DE3729630C1 - Practice explosive compositions formable by hand

Info

Publication number: DE3729630C1
Application number: DE19873729630
Authority: DE
Inventors: Rolf Dipl-Chem Dr Lafferenz; Ulrich Dipl-Ph Sassmannshausen
Original assignee: Dynamit Nobel AG
Current assignee: Dynamit Nobel AG
Priority date: 1987-09-04
Filing date: 1987-09-04
Publication date: 1989-03-02

Abstract

The present invention relates to plastic practice explosive compositions formable by hand. These compositions contain, in place of the highly explosive materials present in the powerful explosive compositions, a mixture of chalk, silicone oil and density regulators. The claimed compositions additionally contain, as additive, finely divided silica having a specific surface area between 130 and 390 m<2>/g in amounts between 0.4 and 1.5% by weight. The density regulators used are either wood flour or, according to the invention, hollow glass spheres and/or kieselguhr. The compositions of the invention are coloured using ultramarine blue as dye. The new practice explosive compositions are characterised by sticking to neither the fingers nor to the packing paper in the temperature range between -30@C and +50@C. Discoloration does not occur either.

Description

Gegenstand der vorliegenden Erfindung ist eine plastische, von Hand verformbare Exerziersprengmasse mit einer Dichte von 1,5 ±0,15 g/cm³ auf der Basis von Kreide, Siliconöl und Zuschlagstoffen. Solche Exerziersprengmassen dienen zu Übungszwecken als Ersatz für Sprengmassen auf der Basis von Pentaerythrittetranitrat oder anderen hochbrisanten, festen Sprengstoffen.The present invention relates to a plastic, hand-deformable explosive with a density of 1.5 ± 0.15 g / cm³ based on chalk, silicone oil and aggregates. Such explosive explosive devices serve Exercise as a replacement for explosives on the base of pentaerythritol tetranitrate or other highly explosive solid explosives.

Sprengmassen auf Basis von hochbrisanten, festen Spreng stoffen sind z. B. in der DE-C-20 27 709 beschrieben. Wenn man solche Sprengmassen zu Übungszwecken verwenden will, sollen sie keine hochbrisanten Sprengstoffe ent halten, aber die sonstigen Bekannten mechanischen Eigen schaften dieser Sprengmassen besitzen. Für solche Übungs zwecke sind bereits Exerziersprengmassen bekannt, die an Stelle des hochbrisanten Sprengstoffs ein Gemisch aus Kreide und Holzmehl aufweisen, dessen Dichte derjenigen des hochbrisanten Sprengstoffs entspricht, wobei das Holzmehl als Dichteregulans (=Dichtereguliermittel) dient. Diese bekannten Exerziersprengmassen enthalten weiterhin Siliconöle als Plastifiziermittel sowie Me tallseifen als Zuschlagstoffe und ggf. geringe Mengen an Farbstoffen.Explosives based on high explosive, solid explosives fabrics are z. B. described in DE-C-20 27 709. If you use such explosives for training purposes want, they should not ent explosive explosives hold, but the other known mechanical property properties of these explosives. For such practice For this purpose, explosive devices are already known to be used Make a mixture of the explosive explosives Have chalk and wood flour, the density of which of the explosive explosive, which is Wood flour as density regulator (= density regulator) serves. These known explosive explosive devices contain also silicone oils as plasticizers and Me tall soaps as additives and possibly small amounts of dyes.

Das Siliconöl in diesen bekannten Exerziersprengmassen dient dazu, der Masse über einen breiten Temperaturbe reich hinweg eine möglichst konstante Viskosität zu verleihen, damit sie in diesem Temperaturbereich pla stisch verformbar ist. Diese Produkte haben beispsiels weise bei +20°C eine Plastizität von 8,7 N und bei -10°C eine solche von 17,8 N (gemessen in einem Haake-Viskosimeter).The silicone oil in these well-known explosive devices serves the mass over a wide temperature range viscosity as constant as possible lend so that they pla is deformable. These products have examples exhibit a plasticity of 8.7 N at + 20 ° C and -10 ° C one of 17.8 N (measured in one Haake viscometer).

