DE3446632A1 - Conductive paper suitable for making decorative laminates - Google Patents
Conductive paper suitable for making decorative laminatesInfo
- Publication number
- DE3446632A1 DE3446632A1 DE19843446632 DE3446632A DE3446632A1 DE 3446632 A1 DE3446632 A1 DE 3446632A1 DE 19843446632 DE19843446632 DE 19843446632 DE 3446632 A DE3446632 A DE 3446632A DE 3446632 A1 DE3446632 A1 DE 3446632A1
- Authority
- DE
- Germany
- Prior art keywords
- paper
- conductive
- laminate
- conductive paper
- ohms per
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
PRINZ, LEISER, BjUiNkE : &/PAR-TO E RPRINZ, LEISER, BjUiNkE: & / PAR-TO E R
Patentanwälte · European. Patent Attorneys O / / £* C OPatent Attorneys European. Patent Attorneys O / / £ * CO
München StuttgartMunich Stuttgart
20. Dezember 1984December 20, 1984
THE MEAD CORPORATION
Courthouse Plaza Northeast
Dayton, Ohio 45463 /USA THE MEAD CORPORATION
Courthouse Plaza Northeast
Dayton, Ohio 45463 / USA
Unser Zeichen: M 1625Our reference: M 1625
Zur Herstellung dekorativer Schichtstoffe geeignetes leitfähiges PapierConductive paper suitable for making decorative laminates
Die Erfindung betrifft leitfähiges Papier, das zur Herstellung dekorativer Schichtstoffe geeignet ist und vorbestimmte elektrische Eigenschaften aufweist, der Art, daß statische elektrische Ladungen wirksam abgeleitet werden.The invention relates to conductive paper suitable for the production of decorative laminates and predetermined has electrical properties such that static electrical charges are effectively dissipated will.
Es sind, ganz allgemein, zwei Arten von Anordnungen zur statischen Entladung bekannt. Bei der einen Art wird die statische Aufladung schnell entladen, bei der anderen Art fließt die statische Ladung langsam ab, wobei ihre Speicherung verhindert wird. Die erstere Art ist für solche Anwendungen geeignet, bei denen die Vermeidung von die statische Entladung begleitenden Funken nichtIn general, two types of static discharge arrangements are known. With one kind, the Discharge static charge quickly, with the other type the static charge drains slowly, with yours Storage is prevented. The former type is suitable for those applications where avoidance sparks accompanying static discharge
Bj/MaBj / Ma
♦ ΟΙ wichtig ist. Die zweite Art wird zur Vermeidung von Funken in gefährlicher Umgebung verwendet, beispielsweise in Getreidehebern und medizinischen Behandlungsräumen, oder in statisch empfindlicher Umgebung, beispielsweise in Räumen mit Computern und Datenverarbeitungsanlagen .♦ ΟΙ is important. The second type is to avoid Sparks used in hazardous environments, such as grain elevators and medical treatment rooms, or in a statically sensitive environment, for example in rooms with computers and data processing systems .
Es gibt eine ganze Reihe von im Handel erhältlichen Materialien für die Steuerung der statischen Entladung, darunter Polymere, die durch Einarbeitung leitender Teilchen oder Fasern leitfähig gemacht wurden, sowie textile Materialien, die ganz oder teilweise aus leitfähigen Fasern gewoben wurden. Aus einigen dieser Materialien wurden Wandbeläge, Fußböden, Tisch- und Möbelbeläge u.dgl. hergestellt (vgl. z.B. US-PS 3 457 499, 4 208 696 und 4 234 648).There are a number of commercially available materials for controlling static discharge, including polymers made conductive by the incorporation of conductive particles or fibers, as well as textile materials that are wholly or partially woven from conductive fibers. From some of these Materials, wall coverings, floors, table and furniture coverings and the like were produced (see e.g. US-PS 3 457 499, 4 208 696 and 4 234 648).
