitteln in Mengen von 2o bis 25 °o seiiies Gewichtes beladen wird.An embodiment through which the achievement of even greater ones Aggravating yields is made possible by the swelling treatment at the same time with 'to carry out the actual aggravation treatments. One gives the tin chloride bath the swelling agent to which such a very smooth penetration of the superpolyamide Jürch enables the saline solution. The subsequent treatment with the phosphate bath can be used without qualification or, as already mentioned, with a preceding reference or can also be done with the addition of the oiling agent to the bath. 11an achieved through this Method that the superpolyamide with weighting agents in amounts of 2o to 25 ° o is loaded by its own weight.
Als Ouellungsrnittel können viele Stoffe verwendet «-erden, z. B. Phenole, Säuren, Amine und Alkohole. Unter diesen Verbinciungen haben die folgenden sehr gute Ergebnisse gezeigt: Phenol, Metakresol, Ameisensaure, Benzolsulfonsäure, Glycerindiclilorlit-drin, Anilin, Schwefelsäure. Wenn diese Verbindungen mit den Bestandteilen des Erschwerungsbades nicht verträglich sind, kann man sie nur als Mittel zur vorausgehenden Quellung benutzen. Die anderen Verbindungen können dagegen unmittelbar in die Er-s chwerungsbäder eingegeben werden.Many substances can be used as source agents, e.g. B. phenols, acids, amines and alcohols. Among these compounds the following have shown very good results: phenol, metacresol, formic acid, benzenesulphonic acid, glycerol diclilorlitin, aniline, sulfuric acid. If these compounds are not compatible with the constituents of the aggravation bath, they can only be used as a preliminary swelling agent. The other compounds, however, can be entered directly into the ER s chwerungsbäder.
Die Konzentration der Quellungsbäder oder der Quellungsmittel in den Erschwerungs-Bädern ist von dem nuellungsvermögen der verschiedenen verwendeten Verbindungen abliängig. Außerdem kann man, indem man die Menget der Quellungsinittel verändert. auch die Menge der auf denGebilden niedergeschlagenen Erschw erungsmittel ändern. 'Man kann «, indem man nur eine einzige Reihe von Ersrhwerungsbädern verwendet, verschiedene Erschwerungsausbeuten bewirken. Selbstverständlich kann man, wie bei Seide.The concentration of the swelling baths or the swelling agents in the Aggravation baths are different from the soaking power of the various ones used Connections dependent. In addition, by changing the amount of the swelling agent changes. also the amount of exacerbations deposited on the buildings change. 'You can', by using just a single row of boost baths, cause different aggravation yields. Of course you can, as with Silk.
die Erschwerungsbehandlungen wiederholen, indem man entweder die Behandlung mit Zinnchlorid oder _ die Behandlung mit 1)inatriumphosphat oder beide Behandlungen wiederholt. Man kann so nach mehreren Durchgängen Erschwerungen bis zu ioo °;" und mehr des ursprünglichen Gewichtes der Gebilde aus Superpolyamiden erhalten.Repeat the aggravation treatments by either stopping the treatment with tin chloride or _ treatment with 1) disodium phosphate or both treatments repeated. In this way, after several rounds, difficulties of up to 100 °; "and retained more of the original weight of the superpolyamide structures.
1)as Verfahren ist von großer Bedeutung, weil es ermöglicht, auf einen Faden Erschwerungen niederzuschlagen, die bedeutend sind, ohne daß die physikalischen Eigenschaften des Fadens beeinträchtigt werden. Die Widerstandsfähigkeit und die Dehnbarkeit «-erden mir wenig oder überhaupt nicht geändert, so daß es ermöglicht wird, den Faden einem Wirk- oder Webvorgang und ohne jede Schwierigkeit allen Textilbehandlungen zu unterwerfen.1) The procedure is of great importance because it allows you to Thread to knock down aggravations that are significant without affecting the physical Properties of the thread are impaired. The resilience and the Extensibility "is changed little or not at all, so that it makes it possible becomes, the thread a knitting or weaving process and without any difficulty all textile treatments to subjugate.
