DE69729883T2 - WEATHERED HERMATYPIC CORAL MATERIAL - Google Patents

WEATHERED HERMATYPIC CORAL MATERIAL Download PDF

Info

Publication number
DE69729883T2
DE69729883T2 DE69729883T DE69729883T DE69729883T2 DE 69729883 T2 DE69729883 T2 DE 69729883T2 DE 69729883 T DE69729883 T DE 69729883T DE 69729883 T DE69729883 T DE 69729883T DE 69729883 T2 DE69729883 T2 DE 69729883T2
Authority
DE
Germany
Prior art keywords
weathered
reef
building coral
water
coral
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
DE69729883T
Other languages
German (de)
Other versions
DE69729883D1 (en
Inventor
Satoshi Yokohama-shi YOSHIZUMI
Toshiharu Urasoe-shi ODA
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Coral Biotech Co Ltd
Original Assignee
Coral Biotech Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Coral Biotech Co Ltd filed Critical Coral Biotech Co Ltd
Priority claimed from PCT/JP1997/003718 external-priority patent/WO1999019259A1/en
Application granted granted Critical
Publication of DE69729883D1 publication Critical patent/DE69729883D1/en
Publication of DE69729883T2 publication Critical patent/DE69729883T2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

Die vorliegende Erfindung betrifft ein Verfahren zum Herstellen eines verwitterten, Riff-bildenden Korallenmaterials, das für Nahrungsmaterialien, Filtermedien und dergleichen geeignet ist, indem organische Substanzen, die von marinen Algen, Mikroorganismen und dergleichen stammen und die in dem porösen Gewebe einer verwitterten Riff-bildenden Koralle enthalten sind, entfernt werden, und sie betrifft ebenfalls ein verwittertes Riff-bildendes Korallenmaterial, das durch dieses Verfahren erhalten wurde.The The present invention relates to a method for producing a weathered, reef-building coral material used for food materials, Filter media and the like is suitable by organic substances, which originate from marine algae, microorganisms and the like and in the porous one Tissues of a weathered reef-building coral are included, It also affects a weathered reef-building Coral material obtained by this method.

Koralleninsekten, die Meeresregionen in der gemäßigten Zone, der subtropischen Zone und der tropischen Zone bewohnen bilden Korallenriffe. Die Korallenriffe verwittern und eines nach dem anderen geht nach dem Ablauf von Tausenden bis Zehntausenden von Jahren nach dem Tod der Koralleninsekten, die in den Korallenriffen leben in Splitter oder Teilchen über. Derartige Splitter oder Teilchen werden von den Ozeanströmungen erfasst und lagern sich auf dem Meeresboden entsprechend ihrer Teilchengröße durch die Einwirkung der Aufschlämmung durch ozeanische Strömungen ab und reichern sich dort an. Die verwitterte Riff-bildende Koralle ist eine Anreicherung derartiger Splitter oder Teilchen.Coral insects, the marine regions in the temperate zone, The subtropical zone and the tropical zone inhabit make coral reefs. The coral reefs weather and one after the other goes to the Expiration of thousands to tens of thousands of years after the death of Coral insects that live in splinters or in coral reefs Particles over. Such splinters or particles are captured by the ocean currents and deposit on the seabed according to their particle size the action of the slurry by oceanic currents and accumulate there. The weathered reef-building coral is an accumulation of such fragments or particles.

Die verwitterte Riff-bildende Koralle hat eine sehr poröse Feinstruktur. Diese poröse Feinstruktur ist ein Wohnsitz für Koralleninsekten und organische Substanzen, die von verschiedenen marinen Algen und Mikroorganismen stammen (beispielsweise Vibrionbakterien), die die Meere bewohnen und werden darin zurückgehalten, solange die verwitterte Riff-bildende Koralle über viele Jahre am Meeresgrund existiert.The weathered reef-building coral has a very porous fine structure. This porous Fine structure is a residence for Coral insects and organic substances by different marine algae and microorganisms (for example, Vibrion bacteria), that inhabit the seas and are held back as long as they weather Reef-building coral over many years on the seabed exists.

Die verwitterte Riff-bildende Koralle wird als Nahrungsmittelmaterial zum Ersatz von Calcium verwendet oder als Filtermedien für Wasserreiniger, landwirtschaftliche Bodenverbesserer und dergleichen. Wenn sie in Nahrungsmaterialien und Filtermedien für Wasserreiniger verwendet wird, ist es erforderlich, die vorstehend erwähnten organischen Substanzen aus Sicherheitsgründen zu entfernen und es ist ebenfalls erforderlich, für die Desinfektion oder Sterilisierung Maßnahmen zu ergreifen, so dass die mikrobiologische Sicherheit gewährleistet werden kann.The weathered reef-building coral is used as food stuff used to replace calcium or as filter media for water purifiers, agricultural soil improvers and the like. When in Food materials and filter media used for water purifiers If necessary, it is necessary to use the above-mentioned organic substances for safety reasons it is also necessary for disinfection or sterilization measures so that microbiological safety is guaranteed can be.

In einem üblichen Verfahren bei dem verwittertes Riff-bildendes Korallenmaterial als Nahrungsmittelmaterialien aus verwitterten Riff-bildenden Korallen hergestellt wird, werden die folgenden Schritte wie es schematisch in 4 gezeigt ist ergriffen.In a conventional process in which weathered reef-building coral material is prepared as food materials from weathered reef-building corals, the following steps are described schematically in FIG 4 shown is taken.

Das heißt, dass zuerst die verwitterte Riff-bildende Koralle vom Meeresboden durch ein Saugboot gesammelt wird und entsprechend den Herstellungszwecken in Teilmengen mit einer vorbestimmten Teilchen- oder Korngröße klassifiziert wird (z. B. durch das Passieren durch ein 10 mesh Sieb (Teilchendurchmesser von 2,0 mm oder kleiner) und des Verbleibens auf einem 80 mesh Sieb (Teilchendurchmesser von 0,81 mm oder größer)).The is called, that first the weathered reef-building coral from the seabed is collected by a suction boat and according to the manufacturing purposes classified in subsets of a predetermined particle or grain size is (for example, by passing through a 10 mesh sieve (particle diameter of 2.0 mm or smaller) and remaining on an 80 mesh screen (Particle diameter of 0.81 mm or larger)).

Die so klassifizierte verwitterten Riff-bildende Koralle wird an Land gebracht und anschließend auf einem Stapelplatz gelagert und der größere Teil des Meereswassersalzes wird durch das Versprühen von Leitungswasser über dem Ganzen entfernt, gefolgt von dem Trocknen an Luft. Dieses Material wird anschließend in eine Fabrik transportiert und im Fabrikhof durch ein Schüttelsieb gemäß der vorbestimmten Partikel oder Korngröße gesiebt und wird anschließend wieder mit Wasser unter Verwendung einer Waschmaschine gewaschen, gefolgt von Entwässerung, Trocknen und weiter gefolgt von Desinfektion durch trockene Hitze oder Trockensterilisierung bei Temperaturen von üblicherweise von 100 bis 200°C. Das so erhaltene Material wird pulverisiert und durchgesiebt, um seine Teilchen oder Korngröße an die vorbestimmte Teilchen- oder Korngröße anzupassen und wird anschließend für die Vermarktung verpackt. Alternativ dazu kann das in die Fabrik transportierte Material gesiebt werden und mit Wasser gewaschen werden, gefolgt von Entwässerung und Trocknen und es wird anschließend bei einer Temperatur geröstet, bei der Calciumcarbonat, der Hauptbestandteil der verwitterten Riff-bildenden Koralle sich nicht zersetzt (250 bis 600°C) und wird anschließend pulverisiert und gesiebt zur Anpassung seiner Teilchen- oder Korngröße an eine vorbestimmte Teilchen- oder Korngröße und anschließend für die Vermarktung verpackt. Das das so erhaltene verwitterte Riff-bildende Korallenmaterial für Lebensmittelzwecke weist Teilchendurchmesser auf, die klein genug sind, um durch ein 300 mesh Sieb zu passen, d. h. Teilchendurchmesser von 45 μm oder kleiner.The so classified weathered reef-building coral gets ashore brought and then stored on a stacking place and the larger part of the seawater salt is through the spraying of tap water over removed from the whole, followed by drying in air. This material will then be in transported a factory and in the factory yard through a shaker according to the predetermined Sieved particle or grain size and afterwards washed again with water using a washing machine, followed by drainage, Dry and continue followed by disinfection by dry heat or dry sterilization at temperatures of usually from 100 to 200 ° C. That so material obtained is pulverized and sieved to its Particles or grain size to the predetermined particle or grain size and is then for marketing packed up. Alternatively, this can be transported to the factory Material is sieved and washed with water, followed of drainage and drying, and then it is roasted at a temperature at the calcium carbonate, the main component of the weathered reef-forming Coral does not decompose (250 to 600 ° C) and is then pulverized and screened to match its particle or grain size to a predetermined particle or grain size and then for marketing packed up. The weathered reef-building coral material thus obtained for food purposes has particle diameters small enough to pass through 300 mesh sieve to fit, d. H. Particle diameter of 45 μm or smaller.

In einem weiteren üblichen Verfahren zur Herstellung von Filtermedien für Wasserreiniger, ähnlich dem vorstehend beschriebenen Verfahren zur Herstellung von verwitterten Riff-bildenden Korallenmaterialien für Nahrungsmittelzwecke, wird das verwitterte Riff-bildende Korallenmaterial gesammelt, im Fabrikhof durch ein Schüttelsieb gesiebt, um Körner auszusieben, damit eine vorbestimmte Größe zu erzielen und damit seine Korngröße zu vereinheitlichen, die geeignet ist für Filtermedien für Wasserreiniger zu dienen, gefolgt von Waschen mit Wasser, Entwässerung und Trocknen. Anschließend wird die erhaltene verwitterte Riff-bildende Koralle geröstet (250 bis 600°C), damit sie zur Vergrößerung der Mineralienelutionsmenge aktiviert wird, und anschließend durchgesiebt, um die Korngröße an eine vorbestimmte Größe anzupassen und für die Vermarktung verpackt, japanisches veröffentlichtes Patent Nr. Hei 3-12983.In another conventional method for making filter media for water purifiers, similar to the method described above for producing weathered reef-building coral materials for food purposes, the weathered reef-building coral material is collected, screened at the factory yard through a shaker screen to screen out grains to allow a To achieve predetermined size and thus to standardize its grain size, which is suitable for filter media for water purifiers to serve, followed by Wa with water, drainage and drying. Then, the resulting weathered reef-building coral is roasted (250 to 600 ° C) to be activated to increase the amount of mineral elution, and then sieved to adjust the grain size to a predetermined size and packaged for marketing, Japanese Patent Publication No. Hei. Hei 3-12983.

Von Materialien, die mit Silber versetzt sind und die durch Beschichten des verwitterten Riff-bildenden Korallenmaterials mit Silber erhalten werden, ist bekannt, dass sie eine verbesserte Sterilisierungsfähigkeit aufweisen (japanische veröffentlichte Patentanmeldung Nr. 51-179107, etc.). Als mit Silber versetzte Materialien werden hauptsächlich diejenigen, die einen Korndurchmesser von 0,71 mm oder größer aufweisen, die hauptsächlich als Filtermedien für Wasserreiniger verwendet werden, und diejenigen, die einen Korndurchmesser kleiner als 0,71 mm aufweisen und die für andere Zwecke verwendet werden, hergestellt. In einem derartigen Verfahren zur Herstellung derartiger mit Silber versetzter Materialien, d. h. den vorstehend beschriebenen Filtermedien für Wasserreiniger, wird das verwitterte Riff-bildende Korallenmaterial in der gleichen Weise wie im Fall von Filtermedien für Wasserreiniger, wie es vorstehend beschrieben wurde, geröstet. Anschließend wird es in eine wässrige Silberlösung eingetaucht, und in eine Lösung mit einem reduzierenden Mittel wie eine Ascorbinsäurelösung eingetaucht und bei 400°C für ungefähr 30 Minuten erhitzt, damit sich Silber abscheidet, gefolgt von Waschen mit Wasser, Trocknen und Verpacken für die Vermarktung.From Materials that are mixed with silver and that by coating of weathered reef-building coral material with silver are known to have improved sterilizing ability (Japanese published Patent Application No. 51-179107, etc.). As with silver offset materials become mainly those having a grain diameter of 0.71 mm or larger, the main ones as filter media for Water purifiers are used, and those that have a grain diameter less than 0.71 mm and that are used for other purposes, produced. In such a process for producing such with silver staggered materials, d. H. the one described above Filter media for Water purifier, becomes the weathered reef-building coral material in the same way as in the case of filter media for water purifiers, roasted as described above. Subsequently, will it in a watery silver solution dipped, and into a solution immersed with a reducing agent such as an ascorbic acid solution and at 400 ° C for about 30 minutes heated so that silver separates, followed by washing with water, Drying and packing for the marketing.

