DE4118063C2 - Process for gluing picture foils on carriers by applying artificial cold and using the process - Google Patents

Process for gluing picture foils on carriers by applying artificial cold and using the process

Info

Publication number
DE4118063C2
DE4118063C2 DE4118063A DE4118063A DE4118063C2 DE 4118063 C2 DE4118063 C2 DE 4118063C2 DE 4118063 A DE4118063 A DE 4118063A DE 4118063 A DE4118063 A DE 4118063A DE 4118063 C2 DE4118063 C2 DE 4118063C2
Authority
DE
Germany
Prior art keywords
substance
degrees celsius
foils
film
cold
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE4118063A
Other languages
German (de)
Other versions
DE4118063A1 (en
Inventor
Manfred Keppeler
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE4118063A priority Critical patent/DE4118063C2/en
Priority to PCT/DE1992/000432 priority patent/WO1992021714A1/en
Publication of DE4118063A1 publication Critical patent/DE4118063A1/en
Application granted granted Critical
Publication of DE4118063C2 publication Critical patent/DE4118063C2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

Zum Kleben von Bildfolien werden unterschiedliche Klebstoffe verwendet und die Klebestellen meist zusätzlich erhitzt oder zusammengepreßt. Werden Gegenstände mit Folien oder Schiebebildern beklebt, so wird die Adhäsionskraft ausgenützt, die Folien werden mit Hilfe eines Vakuums angesaugt oder mechanisch, etwa mit einer Rakel, aufgestrichen.Different adhesives are used to glue picture foils and the glued areas are usually additionally heated or pressed together. If objects are pasted with foils or slide pictures, the Adhesive force is used, the films are vacuumed vacuumed or brushed on mechanically, for example with a squeegee.

Aus der US-Patentschrift 4 010 057 ist eine Vorrichtung bekannt, bei der eine Folie auf Wasser oder einer wäßrigen Lösung schwimmt. In die Folie wird der zu überziehende Gegenstand hineingedrückt, wodurch sich die Folie an den Gegenstand anschmiegt.A device is known from US Pat. No. 4,010,057 which floats a film on water or an aqueous solution. In the Foil is pressed into the object to be coated, which causes the film hugs the object.

Ein ähnliches Verfahren, bei dem die wäßrige Lösung modifiziert wurde, ist in in DE 29 18 639 C2 beschrieben.A similar process in which the aqueous solution was modified is described in DE 29 18 639 C2.

In DE 23 49 145 wird ein Verfahren beschrieben, bei dem mit Hilfe von Nadeln die überschüssige Luft zwischen Gegenstand und Folie herausge­ saugt wird.DE 23 49 145 describes a method in which Needles remove the excess air between the object and the film sucks.

DE 28 38 695 C2 schildert ein Verfahren zum Aufbringen eines trockenen Abziehbildes durch elektrostatische Aufladung und Druck. DE 28 38 695 C2 describes a method for applying a dry Decal by electrostatic charge and pressure.  

DE 33 28 345 C2 schildert die Übertragung eines Films mit aufgedrucktem Muster auf die Oberfläche eines Gegenstandes mit Hilfe eines quellbaren Polymermaterials.DE 33 28 345 C2 describes the transmission of a film with printed Pattern on the surface of an object with the help of a swellable Polymer material.

In DE 37 08 855 C1 sind Verfahren und Vorrichtung für das Aufbringen eines Dekors durch Evakuieren beschrieben.DE 37 08 855 C1 describes methods and devices for the application a decor described by evacuation.

DE 36 38 779 A1 beschreibt ein Verfahren zum großflächigen Verzieren von Flächen, insbesondere lackierten Flächen an Kraftfahrzeugen unter Verwendung eines Klebers, der durch ein Lösungsmittel angelöst wird.DE 36 38 779 A1 describes a method for large-scale decorating of surfaces, especially painted surfaces on motor vehicles Use an adhesive that is dissolved by a solvent.