Diese bekannten Exerziersprengmassen haben jedoch den Nachteil, daß sie im Temperaturbereich zwischen -10°C und +30°C eine zu hohe Klebrigkeit aufweisen, so daß sie in diesem Temperaturbereich an den Fingern oder der Haut sowie dem Einwickelpapier kleben bleiben.However, these known explosive explosive devices have the Disadvantage that they are in the temperature range between -10 ° C. and + 30 ° C have too high stickiness, so that them in this temperature range on the fingers or the Skin and the wrapping paper stick.

Es bestand deshalb die Aufgabe, Exerziersprengmassen aufzufinden, die eine Dichte entsprechend der Dichte von Sprengmassen aus festen, hochbrisanten Sprengstof fen besitzen, die im Temperaturbereich von -10 bis +30°C plastisch verformbar sind, in diesem Tempera turbereich homogen verbleiben und nicht an den Fin gern oder dem Verpackungspapier kleben bleiben. Die Bedingung der Nichtklebrigkeit in dem genannten Tem peraturbereich soll weiterhin bewirken, daß ein in der Masse ggf. enthaltener Farbstoff nicht zum Verfär ben der Haut, die mit der Masse in Berührung kommt, führt.There was therefore the task of explosive ordnance find the one density corresponding to the density of explosives from solid, highly explosive explosives fen have in the temperature range from -10 to + 30 ° C are plastically deformable, in this tempera remain homogeneous and not to the fin like or stick to the packaging paper. The Condition of non-stickiness in the mentioned tem temperature range should continue to cause an in the mass of any dye may not be discolored skin that comes into contact with the mass, leads.

In Erfüllung dieser Aufgabe wurde nun eine Exerzier sprengmasse mit einer Dichte von 1,5 ±0,15 g/cm³ aus Kreide, Siliconöl, Dichteregulanzien und Zuschlagstoffen gefunden, die dadurch gekennzeich net ist, daß sie als Zuschlagstoff feinverteilte Kie selsäure mit einer spezifischen Oberfläche zwischen 130 und 390 g/m² in Mengen zwischen 0,4 und 1,5 Gew.-% enthält.In the fulfillment of this task, an exercise was now carried out explosive mass with a density of 1.5 ± 0.15 g / cm³ Chalk, silicone oil, density regulators and Aggregates found, characterized by net is that they are fine aggregate Kie silica with a specific surface between 130 and 390 g / m² in quantities between 0.4 and 1.5% by weight contains.

Der Zusatz der feinverteilten Kieselsäure bewirkt, daß die Exerziersprengmasse nicht an den Fingern kleben bleibt. Die Kieselsäure kann an Stelle der als Zuschlag stoffe bekannten Metallseifen eingesetzt werden, so daß der Zusatz von Metallseifen erfindungsgemäß nicht not wendig ist. Trotz der Abwesenheit der Metallseifen wei sen die erfindungsgemäßen Exerziersprengmassen alle übrigen wichtigen Eigenschaften der bekannten Massen, die solche Metallseifen enthalten, auf; sie sind im Temperaturbereich zwischen -40°C und +50°C pla stisch, von Hand verformbar und besitzen eine Dichte von 1,5 ±0,15 g/cm³.The addition of the finely divided silica causes that do not stick the explosive device to your fingers remains. The silica can be used as a supplement Fabrics known metal soaps are used, so that the addition of metal soaps according to the invention is not necessary is agile. Despite the absence of metal soaps white sen the explosive bombs according to the invention all other important properties of the known masses, containing such metal soaps; You are in Temperature range between -40 ° C and + 50 ° C pla table, can be deformed by hand and have a density of 1.5 ± 0.15 g / cm³.

Die zuzusetzende feinverteilte Kieselsäure, die im all gemeinen in Form von SiO₂ vorliegt, ist auch unter der Bezeichnung "pyrogene Kieselsäure" bekannt. Solche py rogene Kieselsäure hat spezifische Oberflächen zwischen 100 und 400 m²/g. Die einzusetzende Kieselsäure ist vorzugsweise eine solche pyrogene Kieselsäure; doch kön nen auch andere Kieselsäurearten, wie z. B. die Fäl lungskieselsäure, eingesetzt werden, sofern deren spezi fische Oberfläche zwischen 130 und 390 m²/g liegt. Auch getrocknete Kieselgele mit dieser spezifischen Ober fläche können eingesetzt werden.The finely divided silica to be added, which in all common is in the form of SiO₂, is also under the The term "pyrogenic silica" is known. Such py rogenous silica has specific surfaces between 100 and 400 m² / g. The silica to be used is preferably such a fumed silica; but can NEN other types of silica, such as. B. the fall silicic acid, if their speci fish surface is between 130 and 390 m² / g. Also dried silica gels with this specific upper surface can be used.