Bei den üblichen Verfahren zur Herstellung von verwitterten Riff-bildenden Korallenmaterialien für Nahrungsmittel oder Filtermedien können jedoch verschiedene Meeresalgen, die über viele Jahre gewachsen sind, verschiedene Mikroorganismen einschließlich Vibrionbakterien, die die Meere bewohnen, und andere organische Sub stanzen nicht aus dem Inneren der porösen Feinstruktur der verwitterten Riff-bildenden Koralle entfernt werden. Daher ist das übliche Verfahren in Bezug auf die Gewährleistung der Sicherheit, die für Nahrungsmittelmaterialien erforderlich ist, unzureichend.at the usual Process for producing weathered reef-building coral materials for food or filter media but different sea algae that have grown over many years, various microorganisms including Vibrion bacteria that inhabiting the oceans, and other organic sub stances not from the Interior of the porous Fine structure of weathered reef-building coral removed. Therefore is the usual Warranty procedure security for Food materials required is insufficient.

Wie gut bekannt ist, lecken im Allgemeinen bei Wasserreinigern, bei denen das verwitterte Riff-bildende Korallenmaterial dem Schritt des Erhitzens durch Desinfizierung durch trockene Hitze oder Trockensterilisation unterzogen wurde oder durch Rösten als Filtermedium eingestellt wurde, Mineralien in geringen Mengen aus, wenn Wasser durchläuft, so dass der Geschmack des Wassers verbessert werden kann. Jedoch können die verwitterten Riff-bildenden Korallenmaterialien, die durch übliche Verfahren erhalten werden, Mineralien nicht in derartigen Mengen eluieren, um in größerem Ausmaße die Gesamthärte der Elutionsmenge zu vergrößern. Ebenso hat dieses Material keinen ausreichenden Aktivierungsgrad und es kann daher nicht davon gesprochen werden, dass es eine gute Adsorptionsfähigkeit in Bezug auf Verunreinigungen und dergleichen aufweist.As Well known, generally lick at water purifiers the weathered reef-building coral material to the crotch heating by dry heat disinfection or dry sterilization was subjected or by roasting was set as a filter medium, minerals in small quantities out when water goes through, so that the taste of the water can be improved. however can the weathered reef-building coral materials produced by standard procedures minerals do not elute in such amounts, to a greater extent the total hardness of the To increase the elution amount. As well this material does not have a sufficient degree of activation and it Therefore it can not be said that it has a good adsorption capacity with respect to impurities and the like.

Falls das mit Silber versetzte verwitterte Riff-bildende Korallenmaterial hergestellt wird, tritt ebenfalls das Problem auf, dass Silber nur an der Oberfläche des verwitterten Riff-bildenden Korallenmaterials als Schicht beschichtet wird und nicht in der gesamten porösen inneren Feinstruktur beschichtet wird.If the silvered weathered reef-building coral material Also, the problem arises that silver only on the surface of the weathered reef-building coral material coated as a layer is coated and not in the entire porous inner fine structure becomes.

Die vorliegende Erfindung löst die vorstehend erwähnten Probleme des Standes der Technik. Demgemäß besteht eine Aufgabe darin, ein verwittertes Riff-bildendes Korallenmaterial bereitzustellen, bei dem verschiedene marine Algen, verschiedene Mikroorganismen einschließlich Vibrionbakterien, die die Meere bewohnen und andere verschiedene organische Substanzen, die in der Feinstruktur von verwittertem Riff-bildendem Korallenmaterial enthalten sind, entfernt werden und dadurch die Sicherheit, die für Nahrungsmittelmaterialien erforderlich ist, gewährleistet wird und sie besteht ebenfalls in der Bereitstellung eines Verfahrens zur Herstellung eines derartigen verwitterten Riff-bildenden Korallenmaterials.The present invention solves the aforementioned Problems of the prior art. Accordingly, an object is to to provide a weathered reef-building coral material, in the different marine algae, different microorganisms including Vibrion bacteria inhabiting the oceans and others organic substances that are weathered in the fine structure of Reef-building coral material are removed and thereby the safety for food materials is required, guaranteed and is also in providing a method for producing such weathered reef-building coral material.

Eine weitere Aufgabe besteht in der Bereitstellung von Nahrungsmittelmaterialien und Filtermedien, umfassend ein derartiges verwittertes Riff-bildendes Korallenmaterial.A Another object is the provision of food materials and filter media comprising such weathered reef-building Coral material.

Noch eine weitere Aufgabe besteht in der Bereitstellung eines mit Silber versetzten verwitterten Riff-bildenden Korallenmaterials, das an seiner Oberfläche und ebenfalls in seiner gesamten inneren Feinstruktur des porösen Gewebes mit Silber beschichtet ist und ebenfalls in der Bereitstellung eines Verfahrens zur Herstellung eines derartigen verwitterten Riff-bildenden Korallenmaterials.Yet Another task is to provide one with silver staggered weathered reef-building coral material, that on its surface and also in its entire inner fine structure of the porous tissue coated with silver and also in the provision of a A method of making such a weathered reef-forming Coral material.

Zur Lösung der vorstehenden Aufgaben stellt die vorliegende Erfindung zuerst ein Verfahren zur Herstellung eines verwitterten Riff-bildenden Korallenmaterials bereit, umfassend die Schritte
des Eintauchens einer verwitterten Riff-bildenden Koralle in eine wässrige Alkalilösung unter reduziertem Druck zum Ausführen eines alkalischen Waschens, um ein Eindringen der wässrigen Alkalilösung in die verwitterte Riff-bildende Koralle überall in ihrer Feinstruktur innerhalb des porösen Gewebes hervorzurufen und
deren Waschens mit Wasser bis Waschwasser aus dem Inneren des porösen Gewebe neutralisiert ist, wobei nach dem Waschen mit Wasser das verwitterte Riff-bildende Korallenmaterial bei 100 bis 750°C geröstet wird.To achieve the above objects, the present invention first provides a method for producing a weathered reef-building coral material comprising the steps
immersing a weathered reef-building coral in an aqueous alkali solution under reduced pressure to carry out alkaline washing to cause penetration of the aqueous alkali solution into the weathered reef-building coral throughout its fine structure within the porous web and
their washing with water is neutralized to wash water from the interior of the porous fabric, wherein after washing with water, the weathered reef-building coral material is roasted at 100 to 750 ° C.

Zweitens stellt die vorliegende Erfindung ein verwittertes Riff-bildendes Korallenmaterial bereit, das durch das vorstehende Verfahren zur Herstellung eines verwitterten Riff-bildenden Korallenmaterials erhalten wird.Secondly The present invention provides a weathered reef-building Coral material prepared by the above procedure for Making a weathered reef-building coral material is obtained.

Drittens stellt die vorliegende Erfindung ein Nahrungsmittelmaterial bereit, umfassend eine pulverisierte verwitterte Riff-bildende Koralle, die eine Teilchengröße von 500 mesh oder mehr aufweist (Durchmesser von 27,28 μm oder kleiner) und das durch das vorstehende Verfahren zur Herstellung eines verwitterten Riff-bildenden Korallenmaterials erhalten wurde, bei dem nach dem Waschen mit Wasser die verwitterte Riff-bildende Koralle weiter pulverisiert und durchgesiebt wird.thirdly the present invention provides a food material comprising a pulverized weathered reef-building coral, the particle size of 500 mesh or more (diameter of 27.28 microns or smaller) and that by the above method of producing a weathered reef-forming Coral material was obtained in which after washing with water the weathered reef-building coral further pulverized and screened becomes.

Viertens stellt die vorliegende Erfindung ein Filtermedium bereit, umfassend eine verwitterte Riff-bildende Koralle, das durch das vorstehende Verfahren zur Herstellung eines verwitterten Riff-bildenden Korallenmaterials erhalten wurde.Fourth The present invention provides a filter medium comprising a weathered reef-building coral surrounded by the prominent A method of making a weathered reef-building coral material was obtained.

Fünftens stellt die vorliegende Erfindung ein Verfahren zur Herstellung eines mit Silber versetzten verwitterten Riff-bildenden Korallenmaterials bereit, umfassend nach dem Waschen mit Wasser in dem vorstehenden Verfahren zur Herstellung eines verwitterten Riff-bildenden Korallenmaterials, das Rösten bei 100 bis 750°C, gefolgt von einem Eintauchen in eine wässrigen Silberlösung unter reduziertem Druck, um ein Eindringen der wässrigen Silberlösung in die verwitterte Riff-bildende Koralle überall in ihrer Feinstruktur innerhalb des porösen Gewebes hervorzurufen und das Reduzieren des Silbers mit einem Reduktionsmittel, um die verwitterte Riff-bildende Koralle mit Silber überall in ihrer Feinstruktur innerhalb des porösen Gewebes zu beschichten
und stellt ebenfalls ein mit Silber versetztes verwittertes Riff-bildendes Korallenmaterial bereit, das durch dieses Herstellverfahren erhalten wurde.Fifth, the present invention provides a process for producing a silver-plated weathered reef-building coral material comprising, after washing with water in the above process for producing a weathered reef-building coral material, roasting at 100 to 750 ° C followed by immersing in an aqueous silver solution under reduced pressure to cause penetration of the aqueous silver solution into the weathered reef-building coral throughout its fine structure within the porous tissue and reducing the silver with a reducing agent to silver the weathered reef-building coral everywhere in their fine structure within the porous tissue to coat
and also provides a silver-added weathered reef-building coral material obtained by this production method.

Gemäß dem Verfahren der vorliegenden Erfindung zur Herstellung eines verwitterten Riff-bildenden Korallenmaterials, wird die verwitterte Riff-bildende Koralle in eine wässrige Alkalilösung unter reduziertem Druck zum Ausführen eines alkalischen Waschens eingetaucht, um ein Eindringen der wässrigen Alkalilösung in die verwitterte Riff-bildende Koralle überall in ihrer Feinstruktur innerhalb des porösen Gewebes hervorzurufen. Dadurch können die verschiedenen Meeresalgen, verschiedene Mikroorganismen einschließlich Vibrionbakterien, die die Meere bewohnen und andere verschiedene organische Substanzen, die in der inneren Feinstruktur einer verwitterten Riff-bildenden Koralle enthalten sind, entfernt werden. Daher kann ein verwittertes Riff-bildendes Korallenmaterial erhalten werden, dessen Sicherheit wie sie für Nahrungsmittelmaterialien erforderlich ist, gewährleistet werden kann.According to the procedure of the present invention for producing a weathered reef-building coral material, The weathered reef-building coral is immersed in an aqueous alkali solution reduced pressure to run immersed in an alkaline washing to prevent penetration of the aqueous Alkaline solution in the weathered reef-building coral throughout their fine structure within the porous To cause tissue. Thereby can the various sea algae, various microorganisms including vibrion bacteria, inhabiting the seas and other different organic substances, the in the inner fine structure of a weathered reef-forming Coral are included, removed. Therefore, a weathered Reef-building coral material is obtained, its safety as for Food materials required can be guaranteed.

Insbesondere wird das pulverisierte Material, das erhalten wird, indem die verwitterte Riff-bildende Koralle einem Rösten unterzogen wurde, um eine Teilchengröße von 500 mesh oder größer aufzuweisen (Durchmesser von 27,28 μm oder kleiner), die für Nahrungsmittel erforderliche Sicherheit gewährleisten und ist als Nahrungsmit telmaterialien bevorzugt, das es von einem rauen Gefühl frei ist, wenn es gegessen wird.Especially becomes the powdered material that is obtained by weathering Reef-forming coral a toasting was subjected to have a particle size of 500 mesh or larger (Diameter of 27.28 microns or smaller), which for Food safety and is as food stuffs preferred that it is free from a rough feeling when eaten becomes.

Das Produkt, das durch das Rösten dieses verwitterten Riff-bildenden Korallenmaterials bei 100 bis 750°C erhalten wird, ist hoch aktiviert und ist in Bezug auf die Adsorptionsfähigkeit von Verunreinigungen verbessert und kann daher ein gutes Filtermedium darstellen.The Product by roasting This weathered reef-building coral material obtained at 100 to 750 ° C. is highly activated and is in terms of adsorption capacity improved by impurities and therefore can be a good filter medium represent.

Die verwitterte Riff-bildende Koralle kann einem Rösten unterzogen werden, gefolgt vom Eintauchen in eine wässrige Silberlösung unter reduziertem Druck, um ein Eindringen der wässrigen Silberlösung in die verwitterte Riff-bildende Koralle überall in ihrer Feinstruktur innerhalb des porösen Gewebes hervorzurufen und nachfolgend wird das Silber mit einem Reduzierungsmittel reduziert, wobei ein mit Silber versetztes verwittertes Riff-bildendes Korallenmaterial erhalten werden kann, das mit Silber auch innerhalb seiner Feinstruktur im porösen Gewebe beschichtet wurde.The weathered reef-building coral can be subjected to roasting, followed from immersing in an aqueous silver solution under reduced pressure to prevent ingress of the aqueous silver solution the weathered reef-building coral throughout their fine structure within the porous To cause tissue and subsequently the silver with a Reducing agent reduced, with a silver added weathered Reef-building coral material can be obtained with silver was also coated within its fine structure in the porous tissue.

