DE575793C

DE575793C - Crucible furnace

Info

Publication number: DE575793C
Application number: DEH131533D
Authority: DE
Original assignee: Individual
Current assignee: Individual
Priority date: 1932-04-24
Filing date: 1932-04-24
Publication date: 1933-05-02

Description

TiegeIofen Es ist bekannt, daß die Qualität des Tiegelstahls diejenige des Elektrostahls und des Siemens - Martin - Stahls erheblich übertrifft. Lediglich das Herstellungsverfahren dieses besonderen Stahls erhöht seinen Preis erheblieb. Diese hohen Herstellungskosten werden in erster Linie dadurch hervorgerufen, daß der Schmelzprozeß verhältnismäßig lange dauert, da die Tiegel meistens in Koksöfen stehen, bei denen die Hitzeentwicklung beschränkt ist.Crucible furnace It is known that the quality of crucible steel is the same of electrical steel and Siemens-Martin steel. Only the manufacturing process of this particular steel increases its price considerably. These high manufacturing costs are primarily caused by the fact that the melting process takes a relatively long time because the crucibles are mostly in coke ovens where the heat development is limited.

Bei Tiegelöfen gemäß Erfindung wird dieser Nachteil in erheblichem Maße ausgeschaltet, es besteht hierbei die Möglichkeit, den Sclimelzprozeß erheblich abzukürzen, weil die Hitzeentwicklung und die Hitzeeinwirkung auf das Schmelzgut eine erheblich größere ist. Der neue Tiegelofen bat- außerdem den Vorzug, daß die Hitzeeinwirkung genau kontrolliert und reguliert werden kann.In the case of crucible furnaces according to the invention, this disadvantage becomes considerable Measures turned off, there is the possibility to significantly reduce the liming process to be shortened because the heat development and the heat effect on the melted material a considerably larger one. The new crucible furnace also had the advantage that the Heat exposure can be precisely controlled and regulated.

Neben der Abkürzung des Schmelzprozesses wird auch noch der Vorteil erreicht, daß der Schmelztiegel vollkommen luftdicht abgeschlossen ist, so daß eine Oxydation des zu schmelzenden Gutes nicht eintreten kann. Der zwischen dem eingefüllten Schmelzgut anfangs vorhandene Sauerstoff wird sehr schnell restlos aufgezehrt, und neuer Sauerstoff hat keinen Zutritt. Auf diese Weise wird ein Metallabbrand vermieden.In addition to the shortening of the melting process, there is also the advantage achieved that the crucible is completely airtight, so that a Oxidation of the material to be melted cannot occur. The one between the filled Oxygen which is initially present in the melt material is very quickly consumed completely, and new oxygen has no access. In this way, metal burn-off is avoided.

Die Erfindung besteht darin, daß das Schmelzgefäß (Schmelztiegel) mit einem besonders äusgebildeten Deckel abgedeckt wird (Abb. i), durch den gleichzeitig dein -Schmelzgute in erheblichem Maße Hitzemengen zugeführt werden: Dieser Deckel besteht aus einem Ring i aus hochfeuerfestem Werkstoff, der nach unten durch eine Platte 2 abgeschlossen ist. Diese Platte 2 dient als Diaphragma. Durch sie wird über die Kammer 3 ein Gas-Luft-Gemisch getrieben, das auf der Außenseite - der dem Tiegelinneren zugekehrten Seite - zur Entzündung gebracht wird. Auf diese Weise wird eine flammenlose Oberflächenverbrennung erreicht, welche von oben auf das Schmelzgut wirkt. Da die Hitzeentwicklung dieser flammenlosen Oberflächenvei brennurig ganz erheblich ist, so daß eine Temperatur erzeugt wird, die wesentlich über dem Schmelzpunkte des zu schmelzenden Metalls, besonders Stahl, liegt, wird der Schmelzvorgang von oben her wesentlich gefördert. Von dieser Seite konnte bislang eine Förderung des Schmelzprozesses überhaupt nicht erfolgen. Es ist daher bei dem Tiegelcen gemäß Erfindung möglich, den Schmelzvorgang wesentlich abzukürzen. Diese Abkürzung ist einmal eine Folge der erhöhten Wärmeentwicklung, die beim erfindungsgemäßen Ofen erreichbar ist. Außerdem wird aber noch dadurch, daß die Beschickung von oben geschmolzen wird, eine Beschleunigung des Schmelzvorganges erzielt, indem das oben geschmolzene Gut an den noch nichtgeschmolzenen Teilen der Tiegelfüllung herunterrieselt und auf diese Weise deren Schmelzung vorbereitet.The invention consists in that the melting vessel (crucible) is covered with a specially shaped lid (Fig. i), through which at the same time your melted goods are supplied with considerable amounts of heat: this lid consists of a ring i made of highly refractory material, which goes down through a Plate 2 is complete. This plate 2 serves as a diaphragm. Through it becomes Driven through the chamber 3, a gas-air mixture that is on the outside - the dem Inside of the crucible facing side - is caused to ignite. In this way a flameless surface combustion is achieved, which is applied from above to the melting material works. Since the heat development of this flameless surface turns burnt all over is significant, so that a temperature is generated which is substantially above the melting point of the metal to be melted, especially steel, lies, the melting process of significantly promoted above. So far, funding for the Melting process does not take place at all. It is therefore in accordance with the crucible Invention possible to shorten the melting process significantly. This abbreviation is once a consequence of the increased heat development that occurs in the furnace according to the invention is attainable. In addition, the fact that the feed is melted from above is achieved, an acceleration of the melting process by the above melted Good thing about the not yet melted Parts of the crucible filling trickles down and in this way prepared for their melting.