Dekorative Schichtstoffe werden gewöhnlich als Möbelfurniere, Möbelbeläge, Wandverkleidungsplatten u.dgl.Decorative laminates are usually used as furniture veneers, Furniture coverings, wall cladding panels and the like.
verwendet. Ein dekorativer Schichtstoff besteht aus verschiedenen Lagen aus kunststoffbeschichtetem Papier, die unter Wärme und Druck zu einem Verbund verfestigt werden. Ein typischer dekorativer Schichtstoff enthält verschiedene Lagen eines Kernmaterials, das dem Schichtstoff seine Hauptmasse verleiht, eine Sperrschicht, eine dekorative oder "Dekor"-Schicht, die dem Laminat hauptsächlich das gewünschte Design verleiht, sowie eine klare Uberzugsschicht. Jede dieser Schichten und Lagen besteht aus einem mit Kunststoff imprägnierten Papier.used. A decorative laminate consists of different layers of plastic-coated paper, which are consolidated into a composite under heat and pressure. A typical decorative laminate contains different layers of a core material that gives the laminate its bulk, a barrier layer, a decorative or "decor" layer that primarily gives the laminate the desired design, as well as a clear coating layer. Each of these layers and plies consists of one impregnated with plastic Paper.
Früher wurden dekorative Schichtstoffe bei bestimmten Anwendungsfällen zur Kontrolle der Funkenentladung verwendet. In diesen Fällen wurden eines oder mehrere der die Laminate bildenden Papiere durch Dispergieren von Ruß in der Papierbahn hergestellt. Diese Schichtstoffe waren jedoch nicht ganz befriedigend. Um SchichtstoffeDecorative laminates used to be used at certain Use cases used to control spark discharge. In these cases, one or more of the the papers forming the laminates are made by dispersing carbon black in the paper web. These laminates however, were not entirely satisfactory. About laminates
1 41 4
mit geringem Flächenwiderstand (z.B. 10 bis 10 Ohm pro Quadrat) herzustellen, sind größere Mengen an Ruß erforderlich als von den Papieren, die üblicherweise für dekorative Schichtstoffe verwendet werden, aufgenommen werden können. Wegen dieses Retentionsproblems gab es eine Widerstandsgrenze bei den unter Verwendung von Ruß hergestellten leitfähigen Papieren, die umgekehrt proportional zum Grundgewicht des Papiers ist.with low sheet resistance (e.g. 10 to 10 Ohm per Square), larger amounts of carbon black are required than the papers that are usually used for decorative laminates used can be included. Because of this retention problem, there was a resistance limit in conductive papers made using carbon black that is inversely proportional to the basis weight of the paper.
-^q Die Verwendung von Ruß in dekorativen Schichtstoffen ist auch ästhetisch nicht wünschenswert. Sogar bei den Anwendungsfällen für das langsame Abführen statischer Ladungen, beispielsweise bei den Möbeloberflächen in Computerräumen u.dgl., bei denen die in die Papiere- ^ q The use of carbon black in decorative laminates is also not aesthetically desirable. Even with the use cases for slow discharge of static Charges, for example in the furniture surfaces in computer rooms and the like. Where the in the papers
ic eingearbeiteten Rußmengen geringer sind und die Papiere in der Lage sind, die zur Erzielung der gewünschten Widerstandshöhe erforderliche Rußmenge aufzunehmen, macht der Ruß das Laminat schwarz und ästhetisch■unattraktiv, und der Schichtstoff kann nicht bedruckt oder in üblicher Weise mit einem Dekor versehen werden.ic incorporated amounts of soot are lower and the papers are able to absorb the amount of soot required to achieve the desired level of resistance, the carbon black makes the laminate black and aesthetically ■ unattractive, and the laminate cannot be printed or decorated in the usual way.
Somit besteht ein Bedürfnis für ein leitfähiges Papier, das für die Herstellung dekorativer Schichtstoffe geeignet ist und die für die statische Entladung erforderliehen elektrischen Eigenschaften aufweist, insbesondere bei den Anwendungsfällen, die eine schnelle Entladung erfordern, und das darüber hinaus ästhetisch ansprechend ist.Thus, there is a need for a conductive paper useful for making decorative laminates suitable and required for static discharge Has electrical properties, especially in those applications that require a fast Require discharge, and which is also aesthetically pleasing.
Dieses Bedürfnis wird durch die Bereitstellung des beanspruchten erfindungsgemäßen Papiers befriedigt.This need is satisfied by providing the paper according to the invention as claimed.