EP 03 11 292 A2 beschreibt die Bildung von Methylenbrücken bei Polymeren mit Amidgruppen (-CO-NH-) durch Verwendung einer methanolischen Formaldehydlösung. Die Polymerisation benötigt keine zusätzliche Wärmezufuhr oder Kühlung, ist aber naturgemäß temperatur­ abhängig. Trotz Druck und einer Temperatur von plus 30 Grad Celsius beträgt die geschlossene Wartezeit 36 Stunden. Eine Anwendung des Verfahrens bei künstliche erzeugter Kälte ist technisch nicht sinnvoll, da die Polykondensation bei niedrigen Temperaturen erheblich verlangsamt wird und die Qualität der entstehenden Klebung sehr schlecht ist. Das Verfahren beschränkt sich auf Polyamidfolien.EP 03 11 292 A2 describes the formation of methylene bridges Polymers with amide groups (-CO-NH-) by using a methanolic formaldehyde solution. The polymerization does not require additional heat or cooling, but is naturally temperature dependent. Despite pressure and a temperature of plus 30 degrees Celsius the closed waiting period is 36 hours. An application of the The artificial cold process does not make technical sense, because the polycondensation at low temperatures significantly is slowed down and the quality of the resulting bond very bad is. The process is limited to polyamide films.

In DE 24 60 586 A1 ist ein Verfahren zum Anbringen von Kennzeichnungen auf Kautschukwaren beschrieben, bei dem durch eine Kältebehandlung das Zerreißen der aufgebrachten Farbschicht bewirkt wird. Die Temperatur der Trägerfolie beträgt erfindungsgemäß plus 100 bis 120 Grad Celsius, die Temperatur des zur Abkühlung benutzten Wasserbades plus 20 bis 35 Grad Celsius.DE 24 60 586 A1 describes a method for affixing markings described on rubber goods, in which the Tearing the applied paint layer is caused. The temperature according to the invention, the carrier film is plus 100 to 120 degrees Celsius, the temperature of the water bath used for cooling plus 20 to 35 degrees Celsius.

Alle bisher bekannten Klebeverfahren werden bei normaler Raumtemperatur oder bei darüber liegenden Temperaturen durchgeführt. Auch Verfahren mit der der Bezeichnung "Kaltverklebung" werden im Bereich der normalen Raumtemperatur, also zwischen plus 18 und plus 22 Grad Celsius durchge­ führt (DIN 500 10). All previously known adhesive processes are carried out at normal room temperature or carried out at temperatures above. Even procedures with the designation "cold gluing" are in the normal range Room temperature, i.e. between plus 18 and plus 22 degrees Celsius leads (DIN 500 10).  

Bestimmte Materialien können nach den bekannten Verfahren nicht, oder nur unzureichend bearbeitet werden. Die Verwendung von Wasser oder einer wäßrigen Lösung verbietet sich bei Metallen mit hoher Oxydationsneigung wie beispielsweise Kupfer.Certain materials cannot, or are processed insufficiently. The use of water or an aqueous solution is not suitable for metals with high Oxidation tendency such as copper.

Die Positionierung der Folie oder des Schiebebildes auf einem Gegenstand wird durch vorzeitiges Ankleben beeinträchtigt. Zwischen Bildfolie und permanentem Träger bilden sich Luftblasen. Die Klebesubstanz (Mittlersubstanz) selbst bildet fühlbare und/oder sichtbare Blasen.The positioning of the film or the sliding picture on one Item is affected by premature sticking. Air bubbles form between the image film and the permanent support. The adhesive substance (middle substance) itself forms tactile and / or visible bubbles.

Die Mittlersubstanz bewirkt Veränderungen bei den zu klebenden Materialien.The middle substance causes changes in those to be glued Materials.

Die Mittlersubstanz bewirkt Veränderungen bei aufgebrachten Drucken oder Farben, Toner werden angelöst oder verwischt. Wasserlösliche Kleber sind unbeständig gegen Feuchtigkeit.The mediator causes changes in the applied prints or colors, toners are loosened or blurred. Water-soluble adhesives are not resistant to moisture.

