DE69731067T2 - Process for the production of building mortar - Google Patents

Process for the production of building mortar Download PDF

Info

Publication number
DE69731067T2
DE69731067T2 DE69731067T DE69731067T DE69731067T2 DE 69731067 T2 DE69731067 T2 DE 69731067T2 DE 69731067 T DE69731067 T DE 69731067T DE 69731067 T DE69731067 T DE 69731067T DE 69731067 T2 DE69731067 T2 DE 69731067T2
Authority
DE
Germany
Prior art keywords
average
mortar
percent
prefabricated parts
slag
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE69731067T
Other languages
German (de)
Other versions
DE69731067D1 (en
Inventor
Joan Maria 44550 Teruel Neira Pous
Maria Concepcion 44500 Teruel Garcia Gonzalez
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Innovaciones Neira Y Garcia Sl Teruel Andorra
Original Assignee
Innovaciones Neira Y Garcia Sl Teruel
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Innovaciones Neira Y Garcia Sl Teruel filed Critical Innovaciones Neira Y Garcia Sl Teruel
Application granted granted Critical
Publication of DE69731067D1 publication Critical patent/DE69731067D1/en
Publication of DE69731067T2 publication Critical patent/DE69731067T2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

A concrete mix for bulk use or for casting prefabricated parts contains a small amount of portland cement and water together with ground slag and fly-ash from coal-burning electricity generation plant, the slag and ash being of controlled particle size ranges and content. The mixture may also contain sand and/or expanded clay and a foaming agent may be incorporated. It is formed into shape in vibrating moulds or by extrusion and left to dry in air for 24 hours. Where the products are to be subjected to thermal treatment the cement may be replaced by sodium silicate. A pre-mix may be initially prepared from sodium silicate slag and ash and granulated, the granules being hardened in an oven before being mixed with cement and further ash and slag.

Description

Die vorliegende Erfindung bezieht sich auf ein Verfahren zum Herstellen vorgefertigter Teile aus Mörtel, wie z.B. Ziegel, Gewölbeteile, Balken, Pflastersteine, Stufen und verschiedene Bautypen, die entweder auf Ton oder Beton basieren, wobei auch deren gemeinsame Benutzung für diverse Elemente möglich ist.The The present invention relates to a method of manufacturing prefabricated parts made of mortar, such as. Bricks, vaulted parts, Beams, paving stones, steps and various types of construction, either based on clay or concrete, including their sharing for various Elements possible is.

Es sind verschiedene auf Ton basierende Teile derzeit bekannt, beispielsweise alle Arten von Ziegeln, Kacheln, Gewölbeteilen, Fliesen usw.; bekannt sind auch zahlreiche vorgefertigte Teile aus Beton, wie z.B. Blocks, Platten, Balken, Pflastersteine usw.It For example, various clay-based parts are currently known all kinds of bricks, tiles, vaulted parts, tiles, etc .; known are also numerous prefabricated concrete parts, such. block Plates, beams, paving stones, etc.

Die vorgefertigten Konstruktionsteile, die aus Ton hergestellt sind, haben den Nachteil ihrer Herstellkosten, weil das Material aus den Lagerstätten entnommen werden und ordnungsgemäß damit umgegangen werden muss, um es zum Formen vorzubereiten, damit das Teil wie programmiert erhalten wird. Einen weiteren sich ergebenden Nachteil stellt der Umweltschaden dar, der durch die Tonlagerstätten erzeugt wird, weil die Aushebungen, die im allgemeinen auf Erdbodenniveau sind, niemals nivelliert und wieder aufgefüllt werden.The prefabricated construction parts made of clay, have the disadvantage of their manufacturing costs, because the material from the deposits be taken out and duly with it must be handled in order to prepare it for molding, so that the Part is received as programmed. Another resulting Disadvantage is the environmental damage caused by the clay deposits because of the uplift, which is generally at ground level are never leveled and refilled.

Was die vorgefertigten Elemente aus Beton angeht, so besteht ihr Hauptnachteil in den hohen Herstellkosten; gleichzeitig ist ihr hoher Gehalt an Zement eine andere Ursache für Umweltschaden, weil das Rohmaterial für die Ausarbeitung von Zement den Steinbrüchen entnommen wird.What The prefabricated elements made of concrete, so there is their main disadvantage in the high production costs; at the same time their high salary is Cement another cause for Environmental damage, because the raw material for the preparation of cement the quarries is removed.

