DE606105C

DE606105C - Process for obtaining firmly adhering electrolytic nickel deposits

Info

Publication number: DE606105C
Application number: DEF74465D
Authority: DE
Original assignee: AKTIESELSKAP; Falconbridge Nikkelverk AS
Current assignee: AKTIESELSKAP; Falconbridge Nikkelverk AS
Priority date: 1932-08-27
Filing date: 1932-11-11
Publication date: 1934-11-24

Description

Verfahren zur Erzielung festhaftender elektrolytischer Nickelniederschläge Beim elektrolytischen Raffinieren von Metallen geschieht das Ausfällen oft auf sogenannten Mutterblechen aus demselben Metall, z. B. bei der Kupfer-, Blei- und Nickelraffination. Diese Mutterbleche sind bisher keiner besonderen Behandlung unterworfen worden, was z. B. im Falle des Kupfers auch nicht notwendig ist.Process for obtaining firmly adhering electrolytic nickel deposits When metals are electrolytically refined, precipitation often occurs on what are known as Mother plates made of the same metal, e.g. B. in copper, lead and nickel refining. These mother plates have not yet been subjected to any special treatment, what z. B. is also not necessary in the case of copper.

Beim Nickel dagegen ist die bisher angewandte Praxis mit nicht unbedeutenden Nachteilen verbunden gewesen. Es geschieht nicht selten, daß, das ausgefällte Nickel bereits in den Elektrolysegefäßen von den Mutterblechen abblättert, wodurch Kurzschluß und andere Nachteile verursacht werden, was besonders nachteilig ist, wenn die Elektrolyse des Nickels nach dem wohlbekannten Hybinette-Verfahren ausgeführt wird, bei welchem die Kathoden in Hybinette-Säcken angebracht sind. Beim späteren Zerschneiden der Nickelkathoden in kleinere Stücke tritt meistens !eine Teilung der Kathoden an den Mutterblechen entlang auf; seine Teilung, die bedeutende übelstände mit sich gebracht hat.In the case of nickel, on the other hand, the practice used to date is by no means insignificant Disadvantages have been associated. It not infrequently happens that, the precipitated nickel already flaking off the mother plates in the electrolysis vessels, causing a short circuit and other disadvantages are caused, which is particularly disadvantageous when the electrolysis of nickel is carried out by the well-known Hybinette process in which the cathodes are placed in hybinette bags. When later cutting the Nickel cathodes in smaller pieces usually occur! A division of the cathodes at the Mother plates along on; its division, which brought with it significant evils Has.

In der Galvanostegie -sind auch ähnliche Übelstände bekannt, insofern @es beispielsweise oft schwierig sein kann, das ausgefällte Metall -zum Anhaften an der metallischen Unterlage zu bringen. In dieser Industrie versucht man, diese Schwierigkeiten auf viele Arten, durch Schleifen, Behandlung mit Lauge oder verhältnismäßig starke Säuren usw., mit mehr oder weniger befriedigendem Erfolg zu überwinden. Die Behandlung mit derartigen starken Chemikalien dauert nur ganz kurz (einige Sekunden üder höchstens wenige Minuten) und macht ein nachträgliches gründliches Waschen erforderlich. Diese Mefhoden hat man bei der Nickelraffination als wenig anwendbar und zu kostspielig ,angesehen.Similar deficiencies are also known in the Galvanostegie For example, it can often be difficult for the precipitated metal to adhere to bring to the metallic base. In this industry you try to do this Difficulties in many ways, by grinding, treating with lye or proportionately strong acids, etc., to be overcome with more or less satisfactory results. the Treatment with such strong chemicals only takes a very short time (a few seconds or a few minutes at most) and do a thorough wash afterwards necessary. These mefhodes have been found to be of little use in nickel refining and too expensive to be viewed.

Vorliegende Erfindung betrifft ein Verfahren zur Behandlung von Mutterblechen aus Nickel, durch das die erwähnte Abblätterung und Teilung verhindert werden kann. Dieser Erfolg wird in einfacher und billiger Weise dadurch erreicht, daß die Mutterbleche vor dem Gebrauch einige Zeit (gewöhnlich mehrere Stunden) der Einwirkung einer verdünnten Säure, z. B. Schwefelsäure, unterworfen werden, die vorzugsweise in warmem Zustande angewendet wird. Die benutzte Säure mu,ß so stark verdünnt sein, daß durch mehrstündige Einwirkung derselben auf die Nickelplatten keine nennenswerte Mengen von- Nickel aufgelöst werden, da die Aufgabe der Behandlung mit Säure darin besteht, die anhaftenden Oxyde, basischen Nickelsalze u. dgl. aufzulösen, ohne das Nickelmetall nennenswert anzugreifen. Es hat sich. gezeigt, daß der Grad der Verdünnung in der Größenordnung von r : z oo liegen muß,; die vorteilhaftesfie Säurestärke wird von der Temperatur und der Behandlungszeit etwas abhängig sein. Bei Verwendung von Schwefelsäure hat man so durch -Behandlung während einiger Stunden mit einer Säure, welche nicht mehr als r o g H2 S O" im Liter enthält, befriedigende Erfolge erreicht.The present invention relates to a method for treating mother plates made of nickel, which can prevent the aforementioned peeling and splitting. This success is achieved in a simple and cheap way that the mother plates before use some time (usually several hours) of exposure to a diluted Acid, e.g. B. sulfuric acid, preferably in a warm state is applied. The acid used must be so diluted that it can be used for several hours The effect of the same on the nickel plates does not produce any significant amounts of nickel be dissolved, since the task of the acid treatment is to remove the adhering Dissolve oxides, basic nickel salts and the like without the nickel metal appreciably to attack. It has. demonstrated that the degree of dilution of the order of magnitude must lie from r: z oo; the advantageous fie Acid strength will be somewhat dependent on the temperature and the treatment time. When using Sulfuric acid is obtained by treating it with an acid for a few hours, which does not contain more than r o g H2 SO "per liter has achieved satisfactory results.