Mit der Erfindung wird ein leitfähiges Papier bereitgestellt, das zur Herstellung dekorativer Schichtstoffe geeignet ist, die durch Dispergieren leitfähiger Fasern in einer Papierbahn hergestellt werden. Es wurde gefunden, daß durch die Herstellung leitfähiger Papiere durchThe invention provides a conductive paper which can be used to produce decorative laminates which are made by dispersing conductive fibers in a paper web is suitable. It was found, that by making conductive papers
Dispergieren leitfähiger Fasern, im Gegensatz zu Ruß, in der Papierbahn ein geringerer Widerstand erzielt werden kann. Insbesondere gibt es keine Retentionsprobleme mehr bei geringen Grundgewichten, wie sie bei der Verwendung von Ruß auftraten, und es werden wesentlich geringere Widerstandswerte bei leichten Papieren erreicht. Darüber hinaus sind die Kohlenstoffasern ästhetisch wünschenswerter als Ruß. Bei Anwendungen, bei denen ein höherer Widerstand gewünscht wird, z.B.Dispersing conductive fibers, as opposed to carbon black, in the paper web achieves a lower resistance can be. In particular, there are no longer any retention problems with low basic weights, as in the use of carbon black occurred, and the resistance values are much lower with light papers achieved. In addition, the carbon fibers are more aesthetically desirable than carbon black. For applications where higher resistance is desired, e.g.
für das langsame Abführen statischer Ladung, besitzen die leitfähigen Fasern ein ästhetisch ansprechendes Erscheinungsbild, und die Papiere können bedruckt und in üblicher Weise mit einem Dekor versehen werden. Mit der Erfindung wird außerdem eine Verbesserung im Aussehen der Papiere mit niedrigem Widerstand und der Schichtstoffe erreicht, die größere Fasermengen enthalten. for the slow discharge of static charge, the conductive fibers have an aesthetically pleasing one Appearance, and the papers can be printed and provided with a decoration in the usual way. With of the invention also provides an improvement in the appearance of the low resistance papers and the Reached laminates that contain larger amounts of fiber.
Eine Ausführungsform der Erfindung besteht somit aus einem leitfähigen Papier, das zur Herstellung dekorativer Schichtstoffe geeignet ist und eine Papierbahn mit darin dispergierten leitfähigen Fasern umfaßt, wobei die Fasern in einer Menge vorliegen, die für die Entladung einer statischen elektrischen Ladung ausreicht, wenn das Papier geerdet wird.One embodiment of the invention thus consists of a conductive paper which is suitable for the production of decorative laminates and a paper web with conductive fibers dispersed therein, the fibers being present in an amount suitable for discharge static electrical charge when the paper is grounded.
Eine andere Ausführungsform der Erfindung besteht aus einem dekorativen Schichtstoff aus einer Vielzahl von verfestigten kunststoffimprägnierten Papierlagen, von denen eine oder mehrere ein solches vorstehend beschriebenes leitfähiges Papier ist.Another embodiment of the invention consists of a decorative laminate of a plurality of solidified plastic-impregnated paper layers, one or more of which is described above conductive paper is.
Eine weitere Ausführungsform der Erfindung besteht aus einem leitfähigen Papier mit einem Flächenwiderstand von weniger als 10 Ohm pro Quadrat sowie aus einem dekorativen Schichtstoff, der dieses Papier enthält.Another embodiment of the invention consists of a conductive paper with a sheet resistance of less than 10 ohms per square; as well as a decorative laminate that contains this paper.
Repräsentative Beispiele für leitfähige Fasern, die für die erfindungsgemäßen Zwecke geeignet sind, sind. Kohlenstoff asern, Metallfasern und metallbeschichtete Fasern. Der Ausdruck "Kohlenstoffasern" bezeichnet ganz allgemein kohlenstoffhaltige oder graphithaltige Fasern mit leitfähigen Eigenschaften und schließt durch Karbonisieren von Polyacrylnitrilfasern hergestellte Kohlenstoffasern, Kunstseidespinnfasern und Ligninfasern ein. Das typischste Beispiel für eine erfindungsgemäß verwendbare metallbeschichtete Faser ist metallbeschichtete Glasfaser, beispielsweise eine mit Aluminium beschichtete Faser, die durch Eintauchen von Endlos-Glasfasern in geschmolzenes Aluminium oder durch Aluminiumdampfabscheidung auf der Oberfläche der Glasfaser hergestellt wird.Representative examples of conductive fibers suitable for the purposes of the present invention are. carbon fibers, metal fibers and metal-coated fibers. The term "carbon fibers" denotes very generally carbon-containing or graphite-containing fibers with conductive properties and closes by carbonization carbon fibers made from polyacrylonitrile fibers, Rayon staple fibers and lignin fibers. The most typical An example of a metal-coated fiber that can be used according to the invention is metal-coated glass fiber, For example, an aluminum-coated fiber made by immersing continuous glass fibers in molten Aluminum or by aluminum vapor deposition on the surface of the glass fiber.