Die DE-A1-28 11 910 beschreibt eine trockene Mörtelmischung, die als Linienführung in Minen benutzt wird.The DE-A1-28 11 910 describes a dry mortar mixture used as a line in Mines is used.

Es ist eine Aufgabe der vorliegenden Erfindung die vorstehend angegebenen Nachteile zu überwinden.It An object of the present invention is as set forth above Overcome disadvantages.

Diese Aufgabe wird durch die Merkmale der Patentansprüche 1 und 6 gelöst. Bevorzugte Ausführungsbeispiele sind in den abhängigen Patentansprüchen angegeben.These The object is solved by the features of claims 1 and 6. preferred embodiments are in the dependent claims specified.

Das Verfahren zum Herstellen vorgefertigten Mörtels, Gegenstand der vorliegenden Erfindung, ist entwickelt worden, damit diese Nachteile überwunden werden, wo nämlich zahlreiche vorgefertigte Teile geformt werden können, die Außenflächen präsentieren können, die etwas rauh oder körnig sind, oder glatt, was davon abhängt, wie sie programmiert werden, wobei das Material aus einer Mischung von anorganischen Festkörpern gefertigt ist, die aus Kohle gewonnene Flugaschen und Schlacken enthalten, die mit einer kleinen Menge Portland-Zement und einem anderen kleinen Anteil Wasser vermischt sind, um eine schnelle Trocknung durch den Zusatz eines härtenden Beschleunigers zu bekommen. Im Fall bestimmter vorgefertigter Teile, die eine thermische Behandlung brauchen, wird eine kleine Menge Natriumsilikat der oben beschriebenen Mischung als Ersatz des Portland-Zement zugegeben, so dass dies zum Gewinnen einer perfekten Homogenisierung aller Komponenten beiträgt. Optional kann auch expandierter Ton und gemeiner Sand in die Formel integriert werden.The Method for producing prefabricated mortar, subject matter of the present Invention, has been developed to overcome these disadvantages, where indeed Numerous prefabricated parts can be molded to present the outer surfaces can, the somewhat rough or grainy are, or smooth, what depends as they are programmed, the material being a mixture of inorganic solids is made of coal-derived fly ash and slag Contain that with a small amount of Portland cement and a other small amount of water are mixed to a quick drying by the addition of a hardening To get accelerator. In the case of certain prefabricated parts, who need a thermal treatment will be a small amount Sodium silicate of the mixture described above as a replacement of Portland cement added, allowing this to achieve a perfect homogenization of all components. Optionally, expanded clay and common sand in the formula to get integrated.

Die offenbarte Erfindung bringt zahlreiche Vorteile vor, von denen einige der relevantesten zitiert werden. Besonders hervorzuheben ist die Tatsache, das bis zu 95% des verwendeten Materials wiederaufbereitetes Material ist, das aus Flugasche und Schlacke der Kohle erhalten wird, die in Elektrizitätswerken verbrannt wird. Dieses Rezyklieren des anorganischen Materials, das von der Kohle stammt, reduziert oder verhindert die Bildung großer Gruben, worin das Material abgelagert wird, und die so schädlich für die Umwelt sind.The The invention disclosed has numerous advantages, some of which the most relevant. Particularly noteworthy is the Fact that recycled up to 95% of the material used Material is that obtained from fly ash and slag of coal that's in power plants is burned. This recycling of the inorganic material, which comes from the coal, reduces or prevents the formation greater Pits, where the material is deposited, and so harmful to the environment are.

Ein anderer wesentlicher Vorteil wird von den Kosten abgeleitet, weil das Hinzusetzen von Zement auf ein Minimum herabgesetzt wird, während die Asche und die Schlacke sogar kostenfrei bekommen werden können, denn die Elektrizitätswerke verbrauchen gegenwärtig bedeutende Geldsummen für das Ablagern der voranstehend erwähnten anorganischen Feststoffe.One Another significant advantage is derived from the cost because the addition of cement is reduced to a minimum while the Ashes and the slag can even be gotten for free, because the power stations currently consume significant sums of money for depositing the above-mentioned inorganic solids.