Gemäß der Eintauchbehandlungsvorrichtung, die in 2 gezeigt ist, wird die verwitterte Riff-bildende Koralle in den Korb gegeben und die wässrige Alkalilösung oder Wasser kann kräftig durch die verwitterte Riff-bildende Koralle, die im Korb enthalten ist, durchgeleitet werden. Daher kann die verwitterte Riff-bildende Koralle vollständig in die wässrige Alkalilösung oder in Wasser eingetaucht werden, auch im Inneren des porösen Gewebes, so dass die verwitterte Riff-bildende Koralle mit einer guten Wirksamkeit gewaschen werden kann. In diesem Beispiel kann die verwitterte Riff-bildende Koralle selber ebenfalls gewaschen werden, ohne dass sie hin- und herbewegt wird, und daher kann es vermieden werden, dass die verwitterte Riff-bildende Koralle nach dem Waschen zu einem feinem Pulver wird, so dass die gewünschte Teilchen- oder Korngröße beibehalten werden kann.According to the immersion treatment apparatus described in 2 is shown, the weathered reef-building coral is placed in the basket and the aqueous alkali solution or water can be vigorously passed through the weathered reef-building coral contained in the basket. Therefore, the weathered reef-building coral can be completely immersed in the aqueous alkali solution or in water, even inside the porous fabric, so that the weathered reef-building coral can be washed with good efficiency. In this example, the weathered reef-building coral itself can also be washed without that it is reciprocated, and therefore it can be avoided that the weathered reef-building coral becomes a fine powder after washing, so that the desired particle or grain size can be maintained.

1 ist ein Flussdiagramm eines Verfahrens zur Herstellung des verwitterten Riff-bildenden Korallenmaterials und des mit Silber versetzten verwitterten Riff-bildenden Korallenmaterials der vorliegenden Erfindung. 1 FIG. 10 is a flow chart of a process for producing the weathered reef-building coral material and the silver-stained weathered reef-building coral material of the present invention.

2 veranschaulicht eine Vorrichtung zur Eintauchbehandlung. 2 illustrates a device for immersion treatment.

3 zeigt die Beziehung zwischen Mesh-Größe und Teilchen- oder Korngröße. 3 shows the relationship between mesh size and particle or grain size.

4 ist ein Flussdiagramm eines üblichen Verfahrens zur Herstellung von verwitterten Riff-bildenden Korallenmaterialien. 4 FIG. 10 is a flowchart of a conventional process for producing weathered reef-building coral materials. FIG.

Die vorliegende Erfindung wird nachstehend genauer beschrieben.The The present invention will be described in more detail below.

1 ist ein Flussdiagramm eines Verfahrens zur Herstellung des verwitterten Riff-bildenden Korallenmaterials und des mit Silber versetzten verwitterten Riff-bildenden Korallenmaterials der vorliegenden Erfindung. Dieses Flussdiagramm zeigt die Schritte im Anschluss an den Schritt im Fabrikhof eines üblichen Verfahrens zur Herstellung von verwittertem Riff-bildenden Korallenmaterial wie es in 4 gezeigt ist. 1 FIG. 10 is a flow chart of a process for producing the weathered reef-building coral material and the silver-stained weathered reef-building coral material of the present invention. This flow chart shows the steps following the factory yard step of a conventional process for producing weathered reef-building coral material as shown in FIG 4 is shown.

Die Schritte vor dem Schritt im Fabrikhof sind die gleichen wie diejenigen, die in 4 im Flussdiagramm des herkömmlichen Verfahrens gezeigt sind. Demgemäß wird die verwitterte Riff-bildende Koralle vom Meeresboden aufgesammelt und wird anschließend gemäß ihrer Teilchen- oder Korngröße klassifiziert und mit Wasser zur Entfernung von Meerwassersalz besprüht, gefolgt von Trocknen an Luft und kann als verwitterte Riff-bildende Koralle, die im Herstellungsverfahren der vorliegenden Erfindung verwendet werden kann, gewaschen werden.The steps before the step in the factory yard are the same as those in 4 are shown in the flowchart of the conventional method. Accordingly, the weathered reef-building coral is collected from the seabed and is then classified according to its particle size and sprayed with water to remove seawater salt, followed by drying in air and may be used as weathered reef-building coral used in the production process of the present invention can be used, washed.

Wie in 1 gezeigt, wird im Herstellungsverfahren gemäß der vorliegenden Erfindung die zu waschende verwitterte Riff-bildende Koralle zuerst in einer wässrigen Alkalilösung unter reduziertem Druck eingetaucht, zum Ausführen eines alkalischen Waschens, um ein Eindringen der wässrigen Alkalilösung in die verwitterte Riff-bildende Koralle überall in ihrer Feinstruktur innerhalb des porösen Gewebes hervorzurufen. Der optimale Druck im System während des alkalischen Waschens hängt von der Teilchen- oder Korngröße der verwitterten Riff-bildenden Koralle, die die Form von Fragmenten, Körnchen oder Pulver haben kann. Falls beispielsweise dieses in Form von Fragmenten mit einem durchschnittlichen Korndurchmesser von 0,18 mm bis 0,71 mm vorliegt, liegt der Druck vorzugsweise in einem kontrollierten Bereich von 70 mmHg oder niedriger. Falls es in Form von Körnchen mit einem Durchschnittskorndurchmesser von 8,0 bis 16,0 mm vorliegt, kann der Druck vorzugsweise so eingestellt werden, dass er 30 mmHg oder niedriger beträgt.As in 1 In the manufacturing method according to the present invention, the weathered reef-building coral to be washed is first immersed in an aqueous alkali solution under reduced pressure to carry out alkaline washing to prevent penetration of the aqueous alkali solution into the weathered reef-building coral throughout its fine structure within the porous tissue. The optimum pressure in the system during alkaline washing depends on the particle or grain size of the weathered reef-building coral, which may be in the form of fragments, granules or powder. For example, if it is in the form of fragments having an average grain diameter of 0.18 mm to 0.71 mm, the pressure is preferably in a controlled range of 70 mmHg or lower. If it is in the form of granules having an average grain diameter of 8.0 to 16.0 mm, the pressure may preferably be set to be 30 mmHg or lower.

Als wässrige Alkalilösung, wird vorzugsweise eine wässrige Lösung von NaOH, KOH, Na2CO3, K2CO3 oder dergleichen verwendet werden. Eine Lösung einer einzigen alkalischen Verbindung oder von zwei oder mehreren, oder von gemischten Allkalilösungen kann ebenfalls verwendet werden. Besonders Einschränkungen bezüglich der Konzentration der Alkaliverbindung bestehen nicht. Die wässrige alkalische Lösung liegt vorzugsweise in einer Konzentration von 0,01 N bis 6 N und bevorzugter von 0,1 N bis 1 N vor. Falls die wässrige alkalische Lösung eine Konzentration von weniger als 0,01 N hat, wird es schwierig, die organischen Substanzen wie marine Algen oder Proteine, die aus Mikroorganismen stammen und dergleichen und in der Feinstruktur innerhalb des porösen Gewebes zurückgehalten werden, vollständig zu eluieren. Falls andererseits die wässrige alkalische Lösung eine Konzentration von mehr als 6 N aufweist, muss das Waschen mit Wasser in einem späteren Stadium sehr oft durchgeführt, bis der pH-Wert des Ausflusses neutral wird, was die Möglichkeit einer Abnahme Wirtschaftlichkeit des Verfahrens mit sich bringt.As the aqueous alkali solution, it is preferable to use an aqueous solution of NaOH, KOH, Na 2 CO 3 , K 2 CO 3 or the like. A solution of a single alkaline compound or two or more, or mixed all-caustic solutions may also be used. There are no particular restrictions on the concentration of the alkali compound. The aqueous alkaline solution is preferably present in a concentration of from 0.01 N to 6 N, and more preferably from 0.1 N to 1 N. If the aqueous alkaline solution has a concentration of less than 0.01 N, it becomes difficult to completely elute organic substances such as marine algae or proteins derived from microorganisms and the like and retained in the fine structure within the porous tissue. On the other hand, if the aqueous alkaline solution has a concentration of more than 6N, the washing with water at a later stage must be carried out very often until the pH of the effluent becomes neutral, which brings about the possibility of decreasing the economy of the process.

Die wässrige alkalische Lösung, in die die verwitterte Riff-bildende Koralle eingetaucht wurde, kann vorzugsweise für ungefähr 30 bis 60 Minuten auf 80 bis 100°C erhitzt werden. Dies ermöglicht die Beschleunigung der alkalischen Zersetzung der organischen Substanzen wie Proteine, die in der verwitterten Riff-bildenden Koralle enthalten sind.The aqueous alkaline solution, into which the weathered reef-building coral was immersed, can preferably for approximately 30 to 60 minutes at 80 to 100 ° C to be heated. this makes possible the acceleration of the alkaline decomposition of organic substances like proteins contained in the weathered reef-building coral are.

Es ist ebenso bevorzugt, die wässrige alkalische Lösung durch die verwitterte Riff-bildende Koralle kräftig durchzuleiten (d. h. Flüssigkeitsströme zu bilden, um Flüssigkeitsströme der wässrigen alkalischen Lösung kräftig durch die verwitterte Riff-bildende Koralle durchzuleiten, die in einer wässrigen Alkalilösung eingetaucht ist), damit die wässrige alkalische Lösung wirksam auf die verwitterte Riff-bildende Koralle, die darin eingetaucht ist, wirken kann oder die verwitterte Riff-bildende Koralle, die in der wässrigen alkalischen Lösung eingetaucht ist, hin- und herzubewegen. Das Hin- und Herbewegen der verwitterten Riff-bildenden Koralle führt dazu, dass die verwitterte Riff-bildende Koralle untereinander während des Hin- und Herbewegens zusammenstößt, so dass sie leicht zu einem feinen Pulver wird. Demgemäß ist es in den Fällen, wo die verwitterte Riff-bildende Koralle fein pulverisiert sein kann, bevorzugt, die verwitterte Riff-bildende Koralle in der wässrigen alkalischen Lösung hin- und herzubewegen. Ebenso ist es in den Fällen, in denen beabsichtigt ist, die ursprüngliche Korngröße nach dem alkalischen Waschen beizubehalten, bevorzugt, die wässrige alkalische Lösung durch die verwitterte Riff-bildende Koralle kräftig durchzuleiten.It is also preferable to vigorously pass the aqueous alkaline solution through the weathered reef-building coral (ie, to form liquid streams to vigorously pass liquid streams of the aqueous alkaline solution through the weathered reef-building coral that is in an aqueous alkali solution so that the aqueous alkaline solution can effectively act on the weathered reef-building coral immersed therein or reciprocate the weathered reef-building coral immersed in the aqueous alkaline solution. The agitation of the weathered reef-building coral causes the weathered reef-building coral to collide with each other during reciprocation, so that it easily becomes a fine powder. Accordingly, in cases where the weathered reef-building coral may be finely pulverized, it is preferred to agitate the weathered reef-building coral in the aqueous alkaline solution. Also, in cases where it is intended to maintain the original grain size after the alkaline washing, it is preferable to vigorously pass the aqueous alkaline solution through the weathered reef-building coral.

Nachdem das alkalische Waschen derartig durchgeführt wurde, wird das Innere des Systems auf normalen Druck zurückgebracht, um die Waschlösung abzuleiten und der nächste Schritt wird ausgeführt. Bevor der nächste Schritt ausgeführt wird, muss das alkalische Waschen, das unter reduziertem Druck wie vorstehend beschrieben wurde, öfters wiederholt werden.After this the alkaline washing was carried out in such a way becomes the interior the system returned to normal pressure to drain the wash solution and the next one Step is executed. Before the next Step performed Alkaline washing, which under reduced pressure, must be like described above, more often be repeated.

Das Waschen mit Wasser wird ähnlich dem vorstehend beschriebenen alkalischen Waschen durch das Eintauchen der verwitterten Riff-bildenden Koralle unter reduziertem Druck in Wasser durchgeführt. Dabei wird Leitungswasser als Wasser verwendet und heißes Wasser mit einer Temperatur von 40 bis 60°C wird besonders bevorzugt verwendet werden. In diesem Schritt des Waschens mit Wasser ist es bevorzugt, das Wasser durch die verwitterte Riff-bildende Koralle kräftig durchzuleiten oder die verwitterte Riff-bildende Koralle, die in Wasser eingetaucht ist, hin- und herzubewegen.The Washing with water will be similar the alkaline washing by immersion described above weathered reef-building coral under reduced pressure carried out in water. This tap water is used as water and hot water with a temperature of 40 to 60 ° C is particularly preferably used become. In this step of washing with water it is preferred vigorously channel the water through the weathered reef-building coral or the weathered reef-building coral dipped in water is to move back and forth.

