DE707320C - Matting of cellulose hydrate fiber material - Google Patents
Matting of cellulose hydrate fiber materialInfo
- Publication number
- DE707320C DE707320C DEI55480D DEI0055480D DE707320C DE 707320 C DE707320 C DE 707320C DE I55480 D DEI55480 D DE I55480D DE I0055480 D DEI0055480 D DE I0055480D DE 707320 C DE707320 C DE 707320C
- Authority
- DE
- Germany
- Prior art keywords
- matting
- cellulose hydrate
- fiber material
- molecular weight
- higher molecular
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Mattieren von Cellulosehydratfasergut Das Patent 685 765 betrifft ein Verfahren zum Mattieren von Cellulosehydratkunstseide, nach dem man in der Faser farblose, unlösliche Stannate erzeugt.Matting of hydrate cellulose fiber material. Patent 685,765 relates to a process for matting cellulose hydrate rayon, after which one in the fiber colorless, insoluble stannates are produced.
Es wurde nun gefunden, daß man Cellulosehydratfasergut in besonders vorteilhafter Weise auch dadurch mattieren kann, daß man dasselbe mit wässerigen Lösungen von Alkalistannaten und Salzen von höhenmolekularen organischen, basisch wirkenden Verbindungen behandelt. Geeignete basisch wirkende Verbindungen der genannten Art sind insbesondere solche, -die einen aliphatischen oder gemischt-aliphatisch-aromatischen Rest enthalten, ferner höhenmolekulare Polyamine oder Fettsäureamide von Polyaminen. Beispielsweise kommen in Betracht Octylamin, Dodecylämin, Cetylmethylamin, Octodecylamin, Octodecyläthanolamin, Oleylamin, Montanylamin, Albietinylamin, Octodecyläthylendiami.n, Gemische von Aminen, deren Alkylreste denen der Kokosfettsäuren entsprechen, das Stearinsäureamid des Triäthylentetramins sowie quaternäre Ammonium-verbindungen, quaternäre. Phosphonium-oder ternäre Sulfoniumverbindungen, wie Octodecyltrimethylammoniumhydroxyd, Cetyltrimethylphosphoniumhydroxyd oder Oleyldiäthylsulfoniumhydroxyd.It has now been found that cellulose hydrate fiber is particularly good Advantageously, it can also be used to mattify the same with watery Solutions of alkali stannates and salts of higher molecular weight organic, basic acting compounds treated. Suitable basic compounds of those mentioned Type are in particular those -the one aliphatic or mixed-aliphatic-aromatic Contain the remainder, also higher molecular weight polyamines or fatty acid amides of polyamines. For example, octylamine, dodecylamine, cetylmethylamine, octodecylamine, Octodecylethanolamine, oleylamine, montanylamine, albietinylamine, Octodecyläthylendiami.n, Mixtures of amines whose alkyl radicals correspond to those of coconut fatty acids, the Stearic acid amide of triethylenetetramine and quaternary ammonium compounds, quaternary. Phosphonium or ternary sulfonium compounds, such as octodecyltrimethylammonium hydroxide, Cetyltrimethylphosphonium hydroxide or oleyl diethylsulfonium hydroxide.