Ein weiterer wirtschaftlicher Vorteil ergibt sich aus der Tatsache, dass einige Teile, wie z.B. Ziegel, nicht gebrannt werden müssen, und 48 Stunden nach deren Herstellung benutzbar sind.One further economic advantage stems from the fact that some parts, e.g. Bricks, do not need to be fired, and 48 hours after their production are usable.

Ein anderer erhaltener Vorteil liegt in der Formung eines widerstandsfesten und leichtgewichtigen Betons, mit dem entweder durch manuelle Verfahren oder durch Maschinen, Betonmischer usw. umgegangen werden kann.One Another advantage obtained is the formation of a resistance-resistant and lightweight concrete, using either manual methods or by machines, concrete mixers, etc. can be handled.

Schließlich wird als ein weiterer Vorteil erwähnt, dass die auf anorganischen Feststoffen basierende Struktur bessere technische Eigenschaften für die vorgefertigten Teile besorgt, denn sie liefern, wobei sie leichtgewichtiger sind, gleichzeitig eine Widerstandsfähigkeit ab, die höher als diejenige von Teilen aus Ton oder Beton ist.Finally will mentioned as another benefit, that the inorganic solids-based structure is better technical properties for the prefabricated parts worried, because they deliver, being lighter in weight are at the same time a resistance that is higher than that of pieces of clay or concrete.

Zu einem besseren Verständnis des Gegenstands der Erfindung wird ein bevorzugtes praktisches Ausführungsbeispiel in den begleitenden Zeichnungen vorgestellt, in denenTo a better understanding The subject of the invention will become a preferred practical embodiment presented in the accompanying drawings in which

1 ein allgemeines Schaubild des hier vorgestellten Verfahrens zeigt; 1 shows a general diagram of the method presented here;

2 ein optionales Schaubild des hier vorgestellten Verfahrens zeigt. 2 an optional diagram of the method presented here shows.

Das Verfahren zum Herstellen von Mörtel für die Konstruktion wie hier aufgezeigt, beginnt, wie aus den betreffenden Abbildungen ersichtlich ist, mit den anorganischen Feststoffen (1), von denen Flugaschen (2) und Schlacken (3) abgeleitet werden, die Schlacken (3) am Boden zu einem vorbestimmten Größenmaß (4) gehalten werden, so dass sie danach durch Auswahl in eine brauchbare (Nutz-)Schlacke (5) gewandelt werden; andererseits die Flugaschen (2) ebenfalls selektiert werden, so dass sie zu brauchbaren (Nutz-)Flugaschen (6) werden.The method for producing mortar for the construction as shown here begins, as can be seen from the relevant figures, with the inorganic solids ( 1 ), of which fly ash ( 2 ) and slag ( 3 ), the slags ( 3 ) on the ground to a predetermined size ( 4 ) so that they can then be separated by selection into a useful (useful) slag ( 5 ) are converted; on the other hand the flyashes ( 2 ) are also selected so that they become useful (useful) fly ash ( 6 ) become.

Je nach Art der programmierten vorgefertigten Teile, kann der Mörtel (7) aus Flugaschen (6) und Schlacken (5) unterschiedlicher Korngrößen hergestellt werden, mit dem Zusatz einer kleinen Menge Portland-Zement (8) und dem entsprechenden Wasser (9). Falls die zu formenden oder zu gießenden Teile eine thermische Behandlung benötigen, wird dann eine kleine Menge Natriumsilikat (10) dem Mörtel als Ersatz des Portland-Zements zugegeben.Depending on the type of programmed prefabricated parts, the mortar ( 7 ) from fly ashes ( 6 ) and slag ( 5 ) of different grain sizes, with the addition of a small amount of Portland cement ( 8th ) and the corresponding water ( 9 ). If the parts to be molded or cast require a thermal treatment, then a small amount of sodium silicate ( 10 ) added to the mortar as a replacement of the Portland cement.