Nach dem Waschen mit Wasser wird das Innere des Systems auf normalem Druck zurückgebracht, um das Wasser abzulassen, wobei das Waschen mit Wasser so lange wiederholt wird, bis der pH-Wert des Abwassers neutral ist. Daher wird es üblicherweise ausreichend sein, den Schritt des Waschens mit Wasser zweimal durchzuführen. In einigen Fällen muss er jedoch drei- bis fünfmal durchgeführt werden.To When washing with water, the inside of the system becomes normal Pressure returned to drain the water, repeating the washing with water for so long until the pH of the effluent is neutral. Therefore, it usually becomes be sufficient to perform the step of washing with water twice. In some cases but he has to three to five times carried out become.

Es ist nicht bevorzugt, eine Säure anstelle von Wasser im Schritt des Waschens mit Wasser zu verwenden, da die Verwendung von Säure die Zersetzung des Calciumcarbonats, dem Hauptbestandteil der verwitterten Riff-bildenden Koralle hervorrufen kann und ebenso ein Salzes, das der Reaktion der Neutralisierung der Säure mit einer alkalischen Verbindung zurechenbarbar ist, in unerwünschter Weise innerhalb der verwitterten Riff-bildenden Koralle gebildet werden kann.It is not preferred, an acid instead of using water in the step of washing with water, since the use of acid the decomposition of calcium carbonate, the main component of the weathered Reef-forming coral can cause as well as a salt that the reaction of neutralization of the acid with an alkaline compound is attributable to undesirable Way inside the weathered reef-building coral can be.

Der Waschschritt umfasst das alkalische Waschen und das Waschen mit Wasser und kann für gewöhnlich in insgesamt 30 bis 60 Minuten beendet sein.Of the Washing step includes alkaline washing and washing with Water and can for usually be completed in 30 to 60 minutes.

Nach dem Waschen mit Wasser wird die verwitterte Riff-bildende Koralle durch einen Entwässerer (Zentrifugalabscheider) oder dergleichen entwässert, gefolgt vom Trocknen.To washing with water becomes the weathered reef-building coral through a dehydrator (centrifugal separator) or the like drained, followed by drying.

Anschließend wird das verwitterte Riff-bildende Korallenmaterial einem Rösten unterworfen zur Gewährleistung der mikrobiologischen Sicherheit. In Bezug auf das Rösten der verwitterten Riff-bildenden Koralle wird das Rösten bei 100 bis 750°C durchgeführt und bevorzugt bei 250 bis 750°C.Subsequently, will subjecting the weathered reef-building coral material to roasting to guarantee microbiological safety. Regarding the roasting of weathered reef-building coral, roasting is performed at 100 to 750 ° C and preferably at 250 to 750 ° C.

Die so erhaltene verwitterte Riff-bildende Koralle kann ein verwittertes Riff-bildendes Korallenmaterial sein, das für verschiedene Zwecke wie Nahrungsmittelmaterialien, Filtermedien oder Bodenverbesserer verwendet werden kann. Anschließend wird die verwitterte Riff-bildende Koralle in Bezug auf ihre Teilchen oder Korngrößen für derartige Zwecke eingestellt und anschließend verpackt, um es auf dem Markt zu bringen als Nahrungsmittelmaterialien, Filtermedien oder Bodenverbesserer.The so obtained weathered reef-building coral can be a weathered one Reef-building coral material used for various purposes such as food materials, Filter media or soil conditioner can be used. Subsequently, will the weathered reef-building coral with respect to its particles or grain sizes for such Purpose set and then packaged to bring it to market as food materials, Filter media or soil conditioner.

Das verwitterte Riff-bildende Korallenmaterial der vorliegenden Erfindung weist in Bezug auf seine Form und Größe keine besonderen Beschränkungen auf und kann daher die Form von beispielsweise Blöcken, Körnchen oder Pulver haben. Wenn das verwitterte Riff-bildende Korallenmaterial jedoch als Nahrungsmittelmaterial verwendet wird, wird es vorzugsweise in Form eines Pulvers mit einer Teilchengröße von 500 mesh oder größer (mit einem Teilchendurchmesser von 27,28 μm oder kleiner) hergestellt werden, so dass seine Beschaffenheit als Nahrungsmittel verbessert werden kann. Dies führt dazu, dass das Nahrungsmittel eine von Rauhheiten freie, glatte Beschaffenheit haben kann. Übliche verwitterte Riff-bildende Korallenpulver wurden in Form von Pulvern hergestellt mit einer Teilchengröße, die von 150 mesh bis 500 mesh reicht (mit einem Teilchendurchmesser von 103 μm bis 27,28 μm). Diejenigen Materialien mit einer derartigen Teilchengröße rufen wenn sie gegessen werden ein Gefühl der Rauhheit im Mund hervor und weisen demzufolge eine schlechte Beschaffenheit auf.The weathered reef-building coral material of the present invention There are no particular restrictions on its shape and size and therefore may take the form of, for example, blocks, granules or Have powder. If the weathered reef-building coral material however, as a food material, it is preferably in the form of a powder having a particle size of 500 mesh or larger (with a particle diameter of 27.28 μm or smaller) so that its texture as food improves can be. this leads to to make the food a smooth, roughness-free food Texture can have. usual weathered reef-building coral powder were in the form of powders made with a particle size that from 150 mesh to 500 mesh (with a particle diameter of 103 μm to 27.28 μm). Call those materials with such a particle size if they are eaten a feeling The roughness in the mouth and therefore have a poor texture on.

Der Begriff "Mesh" wie er in der vorliegenden Erfindung in Bezug auf die Beschreibung der Teilchen oder Korngröße verwendet wird, ist eine Einheit gemäß dem ASTM-Sieb, die auch als Tyler oder Tylersieb bezeichnet wird, das nicht nur in großem Umfang in den Vereinigten Staaten von Amerika sondern auch in anderen Ländern einschließlich Japan verwendet wird. Für Refernzzwecke ist die Beziehung zwischen "Mesh" und "Teilchen oder Korngröße (μm)" in 3 gezeigt.The term "mesh" as used in the present invention in relation to the description of the particles or grain size is a unit according to the ASTM sieve, also referred to as Tyler or Tylersieb, which is not only widely used in the United States States of America but also in other countries including Japan is used. For reference purposes, the relationship between "mesh" and "particle or grain size (μm)" in FIG 3 shown.

Falls das verwitterte Riff-bildende Korallenmaterial als Filtermedien verwendet werden soll, wird es bei einer Temperatur von 100 bis 750°C geröstet und bevorzugt bei einer Temperatur von 250 bis 750°C. Dies ermöglicht es, verschiedene Eigenschaften wie Adsorptionsfähigkeit für Gerüche, die Eigenschaft der Elution von Mineralien und der Adsorptionsfähigkeit für Farbstoffe und mehr zu aktivieren, um daher die Brauchbarkeit als Filtermedien für Wasserreiniger noch mehr zu verbessern.If the weathered reef-building coral material as filter media It is used at a temperature of 100 to Roasted 750 ° C and preferably at a temperature of 250 to 750 ° C. This allows for different properties like adsorption capacity for odors that Property of elution of minerals and adsorption capacity for dyes and more, therefore, its usability as filter media for water purifier to improve even more.

Das verwitterte Riff-bildende Korallenmaterial ist ebenfalls als Materialien für mit Silber versetzte Materialien brauchbar. Da im verwitterten Riff-bildenden Korallenmaterial der vorliegenden Erfindung das Material, aus dem die organischen Substanzen, die von Meeresalgen, Mikroorganismen und dergleichen stammen, aus all der Feinstruktur innerhalb des porösen Gewebes entfernt wurden, ist es insbesondere möglich, die verwitterte Riff-bildende Koralle mit Silber auf ihren Teilchen oder Kornoberflächen und ebenso innerhalb ihrer Feinstruktur innerhalb des porösen Gewebes zu beschichten. Daher kann das mit Silber versetzte Material, das durch das Beschichten der verwitterten Riff-bildenden Koralle mit Silber gemäß der vorliegenden Erfindung erhalten wird, eine längere Lebensdauer haben als Filtermedien mit üblichen mit Silber versetzten Materialien. Es kann ebenso in Bezug auf seine Sterilisierungswirksamkeit verbessert werden und kann eine höhere Sterilisierungswirkung gegenüber Bakterien, die zur Art der Escherichia coli gehören, wie Darmbakterien und pathogene Darmbakterien, diatopathogene Bakterien (sitotoxische oder Nahrungsmittel vergiftende Bakterien) wie Salmonellen, Vibrio parahaemoliticus und Staphylococcus aureus, Bacillus anthracis (Anthraxbazillen) und Enterokokken.The weathered reef-building coral material is also available as materials for with Silver offset materials useful. There in the weathered reef-forming Coral material of the present invention, the material from the the organic substances, those of sea algae, microorganisms and the like come from all the fine structure within the porous Tissues were removed, it is possible in particular, the weathered reef-forming Coral with silver on their particles or grain surfaces and as well within their fine structure within the porous tissue to coat. Therefore, the silver added material, the by coating the weathered reef-building coral with Silver according to the present Invention is a longer Lifetime have as filter media with usual offset with silver Materials. It may also be in terms of its sterilization efficacy can be improved and can have a higher sterilizing effect across from Bacteria belonging to the species of Escherichia coli, such as intestinal bacteria and pathogenic intestinal bacteria, diatopathogenic bacteria (sitotoxic or food-poisoning bacteria) such as Salmonella, Vibrio parahaemoliticus and Staphylococcus aureus, Bacillus anthracis (anthrax bacilli) and enterococci.

In einem Verfahren zur Herstellung zur Herstellung des mit Silber versetzten Materials, ausgehend von dem verwitterten Riff-bildenden Korallenmaterial, wie dem vorstehenden Verfahren zur Herstellung von Nahrungsmittelmaterialien oder Filterme dien, wird die verwitterte Riff-bildende Koralle mit Wasser nach dem alkalischen Waschen gewaschen und anschließend getrocknet und wird weiterhin einem Rösten unterzogen. Falls zu diesem Zweck die verwitterte Riff-bildende Koralle verwendet wird, ist es bevorzugt, diejenige zu verwenden, die gemäß den Zwecken für das das mit Silber versetzte Material verwendet werden soll, gesiebt wurde. Wenn das mit Silber versetzte Material beispielsweise als Filtermedien verwendet werden soll, ist es bevorzugt, dasjenige zu verwenden, das eine Korngröße von 0,71 mm oder mehr aufweist.In a process for the preparation of the silver added Material from the weathered reef-building coral material, such as the above method for producing food materials or filter media, the weathered reef-building coral becomes with Washed water after alkaline washing and then dried and will continue to roast subjected. If for that purpose the weathered reef-building Coral is used, it is preferable to use the one the according to the purposes for the the silver-staggered material is to be used has been. For example, if the material added with silver is as Filter media is to be used, it is preferred that one to use that has a grain size of 0.71 mm or more.

Nach dem Rösten wird die verwitterte Riff-bildende Koralle in eine wässrige Silberlösung unter reduziertem Druck eingetaucht, wobei die wässrige Silberlösung in die verwitterte Riff-bildende Koralle überall in ihrer Feinstruktur innerhalb des porösen Gewebes eindringt. Dabei kann als wässrige Silberlösung bevorzugt eine wässrige Silbernitratlösung oder dergleichen verwendet werden. Ihre Konzentration kann geeigneterweise gemäß der Menge an zu beschichtendem Silber bestimmt werden. Üblicherweise kann sie im Bereich von 4 bis 6 Gew.-% eingestellt werden. Das Ausmaß des anzulegenden Vakuums, wenn die verwitterte Riff-bildende Koralle in die wässrige Silberlösung eingetaucht wird, kann das gleiche sein wie dasjenige im Falle des alkalischen Waschens oder des Waschens mit Wasser wie es vorstehend beschrieben wurde. Nachdem die verwitterte Riff-bildende Koralle so in die wässrige Silberlösung eingetaucht wurde, wird die wässrige Silberlösung entfernt und ein Reduktionsmittel zugegeben, so dass das Silber in der wässrigen Silberlösung, das an der verwitterten Riff-bildenden Koralle anhaftet, reduziert wird und sich abscheidet. Als Reduktionsmittel kann eine wässrige Lösung eines Reduktionsmittels, wie eine Ascorbinsäurelösung, eine Erysovinlösung oder eine Glucoselösung verwendet werden. Damit die verwitterte Riff-bildende Koralle mit Silber gut beschichtet werden kann, muss sie üblicherweise über einen Zeitraum von ungefähr 30 bis 60 Minuten in die Lösung des Reduktionsmittels eingetaucht werden. Anschließend wird jeder Überschuss der Reduktionsmittellösung entfernt, gefolgt vom Erhitzen, beispielsweise bei ungefähr 400°C für 30 bis 60 Minuten zur Vervollständigung der Silberreduktion. Dabei kann das Erhitzen vorzugsweise dann ausgeführt werden, wenn die verwitterte Riff-bildende Koralle aus dem Gefäß, in das Reduktionsmittel zugegeben wurde, in einen davon getrennten elektrischen Ofen oder dergleichen überführt wurde.To roasting The weathered reef-building coral is immersed in an aqueous silver solution immersed in reduced pressure, wherein the aqueous silver solution in the weathered reef-building coral throughout their fine structure within the porous Tissue penetrates. Here, as an aqueous silver solution preferably a aqueous Silver nitrate solution or the like can be used. Your concentration may be appropriate according to the amount to be coated on silver to be coated. Usually, she can work in the field be adjusted from 4 to 6 wt .-%. The extent of the vacuum to be applied, when the weathered reef-building coral is immersed in the aqueous silver solution can be the same as that in the case of alkaline Washing or washing with water as described above has been. After soaking the weathered reef-building coral in the aqueous silver solution became the watery Silver solution removed and a reducing agent added so that the silver in the aqueous Silver solution which clings to the weathered reef-building coral, reduced becomes and separates. As the reducing agent, an aqueous solution of a Reducing agent, such as an ascorbic acid solution, a Erysovinlösung or a glucose solution be used. With the weathered reef-building coral Silver can be well coated, it usually has one Period of about 30 to 60 minutes into the solution of the reducing agent are immersed. Subsequently, will every surplus the reducing agent solution followed by heating, for example at about 400 ° C for 30 to 60 minutes to complete the silver reduction. The heating may then preferably be carried out when the weathered reef-building coral emerges from the vessel into which Reducing agent was added, in a separate electric furnace or the like has been transferred.