Die erfindungsgemäß verwendeten leitfähigen Fasern müssen eine Größe besitzen, die im Papierstoff (Pulpe) im Verlauf des Papierherstellungsverfahrens dispergiert werden kann. In der Regel sind Fasern im Bereich zwischen etwa 0,5 bis 30 Denier und zwischen etwa 0,5 bis 30 mm Länge für diesen Zweck geeignet. Vorzugsweise haben die Fasern ein Größenverhältnis (Verhältnis zwischen Länge und Durchmesser) von mindestens 3,0. Fasern, die länger sind als 30 mm, können verwendet werden, sofern bestimmte, darauf speziell abgestimmte Papierherstellungsmaschinen verwendet werden, beispielsweise eine entsprechend angepaßte Foudrinier-Maschine und eine Rotationspapiermaschine, die in der Lage ist, Fasern dieser Länge in der Pulpe zu dispergieren. Fasern, die schwerer sind als 30 Denier, sind im allgemeinen weniger geeignet, weil sie zu schwer zu dispergieren sind, ästhetisch nicht ansprechend sind und dem Papier einen unerwünschten Griff verleihen.The conductive fibers used according to the invention must have a size that is in the paper stock (pulp) can be dispersed in the course of the papermaking process. Usually fibers are in the area between about 0.5 to 30 denier and between about 0.5 to 30 mm in length are suitable for this purpose. Preferably they have Fibers have an aspect ratio (ratio between length and diameter) of at least 3.0. Fibers that are longer are than 30 mm, can be used, provided certain, specially adapted paper making machines can be used, for example a suitably adapted Foudrinier machine and a rotary paper machine, which is able to disperse fibers of this length in the pulp. Fibers that are heavier than 30 denier, are generally less suitable because they are too difficult to disperse aesthetically are not appealing and give the paper an undesirable feel.
Die Fasern können mit einem Finish versehen werden, um ihre Dispergierbarkeit zu verbessern und um zu vermeiden, daß die Fasern in der Pulpe aneinander haften bleiben.The fibers can be given a finish to improve their dispersibility and to avoid that the fibers in the pulp stick together.
Zu diesem Zweck können bekannte, üblicher Finishs verwendet werden, beispielsweise anionische oberflächenaktive Mittel auf Basis sulfonierter öle. Wenn sich die Fasern in befriedigender Weise dispergieren lassen, ist ein Finish natürlich nicht erforderlich.For this purpose, known, customary finishes can be used are, for example, anionic surfactants based on sulfonated oils. If the To allow fibers to disperse in a satisfactory manner, a finish is of course not required.
Die in dem Papier verwendete Fasermenge hängt von deren Größe, Dispergierbarkeit und Leitfähigkeit sowie von den im Papier gewünschten elektrischen Eigenschaften ab. 10The amount of fiber used in the paper depends on them Size, dispersibility and conductivity as well as of the electrical properties desired in the paper. 10
Der Trockenwiderstand des erfindungsgemäßen Papiers kann im Bereich zwischen etwa 10 Ohm pro Quadrat bisThe dry resistance of the paper of the invention can range between about 10 ohms per square to
10
10 Ohm pro Quadrat liegen; üblicherweise wird er aber zwischen etwa 10 bis 10 Ohm pro Quadrat liegen. Wenn
der Flächenwiderstand des Papiers quantitativ wesentlich10
10 ohms per square; but usually it will be between about 10 to 10 ohms per square. When the sheet resistance of the paper is quantitatively significant
4
geringer als 10 Ohm pro Quadrat ist, findet schnelle statische Entladung statt, die von einer Funkenentladung
begleitet sein kann. Liegt der Flächenwiderstand dagegen über 10 Ohm pro Quadrat, neigt das Papier dazu, die
statische Aufladung zu langsam abzuführen und eine stati sche Ladung bis zu einer Höhe aufzubauen, bei der eine
Funkenentladung zu einem Gegenstand niedrigeren Potentials auftreten kann. Bei Anwendungsfällen, bei denen
also eine kontrollierte Entladung ohne Funkenbildung erwünscht ist, sollten die Papiere eine ausreichende
Fasermenge enthalten, um einen Flächenwiderstand im Bereich von 10 bis 10 Ohm pro Quadrat sicherzustellen.