Werden Kleblacke (organische Lösungsmittel), Reaktionsklebstoffe (polymerisierende Kunststoffe), verdunstende Chemikalien o.a. verwendet, ergeben sich bei der Verarbeitung weitere Nachteile:
Geruchsbelästigungen, gesundheitliche Schädigungen der Mitarbeiter, Explosions- und Brandgefahr, Belastung der Umwelt.If adhesive varnishes (organic solvents), reaction adhesives (polymerizing plastics), evaporating chemicals or the like are used, there are further disadvantages during processing:
Odor nuisance, health damage to employees, explosion and fire risk, pollution of the environment.

Ziel der Erfindung ist es, die genannten Nachteile bisher bekannter Verfahren zu vermeiden, oder in ihren Auswirkungen abzuschwächen. Die gestellte Aufgabe wird erfindungsgemäß gelöst, indem die zu ver­ arbeitenden Gegenstände und Materialien künstlich auf eine Temperatur abgekühlt werden, die plus 5 Grad Celsius oder weniger, also etwa plus 3 Grad oder minus 10 Grad Celsius beträgt. Dies kann in einem Kühl­ schrank, einer Kühltruhe, einem speziellen Kälteschrank oder in einem Kühlraum erfolgen. Die Kühlung kann auch durch ein Kältespray, eine Kältemischung, Trockeneis, Flüssigstickstoff oder in ähnlich geeigneter Weise erfolgen. The aim of the invention is to make the disadvantages known to date Avoid proceedings or weaken their effects. The object is achieved according to the invention by ver working objects and materials artificially to a temperature be cooled, the plus 5 degrees Celsius or less, so about plus 3 degrees or minus 10 degrees Celsius. This can be done in a cool cabinet, a freezer, a special refrigerator or in one Cold room. The cooling can also be done by a cold spray, a Cold mix, dry ice, liquid nitrogen or similar appropriately.  

Kühlkombinationen, etwa Kühltruhe - Trockeneis, sind ebenfalls anwendbar.Cooling combinations, such as freezer - dry ice, are also applicable.

Die Mittlersubstanz kann eine Lösung aus dem Material der Grundlage, eine Lösung aus der aufzubringenden Folie sein, aus einem oder mehreren Lösungsmitteln, einem oder mehreren Farbstoffen, Pigmenten oder Tonern, einem oder mehreren Klebstoffen, einem oder mehreren Kältemitteln, sowie eine Mischung aus den vorgenannten Stoffen sein. Die Basis kann aus Metall, Metalloxyden, Kunststoff, Holz, Papier, Pappe, Gummi, Kautschuk, Leder, Wachs, Glas, Porzellan, Stein, Keramik, Lebensmittel, Textilien und deren Kombinationen bestehen.The mediator can be a solution from the material based, be a solution from the film to be applied, from one or several solvents, one or more dyes, pigments or toners, one or more adhesives, one or more Refrigerants, as well as a mixture of the aforementioned substances. The base can be made of metal, metal oxides, plastic, wood, paper, Cardboard, rubber, caoutchouc, leather, wax, glass, porcelain, stone, ceramics, Food, textiles and their combinations exist.

Die Vorteile des Verfahrens ergeben sich durch die künstliche Abkühlung. Störende physikalische und chemische Eigenschaften der verwendeten Substanzen werden solange in einem schwach aktiven Zustand gehalten, bis der Klebevorgang im wesentlichen abgeschlossen ist.The advantages of the method result from the artificial Cooling. Interfering physical and chemical properties of the substances used are as long as in a weakly active state held until the gluing process is essentially complete.

Die lösenden Eigenschaften der Lösungsmittel sind herabgesetzt, dennoch bleibt die erwünschte niedrige Viskosität erhalten. Dadurch ist es möglich, die aufgebrachte Bildfolie exakt zu positionieren, Luftblasen und überschüssige Lösungsmittel durch Abstreifen oder Pressen zu entfernen, sowie Falten oder sonstige fehlerhafte Erscheinungen zu korrigieren.The solvent properties of the solvents are reduced, nevertheless the desired low viscosity is maintained. That’s it possible to position the applied film exactly, air bubbles and excess solvents by stripping or pressing remove, as well as folds or other faulty appearances correct.