Gemäß den üblichen Verfahren werden anschließend die Schritte des Kühlens, des Waschens mit Wasser, des Trocknens und des Verpackens zur Vermarktung durchgeführt.According to the usual Procedures will follow the steps of cooling, washing with water, drying and packaging for marketing carried out.

Wenn das mit Silber versetzte Material so hergestellt wird, kann die Zeit, über die die verwitterte Riff-bildende Koralle in die wässrige Silberlösung eingetaucht wird, und die bei ungefähr 96 Stunden in üblichen Verfahren zur Herstellung von mit Silber versetzten Materialien liegt, auf ungefähr 30 bis 60 Minuten verkürzt werden und daher ist es möglich, die Produktivität in Bezug auf mit Silber versetzten Materialien dramatischem Ausmaß zu verbessern.When the silver-added material is so prepared, the time over which the weathered reef-building coral is immersed in the aqueous silver solution, and at about 96 hours in übli It is possible to shorten the productivity of silver added materials to a dramatic extent by shortening them to about 30 to 60 minutes.

Die Vorrichtung zur Eintauchbehandlung bei der Durchführung des Verfahrens zur Herstellung des verwitterten Riff-bildenden Korallenmaterials der vorliegenden Erfindung ist nachfolgend beschrieben.The Device for immersion treatment in carrying out the A method of making the weathered reef-building coral material The present invention is described below.

2 veranschaulicht eine Vorrichtung zur Eintauchbehandlung zur Behandlung der verwitterten Riff-bildenden Koralle gemäß der vorliegenden Erfindung. Die in 2 gezeigte Vorrichtung umfasst einen abgeschlossenen Behälter 2 für die Aufnahme der zu behandelnden verwitterten Riff-bildenden Koralle 1, einen hohlen zylindrischen Korb 3, der aus Edelstahl besteht und in dem die verwitterte Riff-bildende Koralle 1 innerhalb des abgeschlossenen Containers getan wird; eine Rührflügelblatt 4 am zentralen hohlen Raum des Korbs 3 und einen Motor 5 zum Rotieren lassen des Rührflügelblatts 4. Ein Gefäß zur Lagerung der wässrigen alkalischen Lösung 6 ist am geschlossenen Container 2 angebracht. Der geschlossene Container 2 wird mit einem Zuleitungsrohr 7 versehen, zur Einführung der wässrigen alkalischen Lösung in den geschlossenen Container 2 von dem Vorratsgefäß 6. Der geschlossene Container 2 wird ebenso mit einem Zufuhrrohr 8 zur Zuführung von Wasser oder einer wässrigen Silberlösung in den geschlossenen Container 2 versehen, einer Zufuhrleitung 9 zur Einführung des Reduktionsmittels in dem geschlossenen Container 2 und in einem Flüssigkeitsablassrohr 10 zum Ablassen des Spülwassers aus dem geschlossenen Container 2. Diese Zufuhrrohre 7, 8 und 9 und das Flüssigkeitsablassrohr 10 sind weiterhin mit Ventilen versehen zur Kontrolle der Menge der Flüssigkeit, die eingeführt werden soll oder abgelassen werden soll. Am unteren Ende des geschlossenen Containers 2 wird ein Heizrohr 11 zum Erhitzen des Inneren des geschlossenen Containers 2 intern bereitgestellt. Mit dem geschlossenen Container 2 ist eine Vakuumpumpe 12 zur Evakuierung seines Innenraums verbunden. Innerhalb des geschlossenen Containers 2 ist der Korb 3 durch vier bis sechs Träger 13 unterstützt. 2 FIG. 12 illustrates an immersion treatment apparatus for treating the weathered reef-building coral according to the present invention. FIG. In the 2 The device shown comprises a sealed container 2 for the reception of the weathered reef-building coral to be treated 1 , a hollow cylindrical basket 3 which is made of stainless steel and in which the weathered reef-building coral 1 is done inside the closed container; an agitator blade 4 at the central hollow space of the basket 3 and a motor 5 to rotate the agitator blade 4 , A vessel for storage of the aqueous alkaline solution 6 is at the closed container 2 appropriate. The closed container 2 comes with a supply pipe 7 provided for introducing the aqueous alkaline solution in the closed container 2 from the storage vessel 6 , The closed container 2 is also with a feed tube 8th for supplying water or an aqueous silver solution into the closed container 2 provided, a supply line 9 for the introduction of the reducing agent in the closed container 2 and in a liquid drain tube 10 for draining the rinse water from the closed container 2 , These feed pipes 7 . 8th and 9 and the liquid drain tube 10 are also provided with valves to control the amount of liquid to be introduced or discharged. At the bottom of the closed container 2 becomes a heating pipe 11 for heating the interior of the closed container 2 provided internally. With the closed container 2 is a vacuum pump 12 connected to the evacuation of his interior. Inside the closed container 2 is the basket 3 by four to six carriers 13 supported.

In Bezug auf die inneren Wände von wenigstens dem geschlossenen Container 2, den Zufuhrrohren 7, 8 und 9 und dem Flüssigkeitsablassrohr 10 ist es erforderlich, dass sie aus einem Metall bestehen, das eine Korrosionsbeständigkeit gegenüber einer wässrigen alkalischen Lösung aufweist. Als Vakuumpumpe 12 wird eine Vakuumpumpe verwendet, die das Innere des geschlossenen Containers 2 bis zu einem Vakuum von 70 mmHg oder niedriger evakuieren kann und vorzugsweise 30 mmHg oder niedriger.With respect to the inner walls of at least the closed container 2 , the feed pipes 7 . 8th and 9 and the liquid drain tube 10 It is necessary that they are made of a metal having a corrosion resistance to an aqueous alkaline solution. As a vacuum pump 12 a vacuum pump is used, which is the interior of the closed container 2 can evacuate to a vacuum of 70 mmHg or lower, and preferably 30 mmHg or lower.

In einem Verfahren für das alkalische Waschen der verwitterten Riff-bildenden Koralle 1 unter Verwendung dieser Vorrichtung wird zuerst die verwitterte Riff-bildende Koralle 1 in dem Korb 3 innerhalb des geschlossenen Containers 2 gelegt. Anschließend wird die wässrige alkalische Lösung durch das Zufuhrrohr 7 zugeführt. Anschließend wird die Vakuumpumpe 12 zur Evakuierung des Inneren des geschlossenen Containers 2 auf ein Vakuum von 70 mmHg oder niedriger und bevorzugt 30 mmHg oder niedriger angestellt.In a process for the alkaline washing of the weathered reef-building coral 1 using this device becomes first the weathered reef-building coral 1 in the basket 3 inside the closed container 2 placed. Subsequently, the aqueous alkaline solution is passed through the feed tube 7 fed. Subsequently, the vacuum pump 12 to evacuate the interior of the closed container 2 to a vacuum of 70 mmHg or lower, and preferably 30 mmHg or lower.

Gleichzeitig mit der Evakuierung treibt der Motor 5 das Rührflügelblatt 4 an, um so Flüssigkeitsströme zu bilden, die von oben nach unten in Längsrichtungen innerhalb des Korbes 3 und wie sie durch den Pfeil in 3 gezeigt werden, zu bilden, damit die wässrige alkalische Lösung kräftig durch die verwitterte Riff-bildende Koralle 1, die sich im Korb 3 befindet, durchgeleitet wird. Heißes Wasser wird ebenfalls durch das Heizrohr 11 durchgleitet, um den geschlossenen Container 2 auf 80 bis 100°C zu erhitzen. Ein derartiges alkalisches Waschen wird üblicherweise für 30 bis 60 Minuten durchgeführt. Dadurch werden die Meeresalgen, die organischen Substanzen, die von Mikroorganismen stammen und dergleichen, die an der Oberfläche und in der feinen Struktur innerhalb des porösen Gewebes der verwitterten Riff-bildenden Koralle 1 vorhanden sind, in der wässrigen alkalischen Lösung gelöst und entfernt.Simultaneously with the evacuation drives the engine 5 the agitator blade 4 so as to form liquid flows from top to bottom in longitudinal directions within the basket 3 and as indicated by the arrow in 3 be shown, so that the aqueous alkaline solution vigorously through the weathered reef-building coral 1 that are in the basket 3 is passed through. Hot water is also through the heating tube 11 slides through to the closed container 2 to heat to 80 to 100 ° C. Such alkaline washing is usually carried out for 30 to 60 minutes. Thereby, the marine algae, the organic substances derived from microorganisms and the like, those at the surface and in the fine structure become inside the porous tissue of the weathered reef-building coral 1 are dissolved in the aqueous alkaline solution and removed.

Im Verfahren für das alkalische Waschen der verwitterten Riff-bildenden Koralle 1 unter Verwendung der Vorrichtung in 2, kann der Schritt des Eintauchens der verwitterten Riff-bildenden Koralle 1 in die wässrige alkalische Lösung und den Schritt des Evakuierens des Inneren des geschlossenen Containers 2 jeweils ausgetauscht werden, so dass das Innere des geschlossenen Containers 2 durch die Vakuumpumpe 12 evakuiert wird und anschließend die wässrige alkalische Lösung eingeführt wird, um die verwitterte Riff-bildende Koralle 1 in die wässrige alkalische Lösung einzutauchen. Wenn das Innere des geschlossenen Containers 2 evakuiert wird nachdem die verwitterte Riff-bildende Koralle 1 in die wässrige alkalische Lösung eingetaucht wurde, kann das alkalische Waschen der verwitterten Riff-bildenden Koralle 1 mit guter Funktionsfähigkeit durchgeführt werden. Umgekehrt, wenn die verwitterte Riff-bildende Koralle 1 in die wässrige alkalische Lösung eingetaucht wird, nachdem das Innere des geschlossenen Containers 2 evakuiert wurde, kann die wässrige alkalische Lösung ebenfalls sich innerhalb der gesamten Feinstruktur innerhalb des porösen Gewebes in kurzer Zeit ausbreiten.In the process for the alkaline washing of the weathered reef-building coral 1 using the device in 2 , the step of diving the weathered reef-building coral 1 into the aqueous alkaline solution and the step of evacuating the inside of the closed container 2 each exchanged, leaving the interior of the closed container 2 through the vacuum pump 12 is evacuated and then the aqueous alkaline solution is introduced to the weathered reef-building coral 1 into the aqueous alkaline solution. If the inside of the closed container 2 is evacuated after the weathered reef-building coral 1 was immersed in the aqueous alkaline solution, alkaline washing of the weathered reef-building coral 1 be carried out with good functionality. Conversely, if the weathered reef-building coral 1 immersed in the aqueous alkaline solution after the inside of the closed container 2 Also, the aqueous alkaline solution may spread within the entire fine structure within the porous tissue in a short time.

Nach dem alkalischen Waschen wird die verwendete wässrige alkalische Lösung durch das Flüssigkeitsablassrohr 10 abgelassen.After alkaline washing, the aqueous alkaline solution used is passed through the liquid drain tube 10 drained.