Sobald der Mörtel (7) erhalten wird, geht er entweder zu Gussformen (11), wo die Teile (12) durch Vibrationen geformt werden oder zu Pressen (13), worin die vorgeformten Teile (14) durch Extrusion erhalten werden.Once the mortar ( 7 ), it either goes to molds ( 11 ), where the parts ( 12 ) are formed by vibration or to press ( 13 ), wherein the preformed parts ( 14 ) are obtained by extrusion.

Ein anderer optionaler Prozess zu Herstellen von Mörtel für die Konstruktion, wie hier offenbart, ist in 2 zu sehen, und beginnt ebenfalls mit den brauchbaren Schlacken (5), den brauchbaren Flugaschen (6), einem kleinen Teil Natriumsilikat (15) und Wasser (16), und durch eine geeignete Homogenisierung, woraus ein Voraus-Mörtel (17) gewonnen wird, der in Körner verschiedener Größe (18) umgewandelt wird, die danach zum Härten im passenden Ofen (19) thermisch behandelt werden, woraus gehärtete Körner (20) entnommen werden.Another optional process for making mortar for the construction, as disclosed herein, is in U.S. Patent Nos. 4,135,355 2 and also starts with the usable slags ( 5 ), the useful fly ash ( 6 ), a small portion of sodium silicate ( 15 ) and water ( 16 ), and by a suitable homogenization, from which a preliminary mortar ( 17 ) obtained in grains of various sizes ( 18 ), which are then hardened in the appropriate oven ( 19 ) are thermally treated, from which hardened grains ( 20 ).

Der optionale Mörtel (21) enthält die zuvor beschriebenen Körner (20), denen Nutzschlacken (5), Flugaschen (6), gemeiner Sand (22), Wasser (16), Portland-Zement (8) und Härtungsbeschleunigerzusatz (23) zugegeben sind. Optional wird für die Bildung von Zellenbeton mit Isolierwirkungen ein gaserzeugender Zusatz (24) von der herkömmlicherweise in der Praxis benutzten Art der zuvor beschriebenen Mischung zugefügt.The optional mortar ( 21 ) contains the previously described grains ( 20 ), which use slags ( 5 ), Fly ash ( 6 ), common sand ( 22 ), Water ( 16 ), Portland Cement ( 8th ) and cure accelerator additive ( 23 ) are added. Optionally, for the formation of cellular concrete with insulating effects, a gas generating additive ( 24 ) from the conventionally used type of the above-described mixture.

Sobald der Mörtel (21) homogenisiert ist, wird er entweder zu einem Sammelplatz (25) geleitet, oder zu den Gussformen (26), welche die fertiggestellten Teile beschaffen.Once the mortar ( 21 ) is homogenized, it is either used as a collection point ( 25 ), or to the molds ( 26 ), which procure the finished parts.

Es können Sulfat-resistente oder Meereswasser-resistente Zemente benutzt werden, wenn es die Zusammensetzung des Rohmaterials oder der Endgebrauch des Mörtels oder der Elemente so erfordert.It can Sulphate-resistant or seawater-resistant cements are used, if it is the composition of the raw material or the end use of the mortar or so requires the elements.

PROZENTUALE ZUSAMMENSETZUNGEN MÖRTEL OHNE THERMISCHE BEHANDLUNG

Figure 00040001
PERCENTUAL COMPOSITION MORTAR WITHOUT THERMAL TREATMENT
Figure 00040001

Optional lässt sich der Härtungsbeschleuniger eliminieren, und die Teile können in einem Umwelt-Trocknungsprozess belassen werden.Optionally, the cure accelerator can be eliminated and the parts can be used in one order world-drying process are left.

MÖRTEL MIT THERMISCHER BEHANDLUNG

Figure 00050001
MORTAR WITH THERMAL TREATMENT
Figure 00050001

GEHÄRTESTES GRANULAT (12)

Figure 00050002
HARDENED GRANULATE (12)
Figure 00050002

MÖRTEL (21) MIT GEHÄRTETEM GRANULAT (20)

Figure 00050003
MORTAR (21) WITH HARDENED GRANULATE (20)
Figure 00050003

Optionale Formeln mit den folgenden Prozentualen Zusammensetzungen können auch benutzt werden.optional Formulas with the following percentage compositions can also to be used.