Besonders überraschend am geschilderten Verfahren ist der Umstand, daß auch nachträglich keine Blasenbildung bei Bildfolien erfolgt. Durch das Abstreifen und/oder Auspressen der Mittlersubstanz kann die Schicht­ dicke der Substanz bestimmt werden; selbst hauchdünne Schichten können problemlos erzeugt werden. Diese in ihren chemischen und physikalischen Eigenschaften durch Kälte desaktivierte Schicht ermöglicht das Kleben problematischer Oberflächen:What is particularly surprising about the process described is the fact that no blistering also subsequently occurs with image films. By the The layer can be stripped off and / or squeezed out thickness of the substance can be determined; even extremely thin layers can can be easily generated. These in their chemical and physical Properties by cold-deactivated layer enables gluing problematic surfaces:

Keine oder geringe Zerstörung der Basis und der Deckschicht durch die Folgeerscheinungen chemischer Prozesse, die Wärme freisetzen. Little or no destruction of the base and the top layer by the Consequences of chemical processes that release heat.  

Keine oder nur geringe Veränderungen der Basis und der Deckschicht, sowie der darauf angebrachten Drucke, Farben und Toner durch die Lösungseigenschaften der Mittlerschicht.No or only slight changes in the base and the top layer, and the prints, colors and toners attached to it by the Solution properties of the middle layer.

Die Folienstärke kann wesentlich geringer sein als bei anderen Verfahren, da sich die Folie während des Aufbringens nur geringfügig anlöst; außerdem ist keine Klebstoffschicht notwendig. Das Verfahren eignet sich dadurch zum randlosen Aufbringen von Schiebebildern und zur Anwendung der sog. Hinterglastechnik.The film thickness can be much lower than that of others Procedure, since the film only slightly during application dissolves; in addition, no adhesive layer is necessary. The procedure is therefore suitable for borderless application of sliding pictures and for Application of the so-called back glass technique.

Das erfindungsgemäß beschriebene Verfahren eignet sich in hervor­ ragender Weise zur Verarbeitung feuchtigkeitsempfindlicher Materialien. Der Wasserdampfgehalt der Luft verringert sich bei der Abkühlung von plus 20 Grad Celsius auf minus 20 Grad Celsius etwa um den Faktor 100. Die verbleibende Feuchtigkeit kann bei fast allen erfindungsgemäßen Verarbeitungsprozessen vernachläßigt werden.The method described according to the invention is suitable in FIG excellent for processing moisture-sensitive materials. The water vapor content of the air decreases when it cools down plus 20 degrees Celsius to minus 20 degrees Celsius by a factor of 100. The remaining moisture can almost all of the invention Processing processes are neglected.

Das Verfahren kann daher sehr vorteilhaft bei Folien verwendet werden, auf denen sich Motive aus feuchtigkeitsempfindlichen Farbstoffen befinden. Dies gilt besonders für Schriften und Motive, die durch Tintenstrahldrucker erzeugt werden. Da die getrocknete Tinte in der Kälte nur wenig gelöst wird, zeigen die beim Positionieren und Ent­ fernen von Fremdeinschlüssen auftretenden Kräfte keine Wirkung auf die Konturtreue des Motivs.The method can therefore be used very advantageously for films on which motifs made of moisture-sensitive dyes are located. This is especially true for fonts and motifs that pass through Inkjet printers are generated. Since the dried ink in the Cold is only loosened a little, as shown by positioning and Ent forces occurring from foreign inclusions have no effect on the Contour accuracy of the motif.

Das Beschlagen, also das Abscheiden von Wasserdampf findet haupt­ sächlich beim Herausnehmen eines Gegenstandes aus dem Kühlbereich statt, also zu einem Zeitpunkt, bei dem der wesentliche Teil des Ver­ arbeitungsprozesses bereits abgeschlossen ist.Fogging, i.e. the separation of water vapor, takes place at all mainly when removing an object from the cooling area instead, at a time when the major part of Ver work process has already been completed.

Schiebebilder können mit Hilfe des Verfahrens so auf einen Gegenstand aufgebracht werden, daß sie randlos erscheinen.With the help of the method, sliding pictures can be placed on an object be applied that they appear borderless.