In dem Verfahren zum Waschen der verwitterten Riff-bildenden Koralle mit Wasser nach dem vorstehend erwähnten alkalischen Waschen unter Verwendung der Vorrichtung aus 2, kann die wässrige alkalische Lösung, die in dem alkalischen Waschen verwendet wurde, durch Wasser ersetzt werden und die gleiche Operation wie die vorstehende kann wiederholt werden. Insbesondere wird Wasser durch den geschlossenen Container 2 durch die Zufuhrleitung 8 eingeführt, um die verwitterte Riff-bildende Koralle 1 in Wasser einzutauchen, und anschließend wird das Innere des geschlossenen Containers 2 evakuiert. Alternativ dazu wird das Innere des geschlossenen Containers 2, der die verwitterte Riff-bildende Koralle 1 enthält, vorher evakuiert und anschließend wird Wasser durch das Zufuhrrohr 8 eingeführt, um die verwitterte Riff-bildende Koralle 1 in Wasser einzutauchen. Anschließend lässt man das Rührflügelblatt 4 rotieren, um Wasser durch die verwitterte Riff-bildende Koralle 1, die sich im Korb 3 befindet, kräftig durchzuleiten. Anschließend wird das verwendete Waschwasser durch das Wasserablassrohr 10 abgelassen. Dieses Waschen mit Wasser wird durchgeführt, bis der pH-Wert des Waschwassers, das verwendet wurde und aus dem Flüssigkeitsablassrohr 10 stammt, neutral wird.In the method of washing the weathered reef-building coral with water after the above-mentioned alkaline washing using the apparatus 2 For example, the aqueous alkaline solution used in the alkaline washing may be replaced with water, and the same operation as the above may be repeated. In particular, water is through the closed container 2 through the supply line 8th introduced to the weathered reef-building coral 1 immerse in water, and then the inside of the closed container 2 evacuated. Alternatively, the interior of the closed container 2 who used the weathered reef-building coral 1 contains, previously evacuated and then water is through the supply pipe 8th introduced to the weathered reef-building coral 1 immerse in water. Then you leave the agitator blade 4 rotate to water through the weathered reef-building coral 1 that are in the basket 3 is to pass through vigorously. Subsequently, the used washing water through the water drain pipe 10 drained. This washing with water is carried out until the pH of the wash water that has been used and out of the liquid drain tube 10 comes, becomes neutral.

Die in 2 gezeigte Vorrichtung kann ebenfalls zur Herstellung eines mit Silber versetzten verwitterten Riff-bildenden Korallenmaterials verwendet werden. Dabei wird die verwitterte Riff-bildende Koralle 1, die mit Silber beschichtet werden soll, vorzugsweise einem alkalischen Waschen und Wasserwaschen wie vorstehend beschrieben unterzogen, gefolgt von Trocknen und wird weiter einer Desinfizierung durch trockene Hitze oder durch trockene Sterilisation oder Rösten unterzogen. Die entstehende verwitterte Riff-bildende Koralle 1 wird in den Korb 3 getan. Anschließend wird eine wässrige Silberlösung in den geschlossenen Container 2 durch das Zufuhrrohr 8 eingeführt, um die verwitterte Riff-bildende Koralle in dieser wässrigen Silberlösung unter reduziertem Druck gut einzutauchen. Anschließend wird die überschüssige wässrige Silberlösung durch das Flüssigkeitsablassrohr 10 abgelassen und anschließend wird eine Lösung eines Reduktionsmittels wie eine Ascorbinsäurelösung durch das Zufuhrrohr 9 und durch reduziertem Druck eingeführt, um die wässrige Silberlösung, die sich an der Oberfläche und der Feinstruktur innerhalb des porösen Gewebes der verwitterten Riff-bildenden Koralle 1 anhaftet, zu reduzieren. Anschließend wird die verbliebene Lösung des Reduktionsmittels über das Flüssigkeitsablassrohr 10 abgelassen. Anschließend wird die entstehende verwitterte Riff-bildende Koralle zu Heizmitteln wie einem elektrischen Ofen, der getrennt bereitgestellt ist, überführt und dort bei ungefähr 400°C für 30 bis 60 Minuten erhitzt. Daher ist es möglich, ein mit Silber versetztes Material zu erhalten, dessen verwitterte Riff-bildende Koralle mit Silber auf ihrer Oberfläche und ebenfalls innerhalb ihrer Feinstruktur innerhalb des porösen Gewebes beschichtet wurde und eine verbesserten Sterilisierungswirkung aufweist.In the 2 The apparatus shown may also be used to make a silver-plated weathered reef-building coral material. This is the weathered reef-forming coral 1 which is to be coated with silver, preferably subjected to alkaline washing and water washing as described above, followed by drying, and further subjected to dry heat disinfection or dry sterilization or roasting. The resulting weathered reef-building coral 1 will be in the basket 3 done. Subsequently, an aqueous silver solution in the closed container 2 through the supply pipe 8th to immerse the weathered reef-building coral well in this aqueous silver solution under reduced pressure. Subsequently, the excess aqueous silver solution is passed through the liquid drain tube 10 and then a solution of a reducing agent such as an ascorbic acid solution is discharged through the feed tube 9 and introduced by reduced pressure to the aqueous silver solution adhering to the surface and the fine structure within the porous tissue of the weathered reef-building coral 1 attached, reduce. Subsequently, the remaining solution of the reducing agent via the liquid outlet tube 10 drained. Subsequently, the resulting weathered reef-building coral is transferred to heating means such as an electric furnace provided separately and heated there at about 400 ° C for 30 to 60 minutes. Therefore, it is possible to obtain a silver-added material whose weathered reef-building coral has been coated with silver on its surface and also within its fine structure within the porous tissue and has an improved sterilizing effect.

Die Vorrichtung zur Eintauchbehandlung ist für das alkalische Waschen der verwitterten Riff-bildenden Koralle und für die Herstellung des mit Silber versetzten Materials, wie vorstehend beschrieben, nützlich. Außerdem kann sie ebenso für jede Behandlung, die mit einem Eintauchen zusammenhängt, nützlich sein, beispielsweise für das Waschen, das Beschichten oder das Extrahieren von verschiedenen zu behandelnden Materialien. Insbesondere kann sie beispielsweise als Vorrichtung zur Extrahierung von nützlichen Substanzen oder physiologisch aktiven Substanzen verwendet werden, indem Gewürze, Pflanzenwurzeln oder Borke und getrocknete Produkte, Früchte oder Samen oder andere Ausgangsmaterialien für Nahrungsmittel oder Medizin in einem Extraktionslösungsmittel eingetaucht werden, um Substanzen die in den entsprechenden Ausgangsmaterialien enthalten sind, zu extrahieren.The Device for immersion treatment is for alkaline washing the weathered reef-building coral and for making the one with silver staggered material as described above. Furthermore she can as well for any treatment that comes with a dive, be useful for example washing, coating or extracting different ones to be treated materials. In particular, she can, for example as a device for extracting beneficial substances or physiologically active substances are used by spices, plant roots or bark and dried products, fruits or seeds or other starting materials for food or medicine in an extraction solvent be dipped to substances in the appropriate starting materials are included, extract.

Die Vorrichtung zur Eintauchbehandlung kann in verschiedener Weise modifiziert werden, entsprechend den Zwecken für die die Vorrichtung verwendet wird, solange der geschlossene Container, dessen Inneres evakuiert werden kann, der hohle zylindrische Korb zum Aufnehmen des zu bearbeitenden Materials, der im Container bereitgestellt ist und das Rührflügelblatt, das innerhalb des hohlen Raums rotiert, vorhanden sind, um einen vertikalen Flüssigkeitsstrom im Korb zu erzeugen. Beispielsweise kann der Korb aus einem Material hergestellt sein, das in geeigneter Weise aus denjenigen ausgewählt ist, die nicht durch die Waschlösung oder die Behandlungslösung, die für die zu behandelnden Materialien verwendet wird, angegriffen wird. Ebenso kann das Material des Netzes, das den Korb bildet, jede mesh-Größe, die in geeigneter Weise gemäß der Größe der zu behandelnden Materialien bestimmt wurde, verwendet werden. Die Zufuhrleitungen zur Einführung der Waschlösung oder der Behandlungslösung und das Flüssigkeitsablassrohr müssen ebenfalls nicht notwendigerweise am geschlossenen Container angebracht sein.The Device for immersion treatment can be modified in various ways are used, according to the purposes for which the device will, as long as the closed container evacuates its interior can be, the hollow cylindrical basket for receiving the machined Material provided in the container and the agitator blade, which are rotated within the hollow space, present to one vertical liquid flow to create in the basket. For example, the basket may be made of a material be suitably selected from those not through the washing solution or the treatment solution, the for the materials to be treated is attacked. Likewise, the material of the net that forms the basket can be any mesh size, the appropriately according to the size of the treatment materials was determined. The supply lines for the introduction the washing solution or the treatment solution and the liquid drain tube have to also not necessarily attached to the closed container be.

Die vorliegende Erfindung wird nachstehend detaillierter unter Angabe von Beispielen beschrieben. Die vorliegende Erfindung wird in keiner Weise durch diese Beispiele beschränkt.The The present invention will be described in more detail below described by examples. The present invention is not in any Way limited by these examples.

Vergleichsbeispiel 1Comparative Example 1

Ausgangsmaterial aus verwitterter Riff-bildender Koralle wurde zum Sieben auf ein Schüttelsieb gebracht und 20 kg verwitterter Riff-bildender Koralle mit einer Korngröße von 2 mm bis 1 mm wurden in Korb 3 in den geschlossenen Container 2, der in 2 gezeigten Vorrichtung eingebracht. Zur Vorwäsche dieser verwitterten Riff-bildenden Koralle wurde Leitungswasser durch die Zufuhrleitung 8 eingeführt, das Rührflügelblatt 4 wurde rotieren gelassen, um Wasser durch die verwitterte Riff-bildende Koralle über 30 Minuten kräftig durchzuleiten. Die Waschlösung wurde in einen Abwasserbehandlungstank durch das Flüssigkeitsablassrohr 10 geschickt.Starting material of weathered reef-building coral was placed on a shaking screen for sieving and 20 kg of weathered reef-building coral with a grain size of 2 mm to 1 mm were placed in basket 3 in the closed container 2 who in 2 introduced device shown. For pre-washing this weathered reef-building coral was tap water through the supply line 8th introduced, the agitator blade 4 was rotated to vigorously pass water through the weathered reef-building coral for 30 minutes. The wash solution was placed in a wastewater treatment tank through the liquid drain tube 10 cleverly.

Anschließend wurde während der Operation des alkalischen Waschens zuerst die Vakuumpumpe 12 für die Evakuierung des Inneren des geschlossenen Containers 2 auf ein Vakuum von 10 mmH2O in Betrieb genommen und 25 l einer wässrigen 0,1 N Natriumhydroxidlösung, die vorher in dem Vorratsgefäß 6 hergestellt wurde, in den geschlossenen Container 2 über das Zufuhrrohr 7 zugeführt. Anschließend wurde heißes Wasser mit einer Temperatur von 80°C durch das Heizrohr 11 durchgeleitet, damit über 30 Minuten das Innere des geschlossenen Containers 2, in dem die wässrige Natriumhydroxidlösung kräftig durch die verwitterte Riff-bildende Koralle durchgeleitet wurde, erhitzt wurde. Nachdem das alkalische Waschen vollständig war, wurde die Zufuhr von heißem Wasser in dem Heizrohr 11 gestoppt und ebenso wurde der Zustand des Vakuums des Inneren des geschlossenen Containers 2 auf Normaldruck zurückgeführt. Anschließend wurde die im geschlossenen Container 2 befindliche wässrige Natriumhydroxidlösung vollständig durch das Flüssigablassrohr 10 abgelassen.Subsequently, during the alkaline washing operation, the vacuum pump first became 12 for the evacuation of the interior of the closed container 2 put into operation at a vacuum of 10 mmH 2 O and 25 l of an aqueous 0.1 N sodium hydroxide solution previously in the storage vessel 6 was made in the closed container 2 over the supply pipe 7 fed. Subsequently, hot water at a temperature of 80 ° C through the heating tube 11 passed so that over 30 minutes inside the closed container 2 in which the aqueous sodium hydroxide solution was vigorously passed through the weathered reef-building coral was heated. After the alkaline washing was complete, the supply of hot water in the heating tube became 11 stopped and also the condition of the vacuum of the interior of the closed container 2 returned to normal pressure. Then it was in the closed container 2 aqueous sodium hydroxide solution completely through the liquid drain pipe 10 drained.

Wiederum wurde Leitungswasser durch das Zuflussrohr 10 eingeführt und die gleiche Operation wie vorstehend wurde wiederholt, mit der Ausnahme, dass Leitungswasser anstelle der vorstehenden wässrigen alkalischen Lösung verwendet wurde zur Durchführung des Waschens mit Wasser. Dieses Waschen mit Wasser wurde zweimal wiederholt durchgeführt. Insbesondere wurde nach dem ersten Waschen mit Wasser das Wasser durch das Flüssigablassrohr 10 abgelassen und gesammelt, um seinen pH-Wert zu messen und dieser wurde mit 8,1 bestimmt. Der pH des Abwassers nach dem zweimaligen Waschen mit Wasser betrug 7.0 Dementsprechend wurde das Waschen mit Wasser anschließend gestoppt.Again tap water was through the inflow pipe 10 and the same operation as above was repeated except that tap water was used instead of the above aqueous alkaline solution to carry out the washing with water. This water washing was repeated twice. In particular, after the first water wash, the water passed through the liquid drain tube 10 drained and collected to measure its pH and this was determined to be 8.1. The pH of the effluent after washing twice with water was 7.0. Accordingly, the washing with water was then stopped.

Das alkalische Waschen und das Waschen mit Wasser erforderte insgesamt 30 Minuten.The alkaline washing and washing with water required a total 30 minutes.