Figure 00060001
Figure 00060001

Die für jede Formel hinzuzufügende Menge Wasser entspricht dem Bedarf der Maschine, die den Mörtel und seine vorbestimmte Textur homogenisiert.The for every Formula to add Quantity of water meets the needs of the machine, the mortar and homogenizes its predetermined texture.

Der Mörtel im trockenen Zustand, d.h. bevor er mit Wasser geformt wird, eignet sich zum Verpacken und kann transportiert werden, mit der einzigen Vorbeugung, dass er nicht nass werden kann, wie das bei Zementen der Fall ist.Of the mortar in the dry state, i. before being molded with water to packing and can be transported with the only one Prevention that he can not get wet, as with cements the case is.

Unter den zahlreichen Teilen, die sich mit der vorliegenden Erfindung formen lassen, werden die folgenden nur als Beispiele genannt: Einfach- und Doppel- Ziegel, Hohlziegel mit Gitter, Gitter, flache und gebogene Dachziegel; auch möglich ist das Gießen von Blockes, Gewölbeteilen, Balken, Pflastersteinen, Bodenfliesen, Bordsteinen und sonstigen Gussteilen.Under The numerous parts that are involved with the present invention the following are just examples: simple and double brick, hollow brick with grid, grid, flat and curved roof tiles; also possible is the casting of blocks, vaulted parts, Beams, paving stones, floor tiles, curbs and other Castings.

Nachdem die Natur der vorliegenden Erfindung ausreichend beschrieben worden ist, auch ein Weg sie in der Praxis umzusetzen, ist nur hinzuzufügen, dass es möglich ist, die prozentualen Verhältnisse leicht zu variieren, vorausgesetzt, dass diese Änderungen die Natur der Erfindung, wie sie nachstehend beansprucht wird, nicht wesentlich variieren.After this the nature of the present invention has been sufficiently described is also a way to put it into practice, just add that it possible is, the percentage ratios easy to vary, provided that these changes are the nature of the invention, as claimed below, will not vary significantly.

Claims (10)