Die Menge der feinverteilten Kieselsäure in der neuen Exerziersprengmasse liegt zwischen 0,4 und 1,5 Gew.-%. Der Einsatz größerer Mengen ist prinzipiell möglich, bringt aber keine Vorteile hinsichtlich der Verhinderung der Klebrigkeit.The amount of finely divided silica in the new one Parade explosive is between 0.4 and 1.5 wt .-%. In principle, the use of larger quantities is possible but brings no advantages in terms of prevention of stickiness.

Sofern die Masse eingefärbt vorliegen soll, hat sich Ultramarinblau als Farbstoff besonders gut bewährt. Die Verbindung hat den Vorteil, daß sie nicht abfärbt, weder auf die menschliche Haut noch auf bekannte Verpackungs papiere für Sprengmassen.If the mass is to be colored, it has Ultramarine blue has proven to be a particularly good dye. The Connection has the advantage that it does not rub off, neither on human skin still on familiar packaging papers for explosives.

Als Verpackungspapiere für die erfindungsgemäßen Spreng massen dienen vorzugsweise solche Aluminiumverbundfolien, die auch in den bisher bekannten Exerziersprengmassen eingesetzt werden. Allgemein handelt es sich dabei um solche Aluminiumfolien, die auf der Mattseite auf Poly esterfolie und auf der Glanzseite mit Polyethylenfolie lackkaschiert sind. Dem Fachmann sind solche Verpackungs folien bekannt, die allgemein auch als Einwickelpapiere bezeichnet werden.As packaging paper for the explosives according to the invention such composite aluminum foils are preferably used, which also in the previously known explosive devices be used. In general, it is about such aluminum foils on the matt side on poly ester film and on the glossy side with polyethylene film are lacquered. Such packaging are known to the person skilled in the art foils known, also commonly known as wrapping papers be designated.

Die erfindungsgemäßen Exerziersprengmassen blieben in dem genannten Temperaturbereich an diesen Einwickelpa pieren nicht kleben und können aus diesen problemlos ausgewickelt werden, ohne daß Reste auf dem Papier haf ten bleiben. Dieses geringe Klebeverhalten bleibt auch erhalten, wenn die erfindungsgemäßen Massen einer Tem peraturwechsel-Lagerung unterworfen waren.The explosive devices according to the invention remained in the mentioned temperature range at this wrapping pa do not stick and can easily be made from them be unwrapped without any residue on the paper stay. This low adhesive behavior remains obtained when the masses of the invention a Tem temperature change storage were subjected.

Die erfindungsgemäßen Massen können als Dichteregulan zien außer dem dafür bekannten Holzmehl erfindungsgemäß auch Kieselgur oder Glas-Hohlkügelchen enthalten. Wegen ihrer geringen Dichte können diese Substanzen in erheb lich geringerer Menge als Holzmehl eingesetzt werden. Ihre Menge hängt von ihrer Dichte ab; sie wird so ge wählt, daß sie zusammen mit der Kreide ein Gemisch er gibt, deren spezifisches Gewicht im Bereich zwischen 1,35 und 1,65 g/cm³ liegt. Im allgemeinen sind diese Dichteregulanzien in den erfindungsgemäßen Sprengmassen in Mengen zwischen 2 und 10 Gew.-% enthalten.The compositions according to the invention can be used as density regulators zien except the known wood flour according to the invention also contain diatomaceous earth or hollow glass beads. Because of Their low density can significantly increase these substances Lich less amount than wood flour can be used. Their amount depends on their density; it is so ge chooses to mix it with the chalk there, the specific weight in the range between 1.35 and 1.65 g / cm³ is. Generally these are Density regulators in the explosive compositions according to the invention contained in amounts between 2 and 10 wt .-%.