Eine Probe, die nach dem Waschen mit Wasser gefolgt von Entwässerung und Trocknen erhalten wurde, wurde als Prüfling verwendet und ihr Rohproteingehalt und die Anzahl der allgemeinen Bakterien (Zellen/Gramm) wurde bestimmt. Hier wurde der Rohproteingehalt, ausgehend vom Gesamtstickstoff, über die halbmikroskopische Kjeldahl-Methode bestimmt und die Anzahl der allgemeinen Bakterien (Zel len/Gramm) wurde durch einen mikrobiologischen Test (Standard Agar Medium Verfahren) bestimmt. Es wurden ebenfalls zu Vergleichszwecken der Rohproteingehalt und die Zahl der allgemeinen Bakterien auf dem verwitterten Riff-bildenden Korallenausgangsmaterial gemessen.A Sample after washing with water followed by drainage and drying was used as the sample and its crude protein content and the number of common bacteria (cells / gram) was determined. Here, the crude protein content, starting from the total nitrogen, on the semi-microscopic Kjeldahl method determines and the number of common bacteria (Cell / gram) was determined by a microbiological test (standard Agar medium method). There were also for comparison purposes the crude protein content and the number of common bacteria measured from the weathered reef-building coral source material.

Vergleichsbeispiel 2Comparative Example 2

Das alkalische Waschen wurde in der gleichen Weise wie in Vergleichsbeispiel 1 durchgeführt mit der Ausnahme, dass die verwitterte Riff-bildende Koralle mit einer Korngröße von 2 mm bis 1 mm, die in Vergleichsbeispiel verwendet wurde, durch 20 kg einer verwitterten Riff-bildenden Koralle mit einer Korngröße von 5 mm bis 4 mm ersetzt wurde und 25 l einer wässrigen 0,1 N Natriumhydroxidlösung wurde durch eine wässrige 1,0 N Natriumhydroxidlösung ersetzt. Anschließend wurde die wässrige Natriumhydroxidlösung im Vorratsbehälter vollständig abgelassen.The alkaline washing was carried out in the same manner as in Comparative Example 1 performed with the exception that the weathered reef-building coral with a grain size of 2 mm to 1 mm used in Comparative Example by 20 kg of weathered reef-building coral with a grain size of 5 mm to 4 mm was replaced and 25 l of an aqueous 0.1 N sodium hydroxide solution through an aqueous 1.0 N sodium hydroxide solution replaced. Subsequently became the watery sodium hydroxide in the storage container Completely drained.

Anschließend wurde das Waschen mit Wasser in der gleichen Weise wie im Vergleichsbeispiel wiederholt und der pH-Wert des Abwassers wurde jedes Mal bestimmt, wenn das Waschen mit Wasser vollständig war. Als Ergebnis betrugen die pH-Werte des Abwassers für die ersten bis dritten Male 8,8, 8,1 und 7,4 und der pH-Wert des Abwassers beim vierten Mal betrug 7,0. Dementsprechend wurde das Waschen mit Wasser danach gestoppt.Subsequently was washing with water in the same manner as in the comparative example repeated and the pH of the effluent was determined each time when the washing with water was complete. As a result, the pH of the wastewater for the first to third times 8,8, 8,1 and 7,4 and the pH of the wastewater the fourth time was 7.0. Accordingly, the washing was with Water stopped after that.

Dieses alkalische Waschen und das Waschen mit Wasser benötigte insgesamt 55 Minuten.This alkaline washing and washing with water took a total 55 minutes.

Beispiel 1example 1

Das alkalische Waschen wurde in der gleichen Weise wie in Vergleichsbeispiel 1 durchgeführt mit der Ausnahme, dass die verwitterte Riff-bildende Koralle mit einer Korngröße von 2 mm bis 1 mm, die in Vergleichsbeispiel 1 verwendet wurde, durch eine verwitterte Riff-bildende Koralle mit einer Korngröße von 8 mm bis 5 mm ersetzt wurde. Anschließend wurde die wässrige Natriumhydroxidlösung im Vorratsbehälter vollständig abgelassen. Anschließend wurde das Waschen mit Wasser wiederholt zweimal in der gleichen Weise wie in Vergleichsbeispiel 1 durchgeführt und es wurde nachgewiesen dass sich der pH-Wert des Abwassers auf 7,0 änderte.The alkaline washing was carried out in the same manner as in Comparative Example 1 with the Except that the weathered reef-building coral with a grain size of 2 mm to 1 mm, which was used in Comparative Example 1, was replaced by a weathered reef-building coral with a grain size of 8 mm to 5 mm. Subsequently, the aqueous sodium hydroxide solution in the reservoir was completely drained. Thereafter, washing with water was repeatedly carried out twice in the same manner as in Comparative Example 1, and it was confirmed that the pH of the waste water changed to 7.0.

Anschließend wurden das Waschen mit Wasser, Entwässerung und Trocknen durchgeführt, gefolgt von einem Rösten (500°C, 60 Minuten), Abkühlen und Einstellen der Korngröße (Sieben), um ein Filtermedium für Wasserreiniger zu erhalten.Subsequently were washing with water, drainage and dried, followed by a roasting (500 ° C, 60 minutes), cool down and adjusting the grain size (sieves), to a filter medium for To get water purifier.

Die Zahl der allgemeinen Bakterien (Zellen/Gramm) des Filtermediums für Wasserreiniger, das so erhalten wurde, wurden in der gleichen Weise wie im Vergleichsbeispiel 1 durch einen mikrobiologischen Test (die Standard Agar Medium Methode) bestimmt. Zur Beurteilung der Adsorptionsfähigkeit dieses Filtermediums wurden 50 g dieses Filtermediums in eine Säule mit einem Innendurchmesser von 130 mm und einer Höhe von 130 mm gegeben, um einen Entfärbungstest unter Verwendung von 100 ml einer 0,02% Methylenblaulösung durchzuführen. Die Geschwindigkeit der Adsorption von Methylenblau, das in der Methylenblaulösung vorhanden ist, die durch die Säule durchgeleitet wurde, wurde gemäß dem nachstehenden Ausdruck bestimmt:The Number of common bacteria (cells / gram) of filter media for water purifier, thus obtained were in the same manner as in the comparative example 1 by a microbiological test (the standard agar medium method) certainly. To assess the adsorption capacity of this filter medium 50 g of this filter medium was placed in a column with an inside diameter of 130 mm and a height of 130 mm is given to use a decolorization test of 100 ml of a 0.02% methylene blue solution. The Rate of adsorption of methylene blue present in the methylene blue solution is that through the pillar was conducted according to the following Expression determines:

Figure 00210001
Figure 00210001

Die Aktivität dieses Filtermediums wurde ebenfalls berechnet gemäß: Aktivität (%) = 100 – Adsorptionsgeschwindigkeit The activity of this filter medium was also calculated according to: Activity (%) = 100 - adsorption rate

Die Ergebnisse, die so erhalten wurden, sind in Tabelle 1 gezeigt.The Results thus obtained are shown in Table 1.

Beispiel 2Example 2

Das alkalische Waschen wurde in der gleichen Weise wie in Vergleichsbeispiel 2 durchgeführt mit der Ausnahme, dass eine verwitterte Riff-bildende Koralle mit einer Korngröße von 5 mm bis 4 mm wie sie in Vergleichsbeispiel 2 verwendet wurde, durch 20 kg einer verwitterten Riff-bildenden Koralle mit einer Korngröße von 8 mm bis 5 mm ersetzt wurden. Anschließend wurde das Waschen mit Wasser viermal durchgeführt und der pH des Abwassers wurde dahingehend bestimmt, dass er 7,0 betrug.The alkaline washing was carried out in the same manner as in Comparative Example 2 performed with the exception of having a weathered reef-building coral a grain size of 5 mm to 4 mm as used in Comparative Example 2, by 20 kg of weathered reef-building coral with a grain size of 8 mm to 5 mm were replaced. Subsequently, the washing was done with Water performed four times and the pH of the effluent was determined to be 7.0 amounted to.

Anschließend wurde das Waschen mit Wasser, das Entwässern und das Trocknen durchgeführt, weiter gefolgt von Rösten (500°C, 60 Minuten), Abkühlen und Einstellen der Korngröße (Sieben), um ein Filtermedium für Wasserreiniger zu erhalten.Subsequently was washing with water, draining and the drying carried out, followed by roasting (500 ° C, 60 minutes), cool down and adjusting the grain size (sieves), to a filter medium for To get water purifier.

Die Anzahl der allgemeinen Bakterien (Zellen/Gramm) des Filtermediums für Wasserreiniger, das so erhalten wurde, wurde in der gleichen Weise wie in Beispiel 1 bestimmt. Damit die Adsorptionsfähigkeit dieses Filtermediums bestimmt werden konnte, wurde ein Entfärbungstest in der gleichen Weise wie in Beispiel 1 durchgeführt, um die Adsorptionsgeschwindigkeit von Methylenblau und die Aktivität zu bestimmen.The Number of common bacteria (cells / gram) of the filter media for water purifier, which was thus obtained was in the same manner as in Example 1 determined. Thus the adsorption capacity of this filter medium could be determined, was a decolorization test in the same Manner as in Example 1, to determine the adsorption rate of methylene blue and the activity.

Die erhaltenen Ergebnisse sind in Tabelle 1 gezeigt.The The results obtained are shown in Table 1.

Beispiele 3 und 4Examples 3 and 4

Es wurden Filtermedien für Wasserreiniger in der gleichen Weise wie in Beispiel 2 erhalten mit der Ausnahme, dass die Konzentration der wässrigen Natriumhydroxidlösung, die beim alkalischen Waschen verwendet wurde, gewechselt wurde. In Bezug auf die so erhaltenen Filtermedien wurde der Färbungstest zur Bestimmung der Adsorptionsgeschwindigkeit von Methylenblau und zur Bestimmung der Aktivität durchgeführt.It were filter media for Water purifier obtained in the same manner as in Example 2 with the exception that the concentration of the aqueous sodium hydroxide solution, the was used in alkaline washing, was changed. In relation on the filter media thus obtained was the staining test for determining the Adsorption rate of methylene blue and for the determination of activity carried out.

Wie im Vergleich zu den Beispielen 1 bis 4 gesehen werden kann, nimmt die Aktivität zu bei einer Zunahme der Konzentration der wässrigen Natriumhydroxidlösung und die Mikroorganismen und andere organische Substanzen im Wasser können adsorbiert werden, damit das Wasser gereinigt werden kann.As can be seen in comparison with Examples 1 to 4, the activity increases with an increase in the concentration of the aqueous sodium hydroxide solution and the microorganisms and other organisms The substances in the water can be adsorbed so that the water can be purified.

Vergleichsbeispiel 1Comparative Example 1

Das Ausgangsmaterial der verwitterten Riff-bildenden Koralle, das in Beispiel 1 verwendet wurde, wurde nur vorgewaschen. Anschließend wurde in Bezug auf die so erhaltene verwitterte Riff-bildende Koralle in der gleichen Weise wie in Beispiel 1 die Anzahl der allgemeinen Bakterien (Zellen/Gramm) bestimmt und der Entfärbungstest wurde zur Bestimmung der Adsorptionsgeschwindigkeit von Methylenblau und der Aktivität durchgeführt.The Raw material of weathered reef-building coral that lives in Example 1 was only prewashed. Subsequently was with respect to the weathered reef-building coral thus obtained in the same manner as in Example 1, the number of general Bacteria (cells / gram) were determined and the decolorization test was used for determination the adsorption rate of methylene blue and the activity carried out.

Die erhaltenen Ergebnisse sind in Tabelle 1 gezeigt.The The results obtained are shown in Table 1.

Vergleichsbeispiel 2Comparative Example 2

Das Ausgangsmaterial der verwitterten Riff-bildenden Koralle, das in Beispiel verwendet wurde, wurde vorgewaschen und die so erhaltene verwitterte Riff-bildende Koralle wurde in der gleichen Weise wie in Beispiel 1 geröstet. Anschließend wurde in Bezug auf die so erhaltene verwitterte Riff-bildende Koralle in der gleichen Weise wie in Beispiel 1 die Anzahl der allgemeinen Bakterien (Zellen/Gramm) bestimmt und der Entfärbungstest durchgeführt zur Bestimmung der Adsorptionsgeschwindigkeit von Methylenblau und der Aktivität. Die erhaltenen Ergebnisse sind in Tabelle 1 gezeigt.The Raw material of weathered reef-building coral that lives in Example was prewashed and the thus obtained weathered reef-building coral became like in the same way roasted in Example 1. Subsequently was related to the weathered reef-building coral so obtained in the same manner as in Example 1, the number of general Bacteria (cells / gram) were determined and the decolorization test was carried out for Determination of the adsorption rate of methylene blue and the Activity. The The results obtained are shown in Table 1.