Verfahren zum Herstellen vorgefertigter Teile aus Mörtel, worin anorganische Feststoffe, die durch Verbrennung von Kohle erhalten wurden, so behandelt werden, dass die Flugaschen nach ihrem passenden Größenmaß ausgewählt werden, die Schlacken am Boden gehalten werden, so dass sie auch ein vorbestimmtes Größenmaß erreichen, so dass sie gemäß den herzustellenden Teilen und in einem angemessenen Verhältnis gemischt werden mit den vorgenannten Flugaschen und mit Portland-Zement oder Natriumsilikat, für die Fälle, wo die Teile thermischer Behandlung und Wasser ausgesetzt werden sollen, des weiteren einen Schritt einschließend, wo der Mörtel zu Formen wandert, wobei die vorgefertigten Teile durch Vibration geformt werden, oder einen alternativen Schritt, wo der Mörtel zu Pressen wandert, worin die vorgefertigten Teile durch Extrusion erhalten werden.Method for producing prefabricated parts made of mortar, wherein inorganic solids obtained by burning coal were to be treated so that the fly ashes fit their own Size dimension to be selected the slags are kept on the ground so that they also reach a predetermined size so that they are made according to the Share and be mixed in a reasonable proportion with the fly ash and Portland cement or sodium silicate, for the Cases where the parts should be exposed to thermal treatment and water, further including a step where the mortar to Forms migrate, with the prefabricated parts formed by vibration be, or an alternative step, where the mortar too Presses migrate, wherein the prefabricated parts by extrusion to be obtained. Verfahren zum Herstellen vorgefertigter Teile aus Mörtel gemäß Patentanspruch 1, dadurch gekennzeichnet, dass die Mischungsverhältnisse für den Mörtel ohne thermische Behandlung umfassen: Bodenschlacke zwischen 70 und 90 Prozent, im Durchschnitt 80 Prozent: Flugaschen zwischen 5 und 20 Prozent, im Durchschnitt 12,5 Prozent; Portland-Zement zwischen 4,5 und 9 Prozent, im Durchschnitt 7 Prozent.Method for producing prefabricated parts mortar according to claim 1, characterized in that the mixing ratios for the mortar without thermal treatment include: Floor slag between 70 and 90 percent, on average 80 percent: Fly ashes between 5 and 20 percent, on average 12.5 percent; Portland cement between 4.5 and 9 percent, on average 7 percent. Verfahren zum Herstellen vorgefertigter Teile aus Mörtel gemäß Patentanspruch 1, dadurch gekennzeichnet, dass das Gemisch für den Mörtel ohne thermische Behandlung umfasst: Härtungsbeschleuniger zwischen 0,2 und 0,8 Prozent, im Durchschnitt 0,5 Prozent.Method for producing prefabricated parts mortar according to claim 1, characterized in that the mixture for the mortar without thermal treatment includes: hardening accelerator between 0.2 and 0.8 percent, on average 0.5 percent. Verfahren zum Herstellen vorgefertigter Teile aus Mörtel gemäß Patentanspruch 1, dadurch gekennzeichnet, dass die Mischungsverhältnisse für den Mörtel mit thermischer Behandlung umfassen: Bodenschlacke zwischen 15 und 30 Prozent, im Durchschnitt 22,5 Prozent; Flugaschen zwischen 65 und 80 Prozent, im Durchschnitt 72,5 Prozent; Natriumsilikat zwischen 2 und 8 Prozent, im Durchschnitt 5 Prozent.Method for producing prefabricated parts mortar according to claim 1, characterized in that the mixing ratios for the mortar with thermal treatment include: Floor slag between 15 and 30 percent, on average 22.5 percent; Fly ash between 65 and 80 percent, on average 72.5 percent; sodium silicate between 2 and 8 percent, on average 5 percent. Verfahren zum Herstellen vorgefertigter Teile aus Mörtel gemäß einem der vorangehenden Patentansprüche, dadurch gekennzeichnet, dass gemeiner Sand und/oder expandierter Ton der Mischung zugesetzt werden.Method for producing prefabricated parts mortar according to one of the preceding claims, characterized in that common sand and / or expanded Clay added to the mixture. Verfahren zum Herstellen vorgefertigter Teile aus Mörtel, worin ein Voraus-Mörtel (17) erhalten wird durch eine geeignete Homogenisierung von Nutzschlacken (5), die den Boden bilden, so dass sie auch ein vorbestimmtes Größenmaß erreichen, Natriumsilikaten (15), und Wasser (16) und optionalen Nutz-Flugaschen (6), die nach ihrem passenden Größenmaß ausgesucht werden, wobei der Voraus-Mörtel in Körner unterschiedlicher Größen (18) umgeformt wird, die danach thermisch zur Aushärtung in einem Ofen (19) behandelt werden, dem gehärtete Körner (20) entnommen werden, des weiteren einen Schritt einschließend, worin die besagten Schlacken (5), Wasser (16), Portland-Zement (8) und Härtungsbeschleunigerzusatz (23), sowie optionale Flugaschen (6), gemeiner Sand (22) den Körnern (20) zugesetzt werden, wodurch Mörtel (21) erhalten wird, einen Schritt