Das Verfahren wird beispielsweise ausgeführt, indem man Cellulosehydratfasergut z: B. in Form von Bändern, Fäden, Geweben oder Wirkwaren zunächst mit einer wässerigen Alkalistannatlösung etwa io bis 6o Minuten lang vorteilhaft zwischen 4o bis 6o° behandelt und hierauf, allenfalls nach vorherigem Abquetschen oder Schleudern, in ein zweites Bad einbringt, das ein Salz der genannten höhenmolekularen basisch wirkenden Verbindungen gelöst enthält. Das Cellulosehydratfasergut wird dann bei nicht zu hoher Temperatur getrocknet; es besitzt nun ein gutes, mattes Aussehen. Man kann auch zuerst das Cellulosehydratfasergut mit der Lösung 'des Salzes einer der obigen, basisch wirkenden organischen Verbindungen behandeln und dann in einem zweiten Bade das Alkalistannat zur Einwirkung bringen.The method is carried out, for example, by cellulose hydrate fiber material e.g. in the form of ribbons, threads, fabrics or knitted goods initially with an aqueous one Alkali stannate solution for about 10 to 60 minutes, advantageously between 40 and 60 ° treated and then, if necessary after previous squeezing or centrifuging, in brings in a second bath containing a salt of the higher molecular weight mentioned, which acts as a base Contains dissolved compounds. The cellulose hydrate fiber material is then not too high temperature dried; it now has a good, matte appearance. One can also first the cellulose hydrate fiber with the solution of the salt of one of the above, Treat basic organic compounds and then in a second bath bring the alkali stannate to action.
Es ist vorteilhaft, einem oder beiden- Behandlungsbädern Schutzkolloide oder Dispergiermittel zuzusetzen; ferner empfiehlt es sich, zum Spülen des behandelten Gutes gewöhnliches hartes Wasser, dem außerdem noch Calcium-, Barium- oder Magnesiumsalze zugesetzt sein können, zu verwenden; hierdurch wird die Wirkung noch gesteigert. Den Behandlungsbädern können noch weitere für das Mattieren geeignete Stoffe zugesetzt werden, z. B. hochmolekulare oder hochpolymere synthetische oder natürliche Stoffe oder farblose oder farbige anorganische Pigmente sowie Lösungsmittel oder Formaldehyd.It is advantageous to use protective colloids in one or both treatment baths or to add dispersants; It is also recommended to rinse the treated Good ordinary hard water with calcium, barium or magnesium salts added can be to use; this increases the effect. The treatment baths other substances suitable for matting can also be added, e.g. B. high molecular weight or high polymer synthetic or natural substances or colorless or colored inorganic pigments as well as solvents or formaldehyde.
Die Mattierung kann auch in einem einzigen Bade durchgeführt werden. Dabei arbeitet man am besten unter Zusatz von Verteilungsmitteln und unter Verwendung von Schutzkolloiden. Die Schutzkolloide sollen ein vorzeitiges Ausfallen des entstehenden Umsetzungserzeugnisses aus den Stannaten und den Basen verhindern, sie dürfen aber andererseits nicht so stark wirken, daß sie die Mattierung beeinträchtigen. Solche Schutzkolloide sind beispielsweise die Einwirkungserzeugnisse größerer Mengen Äthylenoxyd auf organische Verbindungen, .die eine oder mehrere umsetzungsfähige Oxy-, Carboxyl-, Amino- oder Merkaptogrupp-en enthalten, insbesondere höhermolekulare aliphatische oder aromatische Verbindungen, z. B. Fettalkohole, Phellole, Fettsäuren, höhermolekulare aliphatische Amine sowie Kasein. Auch lassen sich für das vorliegende Verfahren geeignete unmittelbar gebrauchsfertige Mischungen herstellen, indem man z. B. die Alkalistannate zusammen mit Salzen der erwähnten höhermolekularen organischen, basisch wirkenden Verbindungen mit Schutzkolloiden vermahlt. Beim Eintragen in Wasser erhält man unmittelbar gebrauchsfertige Mattierungsbäder.The matting can also be carried out in a single bath. It is best to work with the addition of distributing agents and using them of protective colloids. The protective colloids are intended to prevent premature precipitation of the resulting Prevent the reaction product from the stannates and the bases, but they are allowed to on the other hand do not act so strongly that they impair the matting. Such Protective colloids are, for example, the products of the action of larger amounts of ethylene oxide to organic compounds that contain one or more reactive oxy, carboxyl, Contain amino or mercapto groups, in particular higher molecular weight aliphatic or aromatic compounds, e.g. B. fatty alcohols, phellols, fatty acids, higher molecular weight aliphatic amines and casein. Can also be used for the present process Prepare suitable ready-to-use mixtures by z. B. the Alkali stannates together with salts of the mentioned higher molecular organic, basic active compounds ground with protective colloids. Receives when submerged in water ready-to-use matting baths.