Tabelle 1

Figure 00240001
Table 1
Figure 00240001

Beispiel 5Example 5

Unter Verwendung des Filtermediums für Wasserreiniger, das in Beispiel 1 erhalten wurde, wurde dieses in den Korb 3 des geschlossenen Containers 2 der Vorrichtung, die in 2 gezeigt ist, getan und das Innere des geschlossenen Containers 2 wurde evakuiert, 20 l einer wässrigen Silbernitratlösung mit 5% Silber wurden zugeführt und das Rührflügelblatt 4 wurde für 30 Minuten rühren gelassen, um die wässrige Silbernitratlösung durch das Filtermedium kräftig durchzuleiten.Using the filter medium for water purifier obtained in Example 1, it was put in the basket 3 of the closed container 2 the device used in 2 shown is done and the inside of the closed container 2 was evacuated, 20 liters of an aqueous silver nitrate solution containing 5% silver were fed and the agitator blade 4 was allowed to stir for 30 minutes to vigorously pass the aqueous silver nitrate solution through the filter medium.

Nachdem die wässrige Silbernitratlösung abgelassen wurde, wurden 20 l einer wässrigen 1,5% Ascorbinsäurelösung durch die Zuleitung 9 zugeführt, und das Rührflü gelblatt 4 wurde für 30 Minuten rotieren gelassen, um die wässrige Silbernitratlösung durch das Filtermedium kräftig durchzuleiten. Anschließend wurde die Ascorbinsäurelösung durch das Flüssigkeitsablassrohr 10 abgelassen und die entstehende verwitterte Riff-bildende Koralle wurde aus dem geschlossenen Container 2 genommen und in einen elektrischen Ofen getan, um sie bei 400°C für 50 Minuten zu erhitzen. Nachdem Erhitzen vollständig war, wurde anschließend abgekühlt, Waschen mit Wasser, Trocknen und Einstellung der Korngröße sukzessiv durchgeführt, gefolgt vom Verpacken, um ein Produkt eines mit Silber versetzten Materials zu erhalten. Das so erhaltene mit Silber versetzte Material hatte ein Silberbeschichtungsgewicht wie es in Tabelle 2 gezeigt.After the aqueous silver nitrate solution was drained, 20 liters of an aqueous 1.5% ascorbic acid solution was passed through the feed line 9 supplied, and the Rührflü gelblatt 4 was allowed to rotate for 30 minutes to vigorously pass the aqueous silver nitrate solution through the filter medium. Subsequently, the ascorbic acid solution was passed through the liquid discharge tube 10 drained and the resulting weathered reef-building coral was removed from the closed container 2 and put into an electric oven to heat at 400 ° C for 50 minutes. After heating was completed, it was then cooled, washed with water, dried and grain size adjusted successively, followed by packaging to obtain a product of silver-added material. The silver-added material thus obtained had a silver coating weight as shown in Table 2.

Beispiel 6Example 6

Ein mit Silber versetztes Material wurde in der gleichen Weise wie in Beispiel 5 erhalten mit der Ausnahme, dass das in Beispiel 2 erhaltene verwitterte Riff-bildende Korallenmaterial verwendet wurde.One Material added with silver was prepared in the same way as in Example 5 were obtained except that obtained in Example 2 weathered reef-building coral material was used.

Das mit Silber versetzte Material das so erhalten wurde, hatte ein Silberbeschichtungsgewicht wie es in der Tabelle 2 gezeigt ist.The Silver-plated material thus obtained had a silver coating weight as shown in Table 2.

Vergleichsbeispiel 3Comparative Example 3

Ein mit Silber versetztes Material wurde in der gleichen Weise wie in Beispiel 5 erhalten, mit der Ausnahme, dass ein Material verwendet wurde, das durch nur das Vorwaschen des Ausgangsmaterials der verwitterten Riff-bildenden Koralle, wie es in Beispiel 1 verwendet wurde, erhalten wurde.One Material added with silver was prepared in the same way as in Example 5, except that a material is used that was weathered by just pre-washing the parent material of the Reef-building coral as used in Example 1 was obtained has been.

Das so erhaltene mit Silber versetzte Material hatte ein Silberbeschichtungsgewicht, wie es in Tabelle 2 gezeigt ist.The silver-containing material thus obtained had a silver coating weight, as shown in Table 2.

Tabelle 2

Figure 00260001
Table 2
Figure 00260001

Gemäß dem Verfahren der vorliegenden Erfindung zur Herstellung eines verwitterten Riff-bildenden Korallenmaterials, kann ein verwittertes Riff-bildendes Korallenmaterial erhalten werden, aus dem verschiedene Meeresalgen, verschiedene Mikroorganismen einschließlich Vibrionbakterien, die die Meere bewohnen, und andere verschiedene organische Substanzen, die in der inneren Feinstruktur einer verwitterten Riff-bildenden Koralle zurückgehalten werden, entfernt worden sind und dessen Sicherheit gewährleistet wurde. Dieses verwitterte Riff-bildende Korallenmaterial kann für verschiedene Zwecke verwendet werden. Insbesondere ist es für Nahrungsmittelmaterialien geeignet. Gemäß der vorliegenden Erfindung kann ebenso ein Filtermedium für Wasserreiniger erhalten werden, das eine hohe Mineralienelution aufweist und ebenso eine hohe Aktivität.According to the procedure of the present invention for producing a weathered reef-building coral material, a weathered reef-building coral material can be obtained from different sea algae, different microorganisms including vibrion bacteria, that inhabit the seas and other different organic substances, the in the inner fine structure of a weathered reef-forming Coral held back be, have been removed and its security guaranteed has been. This weathered reef-building coral material can be used for various Purposes are used. In particular, it is for food materials suitable. According to the present Invention can also be obtained a filter medium for water purifier, which has a high mineral elution and also a high activity.

Erfindungsgemäß kann ebenso ein mit Silber versetztes Material erhalten werden, dessen verwitterte Riff-bildende Koralle mit Silber auf seiner Oberfläche und ebenso innerhalb ihrer Feinstruktur innerhalb des porösen Gewebes beschichtet wurde.Likewise, according to the invention obtained a silver offset material whose weathered reef-forming Coral with silver on its surface and within it as well Fine structure within the porous Tissue was coated.

Claims (13)

Verfahren zum Herstellen eines verwitterten, riffbildenden Korallenmaterials, umfassend die Schritte des Eintauchens einer verwitterten, riffbildenden Koralle in eine wäßrige Alkalilösung unter reduziertem Druck zum Ausführen eines alkalischen Waschens, um ein Eindringen der wäßrigen Alkalilösung in die verwitterte, riffbildende Koralle überall in ihre Feinstruktur innerhalb des porösen Gewebes hervorzurufen und deren Waschens mit Wasser bis Waschwasser aus dem Inneren des porösen Gewebes neutralisiert ist, wobei nach dem Waschen mit Wasser das verwitterte, riffbildende Korallenmaterial bei 100 bis 750°C geröstet wird.Method for producing a weathered, reef-building coral material comprising the steps of Immerse a weathered, reef-forming coral in an aqueous alkali solution below reduced pressure to run an alkaline washing to prevent penetration of the aqueous alkali solution in the weathered, reef-building coral everywhere in their fine structure within the porous Evoke tissue and Washing with water until washing water from the inside of the porous Tissue is neutralized, wherein after washing with water the Weathered, reef-building coral material is roasted at 100 to 750 ° C. Verfahren zum Herstellen eines verwitterten, riffbildenden Korallenmaterials nach Anspruch 1, worin das alkalische Waschen durch kräftiges Durchleiten der wäßrigen Alkalilösung durch die in die wäßrige Alkalilösung eingetauchte, verwitterte, riffbildende Koralle ausgeführt wird.Method of producing a weathered, reef-building Coral material according to claim 1, wherein the alkaline washing through strong Passing the aqueous alkali solution through immersed in the aqueous alkali solution, weathered, reef-building coral is performed. Verfahren zum Herstellen eines verwitterten, riffbildenden Korallenmaterials nach Anspruch 1, worin das alkalische Waschen durch Hin- und Herbewegen der verwitterten, riffbildenden Koralle in der wäßrigen Alkalilösung ausgeführt wird.Method of producing a weathered, reef-building Coral material according to claim 1, wherein the alkaline washing by moving the weathered, reef-building coral back and forth is carried out in the aqueous alkali solution. Verfahren zum Herstellen eines verwitterten, riffbildenden Korallenmaterials nach Anspruch 1, worin das alkalische Waschen während des Erwärmens der wäßrige Alkalilösung ausgeführt wird.Method of producing a weathered, reef-building Coral material according to claim 1, wherein the alkaline washing while of heating the aqueous alkali solution is carried out. Verfahren zum Herstellen eines verwitterten, riffbildenden Korallenmaterials nach Anspruch 1, wobei die wäßrige Alkalilösung eine wäßrige 0,01 bis 6 N alkalische Lösung von NaOH, KOH, Na2CO3 oder K2CO3 umfaßt.A method of producing a weathered reef-building coral material according to claim 1, wherein the aqueous alkali solution comprises an aqueous 0.01 to 6N alkaline solution of NaOH, KOH, Na 2 CO 3 or K 2 CO 3 . Verfahren zum Herstellen eines verwitterten, riffbildenden Korallenmaterials nach Anspruch 2, worin das Waschen mit Wasser durch Eintauchen der verwitterten, riffbildenden Koralle in Wasser unter reduziertem Druck und durch kräftiges Durchleiten des Wassers durch die verwitterte, riffbildende Koralle ausgeführt wird.Method of producing a weathered, reef-building Coral material according to claim 2, wherein the washing with water by immersing the weathered, reef-building coral in water under reduced pressure and by vigorously passing the water is performed by the weathered, reef-building coral. Verfahren zum Herstellen eines verwitterten, riffbildenden Korallenmaterials nach Anspruch 3, worin das Waschen mit Wasser durch Eintauchen der verwitterten, riffbildenden Koralle in Wasser unter reduziertem Druck und durch Hin- und Herbewegen der verwitterten, riffbildenden Koralle im Wasser ausgeführt wird.Method of producing a weathered, reef-building Coral material according to claim 3, wherein the washing with water by immersing the weathered, reef-building coral in water under reduced pressure and by agitating the weathered, reef-building coral is carried out in the water. Verfahren zum Herstellen eines verwitterten, riffbildenden Korallenmaterials nach Anspruch 1, worin nach dem Waschen mit Wasser und nach dem Rösten die verwitterte, riffbildende Koralle pulverisiert und gesiebt wird, um sie zu einem Pulver zu verarbeiten, das eine Teilchengröße von 500 Mesh oder größer aufweist (Teilchendurchmesser von 27,28 μm oder kleiner).Method of producing a weathered, reef-building Coral material according to claim 1, wherein after washing with water and after roasting the weathered, reef-building coral is pulverized and sieved, to process them into a powder having a particle size of 500 Mesh or larger (particle diameter of 27.28 μm or smaller). Verfahren zum Herstellen eines mit Silber versetzten, verwitterten, riffbildenden Korallenmaterials, welches nach dem Waschen mit Wasser und dem Rösten im Verfahren zur Herstellung eines verwitterten, riffbildenden Korallenmaterials nach Anspruch 1 das Unterwerfen der verwitterten, riffbildenden Koralle einem Eintauchen in eine wäßrige Silberlösung unter reduziertem Druck, um ein Eindringen der wäßrigen Silberlösung in die verwitterte, riffbildende Koralle überall in ihre Feinstruktur innerhalb des porösen Gewebes hervorzurufen und das Reduzieren des Silbers mit einem Reduktionsmittel, um die verwitterte, riffbildende Koralle mit Silber überall in ihrer Feinstruktur innerhalb des porösen Gewebes zu beschichten, umfaßt.Method for producing a silver-plated, Weathered, reef-building coral material, which after the Washing with water and roasting in the process of making a weathered reef-building coral material according to claim 1 the subjugation of weathered, reef-building Coral immersed in an aqueous silver solution under reduced pressure Pressure to prevent penetration of the aqueous silver solution into the weathered, reef-building coral everywhere in their fine structure within the porous Evoke tissue and reducing the silver with one Reducing agent to the weathered, reef-building coral with silver throughout to coat their fine structure within the porous tissue, includes. Verwittertes riffbildendes Korallenmaterial, das durch das Herstellungsverfahren nach Anspruch 1 erhalten wird.Weathered reef-building coral material that obtained by the production method according to claim 1. Lebensmittelmaterial, welches das verwitterte, riffbildende Korallenmaterial, das durch das Herstellungsverfahren nach Anspruch 8 erhalten worden ist, umfaßt.Food stuff the weathered, reef-forming Coral material produced by the manufacturing method according to claim 8 has been obtained. Filtermedium, welches das verwitterte, riffbildende Korallenmaterial, das durch das Herstellungsverfahren nach Anspruch 1 erhalten worden ist, umfaßt.Filter medium, which weathered, reef-forming Coral material produced by the manufacturing method according to claim 1 has been obtained. Mit Silber versetztes Material, welches das verwitterte, riffbildende Korallenmaterial, das durch den Herstellungsprozeß nach Anspruch 9 erhalten worden ist, umfaßt.Silver offset material that weathered, reef-building coral material produced by the manufacturing process according to claim 9 has been obtained.
DE69729883T 1997-10-15 1997-10-15 WEATHERED HERMATYPIC CORAL MATERIAL Expired - Lifetime DE69729883T2 (en)