Vorteilhaft ist der relativ geringe Zeitbedarf; der gesamte Klebe­ vorgang, d. h. offene und geschlossene Wartezeit zusammen, betragen weniger als zwei Stunden. The relatively short time requirement is advantageous; all the glue process, d. H. open and closed waiting time together less than two hours.  

Das Verfahren eignet sich auch für dünne lösliche Bildfolien, durch Sprühen hergestellte Folien, sowie mikroporöse oder poröse Folien, wo­ bei ungewöhnliche Materialkombinationen stoffschlüssig und optisch einwandfrei geklebt werden können. Selbst bei der bekanntermaßen schwierigen Klebung von Bildfolien auf unpolare Kunststoffe wie Poly­ äthylen oder Polypropylen sind vergleichsweise zufriedenstellende Ergebnisse erzielbar.The process is also suitable for thin, soluble image films Spray produced foils, as well as microporous or porous foils, where with unusual material combinations, cohesive and optical can be glued properly. Even with the known difficult adhesion of picture foils on non-polar plastics such as poly Ethylene or polypropylene are comparatively satisfactory Results achievable.

Die Klebung von Kunststoffartikeln mit Bildfolien aus identischen Kunststoffen unter Verwendung eines Lösungsmittels führt zu sorten­ reinen Kompositionen, die von erheblicher Bedeutung für das stoffliche Recycling sind. Es ist ein besonderer Vorteil des Verfahrens, daß diese sortenreinen Kompositionen ohne gleichzeitige Belastung der Umwelt durch Lösungsmittel erzeugbar sind.The gluing of plastic articles with picture foils from identical Plastic using a solvent leads to varieties pure compositions that are of considerable importance for the material Are recycling. It is a particular advantage of the process that this single-variety compositions without polluting the environment can be generated by solvents.

Die rasche Verdunstung von Lösungsmitteln gefährdet Mitarbeiter und Umwelt. Verdunstende Stoffe sind zudem häufig leicht entzündlich oder bilden mit Luft explosionsfähige Gemische. Das vorliegende Verfahren verhindert diese negativen Erscheinungen.The rapid evaporation of solvents endangers employees and Environment. Evaporating substances are also often highly flammable or form explosive mixtures with air. The present procedure prevents these negative phenomena.

Die herausgedrückte/überschüssige Mittlersubstanz verdunstet in der Kälte nur wenig und kann gesammelt und wiederverwendet werden. Das Verfahren kann in kleinstem Umfang ebenso wie großtechnisch durch­ geführt werden.The pressed out / excess middle substance evaporates in the Cold only a little and can be collected and reused. The process can be carried out on a small scale as well as on an industrial scale be performed.

Das Verfahren eignet sich zum Aufbringen dünner Bildfolien, sowie von Schiebebildern auf oxydierende Metalle.The process is suitable for the application of thin picture foils as well as Sliding pictures on oxidizing metals.

Obwohl der erfindungsgemäß verwendete Temperaturbereich von plus 5 Grad Celsius bis minus 130 Grad Celsius genau das Gegenteil der üblichen Klebeverfahren darstellt, sind die Ergebnisse überraschend gut.Although the temperature range of plus 5 degrees used according to the invention Celsius to minus 130 degrees Celsius is exactly the opposite of the usual Represents bonding method, the results are surprisingly good.

Die Erfindung wird nachfolgend anhand von Zeichnungen und Beispielen näher erläutert, ohne jedoch darauf beschränkt zu sein.The invention is described below with reference to drawings and examples explained in more detail without being limited thereto.

Beispiel 1example 1

Aufbringen eines Abziehbildes auf einen Gegenstand dergestalt, daß das Abziehbild randlos erscheint.Applying a decal to one Subject such that the decal is borderless appears.

Fig. 1 zeigt die einzelnen Teile und Materialien vor der Verklebung. Eine gereinigte Kupferplatte (1) wird auf -30°C abgekühlt und mit gekühlter Zapponlösung so bestrichen, daß sich ein Flüssigkeitsfilm (3) auf der zu beklebenden Stelle bildet. Auf diesen Flüssigkeitsfilm wird ein Schiebebild (5) aufgebracht und positioniert. Fig. 1 shows the individual parts and materials before gluing. A cleaned copper plate ( 1 ) is cooled to -30 ° C and coated with cooled zappon solution so that a liquid film ( 3 ) forms on the area to be glued. A sliding image ( 5 ) is applied and positioned on this liquid film.