Außer Kreide enthalten die erfindungsgemäßen Exerzier sprengmassen noch Siliconöle, die auch in den bekannten Massen eingesetzt werden. Diese geben der Masse ihre Plastizität in dem gewünschten Temperaturbereich. Dem Fachmann sind die für dieses Einsatzgebiet verwendba ren Siliconöle bekannt; sie haben im allgemeinen eine Viskosität von 4000 bis 20 000 mm²/s. Ihr Anteil in den Sprengmassen hängt von ihrer Viskosität und der ge wünschten Plastizität der Massen ab. Er liegt im allge meinen zwischen 20 und 30 Gew.-%, bezogen auf die Ge samtmasse.In addition to chalk, the exercises according to the invention contain explosives still silicone oils, which are also in the known Masses are used. These give the masses their own Plasticity in the desired temperature range. The Those skilled in the art are usable for this area of application ren known silicone oils; they generally have one Viscosity from 4000 to 20,000 mm² / s. Your share in the explosives depend on their viscosity and the ge wanted plasticity of the masses. It is in general mean between 20 and 30 wt .-%, based on the Ge velvet mass.

Die erfindungsgemäßen Massen besitzen außer der bereits genannten geringen Klebrigkeit die an sie geforderten Plastizitätseigenschaften: Sie sind im Temperaturbereich zwischen -40°C und +50°C von Hand formbar, ohne daß eine Vorbehandlung durch Kneten notwendig ist. Beim Ver formen bilden sich keine Risse. Die Masse bleibt in dem genannten Temperaturbereich homogen, und ein Entweichen einzelner Bestandteile (z. B. Ausseigern von Siliconöl) tritt nicht ein.The masses according to the invention already have that mentioned low stickiness the required of them Plasticity properties: They are in the temperature range can be shaped by hand between -40 ° C and + 50 ° C without pretreatment by kneading is necessary. When ver shapes do not form cracks. The mass stays in that mentioned temperature range homogeneous, and an escape individual components (e.g. silicone oil leaking out) does not occur.

Die Herstellung der erfindungsgemäßen Massen erfolgt in an sich bekannter Weise durch gemeinsames Vermischen der Bestandteile.The compositions of the invention are produced in in a known manner by mixing together of the components.

Example 1

Es wurde eine Masse aus folgenden Bestandteilen herge stellt:
55,4 Gew.-Teile Kreide
(spezifische Oberfläche 10 000 m²/g)
16,4 Gew.-Teile Holzmehl
0,6 Gew.-Teile pyrogene Kieselsäure
(spezifische Oberfläche 200 m²/g)
27,0 Gew.-Teile Siliconöl M 60 000
1,0 Gew.-Teile Ultramarinblau.A mass was produced from the following components:
55.4 parts by weight of chalk
(specific surface area 10,000 m² / g)
16.4 parts by weight of wood flour
0.6 part by weight of fumed silica
(specific surface 200 m² / g)
27.0 parts by weight of silicone oil M 60 000
1.0 part by weight of ultramarine blue.

Nach einer Temperaturwechsel-Lagerung zwischen -40°C und +30°C im Rhythmus von jeweils 48 Stunden war die Masse im Temperaturbereich zwischen -40°C und +50°C von Hand formbar, ohne daß eine Vorbehandlung durch Kneten erforderlich war. Weiterhin blieb sie weder an den Fingern noch am Verpackungspapier haften.After a temperature change storage between -40 ° C and + 30 ° C every 48 hours the mass in the temperature range between -40 ° C and + 50 ° C can be shaped by hand without any pretreatment by kneading was required. She stayed on stick neither to the fingers nor to the packaging paper.

Claims

1. Plastic, hand-deformable explosive explosive with a density of 1.5 ± 0.15 g / cm³ on the basis of chalk, silicone oil, density regulators and additives, characterized in that they are finely divided silica with a specific surface as an additive contains between 130 and 390 m² / g in amounts between 0.4 and 1.5 wt .-%.

2. drill explosive according to claim 1, characterized records that it ent as ultramarine blue dye holds.

3. explosive explosive according to claim 1 or 2, characterized characterized as a glass-hollow density regulator contains beads and / or diatomaceous earth.