DE7413718U - Cement-bonded multilayer chipboard - Google Patents
Cement-bonded multilayer chipboardInfo
- Publication number
- DE7413718U DE7413718U DE7413718U DE7413718DU DE7413718U DE 7413718 U DE7413718 U DE 7413718U DE 7413718 U DE7413718 U DE 7413718U DE 7413718D U DE7413718D U DE 7413718DU DE 7413718 U DE7413718 U DE 7413718U
- Authority
- DE
- Germany
- Prior art keywords
- cement
- weight
- parts
- chipboard
- bonded multilayer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Deutsche Novopan Gesellschaft mbH, 3400 Göttingen, Industriestraße 1Deutsche Novopan Gesellschaft mbH, 3400 Göttingen, Industriestraße 1
Zementgebundene mehrschichtige HolzspanplatteCement-bonded multilayer chipboard
Die Neuerung betrifft eine zementgebundene mehrschichtige Holzspanplatte aus Holzspänen und Magnesiazement.The innovation concerns a cement-bonded multilayer Chipboard made from wood chips and magnesia cement.
Für das Bauwesen werden Plattenwerkstoffe benötigt, die folgende Eigenschaften haben sollen:Panel materials are required for construction, the following Should have:
gute Festigkeit, geringe Bruchempfindlichkeit, einfache Bearbeitbarkeit j geringe Quellneigung unter Wa^sereinwirkung sowie Schwerentflammbarkeit oder besser Nichtbrennbarkeit.good strength, low susceptibility to breakage, easy machinability j low tendency to swell under the action of water as well as flame retardancy or better non-combustibility.
Die bekannten kunstharzgebundenen Holzspanplatten weisen bei geringer Bruchempfindlichkeit gute Festigkeiten auf, jedoch quellen sie stark unter Wassereinwirkung. Ihre Brennbarkeit verhindert zahlreiche Anwendungen, bei denen schwerentflammbare oder nichtbrennbare Baustoffe durch die Baubehörden vorgeschrieben sind.The well-known synthetic resin-bonded wood chipboards have good strengths with low susceptibility to breakage, however, they swell strongly when exposed to water. Your flammability prevents numerous applications in which flame-retardant or non-combustible building materials are used by the building authorities are prescribed.
Neben den Holzspanplatten werden im Bauwesen Gipskarton— platten verwendet, die zwar im Brandverhalten besser als die Spanplatten sind, deren Nachteil darin besteht, daß sie bruchempfindlich sind. Auch ihre Beständigkeit gegen Feuchteeinwirkung ist cering.In addition to chipboard, gypsum plasterboard is used in the building industry, although its fire behavior is better than which are chipboard, the disadvantage of which is that they are fragile. Also their resistance to The effect of moisture is cering.
Außer Holzspanplatten und Gipskartonplatten verwendet man auch Hol!>,woliv2platten, die mit Magnesia- oder Portlandzement gebunden sind. Diese nach dem sogenannten Heraklitverfahren hergestellten Platten verfügen über ein spezifisches Gewicht von 0,45 bis 0,55 g/cm . Diese spezifisch leichten Holzwolle-Zement-Platten besitzen nur eine geringe Biegefestigkeit von etwa 10 bis 20 kp/cm'"o In addition to chipboard and plasterboard, Hol!>, Woliv2 panels are also used, which are bound with magnesia or portland cement. These plates, manufactured using the so-called Heraklit method, have a specific weight of 0.45 to 0.55 g / cm. These specifically light wood wool cement panels have only a low flexural strength of about 10 to 20 kp / cm '" o
741371I2U.7*741371I2U.7 *
Weiter werden im Bauwesen Platten aus Hobelspänen verwendet, die mit Portlandzement gebunden sind. Diese nach dem sogenannten Durisolverfahren hergestellten Platten verfügen überBoards made from wood shavings bound with Portland cement are also used in construction. This after the so-called Panels manufactured using the Durisol process have
2 Biegefestigkeiten von 30 bis CO kp/cir. , bei einem spezifischen Gev.'XCht von 0-,H V>j «=. 0.9 n/cm * Die Biegefestigkeiten der ze— mentgebundenen Holzwolle- und Hobelspanplatten sind für die Anforderungen im Bauwesen oft unzureichend. Ihre rauhe und offenporige Oberfläche erschwert außerdem eine dekorative Gestaltung der Oberfläche.2 flexural strengths from 30 to CO kp / cir. , at a specific Gev.'XCht from 0-, H V> j «=. 0.9 n / cm * The flexural strengths of the ze- Mement-bonded wood wool and chipboard are often inadequate for the requirements in the building industry. Your rough and Open-pored surface also makes decorative design of the surface difficult.