Das vorliegende Verfahren bringt noch andere Vorteile mit sich. Es ist bekannt, daß Fäden oder Gewebe aus Superpolyamiden mit fast allen Farbstoffklassen gefärbt werden können, z. B. mit basischen und sauren Farbstoffen, Entwicklungsfarbstoffen oder Acetatkunstseidefarbstoffen. Indessen ziehen einzelne Farbstoffe weniger gut auf die Faser als andere. Die erschwerten Gebilde aus Superpolyamiden besitzen nun eine verbesserte Aufnahmefähigkeit für Säure-, Direkt-, Acetatkunstseide- und Iüipenfarbstoffe, Einfarben- und Chromfarbstoffe. Der erschwerte Faden ist auch weniger empfindlich gegenüber der Einwirkung von Wärme unter bestimmten Bedingungen, z. B. unter der Einwirkung des Bügeleisens. Beispiel r .Man behandelt Strähnen von Fäden aus Superpolyamiden -.s Stunden bei 2o° in einem Bade, das aus wässeriger Zinnchloridlösung von 3o° 8e besteht, die 2o °;o Ameisensäure enthält. Man wäscht sodann in hartem Wasser, wodurch das Zinnsalz hydrolysiert wird. Man verwandelt das gefällte Hydrat durch Behandlung in einer wässerigen Lösung von 150 - Dinatriurnphosphat im Liter während 15 bis 2o Minuten bei 70° in Zinnphosphat. 14an wiederholt diese Behandlungen fünfmal und gibt schließlich die Strähnen i Stunde in ein Bad von Natriumsilicat von 2° Be bei 4o°. Die Strähnen zeigen eine Gewichtsvermehrung um 8o °/o ihres ursprünglichen Gewichts.The present method has other advantages as well. It is known that threads or fabrics made of superpolyamides can be dyed with almost all classes of dyes, e.g. B. with basic and acidic dyes, developing dyes or acetate rayon dyes. However, some dyes are less well absorbed by the fibers than others. The more difficult structures made of super polyamides now have an improved absorption capacity for acid, direct, acetate rayon and Iüipen dyes, monochrome and chrome dyes. The aggravated thread is also less sensitive to the action of heat under certain conditions, e.g. B. under the action of the iron. Example r. Strands of threads made of superpolyamides are treated for -.s hours at 20 ° in a bath consisting of an aqueous tin chloride solution of 30 ° 8e which contains 20 °; o formic acid. It is then washed in hard water, which hydrolyzes the tin salt. The precipitated hydrate is converted into tin phosphate by treatment in an aqueous solution of 150 - disodium phosphate per liter for 15 to 20 minutes at 70 °. He repeats these treatments five times and finally places the tresses in a bath of sodium silicate of 2 ° Be at 40 ° for one hour. The tresses show an increase in weight of 80% of their original weight.
Beispiel 2 Man behandelt ein Taftgewebe aus Superpolyamiden in einem Zinnchloridbade von 30° Be, das 2 °%o Phenol enthält, 2 Stunden bei 2o°. Man wäscht und führt dann in ein Bad von 15o g/Liter Dinatriumphosphat während 15 bis 2o Minuten bei 70°. Schließlich gibt man in ein Bad von Natriumsilicat 2° Be bei 4o° während 1 Stunde. Das so behandelte Gewebe erhält eine Gewichtsvermehrung von 21 °/o. Sein Griff ist bedeutend besser als vorher, und es hat einen ausgezeichneten Fall. Beispiel 3 Man behandelt einen Satin aus Superpolyamiden in einem Zinnchloridbade von 2o° he, das 2,'1', Phenol enthält, 2 Stunden bei 20°. Man wäscht und gibt dann in ein Dinatriumphosphatbad von 150 g/Liter während 15 bis 2o Minuten bei 70°. Man wiederholt diese Behandlung im ganzen dreimal. Sodann gibt man schließlich in ein Natriumsilicatbad von 2° Be bei q.0° während 1 Stunde. Nach Trocknung wiegt das Gewebe 8o g[m2, während es vor der Behandlung nur 59 9/m2 wog, so daß es also eine Erschwerung vor- 36 % besitzt.EXAMPLE 2 A taffeta fabric made of superpolyamides is treated in a tin chloride bath of 30 ° Be which contains 2% phenol for 2 hours at 20 °. It is washed and then introduced into a bath of 150 g / liter disodium phosphate for 15 to 20 minutes at 70 °. Finally, 2 ° Be are placed in a bath of sodium silicate at 40 ° for 1 hour. The fabric treated in this way has a weight increase of 21%. Its grip is significantly better than before and it has an excellent drape. EXAMPLE 3 A satin made of superpolyamides is treated in a tin chloride bath of 20 ° he which contains 2, '1', phenol, for 2 hours at 20 °. It is washed and then placed in a 150 g / liter disodium phosphate bath for 15 to 20 minutes at 70 °. This treatment is repeated three times in all. Then it is finally placed in a sodium silicate bath of 2 ° Be at q.0 ° for 1 hour. After drying, the fabric weighs 80 g [m2, while before the treatment it weighed only 59 9 / m2, so that it has a difficulty of 36 % .
Claims (3)