Diese Papiere sind allgemein zur Herstellung dekorativer Schichtstoffe geeignet, die als Furnier, Wandverkleidung4th
is less than 10 ohms per square, rapid static discharge occurs, which can be accompanied by a spark discharge. If, on the other hand, the sheet resistance is above 10 ohms per square, the paper tends to dissipate the static charge too slowly and to build up a static charge up to a level at which a spark discharge to an object of lower potential can occur. For applications in which a controlled discharge without spark formation is desired, the papers should contain a sufficient amount of fiber to ensure a sheet resistance in the range of 10 to 10 ohms per square. These papers are generally suitable for the production of decorative laminates, which are used as veneers and wall cladding
^O oder Fußbodenbelag verwendet werden können. Für eine schnelle Entladung oder die Vermeidung einer statischen Aufladung sind Papiere mit einem Trockenwiderstand im^ O or flooring can be used. For one fast discharge or the avoidance of static charge are papers with a dry resistance in the
1 4
Bereich von 10 bis 10 Ohm pro Quadrat wünschenswert.1 4
10 to 10 ohms per square range desirable.
Aus diesen Papieren können Schichtstoffe hergestellt werden, die als Eliminatoren statischer Aufladung geeignet sind. Bei den bekanntesten leitfähigen Fasern kann eine Leitfähigkeit innerhalb der vorstehend genanntenLaminates can be made from these papers suitable as static eliminators. In the case of the most popular conductive fibers, a conductivity within the aforementioned
3443632 -7-ΛΑ- 3443632 -7-ΛΑ-
Bereiche unter Verwendung von etwa 0,25 bis 10 Gew.% leitfähiger Fasern, bezogen auf das Gewicht des Papierstoff eintrage, erzielt werden.Areas using about 0.25 to 10 weight percent conductive fibers based on the weight of the stock entries, can be achieved.
Die erfxndungsgeitiaßen Papiere können unter Verwendung herkömmlicher Papierherstellungsverfahren hergestellt werden. Grob gesagt, werden bei der Herstellung des Papiers folgende Verfahrensstufen durchlaufen:The papers of the invention can be used conventional papermaking processes. Roughly speaking, when making the Paper go through the following process stages:
(i) die leitfähigen Fasern und sonstige Bestandteile des Eintrags werden in Standard-Holländern, Stofflösern oder Vorratsbehältern vermischt;(i) the conductive fibers and other components of the entry are in standard Dutch, Pulpers or storage containers mixed;
(ii) die Papierbahn wird auf einem Standard-Naßzylinder, Langsieb oder Foudrinier-Maschine gebildet und(ii) the paper web is placed on a standard wet cylinder, Fourdrinier or foudrinier machine formed and
(iii) die Bahn wird mittels üblicher Trocknungsbleche oder Öfen getrocknet.(iii) the web is dried using conventional drying trays or ovens.
Wenn die Papierbahn bedruckt werden soll, wird sie vorzugsweise kalandriert. Das Papier kann eingefärbt oder pigmentiert werden, um verschiedene dekorative Effekte zu erzeugen. In manchen Fällen ist es erwünscht, ein undurchoeheinend machendes Mittel wie TiO.-, in die Pulpe einzuarbeiten.If the paper web is to be printed, it is preferably calendered. The paper can be colored or pigmented to create various decorative effects. In some cases it is desirable an impenetrable agent like TiO.-, into the Incorporate pulp.