Die Neuerung besteht in einem magnesiazementgebundenen Werkstoff, der bei glatten, geschlossenen Oberflächen über eine hohe Biegefestigkeit von 150 bis 200 kp/cm verfügt, unter Feuchteeinwirkung wenig quillt und durch seinen hohen mineralischen Anteil mindestens schwerentflammbar ist. Der verwendete Magnesiazement ist ein Gemisch aus Magnesiumoxid (MgO) und Magnesiumchlorid (MgCl2) im Gewichtsverhältnis von 7 ; 1 bis 2 :1* Das Magnesiumchlorid kann auch durch Magnesiumsulfat (MgSO4) ersetzt werden. Das Magnesiumoxid wird durch schonendes Brennen von Magnesit (MgCO,) erhalten. Die Brenntemperatur darf 800 ° nicht überschreiten. Derart erzeugtes Magnesiumoxid wird auch kaustische Magnesia genannt.The innovation consists of a magnesia cement-bound material, which has a high flexural strength of 150 to 200 kp / cm on smooth, closed surfaces, swells little when exposed to moisture and is at least flame retardant due to its high mineral content. The magnesia cement used is a mixture of magnesium oxide (MgO) and magnesium chloride (MgCl 2 ) in a weight ratio of 7; 1 to 2: 1 * The magnesium chloride can also be replaced by magnesium sulfate (MgSO 4 ). The magnesium oxide is obtained by gently burning magnesite (MgCO,). The firing temperature must not exceed 800 °. Magnesium oxide produced in this way is also called caustic magnesia.
Die Oberflächen derartiger Platten sind noch glatter und geschlossener, wenn der Magnesiazement Füllstoffe, wie Tonmehl oder Kieselgur, in Gewichtsanteilen von 10 % bis 30 % enthält.The surfaces of such panels are even smoother and more closed if the magnesia cement contains fillers, such as powdered clay or kieselguhr, in proportions by weight of 10 % to 30 % .
Die Vorteile der erfindungsgemäßen zementgebundenen, mehrschichtigen Holzspanplatte sind hauptsächlich darin zu sehen, daß sie einen für das Bauwesen gut geeigneten neuen Plattenwerkstoff darstellen, der infolge seiner hohen Festigkeit tragend und aussteifend eingesetzt werden kann.The advantages of the cement-bonded, multilayered according to the invention Chipboard is mainly to be seen in the fact that it is a new board material that is well suited for the building industry represent, which can be used load-bearing and stiffening due to its high strength.
74137HIM.7*74137HIM.7 *
> ι ■> ι ■
1 ι ι 1 ι ι
1 t · 1 t
Die geschlossene, glatte Oberfläche erleichtert eine dekorative Gestaltung durch Beklebung mit Tapeten, Aufbringen von Anstrichen oder Beschichtungsmaterialien wie Purnieren, Schichtstoffen oder Folien.The closed, smooth surface facilitates a decorative design by pasting with wallpaper, applying of paints or coating materials such as veneers, Laminates or foils.
Der hohe mineralische Anteil der Platten - besonders in den Deckschichten - verhindert die Entflammbarkeit bei Feuereinwirkung·The high mineral content of the panels - especially in the top layers - prevents flammability in Exposure to fire
Ein Ausführungsbeispiel der Neuerung ist in der Zeichnung dargestellt und wird im Folgenden näher beschrieben. Es zeigt:An embodiment of the innovation is shown in the drawing and is described in more detail below. It shows:
Fig. 1 eine dreischichtige Holzspanplatte mit Magnesiazementbindung, mit einem spezifischen Gewicht von 1,1 g/cm . Die Mittelschicht 1 besteht aus gröberen Spänen in den Abmessungen 5 bis 20 mm Länge, 2 bis 4 mm Breite und 0,5 bis 2 mm Dicke. Sie enthält 40 Gewichtsteile Holz und 60 Gewichtsteile Magnesiazement der zu 70 Gewichtsteilen aus MgO und MgCl2 und zu 30 Gewichtsteilen aus Kieselgur besteht.1 shows a three-layer chipboard with magnesia cement bond, with a specific weight of 1.1 g / cm. The middle layer 1 consists of coarser chips measuring 5 to 20 mm in length, 2 to 4 mm in width and 0.5 to 2 mm in thickness. It contains 40 parts by weight of wood and 60 parts by weight of magnesia cement, 70 parts by weight of MgO and MgCl 2 and 30 parts by weight of kieselguhr.
Die Deckschichten 2 bestehen aus feineren Spänen in den Abmessungen 2 bis 10 mm Länge, 1 bis 4 mm Breite und 0,1 bis 0,8 mm Dicke. Sie enthalten 20 Gewichtsteile Holz und 80 Gewichtsteile Magnesiazement, der zu 70 Teilen aus einem Gemisch von MgO und MgCl2 und zu 30 Teilen aus Tonmehl besteht.The cover layers 2 consist of finer chips measuring 2 to 10 mm in length, 1 to 4 mm in width and 0.1 to 0.8 mm in thickness. They contain 20 parts by weight of wood and 80 parts by weight of magnesia cement, 70 parts of which consists of a mixture of MgO and MgCl 2 and 30 parts of powdered clay.
Claims (2)