Wenn eine Säure verwendet wird, die die gleichen Salze bildet wie die, welche in dem Elektrolyten vorhanden sind, so erübrigt sich das Waschen der Mutterbleche, und diese werden in diesem Falle sogleich nach der Säurebehandlung in den Elektrolysegefäßen angebracht, ohne erst Gelegenheit zum Trocknen erhalten zu haben.When an acid is used that forms the same salts as those which are present in the electrolyte, there is no need to wash them Mother plates, and in this case these are immediately after the acid treatment placed in the electrolysis vessels without first being given an opportunity to dry to have.

Die Säurebehandlung der Nickelplatten wird zweckmäßig durch Einsetzen oder Aufhängen der Platten in Behältern ausgeführt, die mit verdünnter Schwefelsäure gefüllt sind, welche durch Einblasen von Dampf oder Luft oder in anderer Weise in andauernder Bewegung gehalten wird. In diese Säurebehälter werden die Mutterbleche einige Zeit, bevor sie in den Elektrolysegefäßien benutzt werden sollen, z. B. am Abend vor dem Gebrauch, eingesetzt.The acid treatment of the nickel plates is expedient by inserting them or hanging the panels in containers made with dilute sulfuric acid are filled, which by blowing steam or air or in some other way into constant movement. The mother plates are placed in these acid tanks some time before they are to be used in the electrolysis vessels, e.g. B. on The evening before use.

Die Behandlung ist völlig wirksam und erfordert wenig Arbeit und Aufsicht.The treatment is completely effective and requires little work and supervision.

Das Verfahren ist bei der gewöhnlichen elektrolytischen Raffinaiiori von Nickel von großer praktischer Bedeutung und ist besonders vorteilhaft, wenn die hergestellten Nickelkathoden als Anoden in der Vernickelungsindustrie Anwendung finden sollen, in welchem Falle es von besonderer Wichtigkeit ist, zu vermeiden, daß sich das Material während der Anwendung teilt. Beispiel Auf Mutterplatten aus Aluminium wird Nickel elektrolytisch ausgefällt, und wenn der Niederschlag die gewünschte Stärke erreicht hat, wird das Nickel abgezogen. Diese Nickelbleche werden als Mutterbleche für elektrolytisches Ausfällen von Nickel verwendet. Die Anzahl von Mutterblechen (in der Anlage der Erfinderin q.oo bis 5oo), welche den Tagesverbrauch einer Nickelraffinationsanlage ausmacht, wird reinige Zeit vor der Verwendung (vorzugsweise mehrere Stunden) in einem Beizbad angebracht. Die Beizflüssigkeit besteht aus einer ungefähr einprozentigen Schwefelsäure und wird mittels mittelbarer,oder unmittelbarer Dampfheheizung auf einer Temperatur von ungefähr 50° C gehalten. Während des Beizens wird das Bad durch Einblasen von Luft in dauernder Bewegung gehalten, um eine gute Erneuerung der Säure an den Mutterblechen zu bewirken und ein gleichmäßiges Erwärmen zu ermöglichen. Die Mutterbleche verweilen gewöhnlich ungefähr i z Stunden in dem B,eizbad, 70 Mutterbleche- werden auf neinmal aus dem Beizbad herausgenommen, und diese werden dann im Laufe einer 1-/2 Stunde in den Elektrolysiergefäßen angebracht.The process is of great practical importance in the ordinary electrolytic refining of nickel and is particularly advantageous when the nickel cathodes produced are to be used as anodes in the nickel plating industry, in which case it is of particular importance to avoid the material from settling during the process Application shares. Example Nickel is electrolytically precipitated on aluminum mother plates, and when the precipitate has reached the desired thickness, the nickel is stripped off. These nickel sheets are used as mother sheets for electrolytic precipitation of nickel. The number of mother plates (q.oo to 500 in the plant of the inventor), which makes up the daily consumption of a nickel refining plant, is placed in a pickling bath clean time before use (preferably several hours). The pickling liquid consists of approximately one percent sulfuric acid and is kept at a temperature of approximately 50 ° C by means of direct or indirect steam heating. During the pickling process, the bath is kept in constant motion by blowing in air in order to bring about a good renewal of the acid on the mother sheets and to enable uniform heating. The mother sheets usually remain in the pickling bath for about 1 hour, 70 mother sheets are taken out of the pickling bath at once, and these are then placed in the electrolysis vessels over the course of 1/2 hour.

Claims

PATENT CLAIMS: I. Process for obtaining firmly adhering electrolytic Nickel deposits by pretreating the nickel parent sheets with acid, thereby characterized that the nickel parent sheets several-hours in an approximately no percent Acid dipped. a. Method according to claim z, characterized in that r an acid is used for pretreatment which forms the same salts as the present in the electrolyte, and that after the acid treatment the mother sheets, without being washed beforehand and still in a moist state in the nickel refining bath -be introduced.