Es kann praktisch jede herkömmlich hergestellte Pulpe für die erfindungsgemäßen Zwecke verwendet werden. Die Pulpe wird vorzugsweise vor der Zugabe der leitfähigen Fasern raffiniert, um zn vermeiden, daß die Faser nach ihrer Einarbeitung bricht. Eine hierfür angewandte Methode besteht darin, die leitfähige Faser in einem Vorratsbehälter zu raffinierter Zellulosefaser zu geben. Die Pulpe wird üblicherweise in einer Konsistenz von etwa 1 % auf die Papierherstellungsmaschine gegeben.Virtually any conventionally made pulp can be used for the purposes of the present invention. The pulp is preferably refined prior to the addition of the conductive fibers, avoid zn that the fiber breaks after their incorporation. One method used for this is to add the conductive fiber to refined cellulose fiber in a storage container. The pulp is usually placed on the papermaking machine at a consistency of about 1%.
34465323446532
Das erfindungsgemäße leitfähige Papier kann in verschiedenen Gewichten hergestellt werden. Üblicherweise liegen die verwendeten Papiere im Bereich zwischen etwa 0,016 bis 1,63 kg/m2, je nach dem beabsichtigten Verwendungszweck, und häufiger zwischen etwa 0,024 bis 0,195 kg/m2. Für die meisten Anwendungsfälle ist es erwünscht, wenn das Papier eine Naßzugfestigkeit von mehr als 236 g/cm aufweist.The conductive paper according to the invention can be produced in various weights. Typically, the papers used will range between about 0.016 to 1.63 kg / m 2 , depending on the intended use, and more often between about 0.024 to 0.195 kg / m 2 . For most applications it is desirable for the paper to have a wet tensile strength greater than 236 g / cm.
Um die Kunststoffimprägnierung zu erleichtern, ist es erwünscht, daß das Papier eine kurze Kunststoffimprägnierungszeit besitzt. Dies kann durch die Art der verwendeten Pulpe und den Raffinationsgrad, den Grad des Naßpressens und des Kalandrierens während der Papierherstellung beeinflußt und gesteuert werden. Vorzugsweise werden die erfindungsgemäßen Papiere so hergestellt, daß sie eine Kunststoffdurchdringungsgeschwindigkeit von weniger als etwa 40 Sekunden, vorzugsweise von weniger als etwa 20 Sekunden, aufweisen. Diese Geschwindigkeit wird durch Flotten einer Papierprobe auf einem Kunststoffvorrat (z.B. einer Lösung von Monsanto 841 in Wasser und Methanol (50:50) mit einer Viskosität von 92 mPas) bei 250C gemessen, wobei die Zeit gemessen wird, die es dauert, bis die Lösung das Papier durchnäßt hat.In order to facilitate plastic impregnation, it is desirable that the paper have a short plastic impregnation time. This can be influenced and controlled by the type of pulp used and the degree of refining, the degree of wet pressing and calendering during papermaking. Preferably, the papers of the invention are made so that they have a plastic penetration rate of less than about 40 seconds, preferably less than about 20 seconds. This speed is measured by flooding a paper sample on a plastic supply (for example a solution of Monsanto 841 in water and methanol (50:50) with a viscosity of 92 mPas) at 25 ° C., the time it takes to be measured the solution soaked the paper.
Um die gewünschten elektrischen Eigenschaften sowie das gewünschte ästhetische Aussehen zu erreichen, sollten die leitfähigen Fasern gleichmäßig in dem Papier dispergiert werden, so daß weniger als eine MacAdam-Einheit des Farbunterschieds über die ganze Fläche des Papiers, gemessen unter Verwendung eines ACS Color Computers, eines Hunter Colorimeters oder eines MacBeth Colorimeters, auftritt. Vorzugsweise beträgt der Farbunterschied zwischen jeweils zwei benachbarten Bereichen auf der Blattoberfläche weniger als 0,2 MacAdam-Einheiten. In order to achieve the desired electrical properties as well as the desired aesthetic appearance, should the conductive fibers are evenly dispersed in the paper, leaving less than one MacAdam unit the color difference over the whole area of the paper, measured using an ACS Color Computer, a Hunter Colorimeter, or a MacBeth Colorimeter. Preferably the color difference is less than 0.2 MacAdam units between any two adjacent areas on the leaf surface.