Die Behandlung des zu mattierenden Gutes kann man auf dem Foulard durch Klotzen, auf der Haspel oder durch Aufspritzen vornehmen.The material to be matted can be treated on the foulard by padding, on the reel or by spraying.
Man hat schon vorgeschlagen, Lösungen von Gerbsäure oder Tannin zusammen mit Abkömmlingen tertiärer Amine,. die wenigstens einen Rest mit mindestens 6 Kohlenstoffatomen enthalten, iütti Mattieren von Kunstseide zu verwenden; jedoch verursacht dabei die Anwesenheit von Eisensalzen Verfärbungen. Die ferner schon vorgeschlagene Anwendung von Adsorptionsverbindungen aus Pigmenten und neutralen Verbindungen aus kationaktiven und anionaktiven Stoffen wirkt nachteilig beim Färben .mit substantiven Farbstoffen, denn es entstehen Veränderungen im Farbton, und die Lichtechtheit der Färbungen wird beeinträchtigt. Man hat weiter schon zum Mattieren von Kunstseide auf diese wasserunlösliche Umsetzungsprodukte aus Harzsäuren und kationaktiven Stoffen aufgebracht, und in dem Fasergut Metallseifen von Harzsäuren erzeugt; doch treten hierbei nicht nur die bei dem vorher genannten Verfahren erwähnten Nachteile auf, sondern die Seide erhält auch einen unangenehmen harten Griff. Alle diese unerwünschten Erscheinungen werden durch die vorliegende Erfindung vermieden. Die Mattierungen sind sehr gleichmäßig, waschecht, stäuben nicht, verleihen dem Gewebe einen sehr angenehmen weichen Griff u1Ld verursachen keine Änderungen des Farbtons beim Färben mit substantiven Farbstoffen. Im Vergleich zu dem bekannten Mattieren durch Erzeugen -unlöslicher, anorganischer Stannate in der Faser bietet das neue Verfahren den Vorteil, daß die dort mitunter zu beobachtende Fleckenbildung nicht eintritt und daß es ein weicheres Mattierungserzeugnis ergibt.It has already been suggested to combine solutions of tannic acid or tannin with derivatives of tertiary amines. the at least one radical having at least 6 carbon atoms included using iütti matting of rayon; however caused thereby the presence of iron salts discoloration. The application already proposed of adsorption compounds from pigments and neutral compounds from cation-active ones and anion-active substances have a detrimental effect on dyeing. with substantive dyes, because there are changes in the color tone and the lightfastness of the colorations is affected. You have further to matt artificial silk on this water-insoluble reaction products of resin acids and cation-active substances applied, and produces metallic soaps from resin acids in the fiber material; but do not step here only the disadvantages mentioned in the aforementioned method, but the Silk also gets an uncomfortable hard feel. All of these undesirable phenomena are avoided by the present invention. The matting is very even, washable, do not dust, give the fabric a very pleasant soft feel u1Ld do not cause any change in hue when dyeing with substantive dyes. Compared to the well-known matting by creating insoluble, inorganic ones Stannate in the fiber, the new process offers the advantage that the there sometimes the observed staining does not occur and that it is a softer matting product results.