Das Bild wird glattgestrichen, wobei die unter der Folie befindliche Mittlersubstanz (3) größtenteils zum Rand des Schiebebildes gedrückt wird.The picture is smoothed out, whereby the middle substance ( 3 ) located under the film is largely pressed to the edge of the sliding picture.

Die überschüssige Lösung wird abgetupft, oder bei größeren Mengen abge­ streift und gesammelt.The excess solution is dabbed off, or abge with larger amounts grazes and collected.

Die Platte wird anschließend aus dem Kühlbereich herausgenommen.The plate is then removed from the cooling area.

Fig. 2 zeigt das auf einen permanenten Träger aufgebrachte Schiebebild. Die Mittlersubstanz (3) verbindet die Basis (1) und das Schiebebild (5) stoffschlüssig, wodurch eine gute Haltbarkeit gewährleistet ist. Erfindungsgemäß können dünne Folien verwendet werden, wodurch der Eindruck entsteht, das Bild wäre aufgedruckt. Fig. 2 shows the sliding image applied to a permanent carrier. The middle substance ( 3 ) cohesively connects the base ( 1 ) and the sliding pattern ( 5 ), which ensures good durability. According to the invention, thin foils can be used, which gives the impression that the image is printed.

Ein zusätzliches Beschichten verstärkt diesen Eindruck: der Rand des Schiebebildes ist kaum erkennbar.An additional coating reinforces this impression: the edge of the Sliding picture is hardly recognizable.

Besonders gute Ergebnisse können insbesondere dann erzeugt werden, wenn das aufgebrachte Schiebebild (5) aus derselben Substanz wie der Fest­ stoff der Mittlersubstanz (3) besteht, im vorliegenden Beispiel also aus Zapponlack.Particularly good results can be generated in particular if the applied sliding image ( 5 ) consists of the same substance as the solid substance of the middle substance ( 3 ), in the present example, therefore, of zappon lacquer.

Drucke oder Farben sind vorzugsweise auf die Unterseite des Schiebe­ bildes (4) aufzubringen, können sich aber auch, wie in Fig. 1 und Fig. 2 dargestellt, auf der Oberseite (6) des Schiebebildes, oder auf dem permanenten Träger (2) befinden. Prints or colors are preferably to be applied to the underside of the sliding picture ( 4 ), but can also, as shown in Fig. 1 and Fig. 2, on the top ( 6 ) of the sliding picture, or on the permanent support ( 2 ) .

Um beispielsweise einen Raumeffekt zu erzielen, kann sich auf dem Träger (1) Farbe (2) befinden. Die Unterseite des Schiebebildes (5) kann mit einem Druck (4) versehen sein, und ein zweiter Druck (6) auf der Oberseite der Folie (5) angebracht werden. Da keine oder nur geringfügige Veränderungen an den verwendeten Materialien eintreten, und Druckfarben oder Toner kaum an Brillianz verlieren, eignet sich das Verfahren in hervorragender Weise, um Farb­ kopien, die sich auf Folien oder Schiebebildern befinden, auf fast jedes beliebige Material aufzubringen.In order to achieve a spatial effect, for example, color ( 2 ) can be on the carrier ( 1 ). The underside of the sliding image ( 5 ) can be provided with a pressure ( 4 ) and a second pressure ( 6 ) can be applied to the top of the film ( 5 ). Since there are no or only minor changes to the materials used, and printing inks or toners hardly lose their brilliance, the process is ideally suited for applying color copies, which are on foils or sliding pictures, to almost any material.