Das erfindungsgemäße Papier und der erfindungsgemäße Schichtstoff sind für eine ganze Reihe von Anwendungsmöglichkeiten geeignet, unter anderem für die Oberflächenbeschichtung von Möbeln, für Bodenbeläge, Wandverkleidüngen, Wandvertäfelungen für Computerräume, Aufzüge, Behandlungsräume usw. sowie für bestimmte Schnellentladungs-Anwendungen wie z.B. Eliminatoren statischer Ladungen.The paper of the invention and that of the invention Laminates are suitable for a wide range of uses, including surface coating of furniture, for floor coverings, wall cladding, wall paneling for computer rooms, elevators, Treatment rooms etc. as well as for certain rapid discharge applications such as static eliminators Charges.
Das erfindungsgemäße Papier kann mit jedem der hierfür üblicherweise verwendeten Kunststoffe und synthetischen Harze imprägniert werden, mit Kunststoffen also, wie sie zur Herstellung dekorativer Schichtstoffe und Laminate üblich sind. Das Imprägnieren geschieht üblicherweise durch Eintauchen des trockenen Papiers in ein den Kunststoff enthaltendes Bad, wobei das Papier so lange in dem Bad verweilt, bis es die gewünschte Kunststoffmenge aufgenommen hat. Es können sowohl duroplastische als auch thermoplastische Kunststoffe verwendet werden. Repräsen- -20 tative Beispiele für die für die erfindungsgemäßen Zwecke geeigneten Kunststoffe sind Phenol-Formaldehyd-Harze, Amin-Formaldehyd-Harze, Harnstoff-Formaldehyd-Harze, Melamin-Formaldehyd-Harze sowie Epoxyharze, Polyesterharze, Vinylacetat-Copolymere, Acrylharze u.dgl. Vorzugsweise werden Phenol-Formaldehyd- und Melamin-Formaldehyd-Harze verwendet.The paper according to the invention can be used with any of these Usually used plastics and synthetic resins are impregnated with plastics like them for the production of decorative laminates and laminates are common. Impregnation is usually done by immersing the dry paper in a bath containing the plastic, with the paper in the The bath lingers until it has absorbed the desired amount of plastic Has. Both thermosetting and thermoplastic plastics can be used. Representative -20 tative examples of the plastics suitable for the purposes of the invention are phenol-formaldehyde resins, Amine-formaldehyde resins, urea-formaldehyde resins, Melamine-formaldehyde resins as well as epoxy resins, polyester resins, Vinyl acetate copolymers, acrylic resins and the like are preferred phenol-formaldehyde and melamine-formaldehyde resins are used.
Nach dem Imprägnieren werden die Blätter bis zum B-Zustand getrocknet oder gehärtet, zur Form eines "Buches",mit der dekorativen Schicht oben zusammengefaßt und in einer Presse zu einem Verbund laminiert. Typische Schichtstoffe umfassen zwei bis acht Lagen von mit phenolischem Harz imprägniertem Kernmaterial-Papier sowie ein oder mehrere mit Melaminharz imprägnierte dekorative Oberflächenblätter, einschließlich mindestens eines dekorativen Blattes mit hoher Deckkraft (Opazität) sowie gegebenenfalls eines darunterAfter impregnation, the leaves are dried or hardened to the B stage, to the shape of a "Book", combined with the decorative layer on top and laminated in a press to form a composite. Typical laminates comprise two to eight plies of phenolic resin impregnated core paper as well as one or more decorative surface sheets impregnated with melamine resin, including at least one decorative sheet with high covering power (opacity) and possibly one below
befindlichen Sperrblatts. Eine klare Uberzugsschicht kann ebenfalls verwendet werden. Die leitfähigen erfindungsgemäßen Papiere können für alle oder nur für einige ausgewählte Schichten des Laminats verwendet' werden.the locking sheet located. A clear coating layer can also be used. The conductive papers according to the invention can be used for all or only for some selected layers of the laminate are used.