Beispiel i Ein Cellulosehydratkunstsei.dengewebe oder Strangware wird 1J4 Stunde lang bei etwa 45° in einem wässerigen Bad behandelt, das je Liter io g Natriumstannat enthält. Das Gewebe wird dann abgequetscht und in einem wässerigen Bad, däs je Liter 3 g Octodecylaminacetat enthält, io Minuten lang bei gewöhnlicher Temperatur behandelt und hierauf getrocknet. Man erhält eine sehr gute Mattierung, die auch einer nachträglichen Wäsche bei 3o bis 4o° in einem Bad, das je Liter etwa 3 g Seife enthält, weitgehend standhält. Der Griff der mattierten Kunstseide ist besonders weich und geschmeidig.Example i A cellulose hydrate synthetic fabric or knitted fabric is made Treated for 14 hours at about 45 ° in an aqueous bath, which per liter io contains g sodium stannate. The tissue is then squeezed off and placed in an aqueous Bath containing 3 g of octodecylamine acetate per liter, for 10 minutes with a normal one Treated temperature and then dried. A very good matt finish is obtained, also a subsequent wash at 3o to 4o ° in a bath, which is about per liter Contains 3 g of soap, largely withstands. The handle is made of frosted rayon particularly soft and supple.
Beispiel 2 Ein schwarz gefärbtes Viscosekunstseidengewebe wird 1/= Stunde lang in einem wässerigen Bad behandelt, das je Liter 5 g Natriumstannat, 1,5 g des Einwirkungserzeugnisses von etwa $o Mol Äthylenoxyd auf = Mol Oleylalkohol und 3 g Octodecylaminacetat enthält. Nach dem Trocknen erhält man eine gut und sehr gleichmäßig mattierte Kunstseide von sehr weichem, geschmeidigem Griff. Man kann das Gewebe auch klotzen, wobei man dem Bad zweckmäßig größere Mengen der einzelnen Bestandteile zusetzt. Eine besonders gute Mattierung erhält man, Wenn man zum Spülen hartes Wasser anwendet.Example 2 A viscose rayon fabric dyed black becomes 1 / = Treated for one hour in an aqueous bath containing 5 g of sodium stannate per liter, 1.5 g of the product to act from about $ o mole of ethylene oxide to = mole of oleyl alcohol and contains 3 g of octodecylamine acetate. After drying, you get a good and very evenly matted artificial silk with a very soft, supple handle. One can The fabric also padded, with the bath expediently larger amounts of each Adding ingredients. A particularly good matt finish is obtained when you go to rinse applies hard water.
Beispiel 3 Eine wässerige Lösung aus 2,5 Gewichtsteilen Octodecylaminacetat und 1,5 Gewichtsteilen des Einwirkungserzeugnisses von 6o Mol Äthylenoxyd auf i Mol Octodecylalkohol wird zur Trockne eingedampft und das Erzeugnis mit 2,5 Gewichtsteilen wasserfreiem Glaubersalz und hierauf mit 5 Gewichtsteilen Natriumstannat vermischt. Die iMischung wird dann in einer Kugelmühle gut vermahlen.Example 3 An aqueous solution of 2.5 parts by weight of octodecylamine acetate and 1.5 parts by weight of the product of action of 60 moles of ethylene oxide to i Mol octodecyl alcohol is evaporated to dryness and the product with 2.5 parts by weight anhydrous Glauber's salt and then mixed with 5 parts by weight of sodium stannate. The mixture is then ground well in a ball mill.
Man löst nun in kaltem Wasser je Liter 2o g dieser Mischung und erwärmt die Lösung noch.5 bis io Minuten läng auf etwa 7o°. Behandelt man ein Cellulosehydratkunstseidengewebe in diesem Bad bei etwa 400 1/,, Stunde lang, so erhält man eine gute, gleichmäßige, nichtstäubende Mattierung, die einer Seifenwäsche weitgehend standhält. Das behandelte Gewebe besitzt zudem einen angenehmen weichen Griff.20 g of this mixture are then dissolved in cold water per liter and heated the Solution for another 5 to 10 minutes at about 70 °. Treated one a cellulose hydrate rayon fabric in this bath at about 400 1/2 hour for this gives a good, even, non-dusting matt finish, that of a soap wash largely withstands. The treated fabric is also pleasantly soft Handle.
Claims (1)