Claims (11)

1. Verfahren zum Kleben von Bildfolien auf Träger mit Hilfe einer Mittlersubstanz durch Anwendung von künstlicher Kälte, Kältemischungen oder gekühlter Oberflächen dadurch gekennzeichnet, daß während der Dauer des Verfahrens eine Temperatur von minus 130 Grad Celsius bis unterhalb plus 5 Grad Celsius eingehalten wird wobei die verwendeten Materialien soweit abgekühlt werden, daß die Komposition aus Träger, Mittlersubstanz und aufzubringender Folie im Klebebereich eine Temperatur von minus 130 Grad Celsius bis unterhalb plus 5 Grad Celsius aufweist.1. A method for gluing image films on a carrier with the aid of an intermediate substance by using artificial cold, cold mixtures or cooled surfaces, characterized in that a temperature of minus 130 degrees Celsius to below plus 5 degrees Celsius is maintained during the duration of the process, the used Materials are cooled to such an extent that the composition of carrier, intermediate substance and film to be applied has a temperature in the adhesive area of minus 130 degrees Celsius to below plus 5 degrees Celsius. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß für die Mittlersubstanz eine Lösung aus dem Material des Trägers verwendet wird.2. The method according to claim 1, characterized in that for the Intermediate substance used a solution from the material of the carrier becomes. 3. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß für die Mittlersubstanz eine Lösung aus dem Folienmaterial verwendet wird.3. The method according to claim 1, characterized in that for the Middle substance a solution from the film material is used. 4. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß für die Mittlersubstanz Lösungsmittel verwendet werden.4. The method according to claim 1, characterized in that solvents are used for the intermediate substance. 5. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß für die Mittlersubstanz natürliche und synthetische Klebstoffe, Lacke, Dispersionen, Kitt, Leim oder Kleister verwendet werden.5. The method according to claim 1, characterized in that for the Middle substance natural and synthetic adhesives, lacquers, Dispersions, putty, glue or paste can be used. 6. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß für die Mittlersubstanz Celluloseester, natürlicher und synthetischer Kautschuk, Phenoplaste, Aminoplaste, Polyester, Polyisocyanate, Epoxydharze, Silicone oder Polymerisate von substituierten Äthylenen verwendet werden. 6. The method according to claim 1, characterized in that for the Intermediate substance cellulose ester, more natural and synthetic Rubber, phenoplasts, aminoplasts, polyesters, polyisocyanates, Epoxy resins, silicones or polymers of substituted ethylenes be used.   7. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß für die Mittlersubstanz Kältemittel verwendet werden.7. The method according to claim 1, characterized in that for the Medium refrigerant can be used. 8. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß für die Mittlersubstanz Farben, Pigmente und Toner verwendet werden.8. The method according to claim 1, characterized in that for the Medium substance colors, pigments and toners can be used. 9. Verfahren nach Anspruch 1, dadurch gekennzeichnet, daß für die Mittlersubstanz Mischungen der in den Ansprüchen 2 bis 8 enthaltenen Stoffe verwendet werden.9. The method according to claim 1, characterized in that for the middle substance mixtures of those in claims 2 up to 8 contained substances can be used. 10. Verwendung des Verfahrens nach einem oder mehreren der Ansprüche 1 bis 9, dadurch gekennzeichnet, daß Schiebebilder so aufgebracht werden, daß sie randlos erscheinen.10. Use of the method according to one or more of claims 1 to 9, characterized, that slide pictures are applied so that they appear borderless. 11. Verwendung des Verfahrens nach einem oder mehreren der Ansprüche 1 bis 9, dadurch gekennzeichnet, daß Folien oder Schiebebilder auf permanente Träger aufgebracht werden, die aus Metall, Metalloxyden, Kunststoff, Holz, Papier, Pappe, Gummi, Kautschuk, Leder, Wachs, Glas, Porzellan, Stein, Keramik, Lebens­ mitteln, Textilien und deren Kombinationen bestehen.11. Use of the method according to one or more of claims 1 to 9, characterized, that foils or sliding pictures are applied to permanent carriers, made of metal, metal oxides, plastic, wood, paper, cardboard, rubber, Rubber, leather, wax, glass, porcelain, stone, ceramics, life agents, textiles and their combinations.
DE4118063A 1991-06-01 1991-06-01 Process for gluing picture foils on carriers by applying artificial cold and using the process Expired - Fee Related DE4118063C2 (en)