einschließend, worin der Mörtel in Formen wandert, worin die vorgefertigten Teile durch Vibration geformt werden, oder einen alternativen Schritt, worin der Mörtel zu Pressen wandert, worin die vorgefertigten Teile durch Extrusion erhalten werden.Method for producing prefabricated parts from mortar, wherein a preliminary mortar ( 17 ) is obtained by a suitable homogenization of useful slags ( 5 ) that form the soil so that they also reach a predetermined size dimension, sodium silicates ( 15 ), and water ( 16 ) and optional fly ash ( 6 ), which are selected according to their appropriate size, whereby the pre-mortar in grains of different sizes ( 18 ), which is then thermally cured in an oven ( 19 ), the hardened grains ( 20 ), further including a step wherein said slags ( 5 ), Water ( 16 ), Portland Cement ( 8th ) and cure accelerator additive ( 23 ), as well as optional fly ash ( 6 ), common sand ( 22 ) the grains ( 20 ), whereby mortar ( 21 ), including a step wherein the mortar migrates into molds wherein the prefabricated parts are formed by vibration or an alternative step wherein the mortar migrates to presses wherein the prefabricated parts are obtained by extrusion. Verfahren zum Herstellen vorgefertigter Teile aus Mörtel gemäß Patentanspruch 6, dadurch gekennzeichnet, dass die Körner enthalten: Nutzschlacke zwischen 15 und 30 Prozent im Durchschnitt 22,5% Flugaschen zwischen 65 und 80% im Durchschnitt 72,5% Natriumsilikat zwischen 2 und 8% im Durchschnitt 5%.Method for producing prefabricated parts mortar according to claim 6, characterized in that the grains contain: Nutzschlacke between 15 and 30 percent on average 22.5% Fly ash between 65 and 80% on average 72.5% Sodium silicate between 2 and 8% on average 5%. Verfahren zum Herstellen vorgefertigter Teile aus Mörtel gemäß Patentanspruch 6, dadurch gekennzeichnet, dass der Mörtel (21) aus dem Voraus-Mörtel (17) in gehärteten Körnern mit Zusatz von Nutzschlacken, Flugaschen, Portlandzement, Natriumsilikat und Zusatzstoffen angefertigt wird, wodurch der besagte Mörtel mit der folgenden prozentualen Zusammensetzung geformt wird: Nutzschlacke zwischen 20 und 39,64% im Durchschnitt 29,83% Flugaschen zwischen 32 und 76,8% im Durchschnitt 54,4% Portlandzement zwischen 5 und 11,84% im Durchschnitt 8,42% Natriumsilikat zwischen 1 und 6% im Durchschnitt 3,5% Gemeiner Sand zwischen 1 und 6% im Durchschnitt 3,5% Zusatzstoffe zwischen 0 und 0,7% im Durchschnitt 0,35%.Method for producing prefabricated parts from mortar according to claim 6, characterized in that the mortar ( 21 ) from the pre-mortar ( 17 ) is prepared in hardened granules with added slag, fly ash, Portland cement, sodium silicate and additives to form said mortar with the following percentage composition: slag between 20 and 39.64% on average 29.83% flyash between 32 and 76 , 8% on average 54.4% Portland cement between 5 and 11.84% on average 8.42% Sodium silicate between 1 and 6% on average 3.5% Common sand between 1 and 6% on average 3.5% additives between 0 and 0.7% on average 0.35%. Verfahren zum Herstellen vorgefertigter Teile aus Mörtel gemäß Patentanspruch 6, dadurch gekennzeichnet, dass die folgende prozentuale Zusammensetzung vorliegt: Nutzschlacke zwischen 50 und 90% im Durchschnitt 70% Flugaschen zwischen 0 und 20% im Durchschnitt 10% Portlandzement zwischen 4 und 25% im Durchschnitt 14,5% Gemeiner Sand zwischen 0 und 10% im Durchschnitt 5% Zusatzstoffe zwischen 0,2 und 0,8% im Durchschnitt 0,5%.Method for producing prefabricated parts mortar according to claim 6, characterized in that the following percentage composition is present: Slag between 50 and 90% on average 70% Fly ashes between 0 and 20% on average 10% Portland cement between 4 and 25% on average 14.5% Mean sand between 0 and 10% on average 5% Additives between 0.2 and 0.8% on average 0.5%. Verfahren zum Herstellen vorgefertigter Teile aus Mörtel gemäß Patentanspruch 6, dadurch gekennzeichnet, dass die folgende prozentuale Zusammensetzung vorliegt: Asche zwischen 10 und 30% im Durchschnitt 20% Flugaschen zwischen 0 und 10% im Durchschnitt 5% Expandierter Ton zwischen 45 und 70% im Durchschnitt 57,5% Portlandzement zwischen 4 und 20% im Durchschnitt 12% Gemeiner Sand zwischen 0,2 und 0,8% im Durchschnitt 0,5%.Method for producing prefabricated parts of mortar according to claim 6, characterized in that the following percentage composition is present: ashes between 10 and 30% on average 20% fly ashes between 0 and 10% on average 5% Expanded clay between 45 and 70% on average 57.5% Portland cement between 4 and 20% on average 12% Common sand between 0.2 and 0.8% on average 0.5%.
DE69731067T 1997-02-13 1997-02-14 Process for the production of building mortar Expired - Fee Related DE69731067T2 (en)