Der Deckel ist in üblicher Weise Schwenk-oder abhebbar angeordnet. Die Zuleitungen des Gas-Luft-Gemisches sind ebenfalls beweglich ausgebildet.The cover is arranged so that it can be pivoted or lifted off in the usual manner. The supply lines for the gas-air mixture are also designed to be movable.

Weiterhin ist der Deckel so gestaltet, daß die als Diaphragma für die flammenlose Oberflächenverbrennung dienende Platte 2 in genügendem Abstande von dem oberen Tiegelrand bleibt, damit dieser nicht durch die starke Wärmeentwicklung angegriffen wird.Furthermore, the lid is designed so that as a diaphragm for the plate 2 serving the flameless surface combustion at a sufficient distance from the upper edge of the crucible so that it is not caused by the strong heat development is attacked.

Dieser Deckel kann bei allen Tiegelöfen zum Schmelzen von Metallen Anwendung finden. Durch Einbetten des Tiegels in Stücke aus hochfeuerfesten Stoffen oder durch Anordnung eines Diaph,ragmas aus Formstücken kann der Tiegel selbst auch mittels flammenloser Oberflächenverbrennung beheizt werden.This lid can be used in all crucible furnaces for melting metals Find application. By embedding the crucible in pieces made of highly refractory materials or the crucible itself can also be created by arranging a diaph, ragma made of shaped pieces be heated by means of flameless surface combustion.

Abb. 2 zeigt eine Anordnung, bei welcher der Tiegel in Stücke aus hochfeuerfesten Stoffen eingebettet ist und bei der die Beheizung mittels flammenloser Oberflächenverbrennung erfolgt.Fig. 2 shows an arrangement in which the crucible in pieces is embedded in highly refractory materials and in which the heating by means of flameless Surface burn occurs.

Hierin bedeuten i das Ofenfutter, 2 den Deckel mit Diaphragma, 3 eine Abdeckplatte, q. die Füllung des Heizraumes mit Brocken zur flammenlosen Oberflächenverbrennung, 5 das Schmelzgefäß, 6 der Tiegeluntersatz. Der Tiegelofen kann kippbar oder feststehend sein. Bei Öfen, aus denen die Tiegel zum Entleeren des flüssigen Schmelzgutes herausgehoben werden und die vollkommen durch flammenlose Oberflächenverbrennung beheizt werden sollen,. würde gemäß Abb. 3 ein Diaphragma den Schmelztiegel umschließen, während der Raum zwischen diesem und der Ofenausmauerung als Kammer für das einzuführende Gas-Luft Gemisch, das durch Diaphragma hindurchgetrieben wird, dient.Here i mean the oven lining, 2 the lid with diaphragm, 3 one Cover plate, q. the filling of the boiler room with chunks for flameless surface combustion, 5 the melting vessel, 6 the crucible base. The crucible furnace can be tiltable or fixed be. In furnaces from which the crucibles are lifted out to empty the molten liquid and which are fully heated by flameless surface combustion should,. According to Fig. 3, a diaphragm would enclose the crucible while the space between this and the furnace lining as a chamber for the to be introduced Gas-air mixture, which is driven through the diaphragm, is used.

Dieses Diaphragma kann aus einem Stück oder aus mehreren zylindrischen Formstücken bestehen.This diaphragm can be made of one piece or of several cylindrical ones Form pieces exist.

Claims

PATENT CLAIMS: i. Usually heated crucible furnace for melting metals of all kinds, especially steel, with a hinged or liftable lid, characterized in that the lid is entirely or partially designed as a burner for flameless surface combustion.

2. Crucible furnace according to claim i, characterized in that the crucible by embedding in Pieces made of highly refractory material or by arranging a diaphragma Fittings can be heated by means of flameless surface combustion -is .. -