Ein Vorteil der erfindungsgemäßen Papiere besteht darin, daß sie mit zufriedenstellender Qualität bedruckt werden können, mit Kunststoff imprägniert werden können und in der Dekorschicht des Laminats verwendet werden könnenOne advantage of the papers according to the invention is that that they can be printed with satisfactory quality, can be impregnated with plastic and can be used in the decorative layer of the laminate
IQ und gleichzeitig für die erforderlichen elektrischen Eigenschaften sorgen, die für die Ausbreitung und Ableitung statischer Ladungen erforderlich sind. Die üblicherweise zur Herstellung von Dekorschichten verwendeten Druckfarben werden von den erfindungsgemäßen leitfähigen Papieren gut absorbiert. Daher können verschiedene dekorative Effekte und vorteilhafte elektrische Eigenschaften gleichzeitig erzielt werden. IQ and at the same time ensure the necessary electrical properties that are necessary for the propagation and dissipation of static charges. The printing inks usually used to produce decorative layers are well absorbed by the conductive papers according to the invention. Therefore, various decorative effects and advantageous electrical properties can be obtained at the same time.
Die Erfindung wird nachstehend anhand der Beispiele näher erläutert.The invention is explained in more detail below with the aid of the examples.
Ein zur Herstellung eines dekorativen Schichtstoffes geeignetes leitfähiges Papier wurde hergestellt durch Dispergieren eines vorraffinierten Gemischs aus Hartholzpulpe und Weichholzpulpe in Wasser zusammen mit Titandioxidpigment in einer Menge von 40 %, bezogen auf das Gesamtgewicht der Pulpe, durch Zugabe von 5 % Celion C-20 Kohlenstoffasern (Celanese Corp.) unter Rühren mit geringer Scherbeanspruchung, durch Zugabe üblicher Mengen an Chemikalien für die Naßfestigkeit und Retention, und schließlich durch Formen des so entstandenen Papierstoffs zu einem Handblatt mittels einer üblichen Handblattherstellungsvorrichtung. Das Handblattgewicht betrug 0,106 kg/m2 und der Flächenwiderstand betrug 300 Ohm pro Quadrat. Wenn es für dieA conductive paper suitable for the production of a decorative laminate was produced by dispersing a pre-refined mixture of hardwood pulp and softwood pulp in water together with titanium dioxide pigment in an amount of 40%, based on the total weight of the pulp, by adding 5% Celion C-20 carbon fibers ( Celanese Corp.) with low shear agitation, adding conventional amounts of chemicals for wet strength and retention, and finally forming the resulting stock into a handsheet using conventional handsheet making equipment. The handsheet weight was 0.106 kg / m 2 and the sheet resistance was 300 ohms per square. If it's for the
oberste Schicht eines dekorativen Schichtstoffs verwendet wurde, besaß das entstehende Laminat einen Oberflächenwiderstand von 7 00 Ohm pro Quadrat.the top layer of a decorative laminate is used the resulting laminate had surface resistivity of 7 00 ohms per square.
;; Beispiel 2Example 2
Ein Überzugsblatt wurde hergestellt, wie in Beispiel 1 beschrieben, wobei jedoch Titandioxid aus dem Stoffeintrag weggelassen wurde. Dies führte zu einem Papier mit einem Grundgewicht von 0,046 kg/m2 und mit einem Flächenwiderstand von 200 Ohm pro Quadrat. Ein unter Verwendung dieses Überzugsblatts als oberste Schicht hergestellter Schichtstoff besaß einen Flächenwiderstand von 500 Ohm pro Quadrat.A coating sheet was prepared as described in Example 1, except that titanium dioxide was omitted from the furnish. This resulted in paper with a basis weight of 0.046 kg / m 2 and a sheet resistance of 200 ohms per square. A laminate made using this coating sheet as the top layer had a sheet resistance of 500 ohms per square.
Claims (15)
Courthouse Plaza Northeast
Dayton, Ohio 45463 / USA THE MEAD CORPORATION
Courthouse Plaza Northeast
Dayton, Ohio 45463 / USA
leihen.2. Conductive paper according to claim 1, characterized in that the conductive fiber is contained in an amount sufficient to give the paper a dry resistance
Rent.
Quadrat zu verleihen.3. Conductive paper according to claim 2, characterized in that the conductive fiber is contained in an amount sufficient to give the paper a dry resistance in the area
Give square.
von etwa 10 bis 10 Ohm pro Quadrat besitzt.5 10
from about 10 to 10 ohms per square.
besitzt.8. Conductive paper according to one of claims 1 to 6, characterized in that there is a dry resistance in the Bereii
owns.
30own.
30th
besitzt.13. Laminate according to claim 12, characterized in that the conductive paper has a dry resistance in
owns.
35Owns square.
35